Preparation of Sb Doped Nano SnO2/Porous Ti Electrode and Its Degradation of Methylene Orange

利用热分解方法在多孔钛上制备了Sb掺杂纳米SnO2电极。也研究了该电极降解甲基橙的电化学性能。SEM和XRD测试表明,在多孔钛基体上可获得完整的、无裂缝的涂层。无裂缝的涂层表面由粒径范围在80~230 nm的Sb掺杂SnO2纳米颗粒组成。HRTEM测试结果表明,SnO2纳米颗粒由5~6 nm细小颗粒构成。在其余条件相同的情况下,强化寿命试验表明,Sb掺杂纳米SnO2 /多孔Ti电极的寿命远大于致密钛基体上的电极。Sb掺杂纳米SnO2 /多孔Ti电极可将浓度为100 mg/L的甲基橙溶液降解到8 mg/L,显示出该电极具有很强的有机物污染物电催化降解能力。并指出采用简单的表面处理技术,将使多孔钛具有很高的潜力被应用到有机污水降解领域     

锡锑中间层的铕掺杂量对 Ti / PbO2电极性能的影响

采用涂层热解法在Ti基体表面制备不同掺杂量的铕掺杂锡锑中间层,并在锡锑中间层的表面电镀上PbO2。对所制备的电极作LSV曲线,研究了电极的电化学性能;以对硝基苯酚为目标有机物,考察了电极的电催化活性;采用SEM,XRD等分析方法表征了电极中间层的形态、元素组成和结构组成,据此分析了电极的性质。结果表明,铕掺杂量对电极的各项性能有较大影响,制备电极时以n(Sn)∶n(Sb)∶n(Eu)=1∶0.1∶0.01为佳,该掺杂量下得到的电极析氧电位和电催化能力较高,表面涂层结构和覆盖度较好,电化学寿命达78.6 h。     

TiO2-SnO2复合电极的制备及性能

以钛酸丁酯为先驱体、无水乙醇为溶剂、二乙醇胺为鳌合剂,采用溶胶-凝胶浸渍提升法制备钛基TiO2-SnO2复合电极.借助于含油废水化学需氧量(COD)的去除效果和紫外吸收光谱考察了电极的电催化氧化能力.并采用SEM、XRD和EDX等表征方法分析了Sn的掺杂对所制备电极表面形貌、涂层晶体结构和电极表层的元素组成的影响,通过电化学线性伏安扫描测定了其析氧电位,分析了电极结构与电催化特性之间的关系.结果表明,当热处理温度为500℃时,所制备电极的涂层中TiO2主要为锐钛矿型,掺杂适量Sn后,电极的表面变得更加平滑、致密,涂层表面晶粒明显细化.当Sn的摩尔掺杂比为n(Ti):n(Sn)=100:10时,复合氧化物涂层电极的电催化性能最好,电极的析氧电位为2.1 V,此电极处理含油废水60 min时,COD去除率达到了87.5%,较未添加Sn的电极相比对COD的去除率提高了26.7%,这说明掺杂适量的Sn提高了电极的催化性能.     

Sb掺杂纳米SnO_2/多孔Ti电极的制备及其降解甲基橙性能（英文）

利用热分解方法在多孔钛上制备了Sb掺杂纳米SnO2电极。也研究了该电极降解甲基橙的电化学性能。SEM和XRD测试表明,在多孔钛基体上可获得完整的、无裂缝的涂层。无裂缝的涂层表面由粒径范围在80~230 nm的Sb掺杂SnO2纳米颗粒组成。HRTEM测试结果表明,SnO2纳米颗粒由5~6 nm细小颗粒构成。在其余条件相同的情况下,强化寿命试验表明,Sb掺杂纳米SnO2/多孔Ti电极的寿命远大于致密钛基体上的电极。Sb掺杂纳米SnO2/多孔Ti电极可将浓度为100 mg/L的甲基橙溶液降解到8 mg/L,显示出该电极具有很强的有机物污染物电催化降解能力。并指出采用简单的表面处理技术,将使多孔钛具有很高的潜力被应用到有机污水降解领域。     

La掺杂的SnO2-Sb中间层对钛基IrO2+Ta2O5电极性能的影响

目的改善Ti/IrO_2+Ta_2O_5涂层电极的析氧电催化性能。方法用热分解法在钛基材上制备了La掺杂的SnO_2-Sb中间层,并以此作为基体涂覆IrO_2+Ta_2O_5活性层,制备了Ti/SnO_2-Sb-La/IrO_2+Ta_2O_5涂层电极。采用扫描电子显微镜(SEM)、能量散射能谱(EDS)及X-射线衍射光谱(XRD)技术分别分析了中间层和活性层的表面形貌、元素组成及晶相结构。采用线性扫描伏安曲线(LSV)和强化寿命测试方法在硫酸溶液中分别研究了Ti/SnO_2-Sb-La/IrO_2+Ta_2O_5涂层电极的析氧电催化活性和使用稳定性。同时,考察了La的掺杂比例对Ti/SnO_2-Sb-La/IrO_2+Ta_2O_5电极强化寿命的影响。结果相对未掺杂La的中间层,掺杂La后的中间层表面裂纹减少,有更高的析氧过电位和更低的析氧电流密度。La掺杂对活性层的表面形貌和晶相结构基本没有影响,但电极的析氧电流密度有所提高。通过测试不同La掺杂比例涂层电极的强化寿命,发现La最佳掺杂比例为nLa:nSn=0.5:100。和未掺杂La涂层相比,La最佳掺杂比例涂层电极的强化寿命提高了22.8%。结论相对于未掺杂的Ti/SnO_2-Sb/IrO_2+Ta_2O_5电极,La掺杂后的Ti/SnO_2-Sb-La/IrO_2+Ta_2O_5涂层电极析氧电催化活性和强化寿命都得到改善。     

SnO_2-Sb_2O_3-RuO_2/Ti电极制备及其性能研究

采用热分解法制备了SnO_2-Sb_2O_3-RuO_2/Ti电极,并将其用于苋菜红模拟染料废水处理。实验表明电极制备的最佳条件为:烧结温度为500℃,涂层数为6层,n(Sn):n(Sb):n(Ru)=10:1:1。通过XRD、SEM和CV对电极表面形貌、表面微观结构和电化学性能进行测试,结果表明:SnO_2-Sb_2O_3-RuO_2/Ti电极表面晶体为四方金红石结构且晶型单一;表面晶粒细小平整,晶粒间结合紧密;具有较好的电催化活性和较长的强化试验寿命。     

新型二氧化铅电极的制备及其性能研究

用电沉积方法制备了Ti/SnO2+Sb2O3/PbO2,Ti/SnO2+Sb2O3/Bi-PbO2,Ti/PbO2三种二氧化铅电极,采用加速寿命试验对比了电极的寿命,采用扫描电镜表征了电极的表面形貌,并将所制备的电极用于处理苯酚溶液和含铜离子的溶液,分析了电解处理的效果.结果表明:未掺铋二氧化铅电极的加速寿命最长,且其处理的含铜废水可达国家排放标准,但掺铋电极的电催化性能更高.     

新型Nd掺杂PbO2阳极性能及对AOII的电催化氧化研究

采用电沉积法制备了稀土金属Nd改性PbO2电极（Nd-PbO2）,并通过扫描电镜（SEM）、X射线衍射（XRD）、X射线光电子能谱（XPS）、荧光光谱（FP）、线性极化扫描（LSV）、强化寿命测试（ALT）、循环伏安扫描（CV）等方法表征了其表面结构和电化学性能,探讨了对酸性橙II（AOII）的电催化氧化性能。SEM、XRD、XPS测试结果表明,Nd以Nd3 形式掺杂进入电极镀层,同时对表面形貌、元素组成均有不同程度的改变,但不改变镀层表面的β-PbO2晶型;电化学性能测试表明,Nd掺杂可有效提高电极的析氧电位和稳定性;CV测试及AOII降解实验结果表明,Nd-PbO2电极对AOII还表现出直接氧化作用,电催化氧化AOII能力更强;FP分析表明,Nd-PbO2具有较强的催生羟基自由基能力,可增强电极降解有机物的催化活性。     

钛基热氧化对钛阳极组织与性能的影响

将工业纯钛TA1在400～800 ℃热氧化1 h,然后用热分解方法制备RuO230%-TiO270%涂层.通过XRD、SEM分析了热氧化处理后钛基体及所制备电极的组织结构和形貌特征,采用极化曲线和循环伏安两种方法评定电极的电催化性能,用强化测试研究了这几种电极的稳定性.结果表明,随着热氧化温度的升高,基体表面的组织结构和形貌会发生变化;对应于制备的电极的电催化活性和稳定性也发生明显的变化,600 ℃以下热氧化基体制备的电极各项性能较好,500 ℃是最好的热氧化温度,制备的电极电催化活性和稳定性最好.     

La掺杂对Ti/Sb-SnO2电极改性机制的研究：电化学分析

为研究稀土掺杂对Ti/Sb-SnO_2催化电极的改性机理,采用溶胶凝胶法制备了La掺杂Ti/Sb-SnO_2电极,以苯酚为目标有机物,考察了电极的电化学性能。极化曲线和Mott-Schottky分析表明:La改性Ti/Sb-SnO_2电极的析氧电位先增大后减小,且在2.0 V电位下Sn:Sb:La(摩尔比)为100:10:1.5时电极交换电流密度值最大;改性后电极的平带电势负移,Mott-Schottky拟合直线斜率从2.96降为1.66,活性表面积增大,载流子浓度提升。循环伏安和交流阻抗分析表明:掺杂后电极电化学反应电阻减小,活性电荷由14.1μF提升至322μF;苯酚直接氧化峰电流增大,峰电位减小。以上结果解释了电极电催化活性提升的内在原因。     

不同前驱体制备的锡锑中间层对Ti／SnO2＋Sb2O3／PbO2电极性能的影响

研究了以乙二醇与柠檬酸反应制得的乙二醇柠檬酸酯溶液、乙二醇、乙醇、正丁醇为前驱体溶剂制备的锡锑中间层对Ti/SnO2 Sb2O3/PbO2电极性能的影响,用XRD、ESEM对不同前驱体制备的锡锑中间层和对应的二氧化铅活性层进行了表征,并用极化曲线法和阳极寿命快速检测法比较了不同前驱体对Ti/SnO2 Sb2O3/PbO2电极的阳极寿命和在1．0mol/L硫酸溶液中的电催化活性的影响。结果表明,不同前驱体溶剂对锡锑中间层的结构和形貌有着显著的影响;以乙二醇与柠檬酸反应制得的聚合前驱体为溶剂制备的锡锑中间层表面致密,锡锑含量相对较高,该中间层的均匀度和平整度明显好于其它3种前驱体。由聚合前驱体中间层制得的Ti/SnO2 Sb2O3/PbO2电极的使用寿命明显提高,但不同中间层前驱体对电极的电催化活性影响不大。     

Photoelectrocatalytic activity of two antimony doped SnO2 films for oxidation of phenol pollutants

Two types of Sb-doped SnO2 films on titanium substrate were prepared by the combination of electro-deposition and dip-coating (Ti/SnO2-Sb2O4/SnO2-Sb2O4) and single dip-coating (Ti/SnO2-Sb2O4), respectively. The surface morphology and crystalline structure of both film electrodes were characterized using X-ray diffractometry(XRD) and scanning electron microscopy(SEM). XRD spectra indicate that the rutile SnO2 forms in two films and a TiO2 crystallite exists only in Ti/SnO2-Sb2O4 electrode. SEM images show that the surface morphology of two films is typically cracked-mud structure. The photooxidation experiment was proceeded to further confirm the two electrode activity. The results show that the photoelectrocatalytic degradation efficiency of Ti/SnO2-Sb2O4 electrode with sub-layer is higher than that of simple Ti/SnO2-Sb2O4 electrode using phenol as a model organic pollutant. The Ti/SnO2-Sb2O4/SnO2-Sb2O4 photoanode has a better photoelectrochemical performance than Ti/SnO2-Sb2O4 photoanode for the removal of organic pollutants from water.     

Electro-catalytic degradation properties of Ti/SnO<Subscript>2</Subscript>–Sb electrodes doped with different rare earths

Ti/SnO₂–Sb electrode has a good effect on the removal of organic pollutants. But its short service life limits its large-scale application in industry. Electro-catalytic degradation performances and service life of the electrode can be significantly improved by doping rare earth (RE) ions into the oxide coating of Ti/SnO₂–Sb electrode. Ti/SnO₂–Sb electrodes doped with different RE elements (Ce, Dy, La, and Eu) were prepared by the thermal decomposition method at 550 °C. Electro-catalytic degradation performances of electrodes doped with different RE elements were evaluated by linear sweep voltammetry (LSV) and Tafel curves. During the electrolysis, the conversion of p-nitrophenol was performed with these electrodes as anodes under galvanostatic control. The structures and morphologies of the surface coating of the electrodes were characterized by scanning electron microscope (SEM). The results demonstrate that the electro-catalytic degradation performances of Ti/SnO₂–Sb electrodes are improved to different levels by doping different RE ions. Improved Ti/SnO₂–Sb electrodes by the introduction of different RE have higher oxygen evolution potential, better electro-catalysis ability, better coverage, and longer electrode life.     

超声掺Bi二氧化铅电极电氧化降解2-氯苯酚研究

目的提高Pb O_2/Ti的使用寿命、对目标反应物的电氧化催化活性及选择性。方法以覆有Sn O_2+Sb_2O_3的Ti网为阳极,分别在Pb(NO_3)_2、Na F混合溶液及Pb(NO_3)_2、Na F、Bi(NO_3)_3组成的掺Bi混合溶液中,在电沉积液p H=2、60℃、电沉积电流密度为0.04 A/cm~2的条件下,进行常规电沉积及超声电沉积1 h,制备出Pb O_2/Sn O_2+Sb_2O_3/Ti,Bi-Pb O_2/Sn O_2+Sb_2O_3/Ti,Pb O_2(ultrasonic)/Sn O_2+Sb_2O_3/Ti,Bi-Pb O_2(ultrasonic)/Sn O_2+Sb_2O_3/Ti 4类二氧化铅电极。在硫酸溶液中测定其加速寿命,用稳态极化曲线分析电催化性及选择性,以2-氯苯酚的电氧化降解反应为模型反应,考察电解2-氯苯酚废水的处理效果,用X射线衍射仪和电子扫描电镜表征沉积层晶相和形貌。结果 Bi-Pb O_2(ultrasonic)/Sn O_2+Sb_2O_3/Ti的加速寿命比Pb O_2/Sn O_2+Sb_2O_3/Ti提高了54%。电氧化降解2-氯苯酚溶液4 h后,以掺Bi二氧化铅电极为阳极,相比于二氧化铅电极,对2-氯苯酚的脱除率提高了19%,槽压降低了7%,稳态极化曲线和电氧化降解2-氯苯酚溶液试验反映了相同的结论。结论超声波环境和Bi掺杂显著提升电极的性能,掺Bi的二氧化铅沉积层表现出较高的电催化性和电氧化2-氯苯酚的选择性,超声电沉积二氧化铅能增大电极比表面积,提高电极的表观催化活性和电极加速寿命。     

稀土Ce掺杂Ti/Sb-SnO2电极的电化学性能及应用

采用热分解法制备Ti/Sb-SnO2电极和Ti/Sb-SnO2/Ce电极,采用扫描电子显微镜(SEM)、X射线衍射(XRD)仪和电化学实验技术对电极的表面形貌、物相组成和电化学性能进行表征。结果表明:Ti/Sb-SnO2电极表面形成了SnO2晶胞,经稀土Ce改性后SnO2晶粒明显细化,SnO2衍射峰强度变强且峰形宽化。Ti/Sb-SnO2/Ce电极峰电流值最大、表面稳定性增强和催化活性明显提高。在最佳工艺条件下,Ti、Ti/Sb-SnO2和Ti/Sb-SnO2/Ce电极对橙黄G目标污染物的去除率分别为46.6%、61.9%和94.9%,且降解过程均符合一级反应动力学模型,速率常数分别为0.0289、0.0633、0.1971min-1,Ti/Sb-SnO2/Ce电极的速率常数分别是Ti/Sb-SnO2电极的3倍,Ti电极的7倍,表明在电极表面涂层中掺杂稀土元素Ce可有效提高电极的性能。     

耐酸非贵金属Ti／MO2阳极SnO2＋Sb2O4中间层研究

采用热分解法制备了非贵金属Sn02＋Sb204中间层Ti基MO2活性层电极，利用SEM，XRD和XPS方法对中间层进行了表征。测定了Ti／SnO2＋Sb2Od／MnO2和Ti／SnO2＋Sb2O4／PbO2电极在硫酸溶液中的析氧极化曲线，二者起始析氧过电位均比贵金属小；考察了在高电流密度（4A／cm^2）下的加速寿命，二者依次分别达到18h和86h。实验表明，SnO2＋Sb2O4是一种具有良好导电性和结合力的耐酸Ti基MO2电极中间层材料。     

十二烷基硫酸钠对IrO2-Ta2O5/SnO2- Sb-Mn/Ti电极电催化性能影响

采用涂刷-热分解法制备不同浓度阴离子表面活性剂十二烷基硫酸钠（SDS）的IrO2-Ta2O5/SnO2- Sb-MnO2/Ti电极,通过扫描电子显微镜（SEM）和X射线衍射仪（XRD）对其微观形貌及物相组成进行分析;应用循环伏安、极化等测试手段,表征制备电极的电催化活性.结果表明,适量添加十二烷基硫酸钠能够改善IrO2-Ta2O5/SnO2-Sb-Mn/Ti电极的微观形貌,提高电催化活性.在本实验条件下,SDS最佳添加量是1.6 g/L,结晶化度高达99.83%.利用苯酚电催化降解实验和强化寿命测试进一步考察所制电极的电催化活性与稳定性,结果显示,在电流密度15 mA/cm2条件下电解180 min,SDS的加入使苯酚去除率由原来的68.5%提高到79.2%.COD去除率由60.1%提高到 67.5%,电催化性能得到提升,电极强化寿命由52 h延长至68 h.