制备态(Fe88Zr7B5)100-xCux非晶薄膜的磁特性和巨磁阻抗

采用射频溅射法在单晶Si衬底上制备了Fe88Zr7B5)100-xCux(x=0、1、2、3、4)非晶薄膜样品,对其软磁特性和巨磁阻抗(GMI)变化行为进行了测量和研究。测量结果显示,加入适量Cu元素(x=3)的制备态样品具有极好的软磁性能和GMI效应,此样品的矫顽力仅有56A/m,在13MHz的频率下,最大有效磁导率(μe)比和GMI比分别为42.5%和17.0%。研究发现,制备态样品的电阻R、电抗X和阻抗Z都随Cu含量的增加而下降。X=0、4两个样品的μe、R、X、Z对外加磁场响应极不敏感,只有软磁性能优异的x=3样品的μe、R、X、Z才显示出对外加磁场响应敏感,因而有显著的GMI效应。样品拥有高的磁导率、小的矫顽力和低的电阻率是获得大GMI效应的本质条件。     

薄膜厚度对多层膜巨磁阻抗效应的影响研究

采用磁控溅射方法在玻璃基片上制备了FeSiB／Cu／FeSiB多层膜,在100kHz～40MHz范围内研究了FeSiB薄膜厚度对FeSiB／Cu／FeSiB多层膜巨磁阻抗效应的影响。当磁场施加在薄膜的纵向时,巨磁阻抗效应随磁场的增加而增加,在某一磁场下达到最大值,然后随磁场的增加而下降到负的巨磁阻抗效应。当FeSiB薄膜的厚度为1．8μm时,在频率3．2MHz、磁场2．4kA／m时,多层膜巨磁阻抗效应达最大值13．5％;在磁场为9．6kA／m时,巨磁阻抗效应为-9．2％。然而,当FeSiB薄膜的厚度为1μm时,多层膜的巨磁阻抗效应在频率40MHz、磁场1．6kA／m时达最大值5．8％。另外,当磁场施加在薄膜的横向时,薄膜表现出负的巨磁阻抗效应。对于膜厚为1．8μm的FeSiB薄膜,在频率5．2MHz、磁场9．6kA／m时,巨磁阻抗效应为-12％。可见巨磁阻抗效应的最大值及负的巨磁阻抗效应与多层膜中磁各向异性轴的取向及FeSiB薄膜的厚度有关。     

FeCuNbSiB多层膜的磁化特性与巨磁阻抗效应

用射频磁控溅射法制备了FeCuNbSiB多层膜,制备态样品的GMI效应在驱动电流频率为12MHz时达到最大,为44．3％。利用复数磁导率和等效电路讨论了该多层膜的磁化过程,及与GMI效应的关系。外加直流磁场抑制磁畴运动,在等效电路中与抵消并联电路相关。样品磁化的特征弛豫频率在12MHz左右,与出现最大磁阻抗变化的频率接近。     

纳米晶FeCuNbSiB多层膜的巨磁阻抗效应研究

研究了纳米晶态下Fe73.5Cu1Nb3Si13.5 B9多层膜的巨磁阻抗(GMI)效应。研究结果表明纵向巨磁阻抗(LMI)效应在3MHz时取得最大值为44％,横向巨磁阻抗(TMI)效应在6MHz时取得最大值为46％。LMI与TMI随外磁场有不同的变化行为,TMI曲线具有阁值行为,超过阈值磁场后出现明显的磁阻抗效应。晶化后出现最大值阻抗效应所对应的频率下降,由非晶态下的13MHz下降为晶化后的3MHz。薄膜样品的磁阻抗效应与样品中磁矩的空间分布密切相关．磁矩垂直面向分布时。磁阻抗效应下降为5％     

玻璃包覆钴基非晶丝巨磁阻抗效应(英文)

本文讨论了长度对玻璃包覆钴基非晶丝巨磁阻抗效应的影响.通过测量不同频率下(0.1～1MHz)以及不同长度样品的巨磁阻抗效应,结果表明,长度对玻璃包覆钴基非晶丝巨磁阻抗效应有显著影响.通过计算样品的环向磁导率,发现样品的磁畴结构和饱和磁化后的退磁场影响着环向磁导率变化大小.没有加入恒定磁场时,特殊的磁畴结构决定了不同长度样品的环向磁导率近似相等.饱和磁化后,较长的样品的环向磁导率较小,其环向磁导率的变化较大,从而导致相应的巨磁阻抗效应增强.     

FeSiB／Cu／FeSiB多层膜巨磁阻抗效应研究

用磁控溅射法在玻璃基片上制备了FeSiB/Cu/FeSiB多层膜,在100kHz-40MHz范围内研究了FeSiB/Cu/FeSiB多层膜中的巨磁阻抗效应特性。当磁场强度Ha施加在薄膜的长方向时,巨磁阻抗效应随磁场的增加而增加,在某一磁场下达到最大值,然后随磁场的增加而下降到负的巨磁阻抗效应。在频率为3.2MHz时,在磁场强度Ha=2400A/m时巨磁阻抗变化率达到最大值13．50％;在磁场强度Ha=9600A/m时,巨磁阻抗变化率为－9．20％。巨磁阻抗效应的最大值及负的巨磁阻抗效应与多层膜中磁各向异性轴的取向及发散有关。另外,当磁场施加在薄膜的短方向时,薄膜表现出负的巨磁阻抗效应,在频率为3．2MHz,磁场强度Ha=9600A/m时,巨磁阻抗变化率可达－12．50％。     

熔体抽拉非晶微丝长度对巨磁阻抗的影响

研究了不同频率下非晶丝长度对巨磁阻抗(GMI)的影响规律和机制。低频下(<1MHz),由于边界效应对有效磁场的影响使得GMI效应随非晶丝长度减小而逐渐减小,1MHz时,随样品长度由20mm减小到4mm,其最大阻抗变化率ΔZ/Z由8.07%减小到1.03%;频率升高,由于趋肤效应和磁化机制的改变,而电阻随长度减小而减小利于获得大的环向磁导率,边界效应和电阻降低的共同影响下,存在一个最佳长度时,环向磁导率变化剧烈,GMI效应最强,结果表明直径34μm的熔体抽拉Co基非晶丝长度为7mm左右时,GMI效应最敏感,8MHz时最大ΔZ/Z达到86.1%。这一结果将为不同频率下MI传感器制备时样品长度选择提供参考。     

淬态FeNiCrSiB薄带的磁特性和纵向巨磁阻抗效应

采用单辊快淬法制备了(Fe50Ni50)77.5Cr0.5Si11B11合金薄带,测试了淬态薄带样品的微结构、静磁性能、磁导率和磁阻抗。研究结果表明,未经热处理的淬态(Fe50Ni50)77.5Cr0.5Si11B11合金薄带便具有良好的软磁性能和显著的巨磁阻抗效应,在7MHz频率下,纵向最大阻抗比达到31%。同时分析了几个典型频率下的纵向磁阻抗比、电阻比、电抗比和有效磁导率比随外磁场的变化行为,发现薄带样品的电抗比和有效磁导率比之间存在密切联系。由于内部结构的不均匀性,使得样品的横向各向异性场随驱动电流频率增大向高场方向移动。     

三明治结构FeNi/Cu/FeNi多层膜巨磁阻抗效应研究

采用MEMS技术在玻璃基片上制备了三明治结构FeNi/Cu/FeNi多层膜,在1～40 MHz范围内研究了FeNi/Cu/FeNi多层膜中的巨磁阻抗效应特性.当磁场Ha施加在薄膜的长方向时,巨磁阻抗效应随磁场的增加而增加,在某一磁场下达到最大值,然后随磁场的增加而下降到负的巨磁阻抗效应.在频率为5MHz时,巨磁阻抗效应在磁场Ha=800 A/m时达到最大值26.6%.巨磁阻抗效应的最大值及负的巨磁阻抗效应与多层膜中磁各向异性轴的取向及发散有关.另外,当磁场施加在薄膜的短方向时,薄膜表现出负的巨磁阻抗效应,在频率5 MHz、磁场Ha=9600 A/m时,巨磁阻抗效应可达-15.6%.     

FeSiB/Cu/FeSiB多层膜巨磁阻抗效应研究

用磁控溅射法在玻璃基片上制备了FeSiB/Cu/FeSiB多层膜,在100kHz～40MHz范围内研究了FeSiB/Cu/FeSiB多层膜中的巨磁阻抗效应特性.当磁场强度Ha施加在薄膜的长方向时,巨磁阻抗效应随磁场的增加而增加,在某一磁场下达到最大值,然后随磁场的增加而下降到负的巨磁阻抗效应.在频率为3.2MHz时,在磁场强度Ha=2400A/m时巨磁阻抗变化率达到最大值13.50%;在磁场强度Ha=9600A/m时,巨磁阻抗变化率为-9.20%.巨磁阻抗效应的最大值及负的巨磁阻抗效应与多层膜中磁各向异性轴的取向及发散有关.另外,当磁场施加在薄膜的短方向时,薄膜表现出负的巨磁阻抗效应,在频率为3.2MHz,磁场强度Ha=9600A/m时,巨磁阻抗变化率可达-12.50%.     

Insertion of triangulated surfaces into a meccano tetrahedral discretization by means of mesh refinement and optimization procedures

In this paper, we present a new method for inserting several triangulated surfaces into an existing tetrahedral mesh generated by the meccano method. The result is a conformal mesh where each inserted surface is approximated by a set of faces of the final tetrahedral mesh. First, the tetrahedral mesh is refined around the inserted surfaces to capture their geometric features. Second, each immersed surface is approximated by a set of faces from the tetrahedral mesh. Third, following a novel approach, the nodes of the approximated surfaces are mapped to the corresponding immersed surface. Fourth, we untangle and smooth the mesh by optimizing a regularized shape distortion measure for tetrahedral elements in which we move all the nodes of the mesh, restricting the movement of the edge and surface nodes along the corresponding entity they belong to. The refining process allows approximating the immersed surface for any initial meccano tetrahedral mesh. Moreover, the proposed projection method avoids computational expensive geometric projections. Finally, the applied simultaneous untangling and smoothing process delivers a high‐quality mesh and ensures that the immersed surfaces are interpolated. Several examples are presented to assess the properties of the proposed method.     

Certification Institutions Expected to Update and Transfer Information on Present Standards

Standards are the basis for production enterprises to organize production, ex-factory inspection, trade (delivery) and technical exchanges, product certification, quality arbitration and supervision.……     

Flow calorimeter for enthalpy increment measurements on condensed gases

A flow calorimeter for enthalpy increment measurements on condensed gases is presented. A better knowledge of the properties of the liquefied natural gas is needed, and therefore a liquid loop has been designed for our flow calorimeter. The fluid loop in the calorimeter is designed in order to avoid the two-phase region, since two phases would give compositional disturbances in the measurements. The avoidance of the two-phase region is made possible by increasing the pressure of the test fluid after the measurement section, then heating the fluid at super-critical pressure past the critical point. Finally, the fluid is throttled to the low-pressure gas state at the inlet condition of the compressor that circulates the fluid. To perform the pressure increase, a new cryogenic pump has been designed. To evaluate the new equipment, measurements were taken on liquid ethane over the temperature range 146–256 K at pressure between 0.9 and 5.1 MPa.     

Refrigerators Enter a New Era of Health Preservation Frestech initiates the establishment of China's first standard for household sterilization refrigerators

On November 30, 2007, the China Association for Standardization (CAS) held a press conference at Beijing Diaoyutai State Guest House. Leaders from the China Household Electric Appliance Research Institute, the China Household Electric Appliance Association, and the China Consumers' Association attended and made speeches.……     

Optimum-Simulation von Ernteprozessen

Zusammenfassung Bei der Gestaltung von Ernteprozessen — beispielsweise des Prozesses Mähdrusch, Körnertransport und -abnahme — als transportverbundene Fließarbeitsverfahren mit mindestens zwei verschiedenen Arbeitsmitteln gibt es einen großen Optimierungsspielraum. Solche Prozesse sind mehrstufige Bedienungsprozesse mit gemischter Anordnung der Bedienungseinrichtungen. Außerdem besitzen sie stark ausgeprägte räumliche Aspekte. Es wird vor allem gezeigt, welche Merkmale solcher Prozesse in Simulationsmodellen abgebildet sein müssen, welche Zielgrößen in Abhängigkeit von welchen Einflußgrößen unter Berücksichtigung welcher Prozeßbedingungen ermittelt werden sollten und wie der Bewertungsprozeß zur Ermittlung der gewünschten Informationen gestaltet werden muß.     

A study of centrifugal cast high boron high speed steel

In the present study a high‐boron high speed steel (HSS) roll material was designed. Many expensive alloy elements have been substituted by cheap boron alloy, and high‐boron high speed steel roll has been manufactured by centrifugal casting method. The microstructures, mechanical properties and wear resistance of centrifugal casting high‐boron high speed steel roll have been investigated by optical microscopy (OM), scanning electron microscopy (SEM), and X‐ray diffraction (XRD) analysis, hardness test, impact test and wear test. The results indicated that the solidification microstructures of high‐boron high speed steel roll consisted of M₂(B,C), (W,Mo)₂(B,C), M₃(B,C), M₂₃(B,C)₆ type borocarbides and martensite, a small amount of retained austenite. Borocarbides were continuously distributed over the grain boundary. After quenching from 1050 °C, local broken network appeared in partial borocarbides, and fine secondary borocarbide precipitated from the matrix. After tempering from 525 °C, the amount of precipitated borocarbide increased significantly. After heat treatment, the hardness of high‐boron high speed steel roll excelled 60 HRC, and its impact toughness excelled 8.0 J/cm². The single groove steel rolling amount of high‐boron high speed steel rolls increases by 500% than that of bainite cast iron roll, when the rolls are used in K₁ mill housing of bar mill.     

Thixotropy of Systems with Shear Thinning and Plastic Flow Behavior

The definition of the thixotropy is a decrease in viscosity with time in shear and a subsequent recovery of viscosity after the shear deformation is removed.We ...     

Brainstorming for ISO Strategy 2016-2020

正Responding to ISO’s appeal for survey for the to-be-developed ISO Strategy Plan for 2016-2020,SAC hosted a special workshop over the needs and comments of various fi elds on June 8 in Beijing.The workshop was attended by ISO President-elect and Ansteel General Manager Zhang Xiaogang,SAC Vice-Administrator Yu Xinli,and 30 experts from     

CNAS Passes APLAC's PTP Review

正The review group of Asia Pacific Laboratory Accreditation Cooperation(APLAC)carried out a 4-day peer review of the proficiency testing provider(PTP)for China National Accreditation Service for Conformity Assessment(CNAS)from July 28 to 31,2014.CNAS passed the PTP review with excellent performance.Two senior peer reviewers of APLAC made a comprehensive,rigorous and detailed review of CNAS’s PTP accreditation activities,and made the on-spot inspection of the review groups in Shanghai and Shenzhen respectively.