150 mm超厚水电站用钢07MnCrMoVR的组织性能

对150 mm超厚07MnCrMoVR水电钢的组织性能进行了研究,采用光学显微镜、扫描电子显微镜对试验钢的微观形貌进行了观察,采用拉伸试验机和低温冲击韧性试验机对试验钢力学性能进行了检验。结果表明:试验钢经第一次完全淬火和第二次两相区亚温临界淬火后近表面组织转变为板条马氏体和未熔铁素体相间出现,厚度1/4处和厚度1/2处组织转变为贝氏体+铁素体组织,高温回火后近表面转变为回火索氏体组织,厚度1/4处和厚度1/2处组织转变为回火贝氏体+铁素体+大量碳化物。     

150mm超厚水电站用钢07MnCrMoVR的组织性能

摘要：对150mm超厚07MnCrMoVR水电钢的组织性能进行了研究，采用光学显微镜、扫描电子显微镜对试验钢的微观形貌进行了观察，采用拉伸试验机和低温冲击韧性试验机对试验钢力学性能进行了检验。结果表明：试验钢经第一次完全淬火和第二次两相区亚温临界淬火后近表面组织转变为板条马氏体和未熔铁素体相间出现，厚度1/4处和厚度1/2处组织转变为贝氏体+铁素体组织，高温回火后近表面转变为回火索氏体组织，厚度1/4处和厚度1/2处组织转变为回火贝氏体+铁素体+大量碳化物。     

HTP技术在高强度特厚板生产中的应用

 借助于热模拟、数值模拟的方法,采用添加铌、锰、铬、硼,不含钼的低成本合金设计,通过2种铌质量分数（0.09%和0.05%）钢种的对比,探讨了HTP工艺技术在厚度小于等于100mm、屈服强度大于等于600MPa级别高强度钢中的应用。试验结果表明：采用HTP+回火工艺,可提高钢板的未再结晶温度;改善钢板厚度方向均匀性和钢板的心部冲击韧性,钢板表面和厚度1/4处的组织多为板条贝氏体组织,芯部组织为粒状贝氏体+黑色的珠状组织。     

低碳贝氏体钢的回火转变及内耗研究

针对低碳贝氏体钢,采用扫描电镜(SEM)、透射电镜(TEM)、X射线衍射和内耗手段分析了600℃回火过程中的显微组织变化,测试了回火后的屈服强度。结果表明,试验钢轧制态的显微组织是板条贝氏体与粒状贝氏体的混合组织,有少量Mo_2C和NbC析出。随着回火时间延长,贝氏体板条的宽度不断增大,板条内部形成较多不同取向的胞状结构,有些板条逐步演化为多边形状,粒状贝氏体不断吞噬板条贝氏体,使显微组织中粒状贝氏体增多且粗化;Mo_2C和NbC析出物进一步增多,贝氏体铁素体中的位错密度不断降低;内耗-温度谱中Snoek峰值不断降低,表面处的SKK峰值先降低后升高,心部的SKK峰值先降低后变化不大;屈服强度呈现先提高后降低的趋势。     

高强度钢韧化机制及与亚结构关系的研究

摘要：以实际生产制备的800MPa级调质态水电钢为研究对象,结合扫描电子显微镜（SEM）、电子背散射衍射（EBSD）和冲击实验等,利用显微组织晶体学结构可视化与定量化方法,研究了钢板厚度方向不同取样位置低温韧性差异的本质原因。结果表明,高强度中厚板厚度方向由表面向心部过渡,显微组织由板条状贝氏体向粒状贝氏体过渡,低温冲击韧性降低,韧脆转变温度（DBTT）升高。随显微组织由表面向心部过渡（冷速降低）,变体选择加强,心部形成了以单一贝恩（Bain）组为主导的相变组织,大角度晶界密度显著降低,且韧脆转变温度的升高与block界面密度降低紧密相关。此外,研究发现奥氏体晶粒内部的block界面和奥氏体晶界可以有效地偏折和阻止裂纹扩展,但由于奥氏体界面密度显著低于block界面,故对冲击实验过程中裂纹扩展阻力的贡献主要来自晶内的block界面。     

X80级高强低合金管线钢组织与冲击韧性

 为了研究准多边形铁素体/板条贝氏体/粒状贝氏体显微组织的高强低合金X80管线钢的低温韧性与冲击裂纹扩展特点，用OM、SEM、EBSD和TEM等多尺度手段进行了表征。结果表明，与针状铁素体/粒状贝氏体相比，在－60 ℃以上时，准多边形铁素体/板条贝氏体/粒状贝氏体表现出更好的阻止裂纹扩展的能力，准多边形铁素体可以分割显微组织并细化有效晶粒尺寸，增加大角度晶界比例，协调约束冲击裂纹扩展，进而提高韧性；当温度在－60 ℃以下时，这种准多边形铁素体/板条贝氏体/粒状贝氏体对裂纹扩展的协调约束作用减弱，成为显微组织的“软区”，使得材料韧性下降。     

厚规格35CrMo预硬型模具钢板的回火组织与硬度研究

通过扫描电镜的分析手段,研究了莱钢生产35CrMo预硬型模具钢板厚度方向显微组织对硬度分布的影响。结果表明:80mm厚度钢板经过900℃淬火和550~560℃回火后,钢板近表面硬度为HRC32~36,心部硬度超过HRC28,厚度方向硬度波动控制在HRC5以内;120mm厚度钢板经过920℃淬火和570℃回火后,钢板近表面硬度为HRC32~34,心部硬度下降到HRC28~30。回火态钢板表面硬度下降幅度大于心部硬度的下降幅度,钢板近表面处组织中的回火马氏体呈板条状,原始奥氏体被晶界不同取向的板条马氏体分割细化,组织中碳化物呈短棒状,数量相对较少;板厚1/2处组织为回火贝氏体和数量较多的碳化物。随着钢板厚度增加和回火温度升高,显微组织中回火马氏体体积分数逐渐减少,回火贝氏体体积分数逐渐增多,组织中的碳化物析出量逐渐增加,聚集长大趋势明显。     

高强度钢15MnMoVNRE焊接组织的研究——15MnMoVNRE钢研究之四

用光学金相及电子金相法研完了70公斤级高强度钢15MnMoVNRE的焊接组织。熔合区主要为粒状贝氏体组织,热影响区为板条马氏体、板条马氏体 粒状贝氏体,粒状贝氏体组织,基体为回火索氏体。在V型坡口焊接试样中,离熔合线约1.5—1.8毫米处,出现微区片状组织,使冲击韧性下降。     

热处理工艺对EH690级特厚钢板心部组织及性能的影响

针对不同热处理工艺对EH690级特厚钢板心部组织和性能的影响展开研究,结果表明：经过在线淬火+回火处理,钢板心部的强度能够满足性能要求,但冲击韧性极差,显微组织为粗大粒状贝氏体和珠光体的混合组织;一次淬火+回火处理后,强度下降明显,冲击性能有所改善,但是不能满足-40℃低温冲击吸收功≥69 J的要求,存在混晶,组织为粒状贝氏体+少量马氏体;二次淬火+回火处理后,强度整体偏高,冲击功均值满足标准要求,强韧性匹配程度一般,晶粒细化明显,马氏体含量占比增多。通过调整回火温度,最终获得晶粒细小均匀、以高密度位错回火索氏体为主的组织,钢板心部强韧性匹配较好。     

显微组织对X80管线钢力学性能的影响

利用光学显微镜研究了20 mm厚度X80管线钢显微组织类型对强韧性的影响。结果表明:显微组织为针状铁素体和少量的粒状贝氏体时,钢的屈服强度达到512MPa;针状铁素体的晶粒细化、粒状贝氏体和板条贝氏体可以使X80管线钢具有更高的屈服强度,达到600MPa。细小而均匀的粒状贝氏体可以获得良好的冲击韧性。掺杂在一起的细小的针状铁素体、准多边形铁素体、粒状贝氏体促使裂纹扩展路径曲折,改善冲击韧性。     

Effect of center microstructure on fracture mechanism of ultra-thick high strength steel

In order to study the relationship between microstructure and fracture mechanism of ultra-thick steel plate, scanning electron microscopy (SEM), transmission electron microscopy (TEM) and electron backscatter diffraction (EBSD) were used to characterize and analyze the microstructure and crack morphology of 1/4 and 1/2 thickness (center) of the test plate. The results show that the low temperature impact toughness at the center is significantly lower than that at the 1/4 thickness, which is due to the microstructure of the center is tempered lath bainite and tempered granular bainite, and the proportion of granular bainite is higher. The presence of M-A island in granular bainite promotes the initiation of micro pores or micro cracks. The 1/4 thickness is a mixed microstructure of tempered lath martensite and tempered lath bainite. The dislocation movement between laths releases local stress concentration, and relieves the stress at the crack tip region, resulting in crack passivation, hindering crack propagation and improving low temperature impact toughness.     

Impact Toughness of an NM400 Wear-Resistant Steel

An NM400 wear-resistant steel was hot rolled and then the plates were heat-treated by direct quenching and tempering (DQT) and reheat quenching and tempering (RQT) techniques, respectively. The Charpy impact test was carried out with an instrumented Charpy impact tester. The microstructure and fracture surface were investigated by a combination of optical microscopy, transmission electron microscopy and scanning electron microscopy methods. It was found that the impact toughness of DQT specimen was much higher than that of RQT specimen. The microstructure of both DQT and RQT specimens was characterized by a mixture of tempered lath martensite and lower bainite. The lower bainite in DQT specimen extended into prior austenite grains and the content was higher than that in RQT specimen. The lower bainite in DQT specimen improved the impact toughness by increasing the proportion of large-angle boundaries and relieving the stress concentration at the crack tip. A number of fine and dispersed carbides in DQT specimen also contributed to the improvement of the impact toughness.     

Q690q耐候桥梁钢免预热焊接热影响区的组织性能

针对Q690q耐候桥梁钢,利用MMS-300热模拟试验机进行焊接热循环过程模拟试验,研究了10.5～114.9 kJ/cm热输入下粗晶热影响区(CGHAZ)、细晶热影响区(FGHAZ)和不完全相变热影响区(ICHAZ)的微观组织以及冲击韧性、硬度的变化情况,并观察了冲击断口形貌,然后采用优选的焊接热输入,进行了免预热的药芯焊丝熔化极气体保护焊(FCAW)和埋弧焊(SAW)的焊接工艺评定试验。结果表明,热输入较低时,CGHAZ和FGHAZ主要生成板条马氏体组织、ICHAZ出现岛状的M/A组元,其冲击韧性低、硬度高;热输入较高时,CGHAZ主要生成大尺寸的粒状贝氏体、准上贝氏体或上贝氏体组织,同时大尺寸的块状M/A组元数量不断增加、尺寸变大,其冲击韧性显著降低。FGHAZ生成较多多边形或准多边形铁素体、珠光体等高温转变组织,其硬度降低明显。ICHAZ除生成准多边形铁素体、无碳化物贝氏体和退化珠光体外,回火索氏体基体组织中的碳化物颗粒尺寸不断变大,其强韧性不断降低;热输入为18.2～25.7 kJ/cm时,CGHAZ以板条束细小且异向的板条贝氏体为主、FGHAZ形成细小均匀的板条贝氏体和粒状...     

热轧态与回火态 AH80 DB 低碳贝氏体钢组织与冲击韧性

采用光学显微镜、扫描电子显微镜和透射电子显微镜对热轧态和回火态AH80DB低碳贝氏体钢的显微组织、马氏体/奥氏体（M/A）岛、第二相的析出行为以及晶界取向差、有效晶粒尺寸进行研究,揭示回火后低碳贝氏体钢冲击韧性得到改善的原因.结果表明:两种试样的组织均由板条状贝氏体、粒状贝氏体和针状铁素体组成,其中回火态试样中针状铁素体组织较多.热轧态钢中存在较大尺寸M/A岛且呈方向性分布,大角度晶界比例占17.33%,有效晶粒尺寸为3.57μm;而回火态钢中M/A岛的尺寸较小,大角度晶界比例增加3.43%,有效晶粒尺寸减小0.56μm.热轧态钢中析出相主要是（Nb,Ti）C,尺寸在50~150 nm之间,回火态试样中析出较多细小的球状（Nb,Ti）C析出相,尺寸在10 nm左右.      

含Cu的Mn-Nb-B系超低碳贝氏体钢的强韧化机理

对一种含铜超低碳Mn-Nb-B系微合金钢进行TMCP工艺,得到屈服强度达850 MPa的超低碳贝氏体钢。采用光学显微镜和扫描电子显微镜对试验钢不同板厚处的组织进行观察与分析,通过透射电子显微镜分析试验钢板条贝氏体间析出物,结果表明,屈服强度850 MPa超低碳贝氏体钢组织主要为细小的板条贝氏体,沿板厚方向上贝氏体板条宽度变化不大,板条长度从表层到心部逐渐增大。贝氏体板条的细化和微细析出物的形态、大小及分布对试验钢的强韧性起决定作用。     

高铌X80管线钢焊接粗晶区组织和性能研究

采用焊接热模拟技术对高铌X80管线钢进行了热模拟试验,研究了在不同焊接热模拟工艺下贝氏体组织的转变及冲击韧性的变化.结果表明:在不同的焊接热循环条件下,焊接粗晶区组织主要是板条贝氏体和粒状贝氏体.冷却时间t8/5为10 s时,适量的粒状贝氏体起到了分割板条贝氏体的作用,且MA岛的数量较少,呈粒状均匀分布于奥氏体内,使得...     

热处理工艺对100mm特厚07MnCrMoVR水电钢板组织性能的影响

对07MnCrMoR水电钢板的淬透性曲线进行了测定,利用淬火机和热处理炉对100 mm厚试验钢板进行了淬火和回火试验,并对试验钢进行了组织观察和力学性能测定。结果表明,随着试验钢距水冷端的距离增大,淬火组织由马氏体转变为粒状贝氏体,距离端部50 mm处转变为铁素体和粒状贝氏体的混合组织。试验钢板利用淬火机淬火后得到板条贝氏体+粒状贝氏体+先共析铁素体,回火后转变为铁素体+粒状贝氏体,同时大量的碳化物在铁素体基体和晶界处析出。试验钢最合理的热处理工艺为930℃ 30min水冷淬火,660℃ 60min空冷回火。     

New Duplex Microstructure of Grain Boundary Allotriomorphic Ferrite/Granular Bainite

ｈｅｍｏｓｔｐｏｐｕｌａｒｍｉｃｒｏｓｔｒｕｃｔｕｒｅｉｎｃｕｒｒｅｎｔｓｔｒｕｃｔｕｒａｌｓｔｅｅｌｓｉｓｓｔｉｌｌａｍｉｘｔｕｒｅｏｆｆｅｒｒｉｔｅａｎｄｐｅａｒｌｉｔｅ .Ｍｉｃｒｏａｌｌｏｙｉｎｇ (ａｎｄｔｈｅａｓｓｏｃｉａｔｅｄｔｈｅｒｍｏ ｍｅｃｈａｎｉｃａｌｐｒｏｃｅｓｓ)ａｎｄｓｅｃｏｎｄ ｐｈａｓｅｓｔｒｅｎｇｔｈｅｎｉｎｇａｒｅｕｓｕａｌｌｙａｐｐｌｉｅｄｔｏｏｂｔａｉｎｈｉｇｈｓｔｒｅｎｇｔｈａｎｄｔｏｕｇｈｎｅｓｓ.Ｓｉｎｃｅｔｈｅｓｔｒｕｃｔｕｒｅｓｔｒｅｎｇｔｈｏｆｇｒａｎ…