Effect of laser beam welding on fracture toughness of a Ti-6.5Al-2Zr-1Mo-1V alloy sheet

Investigation of fracture toughness on Ti-6.5Al-2Zr-1Mo-1V alloy thin sheet and its laser-welded joints has been carried out. In the test compact tension (CT) specimens and single specimen technology were used. In addition, hardness distribution and microstructure of the welded joints were examined. Fracture test indicates that brittle unstable fracture occurs after slow crack propagation for all the specimens, except that one heat affected zone (HAZ) specimen is brittle crack initiation. It is found that rolling directions have no obvious effect on fracture toughness of base metal. Moreover, fracture toughness of weld metal is obviously decreased in comparison with base metal whatever in as-welded condition or in stress relief condition. Post-weld heat treatment (PWHT) leads to fracture toughness of the welds further decreasing. Fractography observation shows that the fracture mode is predominantly dimpled in base metal. However, there exists intergranular fracture in the weld metal. Thus, the transition of fracture mode from both base metal and HAZ to weld metal may lead to dramatic decrease in fracture toughness. Microstructure examination reveals that the microstructure of weld metal consists of large grains with fine acicular structure. The formation of fine α acicular structure is due to rapid cooling during laser welding. After PWHT, the acicular structure is coarsened.     

Fracture toughness (J1C) of electron beam welded AA2219 alloy

AA2219 (Al–6%Cu) was butt welded in T87 temper (solution heat-treated, cold worked and precipitation hardened) and T6 temper (solution heat-treated and precipitation hardened) using electron beam welding (EBW). Variables studied were base metal temper condition and mode of EBW. Mechanical properties of the weld joint and fracture toughness at fusion zone (FZ) and heat-affected zone (HAZ) were evaluated and compared with those of the base metal. Results showed that EB welds have higher joint efficiency and fracture toughness than that of gas tungsten arc welding (GTAW). Fracture toughness of T6 base metal was found to be higher than its T87 counterpart. When welded, FZ and HAZ in T87 showed higher fracture toughness than that of T6; HAZ was the toughest. Pulsed current (PC) EB weld showed marginal reduction in toughness compared to constant current (CC) weld. Toughness variation is analyzed with the help of tensile test, Charpy impact test and scanning electron microscopy (SEM) and transmission electron microscopy (TEM).     

基于断裂力学的高强度钢材梁柱节点受力性能分析

为了研究国产Q460C高强度结构钢材梁柱节点的断裂行为,该文基于断裂力学理论,计算了Q460C高强度钢材焊缝及热影响区材料的断裂韧性,并且采用三维有限元断裂模型,以I型裂纹尖端应力强度因子K_I和J积分为定量的评价指标,分析了焊缝及热影响区不同长度的裂纹对梁柱节点断裂韧性的需求。弹性分析表明,K_I沿梁翼缘宽度方向呈W形分布,最大值出现在翼缘中心,且与名义弯曲应力呈线性关系,而焊根裂纹的断裂韧性需求比热影响区裂纹更高。弹塑性分析表明,J_I最大值出现在翼缘的边缘,热影响区裂纹的断裂韧性需求比焊根裂纹更高。研究结果表明,Q460C高强度钢材梁柱节点的断裂由焊根裂纹控制,断裂承载力与梁全截面塑性承载力相近,临界转角小于0.02rad,因此建议通过改善焊接工艺或局部构造来保证节点拥有足够的转动能力。     

Single Pass Laser-Arc Hybrid Welding of Maraging Steel Thick Sections

Maraging steel 250 grade plates of 10 mm thickness were welded in single pass using a laser-arc hybrid welding (LHW) setup comprising 3.5 kW CO₂ laser and synergic pulse metal inert gas (MIG) welding power source at a welding speed of 1 m/min. The influence of single-pass welding on the bead characteristics, microstructure, and mechanical properties was investigated. The size and volume fraction of reverted austenite was effectively reduced in the fusion zone. Moreover, the width of the heat-affected zones (HAZ) was reduced and the microhardness results did not show significant softening in the HAZ after post weld aging. Tensile testing of the welds in transverse direction showed 97.3% weld efficiency. The fusion zone exhibited K_Ic fracture toughness of 77.4 MPa√m which was affected by the distribution pattern of reverted austenite. The study vividly brings out the process advantages of LHW for accomplishing thick section welds of maraging steel in single pass with narrow groove and lesser filler wire consumption.     

Experimental investigation of local tensile and fracture resistance behaviour of dissimilar metal weld joint: SA508 Gr.3 Cl.1 and SA312 Type 304LN

The aim of the paper is to evaluate the local tensile and fracture toughness properties of the dissimilar metal weld joints between SA508Gr.3 Cl.1 and SA312 Type 304LN pipe. Weld joints have been prepared by manual gas tungsten arc welding (GTAW) process with conventional V‐groove and automatic hot wire gas tungsten arc welding with narrow gap using different filler wires/electrode such as Inconel 82/Inconel 182 and ER309L/ER308L. The tensile and fracture toughness test specimens have been machined from different regions of dissimilar metal weld such as heat affected zones, fusion lines, buttering layer, weld metal and both base metals. Tensile and fracture toughness tests have been carried out as per the ASTM standard E8 and E1820 respectively. Tensile and fracture toughness results of all the regions of dissimilar metal weld joints have been discussed in this paper. Metallurgical and fracture surface examinations have also been reported to substantiate the tensile and fracture toughness results. Need for the local properties for integrity assessment of the dissimilar metal weld joints has also been brought out.     

Effects of weld strength undermatch on fracture toughness of HAZ notched weldments in a HSLA steel

In the present work the effects of weld strength undermatch on fracture toughness of heat affected zone (HAZ) have been studied. In the investigation a high strength low alloyed steel (HSLA) with 800 MPa strength class was used, and the undermatched welded joints were made with two weld strength mismatch levels. Three-point bending test specimens with crack depth to specimen width ratio a/W ranging from 0.05 to 0.5 were extracted from the welded joints. The test results show that strength mismatching gives an obvious influence on the fracture toughness of coarse grained HAZ for the undermatched joints. The lower the weld strength mismatching, the higher the fracture toughness of the HAZ. In addition the tendency of fracture toughness change with crack depths is much the same as in previous studies on base metals or weld metals, that is, fracture toughness of the HAZ is increased with reduction of crack depths. From the measured results it shows that the macroscopically mechanical heterogeneity of the welds may have more important influence on the fracture toughness of the HAZ than the meso-heterogeneity in the reheated coarse grained HAZ. Furthermore, numerical verification indicates that the stress triaxiality at crack tip may be the essential reason for the change of fracture toughness of HAZ. It is also shown that the yield strength of HAZ determined by the limit load in the three-point bend test represents the combinative effects of HAZ and its surrounding materials. This revised version was published online in August 2006 with corrections to the Cover Date.     

Part-through fracture toughness (KIe) and crack-tip opening displacement (CTOD) of welded joints of AA2014-T6 at low temperatures

The part-through fracture toughness (K_Ie) and crack-tip opening displacement (CTOD, δ_m) of welded joints of aluminum alloy (AA) 20l4-T6, including the weld metal, the fusion zone (FZ), the heat-affected zone (HAZ), and the base material, were investigated at both liquid nitrogen temperature and liquid helium temperature with surface-crack tension (SCT) specimen and single-edge-notched bend (SENB) specimen respectively. Results indicate a conventional fusion welding process leads to formation of second-phase precipitations and inclusions, which cause significant reduction of fracture resistance at the weld metal and the FZ by fractographic analyses of fractured surface.     

Effects of crack size and weld metal mismatch on the has cleavage toughness of wide plates

The heat affect zone (HAZ) is in many cases considered to be the most critical part of a weldment. In this paper, the effect of crack size and weld metal mismatch on the HAZ cleavage toughness of wide plate specimens with X-groove has been investigated by the J-Q-M theories and a simple micromechanism for cleavage fracture. Two crack sizes have been studied (a/w = 0.1 and 0.3). In the analyses, the HAZ yield strength is assumed to be higher than the base metal. For each crack size, weld metal local overmatch and local evenmatch with respect to the HAZ are considered. For a given global strain, the results indicate that weld metal overmatch and evenmatch yield the same crack tip loading in terms of J-integral for a/w = 0.3. For a/w = 0.1, overmatch gives lower crack tip loading than evenmatch. For a given crack tip loading, weld metal local evenmatch in general results in less effective crack tip loading than the overmatch. Overmatch is detrimental to HAZ toughness, but this detrimental effect becomes less significant when the crack size decreases.     

Local mechanical properties of radial friction welded supermartensitic stainless steel pipes

In this work, supermartensitic stainless steel pipes were radial friction (RF) welded and their microstructures and local mechanical properties (hardness, fracture toughness and micro-tensile strength) were characterized in the as-welded condition. Defect-free RF welds were produced with a matching consumable ring (CR) under optimized welding conditions. The formation of a fine structure consisting of a mixture of virgin martensite and some stable austenite retained in the CR region was observed. On the other hand, the presence of virgin martensite plus δ-ferrite was found in the microstructures of the heat affected zone (HAZ) and thermo-mechanically affected zone (TMAZ). A ductile fracture was detected in the CR and weld interface regions at −40 °C. Moreover, both the CR and weld interface regions showed higher hardness and strength values than those of the base material (overmatching), without presenting significant losses in ductility and fracture toughness, which was attributed directly to the fine transformed microstructure of the weld region.     

Fracture toughness analysis of laser-beam-welded superalloys Inconel 718 and 625

In this study, two 3.2‐mm thick Ni‐base superalloys, Inconel 718 and 625, have been laser‐beam‐welded by a 6‐kW CO₂ laser and their room temperature fracture toughness properties have been investigated. Fracture toughness behaviour of the base metal (BM), fusion zone (FZ) and heat affected zone (HAZ) regions was determined in terms of crack tip opening displacement (CTOD) using compact tension‐type (C(T)) specimens. Laser‐beam‐weld regions showed no significant strength overmatching in both alloys. Ductile crack growth analysis (R‐curve) also showed that both materials exhibited similar behaviour. Compared to the BM there is a slight decrease in fracture toughness of the fusion and the HAZ.     

结构钢焊接匹配性研究进展

对结构钢焊接的高强匹配和低强匹配两种技术路线的发展进行了综述。在焊缝金属具有足够韧性的情况下,高强匹配能利用焊缝金属的高强度降低位于焊缝中裂纹的扩展驱动力、从而有利于焊接接头抗断性能的提高;随着结构钢强度的提高,焊接冷裂纹敏感性增大、焊缝韧性降低,采用焊接裂纹敏感性相对较低、焊缝金属塑韧性相对较高的低强匹配焊接技术能较好的控制焊接冷裂纹的产生并保证接头的抗断性能。     

Microstructure and Fracture Morphology in the Welding Zone of Cr18Mo2 Ferritic Stainless Steel

Microstructure, precipitates and fracture morphology in the weld metal and the heat-affected zone (HAZ) of Cr18Mo2 ferritic stainless steel have been studied by means of metalloscope, SEM,TEM and X-ray diffractometer. Experimental results indicate that crystalline grain coarsening in HAZ is one of the reason resulting in the embrittlement fracture in the welding zone of the ferritic stainless steel. Some precipitates (TiC, TiN and Cr2N) in the steel promote production and development of the brittle cracks. In practical applications. the welding heat input should be as small as possible to prevent embrittlement caused by HAZ grain coarsening.     

Microstructure and fracture mechanism of a flash butt welded 380CL steel

High strength low alloy (HSLA) steels have been widely used in the manufacture of wheel rim on account of the higher strength and larger elongation compared to the traditional low carbon steels. This experimental investigation was aimed to evaluate the microstructure and fracture mechanism of a flash butt welded 380CL steel by comparing the failed wheel rim and the survived wheel rim. The results showed that the continuous banded structure in the HAZ and the serious Widmanstatten ferrite in the weld were the major reasons for the failure of the wheel rim. The micro-hardness of two joints was similar in the overall profile. For the joint of the failed rim, the micro-hardness at the weld was the highest at 254 HV and the lowest micro-hardness value was in the HAZ. The high yield ratio of the failed wheel rim resulted in poor formability in the flaring process. The fracture mechanism of the failed rim was the mixture of ductile and brittle fracture modes. The crack initiation was the fusion zone of the weld having highest micro-hardness, then the cracking propagated along the weld metal to the middle of the wheel rim, a limited deviation was found in the terminal of the crack. The large ferrite grain in the HAZ was the main reason for the brittle–ductile transition.     

Pulsed MIG welding of AZ31B magnesium alloy

Abstract

Pulsed metal inert gas welding of AZ31B magnesium alloy is carried out, and continuous butt joints of high quality are obtained at optimised parameters. The effects of parameters on weld formation and welding stability are studied. The microstructure, mechanical properties and fracture of weld beads with different filler wires are investigated. The results show that it is a stable drop transition process with optimised parameters, which belongs to globular transfer. The precipitates in fusion zone and heat affected zone (HAZ) are uniform, dispersive and almost granular. The grain size in fusion zone is fine, and the grain size does not grow too large in HAZ compared with the base metal. The ultimate tensile strength of weld beads can be 94% of base metal, and the average elongation is 11%. Dimples and coarse tearing ridges can be observed on the fracture of the weld bead.     

BT20钛合金激光焊接接头的断裂韧性研究

对BT20钛合金及其激光焊接接头的断裂韧性进行了研究.同时分析了合金及激光焊接接头的硬度分布及显微组织.断裂实验表明,除了一个焊接接头紧凑拉伸(CT)试样是脆性启裂外,其它CT试样均在裂纹延性启裂并缓慢扩展后,发生脆性失稳断裂.母材的断裂韧性明显高于焊接接头,轧制方向对母材断裂韧性的影响不明显.焊接热影响区的断裂韧性介于母材和焊缝金属之间.本研究采用的焊后热处理没有改善焊接接头的断裂韧性,还有进一步恶化的趋势.添加活性剂对焊缝金属的断裂韧性没有明显作用,但对延性裂纹扩展长度有所改善.     

Microstructure-fracture toughness correlation in weld joints of Cr-Mo steel

The strength-toughness-microstructure relationship in relation to the micromechanics of a fracture process has been investigated in the weld joints of two alloys: 0.5 Mo and 2.25 Cr-1 Mo steels. These alloys are extensively used to fabricate super-heater tubes, boilers, piping, gas lines, etc., by welding. The applications require high temperature and pressure to be maintained during service. The crack initiation toughness and tearing resistance were evaluated using crack tip opening displacement/J-integral parameters at different temperatures. Quantitative analysis of micro-structure and fracture surfaces was used to study the micromechanics of fracture process in the heat-affected zone (HAZ) of the alloys. Molybdenum steel exhibited a higher percentage of ferrite and lower martensite content, while the other steel showed aligned carbide as the major constituent. The higher hardness and strength values in the HAZ and welding zone (WZ) of Cr-Mo steel, compared to molybdenum steel, may be attributed to the higher amount of martensite phase in the alloy. The higher initiation toughness at 200° C in both the alloys was reflected in the larger dimple size, compared to the size observed at room temperature. A tendency for void sheet formation was noticed in both alloys. Acicular ferrite and martensite appeared to be the most influential constituents affecting tearing resistance and initiation toughness.     

The effects of functionally graded material structure on wear resistance and toughness of repaired weldments

To perform a long lasting, crack-free repair welding on ultrahigh strength steels, the filler metal must be chosen and applied properly. Avoiding several short-term repairs or replacements, the repaired weldment should reveal comparative characteristics such as wear resistance, toughness and hardness to base metal. In the present study, a novel functionally graded material have been introduced to obtain enhanced wear resistance and hardness at surface as well as improved fracture toughness at fusion line of repaired weldments. A comparative study of wear resistance of repaired weld metals has been carried out by pin-on-disk apparatus at 5 N normal load and 0.14 ms⁻¹ sliding speed. Fracture toughness of weld metal was also evaluated by charpy absorbed fracture energy tests and scanning electron microscopy fractograghs. The results show that by employing functionally graded layers, toughness was enhanced significantly while retaining the surface wear resistance.     

铝合金厚板静止轴肩搅拌摩擦焊接头组织及性能

采用8.5 mm厚度2A14-T4铝合金和自主研制搅拌工具进行静止轴肩搅拌摩擦焊（stationary shoulder friction stir welding,SSFSW）实验,探讨焊接工艺参数对接头组织和力学性能的影响规律。结果表明：只有在低转速工艺参数范围内（转速ω=400~600 r/min与焊接速率v=60~120 mm/min）可获得焊缝表面光滑、无缺陷厚板铝合金SSFSW焊接接头。SSFSW焊缝区主要由焊核区（NZ）组成,周围热力影响区（TMAZ）及热影响区（HAZ）宽度明显减小,焊核区与搅拌针形状类似且由两种不同尺寸细小等轴晶构成,前进侧NZ晶粒比后退侧NZ更为细小。接头显微硬度呈"W"状分布,NZ硬度值可达到母材硬度80%~90%,TMAZ与HAZ交界处存在软化区,硬度最低为母材硬度72%左右。在给定ω=500 r/min,v=140 mm/min焊接参数下,SSFSW接头抗拉强度可达到母材的88%,断裂位置多位于后退侧TMAZ与HAZ交界处软化区,具有韧性断裂特征。     

X65管线钢管闪光对焊工艺参数对焊接接头力学性能和缺陷的影响

利用正交试验法,研究了焊接工艺参数对X65管线钢管闪光对焊焊接接头力学性能的影响。正交试验中选择激发闪光阶段烧化量、稳定闪光阶段烧化量、稳定闪光阶段焊接电流、加速闪光阶段闪光速度作为试验因素,焊接接头抗拉强度、塑性和低温冲击韧性作为焊接工艺的评价指标,得到了最优的焊接工艺参数。接头的金相分析表明,焊接的高热输入使接头焊缝区和部分热影响区的晶粒粗化,形成魏氏组织,降低了接头的冲击韧性。刻槽锤断试验表明,灰斑缺陷内部和边缘的密集裂纹导致接头脆性解理断裂。加速闪光阶段优化的闪光速度有利于减少焊缝区内的缺陷并提高接头的力学性能。     

X90钢级管线钢预精焊接头的性能研究

为综合研究X90管线钢的焊接性,选用国内某钢厂轧制的X90管线钢卷板,利用预精焊工艺制备试验钢管4根,采用金相分析、扫描电镜(SEM)断口分析、夏比V型缺口冲击试验、拉伸、弯曲、硬度等试验,研究了焊接接头各个区域的组织和性能.试验结果表明:内外焊缝区组织均为针状铁素体,热影响区(HAZ)粗晶区晶粒粗化严重,主要组织为粒状贝氏体和贝氏体铁素体,在原奥氏体晶界和贝氏体板条内部存在块状或条状的(马氏体-奥氏体)M-A组元;HAZ冲击功离散性较大,出现了单值较低(45 J)的试样,SEM断口分析呈现典型的解理断裂特征;焊接接头抗拉强度805~815 MPa,断裂位置均在HAZ;焊接接头反弯试样易在HAZ出现裂纹和脆断现象;HAZ硬度在220~250 HV之间,较母材下降30 HV左右.HAZ是X90预精焊钢管焊接接头的薄弱环节,为提高X90管线钢的焊接稳定性,应重点研究精焊内外热循环双热影响亚区的组织转变和脆化机理.