纺织品无氟溶胶-凝胶法拒水整理

利用正硅酸四乙酯及长链烷烃硅氧烷,采用溶胶-凝胶法及自组装方式对棉和涤纶织物进行拒水整理,通过先浸轧二氧化硅溶胶、再浸渍烷烃硅氧烷的方式赋予织物拒水性能.考察了烷烃硅氧烷结构和浓度及皂洗次数对接触角的影响,并利用扫描电子显微镜对二氧化硅溶胶整理前后棉和涤纶织物的表面形态进行比较.结果表明:以不同碳链长度的硅氧烷对经溶胶整理后的织物进行整理,均能提高拒水性能.随着碳链长度的增加,接触角增大;随着水解硅氧烷浓度的增加.拒水性能也得到提高.整理后的棉织物经30次皂洗后,与水的接触角为95°,涤纶织物为110°,仍保持一定拒水性能.性能测试表明整理前后织物的物理机械性能变化较小.     

棉织物溶胶-凝胶法的无氟拒水整理研究

以接触角作为评价依据，研究了纯棉织物经不同改性二氧化硅溶胶处理纯棉织物后的拒水性能。讨论了改性剂结构、浓度、处理物表面粗糙程度及洗涤次数对接触角的影响。试验表明，整理棉织物的拒水性随溶胶中烷基硅烷添加剂浓度和烷基链长度的增加而提高；改性溶胶处理后，织物的拉伸强力减小，而白度和透湿量变化不大。     

涤棉混纺织物纳米无氟拒水整理

采用纳米无氟拒水剂NT-X018对涤棉混纺织物进行整理,以提高其拒水性能。探讨整理液配方、工艺过程对整理后织物拒水性能、断裂强力、透气性、耐久性及手感的影响。结果表明:整理液配方为,拒水剂NT-X018 80g/L、加强剂NT-X628 30g/L、交联剂NT-504M5g/L、催化剂NT-S228 5g/L、渗透剂OS-603 1.0g/L,浴比1∶30,pH4.0左右;采用二浸二轧,预烘条件130℃×2min,焙烘条件160℃×1min,可以达到最佳的拒水整理效果,同时,整理后织物手感基本没有影响,经多次洗涤,拒水等级仍较高,说明该拒水剂的耐久性良好。     

溶胶-凝胶法在织物功能整理中的应用

采用溶胶-凝胶技术,用0.37mol/LTiO2水溶胶处理后的纯棉织物的紫外线(297nm)透过率仅为0.8%,水洗牢度较好,具有一定的拒水作用,耐水压值达193.1Pa,淋水级数50分.与带有环氧基的硅氧烷水溶胶混合使用,能使直接染料皂洗的沾色牢度提高1~2级.     

溶胶-凝胶法对织物的功能整理

采用溶胶-凝胶技术,用TiO2水溶胶处理纯棉织物,可以赋予织物多重整理效果.如:具有较好的屏蔽紫外线的作用,用037 mol/L TiO2水溶胶处理过的织物在297 nm处的紫外线透过率仅为0.8%,且水洗牢度较稳定;处理过的织物同时还具有一定的拒水作用,耐水压值能达到19.7 cm水柱,淋水级数50分;与带有环氧基的硅氧烷水溶胶混合使用能使直接染料染色的皂洗的白布沾色牢度提高1～2级.目前存在的问题是:处理后的织物撕破强力损失较大.     

涤纶织物氧化铝溶胶抗静电整理研究

通过用有机醇铝水解的溶胶-凝胶法制备出稳定、均一、透明的氧化铝溶胶,将其配制成抗静电整理剂,通过轧-烘-焙工艺,应用于涤纶织物抗静电整理并分析了工艺条件对整理效果的影响。实验结果表明:整理剂10 g/L,焙烘温度160℃、时间30 s,织物的峰值电压和半衰期由原先未经整理时的4192 V和大于90 s,下降为9 V和0.41 s,抗静电效果显著。     

涤纶织物的阻燃拒水同浴整理

采用一种水溶性好的高效环化磷酸酯类阻燃剂FR-CU,以浸轧工艺对涤纶织物进行阻燃整理。探讨FR-CU与不同防水剂同浴整理的可行性以及阻燃效果和拒水等级。结果表明,采用15%阻燃剂FR-CU和3%防水剂TG580同浴浸轧整理,加入氨水调节p H值至5.5~6.6,整理织物续燃和阴燃时间均为0,损毁长度120 mm,沾水和变色等级均为4级。     

光固化SiO_2溶胶在棉织物拒水整理中的应用

利用溶胶-凝胶技术,以正硅酸四乙酯、3-叠氮丙基三乙氧基硅烷为前驱体,氨水为催化剂制备光固化二氧化硅溶胶,以十六烷基三甲氧基硅烷为拒水剂对棉织物进行拒水整理.先浸轧光固化二氧化硅溶胶,再浸渍烷烃硅氧烷,无需焙烘,通过紫外光照直接赋予织物拒水性能.采用扫描电镜、X射线光电子能谱仪对整理后的棉织物进行测试.结果表明,光固化二氧化硅溶胶沉积在织物表面,提高了棉织物的粗糙度.接触角测试表明,棉织物对水接触角(5μL)达到155°;整理后的棉织物经30次皂洗后,与水的接触角仍大于135°.     

锦纶/棉混纺织物的耐久无氟拒水整理

为满足锦纶/棉混纺织物用于户外运动产品的特殊要求,采用无氟拒水剂CWR-9A对混纺织物进行拒水涂层处理,并选取黏合剂来进一步提高拒水剂与织物间的粘接牢度.探讨了拒水剂质量浓度、焙烘时间、焙烘温度、黏合剂种类、黏合剂与拒水剂体积比、洗涤次数等对混纺织物拒水效果的影响,得到锦纶/棉混纺织物拒水整理最佳工艺:CWR-9A质量...     

溶胶-凝胶法与固色整理

介绍了溶胶-凝胶法的发展概况、基本原理、影响因素等，以及在纺织上的应用情况，指出该方法有望用于纺织品的固色整理上，成为一种新型的环保的固色方法。     

精纺毛织物的无氟拒水整理

针对含氟拒水剂不环保的缺点,采用无氟拒水整理剂WS CONC.赋予毛织物拒水性能。讨论了拒水整理剂WS CONC.质量浓度、催化剂BC质量浓度、焙烘温度和焙烘时间对毛织物拒水性能的影响。利用水滴接触角方法观察了毛织物的拒水性能。结果表明,在带液率为70%的情况下,较佳的整理工艺为:无氟拒水整理剂WS CONC.质量浓度60 g/L,催化剂BC质量浓度60 g/L,在170℃焙烘70 s。整理后,毛织物的初始拒水等级可达100分,5次干洗后仍可达75分,毛织物的手感不够柔软,颜色轻微泛黄,强力增加。     

Reducing drag force on polyester fabric through superhydrophobic surface via nano-pretreatment and water repellent finishing

Energy saving is a very important factor for athletics that works in high speed and award winning competition. Drag force is of prime importance for determining the speed of objects that moves in the fluid. Nanotechnology is of great potential among the methods for reducing drag force. Enhancing the fabric speed in the fluids could be achieved using superhydrophobic surfaces to reduce the drag force. A simple and versatile method was utilized for the fabrication of superhydrophobic surfaces via pad-dry-cure and in situ synthesis of ZnO nanoparticles as a pre-treatment. The treated samples were examined by SEM for assessing the structure and size of nanoparticles and mapping and EDX analysis was carried out for further characterization. A novel method was designed based on the tensile tester apparatus for studying the changes in drag force. The results indicated a reduction of 80% in drag force of the treated fabric in the optimum conditions of pre-treatment with 10% zinc nitrate (Zn(NO₃)₂) and 5% sodium hydroxide (NaOH) at 130 °C for 1 h.     

棉织物的溶胶-凝胶法拒水整理研究

采用正硅酸乙酯(TEOS)为前躯体,乙醇为溶剂,盐酸为催化剂制备硅溶胶,并加入添加剂对棉织物进行改性;测试整理后织物的拒水性能,以及织物的手感、透气性、断裂强力和染色性能的变化.结果表明,溶胶拒水整理略降低织物的透气性和手感,而断裂强力有所提高;直接染料染色织物拒水整理后,色光略有变化,颜色加深,牢度基本不受影响.     

涤纶织物拒水拒油泡沫涂层工艺研究

采用泡沫整理方法对涤纶织物进行单面涂层,使其具有单面拒水拒油效果且不影响内层的吸湿透气性能.文章通过正交试验确定了拒水拒油泡沫涂层剂的最佳配比,并探讨了该涂层工艺的最佳焙烘温度和时间.实验表明:涤纶织物拒水拒油泡沫整理具有处理浓度低、用水量少、焙烘温度低、时间短等特点.最佳整理剂配方为防水防油剂与10%SDS溶液以2:1混合,并添加CMC 10 g/L,HEC 0.5 g/L,PTF 5 g/L,发泡搅拌时间2 min,焙烘温度160℃、时间2 min 的效果最佳.     

AKD在涤纶防水防油整理中的应用研究

基于烷基烯酮二聚体(AKD)乳液的防水性和柔软性,将AKD用于TG5601有机氟防水剂的增效作用。研究了所制备的AKD乳液的稳定性以及AKD乳液与TG5601乳液复合的整理效果,比较了水洗前后织物的防水性、防油性、接触角及撕破强度的变化。研究结果表明:AKD乳液能明显降低TG5601乳液的表面张力,提高TG5601的防水和防油整理效果和耐水洗性,而且织物的撕破强力也得到了明显提高。     

涤纶纬编装饰布阻燃、拒水整理染整加工

涤纶纬编装饰布经过阻燃、拒水整理后,被赋予耐久性的阻燃效果.20次室温洗涤后,阻燃效果无明显变化.其阻燃指标符合GB5455-85《纺织物阻燃性能测试垂直燃烧法》B1级标准要求.采用表面抗湿性测定方法AATCC22-1977喷射试验法检测,其拒水性能达到4级以上.较佳的助剂用量:阻燃剂尼普威DFR20%(owf),拒水剂KH10012g/L.     

涤棉织物泡沫拒水拒油整理

将泡沫技术应用到涤棉织物的拒水拒油整理加工过程中,使织物具有单面拒水拒油的效果,同时不影响织物内侧的吸湿透气性能。文章首先探讨了泡沫拒水拒油整理加工过程的影响参数,然后通过正交试验确定了泡沫拒水拒油整理的较佳工艺参数,为十二烷基硫酸钠3g/L,稳定剂（海藻酸钠与羧甲基纤维素钠1:1复配）2g/L,拨水拨油整理剂60 g/L,车速7m/min,发泡比11.4,焙烘条件为140℃×5min。最后分析对比了泡沫技术与传统浸轧法拒水拒油整理效果,发现经两种加工工艺整理的布样的拒水拒油性能相当,但是经由泡沫技术整理后织物的机械性能比常规工艺加工效果优良。