热空气老化对丁基橡胶硫化胶阻尼性能的影响

利用动态热机械分析仪研究了丁基橡胶硫化胶老化过程中的阻尼性能,探讨了不同老化温度和老化时间对丁基橡胶阻尼因子及阻尼温域(阻尼因子不小于0.7)的影响规律。结果表明,随着老化时间的延长,丁基橡胶硫化胶的交联密度先增大后减小,损耗因子峰值和阻尼温域都呈先降低而后增高的趋势;在老化时间相同的情况下,阻尼温域与老化温度呈正相关性,老化温度越高阻尼温域越宽。     

热空气老化粘弹性丁基橡胶阻尼材料的性能及其老化机理研究

采用热空气加速老化试验方法对粘弹性丁基橡胶阻尼材料的老化性能及其老化机理进行了研究,获得了老化前后丁基橡胶阻尼材料力学性能、阻尼性能及其变化规律。研究结果表明：在所选定的热空气老化65℃×310天试验条件下,阻尼材料的拉伸强度提高了1MPa,阻尼性能曲线整体向高温区域平移了10℃,而有效阻尼温域基本保持不变,与模拟计算结果一致,可以满足等效25℃×10年储存条件下的使用要求。同时,采用FTIR和SEM技术分析了阻尼材料在热氧老化条件下分子链结构和微观结构的变化,得到了粘弹性丁基橡胶阻尼材料的热空气老化机理。     

丁基橡胶阻尼材料的耐热空气老化性能及老化机理研究

采用加速老化试验方法对粘弹性丁基橡胶(ⅡR)阻尼材料的热空气老化性能及老化机理进行研究,获得老化前后ⅡR阻尼材料力学性能、阻尼性能及其变化规律。研究结果表明:在所选定的热空气老化65℃×310 d试验条件下,阻尼材料的拉伸强度提高了1 MPa,阻尼性能曲线整体向高温区域平移了10℃,而有效阻尼温域基本保持不变,与模拟计算结果一致,可以满足等效25℃×10年储存条件下的使用要求。同时,采用红外光谱仪和扫描电子显微镜分析了阻尼材料在热氧老化条件下分子链结构和微观结构的变化,得到了粘弹性ⅡR阻尼材料的热空气老化机理。     

硅烷偶联剂对热空气老化过程中溶聚丁苯橡胶/白炭黑复合材料性能的影响

研究了硅烷偶联剂双-[3-(三乙氧基硅)丙基]-四硫化物(Si 69)、双-[3-(三乙氧基硅)丙基]-二硫化物(Si 75)及3-辛酰基硫代-1-丙基三乙氧基硅烷(NXT)对丁苯橡胶/白炭黑复合材料的硫化胶在热空气老化过程中力学性能、应力弛豫、交联密度及喷霜现象的影响。结果表明,与未加偶联剂的胶料相比,加入Si 69、Si 75或NXT的溶聚丁苯橡胶/白炭黑硫化胶的力学性能、应力弛豫系数和交联密度都相应提高,其中在热空气老化过程中,应力弛豫系数随老化时间的延长而增大,并且随着老化时间的延长,NXT改性体系的应力弛豫行为逐渐弱于Si 69和Si 75改性体系。加入Si 69可以减小在热空气老化过程中复合材料交联密度的增长率,且增长率随Si 69用量的增加而减小。加入硅烷偶联剂可以减弱溶聚丁苯橡胶/白炭黑复合材料的喷霜现象,体系表面的喷出物主要为白炭黑。     

炭黑对NBR复合材料交联密度和力学性能的影响

采用核磁共振交联密度仪,考察了炭黑粒径、结构度和用量对丁腈橡胶（NBR）复合材料的交联密度和力学性能的影响规律。研究表明：炭黑加入后硫化胶的交联密度增加,且随炭黑用量增加而增加,随粒径增加而减小;炭黑结构度对化学交联密度影响大于物理交联密度。随着炭黑粒径的减小,硫化胶的拉伸强度、撕裂强度、定伸应力增加,高定伸下炭黑粒径对应力的贡献大于低定伸。炭黑结构度增加,硫化胶的拉伸强度、定伸应力增加,撕裂强度降低。     

炭黑对三元乙丙橡胶耐湿热老化和热空气老化性能的影响

研究了半补强(SRF)、高耐磨(HAF)、快压出(FEF)、喷雾(SCB)和导电炭黑(CCB)等5种炭黑对三元乙丙橡胶(EPDM)的补强作用、耐湿热老化性能和耐热空气老化性能的影响。结果表明,在加入炭黑后,随着炭黑粒径减小,炭黑对EPDM的补强效果得到提高。其中小粒径的CCB和HAF能使EPDM硬度和拉伸强度上升幅度较大,同时拉断伸长率降低。而它们良好的补强效果能在EPDM的老化过程中起到显著的稳定作用。EPDM/CCB和EPDM/HAF硫化胶的物理机械性能,均在湿热老化(40℃/93%相对湿度)和热空气老化(120℃)中表现稳定。     

填料对氟橡胶热空气老化性能的影响

研究了片层状、颗粒状和金属氧化物等填料填充改性氟橡胶的耐热空气老化性能。结果表明,片层状填料改性的氟橡胶的耐热性能较差;颗粒状填料BaSO4填充改性的氟橡胶具有优良的耐热老化性,300℃老化24h后,氟橡胶力学性能的保持率在50％左右;金属氧化物Fe2O3和SnO2填充改性的氟橡胶具有较好的耐热老化性,300℃老化24h后,仍保持较好的力学性能,其强度分别为9．3MPa和10．3MPa。     

老化对NR硫化胶的影响

研究了热空气老化和真空老化对ＮＲ硫化胶结构和性能的影响,采用化学探测剂脱硫的方法测定了老化过程中ＮＲ硫化胶交联密度及交联键分布变化的情况,同时测定了硫化胶的力学性能和动态性能随时间变化的情况。结果显示,热空气老化使硫化胶的交联密度增加,但力学性能损失严重,原因是主链氧化断裂。真空老化使ＮＲ硫化胶交联密度略微降低,但力学性能保持良好,类似于硫化返原。热空气老化使ＮＲ硫化胶的动态性能改善,而真空老化后     

硫化剂TMTD/S用量对EPDM/FKM共混胶老化前后交联密度、性能及损耗因子的影响

研究了硫化剂TMTD/S用量对EPDM/FKM共混胶老化前后交联密度、性能及损耗因子的影响。研究发现,随着TMTD/S用量变大,硫化胶t_(90)变小,M_H和M_H-M_L均变大。共混胶中EPDM相交联密度不断变大,老化后,交联密度进一步变大;FKM相交联密度基本不变,老化后,交联密度变大,但与TMTD/S用量基本无关;总交联密度不断变大。拉伸强度变大,扯断伸长率先变大后不变,100%定伸应力和硬度变大;老化后,拉伸强度变大,拉伸强度变化率降低,扯断伸长率变小,100%定伸应力和硬度变大。损耗因子减小;老化后,损耗因子进一步变小;测试温度提高,损耗因子减小。     

热空气老化对丁苯橡胶磨耗性能的影响

以乳聚丁苯橡胶1502、溶聚丁苯橡胶T2000R和2557A为研究对象,以丁苯橡胶基础配方为依据,研究了热氧老化对不同结构丁苯橡胶阿克隆磨耗和DIN磨耗性能的影响。结果表明,热空气老化对不同结构丁苯橡胶阿克隆和DIN磨耗性能的影响不同。对于阿克隆磨耗性能,随老化时间的延长,1502硫化胶的耐磨性能提高,T2000R硫化胶的耐磨性能先升高后下降,而2557A硫化胶的耐磨性能随老化时间的延长而下降。对于DIN磨耗性能,1502,T2000R和2557A硫化胶的耐DIN磨耗性能都随老化时间的延长而逐渐降低,1502和T2000R硫化胶的耐磨耗性能随老化时间的延长明显下降,2557A硫化胶的耐磨耗性能下降却很小。加入防老剂可提高丁苯橡胶的阿克隆磨耗性能,但对DIN磨耗性能的影响却很小。     

苯基硅橡胶的热空气老化性能研究

研究了PS5360苯基硅橡胶在不同试验条件下的热空气老化性能。结果表明,PS5360苯基硅橡胶在200℃可以连续工作1 200 h,在250℃可以连续工作360 h,在300℃可以连续工作48 h;在经历不同温度下的长期热空气老化试验后,仍然具有较好的力学性能,是飞机高温影响区优秀的空气密封材料。     

Effects of Thermal Aging on the Mechanical Properties of a Porous-Matrix Ceramic Composite

The present article focuses on changes in the mechanical properties of an all-oxide fiber-reinforced composite following long-term exposure (1000 h) at temperatures of 1000–1200°C in air. The composite of interest derives its damage tolerance from a highly porous matrix, precluding the need for an interphase at the fiber–matrix boundary. The key issue involves the stability of the porosity against densification and the associated implications for long-term durability of the composite at elevated temperatures. For this purpose, comparisons are made in the tensile properties and fracture characteristics of a 2D woven fiber composite both along the fiber direction and at 45° to the fiber axes before and after the aging treatments. Additionally, changes in the state of the matrix are probed through measurements of matrix hardness by Vickers indentation and through the determination of the matrix Young's modulus, using the measured composite moduli coupled with classical laminate theory. The study reveals that, despite evidence of some strengthening of the matrix and the fiber–matrix interfaces during aging, the key tensile properties in the 0°/90° orientation, including strength and failure strain, are unchanged. This strengthening is manifested to a more significant extent in the composite properties in the ±45° orientation, wherein the modulus and the tensile strength each exhibit a twofold increase after the 1200°C aging treatment. It also results in a change in the failure mechanism, from one involving predominantly matrix damage and interply delamination to one which is dominated by fiber fracture. Additionally, salient changes in the mechanical response beyond the maximum load suggest the existence of an optimum matrix strength at which the fracture energy in the ±45° orientation attains a maximum. The implications for long-term durability of this class of composite are discussed.     

硫化温度对轮胎胶料物理机械性能及交联密度的影响

研究了不同硫化温度对轮胎橡胶的物理机械性能和交联密度的影响,并考察了不同硫化温度下胶料物理机械性能与交联密度之间的关系。结果表明：随着硫化温度的提高,硫化胶的交联密度、定伸应力和拉伸强度下降,扯断伸长率提高;硫化温度在130℃时,硫化胶的综合机械物理能最佳。     

杜仲橡胶硫化胶交联密度与结晶性能关系研究

采用差示扫描量热(DSC)法分析杜仲橡胶硫化胶交联密度对其物理性能和结晶性能的影响。结果表明:随着硫黄用量的增大,杜仲橡胶硫化胶的交联密度增大,邵尔A型硬度减小,100%定伸应力、拉伸强度和拉断伸长率先增大后减小;消除热历史后杜仲橡胶生胶的结晶特征减弱;随着交联密度的增大,硫化胶的DSC特征熔融峰减弱直至消失,结晶峰钝化,峰面积减小。     

硫化剂及填料对氯醚橡胶力学性能和老化性能的影响研究

研究了3种硫化剂——2,3-二巯基-喹喔啉(DNR-12A)、三巯基均三嗪(TCY)和亚乙基硫脲(NA-22)及3种填料——高耐磨炭黑(N330)、木质素-蒙脱土复合物填料(BL-MMT)和碱性木质素(lignin)对共聚型氯醚橡胶(ECO)硫化特性、交联密度、力学性能和老化性能的影响。结果表明,固定填料为N330时,用NA-22硫化的胶料的力学性能最好,但热氧老化性能最差;改变填料后NA-22硫化胶料的老化性能得到提高,固定硫化剂为NA-22时,以碱性lignin为填料的胶料的力学性能与热氧老化性能均最好,拉伸强度达15.5 MPa,断裂伸长率达394%,100%定伸应力达6.4 MPa,老化后拉伸强度保持率为103.2%。     

轮胎胎面胶老化交联密度与机械性能研究

轮胎胎面硫化橡胶的耐老化是其重要性能之一。本文通过不同条件下的老化试验,对比分析了一种胎面硫化橡胶老化条件下的物理机械性能,通过公式计算得出相应的交联密度,分析了交联密度与老化条件之间的关系及其规律。     

PVC木塑发泡复合材料的力学性能和密度

通过挤出、注塑成型工艺对聚氯乙烯/木粉木塑发泡制品的密度和力学性能进行研究,分析发泡剂、聚丙烯酸酯、发泡助剂及木粉粒径对复合材料的影响。由研究结果可知:有机AC发泡剂与无机发泡剂碳酸氢钠的耦合提高了发泡能力,但降低了力学性能。聚丙烯酸酯ACR质量分数为5%时或发泡助剂氧化锌质量分数为0.1%时,在改善制品密度的同时提高了其力学性能,但氧化锌的发泡效果更好些。当木粉粒径为80~100目时,密度较大,弯曲强度和拉伸强度出现最大值。     

预分散酚醛树脂硫化CIIR性能的研究

分别研究了预分散酚醛树脂HY-2045(预)、HY-2055(预)和SP-1055(预)对CIIR胶料硫化特性、力学性能及100℃×72h热空气老化性能的影响,并与原树脂HY-2045(原)、HY-2055(原)和SP-1055(原)的影响效果进行了对比。结果表明,与原酚醛树脂相比,预分散酚醛树脂在CIIR橡胶中的分散性、硫化胶拉伸强度和拉断伸长率均获得提高。加入SP-1055(预)可明显缩短CIIR胶料的t90;加入HY-2045(预)可使胶料的t10和t90延长,交联密度、硬度、100%定伸应力和拉伸强度均最小,拉断伸长率最大;加入HY-2055(预)可使胶料的t90延长,其他性能与加入SP-1055(预)的胶料相差不大。加入HY-2055(预)的硫化胶100℃×72h热空气老化后性能变化最小。     

橡胶型乙烯－醋酸乙烯共聚物配方及老化性能研究

研究了橡胶型乙烯－醋酸乙烯共聚物（ＥＶＭ）的配方及热氧老化性能。试验结果表明：ＥＶＭ具有优异的热空气老化性能，经１７５℃×７２ｈ老化后仍有很高的拉伸强度和扯断伸长率保持率；需采用过氧化物进行硫化，同时并用适量的三烯丙基异氰脲酸酯可以显著改善ＥＶＭ的压缩永久变形性能；它是一种典型非自补强性橡胶．需加入适量的补强填充剂；聚酯增塑剂可以在一定程度上降低ＥＶＭ的硬度，而对老化性能影响不大；防老剂ＲＤ可赋予胶料更优良的热空气老化性能和耐水解性能。     

不同硫化体系EPDM老化性能的研究

研究了DCP用量对EPDM力学性能、老化性能的影响。结果表明,采用过氧化物DCP硫化体系的力学性能优于硫磺硫化体系。DCP硫化的EPDM加入抗氧剂MB后具有较高的耐热氧老化性能,显示出MB具有较高的防护效能。