合金元素对奥氏体热模具钢时效硬化及力学性能的影响

本文对Fe-Ni-Mn-Cr奥氏体热模具钢的时效硬化特性及力学性能进行了探讨。结果表明:在钢中加入少量的铌元素后,在相同的热处理工艺条件下,将使试验钢的最大时效硬度值减小。增加钢中Mn/Ni比可以提高最大时效硬度值,但使试验钢的室温和高温塑性下降     

时效工艺对Fe-Mn-Si-Cr-Ni系合金形状记忆效应的研究

分别对两种成分的Fe-Mn-Si-Cr-Ni系合金进行不同工艺的时效处理，通过金相观察、电镜分析、硬度和形状记忆回复率的测试表明，由于时效沉淀相的析出，强化了奥氏体基体，即使不通过热机械训练，也可获得较明显的形状记忆效应。加入少量Nb和C的合金提高形状记忆效应更为明显。     

2014合金的回归再时效

本文采用拉伸实验和透射电镜法,研究了2014铝合金的回归再时效(RRA)处理.结果表明:采用欠时效(100℃(2×2h)与适当回归处理(200×5min)配合的RRA处理,可同时提高2014合金的强度和塑性.适当的回归处理能使欠时效2014合金组织中部分GP区优先长大.随后再进行峰时效处理,不仅能改善晶界析出相的尺寸和分布,而且还能使基体析出相尺寸产生明显的差异.这种尺寸有明显差异的基体析出相协同强化有利于提高2014合金的强韧性.     

Al,Nb含量对GH706合金长期时效组织及持久性能的影响

铝和铌含量的改变对GH706合金组织及持久性能影响的研究结果表明,将Al的质量分数升高至1.25%,而Nb的质量分数降低至2.0%,抑制了合金晶内强化相γ″-Ni3Nb相的析出,促进了γ′-Ni3Al相的析出,同时阻止了晶界η-Ni3(Ti,Nb)相形成.在650℃长期时效后,降Nb提Al后晶内γ″-Ni3Nb相长大及η相的析出受到抑制,合金组织具有更高的稳定性,合金持久寿命的降低幅度远低于原型合金.     

Al-Mg-Si-Mn合金时效性能及析出行为研究

采用透射电镜、差示扫描量热分析和硬度测试等方法,研究了Al-Mg-Si-Mn合金的时效性能及析出行为。结果表明,实验合金在170℃时效8h达到硬度峰值,并在一段时间内能保持较高硬度,57h后硬度开始迅速下降;主要强化相β″可长时间从基体中析出,当合金中大量析出β′相和B′相时,硬度明显降低。实验合金的析出相析出顺序为,过饱和固溶体→团簇→GP区→β″相→β′相+B′相→β相。     

GH169高温合金长期时效的组织转变

对GH169合金长期时效的组织结构观察表明,合金在650℃以下时效甚至长达5×10⁴h,其组织变化并不明显,保持了良好的组织稳定性。然而超过650℃,合金的组织对温度极为敏感,发生了复杂的相转变。通过对运行2.8×10⁴h的涡轮盘榫齿的研究表明,应力加速诱发这种复杂的相变过程。     

预变形对Al-Cu-Li-(Mg-Ag)合金时效析出行为的影响

通过采用维氏硬度测试、透射电子显微镜(TEM)、差示扫描量热法(DSC)等手段研究了预变形对Al-Cu-Li及Al-Cu-Li-Mg-Ag两种合金时效析出行为的影响。结果表明：在Al-Cu-Li合金中,峰时效后θ’相的析出占据主导,并且通过预变形引入位错有利于Al-Cu-Li合金时效后θ’相的析出,而对T₁相几乎没有促进作用;添加微量Mg、Ag元素后,Al-Cu-Li-(Mg-Ag)合金峰时效后的析出相转变为T₁相并占据主导,θ’相较少;Al-Cu-Li-(Mg-Ag)合金经预变形时效后T₁相和θ’相的数量密度均有所增加,即预变形同时促进了T₁相和θ’相的析出;在ε=0～3%预变形范围内,T₁相的数量密度随着预变形量的增加而增大,并且T₁相的尺寸也变得更加细小和均匀,进而使合金获得更优异的性能。     

合金元素Ni对Fe-Cu合金析出过程的影响

以添加Ni前后的Fe-Cu合金和Fe-Cu-Ni合金为研究对象,采用金相显微镜(OM)观察了Fe-Cu合金与Fe-Cu-Ni合金时效过程中的显微组织形貌变化,借助硬度测试分析了两种合金在等温时效过程中的硬度变化规律,并利用透射电子显微技术(TEM)进行了两种合金的析出相精细结构观察与衍射分析,在此基础上,通过实验与理论...     

预变形Mg-Nd合金时效析出行为的原子尺度

使用球差校正的高角环形暗场扫描透射电镜(HAADF-STEM)系统研究了预变形Mg-2.0%Nd(质量分数)合金250℃等温时效2 h后的时效析出行为.结果表明,预变形产生的位错促进了第二相的形核,导致高密度且有别于传统沿■惯习面均匀分布的亚稳析出相的形成.原子尺度的表征结果表明,合金内部形成的析出链主要由β_S′相和β₁相组成.此外,析出链中还含有少量的β″和β_H′相,以及β_L′相.这些片状或透镜状的β_S′和β₁相与α-Mg基体完全共格,且均具有一个■的惯习面,但沿■3个方向非均匀分布.这些结果有望为形变调控合金的析出行为,提升合金力学性能提供理论指导.     

高Co—Ni二次硬化马氏体钢中合金元素对相变的影响

利用“固体与分子经验电子理论”（ＥＥＴ）分析了高Ｃｏ－Ｎｉ二次硬化马氏体钢中几种主要合金元素在不同状态下的价电子结构，认为Ｃｏ、Ｎｉ在奥氏体中与Ｃ相互作用较强，它们能降低Ｃ的扩散能力，推迟马氏体相变。在马氏体回火过程中，Ｃｏ 和Ｎｉ溶入渗碳体形成的合金渗碳体，在较高的温度下分解，使固溶于基体中的Ｍｏ 与位错充分结合。在渗碳体分解后，Ｍｏ 与Ｃ形成富Ｃ、Ｍｏ的溶质簇，或以Ｍ２Ｃ的形式析出，在基体内弥散分布，形成二次硬化。     

时效处理对变形镁合金延伸率的影响

对ZK60镁合金进行不同工艺的时效处理,分析时效工艺对组织和硬度的影响,同时研究了时效前后的延伸率变化。结果表明：时效处理后,随时效时间的延长和温度的升高,合金组织出现晶粒长大,强化相的扩散,溶解;在120℃,12h处理后,硬度提高43．44％,延伸率达到24．87％。     

塑料模具用NAK80钢时效硬化工艺研究

通过对NAK80钢进行模拟时效实验,研究了时效温度以及时效时间对该钢硬化的影响,并对其硬化机理进行了探讨。研究结果表明,当时效温度为520℃、保温3 h以上时,硬化效果最佳。     

Zn及Ni元素对喷射成形铝合金组织特征和时效行为的影响

Microstructure and aging behavior of spayformed Al-Zn-Mg-Cu alloys were investigated as a func.tion of alloying element addition. It reveals that the grains of the as-deposited alloys are refined with increasing Zn element, while the function of the Ni addition is to reduce grain boundary particles and eutectic in the as-extruded condition. Particles containing Mg and Zn are found to be increased with Zn content increasing, while the role of Ni is to reduce both number and size of these particles. During artificial aging, the increment of Zn content produces not much effect on peak hardness, in addition to an accelerated overage softening. An addition of about 0.13% Ni,however, gives rise to not only an improved peak hardness but also an improvement of property stability at the aging temperature.     

Effect of Sinter Hardening on Microstructure and Mechanical Properties of Astaloy 85Mo

 Effect of sinter hardening on the microstructure, density, hardness and tensile properties of Astaloy 85Mo+0.7% graphite was investigated. For this purpose, Astaloy 85Mo, a pre-alloyed powder, was mixed with 0.7% UF4 graphite and then pressed in single action die and sintered at 1120 ℃ for 30 min in N2-10%H2 atmosphere. Then samples were cooled from 0.5 to 3 ℃/s sintering temperature in accordance with different cooling rates. The difference in microstructure, hardness, density and tensile properties of the samples associated with different cooling rates from sintering temperature has been investigated. The results show that the microstructure remains bainitic by changing cooling rate, but it becomes finer and then the hardness and tensile strength of the samples will increase by increasing the cooling rate from sintering temperature.     

自然时效对7N01铝合金组织和性能的影响

通过电导率、力学性能测试和高分辨电镜分析研究了自然时效对7N01合金组织和性能的影响。结果表明:在自然时效中,由于过饱和固溶体不均匀析出与基体共格的析出相,合金电导率随着自然时效时间的延长逐渐降低,时效20 d后基本达到稳定状态。合金的强度随着时效时间的延长逐渐增大,在20 d后达到稳定,抗拉强度在400 MP以上,屈服强度在260 MPa以上,合金的延伸率在自然时效1 d后达到稳定值(约为15.5%)。稳定态合金的强化相主要为尺寸较小的GPⅡ区。此外,弯折试验表明合金具有良好的弯折性能,在自然时效10～60 d内未出现肉眼可见的裂纹。     

Effect of Continuous Annealing on Microstructure and Bake Hardening Behavior of Low Carbon Steel

The influences of the heating rate,annealing temperature and soaking time during continuous annealing on the microstructure evolution and bake hardening behavior of the low carbon steel were investigated.After 2% prestraining,bake treatment(180 ℃×20 min)was carried out to measure BH(bake hardening)values.The results showed that,with the increase of the annealing temperature,the grain size increased except for annealing in the intercritical region.Furthermore,the BH value increased and the mean grain size reduced with increasing the heating rate from 5to 80 ℃/s.The BH value was very low before complete recrystallization.After a significant decrease from 630 to 720 ℃,the BH value enhanced when the steel was annealed at 750℃.With the increase of the soaking time from 20 to 100s,the BH value reduced linearly due to the segregation of solute C atoms.     

微量元素对Mg-Al-Zn系合金铸态组织及性能的影响

综述了Mg-Al-Zn系合金的化学成分，几种合金元素在镁合金中的作用及添加微量合金元素对Mg-Al-Zn系镁合金铸态显微组织及性能的影响。     

Effect of Manganese on As-Cast Microstructure and Hardening Behavior of High Chromium White Cast Iron

Highchromiumwhitecastironhasbeenusedaswear resistantmaterialsintheminingandmaterialin dustryduetotheirexcellentabrasionresistanceforhardeutecticcarbidesinthemicrostructure[1- 3] .Highchromiumwhitecastironiscommonlyusedafterheattreatment .Thealloyelementsw…     

长期时效对GH4199合金组织和性能的影响

采用金相和电镜微观组织观察、室温和高温拉伸试验、物理化学相分析等综合试验方法,对经600、700、800、900℃和100、200、500、1 000 h长期时效处理的GH4199合金进行测试和研究.结果表明,GH4199合金经长期时效后,其室温和高温力学性能仍保持在较高水平;合金的组织稳定性良好,析出相主要为γ'相和碳化物.据相分析结果可知,在700～900℃时效1 000 h左右,合金组织中存在极微量的脆性(TCP)相--μ相和σ相,它们对合金的力学性能基本无影响,组织中虽然存在微量TCP相,但合金的室温和高温塑性不发生"脆化".