核壳结构TiO2/Ag反蛋白石的制备与形貌观察

用化学还原法制备了银包覆聚苯乙烯(PS)微球结构,通过垂直沉积法排列出具有密堆积结构的PS-Ag蛋白石模板,然后采用溶胶-凝胶法渗透TiO2,最后焙 烧 处 理 除 去PS,制 备 出 了 规 整 的 核 壳 结 构TiO2/Ag反蛋白石。采用扫描电镜、透射电镜和X射线衍射对该样品进行了分析。结果表明,PS球表面包覆的为纳米尺度的金属银;所制备的PS/Ag核壳微球蛋白石经过480℃、12h焙烧处理后获得的核壳TiO2/Ag反蛋白石结构的单胞参数可以通过调节包覆银层的厚度来调变,即改变AgNO3与PS球的质量比获得具有不同银包覆层厚度、不同单胞参数的三维蛋白石和反蛋白石结构。     

纳米尺度PS/Ag核壳结构复合球的制备与表征

采用分步法制备了聚苯乙烯/银(PS/Ag)核壳结构复合纳米球。首先采用无皂乳液聚合法并利用丙烯酸(AA)的羧基对制备的PS球进行改性,使其表面带负电荷;然后通过静电吸附作用在改性PS球的表面沉积[Ag(NH3)2]+,水浴(80℃)环境中利用十二烷基磺酸钠(SDS)作为还原剂将PS球表面的[Ag(NH3)2]+还原,制备出PS/Ag核壳结构复合球。通过动态激光粒度分析仪和透射电子显微镜对PS/Ag核壳纳米球的粒度分布、形貌和结构进行了表征,研究了AA的用量对复合球粒径及包覆的Ag壳厚度的影响。结果表明,随着AA用量的增大,所包覆的银层更加致密,厚度增大,当AA用量为15%时可得到Ag完全包覆的PS/Ag复合纳米球。     

无皂乳液聚合法制备PS/TiO2核-壳复合微球

采用无皂乳液聚合法制备聚苯乙烯(PS)微球,将所制备的PS微球经磺化吸水后,利用钛酸丁酯作前驱体在乙醇中反应,使TiO2包覆在磺化苯乙烯微球表面,得到有机-无机PS/TiO2复合微球。在所得的杂化微球表面接枝上可聚官能团,利用无皂乳液聚合将聚甲基丙烯酸甲酯聚合到微球表面,得到核-壳-壳杂化微球。用FT-IR、SEM和TGA等方法对所制得的复合微球进行表征。结果表明PS、PS/TiO2及PS/TiO2/PMMA微球表面光滑,球形度好,单分散性良好;通过改变TBOT的加入量可以控制TiO2对PS微球的包覆厚度。     

聚苯乙烯/银核壳结构纳米微球的制备与表征

采用两步法的简单路线制备出银纳米粒子包覆的聚苯乙烯(PS)微球,首先通过乳液聚合法合成出聚苯乙烯微球;然后对苯乙烯进行敏化和活化,搅拌下加入银的还原液,从而制备出Ag-PS核壳结构的纳米微球.同时借助于TEM、UV-vis、 FE-SEM进行表征,分析其微观结构.结果表明,所得的聚苯乙烯微球粒径约为40nm;聚苯乙烯/银核壳结构纳米微球粒径为45～350nm,银层厚度可随意调控.     

分散聚合法制备SiO2/PAM核壳复合微球

采用分散聚合法制备出以SiO2为核、PAM为壳的核壳复合微球。根据Stber法制备了单分散SiO2微球,粒径随着TEOS、氨水浓度的增加而增大。采用硅烷偶联剂对SiO2微球进行表面处理,TEM显示处理后的微球继续保持单分散性,粒径有所增加。以SiO2微球或处理后的SiO2微球为核,采用分散聚合法在其上包覆AM,借助TEM、IR对其进行表征;研究发现,以处理后的Si O2微球为核能得到核壳结构,这种SiO2/PAM核壳微球的粒径大约为163 nm,包覆层30 nm左右。     

α-N（OH）2/SiO2核壳以及α-Ni（OH）2空心微球的制备及表征

采用以正硅酸乙酯（TEOS）水解为基础的硅溶胶种子生长法制备了粒径约为270nm的近单分散二氧化硅球型颗粒.采用一种新的溶液生长法,以氢氟酸作为溶液中镍离子配位剂,加入氨水调节溶液pH值的同时作为镍离子补充配位剂,60℃水浴条件下在已制得SiO2微球表面均匀包覆α-Ni（OH）2得到Ni（OH）2/SiO2核壳结构,Ni（OH）2壳层厚度约为35nm.结合多步包覆法提高Ni（OH）2壳层厚度,三次包覆后壳层厚度达到约100nm,四次包覆后约为140nm.采用20wt%的强碱NaOH溶液对三次包覆后的Ni（OH）2/SiO2核壳结构进行处理,得到了壳层厚度约为95nm的α-Ni（OH）2空心微球.空心微球具有较大的比表面积为141.06m2/g.     

α-Ni(OH)2/SiO2核壳以及α-Ni(OH)2空心微球的制备及表征

采用以正硅酸乙酯(TEOS)水解为基础的硅溶胶种子生长法制备了粒径约为270nm的近单分散二氧化硅球型颗粒.采用一种新的溶液生长法,以氢氟酸作为溶液中镍离子配位剂,加入氨水调节溶液pH值的同时作为镍离子补充配位剂,60℃水浴条件下在已制得SiO2微球表面均匀包覆α-Ni(OH)₂得到Ni(OH)₂/SiO₂核壳结构,Ni(OH)₂壳层厚度约为35nm.结合多步包覆法提高Ni(OH)₂壳层厚度,三次包覆后壳层厚度达到约100nm,四次包覆后约为140nm.采用20wt％的强碱NaOH溶液对三次包覆后的Ni(OH)₂/SiO₂核壳结构进行处理,得到了壳层厚度约为95nm的α-Ni(OH)₂空心微球.空心微球具有较大的比表面积为141.06m²/g.     

以油菜花粉为模板水热法制备TiO2中空微球

以油菜花粉为模板,先用超声使花粉分散在无水乙醇中,再通过水热法制备了TiO2前驱体/花粉壳-核微球;550℃焙烧脱除花粉核后得到了TiO2中空微球.采用SEM,TG,XRD,FTIR和N2吸附对TiO2前驱体/花粉壳-核微球及TiO2中空微球进行了表征.结果表明:在TiO2前驱体/花粉壳-核微球的制备过程中,超声波诱导能使TiO2前驱体较均匀的负载在花粉表面,适宜的钛酸丁酯用量为6.6 g/g花粉,适宜的水热处理温度为105℃.在此条件下得到的TiO2前驱体/花粉壳-核微球经550℃焙烧即可制得形状完整、大小约18μm的锐钛矿型TiO2中空微球.具有较窄的中孔结构,平均孔半径为1.9nm,比表面积为26.76 m2·g-1.     

四方排列有序Ag/TiO2空心微球的制备及光催化性能

采用低温垂直沉积法制备了聚苯乙烯(PS)胶体模板,由于低温下粒子热运动受到抑制,排列时发生位错,因此模板中存在大面积四方排列结构。然后采用化学镀法、溶胶-凝胶法在PS微球表面依次沉积银纳米粒子、纳米TiO2,最后高温煅烧除去模板制备了四方排列有序Ag/TiO2空心微球。通过扫描电镜(SEM)、X射线衍射(XRD)对样品进行表征。结果表明这种材料很好地保持了模板的四方排列,具有高度有序的纳米结构。选择降解甲基橙溶液来检验样品的光催化性能,并与纳米TiO2薄膜、四方排列TiO2空心微球的光催化性能进行比较,结果表明四方排列Ag/TiO2空心微球具有最佳的光催化性能。这是有序空心纳米结构和银纳米粒子的沉积共同作用的结果。     

用层层自组装法制备PS/SnO2核壳微球

利用层层自组装(LBL)技术制备了单层和多层吸附SnO2的PS/SnO2核壳微球,采用透射电镜(TEM)、场发射扫描电镜(FESEM)观察了产物的表面形貌,采用傅立叶变换红外分光光度计(FT-IR)分析了产物的结构,用热重分析仪(TGA)研究了不同吸附层产物的壳层比例,并研究了pH值、分散溶液、吸附层数对PS/SnO2核壳微球制备的影响,得到了最佳的制备条件.     

Insertion of triangulated surfaces into a meccano tetrahedral discretization by means of mesh refinement and optimization procedures

In this paper, we present a new method for inserting several triangulated surfaces into an existing tetrahedral mesh generated by the meccano method. The result is a conformal mesh where each inserted surface is approximated by a set of faces of the final tetrahedral mesh. First, the tetrahedral mesh is refined around the inserted surfaces to capture their geometric features. Second, each immersed surface is approximated by a set of faces from the tetrahedral mesh. Third, following a novel approach, the nodes of the approximated surfaces are mapped to the corresponding immersed surface. Fourth, we untangle and smooth the mesh by optimizing a regularized shape distortion measure for tetrahedral elements in which we move all the nodes of the mesh, restricting the movement of the edge and surface nodes along the corresponding entity they belong to. The refining process allows approximating the immersed surface for any initial meccano tetrahedral mesh. Moreover, the proposed projection method avoids computational expensive geometric projections. Finally, the applied simultaneous untangling and smoothing process delivers a high‐quality mesh and ensures that the immersed surfaces are interpolated. Several examples are presented to assess the properties of the proposed method.     

Certification Institutions Expected to Update and Transfer Information on Present Standards

Standards are the basis for production enterprises to organize production, ex-factory inspection, trade (delivery) and technical exchanges, product certification, quality arbitration and supervision.……     

Flow calorimeter for enthalpy increment measurements on condensed gases

A flow calorimeter for enthalpy increment measurements on condensed gases is presented. A better knowledge of the properties of the liquefied natural gas is needed, and therefore a liquid loop has been designed for our flow calorimeter. The fluid loop in the calorimeter is designed in order to avoid the two-phase region, since two phases would give compositional disturbances in the measurements. The avoidance of the two-phase region is made possible by increasing the pressure of the test fluid after the measurement section, then heating the fluid at super-critical pressure past the critical point. Finally, the fluid is throttled to the low-pressure gas state at the inlet condition of the compressor that circulates the fluid. To perform the pressure increase, a new cryogenic pump has been designed. To evaluate the new equipment, measurements were taken on liquid ethane over the temperature range 146–256 K at pressure between 0.9 and 5.1 MPa.     

Refrigerators Enter a New Era of Health Preservation Frestech initiates the establishment of China's first standard for household sterilization refrigerators

On November 30, 2007, the China Association for Standardization (CAS) held a press conference at Beijing Diaoyutai State Guest House. Leaders from the China Household Electric Appliance Research Institute, the China Household Electric Appliance Association, and the China Consumers' Association attended and made speeches.……     

Optimum-Simulation von Ernteprozessen

Zusammenfassung Bei der Gestaltung von Ernteprozessen — beispielsweise des Prozesses Mähdrusch, Körnertransport und -abnahme — als transportverbundene Fließarbeitsverfahren mit mindestens zwei verschiedenen Arbeitsmitteln gibt es einen großen Optimierungsspielraum. Solche Prozesse sind mehrstufige Bedienungsprozesse mit gemischter Anordnung der Bedienungseinrichtungen. Außerdem besitzen sie stark ausgeprägte räumliche Aspekte. Es wird vor allem gezeigt, welche Merkmale solcher Prozesse in Simulationsmodellen abgebildet sein müssen, welche Zielgrößen in Abhängigkeit von welchen Einflußgrößen unter Berücksichtigung welcher Prozeßbedingungen ermittelt werden sollten und wie der Bewertungsprozeß zur Ermittlung der gewünschten Informationen gestaltet werden muß.     

A study of centrifugal cast high boron high speed steel

In the present study a high‐boron high speed steel (HSS) roll material was designed. Many expensive alloy elements have been substituted by cheap boron alloy, and high‐boron high speed steel roll has been manufactured by centrifugal casting method. The microstructures, mechanical properties and wear resistance of centrifugal casting high‐boron high speed steel roll have been investigated by optical microscopy (OM), scanning electron microscopy (SEM), and X‐ray diffraction (XRD) analysis, hardness test, impact test and wear test. The results indicated that the solidification microstructures of high‐boron high speed steel roll consisted of M₂(B,C), (W,Mo)₂(B,C), M₃(B,C), M₂₃(B,C)₆ type borocarbides and martensite, a small amount of retained austenite. Borocarbides were continuously distributed over the grain boundary. After quenching from 1050 °C, local broken network appeared in partial borocarbides, and fine secondary borocarbide precipitated from the matrix. After tempering from 525 °C, the amount of precipitated borocarbide increased significantly. After heat treatment, the hardness of high‐boron high speed steel roll excelled 60 HRC, and its impact toughness excelled 8.0 J/cm². The single groove steel rolling amount of high‐boron high speed steel rolls increases by 500% than that of bainite cast iron roll, when the rolls are used in K₁ mill housing of bar mill.     

Thixotropy of Systems with Shear Thinning and Plastic Flow Behavior

The definition of the thixotropy is a decrease in viscosity with time in shear and a subsequent recovery of viscosity after the shear deformation is removed.We ...     

Brainstorming for ISO Strategy 2016-2020

正Responding to ISO’s appeal for survey for the to-be-developed ISO Strategy Plan for 2016-2020,SAC hosted a special workshop over the needs and comments of various fi elds on June 8 in Beijing.The workshop was attended by ISO President-elect and Ansteel General Manager Zhang Xiaogang,SAC Vice-Administrator Yu Xinli,and 30 experts from     

CNAS Passes APLAC's PTP Review

正The review group of Asia Pacific Laboratory Accreditation Cooperation(APLAC)carried out a 4-day peer review of the proficiency testing provider(PTP)for China National Accreditation Service for Conformity Assessment(CNAS)from July 28 to 31,2014.CNAS passed the PTP review with excellent performance.Two senior peer reviewers of APLAC made a comprehensive,rigorous and detailed review of CNAS’s PTP accreditation activities,and made the on-spot inspection of the review groups in Shanghai and Shenzhen respectively.