Study on hydrogen evolution performance of the carbon supported PtRu alloy film electrodes

The carbon supported PtRu alloy film electrodes having Pt about 0.10 mg/cm2 or even less were prepared by ion beam sputtering method (IBSM). It was valued on the hydrogen analyse performance, the temperature influence factor and the stability by electroanalysis hydrogen analyse method. It was found that the carbon supported PtRu alloy film electrodes had higher hydrogen evolution performance and stability, such as the hydrogen evolution exchange current density (j0) was increase as the temperature (T) rised, and it overrun 150 mA/cm2 as the trough voltage in about 0.68V, and it only had about 2.8% decline in 500 h electrolytic process. The results demonstrated that the carbon supported PtRu alloy film electrodes kept highly catalytic activity and stability, and it were successfully used in pilot plant for producing H2 on electrolysis of H2S.     

Study on hydrogen evolution performance of the carbon supported PtRu alloy film electrodes

1IntroductionIt is the key problemthat howto transformefficiently electric energyinto hydrogen energy for propelFig.l The flowchart of indirect electrolysis of H2Sthe clean energy use extensively[1].At present,the advanced method could avoid passivation of anode bysulfur[2],andit only consumed1/2-1/3electricitythanthat by water electrolysis[3],its basic flowsheet wasshownin Fig.1.Every kinds of hydride such as H2S and so on[1-3],could be used to produce hydrogen by the way of e-lectrolysis …     

La2Mg17稀土镁基储氢合金制备工艺及储氢性能研究

采用熔剂覆盖熔炼的方法制备了La2Mg16Ni合金,并研究了该合金的吸放氢性能及吸放氢过程中合金的相结构变化.用Ni取代La2Mg17合金中的部分Mg,可提高储氢合金的吸放氢动力学性能,在温度高于553K时,所制备的储氢合金具有良好的吸放氢平台性能,其储氢容量可达到4.16％.     

以AB5储氢合金为催化剂制备碳纳米管

在750℃条件下，以AB5储氢合金为催化剂，甲烷为原料气，采用化学气相沉积法制备出多壁碳纳米管．对反应产物进行了结构和X射线衍射分析，比较了反应前后储氢合金催化剂的XRD谱图，同时探讨了储氢合金的催化机理．结果表明．AB5储氢合金粉末在高温氢气气氛下细化分解为纳米级的La和Ni金属颗粒，Ni微粒在反应中作为催化活性中心，催化甲烷裂解生长碳纳米管，而La起分散作用．     

硝酸铜改性超级电容器用煤基活性炭电极材料的电化学性能

以印尼褐煤为原料、KOH活化法制备的煤基活性炭,采用硝酸铜溶液浸渍-高温热解法对其进行改性处理,低温N 2 吸附法对改性前后活性炭的孔结构进行表征,SEM和XRD对改性前后活性炭的表面形态和微晶结构进行表征,并测定KOH对活性炭的润湿性及活性炭电极的恒流充放电、循环伏安、交流阻抗等电化学性能。结果表明：硝酸铜改性可能使部分孔隙（尤其是微孔堵塞）的比表面积和孔容积降低,但中孔率有所提高;硝酸铜改性可以提高KOH溶液对活性炭的润湿性,在活性炭表面负载氧化铜,提高活性炭对电解液的吸附能力,并产生赝电容效应,提高活性炭的电化学性能。在试验条件下改性硝酸铜溶液的最佳浓度为2%,其电容器的质量比电容可达322 F/g,并使交流阻抗等电化学性能得到改善。     

6060铝合金阳极氧化膜受热开裂行为影响因素的分析

研究了硫酸浓度、电流密度、氧化温度、氧化后存放时间、封孔时间以及加热温度和加热时间等因素,对6060铝合金阳极氧化膜受热开裂行为的影响.结果表明:在H2SO4浓度为200 g/L左右,氧化温度为19℃左右,电流密度为1.3～1.6 A/dm2的阳极氧化工艺参数下,所得到的氧化膜热裂性能较好,氧化膜的抗热裂点温度为62℃...     

用过氧化氢控制电解测定砷铜合金中的铜

采用电解重量法测定砷铜合金中的铜,可在砷铜合金电解液中加入适量的过氧化氢阻止砷(Ⅲ)在阴极上沉积.该法回收率为99.95%~102.2%,适合于砷铜合金中铜的精确测定.     

Al-RE中间合金对变形铝合金组织与性能的影响

本文以工业纯铝和混合稀土RE(Ce和La)为原料,制备出Al-8RE、Al-10RE和Al-15RE中间合金,并探讨了Al-RE中间合金对变形铝合金3102的细化机理。结果表明：Al-RE中间合金由α-Al、Al11RE3(Al11Ce3和Al11La3)、Ce和La组成,不同稀土含量Al-RE中间合金微观组织形貌不同,Al-8RE、Al-10RE和Al-15RE中间合金组织分别为亚共晶组织,伪共晶组织和过共晶组织,随稀土含量增加,Al-RE中间合金中Al11RE3相数量增多,尺寸增大;Al-RE中间合金对3102合金具有显著的细化效果,其中Al-10RE中间合金的细化效果最好;添加Al-RE中间合金可以提高产品性能,当添加10%RE时,性能提升最大。     

MINi_(5-x)(CoMnAl)_x贮氢合金铸锭的组织与性能

用XRD,SEM对感应熔炼法制备的MlNi_(5-x)(CoMnAl)_x(Ml为富镧混合稀土)贮氢合金的结构和组织进行了研究,结果表明该合金是单相CaCu_5型贮氢合金,其晶格常数为:α=0.50328nm,c=0.39812nm,用混合酸(V_(硝酸):V_(氢氟酸):V_(甘油)=1:2:3)腐蚀能观察到合金的金相组织形貌.铸态合金表层为细晶粒区,心部为粗晶粒区.EPMA分析表明铸态合金中的成分分布不均匀,心部稀土成分明显偏离平均成分.用BS-9300对合金各部位的样品粉末进行电化学性能测试,心部的电化学性能较差。     

碳纳米球储氢材料的制备及影响因素研究

无烟煤经过脱灰、炭化和预石墨化处理,然后添加活性金属,用充氢反应球磨法制得碳纳米球储氢材料.研究了原料预处理、充氢压强、活性金属等对材料储氢性能的影响.高能反应球磨时,物料在较短时间内即可达到30～50 nm,并具有较高的储氢密度和较低的放氢温度.镁和碳在储氢过程中存在协同效应,Al,Co,Fe,Ni金属催化剂能显著改善储氢材料的吸放氢性能,并对镁碳协同储氢有促进作用.     

氢含量对锆合金蠕变-疲劳行为的影响及机理研究

针对反应堆用锆合金渗氢后易发生蠕变-疲劳失效问题,采用频率修正应变寿命法和频率修正滞回能法研究了再结晶状态的锆合金在320 ^oC、不同渗氢含量下的蠕变-疲劳行为。结果表明：随保持时间增加,无渗氢试样的抗蠕变-疲劳性能降低,但保持时间30 s以上时无明显影响;保持时间对渗氢试样的抗蠕变-疲劳性能无影响。不同保持时间下,未渗氢试样的抗蠕变-疲劳性能最好,0.04%氢含量试样的性能最差,0.005%氢含量在高应变水平(高滞回能)下的抗蠕变-疲劳性能弱于0.02%氢含量试样,而在低应变水平区域优于0.02%氢含量试样。氢含量的影响机理为：固溶氢可提高蠕变-疲劳寿命,氢化物可降低蠕变-疲劳寿命;0.04%氢含量试样中氢化物起主导作用,导致其蠕变-疲劳性能最差。     

红外-热导联合法测定煤中碳氢氮含量的原理解析

为深入阐述红外-热导联合法测定煤中碳氢氮含量的原理,以图示、化学方程式和公式推导的方式对红外法和热导法在煤质分析中的应用进行了解析,指出红外法用于测定煤中碳氢含量和热导法用于测定煤中氮含量时分别使用光电和热导技术对煤中的元素进行定量分析.联合应用红外法和热导法,对提高煤质检测水平有较大的意义.     

纳米晶稀土贮氢合金高倍率放电性能的研究

对快淬法制备的纳米晶贮氢合金的高倍率放电性能进行了研究.结果表明,该贮氢合金7C放电比容量不低于260 mA.h/g,高倍率放电率不低于90%,循环寿命大于600次;10C放电比容量不低于230 mA.h/g,高倍率放电率不低于80%,循环寿命大于500次.X射线衍射分析和金相分析结果表明,该贮氢合金呈均匀的单一CaCu5型相结构,晶粒尺寸小于50nm,为柱状晶结构.     

含铟铝合金焊料及其复合带性能的研究

将铟含量不同的Al-Si-Mg-In焊料与Al-Mn芯材制成复合带材,研究了铟对复合带性能的影响。结果表明：铟含量对焊料与芯材的热复合性能影响不大;当铟含量ωln低于0.027%时,焊料中铟一越高复合带强度和钎焊性能越好;当ωln高于0.027%时,随焊料中铟含量的增加,复合带强度和钎焊性能反而下降;焊料中铟的最佳含量ωln为0.027%。     

纳米晶AB3型稀土镁基贮氢合金研究

用双辊快淬法制备的AB3型稀土镁基贮氢合金,经X射线衍射和SEM分析表明,该贮氢合金具有纳米晶结构,由LaNi3相和LaNi5相组成.PCT测试曲线显示,贮氢合金具有合适的吸放氢平台.该贮氢合金具有比容量高、循环性能稳定的优异电性能,72 mA/g放电比容量达到369 mA.h/g,460次循环后720mA/g容量衰减仅为19.4%.     

复合变质剂对ZL101铝合金力学及电化学腐蚀性能的影响

采用添加Al Ti B和四元复合变质剂对ZL101合金熔体进行处理,研究浇铸产品的力学和耐腐蚀性能。结果表明,Al Ti B和四元复合变质剂不仅能够抑制ZL101合金枝晶的生成,同时也具有良好的晶粒细化作用,加入量为0.5%,保温30 min后,在720℃浇铸变速箱的晶粒由平均150μm减小至62μm,并使合金的强度和伸长率分别提高27%和42%,同时提高ZL101合金的耐蚀性。Al Ti B和四元复合变质剂并不能改变硅形貌,将硅由未变质时的针状生长为球状或块状是Na F的作用。     

煤直接液化循环溶剂供氢性影响因素研究

在煤直接液化生产中,循环溶剂供氢性能的强弱对煤炭转化及油品收率发挥着关键作用,通过试验研究发现,在液化混合重油加工循环溶剂过程中,调整反应压力、反应温度、反应空速、催化剂活性等参数对循环溶剂供氢性能均有较大影响,尤其是反应压力、反应空速的影响更为显著。此次试验研究结果可有效指导工业生产,最大化地提高循环溶剂的供氢性能,从而间接提高煤直接液化的油收率,增加煤制油的经济效益。     

电化学析氢镍基合金材料研究进展

氢气作为一种新型绿色的可再生能源,不仅能有效缓解能源危机问题,而且还可以保护环境。过渡金属镍发现在碱性溶液中具有较高的析氢活性;由于邻近杂原子具有改变镍原子表面吸附能/解吸能的能力,还可以为某些中间体提供吸附/解吸中心,因此镍基合金的形成更有利于促进镍的电化学析氢反应。本文综述了近年来二元及多元镍基合金材料的制备方法,探讨了材料结构与电催化析氢性能之间的联系。并在此基础上,对电催化析氢镍基合金材料的研究方向和应用前景进行了展望。     

航天器用钛合金氢致结构演变及氢脆表征方法研究

采用室温电化学充氢方法对航天器用TC4钛合金式样充氢,通过对充氢式样进行XRD分析,探究了不同氢含量对钛合金结构的影响,分析了不同氢含量的合金组织结构变化及分布情况。采用慢应变速率拉伸、200h持久加载及逐级加载等力学试验,对不同氢含量的TC4合金的氢脆敏感性进行了表征,发现逐级加载不仅能提供氢脆敏感性的定性结论,同时给出不同氢含量合金试样的承载载荷定量数据。