活性艳红K-2BP的电化学脱色及能耗分析

以Pt片作工作电极和辅助电极,NaCl为支持电解质,研究了活性艳红K-2BP的电化学脱色降解行为.通过整体电解获得其电化学反应特性,通过调控溶液的性质考察了不同体系对其降解效果的影响.实验结果表明,NaCl浓度为0.2 mol/L、电流密度为60 mA/cm2和室温条件下,30 mg/L的活性艳红K-2BP经电化学降解1 h,脱色率可达94.4%.单位能耗为10 kWh/kg.     

Ti/SnO2-Sb电极的制备及降解亚甲基蓝的研究

采用高温热氧化法制备了Ti/SnO_2-Sb电极,用扫描电子显微镜(SEM)表征了电极的形貌。以Ti/SnO_2-Sb电极为阳极,钛网为阴极,对亚甲基蓝废水进行电催化氧化降解,研究不同因素对亚甲基蓝脱色率的影响,并分析了亚甲基蓝的降解效果。结果表明,当亚甲基蓝的初始浓度为100mg·L~(-1),电流密度为10mA·cm~(-2),电解质浓度为0.10mol·L~(-1),pH=10时,反应30min,亚甲基蓝的脱色率为98.8%,60min时溶液的COD去除率为72.8%。     

SnWO4/g-C3N4复合光催化剂降解亚甲基蓝溶液

采用溶剂热法制备SnWO_4/g-C_3N_4复合光催化剂,在可见光降解亚甲基蓝实验中研究复合催化剂的光催化性能。考察催化剂投加量、亚甲基蓝溶液初始浓度、溶液pH值、盐效应对光催化性能的影响及SnWO_4/g-C_3N_4复合光催化剂的重复利用性。实验结果表明,在催化剂投加量1.0 g·L~(-1)、亚甲基蓝溶液初始浓度15 mg·L~(-1)和溶液pH值7.08时,在可见光条件下反应3 h,亚甲基蓝溶液脱色率达到94.2%;NaCl对光催化降解亚甲基蓝具有抑制作用,加入10 mmol·L~(-1)的NaCl溶液后亚甲基蓝的脱色率降为76.0%;复合光催化剂循环使用5次后,暗吸附后光照3 h,亚甲基蓝溶液的总脱色率仍可达到78.7%,重复利用性良好。     

改性粉煤灰降解亚甲基蓝溶液的试验研究

探讨以粉煤灰为载体制备粉煤灰／TiO2复合物进行光催化降解亚甲基蓝试验。研究几种因素对亚甲基蓝光降解反应的影响,结果表明,当改性粉煤灰投加量为8g／L,亚甲基蓝浓度30mg／L,高压汞灯250W条件下,反应时间60min左右,亚甲基蓝脱色率达到了95％以上。     

新型钛基体PbO2电极的制备及降解性能研究

采用电沉积法制备钛基体PbO2电极并对其表面形貌进行了表征,所制备的电极具有较高的析氧电位和良好的电催化活性。以制备的钛基PbO2为阳极,抛光钛电极为阴极,分别进行电流密度、反应时间、pH、电解质质量浓度等单因素试验,确定PbO2电极对亚甲基蓝的最优降解条件为:pH=6,电解质质量浓度为5.0 g.L-1,电流密度为5×10-2A.cm-2,该条件下亚甲基蓝1 h的降解率可以达到99%;且电流密度为0.25×10-2A.cm-2时能耗最低。     

黄丝衣霉处理亚甲基蓝废水的研究

本文主要研究了黄丝衣霉对亚甲基蓝染料废水的生物处理效果。采用单因素及正交实验研究了亚甲基蓝浓度、pH值、投菌量等因素对黄丝衣霉降解亚甲基蓝废水的影响和最佳处理条件。实验表明,工艺的最佳运行参数为:组合填料,pH=7,亚甲基蓝浓度为10mg/L,投菌量为10g/L,72h脱色率可达75.27%。     

TiO2膜光电催化氧化法降解印染废水的研究

采用TiO2膜电极,利用电化学和光催化协同作用对印染废水进行了降解,讨论了协同作用的机理。考察了电流密度、溶液pH值和光照强度等因素对降解率的影响。研究结果表明：光电催化氧化法的活性蓝染料溶液降解率高于电极氧化法和光催化法,证明电化学和光催化在反应过程中具有协同作用。在电流密度20 mA/cm2、pH值为4、光照距离为8 cm的条件下,降解初始浓度100 mg/L活性蓝染料模拟印染废水,2.5 h时COD去除率为88.4%,色度脱除率为93%。     

改性粉煤灰对甲基橙废水的电化学氧化

以酸和碱为改性剂,制备改性粉煤灰。考察了不同反应条件改性粉煤灰作为粒子电极对甲基橙染料废水脱色率的影响。试验结果表明：在室温下反应时间为15min、甲基橙初始浓度为100mg／L、改性剂用量为10g／L、电流密度为95mA／cm^2、0．48gNaCl的最佳条件下,甲基橙的脱色率高达96．21％;在最佳反应条件下电解65min,COD去除率可达76.8％。     

活性炭负载锰催化Na_2S_2O_8降解亚甲基蓝的研究

采用浸渍法制备活性炭负载锰的催化剂,探讨了锰负载量、Na_2S_2O_8浓度、催化剂用量、亚甲基蓝的初始浓度、pH值以及无机离子对降解亚甲基蓝的影响,并运用XRD和SEM对该催化剂进行表征。实验结果表明:在锰负载量为6%、Na_2S_2O_8浓度为5.5g/L、催化剂用量为0.25g、亚甲基蓝初始浓度为14mg/L、pH值为5的条件下,亚甲基蓝的降解率最高为97.1%。     

不锈钢基PbO2电极电催化氧化降解甲基橙性能的研究

本研究以自制的不锈钢基PbO2电极对25mg·L^-1的甲基橙溶液进行电催化氧化降解。考察了电流密度、支持电解质浓度、溶液pH值、温度等因素对甲基橙脱色率的影响,确定了电催化氧化甲基橙的最佳反应条件,即电流密度为50mA/cm^2,支持电解质Na2SO4的浓度为0．04mol·L^-1,降解20min后,甲基橙脱色率可达到90％以上。本研究还对几种不同印染废水进行了电催化氧化降解,结果表明,不锈钢基PbO2电极对不同的印染废水均有较好的脱色效果。     

负载型酞菁铜对亚甲基蓝的光催化降解研究

采用浸渍法将α-八环戊氧基酞菁铜(α-CyOPcCu)封装到介孔分子筛SBA-15上,通过电镜扫描、红外光谱扫描及氮气吸附对催化剂结构进行了表征,并研究了其对亚甲基蓝的光催化氧化性质。考察了催化剂用量、过氧化氢浓度对亚甲基蓝脱色率的影响。结果表明:当光照强度500 W,亚甲基蓝质量浓度4 mg/L,催化剂CyOPcCu/SBA-15质量浓度0.6 g/L,过氧化氢浓度0.6 mmol/L时,在90 min内亚甲基蓝降解率达99.60%。影响程度由大到小依次为过氧化氢浓度、催化剂质量浓度,该反应符合一级反应动力学方程,速率常数k=0.052 9 min-1。     

响应曲面法优化电催化降解染料废水工艺的研究

采用中心复合设计的响应曲面法预测电催化降解染料废水的最优条件。具体以Ti/SnO₂-Sb 电极作为阳极,应用响应曲面法研究了pH、施加电压值、电极间距对亚甲基蓝溶液脱色效率的影响。研究结果表明模型拟合精度R²=0.9942,初始pH、施加电压值、电极间距及交互作用对脱色率响应值影响大。模型预测最佳反应条件pH为 6.98,施加电压6.0 V,电极间距为1.01 cm时,脱色效率预测值达到98.68%。采用实验进一步验证该模型,预测最佳条件下三次实验脱色率平均值98.47%。该方法可用于优化电催化降解染料废水的工艺参数,为实际废水处理提供优化方案。     

Fe2+取代阳离子交换树脂催化降解亚甲蓝

采用树脂负载亚铁离子的Fenton试剂对亚甲蓝进行降解,用单因素分析方法,对影响亚甲蓝降解效果的主要因素进行逐一研究,以确定最优反应条件.实验结果表明:室温(17.5℃)条件下,pH值为4,Ｈ2O2及亚甲蓝初始浓度为分别为15 mmol/L和2.5mmol/L,Fe负载量为159.13mg/g的催化剂3 g/L.在此条...     

α-SiW11Ni/PANI光催化降解染料废水的研究

以α-SiW11Ni/PANI为催化剂,在紫外灯辐射下,研究了模拟染料废水亚甲基蓝溶液的光催化降解的反应,讨论了催化剂投加量、亚甲基蓝溶液的初始浓度、酸度等对催化脱色效果的影响。实验结果表明,100 mL的亚甲基蓝溶液在紫外灯辐射下最佳的浓度为5 mg/L,催化剂用量为110 mg/L,溶液酸度为pH2;在不改变溶液酸度的情况下,外加氧化剂H2O2能够显著加速亚甲基蓝的催化降解效果。     

Use of a PbO2 electrode of a lead-acid battery for the electrochemical degradation of methylene blue

In this work, the electrochemical degradation efficiency of synthetic azo dye, methylene blue, at positive electrode PbO₂ of lead-acid battery was investigated. The structure and morphology of the electrode was investigated by X-ray diffraction, scanning electron microscopy, and energy dispersive X-ray spectrometry. The influence of several operating parameters on electro-oxidation of 100 mL of methylene blue solution 100 mg/L was studied. Results indicated that lead-acid battery electrode is effective for removing color and chemical oxygen demand (COD). It is found that current density, the stirring speed, and the supporting electrolyte concentration have a positive effect on decolorization and mineralization, and no significant effect of the distance between the electrodes on methylene blue degradation and COD removal was observed. By contrast, the percentage of color and COD removal decreases with increasing of pH. Kinetic analysis of the results revealed that the COD removal follows a pseudo-first-order kinetics.     

N/F/TiO2的制备及光催化氧化性能

以钛酸四丁酯为钛源,以尿素和氟化铵为N、F源,制备N/F/TiO2光催化材料,用于亚甲基蓝降解效率研究.结果表明,摩尔比为N∶F∶Ti=1∶4∶5的光催化剂在锻烧温度为600℃、pH =7的条件下,100 mg N/F/TiO2光催化剂对100 mL浓度为20 mg/L的亚甲基蓝溶液光催化降解4h时效率最高.     

TiO2-HNTs催化剂协同介质阻挡放电等离子体降解亚甲基蓝废水

为进一步提高介质阻挡放电等离子体（DBD）降解亚甲基蓝（MB）的效率,研究了采用介质阻挡放电等离子体和光催化剂协同技术。实验采用溶胶-凝胶法制备TiO₂-HNTs复合光催化材料,并利用XRD、FTIR、TGA方法对催化剂进行表征分析。考察了该材料的光催化性能,以及它与介质阻挡放电的联合降解过程中操作因素的影响,并对反应进行动力学研究。研究结果表明,TiO₂-HNTs复合光催化材料与介质阻挡放电产生协同作用,并能有效地提高MB的去除率,处理60min后,协同体系对MB的降解率为85.37%,MB的降解过程符合表观一级反应动力学方程。MB的去除率与MB的初始浓度,TiO₂-HNTs的投加量、煅烧温度、放电功率和通气量有关。当MB的初始浓度为100mg/L、TiO₂-HNTs的投加量为70mg/L、煅烧温度为300℃、放电功率为200W、通气量为200mL/min时,MB的去除效果较好。     

Fe-5A催化亚甲基蓝溶液湿式H2O2氧化

以九水硝酸铁[Fe(NO3)3?9H2O]和柱状5A分子筛为原料采用湿法浸渍法制备Fe?5A催化剂,催化湿式H2O2氧化亚甲基蓝溶液,考察了间歇反应器中pH值和温度对亚甲基蓝转化率的影响及在连续固定床反应器中床层催化剂装填量、进料液流量、温度和亚甲基蓝入口浓度对亚甲基蓝降解性能的影响. 结果表明,在间歇反应中,在亚甲基蓝浓度50 mg/L、温度70℃、pH为2、反应20 min的条件下,亚甲基蓝的转化率为95.9%. 固定床反应中,随温度降低及进料液流量增加,亚甲基蓝转化率降低;随亚甲基蓝入口浓度增加,亚甲基蓝和化学需氧量(COD)的转化率变化幅度很小. 在温度70℃及pH=2、进料液流量4 mL/min、Fe?5A催化剂装填量1.25 g、亚甲基蓝浓度50?300 mg/L、固定床连续运转5 h的条件下,亚甲基蓝的转化率超过98%,COD转化率大于82%,铁浸出浓度低于3.5 mg/L,相同条件下,装填2.5 g 5A分子筛的固定床中50 mg/L亚甲基蓝的转化率仅为73.3%.     

Electro-catalytic degradation of methylene blue wastewater assisted by Fe2O3-modified kaolin

The electrochemical oxidation of methylene blue (MB) wastewater assisted by Fe₂O₃-modified kaolin in a 200 mL electrolytic batch reactor with graphite plate as electrodes was investigated. The catalyst was characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The effects of pH, current density and introduction of NaCl on the efficiency of the electrochemical degradation process were also studied. It was found that Fe₂O₃-modified kaolin has higher catalytic activity in the electrochemical degradation of MB wastewater. 96.47% chemical oxygen demand (COD) removal was obtained in 40 min of electrochemical treatment of MB wastewater at pH 3, current density was equal to 69.23 mA cm⁻².     

Ag/Bi2 WO6的制备及光催化氧化性能

以Bi（NO3）3·5H2O、 Na2WO4·2H2O、 AgNO3为原料,利用液相沉淀法制备Bi2WO6及Ag掺杂Bi2WO6光催化剂,以亚甲基蓝溶液为目标降解物,对其降解效率进行研究。研究结果表明,当亚甲基蓝溶液的浓度为15 mg/L,体积为50 mL,降解时间3.5 h, Bi2 WO6降解率仅为55%;当Ag/Bi摩尔比为0.4%时, Ag/Bi2 WO6表现出较好的催化性能,相同时间降解率达到97%。