SiO2/Al2O3对仿铜金属光泽釉面的性能影响

通过单因素实验探讨了SiO2/Al2O3摩尔比对仿铜金属釉的影响,研制了一种釉面耐磨性较高且呈现仿铜金属效果的生料金属釉。实验结果表明:随着SiO2/Al2O3摩尔比的增加,由于釉中析出的晶体种类和数量不同,从而导致釉面光泽度和色泽不一。当SiO2/Al2O3摩尔比为5.6时,釉中析出了CuMn2O4尖晶石晶体,从而使釉面呈现最佳的仿铜金属光泽,该釉面硬度为894.65Kg/mm2。     

无铅绿色金属光泽釉的研制

以钾长石、高岭土、石英、氧化锌、硼砂、方解石、玻璃粉为无铅基础釉原料,CuO、MnO2、TiO2、V2O5为着色剂,采用单因素和正交实验方法,研制出一种无铅绿色金属光泽釉。主要考察了配方组成、工艺条件和烧成制度对绿金属光泽釉的影响,并用X射线衍射(XRD)确定了釉面析出晶体的种类,扫描电镜(SEM)观察了釉面的显微形貌,差热-失重分析(DTA-TG)研究了釉料的反应过程。结果表明:CuMn2O4尖晶石是在1100℃急冷后析出的,粒径为1～2μm,并与釉面平行排列,赋予釉面较好的绿色金属光泽效果;其烧成范围为1230～1270℃,总失重为6%、理论上适合快速烧成;最佳施釉厚度为0.4～0.8 mm。     

配料组成对釉面金属光泽效果的影响

采用高岭土、石英、长石等为原料,并引入氧化铜、氧化锰作为析晶剂,制备金属光泽釉。探讨了配方中SiO2／Al2O3比、析晶剂的含量、PbO的含量对釉面金属光泽的影响规律。实验结果表明：当SiO2／Al2O3比为10,析晶剂的含量为5wt％,PbO的含量为40wt％时,在合适的烧成制度下,釉面具有良好的金属光泽效果。     

MnO2-CuO系金属光泽釉的研究

以熔块釉为基础釉,通过添加MnO2和CuO两种金属氧化物,成功制备了亮银灰色金属光泽釉。系统研究了MnO2与CuO的质量比K、加入量及冷却制度对釉面效果的影响,利用扫描电子显微镜(SEM)分析了釉层微观形貌。研究结果表明:(1)取2～3当CuO加入量为2.25～3%,MnO2为6～9%时,釉面出现高亮金属光泽。如果CuO含量低于1.5%,釉面不易出现金属光泽效果。MnO2的继续加入,有使釉面出现暗黑且无光的趋势;(2)快速冷却较随炉冷却更容易使釉面出现金属光泽效果;(3)快速冷却后试样釉层分布着亚微米级球状晶体,且平行于釉面规则生长,这极有可能是釉面出现高亮金属光泽的重要原因。     

CuO-MnO-V_2O_5-Fe_2O_3-TiO_2仿金属光泽釉的制备

采用生料铅釉作为基础釉,通过加入着色剂(即金属氧化物)CuO-MnO-V_2O_5-Fe_2O_3-TiO_2来制仿金金属光泽釉。考察了不同金属氧化物含量对釉面金属光泽效果的影响。实验结果表明:当金属氧化物含量(wt%)为CuO 3%、MnCO_3 8%、V_2O_5 1%、Fe_2O_3 0.5%和TiO_2 0.5%时,在1250℃下保温20~30 min,并在750℃快速冷却时釉面呈现很强的金属光泽效果。利用XRD对釉层进行分析,随着外加V_2O_5、Fe_2O_3和TiO_2氧化物的加入,促使了CuMn_2O_4尖晶石的进一步析出,使光产生更强的选择性反射,从而釉面的仿金属光泽进一步加强。同时,釉面具有良好的坯釉结合性和高的釉面硬度705.9 kg/mm~2。     

釉面分相对无铅CuO-MnO2系金属光泽釉的影响

以钙系生料釉为基础,引入结晶剂CuO、MnO₂制备无铅CuO-MnO₂系金属光泽釉;结合XRD、SEM-EDS进行物相组成定性分析和显微结构表征,系统探究外加TiO₂、V₂O₅以及玻璃粉对金属光泽釉釉面分相的影响。研究表明:一定量的TiO₂、V₂O₅引入能有效促进釉面的分相,将玻璃粉部分替换基础釉中的钾长石能使得釉熔体的高温粘度降低,并进一步加剧釉面分相,促进CuMn₂O₄铜锰尖晶石在釉层表面的析出和富集;当TiO₂引入量为2%,V₂O₅引入量为1%,玻璃粉引入量为25%(同为质量分数)时,金属光泽釉釉面效果最佳。     

R2O-RO-SiO2-B2O3-Al2O3系统乳浊釉的制备及微观结构分析

通过调整配方组成,成功制备了R2O-RO-SiO2-B2O3-A12 O3多元系统无锫乳浊釉,重点探讨了釉料化学组成关系对釉面乳浊程度的影响,采用扫描电子显微镜(SEM)研究了釉层微观结构及釉层乳浊机理.结果表明:釉料组成中n(R2O)/n(RO)、n(CaO)/n (MgO)、n(SiO2+ B2O3)/n(Al2O3)对釉面白度及质量影响显著.当n(R2O)/n(RO)在0.38～0.49、n(CaO)/n(MgO)在1.03～2.19、n(SiO2+ B2O3)/n(Al2O3)在12.69 ～18.42范围时,釉面自度高、质量好.釉面乳浊的原因是由析晶与分相共同作用,分相促进了晶体的析出,晶体形状主要为短柱状,尺寸约1～4 im,并以类球状团聚包裹形式分散于釉层中.     

CuO-MnO_2-V_2O_5-Fe_2O_3系金属光泽釉的研究

采用四角配料法 ,以高铅生料釉为基础釉 ,外加CuO、MnO2 、V2 O5、Fe2 O3等金属氧化物 ,成功研制出适合快烧工艺的亮银色金属光泽釉 ,并得出了该系釉料出现金属光泽效果的区域图。通过DTA、XRD、高温显微镜等分析手段 ,对釉料的高温熔融性能及釉面呈现金属光泽的机理等进行了初步研究。     

Cu—Mn系中温结晶釉的研制

采用高岭土、石英、钾长石等为基本原料．引入氧化铜、氧化锰为析晶剂．制备了Cu—Mn系中温结晶釉。探讨了配方中SiO2、Al2O3的含量和釉层厚度对釉面性能的影响．并对釉面光泽度和显微硬度进行了测试。实验结果表明：当配方中Al2O3含量为0．125%、SiO2含量为0．758%时,且釉层厚度为1mm左右时。在合适的烧成制度下。釉面晶花均匀、光泽度良好．并具有良好的釉面显微硬度。     

高温无铅仿古金属光泽釉的研制

以高岭土、长石、石英、磷酸钙、氧化锌、氧化铁等原料制备高温无铅仿古金属光泽釉。主要研究了釉料配方组成及烧成制度对釉面效果的影响。结果表明:当在基础釉中添加(wt.%)磷酸钙25,氧化锌2,氧化铁20,在烧成温度为1260℃、保温20min条件下,可获得釉面效果良好的红色仿古金属光泽釉。采用XRD、SEM等现代测试方法对釉层的显微结构和物相组成进行表征,揭示了釉面的呈色效果与配方组成和显微结构之间的关系。     

钒在陶瓷工业中的应用

本文通过钒的应用，阐述了金光釉和凹釉的形成机理。并说明了其在陶瓷釉料生产中所扮演的重要角色。     

燃烧法制备纳米铁酸镉和铁酸铜及表征

以Fe（NO3）3·9H2O、Cu（NO3）2·3H2O和Cd（NO3）2·4H2O为原料,以柠檬酸为还原剂,采用燃烧法制备了CuFe2O4和CdFe2O4纳米粉体,用X-射线粉末衍射仪（XRD）、红外光谱（IR）和振动样品磁强计（VSM）等手段对样品进行了表征,结果表明样品为立方晶系铁酸铜纳米粉体和立方晶系铁酸镉纳米粉体,其平均粒径约为22nm和18nm,并具有超顺磁性。     

均相沉淀法制备掺钕钇铝石榴石纳米粉末的研究

掺钕钇铝石榴石（Nd：YAG）多晶透明陶瓷具有容易制造、成本低、光学性能好、热导率高等优点,是一种很有前途的激光工作物质。以AI（N03）·9H2O,Y2O3,Nd2O3,（NH4）2SO4和尿素为原料,正硅酸乙酯为添加剂,采用均相沉淀法制备出分散均匀、纯YAG立方晶相的Nd：YAG纳米前驱体粉末。采用XRD、FT-IR、TEM等测试手段对前驱体粉末进行表征。研究结果表明：Nd：YAG前驱体粉末在800℃时为无定型态,当温度达到890℃时析出大量的中间相YAlO3（Y=AP）和少量的Y3Al5O5（YAG）,当温度达到1000℃时就全部转化为YAG立方晶相。     

Copper and silver nanocrystals in lustre lead glazes: Development and optical properties

In the early 9th century AD ancient potters of Iraq discovered that after firing some copper oxides and silver salts with clay, iron oxides and some sulphur compounds applied on a ceramic glaze produced a beautiful layer with a wide range of colours, from reddish to yellowish or even greenish, and some with a characteristic metallic copper or purplish shine. Modern studies of these layers showed that they are formed by nanocrystals of copper and silver embedded in a glass matrix. Some attempts have been performed to understand ancient lustre coloration and characteristic gloss but have failed to give a clear correlation between chemical composition and colour, and generally make some assumptions on the shape and the size of the nanoparticles and the lustre nanostructure. The aim of this paper is to establish a basis for understanding lustre nanostructure linked to its optical properties from a sequence of lustre reproductions on traditional lead glazed tiles. These modern lustre decorations have been studied by means of optical microscopy, transmission electron microscopy and electron energy loss spectroscopy, UV–vis spectroscopy, low irradiation angle X-ray diffraction, synchrotron radiation X-ray diffraction and electron microprobe analysis. These results show that changes in the lustre nanostructure affect the glaze colour and shine during the lustre formation process. Lustre nanostructure showed crystal size range as a function of depth, that subsequently disappeared followed by an increase of nanoparticles mean diameter and reduction of the interparticle distances. Consequently, the dipole plasmon coupling between copper nanoparticles appeared, and seems to be responsible for the metallic shine and copper metal like coloration of the copper lustre. However, colour from the glaze surface differs when calculated for diffuse or reflected light. Diffuse coloration appears strongly affected by the copper nanocrystals, while specular coloration is not only affected by copper but also by the presence of an inhomogeneous distribution of silver nanocrystals which gives the lustre a characteristic purplish shine.     

制备条件对柴油车用V2O5-WO3/TiO2催化剂催化性能的影响

采用偏NH4VO3和TiO2为前驱体制备选择性催化还原(SCR)催化剂涂层所需浆料,分别以分步涂覆法和一步涂覆法将浆料浸涂在蜂窝陶瓷载体上,得到了整体涂覆式选择性催化还原催化剂.对草酸添加量、焙烧时间及V2O5含量对催化活性的影响进行了研究,结果表明,V2O5(4%)-WO3/TiO2(450℃,3 h)和V2O5(5...     

多层陶瓷电容器用BSZT纳米瓷粉的制备

以Ti（OC4H9）4、Ba（NO3）2、Sr（NO3）2、Zr（NO3）4为原料,采用微波水热合成技术在较低的温度下合成出多层陶瓷电容器用Ba0.75Sr0.25Zr0.1Ti0.9O3纳米粉体。本文研究了反应温度、反应时间、pH值等因素对BSZT纳米粉体制备的影响机制,通过XRD、TEM、SEM等对粉体结构及形貌进行了表征。结果表明：在反应温度70℃、反应时间10min、pH≥14的条件下便可获得粒径只有60nm,分散良好且高结晶度的Ba0.75Sr0.25Zr0.1Ti0.9O3粉体,并初步探讨了微波水热合成纳米钛酸钡基陶瓷粉体的形成机理。     

钧红分相窑变釉的仿制研究

研究采用现代制瓷工艺,选用景德镇附近所生产的陶瓷原料,在梭式窑中烧成,仿制钧红分相窑变釉,基本达到了其深浅不同的青蓝色流纹与紫红色交相辉映的效果。实验中借助色度计、SEM等手段,探讨了Si/Al摩尔比、促分相剂P2O5添加量及着色氧化物CuO和Fe2O3含量对钧红分相窑变釉呈色的影响。     

黏结剂对柴油车用V_2O_5-WO_3/TiO_2催化剂选择性催化还原性能的影响

采用偏NH_4VO_3和TiO_2为前驱体制备选择性催化还原(SCR)催化剂涂层所需浆料,将浆料浸涂在蜂窝陶瓷载体上,得到整体涂覆式SCR催化剂。研究了SiO_2溶胶、H_3PO_4及H_3NO_3对催化剂涂层耐久性及活性的影响。在模拟评价装置上对催化剂活性进行了评价。结果表明,SiO_2溶胶和H_3PO_4对催化剂涂层耐久性具有明显改善作用,质量分数8%的SiO_2溶胶和4%的H_3PO_4使催化剂涂层脱落率从32.71%降至4.08%和17.89%;V_2O_5-WO_3/TiO_2-4%SiO_2溶胶催化剂表现出较高的活性和选择性,新鲜催化剂NO的起燃温度(T_(50))为205℃,随着H_3PO_4添加量的增加,催化剂低温活性逐渐降低,高H_3PO_4添加量时,催化剂表面被H_3PO_4覆盖,大部分与钛及钒键连接的羟基基团被P—OH所取代,催化剂SCR活性降低。