Remarkable catalytic effect of Ni and ZrO2 nanoparticles on the hydrogen sorption properties of MgH2

In the present study, the catalytic effect of Ni and ZrO₂ nanoparticles on the hydrogen absorption and desorption properties of MgH₂ has been investigated. The MgH₂ nanocomposites were prepared by high-energy ball-milling. The morphology, phase structure, thermal behavior, and hydrogen storage properties of the materials were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), temperature-programmed desorption (TPD), differential scanning calorimetry (DSC), and the pressure-composition temperature (PCT) methods. ZrO₂ and Ni nanoparticles were homogenously dispersed into the MgH₂ matrix. The calculated apparent activation energy for dehydrogenation was 63.4 kJ/mol, which was decreased by 80.1 kJ/mol compared to that of as-milled MgH₂. As a result, MgH₂+5 wt.%Ni+5 wt.%ZrO₂ demonstrated improved dehydrogenation and hydrogenation kinetics at 310 °C. The MgH₂+5 wt.%Ni+5 wt.%ZrO₂ sample released about 6.83 wt.% and absorbed about 6.10 wt.% in less than 30 min. Therefore, the co-catalysis of Ni and ZrO₂ significantly enhances the hydrogenation and dehydrogenation properties of MgH₂.     

Catalysis derived from flower-like Ni MOF towards the hydrogen storage performance of magnesium hydride

Herein, a novel flower-like Ni MOF with good thermostability is introduced into MgH₂ for the first time, and which demonstrates excellent catalytic activity on improving hydrogen storage performance of MgH₂. The peak dehydrogenation temperature of MgH₂-5 wt.% Ni MOF is 78 °C lower than that of pure MgH₂. Besides, MgH₂-5 wt.% Ni MOF shows faster de/hydrogenation kinetics, releasing 6.4 wt% hydrogen at 300 °C within 600 s and restoring about 5.7 wt% hydrogen at 150 °C after dehydrogenation. The apparent activation energy for de/hydrogenation reactions are calculated to be 107.8 and 42.8 kJ/mol H₂ respectively, which are much lower than that of MgH₂ doped with other MOFs. In addition, the catalytic mechanism of flower-like Ni MOF is investigated in depth, through XRD, XPS and TEM methods. The high catalytic activity of flower-like Ni MOF can be attributed to the combining effect of in-situ generated Mg₂Ni/Mg₂NiH₄, MgO nanoparticles, amorphous C and remaining layered Ni MOF. This research extends the knowledge of elaborating efficient catalysts via MOFs in hydrogen storage materials.     

Synthesis of low-cost biomass charcoal-based Ni nanocatalyst and evaluation of their kinetic enhancement of MgH2

In this study, a low-cost biomass charcoal (BC)-based nickel catalyst (Ni/BC) was introduced into the MgH₂ system by ball-milling. The study demonstrated that the Ni/BC catalyst significantly improved the hydrogen desorption and absorption kinetics of MgH₂. The MgH₂ + 10 wt% Ni/BC-3 composite starts to release hydrogen at 187.8 °C, which is 162.2 °C lower than the initial dehydrogenation temperature of pure MgH₂. Besides, 6.04 wt% dehydrogenation can be achieved within 3.5 min at 300 °C. After the dehydrogenation is completed, MgH₂ + 10 wt% Ni/BC-3 can start to absorb hydrogen even at 30 °C, which achieved the absorption of 5 wt% H₂ in 60 min under the condition of 3 MPa hydrogen pressure and 125 °C. The apparent activation energies of dehydrogenation and hydrogen absorption of MgH₂ + 10 wt% Ni/BC-3 composites were 82.49 kJ/mol and 23.87 kJ/mol lower than those of pure MgH₂, respectively, which indicated that the carbon layer wrapped around MgH₂ effectively improved the cycle stability of hydrogen storage materials. Moreover, MgH₂ + 10 wt% Ni/BC-3 can still maintain 99% hydrogen storage capacity after 20 cycles. XRD, EDS, SEM and TEM revealed that the Ni/BC catalyst evenly distributed around MgH₂ formed Mg₂Ni/Mg₂NiH₄ in situ, which act as a “hydrogen pump” to boost the diffusion of hydrogen along with the Mg/MgH₂ interface. Meanwhile, the carbon layer with fantastic conductivity enormously accelerated the electron transfer. Consequently, there is no denying that the synergistic effect extremely facilitated the hydrogen absorption and desorption kinetic performance of MgH₂.     

Studies on de/rehydrogenation characteristics of nanocrystalline MgH2 co-catalyzed with Ti,Fe and Ni

In the present study, we have investigated the combined effect of different transition metals such as Ti, Fe and Ni on the de/rehydrogenation characteristics of nano MgH₂. Mechanical milling of MgH₂ with 5 wt% each of Ti, Fe and Ni for 24 h at 12 atm of H₂ pressure lead to the formation of nano MgH₂-Ti5Fe5Ni5. The decomposition temperature of nano MgH₂-Ti5Fe5Ni5 is lowered by 90 °C as compared to nano MgH₂ alone. It is also found that the nano MgH₂-Ti5Fe5Ni5 absorbs 5.3 wt% within 15 min at 270 °C and 12 atm hydrogen pressures. However, nano MgH₂ reabsorbs only 4.2 wt% under identical condition. An interesting result of the present study is that mechanical milling of MgH₂ separately with Fe and Ni besides refinement in particle size also leads to the formation of alloys Mg₂NiH₄ and Mg₂FeH₆ respectively. On the other hand, when MgH₂ is mechanically milled together with Ti, Fe and Ni, the dominant result is the formation of nano particles of MgH₂. Moreover the activation energy for dehydrogenation of nano MgH₂ co-catalyzed with Ti, Fe and Ni is 45.67 kJ/mol which is 35.71 kJ/mol lower as compared to activation energy of nano MgH₂ (81.34 kJ/mol). These results are one of the most significant in regard to improvement in de/rehydrogenation characteristics of known MgH₂ catalyzed through transition metal elements.     

Synergistic effect of rGO supported Ni3Fe on hydrogen storage performance of MgH2

Bimetallic catalysts possess unique physical and chemical properties that distinct from the individual, which offer the opportunity to ameliorate the hydrogen storage properties of MgH₂. Herein, a Ni₃Fe catalyst homogeneously loaded on the surface of reduced graphene oxide (Ni₃Fe/rGO) was prepared based on layered double hydroxide (LDH) precursor. The novel Ni₃Fe/rGO nano-catalyst was subsequently doped into MgH₂ to improve its hydrogen storage performance. The MgH₂-5 wt.% Ni₃Fe/rGO composite requires only 100 s to reach 6 wt% hydrogen capacity at 100 °C, while for MgH₂ doped with 5 wt% Ni₃Fe, Ni/rGO and Fe/rGO all require more than 500 s to uptake 3 wt% hydrogen under the same condition. The onset dehydrogenation temperature of the MgH₂-5 wt.% Ni₃Fe/rGO composite is about 185 °C, much lower than that of the MgH₂ doped with 5 wt% Ni₃Fe (205 °C), Ni/rGO (210 °C) and Fe/rGO (250 °C), and it can release H₂ completely even in 1000 s at 275 °C. Besides, the MgH₂-5 wt% Ni₃Fe/rGO displays the lowest dehydrogenation apparent activation energy of 59.3 kJ/mol calculated by Kissinger equation. The synergetic effect attributing to rGO, in-situ formed active species of Mg₂Ni and Fe is in charge of the excellent catalytic effect on hydrogen storage behavior of MgH₂. Meanwhile, this study supplies innovative insights to design high efficiency catalysts based on the LDH precursor.     

CNTs decorated with CoFeB as a dopant to remarkably improve the dehydrogenation/rehydrogenation performance and cyclic stability of MgH2

The chain-like carbon nanotubes (CNTs) decorated with CoFeB (CoFeB/CNTs) prepared by oxidation-reduction method is introduced into MgH₂ to facilitate its hydrogen storage performance. The addition of CoFeB/CNTs enables MgH₂ to start desorbing hydrogen at only 177 °C. Whereas pure MgH₂ starts hydrogen desorption at 310 °C. The dehydrogenation apparent activation energy of MgH₂ in CoFeB/CNTs doped-MgH₂ composite is only 83.2 kJ/mol, and this is about 59.5 kJ/mol lower than that of pure MgH₂. In addition, the completely dehydrogenated MgH₂−10 wt% CoFeB/CNTs sample can start to absorb hydrogen at only 30 °C. At 150 °C and 5 MPa H₂, the MgH₂ in CoFeB/CNTs doped-MgH₂ composite can absorb 6.2 wt% H₂ in 10 min. The cycling kinetics can remain rather stable up to 20 cycles, and the hydrogen storage capacity retention rate is 98.5%. The in situ formation of Co₃MgC, Fe, CoFe and B caused by the introduction of CoFeB/CNTs can provide active and nucleation sites for the dehydrogenation/rehydrogenation reactions of MgH₂. Moreover, CNTs can provide hydrogen diffusion pathways while also enhancing the thermal conductivity of the sample. All of these can facilitate the dehydrogenation/rehydrogenation performance and cyclic stability of MgH₂.     

Integrated Ni/Nb2O5 nanocatalytic agent dose for improving the hydrogenation/dehydrogenation kinetics of reacted ball milled MgH2 powders

Reactive ball milling (RBM) technique was employed to synthesize ultrafine powders of MgH₂, using high energy ball mill operated at room temperature under 50 bar of a hydrogen gas atmosphere. The MgH₂ powders obtained after 200 h of continuous RBM time composed of β and γ phases. The powders possessed nanocrystalline characteristics with an average grain of about 10 nm in diameter. The time required for complete hydrogen absorption and desorption measured at 250 °C was 500 s and 2500 s, respectively. In order to improve the hydrogenation/dehydrogenation kinetics of as synthesized MgH₂ powders, three different types of nanocatalysts (metallic Ni, Nb₂O₅ and (Ni)_x/(Nb₂O₅)_y) were utilized with different weight percentages and independently ball milled with the MgH₂ powders for 50 h under 50 bar of a hydrogen gas atmosphere. The results showed that the prepared nanocomposite MgH₂/5Ni/5Nb₂O₅ powders possessed superior hydrogenation/dehydrogenation characteristics, indexed by low values of activation energy for β-phase (68 kJ/mol) and γ-phase (74 kJ/mol). This nanocomposite system showed excellent hydrogenation/dehydrogenization behavior, indexed by the short time required to uptake (41 s) and release (121 s) of 5 wt% H₂ at 250 °C. At this temperature the synthesized nanocomposite powders possessed excellent absorption/desorption cyclability of 180 complete cycles. No serious degradation on the hydrogen storage capacity could be detected and the system exhibited nearly constant absorption and desorption values of +5.46 and −5.46 wt% H₂, respectively.     

Enhanced hydrogen properties of MgH2 by Fe nanoparticles loaded hollow carbon spheres

In the present investigation, we have reported the synergistic effect of Fe nanoparticles and hollow carbon spheres composite on the hydrogen storage properties of MgH₂. The onset desorption temperature for MgH₂ catalyzed with hollow carbon spheres and Fe nanoparticle (MgH₂-Fe-HCS) system has been observed to be 225.9 °C with a hydrogen storage capacity of 5.60 wt %. It could be able to absorb 5.60 wt % hydrogen within 55 s and desorb 5.50 wt % hydrogen within 12 min under 20 atm H₂ pressure at 300 °C. The desorption activation energy of MgH₂-Fe-HCS has been found to be 84.9 kJ/mol, whereas the desorption activation energies for as received MgH₂, Hollow carbon sphere catalyzed MgH₂ and Fe catalyzed MgH₂ are found to be 130 kJ/mol, 103 kJ/mol, and 94.2 kJ/mol respectively. MgH₂-Fe-HCS composite lowered the change in enthalpy of hydrogen desorption from MgH₂ by 20.02 kJ/mol as compared to pristine MgH₂. MgH₂-Fe-HCS shows better cyclability up to 24 cycles of hydrogenation and dehydrogenation of MgH₂. The mechanism for the better catalytic action of Fe and HCS on MgH₂ has also been discussed.     

Effects of nano size mischmetal and its oxide on improving the hydrogen sorption behaviour of MgH2

This paper reports the catalytic effects of mischmetal (Mm) and mischmetal oxide (Mm-oxide) on improving the dehydrogenation and rehydrogenation behaviour of magnesium hydride (MgH₂). It has been found that 5 wt.% is the optimum catalyst (Mm/Mm-oxide) concentration for MgH₂. The Mm and Mm-oxide catalyzed MgH₂ exhibits hydrogen desorption at significantly lower temperature and also fast rehydrogenation kinetics compared to ball-milled MgH₂ under identical conditions of temperature and pressure. The onset desorption temperature for MgH₂ catalyzed with Mm and Mm-oxide are 323 °C and 305 °C, respectively. Whereas the onset desorption temperature for the ball-milled MgH₂ is 381 °C. Thus, there is a lowering of onset desorption temperature by 58 °C for Mm and by 76 °C for Mm-oxide. The dehydrogenation activation energy of Mm-oxide catalyzed MgH₂ is 66 kJ/mol. It is 35 kJ/mol lower than ball-milled MgH₂. Additionally, the Mm-oxide catalyzed dehydrogenated Mg exhibits faster rehydrogenation kinetics. It has been noticed that in the first 10 min, the Mm-oxide catalyzed Mg (dehydrogenated MgH₂) has absorbed up to 4.75 wt.% H₂ at 315 °C under 15 atmosphere hydrogen pressure. The activation energy determined for the rehydrogenation of Mm-oxide catalyzed Mg is ∼62 kJ/mol, whereas that for the ball-milled Mg alone is ∼91 kJ/mol. Thus, there is a decrease in absorption activation energy by ∼29 kJ/mol for the Mm-oxide catalyzed Mg. In addition, Mm-oxide is the native mixture of CeO₂ and La₂O₃ which makes the duo a better catalyst than CeO₂, which is known to be an effective catalyst for MgH₂. This takes place due to the synergistic effect of CeO₂ and La₂O₃. It can thus be said that Mm-oxide is an effective catalyst for improving the hydrogen sorption behaviour of MgH₂.     

Excellent synergistic catalytic mechanism of in-situ formed nanosized Mg2Ni and multiple valence titanium for improved hydrogen desorption properties of magnesium hydride

Nowadays, catalytic doping has been regarded as one of the most promising and effective methods to improve the sluggish kinetics of magnesium hydride (MgH₂). Herein, we synthesized Ni/TiO₂ nanocomposite with the particle sizes about 20 nm by an extremely facile solvothermal method. Then, the Ni/TiO₂ nanocomposite was doped into MgH₂ to enhance its reversible hydrogen storage properties. A remarkably enhancement of de/rehydrogenation kinetics of MgH₂ can be achieved by doped with Ni/TiO₂ nanocomposite, compared to that solely doped with Ni or TiO₂ nanoparticles. The hydrogen desorption peak temperature of MgH₂Ni/TiO₂ is 232 °C, which is 135.4 °C lower than that of ball-milled MgH₂ (367.4 °C). Moreover, the MgH₂Ni/TiO₂ can desorb 6.5 wt% H₂ within 7 min at 265 °C and absorb ∼5 wt% H₂ within 10 min at 100 °C. In particular, the apparent activation energy of MgH₂Ni/TiO₂ is obviously decreased from 160.5 kJ/mol (ball-milled MgH₂) to 43.7 ± 1.5 kJ/mol. Based on the analyses of microstructure evolution, it is proved that metallic Ni particles can react with Mg easily to form fine Mg₂Ni particles after dehydrogenation, and the in-situ formed Mg₂Ni will transform into Mg₂NiH₄ in the subsequent rehydrogenation process. The significantly improved hydrogen absorption/desorption properties of MgH₂Ni/TiO₂ can be ascribed to the synergistic catalytic effect of reversible transformation of Mg₂Ni/Mg₂NiH₄ which act as “hydrogen pump”, and the multiple valence titanium compounds (Ti^4+/3+/2+) which promote the electrons transfer of MgH₂/Mg.     

Excellent catalysis of MoO3 on the hydrogen sorption of MgH2

To improve the hydrogen sorption kinetics of MgH₂, the MoO₃ nanobelts were added into MgH₂ by mechanical milling, leading to fine distribution of MoO₃ in the MgH₂ matrix. Compared to uncatalyzed MgH₂, the hydriding and dehydriding rates of MoO₃-catalyzed MgH₂ were significantly improved. The MgH₂ doped with 2 mol% MoO₃ exhibited fast dehydrogenation without activation, and the initial dehydrogenation amount of 5 wt% could be reached within 900 s at 300 °C. The dehydrogenation apparent activation energy is decreased down to 114.7 kJ/mol. The excellent catalytic effect of MoO₃ originates from its specific role as fast hydrogen diffusion pathways. In the hydrogenation process, the MoO₃ transformed to MoO₂, resulting in the fading of catalytic activity.     

Improved hydrogen storage properties of Mg/MgH2 thanks to the addition of nickel hydride complex precursors

In order to improve the hydrogenation/dehydrogenation properties of the Mg/MgH₂ system, the nickel hydride complex NiHCl(P(C₆H₁₁)₃)₂ has been added in different amounts to MgH₂ by planetary ball milling. The hydrogen storage properties of the formed composites were studied by different thermal analyses methods (temperature programmed desorption, calorimetric and pressure-composition-temperature analyses). The optimal amount of the nickel complex precursor was found to be of 20 wt%. It allows to homogeneously disperse 1.8 wt% of nickel active species at the surface of the Mg/MgH₂ particles. After the decomposition of the complex during MgH₂ dehydrogenation, the formed composite is stable upon cycling at low temperature. It can release hydrogen at 200 °C and absorb 6.3 wt% of H₂ at 100 °C in less than 1 h. The significantly enhanced H₂ storage properties are due to the impact of the highly dispersed nickel on both the kinetics and thermodynamics of the Mg/MgH₂ system. The hydrogenation and dehydrogenation enthalpies were found to be of −65 and 63 kJ/mol H₂ respectively (±75 kJ/mol H₂ for pure Mg/MgH₂) and the calculated apparent activation energies of the hydrogen uptake and release processes are of 22 and 127 kJ/mol H₂ respectively (88 and 176 kJ/mol H₂ for pure Mg/MgH₂). The change in the thermodynamics observed in the formed composite is likely to be due to the formation of a Mg_0.992Ni_0.008 phase during dehydrogenation/hydrogenation cycling. The impact of another hydride nickel precursor in which chloride has been replaced by a borohydride ligand, namely NiH(BH₄)(P(C₆H₁₁)₃)₂, is also reported.     

Effect of Ni/tubular g-C3N4 on hydrogen storage properties of MgH2

Additive doping is one of the effective methods to overcome the shortcomings of MgH₂ on the aspect of relatively high operating temperatures and slow desorption kinetics. In this paper, hollow g-C₃N₄ (TCN) tubes with a diameter of 2 μm are synthesized through the hydrothermal and high-temperature pyrolysis methods, and then nickel is chemically reduced onto TCN to form Ni/TCN composite at 278 K. Ni/TCN is then introduced into the MgH₂/Mg system by means of hydriding combustion and ball milling. The MgH₂–Ni/TCN composite starts to release hydrogen at 535 K, which is 116 K lower than the as-milled MgH₂ (651 K). The MgH₂–Ni/TCN composite absorbs 5.24 wt% H₂ within 3500 s at 423 K, and takes up 3.56 wt% H₂ within 3500 s, even at a temperature as low as 373 K. The apparent activation energy (E_a) of the MgH₂ decreases from 161.1 to 82.6 kJ/mol by the addition of Ni/TCN. Moreover, the MgH₂–Ni/TCN sample shows excellent cycle stability, with a dehydrogenation capacity retention rate of 98.0% after 10 cycles. The carbon material enhances sorption kinetics by dispersing and stabilizating MgH₂. Otherwise, the phase transformation between Mg₂NiH₄ and Mg₂NiH_0.3 accelerates the re/dehydrogenation reaction of the composite.     

Remarkable kinetics of novel Ni@CeO2–MgH2 hydrogen storage composite

Magnesium hydroxide (MgH₂) has excellent reversibility and high capacity, and is one of the most promising materials for hydrogen storage in practical applications. However, it suffers from high dehydrogenation temperature and slow sorption kinetics. Rare earth hydrides and transition metals can both significantly improve the de/hydrogenation kinetics of MgH₂. In this work, MgH₂–Mg₂NiH₄–CeH_2.73 is in-situ synthesized by introducing Ni@CeO₂ into MgH₂. The unique coating structure of Ni@CeO₂ facilitates homogeneous distribution of synergetic CeH_2.73 and Mg₂NiH₄ catalytic sites in subsequent ball milling process. The as-fabricated composite MgH₂-10 wt% Ni@CeO₂ powders possess superior hydrogenation/dehydrogenation characteristics, absorbing 4.1 wt% hydrogen within 60 min at 100 °C and releasing 5.44 wt% H₂ within 10 min at 350 °C. The apparent activation energy of MgH₂-10 wt% Ni@CeO₂ is determined to be 84.8 kJ/mol and it has favorable hydrogen cycling stability with almost no decay in capacity after 10 cycles.     

Improved hydrogen desorption properties of exfoliated graphite and graphene nanoballs modified MgH2

Magnesium hydride is a leading hydrogen storage material with high hydrogen content, however, suffers with sluggish kinetics. Several methods have been adopted to improve its kinetics, out of which, the addition of catalyst is an impressive way. Carbon materials have shown their promises as catalyst for several hydrogen storage materials. The present work is devoted to investigating the catalytic effects of exfoliated graphite and graphene nanoballs on dehydrogenation kinetics of MgH₂. The lowest onset temperature of 282 °C is observed for graphene nanoballs modified MgH₂ system. Exfoliated graphite mixed MgH₂ desorbed hydrogen at onset temperature 301 °C which is also less than the dehydrogenation temperature of pure MgH₂ (410 °C). The dehydrogenation kinetics has significantly improved by the addition of these catalysts as compared to the pure MgH₂. The activation energy for the hydrogen desorption of MgH₂ was reduced from 170 (pure MgH₂) to 136 ± 2 and 140 ± 2 kJ/mol by the addition of exfoliated graphite and graphene nanoballs, respectively. The XRD results confirmed the presence of MgH₂ after milling with exfoliated graphite and graphene nanoballs that indicates that there are no reactions during the milling thus both the additives are effective to improve the dehydrogenation as a catalyst.     

The hydrogen storage properties and reaction mechanism of the MgH2-NaAlH4 composite system

In this study, we report the hydrogen absorption/desorption properties and reaction mechanism of the MgH₂-NaAlH₄ (4:1) composite system. This composite system showed improved dehydrogenation performance compared with that of as-milled NaAlH₄ and MgH₂ alone. The dehydrogenation process in the MgH₂-NaAlH₄ composite can be divided into four stages: NaAlH₄ is first reacted with MgH₂ to form a perovskite-type hydride, NaMgH₃ and Al. In the second dehydrogenation stage, the Al phase reacts with MgH₂ to form Mg₁₇Al₁₂ phase accompanied with the self-decomposition of the excessive MgH₂. NaMgH₃ goes on to decompose to NaH during the third dehydrogenation stage, and the last stage is the decomposition of NaH. Kissinger analysis indicated that the apparent activation energy, E_A, for the MgH₂-relevent decomposition in MgH₂-NaAlH₄ composite was 148 kJ/mol, which is 20 kJ/mol less than for as-milled MgH₂ (168 kJ/mol). X-ray diffraction patterns indicate that the second, third, and fourth stages are fully reversible. It is believed that the formation of Al₁₂Mg₁₇ phase during the dehydrogenation process alters the reaction pathway of the MgH₂-NaAlH₄ (4:1) composite system and improves its thermodynamic properties.     

Characterization of microstructure,hydrogen storage kinetics and thermodynamics of ball-milled Mg90Y1.5Ce1.5Ni7 alloy

In this work, the Mg₉₀Y_1.5Ce_1.5Ni₇ sample is successfully prepared by combining the vacuum induction melting and the mechanical milling. The phase composition and microstructure characteristics are studied by X-ray diffraction, scanning electron microscopy, and transmission electron microscopy measurements. The hydrogenated sample is composed of MgH₂, Mg₂NiH₄, CeH_2.73 phases, whereas only the MgH₂ and Mg₂NiH₄ phases are decomposed during dehydrogenation. The hydrogen storage properties of Mg₉₀Y_1.5Ce_1.5Ni₇ samples are measured by semi-automatic Sievert type apparatus. It is found that the samples could be fully activated within three cycles of absorption and dehydrogenation, with a reversible hydrogen storage capacity of about 5.6 wt%. Also, the “optimal hydrogenation temperature” is reduced to 200 °C, and the dehydrogenation activation energy is calculated to be 68.2 kJ/mol and 65.8 kJ/mol by using the Arrhenius and Kissinger equations, respectively. This work provides a scientific approach to promote the practical application of Mg-based alloy.     

Microstructure characteristics,hydrogen storage thermodynamic and kinetic properties of Mg–Ni–Y based hydrogen storage alloys

In this paper, the Mg_95-X-Ni_x-Y₅ (x = 5, 10, 15) alloy were prepared by vacuum induction melting. The X-ray diffraction was used to analytical phase composition in different states, and the Scanning Electron Microscope and Transmission Electron Microscope were used to characterize the microstructure and crystalline state. Meanwhile, the kinetic properties of isothermal hydrogen adsorption and desorption at different temperatures also were tested by the Sievert isometric volume method. The results indicate that the hydrogenated Mg–Ni–Y samples is a nanocrystalline structure consists of MgH₂, Mg₂NiH₄, and YH₃ phases. And, the in-situ formed YH₃ phase not decompose in the process of dehydrogenation and evenly dispersed in the mother alloy, which plays a paly a positive the catalytic role for the reversible cyclic reaction of Mg and Mg₂Ni phases. In addition, the Ni elements are effectively to improve the thermodynamic properties of the Mg-based hydrogen storage alloy, the desorption enthalpy of the Ni₅, Ni₁₀, and Ni₁₅ samples successively decrease to 84.5, 69.1, and 63.5 kJ/mol H₂. The hydrogen absorption and desorption kinetics of the Mg–Ni–Y alloy are improved obviously with the increase of Ni content, especially for Mg₈₀Ni₁₅Y₅ alloy, which the optimal hydrogenated temperature is reduced to 200 °C, and the 90% of the maximum hydrogen storage capacity can be absorbed within 1 min, about 5.4 wt % H₂. Besides, the dehydrogenated activation energy of the Mg₈₀Ni₁₅Y₅ alloy also is reduced to 67.0 kJ/mol, and it can completely release hydrogen at 320 °C within 5 min, which is almost reached the hydrogen desorption capability of Ni₅ alloy at 360 °C. This means that Ni element is a very positive element to reduce the hydrogen desorption temperature.     

Enhanced hydrogen storage properties of 4MgH2 + LiAlH4 composite system by doping with Fe2O3 nanopowder

In this paper, the hydrogen storage properties and reaction mechanism of the 4MgH₂ + LiAlH₄ composite system with the addition of Fe₂O₃ nanopowder were investigated. Temperature-programmed-desorption results show that the addition of 5 wt.% Fe₂O₃ to the 4MgH₂ + LiAlH₄ composite system improves the onset desorption temperature to 95 °C and 270 °C for the first two dehydrogenation stage, which is lower 40 °C and 10 °C than the undoped composite. The dehydrogenation and rehydrogenation kinetics of 5 wt.% Fe₂O₃-doped 4MgH₂ + LiAlH₄ composite were also improved significantly as compared to the undoped composite. Differential scanning calorimetry measurements indicate that the enthalpy change in the 4MgH₂–LiAlH₄ composite system was unaffected by the addition of Fe₂O₃ nanopowder. The Kissinger analysis demonstrated that the apparent activation energy of the 4MgH₂ + LiAlH₄ composite (125.6 kJ/mol) was reduced to 117.1 kJ/mol after doping with 5 wt.% Fe₂O₃. Meanwhile, the X-ray diffraction analysis shows the formation of a new phase of Li₂Fe₃O₄ in the doped composite after the dehydrogenation and rehydrogenation process. It is believed that Li₂Fe₃O₄ acts as an actual catalyst in the 4MgH₂ + LiAlH₄ + 5 wt.% Fe₂O₃ composite which may promote the interaction of MgH₂ and LiAlH₄ and thus accelerate the hydrogen sorption performance of the MgH₂ + LiAlH₄ composite system.     

Dual-tuning effect of In on the thermodynamic and kinetic properties of Mg2Ni dehydrogenation

Mg₂In_0.1Ni solid solution with an Mg₂Ni-type structure has been synthesized and its hydrogen storage properties have been investigated. The results showed that the introduction of In into Mg₂Ni not only significantly improved the dehydrogenation kinetics but also greatly lowered the thermodynamic stability. The dehydrogenation activation energy (E_a) and enthalpy change (ΔH) decreased from 80 kJ/mol and 64.5 kJ/mol H₂ to 28.9 kJ/mol and 38.4 kJ/mol H₂, respectively. The obtained results point to a method for improving not only the thermodynamic but also the kinetic properties of hydrogen storage materials.