PP-g-GMA对长玻纤增强聚丙烯复合材料性能的影响

采用熔体浸渍工艺制备了长玻纤(LGF)增强聚丙烯材料。研究了甲基丙烯酸缩水甘油酯接枝聚丙烯(PP-g-GMA)对长玻璃纤维增强聚丙烯(PP)复合材料力学性能的影响。结果表明:PP-g-GMA影响长玻璃纤维增强PP复合材料的力学性能;当PP-g-GMA质量分数为1%时,PP/LGF复合材料的力学性能最好,拉伸强度、弯曲强度和悬臂梁缺口冲击强度分别提高32.34%、27.38%和74.51%。     

长玻璃纤维增强聚丙烯复合材料的力学性能研究

采用熔体浸渍技术制备了长玻璃纤维母料(LGF/PP-g-MAH/PP)增强聚丙烯(PP)复合材料(LGF/PP)。通过双螺杆挤出机制备了同等配比的短玻纤增强聚丙烯(SGF/PP)复合材料。研究了LGF含量、环氧树脂(EP)和固化剂(2E4MZ)对LGF/PP复合材料的力学性能影响。结果表明:当LGF质量分数为35%～40%时,LGF/PP的综合力学性能最好,且明显优于同样组成的SGF/PP复合材料。EP和含固化剂(2E4MZ)的EP对LGF/PP复合材料的力学性能提高有一定的作用。SEM照片分析表明:EP的加入能改善玻纤与聚丙烯基体的界面粘接。     

热氧老化对长玻璃纤维增强聚丙烯复合材料的力学性能影响

将熔融浸渍制备的长玻璃纤维(LGF)增强聚丙烯(PP)与PP按照不同比例熔融共混,制备了不同LGF含量的LGF增强PP复合材料。研究了老化时间、LGF含量对LGF增强PP复合材料力学性能的影响。结果表明：随着LGF含量的增加,LGF增强PP复合材料的断裂伸长率稍有下降,拉伸强度、弯曲强度、弯曲模量、冲击强度及缺口冲击强度都显著提高。老化时间的延长,对低LGF含量的LGF增强PP复合材料的力学性能影响不大;老化时间较长时,高LGF含量的LGF增强PP复合材料的总体力学性能有所下降。     

长玻纤增强聚丙烯复合材料力学性能的研究

通过熔体浸渍法制备了一定玻纤含量的长玻纤增强聚丙烯(PP/LGF)母粒,然后将一定配比的母粒与PP通过注射机注塑成样条,研究了LGF用量及相容剂、增韧剂的添加对PP/LGF复合材料力学性能的影响。结果表明:当LGF用量为35%左右时,PP/LGF复合材料的力学性能达到最佳,较之纯PP显著提升。相容剂的加入改善了PP/LGF复合材料的力学性能,并且提高了LGF和PP之间的黏结力。增韧剂的加入使得复合材料的拉伸强度、弯曲强度和弯曲模量呈现下降的趋势,冲击强度则随增韧剂用量的增加逐渐提升。     

反应挤出PP/LGF复合材料的制备及性能

采用熔融浸渍工艺制备了长玻纤增强聚丙烯复合材料,研究了接枝单体GMA、MA以及引发剂DCP含量对长玻璃纤维增强聚丙烯复合材料力学性能的影响。结果表明:与采用接枝单体GMA相比,采用接枝单体MA反应挤出PP/LGF复合材料的力学性能对引发剂DCP的用量更为敏感,严重影响了PP/LGF复合材料的力学性能;当引发剂DCP质量分数为0.1%,采用接枝单体MA反应挤出PP/LGF复合材料性能最优,并且与没有添加相容剂的PP/LGF复合材料相比,拉伸强度、冲击强度分别提高31%、50%。     

剑麻纤维/玻璃纤维混杂增强聚丙烯复合材料的结构与性能

采用熔融共混和模压成型方法将废剑麻纤维(SF)和玻璃纤维(GF)混杂增强聚丙烯(PP)制备SF/GF/PP木塑复合材料.研究复合材料力学性能、热性能、晶型结构和微观结构,探讨混杂纤维增强基体树脂的界面行为.结果表明:所制得复合材料的冲击强度、弯曲强度和弯曲模量都有不同程度的提高.同时,热稳定性、PP相的结晶速率及结晶度也有所提高,晶态结构无变化,仍是典型的α晶型.     

长纤维增强PP复合材料的制备与性能研究

通过开炼–模压成型工艺方法,制备了长玻璃纤维(LGF)增强聚丙烯(PP)复合材料,首先研究了β成核剂对纯PP力学性能和结晶性能的影响,在此基础上研究了LGF对PP/LGF复合材料力学、结晶性能及热稳定性的影响,最后探讨了增容剂马来酸酐接枝三元乙丙橡胶(EPDM-g-MAH)对复合材料力学性能的影响。结果表明,β成核剂可以改善PP的冲击韧性,但降低了PP的拉伸和弯曲强度,当β成核剂质量分数为0.2%时,PP的综合性能最好;随LGF含量增加,PP/LGF复合材料的拉伸、弯曲和冲击强度及结晶度总体上呈先增大后减小的趋势,不同LGF含量下的复合材料起始热分解温度均在390℃以上,当LGF质量分数为20%时,复合材料的综合性能最好;少量的EPDM-g-MAH能改善LGF与PP基体的界面相容性,大幅增强了复合材料的韧性,其最适宜的质量分数为10%。     

长纤混杂增强复合材料注塑成型的微观结构演化

采用熔体浸渍拉挤工艺(LFT-G)制备长碳纤/玻纤混杂增强聚丙烯(LCF/LGF/PP)复合材料。首先研究了纤维表面处理、微观形貌、界面结合状态对复合材料力学性能的影响,并研究了纤维不同混配比对复合材料力学性能的影响。结果表明,纤维经表面处理,增加了与基体的机械啮合作用,改善了界面结合形貌,提高了复合材料的力学性能。与单一纤维增强复合材料相比,混杂增强纤维更易形成随机取向的三维骨架结构。且碳纤和玻纤混合质量比为2∶1时,其注塑制品获得相对较高的强度、韧性和刚度,同时具有相对较低的成本。     

注塑条件对长玻纤增强聚丙烯性能影响研究

利用熔融浸渍装置,采用长玻纤(LGF)增强双马来酰亚胺等改性的聚丙烯(PP),制备了LGF增强PP复合材料。研究了在螺杆转速为80～250 r/min、背压为8～10 MPa的注塑条件下,复合材料的纤维长度、力学性能与热变形温度的变化。在研究范围内,注塑工艺参数的变化对复合材料的弯曲强度和热变形温度没有明显的影响,但随着螺杆转速的提高,纤维长度下降,所得复合材料的冲击强度先降低后升高。     

全塑尾门长玻纤增强聚丙烯的制备及性能研究

以聚丙烯(PP)树脂为基体,玻璃纤维(GF)为增强材料,通过特制的浸渍设备制备长玻璃纤维(LGF)增强PP复合材料PP-LGF。考察了GF的含量、PP树脂的熔体流动速率以及表面极性剂(HT-17)含量对复合材料力学性能和黏结性能的影响。结果表明,复合材料的力学性能随GF含量的增加而增大,且基体树脂的流动性越好,复合材料力学性能越优异;添加表面极性剂能大幅度提高复合材料黏结性能,当其添加的质量分数为3%时,LGF质量分数40%的复合材料的表面张力为48mN/m,制品的剪切强度为1.65kJ/m2,界面破坏形式为80%胶内聚破坏,复合材料的综合性能满足全塑尾门要求。     

Effect of impregnation time on performance of long glass fiber‐reinforced polypropylene composites

Long glass fiber (LGF)‐reinforced polypropylene (PP) composites were prepared using self‐designed impregnation device. Effects of impregnation time on mechanical properties, crystallization, dynamic mechanical properties, and morphology of PP/LGF composites were investigated. The experiment results demonstrate that the excellent tensile strength, Notched Izod impact strength was 152.9 MPa, 31.2 KJ/m², respectively, and the stiffness of PP/LGF composites was higher, when the impregnation time was 7.03 s. The excellent interfacial adhesion between PP and glass fiber indicates that PP/LGF composites possess the outstanding mechanical properties. The impregnation time scarcely influenced thermal properties of PP/LGF composites. J. VINYL ADDIT. TECHNOL., 24:174–178, 2018. © 2016 Society of Plastics Engineers     

Performance of long glass fiber‐reinforced polypropylene composites at different injection temperature

Long glass fiber‐reinforced polypropylene composites were prepared using self‐designed impregnation device. Effects of the different injection temperature on mechanical properties, crystallization, thermal, and dynamic mechanical properties of long glass fiber‐reinforced polypropylene composites were discussed. The differential scanning calorimetry (DSC) results indicate that the melting peak temperature of PP/LGF composites gradually reduced, however, the crystallinity of PP/LGF composites gradually increased with increasing injection temperature. Thermo‐gravimetric analyzer (TGA) results demonstrate that with increasing injection temperature, the temperature of the PP/LGF composites melt increased, the viscosity of the PP/LGF composites melt lowered, the mold filling of the PP/LGF composites melt was easy, the shear force of glass fiber was relatively low, which made the residual length of glass fiber in products increase. Dynamic thermal mechanical analyzer (DMA) results show that the storage modulus of PP/LGF composites is the highest while the injection temperature is at 290°C, and the peak value of tan σ of PP /LGF composites at 290°C is minimal, which indicates that the mechanical properties of PP /LGF composites at 290°C is the best. What' more, the injection temperature at 290°C significantly ameliorated “glass fiber rich skin” of products of glass fiber‐reinforced composites. J. VINYL ADDIT. TECHNOL., 24:233–238, 2018. © 2016 Society of Plastics Engineers     

长玻璃纤维增强PA66复合材料的综合性能及其影响因素研究

利用定制的熔融浸渍装置制备了长玻璃纤维增强聚酰胺66(PA66/LGF)复合材料,并对其力学性能、界面黏结性等进行了表征,探讨了玻璃纤维含量、润滑剂含量、相容剂含量以及切粒长度等因素对复合材料性能的影响,得到了PA66/LGF复合材料优化的配方设计与切粒长度.结果表明,当玻璃纤维含量为43％(质量分数,下同)、切粒长度...     

悬浮浸渍拉挤成型长玻纤增强ABS复合材料工艺研究

摘要：浮液浸渍玻璃纤维，烘干，熔融状态下拉挤成棒型，切粒，注射成型。研究了玻纤用量对复合材料力学性能的影响。研究结果表明，复合材料的冲击强度、拉伸强度随玻纤用量的增加而提高。悬浮法是较好的制备纤维增强ABS复合材料的方法。     

超支化聚合物对聚丙烯/剑麻纤维复合材料性能影响

为改善剑麻纤维(SF)与聚丙烯(PP)之间的相容性,在PP/SF复合材料中添加超支化聚酯(H101)、超支化环氧树脂(E102),研究了两种超支化聚合物(HBP)的热稳定性及对PP/SF复合材力学性能、熔体流动性和微观形貌的影响。热重分析表明,所使用的HBP均具有较好的热稳定性;扫描电子显微镜分析发现,HBP的加入使基体与纤维结合得更加紧密;力学性能测试表明,H101可不同程度地提高复合材料的拉伸、弯曲及冲击强度;E102可提高复合材料的拉伸及冲击强度,当E102含量为10%时,与PP/SF复合材料相比,冲击强度提高了72.24%。尽管HBP含量较高时复合材料的力学性能提高,但HBP会降低复合材料的熔体流动速率,选择HBP含量时需要综合考虑。     

UV老化对ZnO填充PA6/LGF复合材料性能的影响

用熔融共混法制备出长玻璃纤维(LGF)含量为30%的LGF增强尼龙6(PA6)/ZnO(PA6/LGF/ZnO)复合材料,并采用氙灯紫外(UV)老化法研究了ZnO含量为0%~8%及UV老化时间为0~800 h对复合材料力学性能和结晶性能的影响。结果表明,经UV辐照后,PA6/LGF/ZnO复合材料的拉伸强度升高,韧性下降,其中当ZnO添加量为6%时,复合材料在800 h老化后的拉伸强度和缺口冲击强度保留率较未添加ZnO的复合材料分别提高了5.39%和4.98%。SEM分析表明在UV老化过程中,LGF与PA6基体之间的界面并未受到明显破坏,老化主要集中发生在PA6基体上。随着老化时间的延长,PA6/LGF复合材料中的PA6出现UV交联而使其结晶度从26.19%降低至20.70%;对于ZnO含量为6%的PA6/LGF/ZnO复合材料,老化800 h后其结晶度仅从22.92%下降至21.34%,PA6/LGF/ZnO复合材料整体上的结晶性能趋于稳定。     

剑麻纤维/聚丙烯木塑复合材料的热氧老化性能研究

以剑麻纤维(SF)、聚丙烯(PP)为原料,经熔融共混、模压成型工艺制备木塑复合材料。探讨了SF/PP复合材料的力学性能、热性能随老化时间和SF含量的变化规律,借助扫描电镜对复合材料老化前后的冲击断面进行微观结构分析。结果表明:老化后复合材料的冲击强度、弯曲强度和弯曲模量随剑麻含量的增加而降低;同时,复合材料中PP相的结晶速率、结晶度也有所降低,但复合材料的热稳定性基本没有变化。