薄壁1Cr18Ni9Ti奥氏体不锈钢的焊接试验

采用钨极氩弧焊的方法,对0.8 mm厚的1Cr18Ni9Ti奥氏体型不锈钢板实施焊接,并通LOM,SEM方法对焊接接头组织及断口形貌进行观察及分析;利用显微硬度计、电子万能拉伸机测量了焊接接头的力学性能.结果表明,通过手工钨极氩弧焊,采用直流正接接法(焊接电流为20 A,焊接速度为20 m/h)能够获得外观平整、组织均匀、力学性能满足要求的焊接接头.     

TA2钛合金熔丝钨极氩弧焊接头的组织性能

采用熔丝钨极氩弧焊方法应用于钛合金焊接领域,对优化工艺参数下的焊接接头进行显微组织分析和力学性能试验。结果表明,熔丝钨极氩弧焊方法可实现5mm厚TA2板材单面焊双面成形,焊接接头内部无焊接缺陷,焊缝区显微组织由粗大的锯齿状晶粒组成使焊缝中心位置冲击功降低,拉伸试验断裂位置为热影响区,其断口为韧性断裂,焊缝中心维氏硬度高于母材,接头具有较好的塑性和韧性。     

有色金属压力容器非熔化极氩弧焊焊接工艺

在碳钢及低合金钢压力容器焊接工艺中,已广泛采用非熔化极(钨极)氩弧焊焊接方法。有色金属与碳钢及低合金钢相比,可焊性较差,焊接难度较大,所以有色金属非熔化极(钨极)氩弧焊焊接工艺还不够成熟。以有色金属(包括铝、铜、镁等及其合金)压力容器焊接为例,通过大量的工程实践证明,从焊接材料、焊接接头型式及尺寸、焊前准备、焊接过程等方面来研究非熔化极氩弧焊焊接工艺,可以使有色金属压力容器焊接接头的焊接质量达到标准要求。     

外加磁场对不锈钢焊接接头组织和性能的影响

为了优化不锈钢焊接工艺,提高焊接质量,减少不锈钢焊接缺陷,在对奥氏体不锈钢进行钨极氩弧焊时外加纵向磁场,焊后对焊接试样进行弯曲和拉伸试验,并采用电子显微镜对焊接接头进行显微组织分析.研究了外加磁场的磁场参数（磁场电流和磁场频率）对不锈钢焊接接头力学性能的影响规律和磁场频率的作用规律.试验结果表明,外加纵向磁场通过电磁搅拌作用改变了晶粒的结晶方向,使晶粒细化;焊接接头的力学性能随磁场的频率变化而变化,在磁场电流为1A、磁场频率为20Hz时,电磁搅拌达到最佳效果,提高了焊接接头的综合力学性能.     

310S耐热不锈钢TIC焊接接头组织与力学性能研究

采用钨极氩弧焊焊接方法,以不同的焊接工艺方案对310S奥氏体耐热不锈钢进行焊接试验.焊接试验完成以后观察焊缝成形的外观质量,采用金相显微镜对焊接接头进行显微组织观察分析,并进行力学性能测试.结果表明:在焊接电流I=140 A、焊接速度V=0.32m/min的焊接工艺方案下,焊缝外观质量优良,焊接接头的组织和性能是最优的.在该焊接工艺方案下,焊缝区的晶粒组织细小均匀,拉伸试验的断裂位置在母材区域,并且焊接接头的抗拉强度为481MPa,能达到母材抗拉强度的91％以上.     

TA2钨极氩弧焊焊接工艺的优化

为了研究TA2钨极氩弧焊的最佳工艺参数,采用自动TIG焊对厚度为5 mm的TA2试板进行了焊接实验.焊后对焊接接头进行了拉伸实验和硬度实验,并对焊接接头的显微组织和拉伸断口进行了观察.结果表明,在焊接电流为170 A、焊接速度为2.0 mm/s的最优参数条件下,焊接接头的抗拉强度为598.3 MPa,断后伸长率为26.7%,断面收缩率为38.5%,焊缝硬度为209 HB,热影响区硬度为182 HB.适宜的焊接工艺参数能够减少焊接接头中马氏体和魏氏组织的产生,并提高焊接接头的强度和塑性.     

彩色电视教学片《手工钨极氩弧焊》上、下集

手工钨极氩弧焊是一种比较新的焊接方法,它焊接质量好,正在逐步用于锅炉、压力容器等重要结构的焊接。 本片介绍了手工钨极氩弧焊的原理、设备、工具及材料,着重介绍了低碳钢、低合金耐热钢和不锈钢板材对接接头、管材对接接头、管板接头以及铝管和铝板的焊接方法、操作要     

5554铝合金异种焊料焊接的显微组织及力学性能

在5554铝合金钨极氩弧焊焊接工艺基础上,利用万能拉伸试验机、光学显微镜和显微硬度测试仪等仪器,比较了5554铝合金异种焊料焊接接头的微观组织结构和力学性能。结果表明,随着焊料含镁量的增加,焊接接头的力学性能都得到了不同程度的降低,而且随着镁含量的增加,焊接热裂纹越明显。三种焊料焊接的接头显微硬度均比母材低,通过试验验证,得出焊后保温是导致这一结果的主要原因。     

磁场对AZ31镁合金焊接接头疲劳性能的影响

为了研究外加磁场对焊接接头疲劳行为的影响规律,在对5 mm厚的AZ31镁合金板进行钨极氩弧焊过程中,外加纵向交流变频磁场.对不同磁场参数下镁合金焊接接头进行应变控制疲劳实验,采用光学金相和扫描电镜对焊接接头的显微组织和疲劳断口进行分析.实验结果表明：当磁场电流为2 A,频率为20 Hz时,焊缝的疲劳性能达到最佳值.合适的外加纵向磁场可以促使电弧旋转对熔池进行搅拌,改变晶粒结晶过程,使焊缝中晶粒组织得到细化,进而使焊缝的疲劳性能得到改善.     

焊接工艺对双相不锈钢焊接接头力学性能和组织的影响

分析了不同焊接方法对A240-S32205双相不锈钢焊接接头的力学性能及金相组织的影响.结果表明：氩弧焊和手工电弧焊均能使焊接接头获得良好的相比例和耐腐蚀性,但氩弧焊焊接接头的耐腐蚀性优于酸性焊条手工焊焊接接头;氩弧焊焊接接头具有良好的综合力学性能,酸性焊条手工焊的低温冲击性能则不很理想;焊接接头的热影响区产生第3相有害金属相的倾向高于焊缝区,是双相钢焊接耐腐蚀性的薄弱区域.     

摆动磁场条件下的焊接接头组织研究

为了优化不锈钢焊接工艺,提高焊接质量,进行了外加电磁场条件下的304不锈钢钨极氩弧焊(TIG),磁场施加方式分别为横向磁场和旋转磁场.焊后采用电子显微镜对焊接接头进行显微组织观察,研究了不同外加磁场类型和不同焊接速度对不锈钢焊接接头组织的作用规律.试验结果表明,外加磁场改变了熔池的流动形态,使金属液由四周向中心流动并伴有搅拌,也使焊缝熔深增大的同时,抑制柱状晶的形成,细化组织.     

不锈钢TIG焊活性剂对焊缝性能的影响

针对TIG焊生产效率低，单层焊可焊厚度小等问题，采用活性化TIG焊（A-TIG），能够大幅度地提高焊缝熔深，从而提高焊接效率和生产率。研究了在不锈钢TIG焊中，5种单一成分的活性剂（SiO2、CaF2、TiO2、Cr2O3和NaF）对焊缝机械性能和微观组织的影响，试验结果表明，同传统的TIG焊相比，在相同规范下，上述5种活性剂都能够大幅度的提高焊缝的熔深，但是不同的活性剂对焊缝机械性能的影响不同，其中活性剂SiO2所形成的焊缝的抗拉强度和塑性最好，而活性剂Cr2O3所得到的焊缝硬度最大；活性剂对焊缝微观组织没有明显改变，仅仅改变了奥氏体和铁素体组织的纹理结构。     

Effect of welding process on the microstructure and properties of dissimilar weld joints between low alloy steel and duplex stainless steel

To obtain high-quality dissimilar weld joints, the processes of metal inert gas (MIG) welding and tungsten inert gas (TIG) welding for duplex stainless steel (DSS) and low alloy steel were compared in this paper. The microstructure and corrosion morphology of dissimilar weld joints were observed by scanning electron microscopy (SEM); the chemical compositions in different zones were detected by en-ergy-dispersive spectroscopy (EDS); the mechanical properties were measured by microhardness test, tensile test, and impact test; the corro-sion behavior was evaluated by polarization curves. Obvious concentration gradients of Ni and Cr exist between the fusion boundary and the type II boundary, where the hardness is much higher. The impact toughness of weld metal by MIG welding is higher than that by TIG weld-ing. The corrosion current density of TIG weld metal is higher than that of MIG weld metal in a 3.5wt% NaCl solution. Galvanic corrosion happens between low alloy steel and weld metal, revealing the weakness of low alloy steel in industrial service. The quality of joints pro-duced by MIG welding is better than that by TIG welding in mechanical performance and corrosion resistance. MIG welding with the filler metal ER2009 is the suitable welding process for dissimilar metals jointing between UNS S31803 duplex stainless steel and low alloy steel in practical application.     

不锈钢汽车排气管激光焊接残余应力

为了提高不锈钢管的冷加工成形性能,进一步优化相应焊接工艺,在对汽车排气管激光焊接温度场进行数值模拟研究的基础上,分析激光焊接汽车排气管残余应力.在考虑网格的疏密过渡以及材料力学性能参数随温度的变化条件下,分析激光焊接不锈钢管残余应力演变过程及分布特点,即滚轮挤压量越小,平均残余应力越小,但容易出现咬边和未焊透,在局部产生应力集中,更容易在焊接管冷加工时出现开裂;激光焊接线能量减小,轴向残余应力区域变窄,峰值应力增加.将激光焊接残余应力与钨极氩弧焊(TIG)+激光焊的残余应力进行对比实验,结果表明,不锈钢管TIG+激光焊残余应力与激光焊接具有相似的分布,分布区域相对变宽,焊轴向残余应力比激光焊接小,提高了焊接管冷加工成型性能.     

0Cr18Ni9不锈钢焊接温度场的数值仿真

基于有限元软件SYSWELD对不锈钢0Cr18Ni9平板TIG焊的温度场进行三维动态模拟,得出了瞬态温度场分布图和特征点的热循环曲线,同时也得出了焊缝上任一点的温度变化与相变的关系.与文献资料比较表明,所建立的数值模拟仿真模型可以较好的模拟焊接温度场,为研究焊接过程中的应力应变和减少焊接应力与变形提供了参考依据.     

12Cr1MoV/304不锈钢焊接接头高温时效碳迁移现象

针对高温环境下异种钢焊接接头在服役过程中出现碳迁移,进而导致脱碳层在服役中失效的问题,采用电弧堆焊方法研究了12Cr1Mo V低合金耐热钢和304不锈钢焊接接头在不同时效时间下的碳迁移问题.研究表明,经高温时效后,焊态区域的组织并未受到影响;在过热粗晶区形成的碳过饱和的上贝氏体和粒状贝氏体组织则发生退化,转变成回火索氏体组织.形成的脱碳层组织以铁素体为主,里面夹杂少量的颗粒状渗碳体,特别是在增碳层出现大量的碳化物,形成类似于马氏体的复杂的不规则组织.经菲克定律推导出的扩散方程计算后,证明碳扩散的理论曲线与实际曲线较为接近,可用于研究碳扩散的迁移机制.     

铝合金与奥氏体不锈钢的火焰钎焊

通过火焰钎焊的方法,实现铝合金（LF6）与奥氏体不锈钢（1Cr18Ni9Ti）的焊接．首先在不锈钢的表面热浸镀一层ZL102铝合金,然后采用搭接的形式对热浸镀层和铝合金进行焊接,并分析了焊接接头的微观组织和拉伸性能．试验结果表明,采用火焰钎焊的方法能够获得优质的焊接接头,但热浸镀层的结合强度低于母材、钎缝的强度．     

多弧离子镀TiN涂层工艺及耐蚀性研究

为提高4Cr13马氏体不锈钢的耐蚀性,对其进行多弧离子镀处理,获得TiN涂层,并用X射线衍射仪、显微硬度计、扫描电子显微镜、电化学测量仪对涂层进行物相分析、表面形貌观察、硬度检测以及电化学腐蚀性能测试.结果表明:随着电流的增大,表面的液滴数目和尺寸增大,涂层厚度增加,薄膜硬度也增大;相结构主要为TiN,有明显的择优取向,且随着弧电流的增强,衍射峰强度略有增加.TiN试样在3.5％的NaCl溶液中耐蚀性与基体相当,在1 mol/L的H2SO4溶液中的耐蚀性比基体提高了800倍.