氯化丁基橡胶/天然橡胶共混物性能的研究

研究了共混比及硫化体系对氯化丁基橡胶（ＣＩＩＲ）／天然橡胶（ＮＲ）共混物性能的影响，探讨了老化温度及防老剂对氧化锌／促进剂ＴＭＴＤ／促进剂ＤＭ硫化体系硫化的ＣＩＩＲ／ＮＲ共捐物耐热氧老化性能的影响。试验结果表明，氧化锌／促进剂ＴＭＴＤ／促进剂ＤＭ（５．０／１．５／１．０）硫化体系硫化的ＣＩＩＲ／ＮＲ共混物的拉伸强度和扯断伸长率与按共混比计算的平均值差别较小，尤其是拉伸强度与计算值完全一致。当共混物中ＣＩＩＲ用量超过５０份时，共混物的耐热氧老化性能明显改善。不同防老剂对ＣＩＩＲ／ＮＲ（５０／５０）共混物热氧老化的防护效能大小顺序为ＲＤ及４０１０＞４０１０ＮＡ＞ＭＢ＞Ｄ。防老剂ＲＤ先加入到ＮＲ中后再与ＣＩＩＲ共混．其防护效能更佳。     

动态硫化PVC/SBR共混体系的研究

采用动态硫化法制备了ＰＶＣ／ＳＢＲ共混物，考察了橡塑比、硫化体系、相容剂及ＰＶＣ交联对共混物性能的影响。结果表明，当ＰＶＣ／ＳＢＲ并用比为７５／２５，相容剂ＮＢＲ／氯化聚乙烯并用比为２．５／２．５，采用半有效或半有效加２份交联剂ＤＣＰ的硫化体系时，共混物综合性能较好。在ＰＶＣ中加入０．４份促进剂ＮＡ－２２可明显改善共混物的压缩永久变形。     

氯醚橡胶/氯化聚乙烯共混物的性能研究

考察了共混比、硫化体系、高耐磨炉黑（ＨＡＦ）及润滑剂二硫化钼的用量对氯醚橡胶／氯化聚乙烯（ＣＯ／ＣＰＥ）共混物性能的影响,结果表明：ＣＯ中混入ＣＰＥ后硬度增大,而综合性能较好;采用促进剂ＮＡ２２／四氧化三铅硫化体系,促进剂ＮＡ２２为１份时,共混物具有较好的综合性能;当ＨＡＦ用量为４５份时,共混物的拉伸强度及撕裂强度最佳;当润滑剂二硫化钼用量为２～４份时,共混物具有较好的综合性能。用差示扫描量热仪和扫描电子显微镜研究了共混物的形态及相容性,发现ＣＯ／ＣＰＥ是一个热力学相容体系     

一种高阻尼氯化丁基阻尼橡胶及其制备方法

正本发明公开了一种高阻尼氯化丁基阻尼橡胶及其制备方法,高阻尼氯化丁基阻尼橡胶由以下组分混炼得到:100质量份氯化丁基橡胶、12.5~25质量份辛基三嗪酮母炼胶、2~4质量份硫化剂、1~1.5质量份促进剂、1~3质量份硬脂酸、1~3质量份纳米氧化锌、1~3质量份防老剂。实验证明:本发明通过采用辛基三嗪酮母炼胶对氯化丁基橡胶进行改性,得到了阻尼     

动态固化聚丙烯／环氧树脂共混物的制备工艺研究

将动态硫化技术应用于热塑性树脂／热固性树脂体系，制备了动态固化聚丙烯／环氧树脂共混物，研究了动态固化PP／环氧树脂共混物制备工艺条件即增容剂、固化剂、环氧树脂的环氧当量及其含量等因素对共混物力学性能的影响。实验结果表明，选择马来酸酐接枝的均聚聚丙烯(PP-g-MAH)作为增容剂，所制得的动态固化PP／环氧树脂共混物的力学性能较好。2-乙基-4-甲基咪唑(EMI-2，4)的适宜用量为1．2％(每100份环氧树脂使用4份)。环氧当量对共混物的性能影响不大。当环氧树脂的含量为5％～10％时，动态固化PP／环氧树脂共混物的综合性能明显好于PP，特别是具有较高的强度和模量。     

相容剂对NBR/PP共混型TPE的影响

研究了4种增容剂,氯化聚乙烯（CPE）,高氯化聚乙烯,马来酸酐接枝聚丙烯（MP）和氯化丙烯（CPP）对丁腈橡胶／聚丙烯（NBR／PP）共混型热塑性弹性体（TPE）物理机械性能的影响,结查表明,CPP是NBR／PP的理想增容剂,当CPP用量为6份时,NBR／PP共混体体系具有优良的热塑性,拉伸强度13．8MPa,扯断伸长度290％,压缩永久变形32％,共混物的相容性与透射电镜的分析结果一致。     

相容剂对NBR/PP共混型热塑性弹性体性能的影响

考察了普通氯化聚乙烯（ＣＰＥ）、高氯化ＣＰＥ、马来酸酐接枝聚丙烯及复合氯化聚丙烯（ＣＰＰ）等相容剂对ＮＢＲ／ＰＰ共混体系性能的影响。试验结果表明，复合ＣＰＰ是ＮＢＲ／ＰＰ共混体系的理想相容剂，其最佳用量为６份；以此为相容剂的ＮＢＲ／ＰＰ共混体系具有优良的热塑性，ＮＢＲ／ＰＰ共混型热塑性弹性体可采用热塑性塑料通用的加工方法进行加工。     

马来酸酐改性氯化聚丙烯和醇酸树脂相容性的研究

研究了由70％的二甲苯、不同配比的醇酸树脂和马来酸酐改性氯化聚丙烯构成的三元体系复配互容情况。用红外表征了马来酸酐改性氯化聚丙烯与344#树脂的质量比为1／2时复配液的相容性；用光泽值表征溶剂挥发后。马来酸酐改性氯化聚丙烯与醇酸类树脂的质量比分别为2／1、l／l、1／2、1／10、0／10时二元共混涂膜的透明性。结果表明：随着改性氯化聚丙烯接枝率的提高。氯化聚丙烯和醇酸树脂的相容性明显增强。     

氯化聚乙烯/NBR动态硫化共混物性能的研究

在氯化聚乙烯（ＣＰＥ）和ＮＢＲ中加入促进剂ＮＡ２２首先对ＣＰＥ进行动态硫化,然后加入硫黄对ＮＢＲ进行静态硫化制备了ＣＰＥ／ＮＢＲ共混物。考察了促进剂ＮＡ２２用量、ＣＰＥ／ＮＢＲ共混比以及动态硫化温度对共混物性能的影响。结果表明,动态硫化是解决ＣＰＥ与ＮＢＲ相容性问题的有效手段;促进剂ＮＡ２２存在饱和点,用量以２份为宜;ＣＰＥ用量增大,动态硫化共混物交联密度则略有升高;动态硫化温度提高（１６０～１８０℃）,交联密度增大。     

NR/BR/TPI共混物硫化体系的研究

研究了普通硫化体系(CV)、半有效硫化体系(SEV)和有效硫化体系(EV)对NR／BR，TPI共混物(共混比为40／40／20)性能的影响，特别是CV体系中硫黄和促进剂DM用量的影响。结果表明，采用CV体系，NR／BR／TPI共混物的耐疲劳性能等物理性能较好，硫黄用量为3份、促进剂DM用量为1份时，共混物的撕裂强度和耐屈挠性能最好，其它性能也保持在较高水平。配合剂直接加入共混胶中混炼比分别加入3种生胶混炼后再加以混合的方式可获得更好的力学性能，但正硫化时间和焦烧时间缩短。     

Chlorinated butyl rubber/two-step modified montmorillonite nanocomposites: Mechanical and damping properties

Montmorillonite (MMT) was modified by ultrasound and castor oil quaternary ammonium salt intercalation method to prepare a new type of organic montmorillonite (OMMT). The surface structure, particle morphology, interlayer distance, and thermal behavior of the samples obtained were characterized. The modified OMMT was then added to chlorinated butyl rubber (CIIR) by mechanical blending, and a composite material with excellent damping properties was obtained. The mechanical experiment results of CIIR nanocomposites showed that the addition of OMMT improved their tensile strength, hardness, and stress relaxation rate. Compared with pure CIIR, when the content of OMMT was 5 phr (part per hundred of rubber), the tensile strength of the nanocomposite was increased by 677% and the elongation at break was also increased by 105.4%. The enhancement of this performance was mainly due to the dispersion of the nanosheets in CIIR rubber and the chemical interaction between the organoclay and the polymer matrix, which was confirmed by morphology and spectral analysis. OMMT also endowed a positive effect on the damping properties of CIIR nanocomposites. After adding 5 phr of OMMT, the nanocomposite owned the best damping performance, and the damping factor, tanδ_max, was 37.9% higher than that of pure CIIR. Therefore, the good damping and mechanical properties of these CIIR nanocomposites provided some novel and promising methods for preparing high-damping rubber in a wide temperature range.     

CR/CIIR并用胶的性能研究

试验研究CR／CIIR并用胶的性能。结果表明。采用氧化锌／硫黄硫化体系的CR／CIIR并用胶共硫化性较好；当CR／CIIR并用比为80／20、补强剂为炭黑N550（用量40份）、增塑剂为固体古马隆树脂（用量10份）时，并用胶的综合物理性能较好。     

炭黑对IIR/CIIR共混硫化胶压缩弹性模量的影响

研究了IIR／CIIR不同并用比和不同炭黑和用量以及软化剂品种和用量对IIR／CIIR共混硫化胶压缩弹性模量的影响。结果显示：当IIR／CIIR并用比为80／20，N220炭黑用量为80份时共混硫化胶有良好的压缩弹性模量，软化剂的加入会降低共混硫化胶的压缩弹性模量。     

影响IIR／CIIR并用体系力学性能的几个因素

研究了ＩＩＲ／ＣＩＩＲ不同并用比例、不同硫化体系、树脂用量、炭黑品种及用量、操作油种类等对ＩＩＲ／ＣＩＩＲ并用硫化胶力学性能的影响。结果表明：当ＩＩＲ／ＣＩＩＲ并用比例为８０／２０时,并且采用树脂作交联剂进行硫化,所得硫化胶的拉伸强度、扯断伸长率以及撕裂强度都有较好的结果,拉伸强度达到１９．８ＭＰａ,伸长率为６４０％;当树脂用量为１０ｐｈｒ时,硫化胶的永久变形只有４％,硬度为５４度;当ＩＳＡＦ用量     

不同硫化体系动态硫化EPDM/PP热塑性弹性体流变性能的研究

研究了不同硫化体系、硫化剂用量及共混比对ＥＰＤＭ／ＰＰ共混物流变性能的影响。结果表明,选择酚醛树脂硫化体系、控制酚醛树脂用量为５ 份以及ＥＰＤＭ／ＰＰ共混比为５０／５０,可以得到挤出表面最为光滑的共混物。     

动态硫化EPDM/PP热塑性弹性体制备工艺研究

研究了不同硫化体系 ,硫化时间 ,硫化剂的用量 ,共混温度 ,橡塑比 ,填充炭黑和软化剂的用量对动态硫化 EPDM/ PP共混物性能的影响。研究结果表明 :酚醛硫化体系制得的 EPDM/ PP共混物加工性能和力学性较佳 ,硫化时间在 10～ 15 min,硫化剂的用量以完全交联 EPDM为宜 ,共混温度控制在 170℃～ 190℃ ,橡塑比 70 / 3 0～ 5 0 / 5 0 ,填充炭黑在 40份以内 ,软化剂在 2 0份以内较为理想     

硫化体系对氯化丁基橡胶/尼龙12动态硫化胶性能的影响

研究了氧化锌、N,N’-间苯撑双马来酰亚胺(HVA-2)/氧化锌和1,3-双柠糠酰亚胺甲基苯(PK 900)/氧化锌3种硫化体系下氯化丁基橡胶(CIIR)/尼龙(PA)12混炼胶的硫化特性及CIIR/PA 12动态硫化胶(TPV)的物理机械性能和微观相结构,并考察了PK 900与氧化锌不同配比对CIIR/PA 12TPV物理机械性能、流变性能及微观相结构的影响。结果表明,PK 900/氧化锌的硫化速率介于氧化锌和HVA-2/氧化锌两者之间,由其制备的TPV橡胶相粒径为1～2μm,均匀分布在树脂相中,物理机械性能最优;固定PK 900用量为3份时,随着氧化锌用量的减少,CIIR/PA 12 TPV的拉伸强度、扯断伸长率和100%定伸应力均呈现先增大后减小的趋势;当PK 900/氧化锌(质量比)为3/5时,CIIR/PA 12TPV的物理机械性能最佳,且呈现低剪切速率高黏度、高剪切速率低黏度的特性。     

动态硫化TPNR物理性能的研究

研究树脂品种、橡塑共混比及白炭黑用量对动态硫化热塑性天然橡胶（TPNR）物理性能的影响。结果表明，与采用聚丙烯（PP）或线形低密度聚乙烯制备的TPNR相比，采用高密度聚乙烯（HDPE）制备的TPNR综合物理性能较好；当NR／HDPE共混比为60／40、白炭黑用量为24份时，动态硫化TPNR具有优异的物理性能。在硬度接近的条件下，采用HDPE制备的TPNR综合物理性能优于采用PP制备的商品TPNR。     

马来酸酐和苯乙烯接枝改性对天然橡胶/聚丙烯共混物物理机械性能的影响

用动态硫化法制备了天然橡胶(NR)/聚丙烯(PP)热塑性弹性体(TPV)。研究了马来酸酐/苯乙烯/过氧化二异丙苯(MAH/St/DCP)多单体熔融接枝交联改性及纳米二氧化硅用量对NR/PP TPV物理机械性能的影响,讨论了NR/PP TPV的重复加工性能。结果表明,当MAH/St/DCP用量为3.750/1.875/0.375质量份、纳米二氧化硅用量为3质量份时,NR/PP TPV的物理机械性能最好,达到了国内外有关通用橡胶/PP TPV的水平,并且具有较好的重复加工性能。     

用附着型促进剂制备橡胶/蒙脱土纳米复合材料(英文)

用附着型促进剂PBS在机械混炼插层法的基础上制备了天然橡胶/蒙脱土纳米复合材料。由于硫化后大部分促进剂基团都连在橡胶分子链上,因此用分子一端能和蒙脱土片层有相互作用的附着型硫化促进剂,可以大大增强蒙脱土和橡胶基体的相互作用,得到性能优良纳米复合材料。用PBS制备纳米复合材料其硫化体系活性能低,硫化胶交联密度增大,有机蒙脱土片层在橡胶基体中达到纳米级的分散,具有优良的力学性能,加入8%有机蒙脱土100%模量从1.2 MPa增至2.2 MPa,500%模量从8.12 MPa增至18.23 MPa,邵氏GA硬度从45增至55,而加入2%有机蒙脱土500%模量从8.12 MPa增至17.06 MPa,撕裂强度从36.31 kN/m增至43.65kN/m,加入2~10份有机蒙脱土时其效果相当于加入40份半补强炭黑。