槲皮素改性脱细胞猪真皮基质的研究

采用不同浓度的槲皮素(QCT)交联改性脱细胞猪真皮基质(pADM),并对改性后的脱细胞猪真皮基质(QCT-pADM)材料进行傅里叶红外光谱、DSC、TG、表面形貌和耐降解性能等表征。结果显示,槲皮素的引入不会改变pADM中胶原的三股螺旋结构;改性后脱细胞猪真皮基质材料纤维编织更为紧实,热稳定性能得到提升,耐酶解性能和亲水性能大幅提高。     

没食子酸/硫酸铝复合改性猪真皮的研究

用正交实验设计法研究了没食子酸( gallic acid)/硫酸铝(aluminum sulfate)复合交联改性脱细胞猪真皮基质材料的基本性能.考察了反应时间、提碱后pH值、液比、没食子酸用量、硫酸铝用量对改性材料收缩温度的影响,并且对优化改性后的材料进行了性能表征.结果表明:反应时间为6h,提碱后pH值为5.3、液...     

脱细胞猪真皮基质材料改性

分别研究了植物多酚、戊二醛和环氧化合物对脱细胞真皮基质材料的改性性能,对改性后的材料进行收缩温度、力学性能、自由氨基等方面的表征.结果表明:植物多酚对脱细胞真皮基质的抗撕裂能力和硬度都有很大的提高,并且有一定的增厚性;戊二醛改性后脱细胞真皮基质的收缩温度大大提高,但是抗撕裂能力减弱;环氧化合物改性后脱细胞真皮基质的拉伸强度大幅度提高,收缩温度也相应提高.     

缩水甘油改性pADM的亲水性与吸湿动力学研究

采用缩水甘油(Glycido1)对脱细胞猪真皮基质(pADM)进行改性,通过对改性前后材料的接触角和吸湿动力学的研究,探寻改性前后材料亲水性能的变化.研究结果表明:pADM经缩水甘油改性后,材料的接触角降低.材料的吸湿动力学特征符合二级吸附动力学方程,表明吸湿过程属于多分子层吸附;且平衡吸附量随着改性剂用量的增加而提高...     

原花青素交联脱细胞猪真皮基质的研究

采用浓度0.7%(w/w)的天然原花青素(OPC)对脱细胞猪真皮基质(pADM)进行改性,研究了交联材料(OPC-pADM)的收缩温度、机械强度、亲水性、降解性和急性毒性。研究结果显示:经OPC交联后,pADM的收缩温度和变性温度明显升高,证明OPC与pADM产生了明显交联作用;交联后材料抗张强度升高,耐降解能力增强;吸水率、保水率的升高和接触角的降低,说明交联材料的亲水性能增加。动物实验表明,OPC-pADM无明显急性毒性。     

含银海藻酸纤维的制备方法和性能

为了结合银的抗菌性能和海藻酸纤维的高吸湿性,可将银离子加入海藻酸纤维后制备含银的海藻酸纤维和医用敷料。介绍了在海藻酸纤维中加入银离子的各种方法,并分析了含银海藻酸纤维和医用敷料的性能。结果表明:把银的磷酸锆钠化合物颗粒混入海藻酸纤维后可以制备具有白色外观的抗菌性能很好的纤维,与伤口渗出液接触后,这种纤维可以持续地释放出银离子。实验结果显示含银海藻酸纤维有很好的抗菌性能。     

银离子的释放及敷料的抗菌性能

为了确定不同的含银医用敷料在银的释放量和释放速度上的区别,分析了几种含银医用敷料释放银离子的性能。介绍了测试抗菌性能的3种方法,并总结了含银医用敷料的抗菌性能及临床疗效。结果显示,不同的伤口对银离子的释放量有不同的要求。烧伤病人的伤口特别容易受感染,因此在烧伤伤口上使用的含银医用敷料的银离子释放量高,在伤口上可以维持较高浓度的银。在高吸湿性的医用敷料中,细菌和伤口渗出液一起被吸进敷料,从敷料上释放出少量的银离子即可达到抗菌的目的。     

氧化羧甲基壳聚糖交联脱细胞猪真皮基质的微观形态与结构

以羧甲基壳聚糖为原料、高碘酸钠为氧化剂制备了氧化羧甲基壳聚糖,接着用不同浓度的氧化羧甲基壳聚糖改性了脱细胞猪真皮基质(pADM),并通过FT-IR、SEM、AFM、XRD与TG等方法对材料进行微观形态与结构表征。结果发现,氧化羧甲基壳聚糖上的醛基与脱细胞猪真皮基质中胶原分子上的氨基发生了有效共价交联,除席夫碱反应外,还存在氢键作用与静电吸引作用。交联后脱细胞猪真皮基质中的胶原仍然保留其天然的三股螺旋结构和D周期明暗相间横纹结构,横纹间距约为67 nm,交联产物仍然保持原有的三维立体网状结构。     

氧化羧甲基壳聚糖交联脱细胞猪真皮基质的微观形态与结构(续)

以羧甲基壳聚糖为原料、高碘酸钠为氧化剂制备了氧化羧甲基壳聚糖,接着用不同浓度的氧化羧甲基壳聚糖改性了脱细胞猪真皮基质(pADM),并通过FT-IR、SEM、AFM、XRD与TG等方法对材料进行微观形态与结构表征。结果发现,氧化羧甲基壳聚糖上的醛基与脱细胞猪真皮基质中胶原分子上的氨基发生了有效共价交联,除席夫碱反应外,还存在氢键作用与静电吸引作用。交联后脱细胞猪真皮基质中的胶原仍然保留其天然的三股螺旋结构和D周期明暗相间横纹结构,横纹间距约为67 nm,交联产物仍然保持原有的三维立体网状结构。     

纳米材料改性脱细胞猪真皮基质的研究

将纳米SiO2、纳米TiO2及纳米银的溶液与脱细胞猪真皮基质(porcine acellular dermal matrix,pADM)复合,考察改性前后材料的表面微观结构、收缩温度、抗张强度、透水汽性、孔隙率和抗菌性能。研究结果表明:纳米材料能以纳米粒子状态较好地分布于pADM内,随着纳米SiO2、纳米TiO2用量的增大,改性后的pADM收缩温度提高,抗张强度提高,孔隙率增大,透水汽性提高,对大肠杆菌和金黄色葡萄球菌具有良好的抗菌效果;纳米银改性后的pADM收缩温度降低,抗张强度增大,孔隙率减小,透水汽性略有减小,对大肠杆菌和金黄色葡萄球菌具有优良的抗菌效果。     

Preparation and Characterization of Carboxymethyl-Functionalized Chitosan Fiber

Carboxymethyl chitosan fiber (CMCF) was successfully prepared and characterized by FTIR. The swelling behavior, mechanical property, antibacterial activity and indirect cytotoxicity assessment of CMCF were also studied, respectively. The results showed that, CMCF had higher liquid absorption capacity and lower tensile strength and elongation at break than those of chitosan fiber. The antibacterial activity of CMCF was similar with chitosan fiber, and carboxymethylation did not enhance the antibacterial activity directly. Indirect cytotoxicity assessment of the fibers indicated that CMCF was nontoxic to the L929 cell with relatively low extraction concentration. This novel fiber would be used as a potential wound dressing for skin regeneration.     

Evaluation of dermal toxicity of antibacterial cotton textile coated by sol-gel technology

This paper reports about cotton textile modification by sol-gel technology with the purpose of obtaining antibacterial properties, evaluation of antibacterial properties and dermal toxicity tests of cotton textile with Zn and Si coating. Antibacterial properties evaluation against pathogenic microorganisms Pseudomonas aeruginosa, Staphylococcus aureus, and Escherichia coli made using the Parallel streak method in accordance with ATCC147 standard. For more specific evaluation of the coated textile, in vitro cytotoxicity test with epidermal HaCat cells was done. It is concluded that the coatings containing Zn and Si obtained by the sol-gel technology can impart antibacterial properties against pathogenic bacteria to the textile by preventing the bacteria from growing; strong inhibition of growth was detected for all test microorganisms. Based on the dermal toxicity test results, it is not expected that the prolonged contact of the skin with coated textiles will have a negative impact on the skin tissue – epidermis.     

再生竹子纤维理化性能探讨

文章探讨了再生竹子纤维的理化性能,对竹子纤维形态结构进行了微观分析;利用纤维强伸度测试仪对竹子纤维的机械性能进行了测试,利用差示扫描量热器和热重分析仪对竹子纤维的热学性能进行了研究.竹子纤维具有良好的吸湿性、染色性,以及抗菌除臭等特殊功能,是一种具有开发前景的新型纺织材料,在功能性纺织品的应用方面有着独特的优势.     

涤纶/竹纤维非织造抗菌鞋垫的设计与性能

以普通涤纶为主体原料,加入具有抗菌性的竹纤维,生产抗菌性鞋垫.设计4种不同的涤纶/竹纤维配比方案,进行针刺加工生产,并对鞋垫进行轧光处理.对产品的透气性能、孔径、拉伸强度、撕破强力及抑菌性等进行测定.结果表明,竹纤维能明显改善鞋垫的透气性及抗菌性,但鞋垫的力学性能变差,当竹纤维含量为30%时抗菌鞋垫综合性能较优.因此在实际生产中,竹纤维含量不宜过多,需同时考虑产品力学性能.     

亲水抗静电共混聚酯母粒的制备及其性能

为改善聚酯纤维的吸湿性和抗静电性,将具有高吸水性的纳米级聚丙烯酸钠粒子与常规聚酯混合制备共混母粒,对共混母粒的热性能、熔融结晶性能、亲水性能和流变性能进行了表征。结果表明,高吸水性微粉的加入明显改善了聚酯的亲水性,且其热稳定性与普通聚酯相近。然后用一定比例共混母粒与常规聚酯混合进行熔融纺丝,并研究了共混纤维的吸湿性和抗静电性。高吸水性微粉的加入使共混聚酯结晶速率提高,亲水性改善,纤维的吸湿性、抗静电性提高;当聚丙烯酸钠的添加量为0.4%时,可制得力学性能优良且回潮率达到2.09%、体积比电阻达到2.3 ×10⁹Ω?cm的纤维。     

高抗菌性聚乙烯醇/Ag@MOF食品包装膜的制备与表征

为分析银基金属有机框架(Ag@MOF)用于食品包装的可行性,采用流延法制备四种不同的聚乙烯醇(PVA)基食品包装膜(PVA/Ag@MOF、PVA/H₂PYDC、PVA/Ag、PVA),并研究它们的力学性能、热力学性能、水阻隔性、抗菌性、细胞毒性等。结果表明,与PVA、PVA/H₂PYDC膜相比,Ag@MOF的加入改善了薄膜的力学性能,使薄膜最大拉伸强度提高到36.21 MPa。与PVA、PVA/H₂PYDC、PVA/AgNPs膜相比,Ag@MOF的加入增强了膜的热稳定性。与PVA、PVA/H₂PYDC膜相比,AgNPs和Ag@MOF的刚性结构防止了水的扩散,提高了阻水性能。PVA/Ag@MOF膜对金黄色葡萄球菌和大肠杆菌的抗菌活性也很好,其抗菌活性远大于AgNPs和H₂PYDC复合膜,且具有较低的细胞毒性。因此,PVA/Ag@MOF薄膜是一种很有前景的食品包装材料,可以减少环境微生物对食品的干扰且细胞毒性较低,能够有效提高食品的安全性和储存周期。     

抑菌性桑枝低聚糖微胶囊的制备及结构表征

为了降低桑枝低聚糖的吸湿性,提高稳定性,拓展在产品开发中的应用,本实验以麦芽糊精、乳清蛋白为壁材,桑枝低聚糖为芯材,利用喷雾干燥制备稳定性良好、具有抑制变异链球菌活性的微胶囊。探究壁材种类及与芯材的质量比对微胶囊抑菌率的影响,并对微胶囊的吸湿性、分子结构、微观形态、热稳定性、贮藏稳定性等进行综合评价。结果表明:当复合壁材为麦芽糊精与乳清蛋白且质量比为2:1,壁材与芯材质量比为2:1时,制备的微胶囊具有较高的抑菌率（61.31%±3.34%）与较低的吸湿性（12.31%±1.47%）,粒径为6.58±1.76 μm。扫描电镜显示微胶囊颗粒形态完整,表面结构较为光滑;FITR表明微胶囊是麦芽糊精与乳清蛋白通过静电相互作用形成的,桑枝低聚糖较好地被包埋在微胶囊内部;X衍射分析证明桑枝低聚糖在微胶囊中结晶结构发生改变;微胶囊的玻璃化转变温度为96.10 ℃,高于一般贮藏温度。桑枝低聚糖制备成微胶囊后,在温度40.0、60.0 ℃,湿度RH 75.0%、RH 92.5%下稳定性提高。本研究可为桑枝低聚糖作为功能性配料提供一定的理论基础。