PZT陶瓷粉体及其PVDF压电复合材料的制备与性能

采用溶胶-凝胶法合成PZT压电陶瓷粉体,经XRD和SEM分析显示,陶瓷颗粒已形成了钙钛矿型结晶相,颗粒大小在0.1~1μm之间。采用溶液共混法将PZT粒子均匀分散于PVDF基体中,制备了PZT/PVDF压电复合材料。结果表明,增加PZT含量有利于复合材料压电性能的提高,当陶瓷体积分数达70%时,复合材料的压电常数最高。     

0-3型PZT/PVDF压电复合材料制备及性能研究

利用固相法制备了掺杂有Nb2O5的PZT95/5压电陶瓷,采用固化、冷等静压、溶液混合法制备0-3型PZT/PVDF压电复合材料,经过对这几种方法的分析、比较后发现溶液混合法制备的样品中PZT微粉的分散性要优于前两种制备方法;这几种制备方法中PVDF均有晶相转变,但没有较为明显的β相PVDF存在,对复合材料的电性能的影响不大.     

PZN-PZT压电陶瓷及其PVDF压电复合材料的制备和性能

采用固相烧结法合成了PZN-PZT(铌锌锆钛酸铅)三元系压电陶瓷烧结块材和粉末,并采用XRD、SEM等测试方法对其结构和性能进行了分析。PZN-PZT常压烧结陶瓷具有优良的压电性能,PZN-PZT颗粒粒径在0.5~4 μm之间,颗粒形态不太规整。采用溶液共混法将PZN-PZT粒子均匀分散于PVDF基体中,制备了PZN-PZT/PVDF 0-3型压电复合材料。研究了PZN-PZT质量分数、极化电场等因素对该压电复合材料压电和介电性能的影响。实验结果表明,选用压电活性更高的压电陶瓷粉末进行复合,可有效提高压电复合材料的压电性能。增加PZN-PZT质量分数、提高极化电压均有利于复合材料压电性能的提高。     

0-3型PZN-PZT/PVDF压电复合材料的制备工艺条件优化

采用固相法合成了性能良好的PZN-PZT陶瓷粉体.将压电陶瓷粉体分散于PVDF基体中,制备了0-3型PZN-PZT/PVDF压电复合材料.研究了复合材料的复合工艺、极化参数与压电陶瓷的含量对复合材料压电性能的影响.结果表明,溶液混合工艺较好,且当极化电场强度为6kV·mm-1、温度为110℃进行极化20min时,陶瓷粉体质量分数为90%的复合材料的压电性能最好,压电常数d33值达35.9 pC·N-1.     

压电陶瓷粒度分布对锆钛酸铅/聚偏氟乙烯复合材料电性能的影响

将不同粒度的锆钛酸铅(PZT)陶瓷粉进行复配,制成不同粒度分布的PZT陶瓷颗粒,然后与聚偏氟乙烯(PVDF)复合制备不同PZT粒度分布的PZT/PVDF复合材料,研究了复合材料的介电性能和压电性能。结果表明,当陶瓷颗粒体积分数高达70%时,双峰分布复合材料的压电系数可达75 pC·N-1。这是由于双峰分布复合材料中大陶瓷颗粒保持了完整的钙钛矿结构,小陶瓷颗粒填充在大颗粒之间,陶瓷颗粒彼此联接,形成了更多的电-力耦合通道,有效地实现了压电效应的传递。大陶瓷颗粒完整的钙钛矿结构以及大、小颗粒的协同堆砌效应,提高了PZT/PVDF复合材料的电性能。     

0-3型陶瓷/聚合物压电复合材料的压电性能研究

采用溶液共混法和热压法分别制备了PZN-PZT/PI、PZN-PZT/PVDF 0-3型压电复合材料,所得材料具有较高的压电常数和良好的可柔性加工性能。并研究分析了无机压电陶瓷种类、含量,压电聚合物类型、制备工艺与极化参数对压电系数d₃₃的影响,在一定程度上提供了提高0-3型聚合物/陶瓷压电复合材料的压电性能的途径。      

锆钛酸铅/聚苯胺/聚氨酯三元阻尼复合材料

为减少压电陶瓷/导电填料/聚合物阻尼复合材料中填料的含量,制备了锆钛酸铅(PZT)/聚苯胺/聚氨酯三元复合材料,其中,聚苯胺(PANI)通过原位聚合的方法包覆于压电陶瓷粒子的表面.采用FTIR,TGA,SEM、EDS研究了PANI包覆PZT的组成和形态.用DMA评价了复合材料的阻尼性能.结果表明,通过原位聚合的方法能够制备PANI包覆的PZT粉末;三元复合材料的阻尼性能与PANI的导电率有关,在一定的PANI导电率时达到最大,并且在任意导电率下均高于单一聚氨酯.用PANI包覆的压电陶瓷与聚合物复合,能够提高聚合物的阻尼性能.通过调整PANI的导电率,可以使材料的阻尼性能达到相应振动频率下的最大值.     

改性PZT/PVDF体系压电复合材料的介电和压电性能

采用复合材料模压工艺,制备了体积分数不同的改性PZT(含铌的钛锆酸铅)/PVDF(聚偏二氟乙烯)压电复合材料。采用扫描电镜对材料的形貌进行了分析,并利用HP4294A,Z-3A型准静态测试仪等系统地研究了改性PZT体积分数对材料介电、压电性能的影响。结果显示,在改性PZT体积分数为70%时,获得了性能优良的压电复合材料。在压电陶瓷高含量区(>0.5),部分压电陶瓷颗粒相互联接,形成了类似0-3(3-3)型复合连通形式,是复合材料获得优良压电、介电性能的主要原因。     

PVDF/PZNZT压电复合材料的结构与性能

为了扩展压电复合材料的应用领域,首先,通过固相合成法制备了0-3型聚偏氟乙烯(PVDF)/Pb(Zn_1/3Nb_2/3)_0.05Zr_0.47Ti_0.48O₃ (PZNZT)压电复合材料;然后,研究了PVDF含量对PVDF/PZNZT复合材料物相、显微结构及性能的影响。结果表明:PZNZT陶瓷粉料与PVDF粉料混合后,其平均粒度接近于纯PVDF粉料的。于220℃下烧结后, PVDF/PZNZT复合材料在XRD谱图中主要显现出PZNZT钙钛矿结构的衍射峰。当PVDF含量较低时, PZNZT陶瓷晶粒间的结合较松散;随着PVDF含量的增加,陶瓷晶粒几乎都被PVDF相包围。因显微结构不同,不同PVDF含量的PVDF/PZNZT复合材料在极化电场中呈现出不同的串、并联电路。极化后, 5wt% PVDF/PZNZT复合材料的电性能最佳,其介电常数为116、介电损耗tan δ为0.04、压电常数为48 pC/N且机电耦合系数为0.28。随PVDF含量的增加, PVDF/PZNZT复合材料的居里温度降低,维氏硬度有所增加,但仍小于纯PZNZT压电陶瓷的硬度。所得结论显示PVDF/PZNZT压电复合材料的性能可以满足水声、电声及超声换能器等的要求。      

PZT/P VDF 压电复合材料的制备及其性能研究

用氧化物一步合成法制备了PZT 粉末, X 射线衍射测试结果显示, 它是Zr/T i 为52∶48 的纯四方钙钛矿型结晶相, 并用SEM 观察了PZT 粉末的形貌; 用热分析仪测试了PVDF 的固化温度; 在自制模具上采用模压/烧结工艺获得了六种含PZT 不同体积含量的PZT/ PVDF 复合材料; 对其介电性和压电性的测试表明, 随着PZT体积含量的增加, 电性能参数呈非线性增大, 当PZT 的体积份数超过70% 时, 介电常数E和压电常数d₃₃值迅速增加, PZT 体积份数达到90% 时, 其电性能参数与纯PZT 值接近, 但此时复合材料的脆性较大, 已没有实用价值。     

Performance enhancements in poly(vinylidene fluoride)-based piezoelectric films prepared by the extrusion-casting process

The extrusion-casting process can realize large-area and continuous preparation of polymer-based films. In this paper, five different types of polyvinylidene fluoride (PVDF)-based piezoelectric films: PVDF, PVDF/PZT, PVDF/PZT@105, PVDF/PZT/BNNS and PVDF/PZT@105/BNNS were prepared by the extrusion-casting process. The mechanical, dielectric, thermal conductivity and piezoelectric properties were studied. It is found that PZT particles can well improve the dielectric performance and also the mechanical stability under variable temperature conditions. PZT powders modified by titanate coupling reagent (UP-105) can further improve the performance of the PVDF/PZT@105 films by improving the combination and dispersion of organic and inorganic phases. The addition of boron nitride nanosheets (BNNS) can improve the thermal conductivity of the films and the breakdown strength. The piezoelectric coefficient (d₃₃) of PVDF/PZT@105/BNNS composite film can reach 21pC/N, compared with the neat PVDF film (4pC/N) and PZT/PVDF (9pC/N) film realizing great improvement.

     

25 MHz ultrasonic transducers with lead- free piezoceramic, 1-3 PZT fiber-epoxy composite, and PVDF polymer active elements

This paper presents the fabrication and characterization of single-element ultrasonic transducers whose active elements are made of lead-free piezoceramic, 1-3 PZT/polymer composite and PVDF film. The lead free piezoelectric KNNLT- LS(K_0.44Na_0.52Li_0.04)(Nb_0.84Ta_0.10S_0.06b)O₃ powders and ceramics were prepared under controlled humidity and oxygen flow rate during sintering. Due to its moderate longitudinal piezoelectric charge coefficient (175 pC/N) and k_t of 0.50, the KNN-LT-LS composition may be a good candidate for highfrequency transducer applications. PZT fibers with 25 μm diameter formed by the viscose suspension spinning process were incorporated into epoxy to fabricate 1-3 composites with the averaged k_t = 0.64 and d₃₃ = 400 pC/N. Using KNN-LS-LT ceramic, 1-3 PZT fiber composite, and PVDF film, 3 different unfocused single element transducers with center frequencies of 25 MHz were fabricated. The acoustic characterization of the transducers demonstrated that wideband and low insertion loss could be obtained employing KNN-LS-LT ceramic. The ?6 dB bandwidth and insertion loss were 70% and ?21 dB, respectively. In comparison, the insertion loss of the ceramic transducer was much smaller than those made with 1-3 composite and PVDF film. This was attributed to closer electrical impedance match to 50 Ω and higher thickness coupling coefficient of the ceramic transducer.     

0—3型压电陶瓷—聚合物复合材料的制备与压电性

采用电陶瓷锆钛酸铅粉末掺入聚合物基聚偏二硫乙烯的方法，制备了柔性压电复合材料ＰＺＴ－ＰＶＤＦ。本文报导了这两种复合材料的制备工艺及其介电性和压电性，并讨论了在水听器方面的应用。     

PZT陶瓷/橡胶复合材料的压电性能

用PZT压电陶瓷粉末分散在无压电性的橡胶基体中制成压电复合材料。通过压电常数和介电常数测定、扫描电镜、介电谱等手段研究了有关因素对复合材料压电性能的影响。结果表明,复合材料的压电常数d₃₃随PZT体积含量φ和橡胶介电常数ε₁的增加而增大,随PZT介电常数ε₂的增加而减小,符合理论式 d₃₃=15φε₁d₃₃/(1-φ)(2+3φ)ε₂ 橡胶基体的极性基团、极性链节和交联健偶极的转向极化及分子链的柔性对复合材料的极化和压电常数有重要影响。橡胶的极性越大及分子链的柔性越高,则复合材料的压电常数d₃₃越高。      

Microwave Hydrothermal Synthesis PZT of Nanometer Crystal

It was focused on the applications and developments of microwave hydrothermal synthesis piezoelectric ceramic powder. The microwave hydrothermal vessel was designed and manufactured. The microwave hydrothermal synthesis system was established and the PZT piezoelectric ceramic powder was synthesized. XRD and TEM have been used to characterize the products in detail. The diameter of the PZT powder particle is from 40 to 60 nm.