Study of high-temperature proton exchange membrane through one-step encapsulation of ionic liquid in sulfonated poly(ether ether ketone)

The proton exchange membrane (PEM) is the core component of a high-performance proton exchange membrane fuel cell (PEMFC). Since the traditional PEM has the disadvantages of poor cell performance and high cost, a new kind of PEM with good proton conductivity, low cost and simple preparation should be explored. In this paper, several different binary hybrid membranes were successfully prepared through one-step encapsulation of different ionic liquids (ILs) in sulfonated poly(ether ether ketone) (SPEEK). The prepared membranes were characterized by scanning electron microscope (SEM), thermogravimetric analysis (TG), Fourier transform infrared spectroscopy (FT-IR), X-ray photoelectron spectroscopy (XPS), proton conductivity measurements and dynamic mechanical analysis (DMA). SEM images showed that ILs were fully doped into SPEEK. FT-IR and XPS proved that SPEEK and IL formed a new chemical bond combined with intermolecular hydrogen bonds. The TG results showed that the binary hybrid membranes could maintain stability even at 300°C. The water uptake and swelling ratio showed that the water absorption capacity of the binary composite membrane played a vital role in improving proton conductivity. The proton conductivity study showed that ILs doping also helped to improve the proton conductivity of the SPEEK membrane. When the doping amount of IL was maintained at 30 wt.%, it has the highest proton conductivity, 25 mS cm⁻¹ at 120°C. It was proved that anhydrous hybrid membrane tetraphenyl imidazole sulfate/SPEEK ([IM2][H₂PO₄]/SPEEK) could be used in PEMFC at medium temperature.     

聚醚砜/磺化聚醚醚酮共混膜的制备和性能

采用流延法制备了聚醚砜(PES)含量不同的PES/磺化聚醚醚酮(SPEEK)共混膜。PES与SPEEK具有良好的相容性。所制备PES/SPEEK共混膜的含水率、溶胀度和甲醇透过系数均随PES含量的增加而降低。虽然共混膜的质子传导性能有所降低.但阻醇性能和溶胀性能提高,这说明PES/SPEEK共混膜是一种很好的直接甲醇燃料电池用固体高分子电解质膜材料。     

Hydrophilic TiO2 decorated carbon nanotubes/sulfonated poly(ether ether ketone) composite proton exchange membranes for fuel cells

Sulfonated poly(ether ether ketone) (SPEEK) is currently considered to be one of the most potential candidates of commercial perfluorinated sulfonic acid proton exchange membranes. To balance the proton conductivity and mechanical properties of SPEEK, nano TiO₂ coated carbon nanotubes (TiO₂@CNTs) were prepared using a benzyl alcohol-assisted sol-gel method and then used as a new nanofiller to modify SPEEK to prepare SPEEK/TiO₂@CNTs composite membranes. The thick insulated TiO₂ coating layer can effectively avoid the risk of electronic short-circuiting formed by CNTs, while the hydrophilicity of TiO₂ can also reduce the polar difference between CNTs and SPEEK matrix, thus promoting the homogeneous dispersion of CNTs in the composites. As a result, the composite membranes demonstrated simultaneously improved strength and proton conductivity. Incorporating 5 wt% of TiO₂@CNTs exhibited 31% growth in mechanical strength when compared with pure SPEEK. Moreover, the maximum conductivity was 0.104 S cm⁻¹ (80°C) for the composite membrane with 5 wt% of TiO₂@CNTs, which was nearly twice as high as that of SPEEK membrane (0.052 S cm⁻¹).     

Tensile mechanical properties of sulfonated poly(ether ether ketone) (SPEEK) and BPO4/SPEEK membranes

A study to evaluate the tensile mechanical properties of sulfonated poly(ether ether ketone) (SPEEK) and BPO₄/SPEEK composite membranes has been carried out. It is aimed to give an assessment of these materials for applications in proton exchange membrane fuel cells. The stress–strain response of the membranes was measured as a function of the degree of sulfonation (DS) and the filler–matrix ratio. In addition, the effects of immersion in water at various temperatures were explored in situ by means of a homemade testing chamber fitted to the tensile analyzer. The results indicate that the DS has an important influence on the final mechanical behavior of the membranes. The introduction of the BPO₄ solid filler leads to deterioration in mechanical performance compared to unfilled SPEEK. A general picture of the microstructural features influencing the mechanical properties of SPEEK and BPO₄/SPEEK membranes is proposed. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 98: 2380–2393, 2005     

Physicochemical characterization of low sulfonated polyether ether ketone/Smectite clay composite for proton exchange membrane fuel cells

Polyether ether ketone (PEEK) with a low sulfonation degree was blended using different proportions of sodium rich Smectite clay (3 and 6 wt%) to use as an electrolyte membrane for fuel cell application. The structural functionalities, surface morphologies, and the thermal stability of the resultant composite membranes were characterized using Fourier-transform infrared spectroscopy, X-ray diffraction (XRD), scanning electron microscopy, atom force microscopy, and thermo-gravimetric analysis. FT-IR showed that no chemical reactions take place between the sulfonated polyether ether ketone (SPEEK) and the clay with different ratios. XRD diffractograms illustrated a lower degree of crystallinity of the blended SPEEK than pristine SPEEK. The elaborated composite membranes proved to have a higher thermal stability than SPEEK. Furthermore, the SPEEK/clay composite membranes with 3 and 6 wt% in clay loading had higher water uptake and lower methanol uptake than those in pristine SPEEK It was also shown that, the incorporation of sodium ions rich Smectite clay layers between the clusters in SPEEK improved the conductivity to 2 × 10⁻² S/cm at 140°C (for 6 wt% in clay) without compromising the dimensional stability of the composite membranes. These results propose the composite membranes as a potential candidate for methanol fuel cells at temperatures above 120°C making SPEEK composite membrane competitive to that of Nafion membrane.     

Sulfonated poly(ether ether ketone)‐induced porous poly(ether sulfone) blend membranes for the separation of proteins and metal ions

Asymmetric ultrafiltration (UF) membranes were prepared by the blending of poly(ether sulfone) (PES) and sulfonated poly(ether ether ketone) (SPEEK) polymers with N,N′‐dimethylformamide solvent by the phase‐inversion method. SPEEK was selected as the hydrophilic polymer in a blend with different composition of PES and SPEEK. The solution‐cast PES/SPEEK blend membranes were homogeneous for all of the studied compositions from 100/0 to 60/40 wt % in a total of 17.5 wt % polymer and 82.5 wt % solvent. The presence of SPEEK beyond 40 wt % in the casting solution did not form membranes. The prepared membranes were characterized for their UF performances, such as pure water flux, water content, porosity, and membrane hydraulic resistance, and morphology and melting temperature. We estimated that the pure water flux of the PES/SPEEK blend membranes increased from 17.3 to 85.6 L m^?2 h^?1 when the concentration of SPEEK increased from 0 to 40 wt % in the casting solution. The membranes were also characterized their separation performance with proteins and metal‐ion solutions. The results indicate significant improvement in the performance characteristics of the blend membranes with the addition of SPEEK. In particular, the rejection of proteins and metal ions was marginally decreased, whereas the permeate flux was radically improved. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2010     

Sulphonated Poly(ether ether ketone) Proton Exchange Membranes for Fuel Cell Applications

Polymer electrolyte membrane fuel cells (PEMFCs) are promising new power sources for automotive and portable devices. Nafion® is the currently used membrane in PEMFCs. Although these membranes show high proton conductivity and excellent chemical stability, their high cost makes them unpractical for commercial purposes. Sulphonated poly(ether ether ketone) (SPEEK) ionomers were synthesized using chlorosulphonic acid as the sulphonating agent in dichloromethane medium. Homogeneous proton-conducting membranes were developed from the obtained SPEEK by solvent casting method. Membranes were assessed for their suitability in fuel cell applications. The extent of sulphonation was controlled by varying the reaction time, concentration of polymer, and concentration of sulphonating agent. The SPEEK membranes exhibit degree of sulphonation from 10 to 66%, ion exchange capacity from 0.29 to 1.92 meq/g and maximum water and methanol uptake up to 54 and 22%, respectively, at 25°C. The membranes were characterized by FTIR to confirm sulphonation, and DSC and TGA to investigate the thermal stability. The proton conductivities of such membranes were found to be excellent in the order of 10^?2 S/cm in the fully hydrated condition at room temperature as measured by impedance spectroscopy. The durability of the membranes was also tested. The study revealed the possibility of a cheaper alternative membrane for use in PEMFC.     

Incorporating sepiolite and kaolinite to improve the performance of SPEEK composite membranes for proton exchange membrane fuel cells

SPEEK polymer based thermally crosslinked polymer membranes are prepared by sol-gel synthesis using kaolinite and sepiolite clays as additives. Characterization tests, ie, mechanical stability, thermal gravimetric analysis, ion exchange capability, swelling properties, water uptake capacities, electrochemical impedance spectroscopy analysis, and Fourier transform infrared spectroscopy (FTIR) analysis of the membranes were conducted. The sepiolite and kaolinite addition enhanced the thermal stability and the thermal crosslinking reduced the swelling capacity of the synthesized membranes. Proton conductivity results were increased from 0.172 to 0.268 S cm⁻¹ by adding 9% of kaolinite, and to 0.329 S cm⁻¹ at 80°C by adding 9% of sepiolite to the SPEEK membrane's polymer structure. The fuel cell current density and potential measurements of 141 mA cm⁻² and 84.6 mW cm⁻² were found respectively at 0.6 V for the SPEEK/S9 membrane, whereas values of 600 mA cm⁻² and 348 mW cm⁻² were found for the Nafion commercial membrane.     

Compatibility studies of sulfonated poly(ether ether ketone)–poly(ether imide)–polycarbonate ternary blends

Binary blends of the sulfonated poly(ether ether ketone) (SPEEK)–poly(ether imide) (PEI) and SPEEK–polycarbonate (PC), and ternary blends of the SPEEK–PEI–PC, were investigated by differential scanning calorimetry. SPEEK was obtained by sulfonation of poly(ether ether ketone) using 95% sulfuric acid. From the thermal analysis of the SPEEK–PEI blends, single glass transition temperature (T_g) was observed at all the blend composition. For the SPEEK–PC blends, double T_gs were observed. From the results of thermal analysis, it is suggested that the SPEEK–PEI blends are miscible and the SPEEK–PC blends are immiscible. Polymer–polymer interaction parameter (χ₁₂) of the SPEEK–PEI blends was calculated from the modified Lu and Weiss equation, and found to range from −0.011 to −0.825 with the blend composition. For the SPEEK–PC blends, the χ₁₂ values were calculated from the modified Flory–Huggins equation, and found to range from 0.191 to 0.272 with the blend composition. For the SPEEK–PEI–PC ternary blends, phase separation regions that showed two T_gs were found to be consistent with the spinodal curves calculated from the χ₁₂ values of the three binary blends. © 2000 John Wiley & Sons, Inc. J Appl Polym Sci 78: 2488–2494, 2000     

Proton exchange membranes based on modified sulfonated poly(ether ether ketone) membranes with chemically in situ polymerized polypyrrole

Sulfonated poly(ether ether ketone) (SPEEK) membranes were modified with chemically in situ polymerized polypyrrole (PPy). The effects of temperature and methanol concentration on the solution uptake and the swelling ratio of SPEEK/PPy membranes were investigated. The solution uptake and the swelling ratio of the membranes decreased upon the incorporation of PPy. When the methanol concentration increased, both the solution uptake and the swelling ratio increased to a maximum, and then decreased. FT-IR, XRD, DSC and TGA were used to characterize the modified membranes. The methanol permeability of modified SPEEK membranes decreased upon the incorporation of PPy, and higher selectivity values were found for SPEEK/PPy membranes in comparison with pure SPEEK and Nafion^® 117 membranes.     

Sulfonated poly(ether ether ketone)/zirconium tricarboxybutylphosphonate composite proton-exchange membranes for direct methanol fuel cells

Sulfonated poly(ether ether ketone) (SPEEK) is a very promising alternative membrane material for direct methanol fuel cells. However, with a fairly high degree of sulfonation (DS), SPEEK membranes can swell excessively and even dissolve at high temperature. This restricts membranes from working above a high tolerable temperature to get high proton conductivity. To deal with this contradictory situation, insolvable zirconium tricarboxybutylphosphonate (Zr(PBTC)) powder was employed to make a composite with SPEEK polymer in an attempt to improve temperature tolerance of the membranes. SPEEK/Zr(PBTC) composite membranes were obtained by casting a homogeneous mixture of Zr(PBTC) and SPEEK in N,N-dimethylacetamide on a glass plate and then evaporating the solvent at 60°C. Many characteristics were investigated, including thermal stability, liquid uptake, methanol permeability and proton conductivity. Results showed significant improvement not only in temperature tolerance, but also in methanol resistance of the SPEEK/Zr(PBTC) composite membranes. The membranes containing 30 wt-% ∼ 40 wt-% of Zr(PBTC) had their methanol permeability around 10^-7 cm²·s^-1 at room temperature to 80°C, which was one order of magnitude lower than that of Nafion ^¯115. High proton conductivity of the composite membranes, however, could also be achieved from higher temperature applied. At 100% relative humidity, above 90°C the conductivity of the composite membrane containing 40 wt-% of Zr(PBTC) exceeded that of the Nafion ^¯115 membrane and even reached a high value of 0.36 S·cm^-1 at 160°C. Improved applicable temperature and high conductivity of the composite membrane indicated its promising application in DMFC operations at high temperature.     

A convenient crosslinking method for sulfonated poly(ether ether ketone) membranes via friedel–crafts reaction using 1,6‐dibromohexane and aluminum trichloride

In this study, sulfonated poly(ether ether ketone) (SPEEK) was very efficiently crosslinked via a Friedel–Craft reaction using 1,6‐dibromohexane and AlCl₃. The resulting crosslinked SPEEK (c‐SPEEK) membranes exhibited improved dimensional stability, thermal and chemical stability, and mechanical strength with slight reduction in the elongation. The methanol permeability was reduced by approximately two orders of magnitude by the crosslinking reaction. The proton conductivities of c‐SPEEK membranes were greater than Nafion‐212 in the temperature range of 30–90°C. Overall, this new crosslinking method can be conveniently and efficiently applicable to most aromatic hydrocarbon polymer membranes. © 2014 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2014 , 131, 40695.     

Preparation and characterization of new anhydrous, conducting membranes based on composites of ionic liquid trifluoroacetic propylamine and polymers of sulfonated poly (ether ether) ketone or polyvinylidenefluoride

A novel ionic liquid of trifluoroacetic propylamine, i.e., [CH₃CH₂CH₂NH₃⁺] [CF₃COO⁻] (TFAPA), was synthesized from trifluoroacetic acid and propylamine. The ionic liquid of TFAPA was used to prepare anhydrous, conducting membranes based on polymers of sulfonated poly (ether ether) ketone (SPEEK) or polyvinylidenefluoride (PVDF). The ionic conductivity and mechanical strength of the composite membranes were investigated at elevated temperatures and under anhydrous conditions. Conductivity of 0.030 S/cm was achieved with TFAPA at 180 °C, and of 0.019 S/cm with a membrane containing 70% (wt) TFAPA in SPEEK with a sulfonation degree of 86% at 160 °C. Increasing either ionic liquid content or temperature reduced the mechanical strength of the composite membrane. Efforts were made to improve the strength of TFAPA/SPEEK composite membranes by cross-linking the SPEEK, which led to some strength enhancement at 110 °C and 130 °C.     

Effects and properties of poly(arylene ether benzonitrile)s of various molecular weights blended with sulfonated poly(ether ether ketone)

Poly(arylene ether benzonitrile) (PAEBN) was synthesized with 2,6‐dichlorobenzonitrile and biphenol. PAEBNs with various molecular weights (MWs), 1,640,000 and 185,000 g/mol, were synthesized by control of the stoichiometry of the monomers and were blended with sulfonated poly(ether ether ketone) (SPEEK). The effects of MW on the water uptake, swelling, methanol permeability, and proton conductivity of the SPEEK/PAEBN blend membranes were investigated. The molecular mobility of the SPEEK/PAEBN blends was also examined in this study. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Effect of clay modification on the structure and properties of sulfonated poly(ether ether ketone)/clay nanocomposites

Sulfonated poly(ether ether ketone) (SPEEK)/clay hybrid membranes were prepared using three types of commercially available clays, the sodium montmorillonite (IC), hydrophobic organo‐clay with long alkyl chains (OC), and organo‐clay with carboxylic acid end groups (HC). It was found that the SPEEK/HC hybrid membranes achieved the best clay dispersion, with the exfoliation of the clay nano‐platelets when the filler loading was < 10 wt%. The incorporation of the carboxylic acid groups in clay layers also improved the connectivity between the ionic clusters in the membrane, resulting in higher proton conductivity without compromising the dimensional stability of membranes. The selectivity higher than the pristine SPEEK membranes was obtained for the SPEEK/HC hybrid membranes at low filler loading (<10 wt%), with higher proton conductivity and similar methanol permeability. POLYM. COMPOS., 37:2632–2638, 2016. © 2015 Society of Plastics Engineers     

Structural and mechanical characterization of poly(ether ether ketone) (PEEK) and sulfonated PEEK films: Effects of thermal history,sulfonation, and preparation conditions

In this work, virgin and sulfonated poly(ether ether ketone) films (PEEK and SPEEK, respectively) have been studied by dynamic mechanical analysis, modulated differential scanning calorimetry, wide‐angle X‐ray diffraction, birefringence, and optical microscopy. The properties of the unmodified polymer have been addressed to assess the original morphological characteristics and the changes induced by sulfonation. In general, the introduction of ionic groups in the polymer backbone alters dramatically the intrinsic properties of the parent material. The particular thermomechanical response exhibited by PEEK and SPEEK samples, characterized by a hysteresis loop, can be explained by the reversible and irreversible relaxation–orientation of the microstructure, even in the sub‐T_g region. The results showed that the preparation conditions largely determine the nonequilibrium morphological features of both compression‐molded PEEK films and solvent‐cast SPEEK membranes. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 99: 756–774, 2006     

Polymer electrolyte membranes prepared by EB‐crosslinking of sulfonated poly(ether ether ketone) with 1,4‐butanediol

Crosslinked sulfonated poly(ether ether ketone) (SPEEK) membranes were prepared through the electron beam (EB)‐irradiation crosslinking of SPEEK/1,4‐butanediol under various irradiation conditions and used as a proton exchange membrane (PEM) for fuel cell applications. The crosslinked membranes were characterized by gel fraction, a universal testing machine (UTM), dynamic mechanical analysis (DMA), and small‐angle X‐ray scattering (SAXS). The gel fraction of the crosslinked membranes was used to estimate the degree of crosslinking, and the gel fraction was found to be increased with an increase of the crosslinker content and EB‐absorbed dose. The UTM results indicate that a brittle EB‐crosslinked membrane becomes more flexible with an increase in the crosslinker content. The DMA results show that the EB‐crosslinked membranes have well‐developed ionic aggregation regions and the cluster T_g of membranes decrease with an increase in the 1,4‐butanediol crosslinker content. The SAXS results show that the Bragg and persistence distance of crosslinked membranes increase with an increase in the crosslinker content. The proton conductivities of the EB‐crosslinked membranes were more than 9 × 10^?2 S/cm. © 2014 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015 , 132, 41760.     

DMFCs用SPEEK/SiOx-S复合质子交换膜

A sulfonated poly(ether ether ketone) (SPEEK) membrane with a fairly high degree of sulfonation (DS) can swell excessively and even dissolve at high temperature. To solve these problems, insolvable functionalized silica powder with sulfonic acid groups (SiOx-S) was added into the SPEEK matrix (DS 55.1%) to prepare SPEEK/ SiOx-S composite membranes. The decrease in both the swelling degree and the methanol permeability of the membranes was a dose-dependent result of addition of the SiOx-S powder. Pure SPEEK membrane swelled 52.6% at 80°C, whereas the SPEEK/SiOx-S (15%, by mass) membrane swelled only 27.3% at the same temperature. From room temperature to 80℃, all SPEEK/SPEEK/SiOx-S composite membranes had methanol permeability of about one order of magnitude lower than that of Nafion&#61650;115. Compared with pure SPEEK membranes, the addition of the SiOx-S powder not only leads to higher proton conductivity, but also increases the dimensional stability at higher temperatures, and greater proton conductivity can be achieved at higher temperature. The SPEEK/SiOx-S (20%, by mass) membrane could withstand temperature up to 145°C, at which in 100% relative humidity (RH) its proton conductivity exceeded slightly that of Nafion&#61650;115 membrane and reached 0.17 S&#8226;cm－1, while pure SPEEK mem-brane dissolved at 90°C. The SPEEK/SiOx-S composite membranes are promising for use in direct methanol fuel cells because of their good dimensional stability, high proton conductivity, and low methanol permeability.     

DMFCs用磺化聚醚醚酮/磺化酚酞型聚醚砜共混质子交换膜

A sulfonated poly(ether ether ketone) (SPEEK) membrane with fairly high degree of sulfonation (DS) swells excessively and even dissolves at high temperature. To solve these problems, sulfonated phenolphthalein poly(ether sulfone) (SPES-C, DS 53.7%) is blended with the SPEEK matrix (DS 55.1%, 61.7%) to prepare SPEEK/SPES-C blend membrane. The decrease in swelling degree and methanol permeability of the membrane is dose-dependent. Pure SPEEK (DS 61.7%) membrane dissolves completely in water at 70ºC, whereas the swelling degree of the SPEEK (DS 61.7%)/SPES-C (40%, by mass) membrane is 29.7% at 80ºC. From room temperature to 80ºC, the methanol permeability of all SPEEK (DS 55.1%)/SPES-C blend membranes is about one order of magnitude lower than that of Nafion®115. At higher temperature, the addition of SPES-C polymer increases the dimensional stability and greater proton conductivity can be achieved. The SPEEK (DS 55.1%)/SPES-C (40%, by mass) membrane can withstand temperatures up to 150ºC. The proton conductivity of SPEEK (DS 55.1%)/SPES-C (30%, by mass) membrane approaches 0.16 S&#8226;cm－1, matching that of Nafion&#61650;115 at 140ºC and 100% RH, while pure SPEEK (DS 55.1%) membrane dissolves at 90ºC. The SPEEK/SPES-C blend membranes are promising for use in direct methanol fuel cells because of their good dimensional stability, high proton conductivity, and low methanol permeability.     

Novel polymer electrolyte membranes based on semi‐interpenetrating blends of poly(vinyl alcohol) and sulfonated poly(ether ether ketone)

In this work, the properties of novel ionic polymer blends of crosslinked and sulfonated poly(vinyl alcohol) (PVA) and sulfonated poly(ether ether ketone) (SPEEK) are investigated. Crosslinking and sulfonation of PVA were carried out using sulfosuccinic acid (SSA) in the presence of dispersed SPEEK to obtain semi‐interpenetrating network blends. PVA–SSA/SPEEK blend membranes of different compositions were studied for their ion‐exchange capacity, proton conductivity, water uptake, and thermal and mechanical properties. The hydrated blend membranes show good proton conductivities in the range of 10^?3 to 10^?2 S/cm. When compared with pure component membranes, the PVA–SSA/SPEEK blend membranes also exhibit improvement in tensile strength, tensile modulus, and delay in the onset of thermal and chemical degradation. Semi‐interpenetrating nature of the blends is established from morphology and dynamic mechanical analysis. Morphology of the membranes was studied using scanning electron microscopy after selective chemical treatment. The dynamic mechanical properties of the membranes are examined to understand the miscibility characteristics of the blends. The relative proportions of PVA and SPEEK and the degree of crosslinking of PVA–SSA are important factors in determining the optimum properties for the blend. © 2012 Wiley Periodicals, Inc. J. Appl. Polym. Sci., 2013