纺织用纸线原纸的研究

分析了进口纸线原纸的纤维形态、组成及配比;测定了原纸的各项物理性能指标;研究了在针叶木浆中配加棉浆、细菌纤维以及水溶性PVA纤维对纸张强度性能的影响.结果表明当纤维配比为木浆纤维棉浆纤维细菌纤维水溶性纤维=81∶10∶7∶2,且分散剂PEO用量0.07%,湿强剂PAE用量1.8%,CMC用量0.3%时,纸线原纸的主要物理性能为干抗张指数71.10 N·m/g,湿抗张指数30.03N·m/g,撕裂指数8.01 mN·m2/g,耐折度460次、伸长率2.46%.     

聚氨酯乳液在纸张涂布中的应用研究

将咪唑、甲苯-2,4-二异氰酸酯和聚乙二醇(相对分子质量600)合成的聚氨酯预聚体(咪唑-TDI-PEG600)乳液用于纸张涂布,研究其对纸张物理强度的影响。结果表明,当聚氨酯乳液的涂布量为7 g/m2时,纸张的耐折度、撕裂度、抗张强度等物理性能均有明显改善,涂布后滤纸的湿抗张指数、干抗张指数分别为滤纸原纸的19.6倍和1.7倍,耐折度为滤纸原纸的47.0倍。扫描电镜观察显示,聚氨酯乳液的加入使纸张纤维间连接了许多丝状和薄膜状物质,这些物质在纤维之间尤其是纤维与纤维交叉的区域形成架桥,从而使纤维间的连接更紧密。     

动态纸页成形器模拟多层斜网成形器生产水溶性PVA纤维高强纸工艺探讨

采用动态纸页成形器(DSF)模拟实际生产中多层斜网成形器实现纸张的分层抄造,分析讨论水溶性PVA纤维在纸张结构中不同位置对成纸强度性能的影响;探讨纸张成形、干燥过程对PVA纤维结合状况、成纸纵横向强度等主要物理性能的影响;通过优化DSF运行参数,在针叶木长纤维(NBSK)浆料中添加0.8%~1.0%的PVA 70纤维(即温度在70℃左右时就能完全溶解的PVA纤维),压榨气控箱压力在0.2~0.3 MPa之间,干燥温度在95℃情况下,可获得最优增强作用。     

铜版原纸内结合强度影响因素的探讨

铜版原纸的内结合强度是指纤维之间通过氢键结合而产生的强度．它是除纤维自身强度以外影响纸张强度的另一重要因素。它是与纸面垂直的抗张强度．即Z向强度。内结合强度对印刷性能非常重要。如果内结合强度太低，在平板式胶版印刷时．涂布纸可能在原纸处产生脱层现象。因为平板式胶印常用高黏油墨。在HSWO中是以加温来烘干油墨，如果原纸的内结合强度太低，可能由于蒸发水分，增加了原纸中蒸汽压力而导致鼓泡。所以控制原纸的内结合强度对铜版纸生产具有重要意义。     

PLA/苎麻与PVA/苎麻复合材料的制备及其力学性能研究

采用碱-硅烷偶联剂表面复合改性处理,以苎麻织物作为增强材料,分别以聚乳酸(PLA)和聚乙烯醇(PVA)为基体,经过层合热压制备出环保的苎麻织物增强复合材料,对其进行拉伸、弯曲测试,并用SEM进行表征。结果表明,PLA/苎麻、PVA/苎麻复合材料拉伸强度、弯曲强度相比未经表面改性处理复合材料,其提高幅度分别为44.42%、31.45%、35.88%、18.47%。PLA/苎麻、PVA/苎麻增强复合材料纬向拉伸强度和弯曲强度大于经向;SEM结果表明:改性处理后,苎麻纤维表面干净、杂质少,复合材料的界面结合效果较好。PLA基体相较于PVA对苎麻的浸润效果较好。拉伸断裂方式均为韧性断裂,断口参差不齐。     

乙二醛/尿素树脂改善瓦楞原纸强度性能的研究

为改善瓦楞原纸在高湿环境下(80%)的强度性能,克服传统湿强剂释放游离甲醛的缺点(例如UF树脂),采用乙二醛和尿素为原料合成GU树脂对瓦楞原纸进行表面处理。当树脂中乙二醛与尿素的摩尔比R为1.50/1,用量为5%(绝干纸)时,制备的GU树脂对瓦楞原纸的强度性能改善的效果最理想其抗张强度、撕裂度、耐折度、环压强度达到了较好的水平。瓦楞原纸的质量等级由D级提高到A级,较高的提升产品的质量和市场价值。     

芳纶增强阻燃耐磨型装饰原纸的制备及性能研究

以针叶木纤维为基体,通过引入聚多巴胺(PDA)表面修饰后的芳纶纤维(AF)作为增强体,采用湿法成型制备了PDA/AF装饰原纸,重点研究了PDA/AF添加量对装饰原纸物理性能、摩擦磨损性能以及阻燃性能的影响,并探讨了其影响机制。研究结果表明,当PDA/AF添加量为25%时,PDA/AF装饰原纸的干抗张指数为34.2 N·m/g,湿抗张指数为7.56 N·m/g,相比针叶木浆装饰原纸分别提高了22%和80%;磨损率为2.43×10~(-4)mm~3/J,最大热释放速率(PHRR)为125.21 W/g,相比针叶木浆装饰原纸分别降低了46.48%和20.55%,且烟密度明显降低。     

聚乙烯醇在造纸中的应用实验

研究了聚乙烯醇(PVA)在纸张中的应用，通过控制PVA加入状态及其与LSR纤维的配比，研究其对纸张物理性能的影响，同时对所制备的纸张进行二次疏解，并重新进行抄纸，研究二次疏解对纸张性能的影响。研究结果表明：当PVA与LSR纤维配比为1%时，与PVA以溶液形式相比，PVA以纤维状态加入所制备出手抄片的抗张强度提高了47.07%，同时经过二次疏解重新抄纸，与未加PVA纤维的纸张相比，纸张的各项物理性能较优。因此，纸张中加入1%的PVA纤维有利于提升纸张性能，同时还有助于提升废旧纸张二次利用的可行性。     

高档美纹纸层间剥离强度的研究

通过打浆处理、化学品的选择和使用对美纹纸层间剥离强度的影响进行探讨,寻找经济可行的方法来提升美纹纸层间剥离强度。实验结果表明,添加用量0.5%(相对于绝干浆)的环氧氯丙烷树脂(PAE)对美纹纸的层间剥离强度有一定的促进作用;阳离子淀粉可以显著提高美纹纸的层间剥离强度,但成纸较硬,对美纹纸的使用造成负面影响;在PAE用量0.5%的体系中,添加两性聚丙烯酰胺(ACPAM)或羧甲基纤维素(CMC)均有利于美纹纸层间剥离强度的提升,混合添加ACPAM和CMC比分别添加ACPAM或CMC更经济可行;适当调整打浆工艺,添加用量0.05%的ACPAM和用量0.05%的CMC,美纹纸的层间剥离强度可以提升34.8%;添加用量0.05%的ACPAM和用量0.10%的CMC,美纹纸的层间剥离强度可以提升50.6%。     

封闭型水性聚氨酯在造纸湿部的应用

研究咪唑、甲苯-2,4-二异氰酸酯和聚乙二醇600形成的聚氨酯预聚体在造纸湿部添加中的应用。用咪唑-TDI-PEG600聚氨酯预聚体(简称LTP600)溶液,添加到纸浆中,讨论了添加量分别为2%、4%、7%、10%和12%(相对于绝干浆的量)时,成纸各项物理性能的变化。研究结果表明:当LTP600添加量为7%时,成纸的耐折度、抗张强度等物理性能都有明显改善,处理后成纸的湿抗张指数、干抗张指数分别提高到原纸的4.96和2.21倍,耐折度提高了1.44倍。扫描电镜观察可以看出加聚氨酯预聚体进行聚氨酯化后,纸页的纤维间连接了许多丝状和薄膜状物质,这些物质在纤维之间尤其是纤维与纤维交叉的地方形成架桥结构,从而加强了纤维之间的连接。     

不同组织结构织物的拉伸、撕裂和冲击强力效果

织物的组织结构通过组织因子和交织指数表达,这些因素之间的联系是r=0.98,R2=0.97。研究了这些参数对织物拉伸、撕裂和冲击强力的影响。织物的拉伸性能受其参数和结构的影响。因此,这项工作可以帮助理解织物相关强度的决定因素。试验研究织物中纱线相互交织或交错模式对拉伸、撕裂和冲击强力的影响。以12种具有代表性的不同交织方式织成的织物作为研究的对象。本试验工作表明:在这些不同的组织结构中,平纹的组织因子和交织指数是12种组织中最高的,花式组织最低,表明织造类型影响织物的强度性能。利用方差分析帮助进行结果分析。     

Exploring the potential of milkweed stalk in wood plastic manufacture

The physical and mechanical properties of milkweed composites based on different loads of milkweed flour and maleic anhydride grafted polypropylene (MAPP) using polypropylene as matrix are investigated in this study. There levels of milkweed fibers (30, 40, and 50 wt.%), one level of mixed milkweed flour (20:20 wt.% fiber:bark), and two levels of MAPP (4 and 6 wt.%) were used to prepare natural fiber-reinforced composites. Physical and mechanical properties including flexural, tension, impact, and thickness swelling were evaluated according to ASTM standards. The result demonstrated that addition of milkweed flour fluctuates mechanical properties of reinforced composite. However, the optimum load of milkweed flour was different in each test. Generally, 40 wt.% mixed flour composite in comparison with 40 wt.% milkweed composite showed lower mechanical results and higher thickness swelling. MAPP as a coupling agent improved physical and mechanical properties of milkweed-filled composites in most properties. The results of this study depicted positive effects of lignocellulose fibers and coupling gent and also negative effect of bark flour as a function of lower cellulose and higher extractive contents on physical and mechanical properties of milkweed-reinforced composites.     

聚丙烯酰胺在牛皮纸生产中的干增强效果

在牛皮纸生产中,用聚丙烯酰胺千强剂来替代两性淀粉提高纸张的干强度,对比了几种聚丙烯酰胺类增强剂的使用效果,并选用阳离子聚丙烯酰胺增强剂LX进行了中试试验.通过试验发现,在保证成纸原有干强度的前提下,增强剂LX用量为5 kg/t（纸）时,可替代两性淀粉8 kg/t（纸）,同时阳离子松香胶用量降低了2 kg/t（纸）,硫酸铝用量降低了22 kg/t（纸）,吨纸成本比现有工艺降低38元.     

纱线动态强力的测试与研究

纱线的动态强力作为衡量纱线产品质量的重要性质，克服了传统纱线强力指标的局限性，可以更加真实地反映纱线在动态条件下的力学性能。文章利用美国劳森公司的CTT纱线性能测试仪时纱线的动态强力进行了测试研究，对影响纱线动态强力的因素如纤维的长度、纱线的细度、纱线的种类以及纱线运行速度等进行了分析探讨。     

提高明胶可食膜机械强度和热封强度的研究

研究了明胶可食膜的机械强度和热封强度。结果表明：明胶可食膜的机械强度和热封强度受干燥温度的影响大,随干燥温度的升高,明胶膜机械强度和热封强度均呈先递增后递减的变化趋势,其最适干燥温度为６０℃;掺用少量琼脂（０．０２％）可明显改善明胶膜的机械强度和热封强度,特别是其断裂伸长率;用０．２％甘油增塑的明胶膜,其抗拉强度,直角撕裂强度均有所改善,但其热封强度稍有下降;明胶膜在贮藏过程中（－１８、０、２０、４０℃,相对湿度６５％）,其机械强度先递减后趋于稳定,但其热封强度变化不明显。     

The use of nisin as a preservative in fish sausage stored at ambient (28 ± 2 °C) and refrigerated (6 ± 2 °C) temperatures

Summary The efficacy of nisin at three different concentrations, 12.5, 25 and 50 ppm, on the keeping quality of fish sausage in synthetic casing at ambient (28 ± 2 °C) and refrigerated (6 ± 2 °C) temperatures was assessed. Gel strength, expressible water content, total volatile base nitrogen, total plate count and aerobic spore counts were affected by the storage temperatures and nisin concentrations used. Fish sausage treated with 50 ppm of nisin was acceptable after storage at ambient temperature for 20–22 days compared with the control, which were acceptable only for 2 days. The keeping quality of the sausages, at refrigerated temperature, varied from 30 days in the control to 150 days in 50‐ppm nisin‐treated samples. The residual nisin decreased slowly in samples stored at refrigerated temperature, whereas, in fish sausages stored at ambient temperature, the decrease was rapid. Nisin at 50‐ppm level showed a significant effect (P ≤ 0.05) on the gel strength and overall acceptability scores both at ambient and refrigerated temperature.     

干强剂PS-210在铜版原纸生产中的应用

为了提高铜版纸的表面强度,在生产中使用了干强剂PS-210,取得了较好的效果,不仅达到了增强的目的,而且改善了助留助滤效果、节约了生产成本、降轻了废水污染负荷。     

无捻纱平纹机织物机械强力研究

使用扯边纱条样法、单舌撕破法、弹子法对无捻纱平纹机织物和有捻纱平纹机织物的拉伸断裂强力、撕破强力以及顶破强力进行了比较研究。发现无捻纱织物的机械强力低于相应的有捻纱织物的机械强力,并分析了原因,提出了改善无捻纱机械强力的方法。     

商业纤维素酶和磨浆对硫酸盐浆性能的影响:机械处理和酶活性成分影响之间的相互关系

在造纸工业中,酶在生物技术催化剂中的重要性已经得到公认。此次研究选取了五种商业酶来改性纤维。结果显示,经过酶预处理后,浆料达到相同的游离度(下降200m l)所消耗的PFI磨浆机转数大约是未经处理的一半。并且,经过酶预处理及PFI磨浆后,手抄片的性能也会发生改变。最终得出结论,纤维经过酶C1和酶C4在p H=7下预处理后,其手抄片的撕裂强度略微下降。而经过酶C2、酶C3和酶C5预处理后,撕裂强度下降最明显。具有木聚糖酶活性的酶C1和酶C4预处理浆料后能够改善纸张性能,但是其他酶对纸的性能产生了负面影响。因此,水解纤维素活性和水解半纤维素活性之间复杂的平衡是优化生物质精炼和纸张性能的关键。同时发现,p H对酶C1的影响很大,这表明控制p H在开发减少磨浆能耗的酶策略中的重要性。