配料对焚烧飞灰电弧炉熔渣晶化行为的影响

将垃圾焚烧飞灰电弧炉熔融处理后的液态熔渣直接浇铸成型后热处理,运用同步热分析仪、X射线衍射仪和扫描电镜等方法,研究废玻璃和晶核剂(TiO2和Cr2O3)等辅助原料的添加对微晶玻璃晶化行为及性能影响.研究表明,适量掺加废玻璃对微晶玻璃理化性能有显著改善,晶核剂类型及添加比对微晶玻璃主晶相和晶化程度影响较大,微晶玻璃的理想原料配比为m(废玻璃)∶m(垃圾焚烧飞灰)=1∶1,晶核剂TiO2添加质量分数为3%,制成的微晶玻璃主晶相为透辉石Ca(Mg,Al)(Si,Al)2O6和少量普通辉石Ca(Mg,Fe,Al)(Si,Al)2O6,抗弯强度54.96 MPa,主要理化性能达到或优于天然花岗岩和大理石,重金属浸出浓度低于国际建材环保要求限值.     

利用热等离子体熔融垃圾焚烧飞灰

为了评价垃圾焚烧飞灰的热等离子体熔融处理效果, 研究SiO2和CaO对重金属固化效果和重金属毒性浸出特性的影响. 在飞灰中添加一定比例的SiO2和CaO, 配置成不同的配灰样品, 利用纯氩热等离子体在1 400～1 500 ℃下, 对飞灰及配灰进行熔融玻璃化的实验研究, 分别利用X射线能量色散谱仪(EDX)、场发射扫描电子显微镜(FSEM)、X射线衍射仪(XRD)和毒性浸出方法(TCLP)分析飞灰和熔渣的化学组成、微观结构、晶相组成和重金属毒性浸出特性. 结果表明, 热等离子体熔融所得熔渣为无定形的玻璃体, 重金属浸出质量浓度均远低于毒性标准. SiO2和CaO的添加都可以改善重金属固化效果, CaO比SiO2对Cu、Zn、Cd和Pb挥发的抑制效果更好. SiO2的添加可以改善熔渣中重金属的浸出特性, 而CaO的作用与之相反.     

Effect of chemical admixtures on properties of high-calcium fly ash geopolymer

Owing to the high viscosity of sodium silicate solution, fly ash geopolymer has the problems of low workability and rapid setting time. Therefore, the effect of chemical admixtures on the properties of fly ash geopolymer was studied to overcome the rapid set of the geo-polymer in this paper. High-calcium fly ash and alkaline solution were used as starting materials to synthesize the geopolymer. Calcium chloride, calcium sulfate, sodium sulfate, and sucrose at dosages of 1wt% and 2wt% of fly ash were selecte...     

从粉煤灰中浸出锂的工艺研究

研究了从粉煤灰中浸出锂的工艺条件、粉煤灰粒径、碳酸钠溶液浓度、用量,浸出温度对锂浸出率的影响。结果表明,粉煤灰先研磨至细颗粒再水磨成糊状,用50 g/L碳酸钠溶液在140℃下浸出2 h,控制液固质量比100∶1,锂浸出率最高可达70%。     

炉排垃圾焚烧飞灰二级逆流水洗特性

以炉排垃圾焚烧炉飞灰为研究对象，分析水洗液固比和时间对飞灰中氯盐溶出的影响，对二级逆流水洗工艺展开研究. 通过模拟飞灰的二级逆流水洗工艺，建立水洗所产生废液中的氯质量浓度、残渣中氯质量分数的理论计算模型. 结果表明，当水洗液固比为6 mL/g、水洗时间约为20 min时，氯盐溶出质量达到稳定；飞灰经一级、二级水洗后的质量损失分别约为32%、37%；在相同液固比下,与一级水洗相比，二级逆流水洗可以提升飞灰的脱氯效果，当水洗液固比为2~6 mL/g时，提升率可达15.40%~61.15%；模型所得的理论计算值与实验实测值相关性好、均方根误差小. 2种水洗工艺产生的水洗废液中COD、氨氮质量浓度和pH值均高于《污水排入城镇下水道水质标准》的规定，在被排入城市污水系统之前须经过进一步处理.     

陶粒赤泥粉煤灰免烧砖性能研究

基于国家节能环保的要求,以山东信发铝电集团的废弃物赤泥、粉煤灰为主要原料,用石灰、水泥作为激化剂,经压砖机压制成型,自然养护来生产赤泥陶粒粉煤灰免烧免蒸压砖.为了使其工业化生产并能代替粘土砖,对原材料配比和生产工艺进行了定量分析,得出了合理的试验配方和生产工艺参数,探讨了原材料配比和生产工艺参数对砖制品性能的影响.结果表明:(1)当25％赤泥、18％粉煤灰、45％陶粒、12％水泥时,砖制品的强度最高.(2)当18％赤泥,21％粉煤灰,50％陶粒和11％水泥时,强度满足要求,保温性能大大提高,吸水率、冻融性和放射性等各方面物理特性符合要求.     

低浓度含氟废水的粉煤灰综合处理

处理低浓度含氟废水以达到排放要求,试验利用粉煤灰直接除去废水中的氟离子,分别考察了pH值、粉煤灰用量和处理时间对氟去除率的影响,获得了合适的工艺条件.但单独采用粉煤灰直接处理的结果达不到排放标准,另又做了如下复合改进:先用电石渣预处理,后配合使用A型混凝剂进一步处理.考察了不同电石渣用量、搅拌时间、不同A型混凝剂用量和混凝沉降时间对氟去除率的影响,得出了适宜的工艺条件能使含氟为70 mg/L的原始废水(原水)经两级除氟后,氟除去率达97%,达到了良好的效果.     

水胶比和粉煤灰对砼层面砂浆抗折抗压强度影响

通过实验对比分析了在相同水胶比下,粉煤灰掺量对层面处理砂浆抗压、抗折强度的影响,以及在相同粉煤灰掺量下,不同水胶比对层面处理砂浆的抗压、抗折强度的影响。通过对实验数据进行分析,得出了不同水胶比、不同粉煤灰掺量对碾压混凝土坝层面处理砂浆抗折和抗压强度的影响规律。     

粉煤灰处理含铜废水的正交实验研究

利用粉煤灰处理的含铜废水,初步研究粉煤灰对Cu2+的吸附机理,通过试验分析不同浓度、不同pH值、不同的振荡时间、不同的粉煤灰加入量对吸附的影响,并设计正交试验寻找最佳工艺参数。     

搅拌时间对粉煤灰水泥净浆流动性及早期抗压强度的影响

影响粉煤灰水泥净浆的流动性与早期抗压强度等问题一个重要原因就是拌合是否充分,搅拌时间是否合适。现有的相关规范中对于拌合时间的规定大都针对普通混凝土,随着高性能混凝土的发展,尤其是粉煤灰混凝土近几年来的广泛使用,导致现有的拌合时间规定无法满足粉煤灰混凝土均匀性的控制要求。为此,通过初步研究不同拌合时间对不同掺量的粉煤灰水泥净浆流动性及早期抗压强度的影响,最终确定合理的粉煤灰水泥净浆拌合时间,供进一步研究与工程应用参考。     

粉煤灰去除水中活性紫KN—B

以稀盐酸对燃煤电厂粉煤灰进行活化，实验了粉煤灰和活化粉煤灰对水中染料活性紫KN—B的吸附脱色效果．实验结果表明：粉煤灰经活化后对染料的吸附能力明显增强．活化粉煤灰对染料活性紫KN—B具有明显的脱色效果．在足量投加量下，废水脱色率可达99％以上；最佳pH值范围为2～8，最佳反应时间为15min．粉煤灰和活化粉煤灰对水中活性紫KN—B的吸附符合Langmuir吸附等温方程．活化粉煤灰用于实际印染工业废水处理，脱色率和COD去除率同样较高．     

粉煤灰去除水中活性紫KN-B

以稀盐酸对燃煤电厂粉煤灰进行活化,实验了粉煤灰和活化粉煤灰对水中染料活性紫KN B的吸附脱色效果．实验结果表明：粉煤灰经活化后对染料的吸附能力明显增强．活化粉煤灰对染料活性紫KN B具有明显的脱色效果．在足量投加量下,废水脱色率可达99%以上;最佳pH值范围为2～8,最佳反应时间为15?min．粉煤灰和活化粉煤灰对水中活性紫KN B的吸附符合Langmuir吸附等温方程．活化粉煤灰用于实际印染工业废水处理,脱色率和COD去除率同样较高     

逆向涡流等离子体降解飞灰中二恶英的研究

利用氮气逆向涡流非平衡等离子体反应器,进行医疗垃圾焚烧飞灰中二恶英的降解.考察氮气逆向涡流非平衡等离子体放电特性,从而获得反应器稳定的工作条件.在实验过程中分别测量处理后飞灰中和尾气中的二恶英质量分数,分析利用氮气逆向涡流非平衡等离子体反应器降解飞灰中二恶英的效果,初步探索二恶英的降解机理.结果表明,切向进气体积流量是影响放电电弧特性的关键因素,增大切向进气体积流量,可以提高电弧放电的稳定性;逆向涡流等离子体对飞灰中二恶英有明确的降解作用,单位质量飞灰中PCDD/Fs总质量的平均降解率为49.6%,总毒性当量I-TEQ平均降解率为62.3%,飞灰中PCDFs比PCDDs更容易降解.     

Impact properties of engineered cementitious composites with high volume fly ash using SHPB test

The split Hopkinson pressure bar (SHPB) testing with diameter 40 mm was used to investigate the dynamic mechanical properties of engineered cementitious composites (ECCs) with different fly ash content. The basic properties including deformation, energy absorption capacity, strain-stress relationship and failure patterns were discussed. The ECCs showed strain-rate dependency and kept better plastic flow during impact process compared with reactive powder concrete (RPC) and concrete, but the critical compressive strength was lower than that of RPC and concrete. The bridging effect of PVA fiber and addition of fly ash can significantly improve the deformation and energy absorption capacities of ECCs. With the increase of fly ash content in ECCs, the static and dynamic compressive strength lowered and the dynamic increase factor enhanced. Therefore, to meet different engineering needs, the content of fly ash can be an important index to control the static and dynamic mechanical properties of ECCs.     

免烧粉煤灰滤料的制备及其性能的研究

为了扩大粉煤灰的应用范围,减少其对环境的污染,并且寻求一种新的水处理滤料的配方与制备方法,以粉煤灰、粘土为主要原料,以生石灰、石膏、水泥为激发剂,以H2O2(双氧水)、NaHCO3为发泡剂,经搅拌、成型、自然冷却等工艺在实验室制备了免烧粉煤灰滤料.结果表明,如果以孔隙率作为主要的性能评价指标,制备免烧粉煤灰滤料的最佳质量配比为:粉煤灰46.30%,粘土13.89%,生石灰18.52%,水泥13.89%,石膏1.85%,纯H2O25.55%,此时所制滤料的孔隙率为72.24%.     

Effect of fly ash on TSA resistance of cement-based material

Thaumasite form of sulfate attack(TSA)is a major concern in evaluating durability of concrete structures subjected to sulfate and carbonate ions.By means of Fourier transform infrared spectroscopy (FT-IR),X-ray diffraction(XRD),scanning electron microscopy(SEM),and energy dispersive spectrum(EDS) as well as Raman spectra of erosion substances,effect of fly ash on TSA resistance of Portland cement-based material were investigated.Immersed in magnesium sulfate solution with 33 800 ppm mass concentration of SO...     

增钙灰对增钙灰-水泥混凝土体积安定性的影响

增钙灰是发电厂采用立式旋风炉并添加石灰作为助熔剂时产生的副产品，它与普通粉煤灰在诸多方面存在差异，尤其是f-CaO的含量较高，造成了混凝土的体积安定性不良，从而限制了增钙灰在混凝土中的应用。对增钙灰的体积安定性问题进行了实验研究，提出在保证体积安定性合格的前提下增钙灰的混凝土中的极限掺量。     

Physicochemical properties and heavy metals leachability of fly ash from coal-fired power plant

The physicochemical properties of fly ash from two kinds of coal-fired power plants were studied. Three aspects were examined: the micro-morphology, the mineral composition and the content of heavy metals. The results show that the fly ash from plants using a circulating fluidized bed are more irregular particles, while the particles from the plants using a pulverized coal-fired boiler are mainly spherical in shape. Quartz and mullite are the main crystalline phases in the ash. Clearly, both the technology and the coal used by a power plant can influence the mineral composition of the ash. The mineral composition of fly ash from a circulating fluidized bed is more complex than that from a pulverized coal-fired boiler. The quantity of elements found in the fly ash is greater than that found in the bottom ash for the same plant. Heavy metals are likely to be enriched in the fly ash. Heavy metal leachability was studied using two leaching methods. The results indicate that most of the heavy metals that leached during either batch leaching or column leaching experiments did not exceed the related maximum concentration standards. But Ni concentrations in the leachates from both batch and column tests exceed the standard. The highest excess rates in both tests were 572% and 497%, which levels might threaten the environment.     

改性粉煤灰去除城市景观水中磷的试验研究

利用硫酸改性的粉煤灰对模拟城市景观水体中磷的吸附特性进行了试验,并获得了相应的技术参数,在此基础上对实际城市景观水体进行了除磷试验研究.结果表明:改性粉煤灰在5min之内可基本达到磷吸附平衡,吸附反应符合Langmuir方程,相关系数:0.998,最大吸附容量达到9.19 mg/g.搅拌强度G值大于49.7s-1、pH值分别为6 和12 左右时具有良好的吸附效果;磷浓度分别为1 mg/L、0.2 mg/L、0.04 mg/L的模拟景观水体,相应改性粉煤灰投加量分别为670 mg/L、220 mg/L和100 mg/L时,出水磷浓度≤0.02 mg/L;当投加量分别提高到1 000 mg/L、250 mg/L和125 mg/L时,三种水体的出水磷浓度都检测不出.对实际城市景观水体除磷试验表明,总磷(TP) 为0.254 3 mg/L、可溶性磷酸盐(DP) 为0.026 3 mg/L和TP 为0.112 2 mg/L、DP 为0.016 3 mg/L 的两种景观水体粉煤灰投加量为250 mg/L时,具有较好的除磷效果,出水TP和DP分别降到了0.02 mg/L和0.01 mg/L的水平,且出水pH值均呈中性.     

利用高钙粉煤灰做软粘土固化剂

通过室内试验和微观分析，从材性的角度说明用高钙为煤灰做软粘土的固化剂是一种经济可行的办法，为软土地基的加固提供了一条新途径．