烧碱浓度及冲刷对合金铸铁耐碱腐蚀性能的影响

采用失重法测定稀土镍铜合金铸铁在不同浓度烧碱液中以及静、动态下的腐蚀速度.结果表明,随着浓度的升高,稀土镍铜合金铸铁的腐蚀速度加快,而适量的稀土含量可降低合金铸铁对浓度的敏感性.碱液的冲刷会加剧稀土镍铜合金铸铁的腐蚀.     

稀土对镍铜合金铸铁耐烧碱腐蚀性能的影响

针对天然碱制碱工业中设备的腐蚀问题,研制出4种成分的稀土镍铜合金铸铁,进行金相组织分析,利用自制的动态腐蚀试验装置模拟碱腐蚀条件,测试其腐蚀速度,并对耐碱腐蚀性能进行评价.借助扫描电镜对镍铜合金铸铁的表面腐蚀形貌和微区成分分析,详细地讨论了稀土在铸铁中的作用与耐蚀机理.结果表明:稀土镍铜合金铸铁在高温浓烧碱液中宏观上属于全面腐蚀,微观上存在不同程度的镍、铜元素富集.加入适量的稀土,可以减小合金铸铁在烧碱液中的腐蚀速度,有效的改善合金铸铁的耐碱腐蚀性能.但是稀土加入过量会造成合金铸铁的耐碱腐蚀性能的下降.     

稀土镍铜合金铸铁耐碱腐蚀性能研究

采用动态失重法测定稀土镍铜合金铸铁在高温浓碱液中的腐蚀速度,借助光学显微镜和扫描电镜观察显微组织和表面腐蚀形貌,利用能谱仪分析表面微区成分。结果表明：高温浓碱中的动态腐蚀条件下,稀土含量为0.05%的试样耐碱蚀性相对较好,其微观腐蚀表面呈现出平坦、基体面积大和凸起碳化物量少的特点;稀土镍铜合金铸铁的碱腐蚀属于均匀腐蚀,其耐蚀性主要取决于石墨和碳化物的数量、大小和分布;微观基体上富集的镍和铜有利于提高该区域的耐蚀性。     

稀土对铸铁耐高温烧碱腐蚀性能的影响

针对天然碱制碱工业中设备的腐蚀问题,研制出5种成分的稀土镍铜合金铸铁,测试其腐蚀速度,并对其耐碱腐蚀性能进行评价。结果表明:加入适量的稀土可明显提高铸铁的耐烧碱腐蚀性能,但是加入过量稀土会造成铸铁的耐碱腐蚀性能下降。     

镍含量对钼铬铜合金铸铁组织及耐磨性能的影响

采用金相显微镜、洛氏硬度计、扫描电镜等方法,研究镍含量对钼铬铜合金铸铁微观组织及硬度的影响,并研究其二体磨损性能。结果表明:向钼铬铜合金铸铁添加一定的镍可提高合金的淬透性,增加基体中马氏体和贝氏体的含量,提高合金硬度,并细化石墨,同时提高合金的耐磨损性。当镍含量过高时,合金基体中残余奥氏体含量增加,石墨变细,裂纹增多,合金硬度和耐磨性降低。添加Ni含量为1.81%时,钼铬铜合金铸铁的耐磨性能较优。     

铸态马氏体高铬铸铁搅拌机衬板的研究

利用正交试验方法，研究了钼、硼及铜合金元素对高铬铸铁铸态组织和力学性能的影响。研究结果表明：随钼及用含量增加，硬度升高，冲击韧性和抗奇强度降低；而钢对其性能影响不大。铸态马氏体高铬铸铁的耐磨性是镍硬铸铁的3倍以上。用铸态马氏体高铬铸铁制造的沥青混凝土搅拌机衬板耐磨性是低合金白口铸铁衬板的14倍多。     

烧碱浓度、温度、冲刷对镍铜合金铸铁耐碱腐蚀性能的影响

采用失重法测定镍铜合金铸铁在不同浓度、温度烧碱液中以及静、动态下的腐蚀速度.结果表明,随着温度、浓度的升高,镍铜合金铸铁的腐蚀速度加快,而合金元素镍可降低合金铸铁对温度、浓度的敏感性.碱液的冲刷套加剧镍铜合金铸铁的腐蚀.     

镍铜合金铸铁耐碱腐蚀机理

针对天然碱制碱工业中设备的腐蚀问题,研制出5种成分的镍铜合金铸铁,对其进行了金相组织分析,在此基础上,利用自制的动态腐蚀试验装置模拟碱腐蚀条件,测试其腐蚀速度,并对其耐碱腐蚀性能进行评价.借助扫描电镜对镍铜合金铸铁的表面腐蚀形貌和徽区成分分析,详细讨论了镍、铜在铸铁中的作用与耐蚀机理.结果表明,镍铜合金铸铁在高温浓烧碱液中宏观上属于全面腐蚀,微观上存在不同程度的镍、铜元素富集,其中N4、N5合金铸铁耐蚀性较高.     

稀土硬镍合金铸铁的组织与性能研究

硬镍合金铸铁是一种良好的抗磨材料，但由于其碳化物呈网状和组织粗大，使其韧性低和性能不够稳定。为此，研究了稀土变质处理对硬镍合金铸铁组织和性能的影响。试验结果表明，稀土变质处理，可使硬镍舍金铸铁的碳化物呈块状或片状，组织得到明显细化与均匀化，并增加马氏体含量。因此，稀土硬镍合金铸铁具有良好的综合机械性能和较高的抗冲蚀磨损性能，具有广阔的应用前景。     

电铸制备镍铜合金电热组件试验研究

陶瓷基板电热组件具有加热均匀性好、电热转换效率高等优点，广泛应用于需低温加热场合，然而传统金属-陶瓷共烧技术因成本高、效率低而制约发展。通过采用电铸工艺在陶瓷基板上制备镍铜合金电热组件，研究发现镍铜合金电铸层的平均晶粒尺寸随着电铸液温度的升高而增大，电阻率随晶粒尺寸的增大而减小，同时电流密度会显著影响镍铜合金电铸层中镍的含量，进而影响镍铜合金电铸层的线膨胀系数。     

灰口铸铁空泡腐蚀过程的SEM跟踪观察

采用空泡腐蚀与定位跟踪观察交替进行的方式,研究了灰口铸铁在自来水中空泡腐蚀过程的表面形貌演变。结果表明:灰铸铁空泡腐蚀系由两个相继发生而又彼此联系的过程组成:(1)片状石墨由表及里脱落形成表面缝隙;(2)表面缝隙的扩展与交汇导致珠光体团块状剥落。还讨论了石墨片的空间取向对珠光体团剥落的影响。     

In Situ fracture observation and fracture toughness analysis of pearlitic graphite cast irons with different nodularity

Effects of microstructural modification and microfracture mechanisms on fracture toughness of pearlitic graphite cast irons with different nodularity were investigated by in situ observation of microfracture process. Six pearlitic graphite cast irons were fabricated by adding a small amount of Mg as a nodularizing element for graphite, and their microstructures including pearlite, ferrite, graphite, and eutectic carbide were analyzed. Most of ferrites were observed in a layer shape around graphites because of carbon-depleted zones formed near graphites. As the nodularity and nodule count increased, fracture toughness linearly increased in the cast irons except the iron containing many fine graphites. According to in situ observation of microfracture process, cracks initiated at nodular graphites and carbides even at a small load, and then propagated readily through the adjacent graphites or carbides, thereby resulting in the lowest fracture toughness. The cast iron having widely spaced graphites and ferrite layers thickly formed around graphites showed the highest fracture toughness because of the blocking of crack propagation by ductile ferrite layers and the crack blunting and deflection by graphites, which was also confirmed by the R-curve analysis.     

铜镍合金铸铁耐碱腐蚀性能研究

采用动态失重法测定铜镍合金铸铁在高温浓碱液中的腐蚀速度,借助光学显微镜和扫描电镜观察显微组织和表面腐蚀形貌,利用能谱仪分析表面微区成分。结果表明,微观基体上富集的铜和镍有利于提高铜镍合金铸铁的耐蚀性,在高温浓碱液中的动态腐蚀条件下,铜含量为4.5%的D3试样耐碱蚀性较好。当铜含量超过一定值时,铜镍合金铸铁中析出游离铜相,这些新相成为活性阴极相,降低铸铁的耐蚀性。     

耐海水腐蚀低合金球墨铸铁的初步研究

用挂片法研究了HDQ铸铁（耐海水腐蚀低合金球铁）在全浸和半浸状态下的耐海水腐蚀性。结果表明：HDQ铸铁的耐海水腐蚀性能比HD铸铁（耐海水腐蚀低合金铸铁）提高了2．4倍。     

低合金铸铁在流动海水中的腐蚀研究

对四种不同石墨形态、基体和不同低合金成分铸铁 ,在三种流速海水中的腐蚀进行了测试 ,用化学—电化学溶解和冲蚀—腐蚀理论分析了铸铁在流动海水中的腐蚀机理 ,并相应分析了海水流动速度 ,铸铁石墨形态和合金成分对铸铁动海腐蚀的影响     

海洋环境下耐蚀铸铁的研究现状

首先分析了耐蚀铸铁在海水中的腐蚀特性.指出铸铁的石墨形态不影响其均匀腐蚀,但是显著影响铸铁的局部腐蚀,而且在不同的海洋环境下铸铁的腐蚀程度不同;其次列举了几种常用的海水耐蚀铸铁的性能及应用,铸铁低合金化在一定程度上能够改善耐腐蚀性能,而高合金化能够显著改善其耐腐蚀性能,但低合金铸铁的合金元素少,铸造工艺简单,成本低等优势,易于推广使用。最后对现在存在的问题和发展方向作了简要的介绍。     

新型低合金耐磨耐蚀铸铁的开发与应用

通过对不同成分的Cr,Cu,Sb低合金耐磨耐蚀铸铁的研制,获得在合金总量不超过3%,而其耐磨耐蚀性能较好的低合金耐磨耐蚀铸铁NMSHT9。实际应用表明,它是一种价格低廉、性能良好的耐磨耐蚀铸铁。     

渣浆泵过流部件用合金新材料

渣浆泵过流部件工况苛刻,延长渣浆泵过流部件的寿命成为材料工作者关注的课题。在延长使用寿命的前提下,降低贵重合金元素的用量,寻找代用的合金元素,对泵的过流件的工作表面强化可降低材料成本。渣浆泵过流部件合金新材料有高铬铸铁、超高铬铸铁、中铬铸铁、耐腐蚀合金和金属陶瓷。金属陶瓷按制备方法分为整体强化、表面处理强化,表面处理强化的手段有化学热处理、PVD气相沉积和等离子喷涂。     

铸铁在海洋腐蚀环境下的防护措施

普通铸铁、低合金铸铁在海洋腐蚀条件下是不耐蚀的,采取防护措施可使铸铁材料的耐腐蚀性能大幅提高,其中尤以金属热喷涂和有机涂层防护为好,是提高铸铁材料在海洋环境下防腐能力的有效途径。     

耐海水腐蚀低合金铸铁的耐蚀性及保护膜

用全浸、半浸和间歇浸泡的静态方式,将分别具有片状及球团状石墨的低合金耐海水腐蚀铸铁(分别简称HD铸铁及HDQ球铁)在海盐溶液中做对比腐蚀试验后得出:间歇浸泡腐蚀失重最为严重,约为全浸泡时的2倍;HDQ球铁的耐蚀性较HD铸铁提高1倍左右。文中还研究了试样表层保护膜的成分、结构与耐蚀性的关系。