Rapid microwave-assisted synthesis of graphene nanosheet/Co3O4 composite for supercapacitors

Graphene nanosheet (GNS)/Co₃O₄ composite has been rapidly synthesized by microwave-assisted method. Field emission scanning electron microscopy and transmission electron microscopy observation reveals the homogeneous distribution of Co₃O₄ nanoparticles (3-5 nm in size) on graphene sheets. Electrochemical properties are characterized by cyclic voltammetry, galvanostatic charge/discharge and electrochemical impedance spectroscopy. A maximum specific capacitance of 243.2 F g⁻¹ has been obtained at a scan rate of 10 mV s⁻¹ in 6 M KOH aqueous solution for GNS/Co₃O₄ composite. Furthermore, the composite exhibits excellent long cycle life along with ∼95.6% specific capacitance retained after 2000 cycle tests.     

Relationship between microstructure and abrasive wear resistance of Al2O3-FeAl2O4 nanocomposites produced via solid-state precipitation

The work investigates the correlation between the microstructure and wear behaviour of novel Al₂O₃-FeAl₂O₄ nanocomposites, developed by precipitation of FeAl₂O₄ particles through reduction aging of Al₂O₃-10 wt.% Fe₂O₃ solid solutions in N₂/4%H₂. Reduction aging at 1450 °C for 10 and 20 h resulted in considerable improvements in abrasive wear resistance. The nanocomposites developed from solid solutions doped additionally with ∼250 ppm of Y₂O₃ contained finer intergranular second phase particles (by a factor of ∼2) and showed further improvements in the wear resistance. Doped nanocomposites reduction aged for 20 h at 1450 °C exhibited the minimum wear rate (reduced by a factor of ∼2.5 with respect to monolithic Al₂O₃). The suppression of fracture-induced surface pullout in the presence of intragranular nanosized second phase particles was the major factor responsible for the improved wear resistance of the nanocomposites with respect to monolithic alumina; microstructures without these intragranular nanoparticles showed no improvement. Higher aging temperature led to the presence of coarse (>2 μm) intergranular FeAl₂O₄ particles which had a detrimental effect on the wear resistance.     

Fabrication of three-dimensional porous structured Co3O4 and its application in lithium-ion batteries

A novel three-dimensional (3D) porous structured Co₃O₄ was prepared by electrodeposition combined with thermal-treatment method. The electrochemical properties of as-prepared 3D porous Co₃O₄ were closely related to its morphology and structure which can be modified by various thermal-treatment temperatures. The 3D porous Co₃O₄ prepared at 300 °C exhibited smaller crystallite size and higher capacity compared to 400 °C as well as 500 °C. As used in lithium-ion batteries, the porous Co₃O₄ anodes delivered a high reversible capacity of about 1100 mAh g⁻¹ with no obvious capacity fading up to 50 cycles and exhibited higher rate capability compared with Co₃O₄ foil anodes. The enhanced electrochemical performances of 3D porous Co₃O₄ anodes are attributed to its unique 3D porous structure which can offer a large materials/electrolyte contact area and accommodate the strain induced by the volume change during cycling.     

Hydrothermal synthesis of Li(Ni1/3Co1/3Mn1/3)O2 for lithium rechargeable batteries

Ultrafine powders of Li(Ni_1/3Co_1/3Mn_1/3)O₂ cathode materials for lithium-ion secondary batteries were prepared under mild hydrothermal conditions. The influence of the molar ratio of Li/(Ni + Co + Mn) was studied. The products were investigated by XRD, TEM and EDS. The final products were found to be well crystallized Li(Ni_1/3Co_1/3Mn_1/3)O₂ with an average particle size of about 10 nm.     

Characterization of high tap density Li[Ni1/3Co1/3Mn1/3]O2 cathode material synthesized via hydroxide co-precipitation

Li[Ni_1/3Co_1/3Mn_1/3]O₂ cathode material for lithium ion batteries was prepared by mixing metal hydroxide, (Ni_1/3Co_1/3Mn_1/3)(OH)₂, with 6% excess LiOH followed by calcinations. The (Ni_1/3Co_1/3Mn_1/3)(OH)₂ with secondary particle of about 12 μm was prepared by hydroxide co-precipitation. The tap density of the obtained Li[Ni_1/3Co_1/3Mn_1/3]O₂ powder was 2.56 ± 0.21 g cm⁻³. The powder was characterized by X-ray diffraction (XRD), scanning electron microscope (SEM), particle size distribution (PSD) and galvanostatic charge-discharge cycling. The XRD pattern of Li[Ni_1/3Co_1/3Mn_1/3]O₂ revealed a well ordered hexagonal layered structure with low cation mixing. Secondary particles with size of 13-14 μm and primary particles with size of about 1 μm can be identified from the SEM observations. In the voltage range of 2.8-4.3 V, the initial discharge capacity of the Li[Ni_1/3Co_1/3Mn_1/3]O₂ electrode was 166.6 mAh g⁻¹, and 96.5% of the initial capacity was retained after 50 charge-discharge cycling.     

Mixed oxides Ca2Fe2O5 and Ca2Co2O5 as anode materials for Li-ion batteries

The electrochemical performance of mixed oxides, Ca₂Fe₂O₅ and Ca₂Co₂O₅ for use in Li-ion batteries was studied with Li as the counter electrode. The compounds were prepared and characterized by X-ray diffraction and SEM. Ca₂Fe₂O₅ showed a reversible capacity of 226 mAh/g at the 14th cycle and retained 183 mAh/g at the end of 50 cycles at 60 mA/g in the voltage window 0.005-2.5 V. A reversible capacity in the range, 365-380 mAh/g, which is stable up to 50 charge-discharge cycles is exhibited by Ca₂Co₂O₅ in the voltage window, 0.005-3.0 V and at 60 mA/g. This corresponds to recycleable moles of Li of 3.9±0.1 (theoretical: 4.0). Significant improvement in the cycling performance and attainable reversible capacity were noted for Ca₂Co₂O₅ on cycling to an upper cut-off voltage of 3.0 V as compared to 2.5 V. Coulombic efficiency for both compounds is >98%. Electrochemical impedance spectroscopy (EIS) data clearly indicate the reversible formation/decomposition of polymeric surface film on the electrode surface of Ca₂Co₂O₅ in the voltage window, 0.005-3.0 V. Cyclic voltammetry results compliment the galvanostatic cycling data.     

Porous Co3O4 nanoplatelets by self-supported formation as electrode material for lithium-ion batteries

In this paper, we have reported a simple and rapid approach for the large-scale synthesis of β-Co(OH)₂ nanoplatelets via the microwave hydrothermal process using potassium hydroxide as mineralizer at 140 °C for 3 h. Calcining the β-Co(OH)₂ nanoplatelets at 350 °C for 2 h, porous Co₃O₄ nanoplatelets with a 3D quasi-single-crystal framework were obtained. The process of converting the β-Co(OH)₂ nanoplatelets into the Co₃O₄ nanoplatelets is a self-supported topotactic transformation, which is easily controlled by varying the calcining temperature. The textural characteristics of Co₃O₄ products have strong positive effects on their electrochemical properties as electrode materials in lithium-ion batteries. The obtained porous Co₃O₄ nanoplatelets exhibit a low initial irreversible loss (18.1%), ultrahigh capacity, and excellent cyclability. For example, a reversible capacity of 900 mAh g⁻¹ can be maintained after 100 cycles.     

Metal-organic framework as a host for synthesis of nanoscale Co3O4 as an active catalyst for CO oxidation

Co₃O₄ nanoparticles were prepared from cobalt nitrate that was accommodated in the pores of a metal-organic framework (MOF) ZIF-8 (Zn(MeIM)₂, MeIM = 2-methylimidazole) by using a simple liquid-phase method. The ZIF-8 host was removed by pyrolysis under air and subsequently washing with an NH₄Cl–NH₃·H₂O aqueous solution. Transmission electron microscopy (TEM) analysis shows that the obtained Co₃O₄ is composed of separate nanoparticles with a mean size of 18 nm. The Co₃O₄ nanoparticles exhibit excellent catalytic activity, cycling stability, and long-term stability in the low temperature CO oxidation.     

A delithiated LiNi0.65Co0.25Mn0.10O2 electrode material: A structural, magnetic and electrochemical study

A crystalline LiNi_0.65Co_0.25Mn_0.10O₂ electrode material was synthesized by the combustion method at 900 °C for 1 h. Rietveld refinement shows less than 3% of Li/Ni disorder in the structure. Lithium extraction involves only the Ni²⁺/Ni⁴⁺ redox couple while Co³⁺ and Mn⁴⁺ remain electrochemically inactive. No structural transition was detected during cycling in the whole composition range 0 < x < 1.0. Furthermore, the hexagonal cell volume changes by only 3% when all lithium was removed indicating a good mechanical stability of the studied compound. LiNi_0.65Co_0.25Mn_0.10O₂ has a discharge capacity of 150 mAh/g in the voltage range 2.5-4.5 V, but the best electrochemical performance was obtained with an upper cut-off potential of 4.3 V. Magnetic measurements reveal competing antiferromagnetic and ferromagnetic interactions - varying in strength as a function of lithium content - yielding a low temperature magnetically frustrated state. The evolution of the magnetic properties with lithium content confirms the preferential oxidation of Ni ions compared to Co³⁺ and Mn⁴⁺ during the delithiation process.     

Multifuctional Fe3O4@C/YVO4:Dy nanopowers: Preparation,luminescence and magnetic properties

As-synthesized Fe₃O₄ nanoparticles were encapsulated with carbon layers through a simple hydrothermal process. Fe₃O₄/C nanoparticles were coated with YVO₄:Dy³⁺ phosphors to form bifunctional Fe₃O₄@C@YVO₄:Dy³⁺ composites. Their structure, luminescence and magnetic properties were characterized by XRD, SEM, TEM, HRTEM, PL spectra and VSM. The experimental results indicated that the as-prepared bifunctional composites displayed well-defined core–shell structures. The ∼12 nm diameter YVO₄:Dy³⁺ shell exhibited tetragonal structure. Additionally, the composites exhibited a high saturation magnetization (13 emu/g) and excellent luminescence properties, indicating their promising potential as multifunctional biosensors for biomedical applications.     

Comparison of AlPO4- and Co3(PO4)2-coated LiNi0.8Co0.2O2 cathode materials for Li-ion battery

Electrochemical and thermal properties of Co₃(PO₄)₂- and AlPO₄-coated LiNi_0.8Co_0.2O₂ cathode materials were compared. AlPO₄-coated LiNi_0.8Co_0.2O₂ cathodes exhibited an original specific capacity of 170.8 mAh g⁻¹ and had a capacity retention (89.1% of its initial capacity) between 4.35 and 3.0 V after 60 cycles at 150 mA g⁻¹. Co₃(PO₄)₂-coated LiNi_0.8Co_0.2O₂ cathodes exhibited an original specific capacity of 177.6 mAh g⁻¹ and excellent capacity retention (91.8% of its initial capacity), which was attributed to a lithium-reactive Co₃(PO₄)₂ coating. The Co₃(PO₄)₂ coating material could react with LiOH and Li₂CO₃ impurities during annealing to form an olivine Li_xCoPO₄ phase on the bulk surface, which minimized any side reactions with electrolytes and the dissolution of Ni⁴⁺ ions compared to the AlPO₄-coated cathode. Differential scanning calorimetry results showed Co₃(PO₄)₂-coated LiNi_0.8Co_0.2O₂ cathode material had a much improved onset temperature of the oxygen evolution of about 218 °C, and a much lower amount of exothermic-heat release compared to the AlPO₄-coated sample.     

Comparison of structure and electrochemistry of Al- and Fe-doped LiNi1/3Co1/3Mn1/3O2

LiNi_1/3Co_1/3−xM_xMn_1/3O₂ (M = Fe and Al; x = 0, 1/20, 1/9 and 1/6) have been synthesized by firing the co-precipitates of metal hydroxides. The impacts of Fe and Al doping on the structure and electrochemical performances of LiNi_1/3Co_1/3Mn_1/3O₂ are compared by means of powder X-ray diffraction (XRD), scanning electron microscopy (SEM), and galvanostatic charge/discharge test as cathode materials for lithium ion batteries. These materials keep the same layered structure as the LiNi_1/3Co_1/3Mn_1/3O₂ host. It is found that Fe- and Al-doped LiNi_1/3Co_1/3Mn_1/3O₂ show different characteristics in lattice parameter and cycling voltage plateau with increasing dopant dose. More interestingly, low Al doping (x < 1/20) improves the structural stability while Fe doping does not have such effect even at low Fe content.     

Structural,morphological, and magnetic properties of ZnxCo1-xFe2O4 (0 ≤ x ≤ 1) prepared using a chemical co-precipitation method

In the present study, the chemical co-precipitation technique was adopted to synthesize Zn_xCo_1-xFe₂O₄ (ZCF) (0?≤ x?≤?1) ferrites. The thermogravimetric-differential thermal analysis results revealed that above 405?°C, the precursor had decomposed and ferrite formation had occurred. The structure and morphology of the prepared ferrite nanoparticles were investigated using X-ray diffraction, Fourier transform infrared spectroscopy, and field emission scanning electron microscopy (FE-SEM). The synthesized polycrystalline nanoparticles had a cubic spinel structure and the crystallite size was in the range of 6.09–12.98?nm. The prepared ferrites appeared as nearly spherical nanoparticles with a particle size in between 0.13 and 0.23?µm, as confirmed using FE-SEM. The elemental composition was determined using the energy-dispersive X-ray spectroscopy technique. The influence of the Zn-substituted cobalt ferrites (ZCF) on the structural, morphological, and magnetic properties were studied. The magnetic properties of the ZCF samples such as saturation magnetization, remanence magnetization, and coercivity measured at room temperature were 0.387–2.065?emu/g, 0.057–1.282?emu/g, and 60–1834?Oe, respectively. It was confirmed from the nature of the hysteresis loops that the given ZCF samples can be considered as a soft magnetic material.     

Synthesis of compounds, Li(MMn11/6)O4 (M = Mn1/6, Co1/6, (Co1/12Cr1/12), (Co1/12Al1/12), (Cr1/12Al1/12)) by polymer precursor method and its electrochemical performance for lithium-ion batteries

The compounds, Li(MMn_11/6)O₄ (M = Mn_1/6, Co_1/6, (Co_1/12Cr_1/12), (Co_1/12Al_1/12), (Cr_1/12Al_1/12)) are synthesised by the polymer precursor method. The structure and the morphology of the compounds are studied by the Rietveld refined X-ray diffraction (XRD), and transmission electron microscopy (TEM) techniques, respectively. Density and the Brunauer, Emmet and Teller surface area (BET) of the compounds are also studied. The cobalt doped compound, Li(Co_1/6Mn_11/6)O₄ is found to be nanosized particles in the range of 60-100 nm, when compared to the other compounds in our present study. The oxidation state and the local structure of the compounds are analysed by the X-ray absorption spectroscopy (XAS) technique. Cyclic voltammetry (CV) and the galvanostatic charge-discharge cycling (30 mA g⁻¹) studies are made in the voltage range of 3.5-4.3 V at room temperature for all the compounds under study. The bare and (Co_1/6), and (Co_1/12Cr_1/12) substituted spinels are cycled at high current rates of 1, 2 and 5C (assuming 1C∼120 mA g⁻¹). Cycling results of Co-substituted spinels show better and long-term capacity retention at all the current rates. At the end of the second cycle, Li(Co_1/6Mn_11/6)O₄ compound delivers a discharge capacity value of 100 (±3) and 87 (±3) mAh g⁻¹ for the current rate of 2 and 5C, respectively. An excellent capacity retention value of 94% is observed at the end of the 1000 cycles for both 2 and 5C rates.     

Application of EIS and salt spray tests for investigation of the anticorrosion properties of polyurethane-based nanocomposites containing Cr2O3 nanoparticles modified with 3-amino propyl trimethoxy silane

The Cr₂O₃ nanoparticles were modified with 3-amino propyl trimethoxy silane in order to obtain proper dispersion and increment compatibility with the polyurethane coating matrix. The nanocomposites prepared were applied on the St-37 steel substrates. The existence of 3-amino propyl trimethoxy silane on the surface of the nanoparticles was investigated by Fourier transform infrared (FTIR) spectroscopy and thermal gravimetric analysis (TGA). Dispersion of the surface modified particles in the polyurethane coating matrix was studied by a field emission-scanning electron microscope (FE-SEM). The electrochemical impedance spectroscopy (EIS) and salt spray tests were employed in order to evaluate the corrosion resistance of the polyurethane coatings. Polarization test was done in order to investigate the corrosion inhibition properties of the Cr₂O₃ nanoparticle on the steel surface in 3.5 wt.% NaCl solution. The adhesion strengths of the coatings were evaluated by pull-off adhesion tester before and after 120 days immersion in 3.5 wt.% NaCl solution. FT-IR and TGA analyses revealed that surface modification of the nanoparticles with 0.43 silane/5 g pigment resulted in the greatest amount of silane grafting on the surface of particles. Results obtained from FE-SEM analysis showed that the surface modified nanoparticles dispersed in the coating matrix properly. Results obtained from EIS and salt spray analyses revealed that the surface modified particles enhanced the corrosion protection performance of the polyurethane coating considerably. The improvement was more pronounced for the coating reinforced with 0.43 g silane/5 g pigment. Moreover, the adhesion loss decreased in the presence of surface modified nanoparticles with 0.43 silane/5 g pigment.     

Studying the influence of nano-Al2O3 particles on the corrosion performance and hydrolytic degradation resistance of an epoxy/polyamide coating on AA-1050

The aim of this work was studying the effects of addition of Al₂O₃ nanoparticles on the anticorrosion performance of an epoxy/polyamide coating applied on the AA-1050 metal substrate. For this purpose, the epoxy nanocomposites were prepared using 1, 2.5 and 3.5 (w/w) pre-dispersed surface modified Al₂O₃ nanoparticles. Field-emission electron microscope (FE-SEM) and ultraviolet–visible (UV–Vis) techniques were utilized in order to evaluate the nanoparticles dispersion in the epoxy coating matrix. The anticorrosion performance of the nanocomposites was studied by electrochemical impedance spectroscopy (EIS) (in 3.5 wt% NaCl solution for 135 days immersion) and salt spray test for 1000 h. The coating resistance against hydrolytic degradation was also studied by optical microscope and Fourier-transform infrared spectroscopy (FTIR). Results obtained from FE-SEM micrographs and UV–visible spectra showed that the nanoparticles dispersed in the coating matrix uniformly with particle size less than 100 nm even at high loadings. Results revealed that nano-Al₂O₃ particles could significantly improve the corrosion resistance of the epoxy coating. Nanoparticles reduced water permeability of the coating and improved its resistance against hydrolytic degradation.     

Synthesis of LiNi0.9Co0.1O2 from Li2CO3, NiO or NiCO3, and CoCO3 or Co3O4 and their electrochemical properties

Cathode active materials with a composition of LiNi_0.9Co_0.1O₂ were synthesized by a solid-state reaction method at 850 °C using Li₂CO₃, NiO or NiCO₃, and CoCO₃ or Co₃O₄, as the sources of Li, Ni, and Co, respectively. Electrochemical properties, structure, and microstructure of the synthesized LiNi_0.9Co_0.1O₂ samples were analyzed. The curves of voltage vs. x in Li_xNi_0.9Co_0.1O₂ for the first charge–discharge and the intercalated and deintercalated Li quantity Δx were studied. The destruction of unstable 3b sites and phase transitions were discussed from the first and second charge–discharge curves of voltage vs. x in Li_xNi_0.9Co_0.1O₂. The LiNi_0.9Co_0.1O₂ sample synthesized from Li₂CO₃, NiO, and Co₃O₄ had the largest first discharge capacity (151 mA h/g), with a discharge capacity deterioration rate of −0.8 mA h/g/cycle (that is, a discharge capacity increasing 0.8 mA h/g per cycle).     

Enhanced cycling performance of Fe3O4-graphene nanocomposite as an anode material for lithium-ion batteries

Fe₃O₄-graphene nanocomposite was prepared by a gas/liquid interface reaction. The structure and morphology of the Fe₃O₄-graphene nanocomposite were characterized by X-ray diffraction, scanning electron microscopy and high-resolution transmission electron microscopy. The electrochemical performances were evaluated in coin-type cells. Electrochemical tests show that the Fe₃O₄-22.7 wt.% graphene nanocomposite exhibits much higher capacity retention with a large reversible specific capacity of 1048 mAh g⁻¹ (99% of the initial reversible specific capacity) at the 90th cycle in comparison with that of the bare Fe₃O₄ nanoparticles (only 226 mAh g⁻¹ at the 34th cycle). The enhanced cycling performance can be attributed to the facts that the graphene sheets distributed between the Fe₃O₄ nanoparticles can prevent the aggregation of the Fe₃O₄ nanoparticles, and the Fe₃O₄-graphene nanocomposite can provide buffering spaces against the volume changes of Fe₃O₄ nanoparticles during electrochemical cycling.     

Pseudocapacitive behavior of Ti/RhOx + Co3O4 electrodes in acidic medium: application to supercapacitor development

Mixtures of RhO_x+Co₃O₄ have been electrochemically studied by cyclic voltammetry in acid solution as a function of composition. The electrodes were prepared by thermal decomposition at 400 °C of mixtures of nitrate precursors. Their electrochemical behavior shows substantial dependence on the electrode’s composition. The Co site controls the electrochemical behavior of the system in the 5-10 mol.% Rh composition range. A significant increase in the electrodes’ active area is observed for compositions corresponding to more than 10 mol.% RhO_x in admixture with Co₃O₄. Above 10 mol.% Rh, the voltammetric curves become more similar to that for RhO_x and then RhO_x becomes able to stabilize the Co₃O₄ in the mixture. Electrodes of this kind have been found to perform as good materials in electrochemical capacitor applications, exhibiting specific capacitances of 500-800 F g⁻¹ over to 20-60 mol.% RhO_x composition range. The large specific capacitance exhibited by this system arises from a combination of the double-layer capacitance and the pseudocapacitance associated with Rh surface redox-type reactions.     

Characterization of electrode/electrolyte interface using in situ X-ray reflectometry and LiNi0.8Co0.2O2 epitaxial film electrode synthesized by pulsed laser deposition method

An in situ experimental technique was developed for detecting structure changes at the electrode/electrolyte interface of lithium cell using synchrotron X-ray reflectometry and two-dimensional model electrodes with a restricted lattice plane. The electrode was constructed with an epitaxial film of LiNi_0.8Co_0.2O₂ synthesized by the pulsed laser deposition method. The orientation of the epitaxial film depends on the substrate plane; the 2D layer of LiNi_0.8Co_0.2O₂ is parallel to the SrTiO₃ (1 1 1) substrate ((0 0 3)_{LiCo0.2Ni0.8O2}//(1 1 1)SrTiO₃), while the 2D layer is perpendicular to the SrTiO₃ (1 1 0) substrate ((1 1 0)_{LiCo0.2Ni0.8O2}//(1 1 0)SrTiO₃). These films provided an ideal reaction field suitable for detecting structure changes at the electrode/electrolyte interface during the electrochemical reaction. The X-ray reflectometry indicated a formation of a thin-film layer at the LiNi_0.8Co_0.2O₂ (1 1 0)/electrolyte interface during the first charge-discharge cycle, while the LiNi_0.8Co_0.2O₂ (0 0 3) surface showed an increase in the surface roughness without forming the surface thin-film layer. The reaction mechanism at the electrode/electrolyte interface is discussed based on our new experimental technique for lithium batteries.