New pattern Zn-Al-Mg-RE coating technics for steel structure sustainable design

Based on the advanced integrated technology of materials preparation and formation, a new pattern Zn-Al-Mg-RE anti-corrosion coating for steel structure sustainable design was manufactured by cored wires and high velocity arc spraying (HVAS) technologies. The developments of thermally sprayed coatings for steel structure protection were described. Based on Al, Zn, Zn-Al and Zn-Al-Mg coatings, the anti-corrosion properties of new-pattern Zn-Al-Mg-RE coating were evaluated through electrochemical methods including electrochemical polarization and electrochemical impedance spectroscopy (EIS) coupled with SEM and XRD. The models of Zn-Al-Mg-RE coating undergoing corrosion with the initial pinhole defect and the latter with accelerated products were also discussed. The results show that Zn-Al-Mg-RE coating exhibites excellent corrosion resistance for long-term immersion, which is helpful for the sustainable design of steel structure in aggressive corrosion conditions. And the corrosion products seem to possess certain self-sealing function. Foundation item: Project (50235030) supported by the National Natural Science Foundation of China     

热浸镀锌层在中性盐雾试验中的防腐性能研究

采用2种定制的热浸镀锌试件,经5000 h中性盐雾试验后发现镀层防腐性能存在显著差异.采用镀锌层厚度损耗测试法、X射线衍射分析法（XRD）和扫描电镜分析法（SEM）分别测试了镀层的厚度损耗量、盐雾试验前后的晶体物质组成和腐蚀前后的微观形貌.研究表明:2种热浸镀锌试件在盐雾腐蚀过程中的产物和机理相似,而影响其防腐性能的主要因素为热浸镀锌的生产工艺、腐蚀产物的致密程度.     

油田管道用纳米TiO_2改性防腐涂料的研究

制备了TiO2:改性防腐涂料,并对其性能进行了实验研究.结果表明,当纳米粒子添加量为3%时,防腐材料的常规性能、耐磨擦性及耐腐蚀性都得到了较大的提高.说明纳米TiO2对改善石油管道防腐涂料的性能具有重要作用.     

Corrosion resistance of waterborne epoxy coating pigmented by nano-sized aluminium powder on steel

A novel kind of waterborne epoxy coating pigmented by nano-sized aluminium powders on high strength steel was formulated. Several coatings with different pigment volume content (PVC) were prepared. The coating morphology was observed using scanning electron microscopy (SEM), and the electrochemical properties were investigated by electrochemical impedance spectroscopy (EIS). Immersion test and neutral salt spray test were also conducted to investigate the corrosion resistance of the coating. It is demonstrated that the critical pigment volume content (CPVC) value is between 30% and 40%. The coating with PVC of 30% exhibits good corrosion resistance in 3.5% (mass fraction) NaCl solution.     

多弧离子镀TiN涂层工艺及耐蚀性研究

为提高4Cr13马氏体不锈钢的耐蚀性,对其进行多弧离子镀处理,获得TiN涂层,并用X射线衍射仪、显微硬度计、扫描电子显微镜、电化学测量仪对涂层进行物相分析、表面形貌观察、硬度检测以及电化学腐蚀性能测试.结果表明:随着电流的增大,表面的液滴数目和尺寸增大,涂层厚度增加,薄膜硬度也增大;相结构主要为TiN,有明显的择优取向,且随着弧电流的增强,衍射峰强度略有增加.TiN试样在3.5％的NaCl溶液中耐蚀性与基体相当,在1 mol/L的H2SO4溶液中的耐蚀性比基体提高了800倍.     

桥梁用混凝土钢筋的防锈复合涂层的工艺优化及性能研究初探

为了提高钢混结构内部配筋的耐久性,在有机防锈涂料中添加了无机纳米添加剂,研制出"有机-无机纳米复合体涂层",利用纳米材料的"自修复"功能和"超延展"行为,实现钢筋表面的有效覆盖,弥补了普通有机涂层由于涂抹不均导致腐蚀加剧的缺陷。经过宏观形貌的目测、局部形貌的显微观测以及电化学检测等手段,分析了纳米复合体涂层钢筋的锈蚀规律,验证了涂有纳米复合体涂层对提高钢筋耐蚀能力的有效性。实验结果表明:使用了纳米复合体涂层的钢筋,具有一定的"自洁净"功能,能有效抵御外界环境中杂质离子的侵蚀。     

Corrosion behaviors of P110 steel and chromium coating in CO<Subscript>2</Subscript>-saturated simulated oilfield brine

The protective chromium coating was prepared on P110 steel by employing pack cementation.The corrosion behaviors of P110 steel and the obtained coating in CO2-saturated simulated oilfield brine were studied by static complete immersion tests and electrochemical measurements.The corrosion attacks of the samples were determined by mass loss,corroded surface morphologies,corrosion products,and results of electrochemical measurements.The experimental results showed that the coating was uniform,continuous and co...     

Research on the Anticorrosion Coating Under the Paved Layer for Highway Steel Box Bridge Deck

The corrosion of the anticorrosion coating and the defects of the asphalt concrete paved layer have been investigated on long-span steel box bridge decks. The anticorrosion coating lies in the midclle of two entirely different materials： a highway steel box bridge deck and a paved layer, which is used as anticorrosion and waterproof coating for the steel bridge deck. For our study, electrochemical corrosion and pull strength experiments have been selected for the investigation of the corrosion properties of inorganic zinc rich coating, epoxy zinc rich coating and arc sprayed zinc coating. The adhesive strength between the coatings and the panel, and the effect of the coating corrosion on the shear properties of the paved layers including cast asphalt, thermal asphalt mortar, epoxy asphalt and modified asphalt con- crete have been investigated. The results show that the adhesive strength between the coatings and the bridge panel is controlled by the method of pre-processing rust removal. Coating by sandblasting has stronger adhesive strength than coating by shot peening. The results also reveal that shear strength of the paved layer is affected by the corrosion product of zinc coating. The arc sprayed zinc coating has stronger shear strength than zinc rich coatings.     

蒙脱石对改性硅酸盐富锌防腐涂料性能的影响

为了提高富锌防腐涂料的综合性能,以硅丙乳液、硅溶胶、氢氧化钾、鳞片状锌粉为主要原料,分别添加经HOOC(CH2)17NH+3有机改性的蒙脱石与无机蒙脱石作为抗沉剂,制备改性的硅酸钾水性无机富锌防腐涂料.探讨了蒙脱石种类和用量对富锌涂料涂层性能、表面形貌及耐蚀性的影响.结果表明:采用有机蒙脱石作为抗沉剂的富锌防腐涂料的综合性能优于未添加抗沉剂的涂料,而后者的综合性能优于采用无机蒙脱石作为抗沉剂的涂料.当以加入量为涂料总质量的0.3%的有机蒙脱石作为抗沉剂时,所配制的涂料涂层表面平整、致密且机械性能以及耐腐蚀性能优异,是一种绿色长效的防腐涂料.     

Corrosion resistance of plasma sprayed NiCrAl (ZrO_2 Y_2O_3) thermal barrier coating on 18-8 steel surface

1INTRODUCTION Austeniticstainlesssteelisdevelopedtocom pensateforpoorcorrosionresistanceofmartensite stainlesssteelandoverlargebrittlenessofferrite stainlesssteel.Basicconstituentsofitstypicalal loyare18%Crand8%Ni(massfraction),which isusuallycalledas188s…     

Corrosion Behavior of Plasma Transferred Arc Fe-based Coating Reinforced by Spherical Tungsten Carbide in Hydrochloric Acid Solutions

Fe-based coatings reinforced by spherical tungsten carbide were deposited on 304 stainless steel using plasma transferred arc(PTA) technology.The composition and phase microstructure of the coatings were evaluated using scanning electron microscopy(SEM),energy dispersive spectrometer(EDS) and X-ray diffraction(XRD).The corrosion behaviors of the coatings in 0.5 mol/L HCl solution were studied using polarization curve and electrochemical impedance spectroscopy(EIS) measurements.The experimental results shows that the tungsten carbide improves the corrosion resistance of the Fe-based alloy coating,but increase in the mass fraction of tungsten carbide leads to increasing amount of defects of holes and cracks,which results in an adverse effect on the corrosion resistance.The defects are mainly present on the tungsten carbide but also extend to the Fe-based matrix.The tungsten carbide,acting as a cathode,and binding material of Fe-based alloy,acting as an anode,create a galvanic corrosion cell.The binding material is preferentially corroded and causes the degradation of the coating.     

Ce~(3+)-聚苯胺/蒙脱土复合材料掺杂环氧涂层的制备及耐腐蚀性能

采用原位插层聚合法合成了聚苯胺/蒙脱土复合材料(PANI/MMT),通过阳离子交换吸附制得了Ce~(3+)-聚苯胺/蒙脱土复合材料(Ce~(3+)-PANI/MMT).随后对所制备的样品进行表征.将PANI,PANL/MMT,Ce~(3+)-PANI/MMT粉末添加到环氧树脂中(质量分数为5%),涂覆在碳钢表面,干燥.将4种涂层浸泡在3.5%NaCl溶液中,通过电化学实验来比较4种涂层的耐蚀性能.研究结果表明,Ce~(3+)-PANI/MMT复合材料掺杂的环氧涂层的耐腐蚀性能最好,且具有一定的自修复性能.     

Effect of laser remelting on the microstructure and corrosion resistance of plasma sprayed Fe-based coating

Fe-based amorphous and nanocrystalline coatings were fabricated by air plasma spraying. The coatings were further treated by laser remelting process to improve their microstructure and properties. The corrosion resistance of the as-sprayed and laser-remelted coatings in 3.5wt% NaCl and 1 mol/L HCl solutions was evaluated by electrochemical polarization analysis. It was found that laser-remelted coating appeared much denser than the as-sprayed coating. However, laser-remelted coating contains much more nanocrystalline grains than the as-sprayed coatings, resulting from the lower cooling rate in laser remelting process compared with plasma spraying process. Electrochemical polarization results indicated that the laser-remelted coating has great corrosion resistance than the as-sprayed coating because of its dense structure.     

锌粉表面改性对水性富锌防腐涂层性能的影响

为了改善片状锌粉在实际应用中抗沉降性、分散性和耐腐蚀性差的缺点,采用溶胶-凝胶法对片状锌粉进行了表面改性,并利用改性锌粉制备了水性富锌防腐涂层.利用X射线衍射仪、物理性能检测设备和扫描电子显微镜分析了锌粉改性效果及其对富锌防腐涂层性能的影响.结果表明:经过硅烷偶联剂BTSPA掺杂硝酸镱改性后,锌粉分散性提高了53.3%;改性涂层的表干时间缩短了20%,实干时间缩短了8.3%,物理性能得到了提升;涂层表面裂痕减少,孔隙率降低为0.14%;经NaCl溶液浸泡120 h后,涂层表面几乎未发生腐蚀;自腐蚀电位正移15.1%,自腐蚀电流密度降低一个数量级,线性极化电阻增大一个数量级.硅烷偶联剂BTSPA掺杂稀土硝酸镱改性锌粉优于其他改性方法.     

Electrochemical corrosion behavior of arc sprayed Zn and Zn15Al coatings in simulated salina soil and neutral meadow soil solutions

Arc sprayed Zn and Zn15Al coatings were chosen to protect the metal ends of prestressed high-strength concrete (PHC) pipe piles against corrosion of salina soil in northern china and neutral meadow soil in northeast China. The corrosion behavior of the coated Q235 steel samples in two simulated soil solutions were investigated by potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) methods. The experimental results show that the corrosion of the matrix Q235 steel in both simulated solutions is remarkably inhibited by Zn and Zn15Al coatings. The corrosion products on Zn and Zn15Al are thick, compact, firm and protective. The corrosion current density icorr of both Zn and Zn15Al-coated samples is decreased evidently with corrosion time, and the charge transfer resistance Rct is increased greatly. The corrosion resistance indexes of Zn and Zn15Al in simulated neutral meadow soil solution are more outstanding than those in salina soil. The corrosion resistance of Zn15Al in salina soil is slightly superior to that of Zn. When the sprayed coatings are sealed with epoxy resin, the corrosion resistance of the coatings is further enhanced markedly.     

低温烧结活性瓷釉涂层钢筋耐腐蚀性能试验研究

为了研究低温烧结活性瓷釉（LTCRE）涂层的性能和机理,利用差示扫描量热法（DSC）和热重法（TG）对LTCRE涂层的烧结温度进行优化,采用扫描电子显微镜（SEM）、X射线能谱分析（EDS）和X射线衍射（XRD）分析涂层微观结构和腐蚀过程,通过中性盐雾试验和氙灯老化试验研究LTCRE涂层钢筋的耐腐蚀性能. LTCRE涂层的优化烧结温度为500~540 °C,涂层具有结构致密、孔隙率低的特点,LTCRE涂层钢筋在腐蚀后的质量变化为普通钢筋的1.6%,800 h盐雾腐蚀后人为缺陷孔的剥离半径为0.26 mm,在氙灯照射下耐老化时长超过500 h. 结果表明,LTCRE涂层作为无机陶瓷涂层,具有比环氧树脂涂层更优异的耐老化性能,具备长期稳定的耐腐蚀能力. 涂层密实少孔的结构和烧结时良好的化学反应使得LTCRE涂层钢筋能够有效阻止外界腐蚀物质渗入与蔓延,即使在缺陷孔发生腐蚀后也能够阻止腐蚀加剧,起到涂层自愈合的效果.     

Degradation mechanism of lacquered tinplate in energy drink by in-situ EIS and EN

The corrosion process of phenolic epoxy coated tinplate in energy drink was investigated by in-situ electrochemical impedance spectroscopy(EIS) and electrochemical noise(EN) techniques. The experimental results indicate that the degradation process of novolac epoxy coated tinplate in energy drink can be divided into three main stages: organic coating wetted by the beverage; corrosion initiation beneath the organic coating; and corrosion extension process. It was proposed that the tin coating and carbon steel were mainly corroded by organic acids in energy drink through the pores of the organic coating. After the tin coating was corroded, the carbon steel started to corrode due to its higher electrochemical activity and became to be the dominated corrosion reaction.     

Ni—Cu—P镀层在氢氟酸溶液中的耐蚀性研究

为了改善20R钢在氢氟酸介质中的耐蚀性,采用化学镀技术在该材料表面制备了Ni—Cu—P三元合金镀层。通过金相显微镜和X射线衍射观察和分析了镀层的表面形貌和组成,通过浸泡法、电化学系统测试了20R钢和镀层在氢氟酸溶液中的腐蚀性能。结果表明：Ni—Cu—P镀层能顺利地在20R钢表面发生沉积,镀层光滑、致密、无裂纹,阻隔了氢氟酸与20R钢的直接接触。镀层在氢氟酸溶液中更容易发生钝化,具有一定的耐蚀性能。     

Effect of Salt Spray Corrosion on Tribological Properties of HVOF Sprayed NiCr-Cr_3C_2 Coating with Intermediate Layer

The objective of the present work was to determine the influence of the neutral salt spray corrosion on the wear resistance of HVOF sprayed NiCr-Cr_3C_2 coating with intermediate layer. Ni-Zn-Al_2O_3 coatings as interlayers were prepared by low pressure cold spray(LPCS) between NiCr-Cr_3C_2 cermet coatings to form a sandwich structure to enhance the corrosion resistance properties. The tribological properties were examined using the UMT-3 fricition and wear tester by line-contact reciprocating sliding under dry and salt spray one week corrosion. The morphology, element distribution, and phase compositions of the coating and worn sufaces were analyzed by using scanning electron microscopy, energy dispersive spectrometry, and X-ray diffraction respectively. The corrosion behavior of the coating was studied by the open-circuit potential, the electrochemical impedance spectroscopy, potentiodynamic polarization, and salt spray corrosion methods. It is found that the sandwich structured coating has better corrosion resistance than the single layer coating. The results show that under dry wear conditions, the wear mechanism is abrasive and adhesive wear, whereas under salt spray corrosion conditions it becomes corrosion wear. The friction coefficient of the sandwich structured coating after salt spray corrosion is slightly lower than the dry friction coefficient, but the weight of the wear loss is lower than that under dry condition.     

氩弧熔覆镍基自熔合金的工艺研究

采用氩弧熔覆工艺在Q235钢基体上获得了F102Fe镍基合金熔覆层.测试了涂层的硬度和耐腐蚀性，借助光学金相显微镜、扫描电子显微镜观察其显微组织，进而对熔覆工艺、合金组织及熔覆层性能之间的关系进行详细阐述.研究结果表明，采用氩弧熔覆工艺可以在Q235钢基表面上获得与基体结合良好、组织细密、具有较高硬度和耐蚀性的F102Fe合金熔覆层.在相同的情况下，增加电流强度或减少熔覆层的厚度，组织由共晶向亚共晶转变；随熔覆层的硬度、耐蚀性降低，塑性有所改善.