氮化硅/碳化硅纳米陶瓷的显微组织与抗弯性能

研究了氮化硅／碳化硅纳米复合陶瓷经三点弯曲试验后的显微组织和断口形貌。结果表明，随着SiC纳米粉含量的增加，断口从沿晶断裂向穿晶断裂过渡；当SiC的质量分数是15％时，复合陶瓷的显微组织明显细化，抗弯强度、断裂韧度明显提高。     

2.25Cr-1Mo钢回火脆化对氢脆的影响

用冲击试验和电化学充氢方法研究了长期服役的2．25Cr-1Mo钢的回火脆化和氢脆问题．并对试样进行了显微组织分析和断口电镜扫描。结果表明：回火脆化程度不高的母材对氢脆的影响较小，断口形貌为准解理和少量的沿晶断裂；回火脆化程度较严重的焊缝对氢脆的影响较大，断口形貌为沿晶断裂。对于母材．回火脆化与氢脆的关系为线性相加；对于焊缝，回火脆化大大加剧了氢脆的程度。     

脱氢反应器内件焊缝断裂分析

采用断口扫描电镜、金相和力学计算，分析了304H脱氢反应器内件锥形封头沿焊缝的断裂原因。研究显示，内部锥形封头的环焊缝上的未焊透和未熔合缺陷是产生断裂事故的根本原因。长期在应力集中作用下缺陷尖端处出现局部的蠕变和蠕变裂纹扩展，形成空洞和沿晶断裂的颗粒状断口。操作中有过载现象，包括压力的超载，也可能因超温导致材料强度下降而使原始缺陷发生裂纹逐渐扩展（其中包括裂纹的蠕变扩展），也促进了裂纹的扩展。     

金属断口图像句法模式识别与分类方法

针对金属断口图像，提出了一种基于句法模式识别理论的分类方法。该方法通过提取断口图像上反映出的形貌特征。并将这些特征量化成特征参数，分别定义不同类型断口的全图特征参数和典型特征块特征参数，可以较好地将不同类型的断口区分开来。分别对等轴塑坑、拉长塑坑、河流花样、腐蚀疲劳、韧性沿晶和韧性疲劳六类断口进行分类识别研究。实验结果表明，这种方法具有较高的识别率。     

铝铁青铜构件失效分析

对铝铁青铜构件在安装过程中出现的断裂进行了失效分析。通过受力分析、宏观断口分析和微观分析表明，零件的设计和化学成分符合要求；但由于在组织中存在由铁铝化物、铁硅化物和共析体组成软的富铁夹杂，使其易发生沿晶脆性断裂。显微组织中富铁夹杂的出现可能与熔炼时铁的偏聚有关。     

PCrNi3MoVA钢回火脆开裂分裂

高压釜用ＰＣｒＮｉ３ＭｏＶＡ钢股役期间产生裂纹，解剖后宏观断口为结晶状，扫描电镜观察微观断口为沿晶断裂。经俄歇谱仪分析测试，杂质和合金元素在晶界偏聚，钢材的冲击韧性明显下降。分析指出，致使沆压釜开裂的原因是钢材中产生的生二类回火脆性造成的。     

PCrNi_3MoVA 钢回火脆开裂分析

高压釜用ＰＣｒＮｉ３ＭｏＶＡ钢服役期间产生裂纹，解剖后宏观断口为结晶状，扫描电镜观察微观断口为沿晶断裂。经俄歇谱仪分析测试，杂质和合金元素在晶界偏聚，钢材的冲击韧性明显下降。分析指出，致使高压釜开裂的原因是钢材中产生的第二类回火脆性造成的。     

斯贝发动机长时使用后涡轮叶片的失效分析

斯贝512-■发动机在飞机上使用3000小时后其高压一级涡轮叶片出现裂纹。分析结果表明,裂纹区渗铝涂层完全破坏,基体合金氧化腐蚀层深达50μ,断口上大部分区域为沿晶断裂,局部区域出现疲劳条带。试验证实失效是由于氧化腐蚀、蠕变和疲劳复合作用引起的。     

镍基高温合金电子束焊接头高温疲劳性能研究

利用高温疲劳试验机进行GH4169电子束焊接头在不同温度下的疲劳试验,通过接头的高温疲劳数据研究材料在不同温度下的高温疲劳性能。结果表明：随着温度的升高,GH4169电子束焊接头的疲劳性能先降低再升高,当温度达到650℃时,γ′相的析出强化了材料疲劳性能。利用SEM扫描电镜对断口进行微观分析,研究发现室温下GH4169焊接接头的断裂模式为穿晶断裂,随着温度的升高,断口多为穿晶断裂与沿晶断裂的混合断口。     

厚板窄间隙埋弧焊焊缝阶梯形断口形成机理研究

为提高2.25Cr-1Mo-0.25V耐热钢埋弧焊接头的韧性,采用冲击试验和三点弯曲试验找到接头韧性的薄弱环节,并通过进一步的微观分析,试图揭示接头韧性的弱化机理。冲击试验显示,焊缝的韧性低于母材和热影响区,因此利用三点弯曲试验,对裂纹在焊缝中的扩展过程进行更深入的研究。在三点弯曲试验时观察到焊缝中出现阶梯形断口。通过扫描电镜观察到断口表面呈现出韧窝和准解理共存的混合形貌。金相观察发现,阶梯形断口出现在焊缝的柱晶区,其方向与柱晶生长方向平行或垂直。利用苦味酸腐蚀试样,观察到阶梯形断口与结晶方向平行的部分是沿原奥氏体晶界开裂,电子背散射衍射(Electron backscattered diffraction, EBSD)试验结果也证明了这一点,而垂直于结晶方向的部分是沿层状线开裂。因此,原奥氏体晶界和层状线是焊缝中需要特别关注的部位。通过调整焊丝成分和工艺参数,减少了焊缝中的层状线,焊缝韧性明显提高。     

叶切面最大厚度数值计算与应用

以叶切面最大厚度的数值计算方法为基础,探讨叶切面最大厚度计算的计算机实现,介绍叶切面厚度数值计算法的应用实例.     

Natural frequencies of vibration of a class of solids composed of layers of isotropic materials

In a recent paper, the Ritz method with simple algebraic polynomials as trial functions was used to obtain an eigenvalue equation for the free vibration of a class of homogeneous solids with cavities. The method presented is here extended to the study of a class of non-homogeneous solids, in which each solid is composed of a number of isotropic layers with different material properties. The Cartesian coordinate system is used to describe the geometry of the solid which is modelled by means of a segment bounded by the yz, zx and xy orthogonal coordinate planes and by two curved surfaces which are defined by fairly general polynomial expressions in the coordinates x, y and z. The surface representing the interface between two material layers in the solid is also described by a polynomial expression in the coordinates x, y and z. In order to demonstrate the accuracy of the approach, natural frequencies are given for both a two- and three-layered spherical shell and for a homogeneous hollow cylinder, as computed using the present approach, and are compared with those obtained using an exact solution. Results are then given for a number of two- and three-layered cylinders and, to demonstrate the versatility of the approach, natural frequencies are given for a five-layered cantilevered beam with a central circular hole as well as for a number of composite solids of more general shape.     

盘丝极心偏对三爪自定心卡盘找标精度影响的分析

三爪自定心卡盘作为机床的主要附件,已有一百多年的发展历史,尽管目前随着数控技术的不断发展,越来越多地需求高速动力卡盘,但三爪自定心卡盘目前仍有一定的市场。 要保证卡盘可靠地夹紧工件,必须使其有可靠的夹持精度;要保持卡盘的精度,必须要严格控制各零部件公差及误差,如盘丝的极心偏。 　　极心偏是形成圆的渐开线的基圆圆心 (极心 )与盘丝内孔中心不同心所造成的偏差值。它对卡盘精度的影响分两种情况,一是卡爪夹持弧采用配磨,二是卡爪夹持弧采用单磨。本文主要探讨配磨时的影响。 　　卡爪夹持弧采用配磨,即每台卡盘整体…     

圆柱面素线的直线度公差带解析

详细分析了圆柱面素线的直线度公差带在新旧标准中定义和解释的区别，并从对圆柱面素线实际要素检测的角度，提出了推行新标准的实际意义。     

双丝杠驱动机构同步分析

介绍了双丝杠驱动机构工作原理,论述了双丝杠运动产生不同步的原因以及如何判定与解决同步问题。     

膨胀套导向机构的设计

通过分析膨胀套在实际使用产生滑移受阻现象、卡死现象原因的实质,并在分析产生问题原因的基础上提出了改进措施即：增加导向机构。     

广州地铁APM列车制动机理分析

根据广州市珠江新城旅客自动运输系统(APM)列车的运行特点,介绍APM列车制动系统的制动方式及其特点,分析APM列车动态制动和摩擦制动的工作机理及其区别和联系,阐明APM列车制动系统的电控制过程和气控制过程,从而为APM列车制动系统的维护和管理提供一定的依据.     

磨粉机快辊轴承座加工工艺设计

设计了磨粉机快辊轴承座的加工工艺和具体的工装夹具.利用卧式加工中心加工磨粉机快辊轴承座,辅以能够高效快速夹紧的夹具,既可以保证加工精度,又能够提高加工效率.     

活塞销孔加工工艺的改进

我公司于８０年代末引进Aspera公司年产８０万台冰箱（冷柜）压缩机生产线及软件技术，在压缩机加工中，活塞销孔（如图１所示）的加工是难点之一。用镗床加工，质量一直难以达到要求，废品率很高。后来我们将Aspera公司的加工工艺即精镗后滚光改为精镗后用金刚石铰刀粗、精铰孔，由此解决了这个技术难题。（１）原意大利Aspera公司工艺简述其工艺流程为：钻６．５通孔→扩孔至７＋０．１→粗镗７．４７３＋０．０３６、圆柱度０．０１→精镗至７．９３５＋０．００６、圆柱度０．００２→滚光７．９３８＋０．００６、圆柱度０…     

我校工业设计教育改革初探

针对目前市场对工业设计人才的需求,本文论述了我校在工业设计教育方面的改革措施,着重介绍了我校工业设计教育在软件和硬件方面所进行的一系列的改革。