楔横轧多楔轧制光轴表面光滑程度规律研究

楔横轧多楔成形光轴类零件时,内外楔之间轧件的过渡段形状为由外楔楔入段轧制而成的斜台阶,通过有限元模拟和轧制实验,对不同过渡角下多楔轧制光轴表面光滑程度进行分析,得到过渡角对楔横轧多楔轧制光轴表面光滑程度影响规律。研究结果为楔横轧多楔精密成形长轴类零件提供了理论指导。     

横轧非回转体轴类件辊型曲线方程

楔横轧非回转体轴类零件是楔横轧近净成形和精确成形的突破性和创新性发展,而轧辊的辊型则是非回转体轴类零件楔横轧成形的基础和关键.在分析楔横轧非回转体轴类件成形工艺原理的基础上,提出“单阶段”楔横轧非回转体轴类零件新工艺;根据轧制过程中轧件与轧辊的相对共轭运动关系推导出楔横轧非回转体轴类件的辊型曲线方程;针对一典型非回转体轴类零件在试验轧机上进行轧制试验.试验结果表明,“单阶段”楔横轧生产的非回转体轴类件主要尺寸精度达到要求,且内部无明显缺陷,这说明“单阶段”楔横轧非回转体轴类件新工艺是完全可行的,且利用辊型曲线方程加工的辊型可以轧制出符合尺寸要求的非回转体轴类件,因而是实现非回转体类零件少无切削加工,改善劳动条件、节材降耗的优质工艺方法.     

楔横轧轧件滚动半径变化规律的试验研究

楔横轧轧制成形过程中轧件的滚动半径是楔横轧模具设计和进行工艺分析的基本参数之一,它反映了轧辊与轧件的相对运动关系,对非圆截面轴类零件如发动机凸轮轴等模具辊形曲线设计具有重要影响.通过轧制试验,得到楔横轧轧制过程中轧件滚动半径的变化规律和各种工艺参数的影响规律.结果表明:楔入段轧件滚动半径要大于原始坯料尺寸且随着轧制进行逐渐减小;到展宽段保持稳定;进入轧齐后,随着模具楔面抬高,其值逐渐减小,精整段约等于轧件轧后尺寸.展宽角和成形角越大,轧件滚动半径越大;断面收缩率影响规律比较复杂,当断面收缩率小于一定值时,随断面收缩率增大而增大,当断面收缩率大于一定值时,随断面收缩率增大而减小;坯料直径表现为辊径比越大,轧件滚动半径越靠近原始坯料尺寸内侧;轧制温度对轧件滚动半径的影响较小,而模具楔面刻痕状态影响较大.     

楔横轧多楔成形汽车半轴工艺可行性分析

分析多楔成形长轴类零件时内/外楔对接段的各种形状及其优缺点,建立了楔横轧多楔成形汽车半轴的三维有限元模型.通过选取合理的轧制工艺,模拟楔横轧多楔轧制汽车半轴的过程,获得了内/外楔之间过渡光滑的汽车半轴.结果表明:楔横轧多楔成形汽车半轴工艺是可行的,该研究为多楔成形半轴的模具设计提供了理论依据.     

楔横轧多楔轧制铁路车轴可行性有限元分析

采用DEFORM有限元软件，建立楔横轧多楔轧制铁路RD2车轴有限元模型，进行多楔轧制过程有限元仿真，通过分析三楔同时楔入成形RD2轴的金属流动规律、轧件内部应力状态情况等，进一步阐明楔横轧多楔轧制铁路车轴的可行性。有限元分析结果为实现铁路车轴高效化、节能化、专业化生产提供了理论依据。     

轧辊直径对楔横轧大型轴类件应力应变影响分析

合理选择轧辊直径是楔横轧成形大型轴类件的重要技术指标,采用ANSYS/LS-DYNA有限元分析软件,对楔横轧轧制大型轴类件进行模拟,分析轧辊直径对楔横轧大型轴类件应力应变影响规律,阐明轧辊直径对于楔横轧大型轴类件轧件质量的影响程度,研究结果为实现大型轴类件楔横轧经济化生产提供理论依据.     

楔横轧二次楔轧制大断面收缩率的应力应变场分析

利用有限元软件DEFORM-3D,基于三雏刚塑性的有限元理论,对大断面收缩率轴类零件成形过程成功地进行了楔横轧二次楔轧制成形的数值模拟,模拟所得的轧件形状与实际零件基本相同,给出了楔横轧二次楔轧制过程的应力应变分布等重要信息。模拟结果表明：二次楔轧制大断面收缩率轴类零件的心部发生了很大变形;二次楔轧制中间横截面受的横拉应力时间较长、值较大,所以轧件中心更容易产生内部缺陷。     

工艺参数对多楔轧件接口质量的影响规律

楔横轧多楔成形工艺是生产长轴类零件的先进方法,但生产过程中模具工艺参数对轧件接口质量的影响比较复杂。根据楔横轧多楔模具的工艺特点,建立多楔轧制长轴类零件的三维有限元模型。基于ANSYS/LS-DYNA有限元模拟软件,在不同模具工艺参数下对多楔轧制过程进行了有限元模拟,得到模具工艺参数对轧件接口质量的影响规律。在与模拟工艺参数相同的条件下进行轧制试验,试验结果和模拟结果一致。通过对理论模拟和轧制试验获得结果的分析,得到工艺参数中过渡角对轧件的接口质量影响最大、展宽角对轧件接口质量影响最小的结论。综合考虑各工艺参数的影响,给出保证轧件接口质量良好的过渡角选择范围。研究结果为多楔成形长轴类零件的模具设计提供理论依据和参考。     

工艺参数对楔横轧接触区表面应力的影响分析

为深入探明楔横轧接触区变形规律，实现零件楔横轧近终成形，采用有限元数值方法模拟楔横轧轧制过程，获得稳定轧制过程中的接触区的面力和位移，进而求出轧制接触区表面应力。在此基础上，较详细地分析了展宽角、成形角和断面收缩率三个主要工艺参数对接触区表面应力的影响规律，并对所建立的有限元计算模型进行了实验验证。研究结果对合理选择楔横轧工艺参数以及实现零件的精确成形具有重要的现实意义和应用价值。     

楔横轧在汽车等轴类零件上的应用与发展

一、楔横轧技术简况1.楔横轧技术的简要历程20世纪50年代,由原捷克国发明了楔横轧轴类零件成形工艺并首先应用于汽车、五金工具等零件的生产,其技术与设备出口英国、美国等国家,成为国际上公认的轴类零件成形新技术,由于技术复杂等原因,至今只为少数国家全面掌握。     

Analysis and experimental studies of internal voids in multi-wedge cross wedge rolling stepped shaft

In this study, a rigid-plastic finite element method (FEM) simulation model for a multi-wedge cross wedge rolling (MCWR) was developed to analyze the generation mechanisms of internal defects. Two feature parts in MCWR, rod area and store area, were defined to analyze the internal defects mechanisms. The difference of stress states between the rod and store areas was pointed out and an insight into generation mechanism was concluded. Based on simulation, the influence of mold parameters was discussed and an optimized parameter group was achieved. The results indicate that the internal voids in the store and rod areas were extended from microcracks produced by shear stress cycle, and then develop to cracks due to the overlarge first principle tension stress caused by metal backflow. In a certain range, a smaller forming angle and a reasonable area reduction is good for avoid center voids in store area. Subsequently, the industrial test manifested the feasibility of study results.     

固—液态塑性加工技术的新进展

固－液态塑性加工是一种具有省力，节能节材，能一次成形为接近成品形状的制做高质量制件的塑性加工新技术，它目前正越来越多地受到重视，介绍近年来有关该技术的研究，开发与应用方面的新进展。     

超薄塑件注塑成形特性的试验研究与数值模拟

薄壁注塑成形技术具有节约材料、降低成本、减少制品重量和外形尺寸等优点,可促进移动电话等电子产品的迅速发展,特别是超薄塑件的注塑成形技术在微机电领域具有巨大的应用潜力。但随着制品厚度的减小也使注射成形难度加大,填充过程更为复杂,成形特性有待探索。设计制造出可成形超薄塑件的模具,利用正交试验方法(田口方法)进行充模试验和数值模拟技术研究各工艺参数(注射速度、注射压力、熔体温度、注射量和制品厚度等)对超薄塑件注塑成形充模过程的影响。研究结果表明,制品厚度对超薄塑件的填充起决定性作用;注射量及注射速度对超薄塑件注塑成形的填充起主导作用,提高注射速度能大幅度地提高填充率;熔体温度和注射压力相对于注射量和注射速度只起次要作用,但在填充过程中,高的熔体温度和注射压力也是必要的。     

基于铸辗复合成形的42CrMo钢环坯铸造工艺与试验研究

针对目前环形零件生产工艺流程长,加热次数多,浪费材料和能源等问题,提出和研究环形零件短流程铸辗复合成形新工艺。该工艺采用铸造环坯直接辗扩成形,具有节能、节材和缩短工艺流程等优点。在这种新工艺中,环坯的铸造质量、组织和力学性能对后续的辗扩工艺和环形零件组织、性能具有重要的影响。以轴承环件常用的42CrMo钢为研究对象,通过理论分析和模拟研究,提出高质量环形铸坯铸造工艺;并进行实际工业试验。通过试验研究和性能测试,表明该铸造工艺生产的环形铸坯具有良好的质量、组织和力学性能,可以为轴承环件铸辗复合成形提供高质量的铸坯。     

中国特色的再制造零件质量保证技术体系现状及展望

再制造在实现资源能源节约的条件下生产出经济发展所需要的产品,是建设资源节约型、环境友好型社会的有效途径针对中国特色的再制造模式,结合再制造产品及其生产环节,分析影响再制造零件质量的主要因素,指出为保证再制造零件质量应把控的几个环节,即再制造毛坯质量评价、再制造生产过程监测、再制造零件/涂层质量检验,并提出再制造零件质量保证技术体系,介绍我国近几年在再制造标准方面的主要成绩,并指出为适应我国再制造产业快速发展需要,急需加强再制造成形技术方法和再制造质量检测评价方法等方法标准的研究。阐述再制造毛坯和再制造涂层质量无损监/检测评价方法,并结合车辆发动机典型零件再制造实践,介绍无损检测评价技术在再制造质量保证中的应用。展望中国特色再制造零件质量保证技术的未来发展。     

浅谈B柱热成型在车辆节能方面的设计应用

介绍了热成型技术在白车身的应用,阐述B柱热成型对车身减重的效果,进而达到节能减排的作用;同时介绍了热成型零件的优点、热成型技术的加工工艺及热成型B柱车型在侧面碰撞试验中的作用.     

基于CATIA V5的零组件快速装配设计技术研究

研究了零组件快速装配设计的实现途径。提出了"批装配"的概念,解决了"批装配"实现过程中装配特征的定义、零件实例化、实时预览等关键技术。实现了螺栓连接、螺钉连接、销连接等零组件的快速装配设计,大大减轻了设计人员装配设计的工作,提高了装配设计的效率。该研究对于快速智能装配设计、基于实例的设计、家族化设计等有着一定的参考价值。     

圆锥形零件成形时极限承载能力的确定

根据圆锥形零件成形时破裂危险断面处的应力状态，并综合考虑几何尺寸、各向异性、材料硬化等因素的影响，经力学分析得出了圆锥形零件成形时危险断面处的承载能力，以此可作为判断成形过程能否顺利成形，确定极限变形程度的依据。