环氧改性水性醇酸树脂的制备及其性能研究

以豆油酸与环氧树脂E-51进行开环反应制得了环氧酯,将其与豆油酸、三羟甲基丙烷、邻苯二甲酸酐等进行酯化反应,经水性化和中和后得到一种环氧改性水性醇酸树脂。重点考察了环氧酯用量、醇超量、油度、酸值对树脂、涂膜各项性能的影响。结果表明,当环氧酯用量为醇酸树脂总质量的10%时,醇酸树脂油度为50%,醇超量选择在1.10～1.15,终点酸值为40～50 mgKOH/g,可以得到干性好、硬度高、附着力、水溶性、耐水性均优良的环氧改性水性醇酸树脂。     

环氧树脂/丙烯酸改性水性醇酸树脂的制备及性能

以环氧树脂E-44与亚麻酸反应生成环氧酯,将其与亚麻酸、邻苯二甲酸酐、苯甲酸、三羟甲基丙烷、顺丁烯二酸酐等进行酯化反应合成基础醇酸树脂,再用丙烯酸、甲基丙烯酸甲酯、丙烯酸丁酯、苯乙烯对其进行改性,得到一种水性醇酸树脂。采用红外光谱、粒径分析、透射电镜和热重分析研究了产物的结构、粒径和热稳定性以及环氧树脂和丙烯酸用量、终点酸值、中和度对树脂性能的影响。结果表明,改性水性醇酸树脂的最佳合成条件如下:环氧树脂E-44添加质量分数为9%~14%,丙烯酸质量分数7%,终点酸值(KOH)40~50 mg/g,中和度为80%。在该条件下制备出的水性醇酸树脂粒径分布均匀,具有良好的硬度、附着力、水溶性和耐水性。     

水性丙烯酸改性环氧醇酸树脂的制备及性能研究

为了提高水性醇酸涂料的防腐性和耐候性,本文以E-20环氧树脂和亚麻油酸反应制备环氧酯,并与苯甲酸、季戊四醇、苯酐反应制备环氧改性醇酸树脂,进一步采用丙烯酸类单体对制备的环氧改性醇酸树脂进行改性,制备了性能优异的水性丙烯酸改性环氧醇酸树脂,以制备的水性丙烯酸改性环氧醇酸树脂为成膜物质,设计了水性防腐涂料,讨论了脂肪酸的种...     

室温双重固化环氧改性水性醇酸树脂的制备

通过脂肪酸法,选用亚油酸、邻苯二甲酸酐、间苯二甲酸、三羟甲基丙烷、二羟甲基丙酸和顺丁烯二酸酐化亚麻油合成水性醇酸树脂,用环氧树脂对其进行改性,制备出室温双重固化的环氧改性水性醇酸树脂,然后中和后加催干剂和有机胺固化。分析了顺丁烯二酸酐化亚麻油的用量、环氧树脂的种类和用量、催干剂和固化剂对产物性能的影响,从而确定了顺酐油的用量在12%～16%,环氧树脂E-20用量在15%～20%,催干剂为复合型,固化剂为三乙烯四胺,制得的环氧改性水性醇酸树脂清漆表干2 h,实干12 h,铅笔硬度达H,附着力为1级,稳定性好,耐盐雾性佳。     

水溶性自干醇酸树脂的合成研究

以六氢苯酐、间苯二甲酸、亚麻酸、水性单体及三羟甲基丙烷为主要原料合成了水溶性自干醇酸树脂，测试了由该树脂配制的自干涂料的性能；讨论了工艺条件对醇酸树脂性质及涂膜性能的影响。     

羟基丙烯酸树脂改性水溶性醇酸树脂研究

将豆油和三羟甲基丙烷醇解得到甘油酸酯,再加入高固含量羟基丙烯酸树脂,与苯酐、偏苯三酸酐酯化反应制备得到改性水溶性醇酸树脂。采用红外光谱和凝胶色谱对产物结构进行了表征,通过涂料的干燥时间、硬度、耐水性及耐老化性等测试研究了羟基丙烯酸树脂的用量对涂料性能的影响。结果表明:羟基丙烯酸树脂的用量为醇酸树脂质量的50%～60%时涂层性能最佳。与未改性的醇酸涂料相比,改性后的醇酸树脂涂料20 min即可实现表干,涂料的耐水性和耐盐水老化性均得到明显改善。     

水溶性氨基改性醇酸树脂的制备

以亚麻油脂肪酸、三羟甲基丙烷、苯酐、偏苯三酸酐、顺酐以及三聚氰胺树脂为主要原料,采用熔融脂肪酸法制备了水溶性氨基改性醇酸树脂,通过对醇酸树脂的水溶性、黏度、稳定性以及漆膜硬度和附着力进行测试及分析,确定了水溶性醇酸树脂的配方。     

自干型改性水溶性醇酸树脂的研制

用妥尔油酸、间苯二甲酸、顺丁烯二酸酐、三羟甲基丙烷等原材料制得水性醇酸树脂,将苯乙烯、丙烯酸(酯)单体与醇酸树脂通过接枝共聚制得改性醇酸树脂,改性后的醇酸树脂具有较好的干性、硬度和耐水性。     

水性丙烯酸改性醇酸防腐涂料的研制

以松香、亚麻油酸、苯酐、三羟甲基丙烷、新戊二醇为原料合成醇酸树脂,然后用丙烯酸单体接枝共聚制备水性醇酸树脂。采用该树脂制备的水性涂料具有干燥速度快且耐水与防腐性能优异。     

丙烯酸酯改性水性醇酸树脂的制备及表征

以三羟甲基丙烷、邻苯二甲酸酐及亚麻油脂肪酸为主要原料生成所需的醇酸树脂,并加入偏苯三酸酐将其水性化得到具有水溶性的醇酸树脂,运用接枝共聚的方法进行改性得到丙烯酸酯改性的水性醇酸树脂.通过涂膜性能测试研究了引发剂种类、水性醇酸树脂与丙烯酸酯的比例、玻璃化温度对改性树脂性能的影响.采用激光粒度分布仪测定了产物的平均粒径分布...     

水分散型醇酸树脂的合成及性能研究

以脂肪油、邻苯二甲酸酐、偏苯三酸酐和三羟甲基丙烷为主要原料合成了水分散性醇酸树脂。以原料中酸酐的比例为基础设计了合成配方,讨论了合成工艺、脂肪油的种类和比例以及醇解催化剂对水分散性醇酸树脂性能的影响。     

Preparation and characterization of water reducible alkyd resin/colloidal silica nanocomposite coatings

In this study, water reducible alkyd resins containing different amounts of colloidal silica were synthesized for the first time. In order to achieve this, alkyd resin, which has an oil content of 35%, was prepared with tall oil fatty acid, isophthalic acid, trimellitic anhydride, and trimethylolpropane. The alkyd resin was neutralized with triethylamine, and was dissolved in an isobutyl alcohol-isopropyl alcohol-butyl glycol mixture to produce 75% (wt.) solution, which was called stock alkyd resin. The stock alkyd resin was diluted with water to 50% (wt.) concentration with water and colloidal silica mixture in order to prepare an alkyd solution containing 0%, 5%, 10%, 15% and 20% colloidal silica. Then the effect of the silica nanoparticle addition on the surface coating properties, thermal behaviors and surface morphologies of water reducible alkyd resins was investigated. As a result, the addition of colloidal silica has improved surface coating properties and thermal behaviors of nanocomposite water reducible alkyd resin.     

水性环氧改性醇酸树脂及其涂料的制备

采用环氧树脂为改性剂,以及偏苯三酸酐和自制助剂改性,制成了水溶性且性价比较高的水性环氧改性醇酸树脂及其涂料。讨论了各种因素对树脂和涂料性能的影响。试验结果表明：配制底漆的性能与溶剂型涂料相当。     

水溶性醇酸氨基烘漆的研制

采用饱和脂肪酸、苯酐、三羟甲基丙烷、新戊二醇和偏苯三酸酐合成水溶性醇酸树脂,与甲醚化三聚氰胺甲醛树脂制备水溶性醇酸氨基烘漆。该水溶性醇酸氨基烘漆的漆膜性能均达到并超过溶剂型醇酸氨基烘漆的漆膜性能。讨论了酸值、羟值、油度、氨基树脂、中和剂、助溶剂和树脂结构等因素对树脂合成及应用性能的影响。水溶性醇酸氨基烘漆与水性醇酸防锈底漆配套使用具有优异的防腐性能。     

水性醇酸树脂的合成及其耐水性的研究

以甘油、亚麻油酸、三羟甲基丙烷、邻苯二甲酸酐,间苯二甲酸及偏苯三酸酐等为原料合成了水性醇酸树脂,通过涂膜性能测试研究了反应温度、反应时间及偏苯三酸酐用量对水性醇酸树脂性能的影响。对比研究了氮丙啶型、硅氧烷型及多碳二亚胺型3种室温固化交联剂对水性醇酸树脂涂膜性能的影响。结果表明:水性化阶段偏苯三酸酐用量为10%,反应时间为1.5 h,反应温度为170 ℃时树脂性能较优。耐水性研究表明:加入硅氧烷型交联剂A后涂膜的耐水性最优,吸水率最低,当用量为6%时,清漆涂膜的硬度、光泽、附着力、耐水性、耐溶剂性均达到预期效果。加入辛酸亚锡后,涂膜在低温高湿环境下,干燥性及耐水性均得到明显改善。     

改性醇酸树脂的合成

以桐油、豆油、三羟甲基丙烷、苯酐、己二酸为原料合成基础醇酸树脂 ,再用苯乙烯、丙烯酸酯进行接枝共聚就制得改性醇酸树脂。在制造醇酸树脂过程中添加适量的抗氧剂 ,就可以防止胶化。制得的产品是均匀透明的 ,可用于制造浅色的不泛黄的涂料     

紫胶改性水性醇酸树脂的合成工艺研究

从改进树脂综合性能着手,研究了水性醇酸树脂的合成工艺。确定了以熔融法和分步加料来制备醇酸树脂。以紫胶部分替代三羟甲基丙烷,顺丁烯二酸酐/偏苯三酸酐部分替代苯酐,所得水性醇酸树脂的干燥性能、硬度和柔韧性等性能得以提高。紫胶用量以5%为宜。     

水性醇酸树脂的合成及性能研究

通过脂肪酸法，选用豆油脂肪酸、偏苯三甲酸酐和不同的多元醇、多元酸制备了一系列水性醇酸树脂，用苯甲酸、顺丁烯二酸酐和油酸对其改性进行了研究。通过对合成产品性能如黏度、粒径、硬度、附着力、耐水性、耐汽油性等的研究，确定了综合性能较好的水性醇酸树脂。