热处理对2519铝合金接头组织及性能的影响

研究了焊后时效及固溶＋时效热处理对2519铝合金焊接接头组织和力学性能的影响．结果表明,时效处理后,处于欠时效态的焊缝析出强化相增加,硬度升高,而过时效态的热影响区软化区组织和硬度没有明显变化,焊接接头的强度略微提高,塑性下降．固溶＋时效处理后,焊缝中网状共晶减少,焊缝和热影响区软化区内的析出相形态变为细小的针状,且数量增加,焊缝金属硬度明显提高,热影响区的软化现象消失,焊接接头的强度和塑性显著增加．     

人工时效对7003/7046铝合金搅拌摩擦焊接头组织和力学性能的影响

采用差示扫描量热分析、硬度、室温拉伸实验、背散射电子衍射和透射电子显微镜等手段研究了焊后人工时效对7003-7046异种铝合金搅拌摩擦焊接(FSW)接头的微观组织和力学性能的影响。结果表明：FSW接头后退侧(7046铝合金侧)的硬度明显高于前进侧(7003铝合金侧),两侧平均硬度的差约为30HV;人工时效后接头的硬度提高,两侧平均硬度的差增大到约50HV,接头的屈服强度提高,抗拉强度略有提高,伸长率几乎不变。根据时效前后FSW接头不同区域微观组织的特征,分析了接头力学性能变化的原因。     

摩擦压力对Super304H/T92摩擦焊焊接接头性能的影响

利用连续驱动摩擦焊技术焊接Super304H和T92钢管,焊接接头具有良好的显微组织和力学性能。考察摩擦压力对焊接接头显微组织和力学性能的影响,研究表明:随着摩擦压力增加,焊合区和热影响区晶粒尺寸没有明显变化,热影响区碳化物析出相的数量略微增加,显微硬度逐渐增大,冲击韧性逐渐降低,拉伸断裂位置和拉伸强度没有变化。     

焊后热处理对7055-0.1Sc铝合金搅拌摩擦焊接头的组织与力学性能的影响

对11 mm厚的7055-0.1Sc-T4铝合金板材进行搅拌摩擦焊接，研究了焊后热处理对接头的组织和力学性能的影响。结果表明，热处理前接头的硬度分布呈“W”形，接头前进侧和后退侧都有一个最低硬度区，强度系数为63.0%～73.8%，拉伸断口位于后退侧最低硬度区。焊后人工时效(120℃×24 h)热处理使焊核的硬度提高，但是不改变接头最低硬度区的硬度，对拉伸性能和断裂行为的影响甚微。焊后的固溶(470℃×1.5 h+水淬)+人工时效(120℃×24 h)(T6)热处理不改变低焊速接头的晶粒组织，但是使高焊速接头焊核区底部的晶粒异常长大；T6热处理使接头各区域原有的沉淀相溶解，重新生成细小均匀的η’和η(MgZn₂)沉淀相，使其硬度显著提高；T6热处理使接头沿“S”线附近出现微小的孔洞、在拉伸过程中沿“S”线开裂、其抗拉强度比焊接态大幅度提高，达到母材强度的87%，但是其塑性严重降低。     

Ti-22Al-25Nb合金惯性摩擦焊接头显微组织与力学性能EI北大核心CSCD

采用惯性摩擦焊技术焊接Ti-22Al-25Nb合金,研究热处理前后焊接接头微观组织和显微硬度的变化,分析接头在650℃和750℃高温拉伸力学性能.结果表明:接头原始态焊合区由B2相和极少量残余α2相构成,热处理后焊合区由B2相和O相构成,O相由B2相直接相变产生,相变过程无成分变化.原始态焊合区的显微硬度高于母材,780℃/3 h热处理后焊合区的显微硬度陡升,大量析出的细小O相促进硬度升高,800℃/3 h热处理后焊合区显微硬度介于原始态和780℃/3 h热处理之间.高温拉伸断裂位置均位于母材区域,650℃拉伸断口微观形貌呈韧性断裂特征,断口存在较多浅而小的韧窝.     

Ti-22Al-25Nb合金惯性摩擦焊接头显微组织与力学性能

采用惯性摩擦焊技术焊接Ti-22Al-25Nb合金,研究热处理前后焊接接头微观组织和显微硬度的变化,分析接头在650℃和750℃高温拉伸力学性能。结果表明:接头原始态焊合区由B2相和极少量残余α_2相构成,热处理后焊合区由B2相和O相构成,O相由B2相直接相变产生,相变过程无成分变化。原始态焊合区的显微硬度高于母材,780℃/3 h热处理后焊合区的显微硬度陡升,大量析出的细小O相促进硬度升高,800℃/3 h热处理后焊合区显微硬度介于原始态和780℃/3 h热处理之间。高温拉伸断裂位置均位于母材区域,650℃拉伸断口微观形貌呈韧性断裂特征,断口存在较多浅而小的韧窝。     

时效处理对Super304H摩擦焊焊接接头析出相和显微硬度的影响

对Super304H摩擦焊焊接接头进行不同时间的625 ℃时效处理。随着时效处理时间的延长,焊合区、热影响区和母材区基体组织仍为奥氏体组织,晶粒无明显长大,析出相数量逐渐增多,显微硬度逐渐增加并在时效处理500 h达到最大值;随着时效时间的继续延长,M₂₃C₆碳化物聚集和长大导致显微硬度缓慢下降。     

转速对水下搅拌摩擦焊接7A04-T6铝合金组织与性能的影响

对7A04-T6铝合金板进行水下搅拌摩擦焊接(FSW),研究转速对水下FSW接头组织和力学性能的影响。结果表明:水下FSW接头的硬度最小值均位于热机械影响区。高转速条件下(950r/min)接头的硬度分布呈现"W"形,焊核区平均硬度值高于低转速条件下(475,600,750r/min)接头的硬度值。当焊速恒定为235mm/min,转速从475r/min提高到750r/min时,接头焊核区的析出相随转速的增大逐渐粗化,接头抗拉强度系数从89.71%降低到82.33%;当转速升高到950r/min时,析出相发生固溶时效,呈现细小弥散的分布特征,接头的强度系数提高到89.04%。接头具有较高的应变硬化能力,塑性伸长率较高。水下FSW接头的拉伸断口均呈现微孔聚合和解理混合断裂特征。     

ER5356焊丝用于7075铝合金MIG焊接头热处理性能

采用MIG焊使用ER5356焊丝进行3 mm厚7075铝合金对接焊,焊后接头进行T6热处理。通过光学显微镜、X射线衍射仪、扫描电镜与能谱仪结合室温拉伸、显微硬度与电化学腐蚀分析接头组织、力学性能与耐蚀性。结果表明：焊接时熔池流动将母材熔化部位的Zn,Cu等合金元素带入焊缝,析出MgZn₂与AlCuMg相,成为焊缝进行热处理强化的基础;热处理后,大部分析出相溶入基体形成固溶+时效强化,接头抗拉强度提升20%,焊缝硬度提升18.4%,耐蚀性提高。但由于从母材流入焊缝的合金元素含量有限,焊丝与母材力学性能的差异与热影响区软化现象无法消除。     

2060搅拌摩擦焊对接接头显微组织与析出相分析

选用Al-Li-Cu-Mg系铝锂合金2060,开展搅拌摩擦焊对接接头显微组织与析出相演变规律研究.搅拌摩擦焊对接接头,呈现典型的母材、热影响区、热机影响区和焊核区四区分布特点.母材为双向板条组织,在α板条中有大量三角形AlCu2Mn化合物析出,但在其它相区,当受到热影响时,该相消失;热影响区组织粗大,热机影响区晶粒受到机械力作用,前进侧拉长,后退侧破碎;焊核区为等轴晶组织,出现了高温析出相AlxCuxMn,均布于整个焊核区域.接头显微硬度在母材区最高,热影响区最低,焊核区低于母材,稳定在115 HV.     

焊后热处理对AA7204-T4铝合金搅拌摩擦焊接头组织与力学性能的影响

采用搅拌摩擦焊对AA7204-T4铝合金板材进行焊接,研究焊后热处理对FSW接头组织与力学性能的影响。结果表明:焊后(AW)态焊核区平均晶粒尺寸和再结晶分数分别为4.7μm和81.9%,焊后直接人工时效(AA)后二者分别为4.8μm和82.4%,焊后固溶+人工时效(SAA)后分别为5.9μm和86.5%,AA态并未对焊核区的晶粒结构产生明显的影响,而SAA态则使其分别提高了25.5%和5.6%。AW态,AA态和SAA态接头抗拉强度分别为296.6,318.2 MPa和357.4 MPa,AA态对接头力学性能提升有限,而SAA态则有效提升接头力学性能,焊接系数达92.0%。焊后固溶淬火导致接头连接界面"S"线处产生微裂纹,接头断裂于此,且伸长率严重降低。     

锂电池PACK包Al-Zn-Mg-Cu铝合金CMT 焊接组织与性能研究

以锂电池包箱体常用的7003铝合金为研究对象,采用冷金属过渡焊接工艺(CMT)对7003铝合金进行焊接后,经过固溶(485 ℃,3 h)、人工时效(160 ℃,2 h)和自然时效(72 h)热处理后,进行组织和性能研究。通过慢应变速率拉伸试验、常温拉伸试验、显微维氏硬度测试、扫描电子显微镜分析等方法,对该铝合金接头的母材和焊缝的抗腐蚀性能、力学性能以及微观组织形貌进行研究。结果表明:当慢应变速率为1×10-6 s-1时,基材和焊接试样的应力腐蚀敏感性指数(ISSRT)分别为2.73%和9.74%;对焊接试样的接头进行晶间腐蚀和剥落腐蚀测试并评级,晶间腐蚀为4级,剥落腐蚀为PA级;焊接接头的电导率、抗拉强度、延伸率分别为22.0%(IACS)、330.7 MPa、10.0%。     

The microstructure and mechanical properties of friction stir welded Al–Zn–Mg alloy in as welded and heat treated conditions

High strength aluminium alloys generally present low weldability because of the poor solidification microstructure, porosity in the fusion zone and loss in mechanical properties when welded by fusion welding processes which otherwise can be welded successfully by comparatively newly developed process called friction stir welding (FSW). This paper presents the effect of post weld heat treatment (T₆) on the microstructure and mechanical properties of friction stir welded 7039 aluminium alloy. It was observed that the thermo-mechanically affected zone (TMAZ) showed coarser grains than that of nugget zone but lower than that of heat affected zone (HAZ). The decrease in yield strength of welds is more serious than decrease in ultimate tensile strength. As welded joint has highest joint efficiency (92.1%). Post weld heat treatment lowers yield strength, ultimate tensile strength but improves percentage elongation.     

Effect of a post-weld heat treatment on the mechanical and microstructure properties of AA6061 joints welded by the gas metal arc welding cold metal transfer method

This work studies the effect of a post-weld heat treatment (PWHT) on the mechanical and microstructure properties of an AA6061 sample welded using the gas metal arc welding (GMAW) cold metal transfer (CMT) method. The CMT method was used because the method provides spatter-free welding, outstanding gap bridging properties, low heat input and a high degree of process flexibility. The welded samples were divided into as-welded and PWHT samples. The PWHTs used on the samples were solution heat treatment, water quenching and artificial aging. Both welded samples were cut according to the ASTM E8M-04 standard to obtain the tensile strength and the elongation of the joints. The failure pattern of the tensile tested specimens was analysed using scanning electron microscopy (SEM). A Vickers microhardness testing machine was used to measure the hardness across the joints. From the results, the PWHTs were able to enhance the mechanical properties and microstructure characteristics of the AA6061 joints welded by the GMAW CMT method.     

热处理温度对TC17(α+β)/TC17(β)钛合金线性摩擦焊接头组织及力学性能的影响

对TC17(α+β)/TC17(β)钛合金线性摩擦焊接头进行热处理实验,采用光学显微镜(OM),扫描电子显微镜(SEM)和显微硬度仪等检测手段,研究不同热处理温度对焊接接头微观组织及力学性能的影响。结果表明:焊态下,接头焊缝区发生再结晶,界面处为亚稳定β相组织,显微硬度低于母材,接头高周疲劳强度为345 MPa。TC17(α+β)侧热力影响区因焊接速率过快,残留了大量的初生α相。经过焊后热处理,亚稳定β相分解,焊缝析出弥散的(α+β)相。随着热处理温度的升高,细小的次生α相长大,部分发生球化。热处理后,因亚稳定β相分解,焊缝及热力影响区的显微硬度大幅度升高,接头疲劳强度平均提高65 MPa;随着热处理温度的升高,接头热力影响区的断裂韧度增加。     

热处理对6005A铝合金激光焊接头组织和性能的影响

高速列车车体轻量化制造的迫切需求,使得铝合金结构在车体制造中得到广泛应用,而铝合金焊接也成为高铁车体制造的关键工艺.本文采用激光填丝焊方法焊接6005A-T6铝合金,并对焊接接头进行了固溶/时效热处理.利用扫描电镜、XRD能谱分析及拉伸实验,对焊后热处理的焊接接头组织及性能进行研究.研究发现,与母材相比,由于焊接接头中...     

6005A-T6铝合金搅拌摩擦焊接头组织与力学性能特征

采用光学显微镜、扫描电子显微镜、透射电子显微镜、拉伸实验机和显微硬度计对6005A铝合金搅拌摩擦焊接头的微观组织及力学性能进行了研究。结果表明:焊核区为细小的等轴晶,几乎所有粒子溶于基体;热机械影响区呈现为被拉长的畸变晶粒,且存在大量的位错;热影响区的组织明显粗化,处于过时效状态。与母材相比,搅拌摩擦焊接头的强度及伸长率均有下降趋势,且接头出现软化,最小硬度值出现在前进侧的热影响区内。搅拌头旋转速率为1200r/min、焊接速率为200mm/min时可获得优质接头,抗拉强度达到母材强度的72%,伸长率达到母材的69%。     

Effect of pre- and post-weld heat treatment on metallurgical and tensile properties of Inconel 718 alloy butt joints welded using 4 kW Nd:YAG laser

The effects of pre- and post-weld heat treatments on the butt joint quality of 3.18-mm thick Inconel 718 alloy were studied using a 4 kW continuous wave Nd:YAG laser system and 0.89-mm filler wire with the composition of the parent metal. Two pre-weld conditions, i.e., solution treated, or solution treated and aged, were investigated. The welds were then characterized in the as-welded condition and after two post-weld heat treatments: (i) aged, or (ii) solution treated and aged. The welding quality was evaluated in terms of joint geometries, defects, microstructure, hardness, and tensile properties. HAZ liquation cracking is frequently observed in the laser welded Inconel 718 alloy. Inconel 718 alloy can be welded in pre-weld solution treated, or solution treated and aged conditions using high power Nd:YAG laser. Post-weld aging treatment is enough to strengthen the welds and thus post-weld solution treatment is not necessary for strength recovery.