1.
This work reports the procedure for selection of alloying elements to refine the microstructure of hardfacing Ni–Cr–B–Si–C alloys by providing in situ formed nucleation agents. It is concluded that the refining element should be able to spontaneously produce precipitates at high temperatures with little solubility in their Cr-rich counterparts. After exploring the theoretical backgrounds on how to select the refining element, Nb and Zr were selected and the phase formation reactions of Zr- or Nb-modified Ni–Cr–B–Si–C alloys were calculated using Thermo-Calc® simulations. Detailed microstructural analyses of the rapidly solidified samples deposited from the modified alloys showed that addition of Nb in specific quantities induces a significant microstructural refinement in the original Ni–Cr–B–Si–C alloy without deteriorating its high hardness. The Nb-modified alloy could be used to further investigate the viability of microstructural refinement as an effective toughening mechanism for Ni–Cr–B–Si–C and similar alloy systems. 相似文献
2.
《Scripta materialia》2004,50(5):583-588
Zr52.5Ti5Cu17.9Ni14.6Al10 metallic glass machining chips were characterized using SEM, X-ray diffraction and nano-indentation. Above a threshold cutting speed, oxidation of the Zr produces high flash temperatures and causes crystallization. The chip morphology was unique and showed the presence of shear bands, void formation and viscous flow. 相似文献
3.
Sluggish diffusion kinetics is an important contributor to the outstanding properties of high-entropy alloys. However, the diffusion kinetics in high-entropy alloys has never been probed directly. Here, the diffusion couple method was used to measure the diffusion parameters of Co, Cr, Fe, Mn and Ni in ideal-solution-like Co–Cr–Fe–Mn–Ni alloys. These parameters were compared with those in various conventional face-centered cubic metals. The results show that the diffusion coefficients in the Co–Cr–Fe–Mn–Ni alloys are indeed lower than those in the reference metals. Correspondingly, the activation energies in the high-entropy alloys are higher than those in the reference metals. Moreover, the trend of the normalized activation energy is positively related to the number of composing elements in the matrix. A quasi-chemical model is proposed to analyze the fluctuation of lattice potential energy in different matrices and to explain the observed trend in activation energies. Greater fluctuation of lattice potential energy produces more significant atomic traps and blocks, leading to higher activation energies, and thus accounts for the sluggish diffusion in high-entropy alloys. 相似文献
4.
It has been recently pointed out that the compositions of industrial alloys are originated from cluster-plus-glueatom structure units in solid solutions. Specifically for Ni-based superalloys, after properly grouping the alloying elements into Al, Ni-like(■), r-forming Cr-like(■) and c-forming Cr-like(■), the optimal formula for single-crystal superalloys is established [Al–Ni_(12)](Al_1■~_(0:5) ■_(1:5)). The Co substitutions for Ni at the shell sites are conducted on the basis of the first-generation single-crystal superalloy AM3, formulated as [Al–■_(12)Co_x](Al_1Ti_(0.25)Ta_(0.25)Cr_1W_(0.25)Mo_(0.25)), with x = 1.5, 1.75, 2 and 2.5(the corresponding weight percents of Co are 9.43, 11.0, 12.57 and 15.71, respectively). The900 ℃ long-term aging follows the Lifshitz–Slyozov–Wagner theory(LSW theory), and the Co content does not have noticeable influence on the coarsening rate of c0. The microstructure and creep behavior of the four(001) single-crystal alloys are investigated. The creep rupture lifetime is reduced as Co increases. The alloy with the lowest Co(9.43 Co) shows the longest lifetime of about 350 h at 1050 ℃/120 MPa, and all the samples show N-type rafting after creep tests. 相似文献
5.
K. Rolfs M. Chmielus R.C. Wimpory A. Mecklenburg P. Müllner R. Schneider 《Acta Materialia》2010,58(7):2646-2651
Magnetic shape-memory alloys tend to deform via magnetic-field-induced and stress-induced twin-boundary motion. The rather low martensite transformation temperature of ternary Ni–Mn–Ga limits the operating temperature for potential applications. By alloying 5 at.% cobalt, the martensite transformation temperature and the Curie temperature was increased from 70 and 110 °C respectively up to 160 °C. In the single crystalline samples two non-modulated structures with tetragonal and orthorhombic lattices were found. The non-modulated orthorhombic structure has similar lattice parameters to the pseudo-orthorhombic 14M Ni–Mn–Ga phase. The single crystal specimen with the non-modulated orthorhombic structure exhibited a cyclic permutation of all three crystallographic axes in response to uniaxial loading. The parallelepiped-shaped sample was compressed repeatedly in all three directions. While maximizing work done by the load during deformation required three different martensite variants to result from deformation in three different directions, only two different martensite variants were found. The analysis of the sample shape revealed two variants mutually related through cyclic permutation of the lattice parameters, which cannot result from a single twinning event. The cyclic permutation is discussed in the light of Crocker’s double twinning mechanism. 相似文献
6.
《Intermetallics》2015
An amorphization process in (Cu49Zr45−xAl6+x)100−y−zNiyTiz (x = 1, y, z = 0; 5; 10) induced by ball-milling is reported in the present work. The aim was investigation of the effect of Ni and Ti addition to Cu49Zr45Al6 and Cu49Zr44Al7 based alloys as well as type of initial phases on the amorphization processes. Also the milling time sufficient for obtaining fully amorphous state was determined. The entire milling process lasted 25 h. Drastic structural changes were observed in each alloy after first 5 h of milling. In most cases, after 15 h of milling the powders had fully amorphous structure according to XRD except for those ones, where TEM revealed a few nanosized crystalline particles in the amorphous matrix. In (Cu49Zr45Al6)80Ni10Ti10 alloy the amorphization process took place after 12 h of milling and the amorphous state was stable up to 25 h of milling. In the case of (Cu49Zr44Al7)80Ni10Ti10 alloy the powders have fully amorphous structure between 12 h and 15 h of milling. 相似文献
7.
《Intermetallics》2005,13(3-4):429-435
The high-cycle fatigue (HCF) behavior of the Zr41.2Ti13.8Cu12.5Ni10Be22.5 (in at.%) bulk-metallic glass (BMG) was studied. Two batches of samples that are from different lots (Batches 59 and 94) are employed in present experiments. The HCF experiments were conducted, using an electrohydraulic machine at a frequency of 10 Hz with a R ratio of 0.1 in air at room temperature and under tension-tension loading, where R=σmin./σmax.. (σmin. and σmax. are the applied minimum and maximum stresses, respectively). A high-speed and high-sensitivity thermographic-infrared (IR) imaging system was employed for the nondestructive evaluation of temperature evolutions during fatigue testing. No distinct sparking phenomenon was observed at the final fracture moment for this alloy. The fatigue lifetime of Batch 59 is longer than that of Batch 94 at high stress levels (maximum stresses >864 MPa). Moreover, the fatigue-endurance limit of Batch 59 (703 MPa) is somewhat greater than that of Batch 94 (615 MPa). The vein pattern and liquid droplets were observed in the apparent-melting region along the edge of the fractured surfaces. The fracture morphology suggests that fatigue cracks initiated from casting defects, such as porosities and inclusions, which have an important effect on the fatigue behavior of BMGs. 相似文献
8.
9.
用RE-N-C-S-V-Nb盐浴多元共渗的方法对H13钢表面进行改性处理,形成了含有钒铌碳氮化物的高性能复合层。以多元共渗渗层厚度和显微硬度作为正交试验的参考指标,对多元共渗配方成分进行优化。根据正交试验中各因素水平对指标的影响结果得到最优的成分为:硼砂盐浴中,稀土质量分数5%,V2O5质量分数6%,Nb2O5质量分数6%;盐浴回火中,稀土质量分数1%,CNO-质量分数34%。利用X射线衍射仪(XRD)和扫描电子显微镜(SEM)对多元共渗层的组成和显微结构进行了分析和研究,结果表明:共渗后试样表面形成了NbN、VN、NbC、V8C7等高性能物相和组织,渗层厚度达100~120μm且组织致密并呈弥散性分布。与常规氮化处理的试样比较,高温氧化增重速率缓慢仅为氮化处理的1/4,微裂纹出现在热疲劳循环2 000次以上。 相似文献
10.
《稀有金属(英文版)》2019,(2)
Single-pass compression tests of an aluminaforming austenite(AFA) alloy(Fe–20Cr–30Ni–0.6Nb–2Al–Mo) were performed using a Gleeble-3500 thermal–mechanical simulator. By combining techniques of electron back-scattered diffraction(EBSD) and transmission electron microscopy(TEM), the dynamic recrystallization(DRX) behavior of the alloy at temperatures of 950–1100 ℃ and strain rates of 0.01–1.00 s~(-1) was investigated. The regression method was adopted to determine the thermal deformation activation energy and apparent stress index and to construct a thermal deformation constitutive model. Results reveal that the flow stress is strongly dependent on temperature and strain rate and it increases with temperature decreasing and strain rate increasing. The DRX phenomenon occurs more easily at comparably higher deformation temperatures and lower strain rates. Based on the method for solving the inflection point via cubic polynomial fitting of strain hardening rate(h) versus strain(e) curves, the ratio of critical strain(ec) to peak strain(ep) during DRX was precisely predicted. The nucleation mechanisms of DRX during thermal deformation mainly include the strain-induced grain boundary(GB)migration, grain fragmentation, and subgrain coalescence. 相似文献
11.
《稀有金属(英文版)》2017,(3)
Nb-24Ti-18Si-2Al-2Hf-4Cr and Nb-24Ti-18Si-2Al-2Hf-8Cr alloys were prepared by arc melting in a water-cooled crucible under argon atmosphere.Microstructural characteristics and oxidation resistance of the alloys at 1250 ℃ were investigated.The results show that,when the Cr content is 4 at%,the microstructures consist of(Nb,Ti)_(ss) and Nb_5Si_3;as Cr content increases to8 at%,C14 Laves phase Cr_2Nb is formed.The isothermal oxidation tests show that the oxidation kinetics of the two alloys follow similar features.The weight gains of the two alloys after oxidation at 1250℃ for 100 h are 235.61 and198.50 mg·cm~(-2),respectively.During oxidation,SiO_2,TiO_2,Nb_2O_5 and CrNbO_4 are formed at first.Then,Ti_2Nb_(10)O_(29) is formed after oxidation for 20 min and begins to change into TiNb_2O_7 as the oxidation proceeds.SiO_2 is formed as solid state at first but later evolves into glassy state to improve the cohesion of the scale.After oxidation for 100 h,oxidation products consist of SiO_2,TiNb_2O_7,Nb_2O_5 and CrNbO_4. 相似文献
12.
《Acta Materialia》2003,51(17):5199-5209
The structure–property relationship of a spray formed Al–Y–Ni–Co alloy with two sets of processing conditions was investigated. Significant differences in tensile strength, yield strength, and high temperature ductility were observed with respect to the microstructural changes. Fracture toughness values were determined for both sets of specimens and found to be 7.5 and 5.8 MPa·m1/2, respectively. Three intermetallic phases were observed in the matrix and constitute a volume fraction of approximately 75%. It is believed that the specimens failed during fracture toughness testing by the mechanism of cleavage, observed in the Al3Y intermetallic particles. 相似文献
13.
《Acta Materialia》2002,50(3):489-497
Bulk metallic glasses with a maximum thickness (tmax) of 1.0–2.7 mm were synthesized in the Fe43Cr16Mo16(C, B, P)25 system over a wide composition range by copper mold casting. They exhibit a large supercooled liquid region (ΔTx) of 40–90 K and a high reduced glass transition temperature (Tg/Tl) of 0.54–0.60, indicating high glass-forming ability (GFA) and high thermal stability of the supercooled liquid. The critical cooling rate for glass formation was evaluated to be of the order of 102 K s−1. The bulk metallic glasses exhibited high corrosion resistance in aggressive HCl solutions. The alloying element P has a beneficial effect on corrosion resistance. 相似文献
14.
N. A. Belov O. O. Stolyarova T. I. Murav’eva D. L. Zagorskii 《The Physics of Metals and Metallography》2016,117(6):579-587
The structure and phase composition of cast and heat treated Al–Cu–Si–Sn–Pb alloys containing 6 wt % Sn, 2 wt % Pb, 0–4 wt % Cu, 0–10 wt % Si have been studied using calculations and experimental methods. Polythermal and isothermal sections are reported, which indicate the existence of two liquid phases. It was found that the low-melting phase is inhomogeneous and consists of individual leadand tin-based particles. 相似文献
15.
N. B. Pugacheva D. I. Vichuzhanin S. T. Kalashnikov A. V. Ivanov S. V. Smirnov N. Yu. Frolova 《The Physics of Metals and Metallography》2016,117(9):920-926
The material of a shell structure subjected to 20-year use under ambient conditions has been studied. The structure and mechanical characteristics of a strain-hardened AMg6 alloy, as well as the effect of subsequent holdings of this alloy for 10–3000 h at temperatures of 50, 70, 80, 100, 130, 150, 180, and 220°C, on changes in its dislocation structure and mechanical characteristics have been investigated. It has been shown that, in the structures under study, the AMg6 alloy has a cellular structure with a high density of dislocations and the ultimate strength σu = 445.5 ± 2.5 MPa, the proof stress σ0.2 = 326.5 ± 3.5 MPa, and the relative elongation δ = 11.7 ± 0.5%. Polygonization in the alloy occurs at a temperature of 220°C and the initial stage of the recovery process corresponds to a temperature range of 50–100°С in which the softening process can be divided into two stages, i.e., stage (1) of active softening due to the interaction of point defects with each other and stage (2) of the stabilization of the characteristics of the alloy. 相似文献
16.
《International Journal of Cast Metals Research》2013,26(1-4):264-267
AbstractAn Fe–Mo–Cr–Mn–Si–C alloy was prepared in an induction furnace and was cast into cylindrical rod in a copper mould in castmatic equipment (low pressure casting). A single phase non-equilibrium featureless (no visible microstructures after deep etching) phase was observed over a certain range of thickness of the rod. In this present work, the extent of the featureless phase was studied with different concentrations of Mo (5–25 wt-%) for 5·5 mm diameter of cylindrical rod at a cooling rate of 1100 K s–1. Light optical microscopy, scanning electron Microscopy and Vickers hardness tests were used to analyse the samples. The amount of the featureless area varies as the Mo content changes and the maximum featureless area was obtained for 7 wt-% of Mo. This single phase featureless structure exhibits very high hardness (>1350 HV) which can be used in many interesting applications with or without suitable heat treatments. 相似文献
17.
《中国有色金属学会会刊》2022,32(4):1070-1082
The effect of quenching rate on the aging precipitation behavior and properties of Al–Zn–Mg–Cu–Zr–Er alloy was investigated. The scanning electron microscopy, transmission electron microscopy, and atom probe tomography were used to study the characteristics of clusters and precipitates in the alloy. The quench-induced η phase and a large number of clusters are formed in the air-cooled alloy with the slowest cooling rate, which contributes to an increment of hardness by 24% (HV 26) compared with that of the water-quenched one. However, the aging hardening response speed and peak-aged hardness of the alloy increase with the increase of quenching rate. Meanwhile, the water-quenched alloy after peak aging also has the highest strength, elongation, and corrosion resistance, which is due to the high driving force and increased number density of aging precipitates, and the narrowed precipitate free zones. 相似文献
18.
19.
《Acta Materialia》2003,51(17):5223-5234
A group of Ti–Cu–Ni–Sn–Ta multicomponent alloys is prepared by copper mold casting and arc melting, respectively, in which nanostructured (or ultrafine-grained) matrix-dendrite composites can be obtained. With increasing Ti and Ta contents, the volume fraction of the dendritic phase increases. The grain size of the matrix phase depends on the preparation method, and is 30–70 nm for as-cast 2–3 mm diameter cylinders and about 100–200 nm for the as-arc melted samples. Compression test results indicate that fully nanostructured samples exhibit very high yield strength of 1800 MPa with a limited plastic strain of 1.4%. The nanostructure-dendrite composites exhibit high yield strengths of 1525–1755 MPa together with large plastic strains of 4.7–6.0%. The as-arc melted samples exhibit relatively lower yield strengths of 1037–1073 MPa with very large plastic strains of 16.5–17.9% because of the coarser grain size of the matrix. The large plasticity of the composites is attributed to the retardation of localized shear banding and the excessive deformation in the nanostructured matrix due to the in situ formed dendrites. The deformation and the fracture mechanisms of the nanostructure-dendrite composites are discussed based on fractography observations. 相似文献
20.
《Scripta materialia》2003,48(5):559-563
The phase fields of the Laves phase in the Cr–Zr–Nb and Cr–Zr–Hf alloy systems were investigated at 1573 K. The Laves phase formed in the Cr–Zr–Nb alloy system had a broad off-stoichiometric range in the center of ZrCr2–NbCr2 pseudo-binary line, while the Laves phase formed in the Cr–Zr–Hf alloy system had a uniform and limited off-stoichiometric range along ZrCr2–HfCr2 pseudo-binary line. The results are discussed, in terms of geometric concept of atomic sizes of the constituent atoms. 相似文献