Effect of clay modification on the structure and properties of sulfonated poly(ether ether ketone)/clay nanocomposites

Sulfonated poly(ether ether ketone) (SPEEK)/clay hybrid membranes were prepared using three types of commercially available clays, the sodium montmorillonite (IC), hydrophobic organo‐clay with long alkyl chains (OC), and organo‐clay with carboxylic acid end groups (HC). It was found that the SPEEK/HC hybrid membranes achieved the best clay dispersion, with the exfoliation of the clay nano‐platelets when the filler loading was < 10 wt%. The incorporation of the carboxylic acid groups in clay layers also improved the connectivity between the ionic clusters in the membrane, resulting in higher proton conductivity without compromising the dimensional stability of membranes. The selectivity higher than the pristine SPEEK membranes was obtained for the SPEEK/HC hybrid membranes at low filler loading (<10 wt%), with higher proton conductivity and similar methanol permeability. POLYM. COMPOS., 37:2632–2638, 2016. © 2015 Society of Plastics Engineers     

Incorporating of layered double hydroxide/sepiolite to improve the performance of sulfonated poly(ether ether ketone) composite membranes for proton exchange membrane fuel cells

Sulfonated poly(ether ether ketone) (SPEEK) with a low sulfonation degree was blended using nanofiller layered double hydroxide (LDH, Mg₂AlCl)/sepiolite nanostructured material as additive to use as an electrolyte membrane for fuel cell application. Characterization assessments, that is, mechanical stability, thermal gravimetric analysis, ion exchange capability, swelling properties, water uptake capacities, electrochemical impedance spectroscopy analysis, and Fourier transform infrared spectroscopy of the composite membranes were conducted. The presence of LDH/sepiolite nanoarchitectured material within SPEEK was found to have the highest water retention and proton conductivity value at high temperature rather than LDH/SPEEK and pristine SPEEK membranes.     

Sulfonated Poly (Ether Ether Ketone) / Barium Strontium Titanium Oxide Polymer Nanocomposite Membranes for Fuel Cell Applications

ABSTRACT

Polymer nanocomposite membranes based on sulfonated poly (ether ether ketone) (SPEEK) and barium strontium titanium oxide (BSTO) have been prepared by solution casting technique. The SPEEK was obtained by direct sulfonation of poly (ether ether ketone) using concentrated sulfuric acid. The degree of sulfonation of SPEEK was determined by ¹H NMR spectroscopy. The composite membranes showed higher water uptake capacity when compared to SPEEK. The ion-exchange capacity of the composite membranes was found in the range between 1.48 and 1.62 meq. g^?1. The thermal stability of composite membrane was found to be good enough to use in fuel cell.     

Sulfonated poly(ether ether ketone)/epoxy/phenol novolac blend proton‐exchange membranes with low methanol permeability

A crosslinked epoxy [4,4′‐diglycidyl‐(3,3′,5,5′‐tetramethylbiphenyl) epoxy resin (TMBP)], cured by phenol novolac (PN), was introduced into a sulfonated poly(ether ether ketone) (SPEEK) membrane (ion‐exchange capacity = 2.0 mequiv/g) with a casting‐solution, evaporation, and heating crosslinking method to improve the mechanical properties, dimensional stability, water retention, and methanol resistance. By Fourier transform infrared analysis, the interactions between the sulfonic acid groups and hydroxyl groups in the blend membranes were confirmed. The microstructure and morphology of the blend membranes were investigated with atomic force microscopy. As expected, the blend membranes showed excellent mechanical properties, good thermal properties (thermal stability above 200°C), lower swelling ratios (1.4% at 25°C and 7.0% at 80°C), higher water retention (water diffusion coefficient = 9.8 × 10^?6 cm²/s), and a lower methanol permeability coefficient (3.6 × 10^?8 cm²/s) than the pristine SPEEK membrane. Although the proton conductivity of the blend membranes decreased, a higher selectivity (ratio of the proton conductivity to the methanol permeability) was obtained than that of the pristine SPEEK membrane. The results showed that the SPEEK/TMBP/PN blend membranes could have potential use as proton‐exchange membranes in direct methanol fuel cells. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2009     

Sulfonated poly(ether ether ketone)/zirconium tricarboxybutylphosphonate composite proton-exchange membranes for direct methanol fuel cells

Sulfonated poly(ether ether ketone) (SPEEK) is a very promising alternative membrane material for direct methanol fuel cells. However, with a fairly high degree of sulfonation (DS), SPEEK membranes can swell excessively and even dissolve at high temperature. This restricts membranes from working above a high tolerable temperature to get high proton conductivity. To deal with this contradictory situation, insolvable zirconium tricarboxybutylphosphonate (Zr(PBTC)) powder was employed to make a composite with SPEEK polymer in an attempt to improve temperature tolerance of the membranes. SPEEK/Zr(PBTC) composite membranes were obtained by casting a homogeneous mixture of Zr(PBTC) and SPEEK in N,N-dimethylacetamide on a glass plate and then evaporating the solvent at 60°C. Many characteristics were investigated, including thermal stability, liquid uptake, methanol permeability and proton conductivity. Results showed significant improvement not only in temperature tolerance, but also in methanol resistance of the SPEEK/Zr(PBTC) composite membranes. The membranes containing 30 wt-% ∼ 40 wt-% of Zr(PBTC) had their methanol permeability around 10^-7 cm²·s^-1 at room temperature to 80°C, which was one order of magnitude lower than that of Nafion ^¯115. High proton conductivity of the composite membranes, however, could also be achieved from higher temperature applied. At 100% relative humidity, above 90°C the conductivity of the composite membrane containing 40 wt-% of Zr(PBTC) exceeded that of the Nafion ^¯115 membrane and even reached a high value of 0.36 S·cm^-1 at 160°C. Improved applicable temperature and high conductivity of the composite membrane indicated its promising application in DMFC operations at high temperature.     

The Preparation of Metal–Organic-Framework/Boron Phosphate Hybrid Materials for Improved Performances in Proton Exchange Membranes

New types of metal–organic framework based hybrid materials are designed and prepared, which involving the hybridization of various content of boron phosphate (BPO₄) with the precursor of HKUST-1. The structure of obtained HKUST-1/BPO₄ hybrid materials (HB) is fully investigated, and then applied to construct sulfonated poly (ether ether ketone) (SPEEK) based proton exchange membranes (SPEEK/HB). Owing to effective interactions between hybrid materials and SPEEK matrix, the achieved composite membranes reflect a considerable improvement in mechanical and thermal stability, oxidative stability, methanol permeation, and proton conductivity. In particular, the tensile strength of SPEEK/HB-20 composite membrane is 41.3 MPa, which is 1.5 times higher than pristine SPEEK, and the methanol permeability reduced to one-third of SPEEK at the same time. The SPEEK/HB-10 displays the highest proton conductivity of 37.4 mS cm⁻¹ at 80 °C, which is obviously higher than pristine SPEEK. These results reveal that the hybridization of HKUST-1 with BPO₄ provide a promising candidate in the modification of proton exchange membranes (PEMs), and this strategy also possess great application potential in other types of MOFs-based hybrid materials.     

Solution‐blown SPEEK/POSS nanofiber–nafion hybrid composite membranes for direct methanol fuel cells

This study aims to develop novel hybrid composite membranes (NHMs) by impregnating Nafion solution into the porous sulfonated poly(ether ether ketone)/polyhedral oligomeric silsesquioxanes (SPEEK/POSS) nanofibers (NFs). The composite membrane was prepared by solution blowing of a mixture of SPEEK/POSS solution. The characteristics of the SPEEK/POSS NFs and the NHMs, including morphology, thermal stability, and performance of membrane as PEMs, were investigated. The performance of NHMs was compared with that of Nafion117 and SPEEK/Nafion composite membranes. Results showed that the introduction of POSS improved the proton conductivity, water swelling, and methanol permeability of membranes. A maximum proton conductivity of 0.163 S cm^?1 was obtained when the POSS content was 6 wt % at 80°C, which was higher than that of Nafion117 and SPEEK/Nafion. NHMs could be used as proton exchange membranes (PEMs) for fuel cell applications. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015 , 132, 42843.     

Preparation and investigation of acid–base composite membranes with modified graphitic carbon nanosheets for direct methanol fuel cells

The ethylenediamine-modified graphite oxide (EGO)-doped sulfonated poly (arylene ether ketone) (SPEEK) composite membranes have been prepared and developed for fuel cell applications in the present work. The base-modified EGO improves the dispersion of inorganic nanosheet in the polymer matrix and enhances proton conductivity by creating continuous conduction pathways. Furthermore, the methanol barrier property also be enhanced due to the nanosheet block the methanol-transport channels. EGO-filled membranes display improved dimensional stability, proton conductivity, and ethanol permeability than those using SPEEK control and graphite oxide (GO)-filled membranes. In the direct methanol fuel cells (DMFCs), the SPEEK/EGO-1.5 membrane displays the highest current density of 395.9 mA/cm² at 60°C, which is 1.6- and 1.4-fold higher than that of SPEEK (254.0 mA/cm²) and SPEEK/GO membrane (292.6 mA/cm²).     

Modified Sulfonated Poly(ether ether ketone) Based Mixed Matrix Membranes for Direct Methanol Fuel Cells

Mixed matrix membranes based on zeolite 4A‐methane sulfonic acid (MSA)‐sulfonated poly(ether ether ketone) (SPEEK) are evaluated as a potential polymer electrolyte membrane (PEM) for direct methanol fuel cells (DMFCs). Ion‐exchange capacity, sorption of water, and water–methanol mixture, proton conductivity, and methanol permeability for the mixed‐matrix membranes have been extensively investigated. The mixed‐matrix membranes are also characterized for their cross‐sectional morphology, mechanical, and thermal properties. DMFCs employing SPEEK‐MSA (20 wt.%) blend, zeolite 4A (4 wt.%)‐SPEEK‐MSA (20 wt.%) mixed matrix membranes deliver peak power densities of 130 and 159 mW cm^–2, respectively; while a peak power density of only 95 mW cm^–2 is obtained for the DMFC employing pristine SPEEK membrane at 70 °C. The results showed that these SPEEK based mixed matrix membranes exhibit higher DMFC performance and lower methanol permeability in comparison to Nafion‐117 membrane.     

直接甲醇燃料电池用新型质子交换膜的研究

以聚醚醚酮(PEEK)为原料,浓硫酸为磺化剂制备了不同磺化度的磺化聚醚醚酮(SPEEK)膜,以及磺化聚醚醚酮与聚乙烯醇(PVA)、正硅酸乙酯(TEOS)、磷钨酸的复合膜.分别对膜的电导率、阻醇性能和吸水率进行了研究.随着SPEEK膜磺化度的增大,膜的电导率有所提高,然而甲醇渗透系数也增大,膜的机械强度明显降低.SPEEK膜的吸水率低于Nafion 115膜,而PVA膜的吸水率则过高.     

DMFCs用SPEEK/SiOx-S复合质子交换膜

A sulfonated poly(ether ether ketone) (SPEEK) membrane with a fairly high degree of sulfonation (DS) can swell excessively and even dissolve at high temperature. To solve these problems, insolvable functionalized silica powder with sulfonic acid groups (SiOx-S) was added into the SPEEK matrix (DS 55.1%) to prepare SPEEK/ SiOx-S composite membranes. The decrease in both the swelling degree and the methanol permeability of the membranes was a dose-dependent result of addition of the SiOx-S powder. Pure SPEEK membrane swelled 52.6% at 80°C, whereas the SPEEK/SiOx-S (15%, by mass) membrane swelled only 27.3% at the same temperature. From room temperature to 80℃, all SPEEK/SPEEK/SiOx-S composite membranes had methanol permeability of about one order of magnitude lower than that of Nafion&#61650;115. Compared with pure SPEEK membranes, the addition of the SiOx-S powder not only leads to higher proton conductivity, but also increases the dimensional stability at higher temperatures, and greater proton conductivity can be achieved at higher temperature. The SPEEK/SiOx-S (20%, by mass) membrane could withstand temperature up to 145°C, at which in 100% relative humidity (RH) its proton conductivity exceeded slightly that of Nafion&#61650;115 membrane and reached 0.17 S&#8226;cm－1, while pure SPEEK mem-brane dissolved at 90°C. The SPEEK/SiOx-S composite membranes are promising for use in direct methanol fuel cells because of their good dimensional stability, high proton conductivity, and low methanol permeability.     

DMFCs用磺化聚醚醚酮/磺化酚酞型聚醚砜共混质子交换膜

A sulfonated poly(ether ether ketone) (SPEEK) membrane with fairly high degree of sulfonation (DS) swells excessively and even dissolves at high temperature. To solve these problems, sulfonated phenolphthalein poly(ether sulfone) (SPES-C, DS 53.7%) is blended with the SPEEK matrix (DS 55.1%, 61.7%) to prepare SPEEK/SPES-C blend membrane. The decrease in swelling degree and methanol permeability of the membrane is dose-dependent. Pure SPEEK (DS 61.7%) membrane dissolves completely in water at 70ºC, whereas the swelling degree of the SPEEK (DS 61.7%)/SPES-C (40%, by mass) membrane is 29.7% at 80ºC. From room temperature to 80ºC, the methanol permeability of all SPEEK (DS 55.1%)/SPES-C blend membranes is about one order of magnitude lower than that of Nafion®115. At higher temperature, the addition of SPES-C polymer increases the dimensional stability and greater proton conductivity can be achieved. The SPEEK (DS 55.1%)/SPES-C (40%, by mass) membrane can withstand temperatures up to 150ºC. The proton conductivity of SPEEK (DS 55.1%)/SPES-C (30%, by mass) membrane approaches 0.16 S&#8226;cm－1, matching that of Nafion&#61650;115 at 140ºC and 100% RH, while pure SPEEK (DS 55.1%) membrane dissolves at 90ºC. The SPEEK/SPES-C blend membranes are promising for use in direct methanol fuel cells because of their good dimensional stability, high proton conductivity, and low methanol permeability.     

Effects of microstructural functional polyaniline layers on SPEEK/HPW proton exchange membranes

In this study, a method is developed to fabricate sulfonated poly (ether ether ketone)/phosphotungstic acid‐polyaniline (SPEEK/HPW‐PANI) membranes by in situ polymerization of aniline for the purpose of decreasing the weight loss of HPW in the membranes. The synthesis involves the production of a SPEEK/HPW hybrid membrane followed by different layer of PANI coatings on the membrane surface, and subsequent treatment using drying in vacuum procedures. The scanning electronic microscopy images showed that HPW had good compatibility with SPEEK polymers and energy dispersive X‐ray spectroscopy revealed the successfully doping with HPW and polymerization of PANI. The surface of SPEEK/HPW‐PANI becomes more compact than that of SPEEK/HPW and pure SPEEK, which may lead to reduce the water uptake and swelling property. The proton conductivity was found for the SPEEK/HPW‐PANI‐5 composite membrane (91.53 mS/cm at 80°C) higher than that of pure SPEEK membrane (68.72 mS/cm at 80°C). Better thermal stability was determined in both SPEEK/HPW and SPEEK/HPW‐PANI membranes than pristine SPEEK membrane. Therefore, PANI is a good potential coating for organic–inorganic hybrid e.g. SPEEK/HPW membrane materials to improve their hydrothermal stable properties and SPEEK/HPW PANI is a material that shows promise as a proton exchange membranes. © 2014 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2014 , 131, 41033.     

Effect of PES on the morphology and properties of proton conducting blends with sulfonated poly(ether ether ketone)

Development of alternate materials to Nafion, based on ionically conducting polymers and their blends is important for the wider applications of proton exchange membrane fuel cells. In this work, blends of sulfonated poly(ether ether ketone) (SPEEK) with poly(ether sulfone) (PES) are investigated. SPEEK with various ion exchange capacity (IEC) was prepared and blended with PES, which is nonionic and hydrophobic in nature. A comparative study of the water uptake, proton conductivity, and thermo‐mechanical characteristics of SPEEK and the blend membranes as a function of the IEC is presented. Addition of PES decreases the water uptake and conductivity of SPEEK. Chemical and thermal stability and mechanical properties of the membrane improve with the addition of PES. The effect of water content on the thermo‐mechanical properties of membranes was also studied. The morphology of blend membranes was studied using SEM to understand the microstructure and miscibility of the components. On the basis of the results, a plausible microstructure of the blends is presented, and is shown to be useful in understanding the variation of different properties with blending. © 2012 Wiley Periodicals, Inc. J. Appl. Polym. Sci., 2013     

Sulfonated poly(ether ether ketone)/zirconium tricarboxybutylphosphonate composite proton-exchange membranes for direct methanol fuel cells

Sulfonated poly(ether ether ketone) (SPEEK) is a very promising alternative membrane material for direct methanol fuel cells. However, with a fairly high degree of sulfonation (DS), SPEEK membranes can swell excessively and even dissolve at high temperature. This restricts membranes from working above a high tolerable temperature to get high proton conductivity. To deal with this contradictory situation, insolvable zirconium tricarboxybutylphosphonate (Zr(PBTC)) powder was employed to make a composite with SPEEK polymer in an attempt to improve temperature tolerance of the membranes. SPEEK/Zr(PBTC) composite membranes were obtained by casting a homogeneous mixture of Zr(PBTC) and SPEEK in N,N-dimethylacetamide on a glass plate and then evaporating the solvent at 60°C. Many characteristics were investigated, including thermal stability, liquid uptake, methanol permeability and proton conductivity. Results showed significant improvement not only in temperature tolerance, but also in methanol resistance of the SPEEK/Zr(PBTC) composite membranes. The membranes containing 30 wt-% ∼ 40 wt-% of Zr(PBTC) had their methanol permeability around 10⁻⁷ cm²·s⁻¹ at room temperature to 80°C, which was one order of magnitude lower than that of Nafion?115. High proton conductivity of the composite membranes, however, could also be achieved from higher temperature applied. At 100% relative humidity, above 90°C the conductivity of the composite membrane containing 40 wt-% of Zr(PBTC) exceeded that of the Nafion?115 membrane and even reached a high value of 0.36 S·cm⁻¹ at 160°C. Improved applicable temperature and high conductivity of the compositemembrane indicated its promising application inDMFC operations at high temperature. __________ Translated from Acta Polymerica Sinica, 2007, (4): 337–342 [译自:高分子学报]     

Sulphonated Poly(ether ether ketone) Proton Exchange Membranes for Fuel Cell Applications

Polymer electrolyte membrane fuel cells (PEMFCs) are promising new power sources for automotive and portable devices. Nafion® is the currently used membrane in PEMFCs. Although these membranes show high proton conductivity and excellent chemical stability, their high cost makes them unpractical for commercial purposes. Sulphonated poly(ether ether ketone) (SPEEK) ionomers were synthesized using chlorosulphonic acid as the sulphonating agent in dichloromethane medium. Homogeneous proton-conducting membranes were developed from the obtained SPEEK by solvent casting method. Membranes were assessed for their suitability in fuel cell applications. The extent of sulphonation was controlled by varying the reaction time, concentration of polymer, and concentration of sulphonating agent. The SPEEK membranes exhibit degree of sulphonation from 10 to 66%, ion exchange capacity from 0.29 to 1.92 meq/g and maximum water and methanol uptake up to 54 and 22%, respectively, at 25°C. The membranes were characterized by FTIR to confirm sulphonation, and DSC and TGA to investigate the thermal stability. The proton conductivities of such membranes were found to be excellent in the order of 10^?2 S/cm in the fully hydrated condition at room temperature as measured by impedance spectroscopy. The durability of the membranes was also tested. The study revealed the possibility of a cheaper alternative membrane for use in PEMFC.     

SPEEK-Tin dioxide proton conducting membranes: Effect of modifying agent of tin dioxide particles surface

Proton-conducting membranes based on sulphonated poly (ether ether ketone) (SPEEK) polymer matrix and tin dioxide have been synthesized. Their local structure has been studied by FTIR and XRD whereas their structural features at nanometer scale has been investigated by Small-Angle X-ray Scattering (SAXS) and transmission electron microscopy (TEM). SAXS and TEM results show that incorporation of the inorganic particles in SPEEK promotes dispersion of the hydrophilic sulfonic groups in the polymer matrix, inhibiting the formation of the water-filled ionic clusters usually observed in hydrated SPEEK membranes. The changes in SPEEK nanostructure are induced by incorporation of particles modified by Tiron that promotes the connectivity between hydrated channels and reduces diffusion of alcohol, as evidenced by permeability measurements. The resulting increase of proton conductivity compared to pristine SPEEK, particularly at medium temperature (80°C), combined to an improved dimensional stability, make this family of membranes very promising for future applications in fuel cell.     

Proton exchange membranes based on modified sulfonated poly(ether ether ketone) membranes with chemically in situ polymerized polypyrrole

Sulfonated poly(ether ether ketone) (SPEEK) membranes were modified with chemically in situ polymerized polypyrrole (PPy). The effects of temperature and methanol concentration on the solution uptake and the swelling ratio of SPEEK/PPy membranes were investigated. The solution uptake and the swelling ratio of the membranes decreased upon the incorporation of PPy. When the methanol concentration increased, both the solution uptake and the swelling ratio increased to a maximum, and then decreased. FT-IR, XRD, DSC and TGA were used to characterize the modified membranes. The methanol permeability of modified SPEEK membranes decreased upon the incorporation of PPy, and higher selectivity values were found for SPEEK/PPy membranes in comparison with pure SPEEK and Nafion^® 117 membranes.     

Basicity‐based screening of aniline derivative for composite proton exchange membranes

The aim of this study was to find a suitable aniline derivative to develop composite sulfonated poly(ether ether ketone) (SPEEK) membranes and detail evaluation of their physico‐ and electrochemical properties. The hypothesis was high basicity of the aniline derivatives could form good composite membranes with better physicochemical and electrochemical properties. To assess the basicity we measured the zeta potentials of the polymers and correlated them with ion‐exchange capacities, water uptakes, transport numbers, water‐diffusion coefficients, conductivities, and methanol permeabilities. The obtained values of zeta potentials at pH 7 were 6.52, ?14.66, ?25.17, and ?28 for SPEEK/polynaphthalene (PNAPH), SPEEK/polyanisidine (PANIS), SPEEK/polyaniline (PANI), and SPEEK/polyxylindine (PXYL), respectively supports the hypothesis and strongly suggests polyaniline derivative's basicity‐dependent properties. Of the four derivatives (PNAPH, PANIS, PANI, and PXYL), the SPEEK/PXYL composite membrane had the lowest methanol permeability of 1 × 10^?4 cm²/s and highest proton conductivity of 161 mS/cm. These values are far better than the neat SPEEK and SPEEK/PANI composite. The suitability of SPEEK/PXYL can be explained by the high basicity of the PXYL composite membrane, which leads to the formation of effective Debye spheres, meaning that the ionic complex can interact with surrounding hydronium ions and form hydrophilic channels resulting in high proton conductivity and low methanol permeability. These results suggest that SPEEK/PXYL is a highly suitable membrane for methanol fuel cells or other electrochemical applications. © 2016 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016 , 133, 43978.     

Proton conducting blend membranes: physical,morphological and electronic properties

Blend membranes of sulfonated poly(ether ether ketone) (SPEEK) and sulfonated polyetherimide (SPEI) have been prepared and investigated as a potential polymer electrolyte membrane (PEM) for direct methanol fuel cell (DMFC). Polymers were dissolved in N-methyl-2-pyrrolidone (NMP) in different mixing ratios and membranes were casted using a semi-automatic casting machine on a pre-cleaned glass plate. The influence of SPEI percentage on ion exchange capacity (IEC), water uptake, methanol permeability and proton exchange capacity have been investigated. Blend membranes showed slightly better IEC, water uptake and methanol crossover properties as compare to pure SPEEK; but proton conductivity was slightly lower than that of pure SPEEK membrane. Membrane morphology was investigated by FESEM, TGA and AFM. Overall, a homogeneous surface was observed for most of the blend membranes, with minor phase separation at higher SPEI contents samples. AFM image of the membrane surface shows nanoscale surface roughness.