咪唑烷修饰的吸附树脂对水溶液中2-咪唑烷酮的吸附

合成了一种用咪唑烷修饰的超高交联吸附树脂LG-01,并用二甲氨基修饰的超高交联吸附树脂NDA99作对照,比较了它们对水溶液中2-咪唑烷酮的静态吸附和脱附行为。结果表明,经过咪唑烷修饰的吸附树脂LG-01在一定温度时对2-咪唑烷酮的吸附过程中存在不可逆吸附作用和氢键作用,LG-01对2-咪唑烷酮的吸附能力明显强于NDA99,2种树脂对2-咪唑烷酮的吸附均符合Langmuir方程和Freundlich方程。     

氧化树脂对水溶液中2,4-二氯苯酚的吸附特征

用H2O2或HNO3氧化超高交联吸附树脂NDA150的方法制备了新型吸附树脂ZH-07和ZH-08,并通过元素分析和比表面积及孔径分布仪进行了表征。同时以NDA150作为参照,研究了它们对不同温度下水溶液中2,4-二氯苯酚的静态吸附和脱附特征,并对其吸附机理进行了探讨。结果表明,ZH-07和ZH-08对2,4-二氯苯酚具有和NDA150相近或更优的吸附容量,对水溶液中2,4-二氯苯酚的吸附过程存在化学吸附作用,也可以提高它们对水溶液中2,4,-二氯苯酚的吸附容量。     

氨基酸修饰的吸附树脂对间苯三酚的吸附效果

采用脯氨酸、甘氨酸或L-谷氨酸三种氨基酸分别在NDA150上进行化学修饰(分别代号为ZHP02、ZHG02、ZHL02),并以NDA150为参照,用红外、比表面积孔径测定仪和元素分析仪进行了表征。在不同温度下将修饰的树脂用于对水中间苯三酚进行静态吸附实验,考察其吸附容量,并以实际废水进行了动态吸附和脱附验证,结果表明,羧酸基对吸附间苯三酚具有较好的吸附选择性,静态吸附和脱附条件的比较结果也证实了吸附过程中存在不可逆化学吸附。     

啶虫脒在超高交联吸附树脂上的吸附及脱附性能研究

本文从动态和静态的角度研究了均苯四甲酸酐修饰的超高交联吸附树脂（PMAR）和1,2,4-苯三酸酐修饰的超高交联吸附树脂（TMAR）对啶虫脒的吸附和脱附行为。结果表明：两种树脂对啶虫眯的吸附和脱附效果都比较好,TMAR的静态吸附量为470．9mg·g^-1干树脂,饱和吸附量为562．7mg·g^-1干树脂;PMAR的静态吸附量为453．4mg·g^-1干树脂,饱和吸附量为559．1mg·g^-1干树脂。两种树脂都易于脱附,用2mol·L^-1 HCl：乙醇（体积比1：1）作脱附剂,温度323K,脱附剂体积为9．5BV（床体积）时,PMAR的脱附率为98．13％,TMAR的脱附率为99．83％。     

萘酚修饰超高交联吸附树脂的制备及吸附动力学

明胶为分散剂,液蜡为致孔剂,交联反应中溴乙烷代替有毒氯甲醚,以β-萘酚参与Friedel-Crafts后交联反应,成功制备了酚羟基修饰的超高交联吸附树脂LM-6。树脂物理性能研究表明,LM-6具有比苯酚修饰超高交联树脂更大的比表面积和酚羟基含量;扫描电镜(SEM)表明,β-萘酚修饰的超高交联吸附树脂具有纳米吸附高分子材料特征;动力学分析表明,树脂对β-萘酚吸附界面层厚于萘,树脂和β-萘酚分子间具有更大的吸附力;拟合曲线均不经过原点说明LM-6对β-萘酚和萘的吸附由颗粒内扩散和颗粒外膜扩散共同控制。     

萘酚修饰超高交联吸附树脂的制备及吸附动力学EI北大核心

明胶为分散剂,液蜡为致孔剂,交联反应中溴乙烷代替有毒氯甲醚,以β-萘酚参与Friedel-Crafts后交联反应,成功制备了酚羟基修饰的超高交联吸附树脂LM-6。树脂物理性能研究表明,LM-6具有比苯酚修饰超高交联树脂更大的比表面积和酚羟基含量;扫描电镜(SEM)表明,β-萘酚修饰的超高交联吸附树脂具有纳米吸附高分子材料特征;动力学分析表明,树脂对β-萘酚吸附界面层厚于萘,树脂和β-萘酚分子间具有更大的吸附力;拟合曲线均不经过原点说明LM-6对β-萘酚和萘的吸附由颗粒内扩散和颗粒外膜扩散共同控制。     

乙酰苯胺修饰的吸附树脂对对甲苯胺的吸附机理研究

合成了一种用乙酰苯胺修饰的新型超高交联吸附树脂ZH-05,并用Amberlite XAD-4作对照,比较了它们对水溶液中对甲苯胺的静态吸附和脱附行为。结果表明:经过乙酰苯胺修饰的吸附树脂ZH-05在一定温度下对对甲苯胺的吸附过程中存在化学吸附,ZH-05对对甲苯胺的吸附能力明显强于AmberliteXAD-4,两种树脂对甲苯胺的吸附均符合Freundlich方程。     

巯基修饰的超高交联树脂对酚类化合物的吸附

对超高交联聚苯乙烯树脂进行巯基修饰,对比大孔吸附树脂(Amberlite XAD-4)对苯酚、对甲苯酚、对氯苯酚、对硝基苯酚在水溶液中进行吸附研究。经过巯基修饰的超高交联聚苯乙烯树脂(JN-8)具有亲水性高、对酚类化合物吸附容量大的优点,该树脂可望在高浓度含酚废水治理中得到应用。     

乙酰苯胺和水杨酸修饰的两种吸附树脂对对氯苯酚的吸附行为

分别用乙酰苯胺、水杨酸化学修饰氯甲基化低交联大孔苯乙烯-二乙烯苯聚合物,合成超高交联吸附树脂FZH03、FZH04。与Amberlite XAD-4对照,研究了这两种树脂在不同温度下对水溶液中对氯苯酚的静态吸附和动态吸附行为。结果表明,两种树脂的等温吸附数据可被Langmuir和Freundlich等温吸附方程很好地进行拟合,对对氯苯酚的吸附量明显高于XAD-4,是焓推动的吸附过程,对对氯苯酚吸附动力学均符合一级动力学方程,有两个独立的动力学过程,颗粒内扩散是该吸附过程的速控步骤。     

一种新型两亲性超高交联树脂对p-硝基苯酚的吸附行为研究

选用N-乙烯基吡咯烷酮和间苯型不饱和聚酯为单体,合成了新型两亲性的超高交联吸附树脂(NU).通过静态吸附实验,研究了NU树脂在不同温度下吸附水溶液中p-硝基苯酚的热力学和动力学特性,结果表明,吸附符合一级动力学方程,NU树脂吸附p-硝基苯酚符合Freundlich模型,通过计算△H＜0,为放热反应.     

Adsorption of trichloroethylene and benzene vapors onto hypercrosslinked polymeric resin

In this research, the adsorption equilibria of trichloroethylene (TCE) and benzene vapors onto hypercrosslinked polymeric resin (NDA201) were investigated by the column adsorption method in the temperature range from 303 to 333 K and pressures up to 8 kPa for TCE, 12 kPa for benzene. The Toth and Dubinin–Astakov (D–A) equations were tested to correlate experimental isotherms, and the experimental data were found to fit well by them. The good fits and characteristic curves of D–A equation provided evidence that a pore-filling phenomenon was involved during the adsorption of TCE and benzene onto NDA-201. Moreover, thermodynamic properties such as the Henry's constant and the isosteric enthalpy of adsorption were calculated. The isosteric enthalpy curves varied with the surface loading for each adsorbate, indicating that the hypercrosslinked polymeric resin has an energetically heterogeneous surface. In addition, a simple mathematic model developed by Yoon and Nelson was applied to investigate the breakthrough behavior on a hypercrosslinked polymeric resin column at 303 K and the calculated breakthrough curves were in high agreement with corresponding experimental data.     

光氯化-烷基化两步法制备超高交联树脂及对苯酚的吸附性能

通过对二甲苯侧链光氯化产物(CP)与苯(BE)的Friede-l Crafts烷基化聚合反应制备比表面积高达905m2/g的超高交联吸附树脂(CP-BE)材料,并用红外光谱(FT-IR)、元素分析(EA)及比表面积(BET)对其结构进行表征。以XDC-BE和市售Amberlite XAD-4为参照,在不同温度下,测试了三种吸附树脂对水溶液中苯酚的吸附性能,结果表明,CP-BE和XDC-BE树脂对苯酚的吸附量分别高达171 mg/g和143 mg/g,远高于国内外用于酚类吸附的Amberlite XAD-4树脂,有望在酚类废水资源化治理中得到实际应用。     

乙酰苯胺修饰的后交联树脂的制备及对香兰素吸附性能

用二氯乙烷为溶剂,用FeCl3为催化剂,使氯球和乙酰苯胺发生Friedel-Crafts反应制得了乙酰苯胺修饰的后交联树脂,详细研究了反应条件对树脂孔结构及对香兰素吸附性能的影响。根据树脂的比表面积、孔容、持水量、氯含量和对香兰素的吸附量等孔结构和性能指标来看,乙酰苯胺修饰的后交联树脂制备的最优条件为：用二氯乙烷为溶剂...     

超高交联树脂对氯酚类化合物的吸附性能

通过静态吸附研究,比较了Am berlite XAD-4和ZH-01吸附树脂对水溶液中2-氯苯酚、2,4-二氯苯酚、2,4,6-三氯苯酚的吸附热力学特性。结果表明,在288 K~318 K和研究的浓度范围内,ZH-01、XAD-4对氯酚类化合物的吸附平衡数据符合F reund lich和L angm u ir吸附等温方程。2-氯苯酚在两树脂上的吸附为放热过程,是单分子层的物理吸附;而2,4-二氯苯酚和2,4,6-三氯苯酚在XAD-4吸附是单分子层物理吸附,在ZH-01的吸附属单分子层吸热过渡化学吸附,主要是毛细管凝聚和微孔填充作用造成的吸附。并计算了氯酚类化合物在两树脂上的吸附焓变、自由能变、吸附熵变,对吸附行为进行了合理的解释。     

非苯乙烯型超高交联树脂的修饰及对酚类化合物的吸附

分别通过4,4'-二氯甲基联苯与1,4'-二氟甲基苯的傅克烷基化聚合和胺化反应,制得一类比表面积可达1138 m2/g的胺基吸附树脂新材料.研究表明,这类非苯乙烯型胺基树脂对苯酚、对硝基苯酚的饱和吸附容量分别可达140 mg/g和331 mg/g,明显优于国内外用于酚类吸附的AmberliteXAD-4、H103等吸附...     

吸附树脂及其在水与废水处理中的应用

主要论述了吸附树脂的分类、合成、性能及其在水处理中的应用,重点讨论了人工合成及天然高分子改性吸附树脂的合成、性能及其在微污染水源给水处理及废水处理中应用的研究进展.其由于在废物处理和资源回收方面的良好前景而受到青睐,并有逐渐取代活性炭成为新一代吸附剂的趋势,但对其工程化的应用尚需继续研究.最后展望了高分子吸附剂(吸附树脂)的研究及应用前景,提出了今后吸附树脂的研究发展方向.     

SBA-15介孔分子筛吸附电镀废水中Cu2＋的最佳条件和效果

为了开发新型高效廉价的吸咐材料,利用常压微波辐射法在酸性条件下以三嵌段共聚物（P123）为模板剂,制备了高度有序的SBA．15型介孔分子筛。研究了静态条件下SBA-15对电镀废水中Cu2＋的吸附,探讨了SBA-15用量、废水pH值、吸附时间、吸附温度对去除Cun效果的影响。结果表明：废水pH值为5．0,Cu2＋在0—1...