Size control of poly(2‐oxy‐6‐naphthoyl) whiskers by the addition of oligomers during polymerization

The method of controlling the size of a poly(2‐oxy‐6‐naphthoyl) (PON) whisker was examined with a focus on lengthening the whisker. PON whiskers were prepared by the polymerization of 2‐acetoxy‐6‐naphthoic acid in liquid paraffin at 330°C. The whiskers were very symmetrical. and both tips were very sharp. Growth of the whiskers along the length took place by which oligomer lamellae piled up along the long axis of the needlelike crystals with spiral growth. During steady growth until 8 min, the tip angle of the whiskers was constant at 80°. However, it became significantly sharper (22°) at 30 min, and later the trunk part of the whiskers stopped increasing. To depress the sharpening of the tips and to extend the steady‐growth period for longer whiskers, oligomers were added to the polymerization system after 8 min, just before the tip angle became sharper, to keep the concentration of the oligomers in the polymerization system constant. The addition of the oligomers extended the steady‐growth period, and the length increased from 12.5 to 17.3 μm. Although the width of the whiskers increased very slightly with the addition of the oligomers, the axial ratio of the whiskers increased from 19.4 to 24.7. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 88: 1320–1327, 2003     

Polymerization of 4‐(4′‐N‐1,8‐naphthalimidophenyl)‐1,2,4‐triazolidine‐3,5‐dione with diisocyanates

4‐(4′‐Aminophenyl)‐1,2,4‐triazolidine‐3,5‐dione ( 1 ) was reacted with 1,8‐naphthalic anhydride ( 2 ) in a mixture of acetic acid and pyridine (3 : 2) under refluxing temperature and gave 4‐(4′‐N‐1,8‐naphthalimidophenyl)‐1,2,4‐triazolidine‐3,5‐dione ( NIPTD ) ( 3 ) in high yield and purity. The compound NIPTD was reacted with excess n‐propylisocyanate in N,N‐dimethylacetamide solution and gave 1‐(n‐propylamidocarbonyl)‐4‐[4′‐(1,8‐naphthalimidophenyl)]‐1,2,4‐triazolidine‐3,5‐dione ( 4 ) and 1,2‐bis(n‐propylamidocarbonyl)‐4‐[4′‐(1,8‐naphthalimidophenyl)]‐1,2,4‐ triazolidine‐3,5‐dione ( 5 ) as model compounds. Solution polycondensation reactions of monomer 3 with hexamethylene diisocyanate ( HMDI ), isophorone diisocyanate ( IPDI ), and tolylene‐2,4‐diisocyanate ( TDI ) were performed under microwave irradiation and conventional solution polymerization techniques in different solvents and in the presence of different catalysts, which led to the formation of novel aliphatic‐aromatic polyureas. The polycondensation proceeded rapidly, compared with conventional solution polycondensation, and was almost completed within 8 min. These novel polyureas have inherent viscosities in a range of 0.06–0.20 dL g^?1 in conc. H₂SO₄ or DMF at 25°C. Some structural characterization and physical properties of these novel polymers are reported. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 90: 2861–2869, 2003     

Preparation and characterization of new optically active poly(amide‐imide)s derived from N,N‐(4,4′‐Oxydiphthaloyl)‐bis‐(s)‐(+)‐valine diacid chloride and aromatic diamines

4,4′‐Oxydiphthalic anhydride (1) was reacted with (s)‐(+)‐valine (2) in acetic acid and the resulting imide‐acid 3 was obtained in high yield. This compound 3 was converted to diacid chloride 4 by reaction with excess amount of thionyl chloride. The polycondensation reaction of diacid chloride 4 with several aromatic diamines such as 4,4′‐sulfonyldianiline (5a), 4,4′‐diaminodiphenyl methane (5b), 4,4′‐diaminodiphenylether (5c), p‐phenylenediamine (5d), m‐phenylenediamine (5e), and 4,4′‐diaminobiphenyl (5f) was performed by two conventional methods: low temperature solution polycondensation and a short period reflux conditions. To compare conventional solution polycondensation reaction methods with microwave‐assisted polycondensation, the reactions were also carried out under microwave conditions in the presence of small amount of o‐cresol that acts as a primary microwave absorber. The reaction mixture was irradiated for 4 min with 100% of radiation power. Several new optically active poly(amide‐imide)s with inherent viscosity ranging from 0.26–0.44 dL/g were obtained with high yield. All of the above polymers were fully characterized by ¹H‐NMR, FTIR, elemental analyses, and specific rotation techniques. Some structural characterizations and physical properties of these new optically active poly (amide‐imide)s are reported. POLYM. ENG. SCI. 46:558–565, 2006. © 2006 Society of Plastics Engineers     

Synthesis of poly(ester‐anhydride)s based on poly(ϵ‐caprolactone) prepolymer

The objective of this study was to prepare high molecular weight poly(ester‐anhydride)s by melt polycondensation. The polymerization procedure consisted of the preparation of carboxylic acid terminated poly(?‐caprolactone) prepolymers that were melt polymerized to poly(?‐caprolactone)s containing anhydride functions along the polymer backbone. Poly(?‐caprolactone) prepolymers were prepared using either 1,4‐butanediol or 4‐(hydroxymethyl)benzoic acid as initiators, yielding hydroxyl‐terminated intermediates that were then converted to carboxylic acid‐terminated prepolymers by reaction with succinic anhydride. Prepolymers were then allowed to react with an excess of acetic anhydride, followed by subsequent polycondensation to resulting high molecular weight poly(ester‐anhydride)s. Upon coupling of prepolymers, size exclusion chromatography analyses showed an increase from 3600 to 70,000 g/mol in number‐average molecular weight (M_n) for the 1,4‐butanediol initiated polymer, and an increase from 7200 to 68,000 g/mol for the 4‐(hydroxymethyl)benzoic acid‐initiated polymer. 4‐Hydroxybenzoic acid and adipic acid were also used as initiators in the preparation of poly(?‐caprolactone) prepolymers. However, with these initiators, the results were not satisfactory. © 2001 John Wiley & Sons, Inc. J Appl Polym Sci 81: 176–185, 2001     

Synthesis and characterization of novel heat resistance poly(amide‐imide)s from N,N′‐[2,5‐bis(4‐aminobenzylidene) cyclopentanone] bistrimellitimide acid and various aromatic diamines

A new‐type of dicarboxylic acid was synthesized from the reaction of 2,5‐bis(4‐aminobenzylidene)cyclopentanone with trimellitic anhydride in a solution of glacial acetic acid/pyridine (Py) at refluxing temperature. Six novel heat resistance poly(amide‐imide)s (PAIs) with good inherent viscosities were synthesized, from the direct polycondensation reaction of N,N′‐[2,5‐bis(4‐aminobenzylidene)cyclopentanone]bistrimellitimide acid with several aromatic diamines, by two different methods such as direct polycondensation in a medium consisting of N‐methyl‐2‐pyrrolidone (NMP)/triphenyl phosphite (TPP)/calcium chloride (CaCl₂)/pyridine (Py) and direct polycondensation in a p‐toluene sulfonyl chloride (tosyl chloride, TsCl)/pyridine (Py)/N,N‐dimethylformamide (DMF) system. All of the above polymers were fully characterized by ¹H NMR, FTIR, elemental analysis, inherent viscosity, solubility tests, UV‐vis spectroscopy, differential scanning calorimeter (DSC), thermogravimetric analysis (TGA), and derivative of thermaogravimetric (DTG). The resulted poly(amide‐imide)s (PAIs) have showed admirable good inherent viscosities, thermal stability, and solubility. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

Synthesis and characterization of polyamides and poly(amide‐imide)s derived from 2,6‐bis(3‐aminophenoxy)benzonitrile or 2,6‐bis(4‐aminophenoxy)benzonitrile

A series of polyamides and poly(amide‐imide)s was prepared by direct polycondensation of ether and nitrile group containing aromatic diamines with aromatic dicarboxylic acids and bis(carboxyphthalimide)s respectively in N‐methyl 2‐pyrrolidone (NMP) using triphenyl phosphite and pyridine as condensing agents. New diamines, such as 2,6‐bis(4‐aminophenoxy)benzonitrile and 2,6‐bis(3‐aminophenoxy)benzonitrile, were prepared from 2,6‐dichlorobenzonitrile with 4‐aminophenol and 3‐aminophenol, respectively, in NMP using potassium carbonate. Bis(carboxyphthalimide)s were prepared from the reaction of trimellitic anhydride with various aromatic diamines in N,N′‐dimethyl formamide. The inherent viscosities of the resulting polymers were in the range of 0.27 to 0.93 dl g^?1 in NMP and the glass transition temperatures were between 175 and 298 °C. All polymers were soluble in dipolar aprotic solvents such as dimethylsulfoxide, dimethylacetamide and NMP. All polymers were stable up to 350 °C with a char yield of above 40 % at 900 °C in nitrogen atmosphere. All polymers were found to be amorphous except the polyamide derived from isophthalic acid and the poly(amide‐imide)s derived from diaminodiphenylether and diaminobenzophenone based bis(carboxyphthalimide)s. Copyright © 2004 Society of Chemical Industry     

Synthesis and characterization of novel aromatic poly(amide‐imide)s derived from 2,2′‐bis(4‐trimellitimidophenoxy)biphenyl or 2,2′‐bis(4‐trimellitimidophenoxy)‐1,1′‐binaphthyl and various aromatic diamines

New aromatic diimide‐dicarboxylic acids having kinked and cranked structures, 2,2′‐bis(4‐trimellitimidophenoxy)biphenyl (2a) and 2,2′‐bis(4‐trimellitimidophenoxy)‐1,1′‐binaphthyl (2b), were synthesized by the reaction of trimellitic anhydride with 2,2′‐bis(4‐aminophenoxy)biphenyl (1a) and 2,2′‐bis(4‐aminophenoxy)‐1,1′‐binaphthyl (1b), respectively. Compounds 2a and 2b were characterized by FT‐IR and NMR spectroscopy and elemental analyses. Then, a series of novel aromatic poly(amide‐imide)s were prepared by the phosphorylation polycondensation of the synthesized monomers with various aromatic diamines. Owing to structural similarity, and a comparison of the characterization data, a model compound was synthesized by the reaction of 2b with aniline. The resulting polymers with inherent viscosities of 0.58–0.97 dl g^?1 were obtained in high yield. The polymers were fully characterized by FT‐IR and NMR spectroscopy. The ultraviolet λ_max values of the poly(amide‐imide)s were also determined. The polymers were readily soluble in polar aprotic solvents. They exhibited excellent thermal stabilities and had 10% weight loss at temperatures above 500 °C under a nitrogen atmosphere. Copyright © 2003 Society of Chemical Industry     

Microwave‐promoted rapid synthesis of new optically active poly(amide imide)s derived from N,N′‐(pyromellitoyl)‐bis‐L‐isoleucine diacid chloride and aromatic diamines

A pyromellitic dianhydride (benzene‐1,2,4,5‐tetracarboxylic dianhydride) was reacted with L ‐isoleucine in acetic acid, and the resulting imide acid [N,N′‐(pyromellitoyl)‐bis‐L ‐isoleucine] (4) was obtained in a high yield. 4 was converted into N,N′‐(pyromellitoyl)‐bis‐L ‐isoleucine diacid chloride by a reaction with thionyl chloride. The polycondensation reaction of this diacid chloride with several aromatic diamines, including 1,4‐phenylenediamine, 4,4′‐diaminodiphenyl methane, 4,4′‐diaminodiphenylsulfone (4,4′‐sulfonyldianiline), 4,4′‐diaminodiphenylether, 2,4‐diaminotoluene, and 1,3‐phenylenediamine, was developed with two methods. The first method was polymerization under microwave irradiation, and the second method was low‐temperature solution polymerization, with trimethylsilyl chloride used as an activating agent for the diamines. The polymerization reactions proceeded quickly and produced a series of optically active poly(amide imide)s with good yields and moderate inherent viscosities of 0.17–0.25 dL/g. All of the aforementioned polymers were fully characterized by IR, elemental analyses, and specific rotation. Some structural characterization and physical properties of these optically active poly(amide imide)s are reported. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 92: 951–959, 2004     

Synthesis and properties of poly(amide–imide)s based on N,N′‐bis(4‐carboxyphenyl)‐4,4′‐oxydiphthalimide,p‐aminobenzoic acid and various aromatic diamines

A new diimide–diacid monomer, N,N′‐bis(4‐carboxyphenyl)‐4,4′‐oxydiphthalimide (I), was prepared by azeotropic condensation of 4,4′‐oxydiphthalic anhydride (ODPA) and p‐aminobenzoic acid (p‐ABA) at a 1:2 molar ratio in a polar solvent mixed with toluene. A series of poly(amide–imide)s (PAI, III_a–m) was synthesized from the diimide–diacid I (or I′, diacid chloride of I) and various aromatic diamines by direct polycondensation (or low temperature polycondensation) using triphenyl phosphite and pyridine as condensing agents. It was found that only III_k–m having a meta‐structure at two terminals of the diamine could afford good quality, creasable films by solution‐casting; other PAIs III using diamine with para‐linkage at terminals were insoluble and crystalline; though III_g–i contained the soluble group of the diamine moieties, their solvent‐cast films were brittle. In order to improve their to solubility and film quality, copoly(amide–imide)s (Co‐PAIs) based on I and mixtures of p‐ABA and aromatic diamines were synthesized. When on equimolar of p‐ABA (m = 1) was mixed, most of Co‐PAIs IV had improved solubility and high inherent viscosities in the range 0.9–1.5 dl g^?1; however, their films were still brittle. With m = 3, series V was obtained, and all members exhibited high toughness. The solubility, film‐forming ability, crystallinity, and thermal properties of the resultant poly(amide–imide)s were investigated. © 2002 Society of Chemical Industry     

Synthesis and characterization of new thermally stable poly(ester‐imide)s derived from 2,2′‐bis(4‐trimellitimidophenoxy)biphenyl and 2,2′‐bis(4‐trimellitimidophenoxy)‐1,1′‐binaphthyl and various aromatic dihydroxy compounds

A series of new alternating aromatic poly(ester‐imide)s were prepared by the polycondensation of the preformed imide ring‐containing diacids, 2,2′‐bis(4‐trimellitimidophenoxy)biphenyl (2a) and 2,2′‐bis(4‐trimellitimidophenoxy)‐1,1′‐binaphthyl (2b) with various aromatic dihydroxy compounds in the presence of pyridine and lithium chloride. A model compound (3) was also prepared by the reaction of 2b with phenol, its synthesis permitting an optimization of polymerization conditions. Poly(ester‐imides) were fully characterized by FTIR, UV‐vis and NMR spectroscopy. Both biphenylene‐ and binaphthylene‐based poly(ester‐imide)s exhibited excellent solubility in common organic solvents such as tetrahydrofuran, m‐cresol, pyridine and dichloromethane. However, binaphthylene‐based poly(ester‐imide)s were more soluble than those of biphenylene‐based polymers in highly polar organic solvents, including N‐methyl‐2‐pyrrolidone, N,N‐dimethylacetamide, N,N‐dimethylformamide and dimethyl sulfoxide. From differential scanning calorimetry thermograms, the polymers showed glass‐transition temperatures between 261 and 315 °C. Thermal behaviour of the polymers obtained was characterized by thermogravimetric analysis, and the 10 % weight loss temperatures of the poly(ester‐imide)s was in the range 449–491 °C in nitrogen. Furthermore, crystallinity of the polymers was estimated by means of wide‐angle X‐ray diffraction. The resultant poly(ester‐imide)s exhibited nearly an amorphous nature, except poly(ester‐imide)s derived from hydroquinone and 4,4′‐dihydroxybiphenyl. In general, polymers containing binaphthyl units showed higher thermal stability but lower crystallinity than polymers containing biphenyl units. Copyright © 2005 Society of Chemical Industry     

Synthesis and antitumour and antiangiogenesis activity of polymers containing methacryloyl‐2‐oxy‐1,2,3‐propane tricarboxylic acid

A new monomer, methacryloyl‐2‐oxy‐1,2,3‐propane tricarboxylic acid (MTCA), was synthesized from citric acid and methacrylic anhydride. Poly(methacryloyl‐2‐oxy‐1,2,3‐propane tricarboxylic acid) and poly(methacryloyl‐2‐oxy‐1,2,3‐propane tricarboxylic acid)‐co‐(maleic anhydride) were prepared by radical polymerizations. Terpoly(methacryloyl‐2‐oxy‐1,2,3‐propane tricarboxylic acid–maleic anhydride–furan) was obtained by in situ terpolymerization of MTCA and exo‐3,6‐epoxy‐1,2,3,6‐tetrahydrophthalic anhydride. The synthesized samples were identified by FTIR, ¹H NMR and ¹³C NMR spectroscopies. The number‐average molecular weights of the fractionated polymers determined by GPC were in the range 14 900–16 600 and polydispersity indices were less than 1.14. The in vitro IC₅₀ values of the monomer and polymers against cancer and normal cell lines were much higher than those of 5‐fluorouracil (5‐FU). The in vivo antitumour activities of the synthesized samples at a dosage of 0.8 mg kg⁻¹ against mice bearing the sarcoma 180 tumour cell line decreased in the order terpoly(MTCA‐MAH‐FUR) > poly(MTCA‐co‐MAH) > poly(MTCA) > MTCA > 5‐FU. The synthesized samples inhibited DNA replication and angiogenetic activity more than did 5‐FU. © 2001 Society of Chemical Industry     

Synthesis and characterization of new aromatic poly(amide–imide)s based on 4‐aryl‐2,6‐bis(4‐trimellitimidophenyl) pyridines

New diimide–dicarboxylic acids, ie 4‐phenyl‐2,6‐bis(4‐trimellitimidophenyl)pyridine and 4‐p‐biphenyl‐2,6‐bis‐(4‐trimellitimidophenyl)pyridine, were synthesized by the condensation reaction of 4‐phenyl‐2,6‐bis(4‐aminophenyl)pyridine and 4‐p‐biphenyl‐2,6‐bis(4‐aminophenyl)pyridine with trimellitic anhydride in glacial acetic acid or dimethylformamide. The monomers were fully characterized by FT‐IR and NMR spectroscopies, and elemental analyses. A series of novel poly(amide–imide)s with inherent viscosities of 0.68–0.87 dl g^?1 was prepared from the two diimide–diacids with various aromatic diamines by direct polycondensation. The poly(amide–imide)s were characterized by FT‐IR and NMR spectroscopies. The λ_max data for the resulting poly(amide–imide)s were in the range of 260–292 nm. These polymers exhibited good solubilities in polar aprotic solvents. The 10 % weight loss temperatures are above 485 °C under a nitrogen atmosphere. Copyright © 2004 Society of Chemical Industry     

Synthesis and properties of fluorinated aromatic poly(amide imide)s based on 4,4′‐bis(4‐amino‐2‐trifluoromethylphenoxy)benzophenone and various bis(trimellitimide)s

A CF₃‐containing diamine, 4,4′‐bis(4‐amino‐2‐trifluoromethylphenoxy)benzophenone ( 2 ), was synthesized from 4,4′‐dihydroxybenzophenone and 2‐chloro‐5‐nitrobenzotrifluoride. Imide‐containing diacids ( 3 and 5B_a – 5B_g ) were prepared by the condensation reaction of aromatic diamines and trimellitic anhydride. Then, two series of novel soluble aromatic poly(amide imide)s (PAIs; 6A_a – 6A_k and 6B_a – 6B_g ) were synthesized from a diamine ( 4A_a – 4A_k or 2 ) with the imide‐containing diacids ( 3 and 5B_a – 5B_g ) via direct polycondensation with triphenyl phosphate and pyridine. The aromatic PAIs had inherent viscosities of 0.74–1.76 dL/g. All of the synthesized polymers showed excellent solubility in amide‐type solvents, such as N‐methyl‐2‐pyrrolidone and N,N‐dimethylacetamide (DMAc), and afforded transparent and tough films by DMAc solvent casting. These polymer films had tensile strengths of 90–113 MPa, elongations at break of 8–15%, and initial moduli of 2.0–2.9 GPa. The glass‐transition temperatures of the aromatic PAIs were in the range 242–279°C. They had 10% weight losses at temperatures above 500°C and showed excellent thermal stabilities. The 6B series exhibited less coloring and showed lower yellowness index values than the corresponding 6A series. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102:3641–3653, 2006     

Novel organosoluble poly(amide‐imide‐imide)s synthesized from new tetraimide‐dicarboxylic acid by condensation with 4,4′‐oxydiphthalic anhydride, 1,4‐bis(4‐amino‐2‐trifluoromethylphenoxy)benzene,trimellitic anhydride,and various aromatic diamines

A new monomer of tetraimide‐dicarboxylic acid (IV) was synthesized by starting from ring‐opening addition of 4,4′‐oxydiphthalic anhydride, trimellitic anhydride, and 1,4‐bis(4‐amino‐2‐trifluoromethylphenoxy)benzene at a 1:2:2 molar ratio in N‐methyl‐2‐pyrrolidone (NMP). From this new monomer, a series of novel organosoluble poly(amide‐imide‐imide)s with inherent viscosities of 0.7–0.96 dL/g were prepared by triphenyl phosphite activated polycondensation from the tetraimide‐diacid with various aromatic diamines. All synthesized polymers were readily soluble in a variety of organic solvents such as NMP and N,N‐dimethylacetamide, and most of them were soluble even in less polar m‐cresol and pyridine. These polymers afforded tough, transparent, and flexible films with tensile strengths ranging from 99 to 125 MPa, elongations at break from 12 to 19%, and initial moduli from 1.6 to 2.4 GPa. The thermal properties and stability were also good with glass‐transition temperatures of 236–276°C and thermogravimetric analysis 10 wt % loss temperatures of 504–559°C in nitrogen and 499–544°C in air. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 101: 2854–2864, 2006     

Microwave‐assisted synthesis of new optically active poly(ester‐imide)s containing N,N′‐(pyromellitoyl)‐bis‐L‐phenylalanine moieties

Pyromellitic dianhydride (benzene‐1,2,4,5‐tetracarboxylic dianhydride) (1) was reacted with L‐phenylalanine (2) in a mixture of acetic acid and pyridine (3 : 2) and the resulting imide‐acid [N,N′‐(pyromellitoyl)‐bis‐L‐phenylalanine diacid] (4) was obtained in quantitative yield. The compound (4) was converted to the N,N′‐(pyromellitoyl)‐bis‐L‐phenylalanine diacid chloride (5) by reaction with thionyl chloride. A new facile and rapid polycondensation reaction of this diacid chloride (5) with several aromatic diols such as phenol phthalein (6a), bisphenol‐A (6b), 4,4′‐hydroquinone (6c), 1,8‐dihydroxyanthraquinone (6d), 4,4‐dihydroxy biphenyl (6e), and 2,4‐dihydroxyacetophenone (6f) was developed by using a domestic microwave oven in the presence of a small amount of a polar organic medium such as o‐cresol. The polymerization reactions proceeded rapidly and are completed within 20 min, producing a series of optically active poly(ester‐imide)s with good yield and moderate inherent viscosity of 0.10–0.26 dL/g. All of the above polymers were fully characterized by IR, elemental analyses, and specific rotation. Some structural characterization and physical properties of these optically active poly(ester‐imide)s are reported. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 86: 2211–2216, 2002     

Microwave‐assisted and conventional polycondensation reaction of optically active N,N′‐(4,4′‐sulphonediphthaloyl)‐bis‐L‐leucine diacid chloride with aromatic diamines

3,3′,4,4′‐Diphenylsulfonetetracarboxylic dianhydride ( 1 ) was reacted with L‐leucine ( 2 ) in acetic acid and the resulting imide‐acid ( 3 ) was obtained in high yield. The diacid chloride ( 4 ) was prepared from diacid derivative ( 3 ) by reaction with thionyl chloride. The polycondensation reaction of diacid chloride ( 4 ) with several aromatic diamines such as 4,4′‐sulfonyldianiline ( 5a ), 4,4′‐diaminodiphenyl methane ( 5b ), 4,4′‐diaminodiphenylether ( 5c ), p‐phenylenediamine ( 5d ), m‐phenylenediamine ( 5e ), 2,4‐diaminotoluene ( 5f ), and 1,5‐diaminonaphthalene ( 5g ) was developed by using a domestic microwave oven in the presence of a small amount of a polar organic medium such as o‐cresol. The polymerization reactions were also performed under two conventional methods: low temperature solution polycondensation in the presence of trimethylsilyl chloride, and a short period reflux conditions. A series of optically active poly(amide‐imide)s with inherent viscosity of 0.25–0.42 dL/g were obtained with high yield. All of the above polymers were fully characterized by IR, elemental analyses, and specific rotation techniques. Some structural characterizations and physical properties of these optically active poly (amide‐imide) s are reported. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 91: 2992–3000, 2004     

Microwave‐assisted rapid polycondensation reaction of 4‐(4′‐acetamidophenyl)‐1,2,4‐triazolidine‐3,5‐dione with diisocyanates

4‐(4′‐Aminophenyl)‐1,2,4‐triazolidine‐3,5‐dione was reacted with 1 mol of acetyl chloride in dry N,N‐dimethylacetamide (DMAc) at ?15°C and 4‐(4′‐acetamidophenyl)‐1,2,4‐triazolidine‐3,5‐dione [4‐(4′‐acetanilido)‐1,2,4‐triazolidine‐3,5‐dione] (APTD) was obtained in high yield. The reaction of the APTD monomer with excess n‐isopropylisocyanate was performed at room temperature in DMAc solution. The resulting bis‐urea derivative was obtained in high yield and was finally used as a model for the polymerization reaction. The step‐growth polymerization reactions of monomer APTD with hexamethylene diisocyanate, isophorone diisocyanate, and tolylene‐2,4‐diisocyanate were performed under microwave irradiation and solution polymerization in the presence of pyridine, triethylamine, or dibutyltin dilaurate as a catalyst. Polycondensation proceeded rapidly, compared with conventional solution polycondensation; it was almost completed within 8 min. The resulting novel polyureas had an inherent viscosity in the range of 0.07–0.17 dL/g in dimethylformamide or sulfuric acid at 25°C. These polyureas were characterized by IR, ¹H‐NMR, elemental analysis, and thermogravimetric analysis. The physical properties and structural characterization of these novel polyureas are reported. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 91: 2103–2113, 2004     

Application of microwave irradiation for synthesis of novel optically active poly(amide imides) derived from diacid chloride containing epiclon and L‐isoleucine with aromatic diamines

Epiclon [3a,4,5,7a‐tetrahydro‐7‐methyl‐5‐(tetrahydro‐2,5‐dioxo‐3‐furanyl)‐1,3‐isobenzofurandione] or [5‐(2,5‐dioxotetrahydrofurfuryl)‐3‐methyl‐3‐cyclohexyl‐1,2‐dicarboxylic acid anhydride] (1) was reacted with L ‐isoleucine (2) in acetic acid and the resulting imide acid (3) was obtained in high yield. The diacid chloride (4) was obtained from diacid derivative (3) by reaction with thionyl chloride. The polycondensation reaction of diacid chloride (4) with several aromatic diamines such as 4,4′‐sulfonyldianiline (5a), 4,4′‐diaminodiphenyl methane (5b), 4,4′‐diaminodiphenylether (5c), p‐phenylenediamine (5d), m‐phenylenediamine (5e), 2,4‐diaminotoluene (5f), and 4,4′‐diaminobiphenyl (5g) was developed by using a domestic microwave oven in the presence of a small amount of a polar organic medium such as o‐cresol. The polymerization reactions were also performed in two other different methods: low‐temperature solution polycondensation and reflux conditions. A series of optically active poly(amide imides) with inherent viscosity of 0.12–0.30 dL/g were obtained. All of the above polymers were fully characterized by IR, elemental analyses, and specific rotation techniques. Some structural characterizations and physical properties of these optically active poly(amide imides) are reported. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 93: 2218–2229, 2004     

New poly(amide‐imide) syntheses. 24. Synthesis and properties of fluorinated poly(amide‐imide)s based on 2,2‐bis[4‐(trimellitimidophenoxy)phenyl]hexafluoropropane and various aromatic diamines

An imide ring‐performed dicarboxylic acid bearing one hexafluoroisopropylidene and two ether linkages between aromatic rings, 2,2‐bis[4‐(4‐trimellitimidophenoxy)phenyl]hexafluoropropane (II), was prepared from the condensation of 2,2‐bis[4‐(4‐aminophenoxy)phenyl]hexafluoropropane and trimellitic anhydride. A novel series of poly(amide‐imide)s having inherent viscosities of 0.72 ∼ 1.86 dL g⁻¹ was prepared by the triphenyl phosphite‐activated polycondensation from the diimide‐diacid (II) with various aromatic diamines in a medium consisting of N‐methyl‐2‐pyrolidone, pyridine, and calcium chloride. Several of the resulting polymers were soluble in polar amide solvents, and their solutions could be cast into transparent, thin, flexible films having good tensile properties and high thermal stability. The 10% weight loss temperatures were all above 495°C in air or nitrogen atmosphere, and the glass transition temperatures were in the range of 237°–276°C. © 1999 John Wiley & Sons, Inc. J Appl Polym Sci 71: 823–831, 1999     

Synthesis and characterization of new cardo poly(ether imide)s derived from 9,9‐bis [4‐(4‐aminophenoxy)phenyl]xanthene

A series of new cardo poly(ether imide)s bearing flexible ether and bulky xanthene pendant groups was prepared from 9,9‐bis[4‐(4‐aminophenoxy)phenyl]xanthene with six commercially available aromatic tetracarboxylic dianhydrides in N,N‐dimethylacetamide (DMAc) via the poly(amic acid) precursors and subsequent thermal or chemical imidization. The intermediate poly(amic acid)s had inherent viscosities between 0.83 and 1.28 dL/g, could be cast from DMAc solutions and thermally converted into transparent, flexible, and tough poly(ether imide) films which were further characterized by X‐ray and mechanical analysis. All of the poly(ether imide)s were amorphous and their films exhibited tensile strengths of 89–108 MPa, elongations at break of 7–9%, and initial moduli of 2.12–2.65 GPa. Three poly(ether imide)s derived from 4,4′‐oxydiphthalic anhydride, 4,4′‐sulfonyldiphthalic anhydride, and 2,2‐bis(3,4‐dicarboxyphenyl))hexafluoropropane anhydride, respectively, exhibited excellent solubility in various solvents such as DMAc, N,N‐dimethylformamide, N‐methyl‐2‐pyrrolidinone, pyridine, and even in tetrahydrofuran at room temperature. The resulting poly(ether imide)s with glass transition temperatures between 286 and 335°C had initial decomposition temperatures above 500°C, 10% weight loss temperatures ranging from 551 to 575°C in nitrogen and 547 to 570°C in air, and char yields of 53–64% at 800°C in nitrogen. © 2012 Wiley Periodicals, Inc. J Appl Polym Sci, 2012