铜钼混合精矿分离浮选试验研究

对国内某大型铜钼矿浮选厂的铜钼混合精矿进行了分离浮选试验研究.在分离前对精矿进行强化脱药,采用组合抑制剂YF851和YF212进行分段抑制,可显著改善铜钼分离效果,获得了较好试验指标:钼精矿品位为49.91%、含铜0.69%,钼回收率为84.45%;铜精矿品位为32.90%,含钼0.07%,铜回收率为99.98%.     

新疆某钼矿选矿试验研究

新疆某钼矿是具有较高开发价值的硫化钼矿床。原矿含钼0.11%,主要目的矿物辉钼矿的嵌布粒度较粗,多在0.1 mm左右,钼氧化率7.69%。主要脉石矿物为石英、绢云母和粘土矿物。选矿试验最终采用"钼硫混合浮选—钼硫分离"的工艺流程。钼硫混合浮选采用BP+乳化煤油作捕收剂,经一粗三扫二精后获得钼硫混合精矿;混合精矿经再磨后,采用石灰+水玻璃+硫化钠作抑制剂,经一粗三扫四精获得钼精矿产品。闭路试验中矿顺序返回,获得了含Mo 52.05%,钼回收率92.25%的精矿产品。     

新型硫化铁矿抑制剂T-506在某铜钼矿浮选中的应用研究

某大型铜钼矿,原矿含铜0.49%,钼0.021%,硫3.89%,矿石性质复杂,现场采用铜钼混合浮选,最终铜钼分离的浮选工艺流程。在铜钼混合浮选作业中,采用石灰作为硫化铁矿的抑制剂,生产中出现石灰用量大,指标不稳定,尤其是精矿铜品位达不到18%的标准要求。经过大量试验,确定采用新型抑制剂T-506与石灰联合作为硫化铁矿的抑制剂,最终取得铜回收率88.23%,精矿铜品位22.06%的较理想选矿指标。     

某铜矿石选矿试验研究

根据矿石中铜钼矿物嵌布特征,试验采用铜钼混合浮选方案,铜钼粗精矿两次精选后再磨,然后进行铜钼分离;由于原矿钼含量较低,采用多次精选钼品位达到合格品级.原矿含铜0.454%,含钼0.035%,试验获得铜精矿含铜20.03%,回收率88.57%,钼精矿含钼45.10%,回收率为71.89%.     

河南某含金银硫化铜矿选矿试验研究

对河南某含金银硫化铜矿开展了工艺矿物学和选矿试验研究。结果表明：矿石中主要有用元素铜含量为0.82%,伴生的有益组分为硫、金和银,主要有用金属矿物为黄铜矿、辉铜矿和黄铁矿,脉石矿物主要为石英。试验以新型药剂TB1021为铜硫分离捕收剂,采用混合浮选—铜硫分离工艺获得铜精矿和硫精矿,硫精矿再经摇床重选回收部分微细粒铜精矿。混合浮选采用丁基黄药和丁铵黑药组合捕收剂,总药剂用量为120 g/t,采用一粗两精三扫工艺流程;铜硫分离浮选采用新型捕收剂TB1021,采用一粗三精三扫工艺流程。最终获得铜品位为15.21%、铜回收率为80.13%,金品位为3.02 g/t、金回收率为66.51%,银品位为160.43 g/t、银回收率为41.82%的铜精矿,以及硫品位为49.13%、回收率为54.34%的硫精矿。     

低品位铜钼精矿三级流动性脱药铜钼分离试验研究

甲玛铜钼混合精矿因药剂、微细粒泥和辉钼矿紧密吸附,导致钼品位及回收率很难提高,针对这一技术难题,对该含泥铜钼精矿进行了详细的试验研究,最终获得流动性摩擦脱药高浓度浮选新工艺在铜钼混合浮选-抑铜浮钼中应用。采用此工艺进行试验,在铜钼混合精矿钼品位0.52%,铜品位23.37%的情况下,可获得钼精矿钼品位45.19%、作业回收率82.05%,铜精矿铜品位23.58%、作业回收率99.95%的生产指标,为该含泥低品位铜钼矿石的选矿提供了技术依据。该技术理念可作为铜、铅、锌、金、银、钼、硫、铁等依次浮选设计资源依据。     

某高铁铜硫矿石的选矿试验工艺研究

针对某高铁铜硫矿石的性质,将原矿磨至细度为≤74μm占70%、以碳酸钠为pH调整剂、丁基黄药+丁铵黑药为组合捕收剂混合浮选铜硫,铜硫粗精矿再磨至≤45μm占85%后,主要以新型无机抑制剂DT-2#(次氯酸钙为有效成分)为黄铁矿抑制剂进行铜硫分离,浮选尾矿进行磁选选铁.试验结果表明,采用"铜硫混浮-粗精矿再磨-铜硫分离-浮选尾矿磁选"流程,在原矿含铜0.52%、硫2.31%、铁49.26%的条件下,可获得含铜22.36%、回收率为87.29%的铜精矿,含硫38.43%、回收率为62.88%的硫精矿,含铁66.98%,回收率为91.34%的铁精矿.所用工艺流程简单,选矿指标较佳.     

某低品位铜钼矿浮选及分离试验研究

针对广西某低品位斑岩型铜钼矿开展了浮选试验研究。该铜钼矿中的硫化矿物具有复杂的交代嵌生关系,本研究采用铜钼硫混浮-混合精矿再磨-铜钼与硫分离-铜钼分离的工艺流程,提高了交代嵌生的黄铜矿、辉钼矿、黄铁矿的单体解离度。同时,采用硫化钠+氧肟酸淀粉作为铜矿物的组合抑制剂,实现了铜钼矿物的有效分离。     

某难选高硫含铜白钨矿选矿试验研究

某难选高硫含铜白钨矿中钨主要以白钨矿的形式存在,硫化铁主要以磁黄铁矿的形式存在。为给该矿石的开发利用提供技术支持,采用磁选-铜硫混合浮选-白钨浮选原则流程进行条件试验。结果表明,原矿磨矿至-74μm占65%时进行磁选,可获得品位为38.33%、回收率为51.14%的硫精矿,而磁选尾矿经铜硫混合-铜硫分离浮选,可分别获得品位为20.06%、回收率为73.12%的铜精矿和品位为35.20%、回收率为42.11%的硫精矿;其中铜硫混合浮选尾矿以碳酸钠为调整剂、水玻璃为抑制剂、731氧化石蜡皂为捕收剂,进行一粗一扫三精白钨常温浮选,可得到WO_3品位为63.93%、回收率为89.60%的白钨精矿,有效地实现了铜硫的分离和白钨矿的回收。     

某选铁尾矿低碱度铜硫分离试验研究

针对某选铁尾矿矿石性质,进行铜硫混合浮选,混合精矿再磨后铜硫分离的选别工艺,以乙黄药+丁胺黑药为组合捕收剂,新型抑制剂DT-4与石灰为铜硫分离抑制剂,进行铜硫浮选试验,最终获得铜品位26.68%,回收率80.39%铜精矿;硫品位47.68%,回收率74.82% 硫精矿,实现了铜硫的分离及铜硫的综合回收。     

难选铜钼矿铜钼分离新工艺研究

以某地斑岩型铜钼矿浮选产出的铜钼混合精矿为原料,经650℃焙烧后先用水浸出部分铜,浸铜渣用纯碱浸出钼,钼浸出率达96 05%,浸出液中的钼可用沉淀法回收。铜在浸钼渣中的品位达27 93%,并含有13 8g/t金和144g/t银。     

某钼铜硫多金属矿钼铜混合浮选分离研究

对某铜钼硫多金属矿进行了选矿试验。采用钼铜混合浮选再分离工艺流程,在原矿含 Mo 0．17％、Cu 0．137％、S 5．36％、Pb 0．067％的条件下,获得了含钼49．26％、钼回收率82．66％的钼精矿及含铜15．45％、铜回收率53．52％的铜精矿。实现了钼铜硫矿物与脉石及钼铜硫矿物之间的有效分离,获得了良好的技术指标。     

某斑岩型铜钼矿等可浮浮选分离研究

对某斑岩型铜钼矿进行了选矿试验研究。采用钼铜等可浮浮选再分离-强化选铜工艺流程,采用CSU31作等可浮浮选捕收剂,在原矿含铜0．49％、含钼0．0115％的条件下,获得了含铜26．71％、总铜回收率86．11％的铜精矿及含钼48．03％、钼回收率83．53％的钼精矿,实现了铜、钼矿物与脉石的有效分离,获得了良好的技术指标。     

陕西某低品位铜钼矿选矿试验研究

The copper grade the low-grade copper-molybdenum ore in Shaanxi is 0.32% and the molybdenum grade is 0.048%.The copper and molybdenum minerals mainly exist in the form of sulfide ore. The properties are complex that there are many kinds of minerals in the ore, which are closely distributed and fine dissemination size. According to the properties of the ore, the technological process of bulk flotation and separation of copper and molybdenum was adopted in the experiment. With lime as regulator and reagent L03 as collector, the mixed concentrate of copper and molybdenum was obtained by the bulk flotation which flow-sheet is one roughing, three refining and two scavenging process. Then regrinding the mixed concentrate, use sodium sulfide as inhibitor of copper minerals, sodium silicate as slurry dispersant and inhibitor of silicate gangue minerals , kerosene as collector, can separate copper and molybdenum with the flow-sheet which one roughing, five refining and three scavenging. The copper concentrate with copper grade of 18.82% and copper recovery rate of 85.35% and molybdenum concentrate with molybdenum grade of 47.14% and molybdenum recovery rate of 79.24% were obtained by the final closed-circuit flotation test process, the indicator is nearly ideal.     

江西某钨矿重选尾矿中硫化矿的回收试验研究

江西某钨多金属矿中钨矿主要为黑钨矿,矿石中具有回收价值的元素为WO3、Sn、Mo、Cu.该钨多金属矿经常规重选回收钨锡矿物后,尾矿中含有大量黄铜矿、辉钼矿.试验针对此重选尾矿的性质特点,采用铜钼混浮再分离的浮选工艺回收硫化矿,取得较好指标,获得铜精矿中C u品位23.13%,回收率95.21%;钼精矿中Mo品位43.49%,回收率81.93%.     

超声波强化铜钼浮选过程的研究

斑岩型铜钼矿具有矿石性质复杂、嵌布粒度细、辉钼矿与黄铜矿可浮性相近等特点,导致在浮选过程中铜钼分离困难。利用超声波改变矿浆性质、矿物表面性质及药剂溶液性质。通过对某铜钼矿石采用超声波技术处理强化铜钼浮选分离,纯矿物浮选研究表明,采用超声波处理可以有效实现黄铜矿与辉钼矿的分离。实际矿石分选表明:在磨矿浓度为66.7%、矿浆pH=10.0、石灰用量为450 g/t、水玻璃用量为1 kg/t、YC药剂+丁基黄药用量为160 g/t+50 g/t、2#油30 g/t、磨矿细度 < 0.074 mm占77.2%时,获得混合铜钼精矿钼品位为2.96%,钼回收率为87.44%;铜品位为0.76%,铜回收率为92.77%。对铜钼混合精矿,在矿浆浓度10%下,经超声功率2 000 W处理时间20 min,浮选条件为矿浆pH=10、煤油用量为80 g/t、2#油用量为15 g/t、硫化钠用量为300 g/t,获得最终钼精矿Mo品位为22.19%,作业回收率为95.95%,钼总回收率为83.90%;铜精矿Cu品位为11.88%,作业回收率为98.27%,铜总回收率为91.16%,实现了铜钼矿物良好分离。      

香格里拉铜硫矿选矿工艺研究

针对香格里拉铜硫矿的矿石性质,进行了先铜后硫的优先浮选工艺流程和铜硫混选一分离工艺流程及这两种工艺的粗精矿再磨试验研究,通过对三种工艺流程浮选指标的对比,最终确定了原矿磨矿（80％．74μm）人选的优先浮选工艺流程,在其小型闭路试验中可以获得铜品位19．80％,铜回收率83．06％的铜精矿;硫品位40．35％、硫回收率66．32％的硫精矿。有价元素铜、硫得到了有效回收。     

内蒙古兴和县曹四夭超大型钼矿床物质组成及选矿新工艺研究

曹四夭超大型钼矿床赋矿围岩为中太古界中深变质结晶岩系,主要矿石类型为细脉浸染状。除主要有用矿物辉钼矿外,尚含少量黄铁矿、黄铜矿及磁黄铁矿。总体选矿方案为浮选,通过一段、二段探索性试验、细度条件实验、开路实验及闭路实验,使Mo的回收率达到93.02%,最终钼精矿的品位达45.48%,达到行业标准二级品二类要求,充分证明该矿床矿石为易选。     

某高品位钼铋硫化矿选矿试验研究

内蒙古某钼铋多金属硫化矿,含钼0.65 %,含铋1.12 %,钼铋品位较高,有较大的工业回收价值.采用“混合浮选—钼铋分离”的选矿工艺回收该矿石中的有用矿物,以乙硫氮和煤油作为捕收剂进行混合浮选,以硫化钠和亚硫酸钠作为组合抑制剂,煤油为捕收剂进行钼铋分离,最终实验室小型闭路试验可以获得含钼47.31 %,钼回收率89.52 %的钼精矿以及含铋42.64 %,铋回收率86.04 %的铋精矿,较好地实现了钼铋分离.      

某铜钼矿铜钼分离工艺试验研究

介绍了某铜钼矿石铜钼分离的药剂试验成果，在硫化钠用量15．5kg／t、水玻璃用量0．55kg／t，闭路试验指标：当铜钼混合精矿中含铜17．85％，钼0．251％时，获得的钼精矿品位46．77％，钼回收率85．72％，其中含铜0．205％，铜精矿品位17．93％，铜回收率99．995％。