Mechanical and tribological properties of NiCr–Al2O3 composites at elevated temperatures

The effect of Al₂O₃ content on the mechanical and tribological properties of Ni–Cr alloy was investigated from room temperature to 1000 °C. The results indicated that NiCr–40 wt% Al₂O₃ composite exhibited good wear resistance and its compressive strength remained 540 MPa even at 1000 °C. The values obtained for flexural strength and fracture toughness at room temperature were 771 MPa, 15.2 MPa m^1/2, respectively. Between 800 °C and 1000 °C, the adhesive and plastic oxide layer on the worn surface of the composite was claimed to be responsible for low friction coefficient and wear rate.     

Tribological properties of Ni-17.5Si-29.3Cr alloy at room and elevated temperatures

The tribological properties of Ni-17.5Si-29.3Cr alloy against Si₃N₄ were studied on a ball-on-disc tribotester between room temperature and 1000 °C. The effects of temperature on the tribological properties of the alloy were investigated. The worn surfaces of the alloy were examined using scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). The results indicated that the tribological behavior of the alloy expressed some differences with increase in testing temperature. At low and moderate temperatures (below 800 °C), the alloy showed excellent wear and oxidation resistances, and the wear rate of the alloy remained in the magnitude of 10^?5 mm³/Nm; but at elevated temperature (800–1000 °C), the wear and oxidation resistances decreased, and the wear rate of the alloy increased up to 10^?4 mm³/Nm. The friction coefficient decreased from 0.58 to 0.46 with the rising of testing temperature from 20 to 600 °C, and then remained nearly constant. The wear mechanism of the alloy was mainly fracture and delamination at low and moderate temperatures, and transformed to adhesive and oxidation at elevated temperatures.     

The tribological characteristics of TiCN coating at elevated temperatures

The tribological behaviour of TiCN coating prepared by unbalanced magnetron sputtering is studied in this work. The substrates made from austenitic steel were coated by TiCN coatings during one deposition. The measurements were provided by high temperature tribometer (pin-on-disc, CSM Instruments) allowing measuring the dependency of friction coefficient on cycles (sliding distance) up to 500 °C. The evolution of the friction coefficient with the cycles was measured under different conditions, such as temperature or sliding speed and the wear rate of the ball and coating were evaluated. The 100Cr6 balls and the Si₃N₄ ceramic balls were used as counter-parts. The former were used at temperatures up to 200 °C, the latter up to 500 °C. The wear tracks were examined by optical methods and SEM. The surface oxidation at elevated temperatures and profile elements composition of the wear track were also measured.The experiments have shown considerable dependency of TiCN tribological parameters on temperature. Rise in temperature increased both friction coefficient and the wear rate of the coating in case of 100Cr6 balls. The main wear mechanism was a mild wear at temperatures up to 200 °C; fracture and delamination were dominating wear mechanisms at temperatures from 300 to 500 °C.     

Studies on wear behavior of nano-intermetallic reinforced Al-base amorphous/nanocrystalline matrix in situ composite

Resistance to wear is an important factor in design and selection of structural components in relative motion against a mating surface. The present work deals with studies on fretting wear behavior of in situ nano-Al₃Ti reinforced Al–Ti–Si amorphous/nanocrystalline matrix composite, processed by high pressure (8 GPa) sintering at room temperature, 350, 400 or 450 °C. The wear experiments were carried out in gross slip fretting regime to investigate the performance of this composite against Al₂O₃ at ambient temperature (22–25 °C) and humidity (50–55%). The highest resistance to fretting wear has been observed in the composites sintered at 400 °C. The fretting wear involves oxidation of Al₃Ti particles in the composite. A continuous, smooth and protective tribolayer is formed on the worn surface of the composite sintered at 400 °C, while fragmentation and spallation leads to a rougher surface and greater wear in the composite sintered at 450 °C.     

Sliding wear of silicon carbide modified by etching with chlorine at various temperatures

The effect of reaction temperature on the formation of a carbon layer on the surface of SiC has been investigated. Subsequently, the tribological properties of the formed carbon layers were studied. The experimental procedure involved exposing reaction-bonded SiC balls to a flowing gas mixture of 5% Cl₂, 2.5% H₂, and Ar at a high temperature of 800, 1000, or 1200 °C. A ball-on disk tribometer was used to investigate the friction and wear behavior of the treated specimens. While partially unreacted SiC phases were observed in the layer modified at 800 °C, rhombohedral graphite crystals were formed in the layer modified at 1200 °C. Compared to untreated SiC, the treated SiC materials were found to have relatively low friction coefficients and better wear resistance. Increasing the treatment temperature was found to improve the tribological performance of the resulting surface-modified SiC balls. A possible reason for this tribological improvement has been discussed based on the observed carbon phases.     

Tribological properties of laser-textured and ta-C coated surfaces with burnished WS2 at elevated temperatures

The possibility of enhancing the tribological properties of ta-C at elevated temperature (250 °C) by laser surface texturing and burnished WS₂ addition were investigated. Laser texturing was applied prior to ta-C coating process. Samples were tribologically tested at room temperature and elevated (250 °C) temperature using pin-on-disc. WS₂ addition increased remarkably the wear life of ta-C at 250 °C and low COF values (0.01–0.02) were achieved. Laser surface texturing (LST) increased the wear life of WS₂/ta-C surfaces by more than two times compared to non-textured surface. The LST dimples functioned as solid lubricant reservoirs and improved the wear life of the initial WS₂ layer. This was noticed to be related to wear mechanism with raised position dimples and partly oxidized WS₂.     

WC–ZrO2 composites: processing and unlubricated tribological properties

In the present work, we report the processing and properties of WC–6 wt.% ZrO₂ composites, densified using the pressureless sintering route. The densification of the WC–ZrO₂ composites was carried out in the temperature range of 1500–1700 °C with varying time (1–3 h) in vacuum. The experimental results indicate that significantly high hardness of 22–23 GPa and moderate fracture toughness of ∼5 MPa m^1/2 can be obtained with 2 mol% Y-stabilized ZrO₂ sinter-additive, sintered at 1600 °C for 3 h. Furthermore, the friction and wear behavior of optimized WC–ZrO₂ composite is investigated on a fretting mode I wear tester. The tribological results reveal that a moderate coefficient of friction in the range from 0.15 to 0.5 can be achieved with the optimised composite. An important observation is that a transition in friction and wear with load is noted. The dominant mechanisms of material removal appear to be tribochemical wear and spalling of tribolayer.     

Characteristics of oxidative wear and oxidative mildwear

Dry sliding tests were performed for 45, 4Cr5MoSiV1 steels and 3Cr3Mo2V cast steel at 200 and 400 °C. The wears at 200 and 400 °C are of oxidative wear characteristic due to tribo-oxides formed on worn surfaces. However, the wear at 200 °C presents different wear behaviors and characteristics from the one at 400 °C. The wear at 200 °C is a typical oxidative mild wear, but the wear at 400 °C is beyond oxidative mild wear, here called oxidative wear. The characteristics of oxidative mild wear and oxidative wear were clarified.     

Wear behavior of electroless Ni–P–B4C composite coatings

In this research, the wear of electroless Ni–P and Ni–P–B₄C composite coatings was reviewed. Auto catalytic reduction of Ni in nickel sulfate and sodium hypophosphate bath including suspended B₄C particles with different concentration was used to create composite coatings with 12, 18, 25 and 33 vol.% of B₄C particles. Coatings 35 μm thick were heat treated at 400 °C for one hour in an argon atmosphere and the wear resistance and friction coefficient of heat-treated samples were determined by block-on-ring tests. All wear tests were carried out at 24 °C, 35% moisture, 0.164 m/s sliding speed and about 1000 m sliding distance. Graphs show that an electroless Ni–P–B₄C composite coating with 25 vol.% of B₄C had the best wear resistance against a CK45 steel counterface.     

Tribological properties of nanostructured DLC coatings deposited by C60 ion beam

The frictional and wear characteristics of nanostructured DLC films were investigated. The coatings were deposited on silicon substrates by irradiation of a mass-separated C₆₀ ion beam with 5 keV of energy and a deposition temperature ranging from 100 to 450 °C. The effects of deposition temperature on the surface morphology, nano-structure, mechanical properties and tribological characteristics of the coatings were assessed. Results showed that deposition temperature strongly affects the nanostructure and surface morphology of the coatings. Coatings deposited at temperatures exceeding 350–400 °C exhibited an increase in surface roughness as well as compressive stress due to the formation of graphite, which led to a significant increase in the friction coefficient and wear rate. Coatings deposited at 300 °C showed the best tribological properties.     

Tribological behavior of graphite-containing nickel-based composite as function of temperature,load and counterface

Nickel-based graphite-containing composites were prepared by powder metallurgy method. Their mechanical properties at room temperature and friction and wear properties from room temperature to 600 °C were investigated by a pin-on-disk tribometer with alumina, silicon nitride and nickel-based alloy as counterfaces. The effects of graphite addition amount, temperature, load, sliding speed and counterface materials on the tribological properties were discussed. The micro-structure and worn surface morphologies were analyzed by scanning electron microscope (SEM) attached with energy dispersive spectroscopy (EDS). The results show that the composites are mainly consisted of nickel-based solid solution, free graphite and carbide formed during hot pressing. The friction and wear properties of composites are all improved by adding 6–12 wt.% graphite while the anti-bending and tensile strength as well as hardness decrease after adding graphite. The friction coefficients from room temperature to 600 °C decrease with the increase of load, sliding speed while the wear rates increase with the increasing temperature, sliding speed. The lower friction coefficients and wear rates are obtained when the composite rubs against nickel-based alloy containing molybdenum disulfide. Friction coefficients of graphite-containing composites from room temperature to 600 °C are about 0.4 while wear rates are in the magnitude of 10^?5 mm³/(N m). At high temperature, the graphite is not effective in lubrication due to the oxidation and the shield of ‘glaze’ layer formed by compacting back-transferred wear particles. EDS analysis of worn surface shows that the oxides of nickel and molybdenum play the main role of lubrication instead of graphite at the temperature above 400 °C.     

Tribological properties of NiCr–Al2O3 cermet-based composites with addition of multiple-lubricants at elevated temperatures

The tribological properties of NiCr-40 wt% Al₂O₃ (NC40A) cermet-based composites containing SrSO₄ and other lubricant (graphite, MoS₂ and Ag) against alumina ball were evaluated to identify their self-lubrication mechanisms from room temperature to 800 °C. The composites demonstrated distinct improvements in effectively reducing friction and wear, as compared to NC40A cermet. The best results were observed for NC40A–10SrSO₄–10Ag composite, which exhibited satisfactory reproducibility of friction coefficient over a wide temperature range (200–800 °C) through high temperature cyclic friction tests due to the formation of synergistic lubricating films SrAl₄O₇, NiCr₂O₄ and Ag on the contact surface.     

Effect of thermal activation on the tribological behaviours of serpentine ultrafine powders as an additive in liquid paraffin

The influence of thermal activation temperature on the tribological properties of surface-coated serpentine ultrafine powders as liquid paraffin additives was studied. It is found that the serpentine powders suspended in liquid paraffin present excellent tribological properties. Thermal activations in a temperature range from 300 to 600 °C increase the film forming ability and tribofilm completeness of the serpentine, keep the layer structure and accordingly further improve the tribological properties. However, the layer structure is destroyed and hard phases appear after thermal activated at or higher than 850 °C, as results in the aggravation of friction and wear.     

Tribological performance of α-Fe(Cr)-Fe2B-FeB and α-Fe(Cr)-h-BN coatings obtained by laser melting

α-Fe(Cr)-h-BN and α-Fe(Cr)-Fe₂B-FeB coatings on X30Cr13 stainless steel are synthesized by laser melting with incorporation of hexagonal boron nitride, or by alloying of boron. The additive powders are deposited on steel before pulsed irradiation by Nd-YAG laser beam. The solidification structures of the obtained coatings are investigated by optical microscopy and X-ray diffractometry. The mechanical properties are investigated by nanoindentation and the tribological behaviour is characterized on pin-on-disc tribometer, under dry-sliding conditions with different loads and a temperature range 25–500 °C. h-BN-α-Fe(Cr) and Fe₂B-α-Fe(Cr) coatings have average hardnesses 10.0 and 14.5 GPa, respectively, while hardness of untreated stainless steel is 4.2 GPa. In comparison with this untreated steel, the sliding contact on ceramic (ruby) of such coating shows a lower coefficient friction and a definitively better wear resistance.     

Effects of sliding velocity and normal load on friction and wear characteristics of multi-layered diamond-like carbon (DLC) coating prepared by reactive sputtering

Friction and wear tests were performed to investigate effects of sliding velocity and normal load on tribological characteristics of a multi-layered diamond-like carbon (DLC) coating for machine elements. The DLC coatings which consist of sequentially deposited gradient Cr/CrN, W-doped DLC (a-C:H:W) and DLC (a-C:H) layers were formed on carburized SCM 415 Cr–Mo steel disks using a reactive sputtering system. The tests against AISI 52100 steel balls were performed under various sliding velocities (0.0625, 0.125, 0.25, 0.5, 1 and 2 m/s) and normal loads (6.1, 20.7 and 49.0 N) in ambient air (relative humidity=26±2%, temperature=18±2 °C). Each test was conducted for 20 km sliding distance without lubricating oil. The results show that friction coefficients decrease with the increase in sliding velocity and normal load. Wear rates of both surfaces decrease with the increase in normal load. The increase in sliding velocity leads initially to the increase in wear rates up to the maximum value. Then, they decrease, as the sliding velocity increases above specific value that corresponds to the maximum wear rate. Through surface observation and analysis, it is confirmed that formation of transfer layers and graphitized degree of wear surfaces of DLC coatings mainly affect its tribological characteristics.     

Effect of surface laser texture on friction properties of nickel-based composite

Laser surface texturing (LST) was performed on the nickel-based composites by a Nd:YAG pulsed laser and the regular-arranged dimples with diameter of 150 μm were fabricated on their surfaces. The textured surfaces were smeared with molybdenum disulfide powder. The tribological properties of the textured and filled composites were investigated by carrying out sliding wear tests against an alumina ball as a counterface using a high temperature ball-on-disk tribometer. The tests were conducted at a sliding speed of 0.4 m/s and at normal loads ranging from 20–100 N and from room temperature to 600 °C. The friction coefficient of nickel-based composite textured and smeared with molybdenum disulfide was found to reduce from 0.18 to 0.1 at the temperature range from 200 to 400 °C. The texture with a dimple density of 7.1% was observed to prolong wear life of MoS2 film by more than four times in comparison to the texture with other dimple densities. The lubricious oxide particles stored in the dimples reduce friction coefficient at elevated temperatures and compensate for the extra lubricant owing to the degradation of MoS₂ caused by its oxidation at high temperatures.     

Comparison of self-mated hardmetal coatings under dry sliding conditions up to 600 °C

Hardmetal coatings prepared by high velocity oxy-fuel (HVOF) spraying represent an advanced solution for surface protection against wear. In the current systematic study the high-temperature oxidation and unidirectional sliding wear in dry and lubricated conditions were studied. Results for a series of experiments on self-mated pairs in dry conditions as part of that work are described in this paper. Coatings with nominal compositions WC-10%Co4%Cr, WC-(W,Cr)₂C-7%Ni, Cr₃C₂-25%NiCr, (Ti,Mo)(C,N)-29%Ni and (Ti,Mo)(C,N)-29%Co were prepared with an ethylene-fuelled DJH 2700 HVOF spray gun. Electrolytic hard chromium (EHC) coatings and bulk (Ti,Mo)(C,N)-15%NiMo (TM10) hardmetal specimens were studied for comparison. The wear behaviour was investigated at room temperature, 400 and 600 °C. For the coatings sliding speeds were varied in the range 0.1–1 m/s for a wear distance of 5000 m and a normal force of 10 N. In some cases the WC- and (Ti,Mo)(C,N)-based coatings showed total wear rates (sum of wear rates of the rotating and stationary samples) of less than 10^?6 mm³/Nm, i.e., comparable to values typically measured under mixed/boundary conditions. Coefficients of friction above 0.4 were found for all test conditions. The P × V values as an engineering parameter for coating application are discussed. The microstructures and the sliding wear behaviour of the (Ti,Mo)(C,N)-based coatings and the (Ti,Mo)(C,N)-15%NiMo hardmetal are compared.     

Tribological property of self-lubricating PM304 composite

PM304 composite has been prepared by high-energy ball milling and powder metallurgy. The composition of the PM304 composite is the same as that of PS304, but the microstructure is quite different. The microstructure of PM304 composite was fine and dense, the size of self-lubricating particles in the composite was very small. The tribological properties of PM304 composites against Inconel X-750 were examined in the temperature range from room temperature to 800 °C. The friction coefficient of PM304 was ranged from 0.32 to 0.41. At room temperature, brittle fracture occurred on the worn surface. With the increase of temperature up to 200 °C, a protective layer consisting of fluorides and Ag existed on the worn surface and led to a low wear rate. The wear resistance of the PM304 was superior to that of the PS304 in the temperature range from room temperature to 650 °C. The improvement in wear resistance of the PM304 was discussed in the terms of its microstructural characteristics.     

Tribological properties of Ni-based self-lubricating composites with addition of silver and molybdenum disulfide

Tribological properties of Ni-based composites containing silver and molybdenum disulfide were studied from room temperature to 700 °C. The composites were prepared by powder metallurgy technique and the phase composition and microstructure were addressed according to the characterization by SEM and XRD. The results show that the composites were composed of Ni, Cr₂O₃, Ag and Cr_xS_y phases after sintering. The best tribological properties were obtained when the silver and molybdenum disulfide contents were 20 wt% and 8.5 wt%, respectively. The tribo-chemical reaction occurred between Ag and Mo oxide during the rubbing process, which led to the formation of silver molybdate lubricating film. The improved tribological properties were attributed to the formation of silver molybdate lubricating tribolayers.     

Influence of fiber orientation on abrasive wear of unidirectionally reinforced carbon fiber–polyetherimide composites

A composite with continuous carbon fibers (CF) (80% by vol.) and high performance thermoplastic polyetherimide (PEI) matrix was developed and evaluated for various mechanical properties as a function of fiber orientation angle (0°, 30°, 45°, 60° and 90°). It was observed that Young's modulus, Poisson's ratio, toughness and % strain decreased with the increase of fiber orientation angle with respect to loading direction. In-plane shear modulus was highest for fibers with 45°. Overall, unidirectional (UD) CF reinforcement enhanced all strength properties of PEI significantly. Composites with fibers in 0° (parallel to loading direction) proved best in almost all the properties. Tribological evaluation in abrasive wear mode under different loads and fiber orientations indicated that coefficient of friction (μ) and specific wear rate (K₀) decreased with load, in general. Comparatively low specific wear rate (K₀), (in the order of 0.7 1×10^?9 m³/Nm) was observed for 0° fiber orientation, while fibers in 90° showed almost three times higher wear rate. Overall fiber reinforcement in 0° orientations proved beneficial from both strength and tribological performance point of view. SEM proved useful to correlate wear rate with surface topography.