Characterization of sol-gel synthesised lead-free (1 − x)Na0.5Bi0.5TiO3-xBaTiO3-based ceramics

The crystal structure, microstructure, dielectric and ferroelectric properties of (1 − x)Na_0.5Bi_0.5TiO₃-xBaTiO₃ ceramics with x = 0, 0.03, 0.05, 0.07 and 0.1 are investigated. A structural variation according to the system composition was investigated by X-ray diffraction (XRD) analyses. The results revealed that the synthesis temperature for pure perovskite phase powder prepared by the present sol-gel process is much lower (800 °C), and a rhombohedral-tetragonal morphotropic phase boundary (MPB) is found for x = 0.07 composition which showing the highest remanent polarization value and the smallest coercive field. The optimum dielectric and piezoelectric properties were found with the 0.93Na_0.5Bi_0.5TiO₃-0.07BaTiO₃ composition. The piezoelectric constant d₃₃ is 120 pC/N and good polarization behaviour was observed with remanent polarization (P_r) of 12.18 pC/cm², coercive field (E_c) of 2.11 kV/mm, and enhanced dielectric properties ?_r > 1500 at room temperature. The 0.93Na_0.5Bi_0.5TiO₃-0.07BaTiO₃-based ceramic is a promising lead-free piezoelectric candidate for applications in different devices.     

Microstructure, ferroelectric, and piezoelectric properties of (1 − x − y)Bi0.5Na0.5TiO3-xBaTiO3-yBi0.5Ag0.5TiO3 lead-free ceramics

Lead-free (1 − x − y)Bi_0.5Na_0.5TiO₃-xBaTiO₃-yBi_0.5Ag_0.5TiO₃ (BNT-BT-BAT-x/y, x = 0-0.10, y = 0-0.075) piezoelectric ceramics were synthesized by conventional oxide-mixed method. The microstructure, ferroelectric, and piezoelectric properties of the ceramics were investigated. Results show that a morphotropic phase boundary (MPB) between rhombohedral and tetragonal phases of BNT-BT-BAT-x/0.04 ceramics is formed at x = 0.06-0.08. The addition of BAT has no obvious change on the crystal structure of BNT-BT ceramics while it causes the grain size of the ceramics to become more homogenous. Near the MPB, the ceramics with x = 0.06 and y = 0.05-0.06 possess optimum electrical properties: P_r ∼ 42.5 μC/cm², E_c ∼ 32.0 kV/cm, d₃₃ ∼ 172 pC/N, k_p ∼ 32.6%, and k_t ∼ 52.6%. The temperature dependences of k_p and polarization versus electric hysteresis loops reveal that the depolarization temperature (T_d) of BNT-BT-BAT-0.06/y ceramics decreases with increasing y. In addition, the polar and non-polar phases may coexist in the BNT-BT-BAT-x/y ceramics above T_d.     

Synthesis of (Bi0.5Na0.5)TiO3 (BNT) and Pr doped BNT using the soft combustion technique and its properties

In this work, bismuth sodium titanate (Bi_0.5Na_0.5)TiO₃ (BNT) and praseodymium (Pr)-doped BNT were successfully produced using the soft combustion technique. The effects of Pr doping on stoichiometry, microstructure, density and dielectric properties were studied. Pure Pr-doped BNT was obtained in all samples containing 5, 10 and 20 mol% Pr after calcination at 800 °C for 3 h. The produced powders were then pressed into pellets and sintered at 1100 °C for 3 h. The very similar ionic radii of Pr³⁺ with Bi³⁺ and Na⁺ made it possible to substitute both Bi and Na. The crystallite size and grain size decreased with increasing Pr amount because Pr acted as grain growth inhibitor, both for calcined powders and for sintered pellets. Maximum density was obtained in 5 mol% Pr-doped BNT, beyond which density decreased. The maximum dielectric constant of 756 was obtained in 5 mol% Pr-doped BNT and decreased at higher levels of Pr doping. Pr doped into BNT also caused a decrease in dielectric loss.     

The temperature-dependent electrical properties of Bi0.5Na0.5TiO3-BaTiO3-Bi0.5K0.5TiO3 near the morphotropic phase boundary

Bi_0.5Na_0.5TiO₃-BaTiO₃-Bi_0.5K_0.5TiO₃ (BNT-BT-BKT) lead-free piezoceramics with compositions near the rhombohedral-tetragonal morphotropic phase boundary (MPB) were prepared and investigated. At room temperature, all ceramics show excellent electrical properties. In this study, the best properties were observed in 0.884BNT-0.036BT-0.08BKT, with the remnant polarization, bipolar total strain, unipolar strain, piezoelectric constant, and planar electromechanical coupling factor being 34.4 μC cm⁻², 0.25%, 0.15%, 122 pC N⁻¹, and 0.30, respectively. Detailed analysis of the temperature dependence of polarization-electric field (P-E) loops and bipolar/unipolar strain-electric field (S-E) curves of this composition revealed a ferroelectric-antiferroelectric phase transition around 100 °C. Around this temperature, there is a significant shape change in both P-E and S-E curves, accompanied by enhanced strain and decreased polarization; the largest recoverable strain reaches 0.42%. These results can be explained by the formation of antiferroelectric order and the contribution of field-induced antiferroelectric-ferroelectric phase transition to piezoelectric response. Our results indicate that BNT-BT-BKT lead-free piezoceramics can have excellent electrical properties in compositions near the MPB and also reveal some insight into the temperature dependence of the electrical performance with the MPB composition.     

Piezoelectric and dielectric properties of Dy2O3-doped (Bi0.5Na0.5)0.94Ba0.06TiO3 lead-free ceramics

(Bi_0.5Na_0.5)_0.94Ba_0.06TiO₃ + x wt% Dy₂O₃ with x = 0-0.3 ceramics were synthesized by conventional solid-state processes. The effects of Dy₂O₃ on the microstructure, the piezoelectric and dielectric properties were investigated. X-ray diffraction pattern confirmed that the coexistence of tetragonal and rhombohedral phases in the (Bi_0.5Na_0.5)_0.94Ba_0.06TiO₃ composition was not changed by adding 0.05-0.3 wt% Dy₂O₃. SEM images indicate that all the ceramics have pore-free microstructures with high density, and that doping of Dy₂O₃ inhibits the grain growth of the ceramics. The addition of Dy₂O₃ shows the double effects on decreasing the piezoelectric and dielectric properties for 0 < x < 0.15 when Dy³⁺ ions substitute B-site Ti⁴⁺ ions, and increasing the properties for 0.15 < x < 0.3 when Dy³⁺ ions enters into A-site of the perovskite structure. The optimum electric properties of piezoelectric constant d₃₃ = 170 pC/N and the dielectric constant ?_r = 1900 (at a frequency of 1 kHz) are obtained at x = 0.3.     

Phase structure and electrical properties of (0.8 − x) BaTiO3-0.2Bi0.5Na0.5TiO3-xBaZrO3 lead-free piezoceramics

Lead-free piezoelectric ceramics (0.8 − x)BaTiO₃-0.2Bi_0.5Na_0.5TiO₃-xBaZrO₃ (BT-BNT-xBZ, 0 ≤ x ≤ 0.08) doped with 0.3 wt% Li₂CO₃ were prepared by conventional solid-state reaction method. With the Li₂CO₃ doping, all the ceramics can be well sintered at 1170-1210 °C. The phase structure, dielectric, ferroelectric and piezoelectric properties of the ceramics were investigated. Results show that a morphotropic phase boundary (MPB) between tetragonal and pseudocubic phases exists at x = 0.03-0.04. The addition of Zr can improve the piezoelectric properties of BT-BNT ceramics. Furthermore, a relaxor behavior is induced and the tetragonal-cubic phase transition shifts towards lower temperatures after the addition of Zr. The ceramics with x = 0.03 possess the optimum electrical properties: d₃₃ = 72 pC/N, k_p = 15.4%, ?_r = 661, P_r = 18.5 μC/cm², E_c = 34.1 kV/cm, T_c = 150 °C.     

Preparation and electrical properties of Bi0.5Na0.5TiO3-BaTiO3-KNbO3 lead-free piezoelectric ceramics

Lead-free (1 − x)Bi_0.47Na_0.47Ba_0.06TiO₃-xKNbO₃ (BNBT-xKN, x = 0-0.08) ceramics were prepared by ordinary ceramic sintering technique. The piezoelectric, dielectric and ferroelectric properties of the ceramics are investigated and discussed. The results of X-ray diffraction (XRD) indicate that KNbO₃ (KN) has diffused into Bi_0.47Na_0.47Ba_0.06TiO₃ (BNBT) lattices to form a solid solution with a pure perovskite structure. Moderate additive of KN (x ≤ 0.02) in BNBT-xKN ceramics enhance their piezoelectric and ferroelectric properties. Three dielectric anomaly peaks are observed in BNBT-0.00KN, BNBT-0.01KN and BNBT-0.02KN ceramics. With the increment of KN in BNBT-xKN ceramics, the dielectric anomaly peaks shift to lower temperature. BNBT-0.01KN ceramic exhibits excellent piezoelectric properties and strong ferroelectricity: piezoelectric coefficient, d₃₃ = 195 pC/N; electromechanical coupling factor, k_t = 58.9 and k_p = 29.3%; mechanical quality factor, Q_m = 113; remnant polarization, P_r = 41.8 μC/cm²; coercive field, E_c = 19.5 kV/cm.     

Coexistence of room temperature ferroelectricity and ferrimagnetism in multiferroic BiFeO3-Bi0.5Na0.5TiO3 solid solution

The structure, ferroelectric and magnetic properties of (1 − x)BiFeO₃-xBi_0.5Na_0.5TiO₃ (x = 0.37) solid solution fabricated by a sol-gel method have been investigated. X-ray diffraction and Raman spectroscopy measurements show a single-phase perovskite structure with no impurities identified. Compared with pure BiFeO₃, the coexistence of ferroelectricity and ferrimagnetism have been observed at room temperature for the solution with remnant polarization P_r = 1.41 μC/cm² and remnant magnetization M_r = 0.054 emu/g. Importantly, a magnetic transition from ferrimagnetic (FM) ordering to paramagnetic (PM) state is observed, with Curie temperature T_C ∼ 330 K, being explained in terms of the suppression of cycloid spin configuration by the structural distortion.     

Structure, microstructure and electrical properties of (1 − x − y)Bi0.5Na0.5TiO3–xBi0.5K0.5TiO3–yBi0.5Li0.5TiO3 lead-free piezoelectric ceramics

The ternary system (1 − x − y)Bi_0.5Na_0.5TiO₃–xBi_0.5K_0.5TiO₃–yBi_0.5Li_0.5TiO₃ (abbreviated to BNKLT-x/y) was synthesized by conventional oxide-mixed method. The phase structure, microstructure, and dielectric, ferroelectric and piezoelectric properties of the ceramics were investigated. The X-ray diffraction patterns showed that pure perovskite phase with rhombohedral structure can be obtained in all the ceramics. The grain size varied with x and y. The temperature dependence of dielectric constant and dielectric loss revealed there were two phase transitions which were from ferroelectric (tetragonal) to anti-ferroelectric (rhombohedral) and anti-ferroelectric to paraelectric (cubic). Either increasing x or y content can make T_m (the temperature at which dielectric constant _r reaches the maximum) increase. With the addition of Bi_0.5K_0.5TiO₃, the remanent polarization P_r increased but the coercive field E_c decreased. With the addition of Bi_0.5Li_0.5TiO₃, P_r increased obviously and E_c increased slightly. Due to the stronger ferroelectricity by modifying Bi_0.5K_0.5TiO₃ and Bi_0.5Li_0.5TiO₃, the piezoelectric properties were enhanced at x = 0.22 and y = 0.10, which were as follows: P_r = 31.92 μC/cm², E_c = 32.40 kV/cm, _r = 1118, tan δ = 0.041, d₃₃ = 203 pC/N and K_p = 0.31. The results show that the BNKLT-x/y ceramics are promising candidates for the lead-free materials.     

High-dielectric-constant and low-loss microwave dielectric in the (1 − x)La(Mg0.5Ti0.5)O3-x(Ca0.8Sr0.2)TiO3 solid solution system

The microwave dielectric properties and microstructures of (1 − x)La(Mg_0.5Ti_0.5)O₃-x(Ca_0.8Sr_0.2)TiO₃ ceramics, prepared by a mixed oxide route, have been investigated. The forming of solid solutions was confirmed by the XRD patterns and the measured lattice parameters for all compositions. A near zero τ_f was achieved for samples with x = 0.5, although the dielectric properties varied with sintering temperature. The Q × f value of 0.5La(Mg_0.5Ti_0.5)O₃-0.5(Ca_0.8Sr_0.2)TiO₃ increased up to 1475 °C, after which it decreased. The decrease in dielectric properties was coincident with the onset of rapid grain growth. The optimum combination of microwave dielectric properties was achieved at 1475 °C for samples where x = 0.5 with a dielectric constant ?_r of 47.12, a Q × f value of 35,000 GHz (measured at 6.2 GHz) and a τ_f value of −4.7 ppm/°C.     

Ferroelectric relaxor behavior and dielectric spectroscopic study of 0.99(Bi0.5Na0.5TiO3)-0.01(SrNb2O6) solid solution

0.99(Bi_0.5Na_0.5TiO₃)-0.01(SrNb₂O₆) was prepared by simple solid state reaction route. Material stabilized in rhombohedral perovskite phase with lattice constants a = 3.9060 Å, α = 89.86° and a_h = 5.4852 Å, c_h = 6.7335 Å for hexagonal unit cells. Density of material was found 5.52 g_m/cm³ (92.9% of theoretical one) in the sample sintered at 950 °C. The temperature dependent dielectric constant exhibits a broad peak at 538 K (?_m = 2270) at 1 kHz that shows frequency dependent shifts toward higher temperature - typical relaxor behavior. Modified Curie-Weiss law was used to fit the dielectric data that exhibits almost complete diffuse phase transition characteristics. The dielectric relaxation obeys the Vogel-Fulcher relationship with the freezing temperature 412.4 K. Significant dielectric dispersion is observed in low frequency regime in both components of dielectric response and a small dielectric relaxation peak is observed. Cole-Cole plots indicate polydispersive nature of the dielectric relaxation; the relaxation distribution increases with increase in temperature.     

A diffuse phase transition study on Ba substituted (Na0.5Bi0.5)TiO3 ferroelectric ceramic

Polycrystalline perovskite lead free material (Na_0.5Bi_0.5)_0.91Ba_0.090TiO₃ was prepared by solid state reaction method. The crystal structure examined by X-ray powder diffraction indicates that the material was single phase with tetragonal structure. Dielectric studies exhibit a diffuse phase transition and characterized by a strong temperature and frequency dispersion of permittivity which relates cation disorder at A-site and exhibits relaxor behaviour. The dielectric relaxation has been modeled using the Vogel-Fulcher relationship, the calculated activation energy found to be E_a = 0.021 eV. Complex impedance analysis indicates the system undergoing a polydispersive non-Debye type relaxation. Also, used to characterize grain and grain-boundary resistivities of Ba substituted (Na_0.5Bi_0.5)TiO₃ ceramic. The phenomenon was also interpreted by accounting for microstructural differences. The corresponding relaxation times were also used to confirm the interpretation of complex impedance spectra. Overlapping of grain boundary and electrode relaxation processes can be separated above about 4000 C. Electrical modulus spectroscopy studies have been performed. The conductivity parameters such as ion-hopping rate (ω_p) and the charge carrier concentration (K¹) have been calculated using Almond and West formalism.     

The structural and electric properties of Li- and K-substituted Bi0.5Na0.5TiO3 ferroelectric ceramics

The structure, dielectric properties and phase transition of lithium and potassium modified Bi_0.5Na_0.5TiO₃ ceramics were investigated widely. The phase transition behavior with respect to changes in composition and temperature was investigated using X-ray diffraction analysis, dielectric and ferroelectric characterizations. The experimental results show that there is a diffusion phase transition in (Na_1−xK_x)_0.5Bi_0.5TiO₃ ceramics at T_m and the diffuseness of the phase transition is more obvious for the samples near the morphotropic phase boundary. In (Na_1−xLi_x)_0.5Bi_0.5TiO₃ system, due to the space charge polarization induced by ions conductivity, the low frequency permittivity increases so remarkably at high temperature that the peak of maximum permittivity vanishes. The hysteresis loops at different temperatures indicate that there is no existence of anti-ferroelectrics in lithium and potassium modified Bi_0.5Na_0.5TiO₃ ceramics above the depolarization temperature T_d. The depolarization reason is that the tetragonal nonpolar phase occurs and leads to the macro-micro domain transformation at about T_d.     

Relationship between structure and properties in high-temperature Bi(Al0.5Fe0.5)O3-PbTiO3 piezoelectric ceramics

Ceramic samples of xBi(Al_0.5Fe_0.5)O₃-(1 − x)PbTiO₃ (BAF-PT, x = 0.05-0.5) solid solutions were fabricated using the conventional solid state reaction method. X-ray diffraction analysis revealed that all compositions can form single perovskite phase with tetragonal symmetry. The relationship between the tetragonal lattice parameters, tetragonality c/a, cell volume, and ferro-piezoelectric characterization as a function of x was systematically investigated. The BAF modification can effectively improve the poling condition at a proper BAF content. A combination of piezoelectric constant of d₃₃ (50-60 pC/N), electromechanical planar coupling coefficients of k_p (20.3-22.5%), and high Curie temperature T_c (>478 °C) suggested that BAF-PT could be a good candidate for high-temperature piezoelectric applications.     

Preparation of Ni0.5Zn0.5Fe2O4/SiO2 nanocomposites and their adsorption of bovine serum albumin

The magnetic nanocomposites of (1 − x)Ni_0.5Zn_0.5Fe₂O₄/xSiO₂ (x = 0-0.2) were synthesized by the citrate-gel process and their absorption behavior of bovine serum albumin (BSA) was investigated by UV spectroscopy at room temperature. The gel precursor and resultant nanocomposites were characterized by FTIR, XRD, TEM and BET techniques. The results show that the single ferrite phase of Ni_0.5Zn_0.5Fe₂O₄ is formed at 400 °C, with high saturation magnetization and small coercivity. A porous, amorphous silica layer is located at the ferrite nanograin boundaries, with the silica content increasing from 0 to 0.20, the average grain size of Ni_0.5Zn_0.5Fe₂O₄ calcined at 400 °C reduced from about 18-8 nm. Consequently, the specific surface area of the nanocomposites ascends clearly with the increase of silica content, which is largely contributed by the increase in the thickness of the porous silica layer. The Ni_0.5Zn_0.5Fe₂O₄/SiO₂ nanocomposites demonstrate a better adsorption capability than the bare Ni_0.5Zn_0.5Fe₂O₄ nanoparticles for BSA. With the increase of the silica content from 0 to 0.05 and the specific surface area from about 49-57 m²/g, the BSA adsorption capability of the Ni_0.5Zn_0.5Fe₂O₄/SiO₂ nanocomposites calcined at 400 °C improve dramatically from 22 to 49 mg/g. However, with a further increase of the silica content from 0.05 to 0.2, the specific surface area increase from about 57-120 m²/g, the BSA adsorption for the nanocomposites remains around 49 mg/g, owing to the pores in the porous silica layer which are too small to let the BSA protein molecules in.     

Sintering behaviors, magnetic and electric properties of Bi-Zn co-doped Co2Y ferrites

The Bi and Zn substitution effects on the sintering behaviors, magnetic and electric properties of hexagonal ferrites with a composition of 2(Ba_1−xBi_xO)·2(Zn_yCo_0.8−yCu_0.2O)·6(Fe_2−x/3Zn_x/3O₃) were investigated. The results showed that the addition of Bi and Zn can significantly promote Co₂Y densification. The Y phase may be triggered to decompose into M and spinel phases at high sintering temperatures (above 1050 °C) for samples with excess Bi (x = 0.2) substitution, which resulted in densification and magnetic properties degradation. Co₂Y ferrites with x = 0.1 and y = 0.4 sintered at 1050 °C show a relative density of 94%, a high initial permeability of 4.5, a quality factor (Q) of 50.     

Crystal structure and dielectric properties of La(Mg0.5Ti0.5)O3-Ca0.8Sm0.4/3TiO3 solid solution system at microwave frequencies

The crystal structure and the dielectric properties of (1 − x)La(Mg_0.5Ti_0.5)O₃-xCa_0.8Sm_0.4/3TiO₃ ceramics have been investigated. Ca_0.8Sm_0.4/3TiO₃ was employed as a τ_f compensator and was added to La(Mg_0.5Ti_0.5)O₃ to achieve a temperature-stable material. The formation of (1 − x)La(Mg_0.5Ti_0.5)O₃-xCa_0.8Sm_0.4/3TiO₃ solid solutions were confirmed by the XRD results and the measured lattice parameters for all compositions. The dielectric properties are strongly correlated to the sintering temperature and the compositional ratio of the specimens. Although the ?_r of the specimen could be boosted by increasing the amount of Ca_0.8Sm_0.4/3TiO₃, it would instead render a decrease in the Q × f. The τ_f value is strongly correlated to the compositions and can be controlled by the existing phases. A new microwave dielectric material 0.45La(Mg_0.5Ti_0.5)O₃-0.55Ca_0.8Sm_0.4/3TiO₃, possessing a fine combination of microwave dielectric properties with an ?_r of 47.83, a Q × f of 26,500 GHz (at 6.2 GHz) and a τ_f of −1.7 ppm/°C, is proposed as a very promising candidate material for today's 3G applications.     

Phase evolution and microwave dielectric properties of TiO2-modified (Mg0.95Co0.05)2TiO4 ceramics

Phase evolution and microwave dielectric properties of (1 − x)(Mg_0.95Co_0.05)₂TiO₄-xTiO₂ (x = 0-1) ceramics prepared by the conventional mixed oxide route have been investigated. Increasing the TiO₂ content would lead to a main phase transformation from (Mg_0.95Co_0.05)₂TiO₄ to (Mg_0.95Co_0.05)TiO₃, (Mg_0.95Co_0.05)Ti₂O₅ and then TiO₂. Not only did the TiO₂ addition compensate the τ_f, it also lowered the sintering temperature of specimen. A huge drop of Q × f occurs at a 40-60 mol% TiO₂ addition was attributed to the formation of (Mg_0.95Co_0.05)Ti₂O₅ phase. Specimen with x = 0.78 can possess an excellent combination of microwave dielectric properties: ?_r ∼ 24.77, Q × f ∼ 38,500 GHz and τ_f ∼ −1.3 ppm/°C.     

Microwave dielectric properties of (1 − x)ZnMoO4-xTiO2 composite ceramics

(1 − x)ZnMoO₄-xTiO₂ (x = 0.0, 0.05, 0.158, 0.25, and 0.35) composite ceramics were synthesized by the conventional solid state reaction process. The sintering behavior, phase composition, chemical compatibility with silver, and microwave dielectric properties were investigated. All the specimens can be well densified below 950 °C. From the X-ray diffraction analysis, it indicates that the triclinic wolframite ZnMoO₄ phase coexists with the tetragonal rutile TiO₂ phase, and it is easy for silver to react with ZnMoO₄ to form Ag₂Zn₂(MoO₄)₃ phase and hard to react with TiO₂. When the volume fraction of TiO₂ (x value) increasing from 0 to 0.35, the microwave dielectric permittivity of the (1 − x)ZnMoO₄-xTiO₂ composite ceramics increases from 8.0 to 25.2, the Q_f value changes in the range of 32,300-43,300 GHz, and the temperature coefficient τ_f value varies from −128.9 to 157.4 ppm/°C. At x = 0.158, the mixture exhibits good microwave dielectric properties with a ?_r = 13.9, a Q_f = 40,400 GHz, and a τ_f = +2.0 ppm/°C.