Flexural Behavior of Continuous FRP-Reinforced Concrete Beams

Continuous concrete beams are commonly used elements in structures such as parking garages and overpasses, which might be exposed to extreme weather conditions and the application of deicing salts. The use of the fiber-reinforced polymers (FRP) bars having no expansive corrosion product in these types of structures has become a viable alternative to steel bars to overcome the steel-corrosion problems. However, the ability of FRP materials to redistribute loads and moments in continuous beams is questionable due to the linear-elastic behavior of such materials up to failure. This paper presents the experimental results of four reinforced concrete beams with rectangular cross section of 200×300?mm continuous over two spans of 2,800 mm each. The material and the amount of longitudinal reinforcement were the main investigated parameters in this study. Two beams were reinforced with glass FRP (GFRP) bars in to different configurations while one beam was reinforced with carbon FRP bars. A steel-reinforced continuous concrete beam was also tested to compare the results. The experimental results showed that moment redistribution in FRP-reinforced continuous concrete beams is possible if the reinforcement configuration is chosen properly. Increasing the GFRP reinforcement at the midspan section compared to middle support section had positive effects on reducing midspan deflections and improving load capacity. The test results were compared to the available design models and FRP codes. It was concluded that the Canadian Standards Association Code (CSA/S806-02) could reasonably predict the failure load of the tested beams; however, it fails to predict the failure location.     

Flexural Behavior of Concrete Beams Reinforced with Hybrid (GFRP and Steel) Bars

Reinforcing concrete with a combination of steel and glass fiber-reinforced polymer (GFRP) bars promises favorable strength, serviceability, and durability. To verify its promise and to support design of concrete structures with this hybrid type of reinforcement, we have experimentally and theoretically investigated the load-deflection behavior of concrete beams reinforced with hybrid GFRP and steel bars. Eight beams, including two control beams reinforced with only steel or only GFRP bars, were tested. The amount of reinforcement and the ratio of GFRP to steel were the main parameters investigated. Hybrid GFRP/steel-reinforced concrete beams with normal effective reinforcement ratios exhibited good ductility, serviceability, and load carrying capacity. Comparisons between the experimental results and the predictions from theoretical analysis showed that the models we adopted could adequately predict the load carrying capacity, deflection, and crack width of hybrid GFRP/steel-reinforced concrete beams.     

Flexural Behavior of Continuous GFRP Reinforced Concrete Beams

The results of testing two simply and three continuously supported concrete beams reinforced with glass fiber-reinforced polymer (GFRP) bars are presented. The amount of GFRP reinforcement was the main parameter investigated. Over and under GFRP reinforcements were applied for the simply supported concrete beams. Three different GFRP reinforcement combinations of over and under reinforcement ratios were used for the top and bottom layers of the continuous concrete beams tested. A concrete continuous beam reinforced with steel bars was also tested for comparison purposes. The experimental results revealed that over-reinforcing the bottom layer of either the simply or continuously supported GFRP beams is a key factor in controlling the width and propagation of cracks, enhancing the load capacity, and reducing the deflection of such beams. Comparisons between experimental results and those obtained from simplified methods proposed by the ACI 440 Committee show that ACI 440.1R-06 equations can reasonably predict the load capacity and deflection of the simply and continuously supported GFRP reinforced concrete beams tested.     

Shear Strength of Large Concrete Members with FRP Reinforcement

Increasing interest in the use of fiber-reinforced polymer (FRP) reinforcement for reinforced concrete structures has made it clear that insufficient information about the shear performance of such members is currently available to practicing engineers. This paper summarizes the results of 11 large shear tests of reinforced concrete beams with glass FRP (GFRP) longitudinal reinforcement and with or without GFRP stirrups. Test variables were the member depth, the member flexural reinforcement ratio, and the amount of shear reinforcement provided. Results showed that the equations of the Canadian CSA shear provisions provide conservative estimates of the shear strength of FRP-reinforced members. Recommendations are given along with a worked example on how to apply these provisions including to members with FRP stirrups. It was found that members with multiple layers of longitudinal bars appear to perform better than those with a single layer of longitudinal reinforcing bars. Overall, it was concluded that the fundamental shear behavior of FRP-reinforced beams is similar to that of steel-reinforced beams despite the brittle nature of the reinforcement.     

Behavior and Ductility of Simple and Continuous FRP Reinforced Beams

The behaviors of simply and continuously supported beams reinforced with fiber reinforced polymer (FRP) materials are presented in this paper. The experimental testing program included seven simple rectangular beams and seven continuous T-section beams. Reinforcing bars and stirrups were made of steel, carbon, or glass fiber reinforced polymer (GFRP). It was concluded that the use of GFRP stirrups increased the shear deformation, and as a result deflection increased. Also, GFRP stirrups changed the failure mode from flexural to shear or flexural-shear, depending on the type of reinforcement bars (FRP or steel). Furthermore, the use of FRP reinforcement in continuous beams increased deformation. This increase remained small and acceptable at the service load level, but significantly increased near failure. While different FRP reinforcement arrangements were found to have the same load capacity as steel reinforcements in conventional beams, failure modes and ductility differed. Failure mode was governed by both the type of reinforcing bars and the type of stirrups. Additionally, the dowel effect influences the load carrying capacity of FRP reinforced continuous beams. A method for evaluating the ductility is presented. The ratio of absorbed energy at failure to the total energy, “energy ratio,” was used as a measure of ductility. Based on this definition, a classification of ductile, semiductile, and brittle behavior is suggested. The theoretical results obtained using the suggested method were substantiated experimentally. The continuous beams experienced higher “energy ratios” than did simple beams.     

Experimental Observation on the Effectiveness of Fiber Sheet Strip Stirrups in Concrete Beams

Experimental observations were made for the effectiveness of fiber sheet strips (FSSs) as internal stirrups in comparison with fiber-reinforced polymer (FRP) rod stirrups and steel stirrups. A total number of 10 concrete beams were tested under three-point loading. Each beam measured 1,400 mm long, 150 mm wide, and 250 mm deep. Their shear span-depth ratios were 2.5. The beams were composed of different shear reinforcements: one without stirrups, two with steel stirrups, one with carbon FRP rod stirrups, and the rest with different types of FSS stirrups. The main variables include stirrup types, strengthening of bent portions of FSS stirrups, impregnation, and shear reinforcement ratio for FSS stirrups. Test results indicated that concrete beams reinforced with FSS stirrups had enhanced shear strength over the beam without shear reinforcements. Moreover, the FSS stirrup-reinforced beams could maintain comparable shear behavior to that of the concrete beam reinforced with steel stirrups in overall load-deflection relationships, shear strengths, crack patterns, and crack widths at maximum load.     

Bond Strength of Tension Lap Splices in High-Strength Concrete Beams Strengthened with Glass Fiber Reinforced Polymer Wraps

This paper presents the experimental results of the first phase of a study undertaken at the American University of Beirut to examine the effectiveness of fiber reinforced polymer (FRP) wraps to confine steel reinforcement in a tension lap splice region anchored in high-strength reinforced-concrete beams. Seven beam specimens were constructed. The specimens were reinforced on the tension side with three deformed bars spliced at midspan. The splice region was devoid of any transverse reinforcement to allow a full examination of the FRP wrap contribution. Glass fiber reinforced polymer (GFRP) sheets were used. The main test variables were the GFRP configuration in the splice region (one strip, two strips, or a continuous strip), and the number of layers of the GFRP wraps placed around the splice region (one layer or two layers). All GFRP wraps were U-shaped. Except for the epoxy adhesive, no other anchorage mechanism or bonding procedure was applied for the GFRP wraps on the concrete beam. Following the application of the GFRP wraps, the beams were tested in positive bending. The test results demonstrated that GFRP wraps were effective in enhancing the bond strength and ductility of failure mode of the tension lap splices, especially when continuous strips were applied over the splice region.     

Bond Performance of GFRP Bars in Tension: Experimental Evaluation and Assessment of ACI 440 Guidelines

The development/splice strength and the pullout local bond stress-slip response of glass fiber-reinforced polymer (GFRP) bars in tension were experimentally investigated using beam specimens and pullout specimens, respectively. Two types of 12-mm (0.47-in.)-diameter GFRP bars were evaluated, namely, thread wrapped and ribbed. The test parameters included the concrete cover, the splice length, and the area of steel confinement for the beam specimens, and the concrete compressive strength for the pullout specimens. Companion steel reinforced beams were also tested for comparison. All beam specimens reinforced with thread-wrapped GFRP bars experienced pullout mode of bond failure, while all specimens reinforced with ribbed GFRP bars or steel bars experienced splitting mode of bond failure. It was found that the bond strength of FRP bars is largely dependent on the surface conditions of the bars. The pullout local bond stress-slip response of ribbed GFRP bars is intrinsically similar to that of steel bars reported in the literature. The bond strength of both types of GFRP bars investigated was about two to three times lower than that of steel bars. Predictions of the development/splice strength of GFRP bars in accordance with the ACI Committee 440 guidelines were unconservative in comparison with the test data. Also, in contradiction with the current ACI 440 report, the use of transverse confining reinforcement increased the bond strength by a sizable 15–30%.     

Designing and Testing of Concrete Bridge Decks Reinforced with Glass FRP Bars

In addition to their high strength and light weight, fiber-reinforced polymer (FRP) composite reinforcing bars offer corrosion resistance, making them a promising alternative to traditional steel reinforcing bars in concrete bridge decks. FRP reinforcement has been used in several bridge decks recently constructed in North America. The Morristown Bridge, which is located in Vermont, United States, is a single span steel girder bridge with integral abutments spanning 43.90 m. The deck is a 230 mm thick concrete continuous slab over girders spaced at 2.36 m. The entire concrete deck slab was reinforced with glass FRP (GFRP) bars in two identical layers at the top and the bottom. The bridge is well instrumented at critical locations for internal temperature and strain data collection with fiber-optic sensors. The bridge was tested for service performance using standard truck loads. The construction procedure and field test results under actual service conditions revealed that GFRP rebar provides very good and promising performance.     

Flexural Load Testing of Concrete-Filled FRP Tubes with Longitudinal Steel and FRP Rebar

The flexural performance of reinforced concrete-filled glass-fiber reinforced polymer (GFRP) tubes (CFFTs) has been investigated using seven specimens, 220?mm in diameter and 2.43?m long. Specimens were reinforced with either steel, GFRP, or carbon–fiber reinforced polymer (FRP) rebar of various sizes. Prefabricated GFRP tubes with most of the fibers oriented in the hoop direction were used in five specimens. One control specimen included conventional steel spirals of stiffness comparable to the GFRP tube and the other had no transverse reinforcement. Test results have shown that CFFT beams performed substantially better than beams with a steel spiral. Unlike CFFTs with FRP rebar, CFFTs with steel rebar failed in a sequential progressive manner, leading to considerable ductility. An analytical model capable of predicting the full response of reinforced CFFT beams, including the sequential progressive failure, has been developed, verified, and used in a parametric study. It is shown that laminate structure of the tube affects the behavior, only after yielding of the steel rebar. Steel reinforcement ratio significantly affects stiffness and strength, whereas concrete strength has an insignificant effect on the overall performance.     

Evaluation of Flexural Behavior and Serviceability Performance of Concrete Beams Reinforced with FRP Bars

Flexural behavior and serviceability performance of 24 full-scale concrete beams reinforced with carbon-, glass-, and aramid-fiber-reinforced-polymer (FRP) bars are investigated. The beams were 3,300?mm long with a rectangular cross section of 200?mm in width and 300?mm in depth. Sixteen beams were reinforced with carbon-FRP bars, four beams were reinforced with glass-FRP bars, two beams were reinforced with aramid-FRP bars, and two were reinforced with steel, serving as control specimens. Two types of FRP bars with different surface textures were considered: sand-coated bars and ribbed-deformed bars. The beams were tested to failure in four-point bending over a clear span of 2,750?mm. The test results are reported in terms of deflection, crack-width, strains in concrete and reinforcement, flexural capacity, and mode of failure. The experimental results were compared to the available design codes.     

Effect of Transverse Steel on the Response of RC Beams Strengthened in Shear by FRP: Experimental Study

The present paper shows and discusses some of the results obtained within an experimental investigation carried out on 15 reinforced concrete (RC) beams strengthened in shear by externally bonded fiber-reinforced plastics (FRP) sheets. The aim of the study is to analyze the influence that the geometrical percentage of transverse steel reinforcement could have on the FRP resisting action. In particular, the objectives of the experimental campaign are to explore the possible interaction between FRP and steel transverse reinforcement resisting actions, analyzing the deformation behavior of the shear resisting system (FRP, transverse steel, and concrete) and the modes of failure of the strengthened and not strengthened beams. The results of the tests in terms of shear capacity are compared to the design formulations provided by the American Concrete Institute and the National Research Council of Italy code-format recommendations.     

Deflection Prediction of Steel and FRP-Reinforced Concrete-Filled FRP Tube Beams

This paper presents the results of experimental and theoretical investigations that study the flexural behavior of reinforced concrete-filled fiber-reinforced polymer (FRP) tubes (RCFFTs) beams. The experimental program consists of 10 circular beams [6 RCFFT and 4 control reinforced concrete (RC) beams] with a total length of 2,000?mm, tested under four-point bending load. The experimental results were used to review and verify the applicability of various North American code provisions and some available equations in the literature to predict deflection of RCFFT beams. The measured deflections and the experimental values of the effective moment of inertia were analyzed and compared with those predicted using available models. The results of the analysis indicated that the behavior of steel and FRP-RCFFT beams under the flexural load was significantly different than that of steel and FRP-RC members. This is attributed to the confining effect of the FRP tubes and their axial contribution. This confining behavior in turn enhanced the overall flexural behavior and improved the tension stiffening of RCFFT beams. For that, the predicted tension stiffening of steel and FRP-RCFFT beams using the conventional equations (steel or FRP-RC member) underestimates the flexural response; therefore, the predicted deflections are overestimated. Based on the analysis of the test results, the Branson’s equation for the effective moment of inertia of RC structures is modified, and new equations are developed to accurately predict the deflection of concrete-filled FRP tube (CFFT) beams reinforced with steel or FRP bars.     

Shear Resistance of FRP RC Beams: Experimental Study

This study investigates the shear behavior of concrete beams reinforced with fiber-reinforced polymer (FRP) reinforcement. Six beams were subjected to two successive phases of testing. Half of the beams were reinforced in flexure with conventional steel reinforcement, while the other half were reinforced with glass fiber bars. Different shear span to depth ratios, ranging from 1.1 to 3.3, were analyzed in order to study the variation in the shear behavior of beams characterized by different types of shear failure. No shear reinforcement was provided in the first phase of testing, while in the second phase, just enough glass and carbon shear reinforcement was provided to enable failure due to shear. The results of these tests are presented and compared to predictions according to the design recommendations proposed by the ACI and the Institution of Structural Engineers, U.K. The results of this study show that these approaches, which are based on modifications of equations derived for steel reinforcement, underestimate the contribution of the concrete and the shear reinforcement to the total shear capacity of FRP RC beams. It is shown that both approaches can be modified to become less conservative.     

Does the Use of FRP Reinforcement Change the One-Way Shear Behavior of Reinforced Concrete Slabs?

For members with no transverse reinforcement, numerous models have been proposed for determining shear capacity, most often based on a statistical curve fit to experimental beam test results. The shear provisions of the Canadian code (CSA) for steel-reinforced concrete, by contrast, are based on a theoretical model, the modified compression field theory. This paper demonstrates that the CSA shear provisions for steel-reinforced members can be safely applied to members with internal fiber-reinforced polymer (FRP) bars by adjusting the term EsAs in the method to ErAr. A database of 146 shear failures of specimens reinforced with carbon, glass, or aramid FRP or steel is presented and gives an average test to predicted ratio of 1.38 with a coefficient of variation (COV) of 17.2%. The CSA code equations were optimized for the typical strain range of steel-reinforced concrete and when an equation appropriate for the wider range of strains associated with FRP is used, then a better statistical result can be achieved. Application of this expression to the database resulted in an average test to predicted strength ratio of 1.15 with a COV of 14.9%. As both methods are based on a theoretical shear model that was derived for steel-reinforced concrete and since both methods work safely, it can be concluded that the use of internal FRP bars does not change the one-way shear behavior of reinforced concrete beams and slabs without stirrups.     

New Approach for Estimating the Deflection of Beams Reinforced with FRP Reinforcement

Due to concerns with corrosion, the use of fiber-reinforced polymer (FRP) as a replacement to conventional steel reinforcement has greatly increased over the last decade. Researchers have identified the distinctive mechanical and bond properties of FRP reinforcement that prevent the use of existing relationships to establish serviceability of concrete structures reinforced with such products. Although studies have modified these empirical relationships to describe the behavior of structures reinforced with FRP reinforcement, this paper will provide a new approach to estimate deflection of concrete beams by considering material properties of the reinforcement and incorporating the effects of tension stiffening. Accuracy and precision of the approach was established by performing a statistical analysis on a database containing 171 FRP-reinforced concrete beams. Results were compared to those from existing proposed relationships and indicate the potential of the method to estimate deflection at various service conditions.     

Fatigue Performance of RC Beams Strengthened in Shear with CFRP Fabrics

In recent years, a tremendous effort has been directed toward understanding and promoting the use of externally bonded fiber-reinforced polymer (FRP) composites to strengthen concrete structures. Despite this research effort, studies on the behavior of beams strengthened with FRP under fatigue loading are relatively few, especially with regard to its shear-strengthening aspect. This study aims to examine the fatigue performance of RC beams strengthened in shear using carbon FRP (CFRP) sheets. It involves six laboratory tests performed on full-size T-beams, where the following parameters are investigated: (1) the FRP ratio and (2) the internal transverse-steel reinforcement ratio. The major finding of this study is that specimens strengthened with one layer of CFRP survived 5 million cycles, some of them with no apparent signs of damage, demonstrating thereby the effectiveness of FRP strengthening systems on extending the fatigue life of structures. Specimens strengthened with two layers of CFRP failed in fatigue well below 5 million cycles. The failure mode observed for these specimens was a combination of crushing of the concrete struts, local debonding of CFRP, and yielding of steel stirrups. This failure may be attributed to the higher load amplitude and also to the greater stiffness of the FRP which may have changed the stress distribution among the different components coming into play. Finally, comparison between the performance of specimens with transverse steel and without seems to indicate that the addition of transverse steel extends the fatigue life of RC beams.     

3D Finite-Element Analysis of Substandard RC Columns Strengthened by Fiber-Reinforced Polymer Sheets

Numerical analyses are performed to predict the stress–strain behavior of square reinforced concrete columns strengthened by fiber-reinforced polymer (FRP) sheet confinement. The research focuses on the contribution of FRP sheets to the prevention of elastic buckling of longitudinal steel bars under compression, in cases of inadequate stirrup spacing. A new Drucker–Prager-type plasticity model is proposed for confined concrete and is used in constructed finite-element model. Suitable plasticity and elasticity models are used for steel reinforcing bars and fiber-reinforced polymers correspondingly. The finite-element analyses results are compared against published experimental results of columns subjected to axial compression, to validate the proposed finite-element model. Stress concentrations in concrete core and on FRP jacket are investigated considering circular or square sectioned, plain or reinforced concrete columns. Geometry of the section as well as the presence of steel bars and stirrups affect remarkably the variation and magnitude of stress on FRP as percentage of its tensile strength.     

Flexural Behavior of GFRP-Reinforced Concrete Masonry Beams

An experimental and analytical study is conducted in order to investigate the flexural behavior of masonry beams that are internally reinforced using glass fiber-reinforced polymers (GFRP) rebars. Seven reinforced masonry beams with 4.0- and 2.4-m spans were tested under four-point bending setup. The beams were loaded monotonically up to failure. One had two courses of hollow concrete masonry units and the remaining six beams had three courses. Two masonry beams were reinforced using conventional steel rebars and were considered as the control specimens. The remaining five beams were internally reinforced using GFRP rods with different reinforcement ratios. Beams were detailed to have sufficient shear reinforcement such that they do not fail in shear. Flexural capacity, deformation, curvature, and strains of the tested GFRP-reinforced and steel-reinforced masonry beams were compared and discussed. Using the acquired data from the experimental and analytical studies, effectiveness of GFRP rods as internal reinforcement for concrete masonry beams is demonstrated.     

Experimental Analysis of Crack Growth in GFRP Reinforced Concrete

For decades, bridge slabs have been troubled by the corrosion of steel reinforcement. The unique corrosion resistance of glass fiber-reinforced polymer (GFRP) bars makes them a promising alternative to steel bars. Experiments have been conducted to investigate the bond performance of GFRP reinforced concrete under constant amplitude cyclic fatigue loading. Each specimen was an identical length beam with a single GFRP bar at the bottom, intended to simulate a transverse strip of a typical bridge deck slab. The crack growth was monitored for specimens of different widths, simulating different transverse reinforcement spacings. Up to 2?million?cycles of cyclic loads were applied at 100% typical service load levels. No fatigue failure was encountered in the testing. The effects of moderate overloads were also investigated.