1.
Abstract: The effects of shot‐peening on fretting fatigue crack growth behaviour in titanium alloy, Ti‐6A1‐4V were investigated. Three shot‐peening intensities: 4A, 7A and 10A were considered. The analysis involved the fracture mechanics and finite element sub‐modelling technique to estimate crack propagation lives. These computations were supplemented with the experimentally measured total fretting fatigue lives of laboratory specimens to assess the crack initiation lives. Shot‐peening has significant effect on the initiation/propagation phases of fretting fatigue cracks; however this effect depends upon the shot‐peening intensity. The ratio of crack initiation and total life increased while the ratio of the crack propagation and total life decreased with an increase of shot‐peening intensity. Effects of residual compressive stress from shot‐peening on the crack growth behaviour were also investigated. The fretting fatigue crack propagation component of the total life with relaxation increased in comparison to its counterpart without relaxation in each shot‐peened intensity case while the initiation component decreased. Improvement in the fretting fatigue life from the shot‐peening and also with an increase in the shot‐peening intensity appears to be not always due to increase in the crack initiation resistance from shot‐peened induced residual compressive stress. 相似文献
2.
This work focuses on determining the effect of shot and laser peening on fretting fatigue in the Al 7075-T651 alloy. These surface treatments generate a residual compressive stress field near the treated surface where contact under fretting fatigue produces high stress levels. The fretting fatigue resistance of shot and laser peened specimens was assessed in a series of tests involving measurements of the residual stress field, residual stress relaxation under the action of cyclic loads, the friction coefficient, surface roughness and material hardness. The obtained results are compared with those for untreated specimens. The tests show the beneficial effect of the compressive residual stresses and the improvement that surface roughness causes in fretting fatigue life, especially in shot peened specimens. Another important effect observed, is the partial residual stress relaxation produced during the fretting fatigue tests. 相似文献
3.
V. SABELKIN S. A. MARTINEZ S. MALL S. SATHISH M. P. BLODGETT 《Fatigue & Fracture of Engineering Materials & Structures》2005,28(3):321-332
The effects of shot‐peening intensity on fretting fatigue crack‐initiation behaviour of titanium alloy, Ti–6Al–4V, were investigated. Three intensities, 4A, 7A and 10A with 100% surface coverage, were employed. The contact geometry involved a cylinder‐on‐flat configuration. Residual stress and improvement in fretting fatigue life were directly related to shot‐peening intensity. The magnitude of compensatory tensile stress and its location away from the contact surface increased with increasing intensity. The relaxation of residual stress occurred during fretting fatigue which increased with increasing the number of cycles. An analysis using a critical plane‐based fatigue crack‐initiation model showed that stress relaxation during the fretting fatigue affects life and location of crack initiation. Greater relaxation of the residual stress caused greater reduction of fatigue life and shifted the location of crack initiation from inside towards the contact surface. Modified shear stress range (MSSR) parameter was able to predict fretting fatigue crack‐initiation location, which agreed with the experimental counterparts. Also, the computed parameter showed an appropriate trend with the experimental observations of the measured fretting fatigue life based on the shot‐peening intensity. 相似文献
4.
激光喷丸强化对半圆孔件疲劳寿命的影响 总被引:2,自引:1,他引:1
为研究激光喷丸强化对7075-T6铝合金半圆孔件疲劳寿命的影响,对激光喷丸与未喷丸的试样进行了对比试验,利用X射线应力仪测定其表面残余应力,并对试样进行疲劳拉伸试验.用扫描电镜观察了两类试样疲劳断口的形貌,并采用数理统计方法对其疲劳寿命进行分析.研究表明:经激光喷丸处理区域,表面存在较大的残余压应力,幅值为310 MPa;未喷丸试样疲劳裂纹条带的宽度为0.7~0.8μm,而喷丸试样疲劳裂纹条带的宽度为0.3~0.4μm,说明喷丸试样裂纹扩展的速度比未喷丸试样慢很多;激光喷丸后半圆孔件的疲劳寿命比未喷丸的疲劳寿命提高了2.8~7.2倍. 相似文献
5.
A new mechanism modelling is proposed in this paper to explain the shot peening effect on fatigue life predictions of mechanical components. The proposed methodology is based on the crack growth analysis of shot peened specimens, which are affected by the interaction of surface roughness and residual stress produced during the shot peening process. An asymptotic stress intensity factor solution is used to include the surface roughness effect and a time‐varying residual stress function is used to change the crack tip stress ratio during the crack propagation. Parametric studies are performed to investigate the effects of surface roughness and the residual stress relaxation rate. Following this, a simplified effective residual stress model is proposed based on the developed mechanism modelling. A wide range of experimental data is used to validate the proposed mechanism modelling. Very good agreement is observed between experimental data and model predictions. 相似文献
6.
The effect of residual stresses arising from laser shock peening on fatigue crack growth 总被引:1,自引:0,他引:1
Residual stresses have in the past been introduced to manipulate growth rates and shapes of cracks under cyclic loads. Previously, the effectiveness of shot peening in retarding the rate of fatigue crack growth was experimentally studied. It was shown that the compressive residual stresses arising from the shot peening process can affect the rate of crack growth. Laser shock peening can produce a deeper compressive stress field near the surface than shot peening. This advantage makes this technique desirable for the manipulation of crack growth rates. This paper describes an experimental program that was carried out to establish this effect in which steel specimens were partially laser peened and subsequently subjected to cyclic loading to grow fatigue cracks. The residual stress fields generated by the laser shock peening process were measured using the neutron diffraction technique. A state of compressive stress was found near the surface and tensile stresses were measured in the mid-thickness of the specimens. Growth rates of the cracks were observed to be more affected by the tensile core than by the compressive surface stresses. 相似文献
7.
Daniel J. Chadwick Siavash Ghanbari David F. Bahr Michael D. Sangid 《Fatigue & Fracture of Engineering Materials & Structures》2018,41(1):71-83
Shot peening is a dynamic cold‐working process involving the impingement of peening media onto a substrate surface. Shot peening is commonly used as a surface treatment technique within the aerospace industry during manufacturing to improve fatigue performance of structural components. The compressive residual stress induced during shot peening results in fatigue crack growth retardation, improving the performance of shot‐peened components. However, shot peening is a compromise between the benefit of inducing a compressive residual stress and causing detrimental surface damage. Because of the relatively soft nature of AA7050‐T7451, shot peening can result in cracking of the constituent precipitate particles, creating an initial damage state. The aim of this paper is to understand the balance and fundamentals of these competing phenomena through a comparative study throughout the fatigue lifecycle of baseline versus shot‐peened AA7050‐T7451. Microstructure and surface topology characterization and comparison of the baseline and shot‐peened AA7050‐T7451 has been performed using scanning electron microscopy, electron backscatter diffraction, energy dispersive spectroscopy, and optical profilometry techniques. A residual stress analysis through interrupted fatigue of the baseline and shot‐peened AA7050‐T7451 was completed using a combination of X‐ray diffraction and nanoindentation. The fatigue life performance of the baseline versus shot‐peened material has been evaluated, including crack initiation and propagation. Subsurface particles crack upon shot peening but did not incubate into the matrix during fatigue loading, presumably due to the compressive residual stress field. In the baseline samples, the particles were initially intact, but upon fatigue loading, crack nucleation was observed in the particles, and these cracks incubated into the matrix. In damage tolerant analysis, an initial defect size is needed for lifetime assessment, which is often difficult to determine, leading to overly conservative evaluations. This work provides a critical assessment of the mechanism for shot peening enhancement for fatigue performance and quantifies how incubation of a short crack is inhibited from an initially cracked particle into the matrix within a residual stress field. 相似文献
8.
The influence of shot peening on the fatigue durability of normalized carbon steels subjected to variable amplitude loading has been investigated. The relaxation of residual stresses was recorded during the fatigue life time. Strain amplitude spectra were extracted from real spectra recorded from components in service. The results were compared with data achieved from constant amplitude testing. In both types of tests parallel studies were made on both peened and unpeened specimens. Shot peening leads to pronounced increase in life time, especially for smaller amplitudes. For both variable and constant amplitude loading shot peened specimens exhibit longer life provided the residual stresses during fatigue loading do not relax more than to about 60% of their initial value. To get an improvement in life time of at least a factor two for peened specimens, the stress amplitude in constant amplitude loading or the maximum stress amplitude in variable amplitude history must not be more than 20% larger than the magnitude of the initial residual stresses. This limit corresponds to 1.2 times the yield strength of the unaffected material. 相似文献
9.
Fretting fatigue behaviour of shot‐peened titanium alloy, Ti‐6Al‐4V was investigated at room and elevated temperatures. Constant amplitude fretting fatigue tests were conducted over a wide range of maximum stresses, σmax= 333 to 666 MPa with a stress ratio of R= 0.1 . Two infrared heaters, placed at the front and back of specimen, were used to heat and maintain temperature of the gage section of specimen at 260 °C. Residual stress measurements by X‐ray diffraction method before and after fretting test showed that residual compressive stress was relaxed during fretting fatigue. Elevated temperature induced more residual stress relaxation, which, in turn, decreased fretting fatigue life significantly at 260 °C. Finite element analysis (FEA) showed that the longitudinal tensile stress, σxx varied with the depth inside the specimen from contact surface during fretting fatigue and the largest σxx could exist away from the contact surface in a certain situation. A critical plane based fatigue crack initiation model, modified shear stress range parameter (MSSR), was computed from FEA results to characterize fretting fatigue crack initiation behaviour. It showed that stress relaxation during test affected fretting fatigue life and location of crack initiation significantly. MSSR parameter also predicted crack initiation location, which matched with experimental observations and the number of cycles for crack initiation, which showed the appropriate trend with the experimental observations at both temperatures. 相似文献
10.
Short‐crack thresholds and propagation in an AISI 4340 steel under the effect of SP residual stresses
下载免费PDF全文
![点击此处可从《Fatigue & Fracture of Engineering Materials & Structures》网站下载免费的PDF全文](/ch/ext_images/free.gif)
L. Patriarca M. Filippini S. Beretta 《Fatigue & Fracture of Engineering Materials & Structures》2018,41(6):1275-1290
The effect of residual stresses induced by shot‐peening in a high‐strength AISI 4340 steel has been studied with the purpose of deriving a consistent fatigue model incorporating the results of fatigue crack growth experiments in the threshold region for a broad range of load ratio (R‐ratio ranging from ?2.5 to 0.7), and the effect of short cracks by means of a modified El‐Haddad model. The proposed model, taking into account the effect of crack closure and being capable to assess the conditions for fatigue propagation of short cracks partially embedded in the shot‐peened surface layer, was validated against constant amplitude fatigue experiments conducted in the endurance strength region, ie, for fatigue lives up to 107 cycles, with micronotched specimens in the presence of shot‐peening residual stresses. The proposed model was also validated by comparing the results of fatigue crack propagation simulations with fatigue crack growth experiments under variable amplitude loading, experimentally reproducing the combined effect of service fatigue loads and shot‐peening residual stresses. 相似文献
11.
A lot of research has been done to improve fatigue strength of materials by creating compressive residual stress field in their surface layers through shot peening. In this paper, fatigue strength of shot peened leaf springs has been calculated from laboratory samples. The axial fatigue strength of EN45A spring steel specimen is evaluated experimentally as a function of shot peening in the conditions used for full-scale leaf springs testing in industries. Optimum shot peening condition for specimen is found and S/N curves of the specimens are correlated with leaf springs curve. A mathematical model has been developed which predicts the fatigue life of leaf springs for a given stress at varying shot peening conditions. Predictions from this model are compared with experimental data. The estimation of fatigue life and relaxation of compressive residual stress field are discussed. 相似文献
12.
《Materials Science & Technology》2013,29(9):1067-1072
AbstractThe potential of fretting fatigue strength enhancement by a duplex surface engineering process involving shot peening of plasma nitrided steel, termed duplex SP/PN, is demonstrated. Specimens of 709M40 steel were individually plasma nitrided, shot peened, or duplex SP/PN treated. Fretting fatigue properties of the surface engineered specimens were evaluated. Surface roughness, residual stress, and hardening effect following the various surface treatments were examined and compared. It has been found that the duplex treatment can significantly improve the fretting fatigue strength of the investigated low alloy steel. Under the present testing conditions, the duplex SP/PN treatment increased the fretting fatigue strength (at 107 cycles) of 709M40 steel by more than 70% relative to the nitrided, 120% to the shot peened, and 500% to the untreated steel. The improvement has been explained in terms of the significantly increased surface hardness and compressive residual stress in the near surface region following the duplex SP/PN treatment. By analysing the stress distributions in a shot peened surface, the influence of surface roughness on fretting fatigue strength is also discussed. 相似文献
13.
Omar Hatamleh 《International Journal of Fatigue》2009,31(5):974-988
The effects of various surface treatment techniques on the fatigue crack growth performance of friction stir welded 2195 aluminum alloy were investigated. The objective was to reduce fatigue crack growth rates and enhance the fatigue life of welded joints. The crack growth rates were assessed and characterized for different peening conditions at a stress ratio (R) of 0.1, and 0.7. The surface and through-thickness residual stress distribution were also investigated and presented for the various regions in the weld. Tensile residual stresses introduced during the welding process were found to become significantly compressive, particularly after laser peening. The effect of the compressive stresses was deemed responsible for increasing the resistance to fatigue crack growth of the welds. The results indicate a significant reduction in fatigue crack growth rates using laser peening compared to shot peening and native welded specimens. This reduced fatigue crack growth rate was comparable to the base unwelded material. 相似文献
14.
The so called “severe plastic deformation” (SPD) processes are object of increasing interest due to their ability to obtain a nanostructured surface layer of material with supposed superior properties. Among these processes, severe shot peening (SSP) is very attractive from an industrial point of view, due to its versatility and wide applicability.In this study the X70 microalloyed steel is considered and treated by severe shot peening.Fatigue tests were performed to assess how SSP treatment affects the fatigue behavior of this steel.Roughness and X-ray diffraction residual stress measurements as well as microscopy observations have been carried out on the treated specimens. Rotating bending fatigue tests at room temperature on smooth and notched specimens were performed to evaluate the effect of the treatment on fatigue strength. Fracture surfaces have been then observed by scanning electron microscopy. The results were compared with the ones of a series of not peened specimens and another series of specimens shot peened with conventional parameters and interpreted by considering the characteristics of the nanostructured layer, the induced residual stresses and the surface work hardening. The comparison shows a very significant fatigue strength improvement for severely shot peened specimens, especially for the notched specimens. 相似文献
15.
A. CAMARGO H. VOORWALD 《Fatigue & Fracture of Engineering Materials & Structures》2007,30(11):993-1007
In recent years, with higher demand for improved quality and corrosion resistance, recovered substrates have been extensively used. Consequently residual stresses originated from these coatings reduce the fatigue strength of a component. Due to this negative influence occasioned by corrosion resistance protective coatings, an effective process like shot peening must be considered to improve the fatigue strength. The shot peening treatment pushes the crack sources beneath the surface in most of medium and high cycle cases due to the compressive residual stress field (CRSF) induced. The aim of this study was to evaluate the influence on the fatigue life of anodic films grown on 7050-T7451 aluminium alloy by sulphuric acid anodizing, chromic acid anodizing and hard anodizing. The influence on the rotating and reverse bending fatigue strength of anodic films grown on the aluminium alloy is to degrade the stress life fatigue performance of the base material. A consistent gain in fatigue life in relation to the base material was obtained through the shot peening process in coated specimens, associated to a residual stress field compressive near the surface, useful to avoid fatigue crack nucleation and delay or even stop crack propagation. 相似文献
16.
Shot peening has been widely applied in industrial design to improve fatigue durability of high loaded machine components. The compressive residual stress induced by shot peening is in general assumed to be responsible for the improvement of material fatigue strength. In the present work a cyclic cohesive zone model is extended to analyze three-dimensional fatigue crack growth in shot-peened specimens. Fatigue crack growth behaviors in both unpeened and peened specimens are investigated using 3D finite element analysis. The parameters of the cohesive zone model have been identified in 2D unpeened specimens and are applied to predict peened specimens directly. The results indicate that shot peening strongly affects crack initiation time and crack profiles, but has little effect on crack propagation rate. It implies that the shot peening will hardly change Paris’ law used for the damage tolerant design. 相似文献
17.
The influence of partial surface shot peening on fatigue crack growth behaviour of a high‐strength ferritic steel
下载免费PDF全文
![点击此处可从《Fatigue & Fracture of Engineering Materials & Structures》网站下载免费的PDF全文](/ch/ext_images/free.gif)
A. Al‐Turaihi A. Mehmanparast F. Brennan 《Fatigue & Fracture of Engineering Materials & Structures》2018,41(3):663-674
The effects of partial surface shot peening on the fatigue crack growth behaviour of a ferritic steel have been experimentally investigated in this paper. Dog‐bone specimens fabricated from Optim700QL were tested under tension‐tension fatigue loads. Three distinct extents of partial shot peening, with respect to the crack tip and specimen symmetry line, were tested. The fatigue crack growth results from these experiments have been compared with those obtained from the same specimen geometry but with no peening. The results show that the residual stress fields formed ahead of the initial notch tip due to the partial peening process play a significant role in the fatigue crack growth behaviour of the material and effectively result in accelerated crack propagation at the midwidth of the specimens. It has been shown in this study that partial peening can lead to a fatigue crack growth rate around twice as fast as that of the unpeened specimen. 相似文献
18.
Low cycle fatigue life prediction in shot‐peened components of different geometries—part I: residual stress relaxation
下载免费PDF全文
![点击此处可从《Fatigue & Fracture of Engineering Materials & Structures》网站下载免费的PDF全文](/ch/ext_images/free.gif)
C. You M. Achintha K. A. Soady N. Smyth M. E. Fitzpatrick P. A. S. Reed 《Fatigue & Fracture of Engineering Materials & Structures》2017,40(5):761-775
In this study, the residual stress relaxation behaviour occurring during low‐cycle fatigue in shot‐peened specimens with either a flat or a notched geometry has been studied. A representative low‐pressure steam turbine material, FV448, was used. The residual stress and strain hardening profiles caused by shot peening were measured experimentally and were then incorporated into a finite element model. By allowing for both effects of shot peening, the residual stress relaxation behaviour was successfully simulated using this model and correlated well with the experimental data. Although more modelling work may be required to simulate the interaction between shot peening effects and external loads in a range of notched geometries, the model predictions are consistent with the specimens tested in the current study. The novelty of this study lies in the development of such a modelling approach which can be used to effectively simulate the complex interaction between shot peening effects and external loads in notched regions. Compared with the un‐notched geometry, the notched geometry was found to be more effective in retaining the improvement in fatigue life resulting from shot peening, by restricting the compressive residual stress relaxation during fatigue loading. 相似文献
19.
The present paper is aimed at investigating the effect of shot peening on the high and very-high cycle plain fatigue resistance of the Al-7075-T651 alloy. Pulsating bending fatigue tests (R = 0.05) were carried out on smooth samples exploring fatigue lives comprised between 105 and 108 cycles. Three peening treatments were considered to explore different initial residual stress profiles and surface microstructural conditions. An extensive analysis of the residual stress field was carried out by measuring with the X-ray diffraction (XRD) technique the residual stress profile before and at the end of the fatigue tests. Fatigue crack initiation sites were investigated through scanning electron microscopy (SEM) fractography. The surface morphology modifications induced by shot peening were evaluated using an optical profilometer. The influence of surface finishing on the fatigue resistance was quantified by eliminating the surface roughness in some peened specimens through a tribofinishing treatment. The capability of shot peening to hinder the initiation and to retard the subsequent propagation of surface cracks is discussed on the basis of a model combining a multiaxial fatigue criterion and a fracture mechanics approach. 相似文献
20.
A literature survey on the stability and significance of residual stresses during fatigue 总被引:1,自引:0,他引:1
R. C. McCLUNG 《Fatigue & Fracture of Engineering Materials & Structures》2007,30(3):173-205
Many manufacturing processes can induce residual stresses in components. These residual stresses influence the mean stress during cyclic loading and so can influence the fatigue life. However, the initial residual stresses induced during manufacturing may not remain stable during the fatigue life. This paper provides a broad and extensive literature survey addressing the stability of surface and near‐surface residual stress fields during fatigue, including redistribution and relaxation due to static mechanical load, repeated cyclic loads, thermal exposure and crack extension. The implications of the initial and evolving residual stress state for fatigue behaviour and life prediction are addressed, with special attention to fatigue crack growth. This survey is not a critical analysis; no detailed attempt is made to evaluate the relative merits of the different explanations and models proposed, to propose new explanations or models or to provide quantitative conclusions. Primary attention is given to the residual stresses resulting from four major classes of manufacturing operations: shot peening and related surface treatments, cold expansion of holes, welding and machining. 相似文献