Bias effects on microstructure, mechanical properties and corrosion resistance of arc-evaporated CrTiAlN nanocomposite films on AISI 304 stainless steel

CrTiAlN films were deposited on AISI 304 stainless steel by cathodic arc evaporation under a systematic variation of the substrate bias voltage. The effects of substrate bias on the coating morphology and mechanical properties, such as structure, composition, adhesion, hardness and Young's modulus, were studied in details using field emission scanning electron microscopy, X-ray diffraction, electron probe microanalysis and indenter. Polarization test and immersion test were also carried out to evaluate the corrosion behavior of the various films. CrTiAlN films are nanocrystalline that exhibit a CrN/TiAlN multi-layered morphology. At the optimal value of substrate bias voltage (i.e., − 150 V), the CrTiAlN film showed an increased Cr content and improved properties, such as higher adhesion, higher hardness (38 ± 2 GPa), and greater Young's modulus (319 ± 16 GPa) vs. the films deposited at other substrate bias voltages. Moreover, the optimum film has better corrosion resistance in 3.5 wt.% NaCl and 20 vol.% HCl solutions.     

Effect of bias voltage on microstructure, mechanical and wear properties of Al-Si-N coatings deposited by cathodic arc evaporation

Al-Si-N coatings were deposited on tungsten carbide (WC-Co) and silicon wafer substrates using Cr and AlSi (12 at.% Si) alloy targets using a dual cathode source with short straight-duct filter in the cathode arc evaporation system. Al-Si-N coatings were synthesized under a constant flow of nitrogen, using various substrate bias voltages at a fixed AlSi cathode power. To enhance adhesive strength, the Cr/(Cr_xAl_ySi_z)N graduated layer between the top coating and the substrate was deposited as a buffer interlayer. The effects of bias voltage on the microstructure, mechanical and wear properties of the Al-Si-N films were investigated. Experimental results reveal that the Al-Si-N coatings exhibited a nanocomposite structure of nano-crystalline h-AlN, amorphous Si₃N₄ and a small amount of free Si and oxides. It was also observed that the deposition rate of as-deposited films gradually decreased from about 25.1 to 18.8 nm/min when the substrate bias was changed from − 30 to − 150 V. The XRD results revealed that h-AlN preferred orientation changed from (002) to (100) as the bias voltage increased. The maximum hardness of approximately 35 GPa was obtained at the bias voltage of −90 V. Moreover, the grain size was inversely proportional to the hardness of the film. Wear test results reveal that the Al-Si-N film had a lower coefficient of friction, between 0.5 and 0.7, than that 0.7 of the AlN film.     

Gradient CrCN cathodic arc PVD coatings

This work reports on the growth and properties of Cathodic Arc Physical Vapor Deposition of low friction-coefficient CrCN coatings, as deposited on the basis of complementary carbon/nitrogen gradient concentrations through the film thickness. The coatings developed in this study exhibited friction coefficients ranging from 0.2 to 0.6, against 100Cr6 bearing steel, depending on the preparation conditions. Gradient CrCN films with COF of 0.35 and comparable mechanical strength to that of CrN were achieved. The adhesion rate of metallic elements such as Fe during the sliding process of CrCN coated tools on AISI316L steels were monitored using a pin-on-disc experimental set-up. The results demonstrated a low tendency of the gradient CrCN deposited films to pick up material from the AISI316L steels surfaces, in contrast to that found when using standard CrN cathodic arc PVD films.     

Fracture failure analysis of AISI 304L stainless steel shaft

Fracture failure analysis of an agitator shaft in a large vessel is investigated in the present work. This analysis methodology focused on fracture surface examination and finite element method (FEM) simulation using Abaqus software for stress analysis. The results show that the steel shaft failed due to inadequate fillet radius size and more importantly marking defects originated during machining on the shaft. In addition, after visual investigation of the fracture surface, it is concluded that fracture occurred due to torsional–bending fatigue during operation.     

The thermal conductivity of AISI 304L stainless steel

A compilation and critical analysis of the thermal conductivity () of AISI 304 stainless steel (SS) between 100 and 1707 K has been given in the literature. The author represented his recommended values of by an inflection in the A versus temperature relationship between 300 and 500 K. Because a physical mechanism had not been identified that would produce such a temperature dependence in of 304 SS, interest was generated in the possible existence of an as yet undiscovered phenomenon that might cause such an inflection. Consequently, experimental verification of the inflection was sought. The present paper presents recent measurements of , the electrical resistivity, and the absolute Seebeck coefficient of 304L SS from 300 to 1000 K and of the thermal diffusivity () from 297 to 423 K. The values computed from the a measurements were within ± 1.6% of the directly measured An inflection was not observed in the temperature dependence of between 300 and 500 K. After careful evaluation and because a physical mechanism still has not been identified which would produce such an inflection, the authors conclude that the inflection in the vs T relationship reported in the literature was caused by the data analysis technique.     

Deposition of nano-scaled CrTiAlN multilayer coatings with different negative bias voltage on Mg alloy by unbalanced magnetron sputtering

In a magnetron sputtering system, the negative substrate bias voltage has been used as a basic process parameter to modify the deposition structure and properties of coatings. In this paper we report the effect of bias voltage ranging from −40 V to −90 V on nano-scaled CrN/TiN/CrN/AlN (CrTiAlN) multilayer coatings synthesized on a Mg alloy by a closed-field unbalanced magnetron sputtering ion plating system in a gas mixture of Ar + N₂. The technological temperature and atomic concentration in the multilayer coatings were controlled by adjusting the current density of different metal magnetron targets and the plasma optical emission monitor. The composition, crystallographic structure, deposition model and friction coefficient of multilayer coatings were characterized by X-ray photoelectron spectrometry (XPS), X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM) and ball-on-disc testing. The experimental results show that the deposition model and friction coefficient of nano-scaled CrTiAlN multilayer coatings were significantly affected by the negative bias voltage (V_b). The nitride species in multilayer coatings mainly involve CrN, AlN and TiN, and XRD analysis shows that the crystallographic structure was face-centered cubic. Under different bias voltage conditions, the multilayer coating composition shows a fluctuation, and the Al and Cr concentrations respond in the opposite sense to the bias voltage, attaining their greatest values at V_b = −70 V. The surface and cross-sectional morphology shows deposition model change from a columnar model into non-columnar model with the increase in negative bias voltage. The friction coefficient of the nano-scaled multilayer coatings at V_b = −55 V stabilize after 10 000 cycles.     

Friction stir welding of AISI 304 austenitic stainless steel

The objective of this work is to demonstrate the feasibility of friction stir welding (FSW) AISI 304 austenitic stainless steels. The tool used was formed of a tungsten‐based alloy. The specimens were welded on an 11 kW vertical milling machine. Defect‐free welds were produced on 2.5 mm plates of hot‐rolled AISI 304 austenitic stainless steels at travel speeds ranging from 40 to 100 mm/min with a constant rotating speed of 1000 rpm. Tensile strengths and hardness values of the weld interface were determined and microstructure features of these samples were investigated.     

Corrosion resistance of the layers formed on the surface of plasma-nitrided AISI 304L steel

Austenitic stainless steels have good corrosion resistance, but their low hardness and low wear resistance limit their use whenever surface hardness is required. Nitriding treatments have been successfully applied to stainless steels to improve their mechanical and tribological properties; however, at temperatures above 723 K, gas or salt bath nitriding processes decrease the corrosion resistance due to the formation of CrN and other phases within the modified layer. Chromium compounds draw chromium and nitrogen from the adjacent regions, degrading the corrosion resistance. The plasma nitriding technique permits the use of treatment temperatures as low as 623 K without promoting degradation in the corrosion resistance of stainless steel. In this work, the pulsed glow discharge (PGD) technique was used for nitriding steel (AISI304L) in order to investigate the effect of the temperature of this treatment in the morphology and, as a consequence, in the anodic behavior of the formed layers, in solution with and without chloride ions. Four different temperatures were employed (623, 673, 723, and 773 K). The samples were characterized by optical microscopy (OM), scanning electron microscopy (SEM) with energy-dispersive spectroscopy (EDS), X-ray diffraction (XRD), microhardness measurements, and electrochemical tests with potentiodynamic anodic polarization curves. The nitriding temperature alters the anodic behavior due to a displacement of the polarization curve towards higher currents, in a solution free of chloride ions. In a chloride solution, the nitriding temperature increases the pitting potential up to the oxygen evolution region.     

A study on the abrasive and erosive wear behavior of arc-deposited Cr-N-O coatings on tool steel

In this study, the cathodic arc evaporation technique, by using the chromium target and controlling the flow rate of nitrogen/oxygen reactive gases, was utilized to deposit three different Cr-N-O coatings (CrN, CrN/Cr(N,O), CrN/Cr₂O₃) on AISI M2 tool steel. Two types of wear tests were applied to evaluate the abrasive and erosive wear behavior of the coated and uncoated specimens. One was the ball-on-disk abrasion test to measure the friction coefficient of these specimens. The other was the erosion test using Al₂O₃ particles (~ 177 µm in size and Mohr 7 scale) of about 5 g, and then the surface morphologies of the eroded specimens were observed. To further understand the coating effects on the two wear behaviors of M2 steel, coating structure, morphology, and adhesion were analyzed using XRD, SEM, and TEM, respectively. The results showed that surface roughness and adhesion of the double-layered coatings (CrN/Cr(N,O) and CrN/Cr₂O₃) were inferior to those of monolithic CrN, but their hardness and elastic modulus were superior to those of CrN. In the abrasive behavior, Cr-N-O coatings reduced the friction coefficient of M2 substrate. In particular, the CrN/Cr₂O₃ has the highest hardness/elastic (H/E) modulus ration, therefore the lowest friction coefficient, among all the coated-specimens tested. In the erosive behavior, the coated specimens exhibited better erosion resistance as compared to the uncoated ones, at the impingement angles of either 30^o or 90^o. Moreover, the erosion resistance of CrN/Cr(N,O) coatings was superior to that of CrN/Cr₂O₃ coatings due to its better adhesion.     

Influence of bias voltages on the structure and wear properties of TiSiN coating synthesized by cathodic arc plasma evaporation

Nanocomposite TiSiN films have been deposited on M2 tool steel substrates using TiSi alloy as target by a dual cathodic arc plasma deposition (CAPD) system. The influences of bias voltages on the microstructure, mechanical and tribological properties of the films were investigated. Scanning electron microscopy, transmission electron microscopy, X-ray diffraction techniques were employed to analyse the microstructure, grain size and residual stress. Nano-indentation and tribometer testers were used to measure the mechanical and tribological properties of nanocomposite TiSiN thin films. The results showed that the hardness of the films ranged from 25 to 37 GPa, which were higher than that of TiN (21 GPa). The coefficient of friction of the TiSiN thin films was more stable but was higher than that of TiN when wear against both Cr steel and WC-Co ball, respectively. When encountered with both Cr steel and WC-Co ball of the counter ball, the tribological mechanisms of TiSiN thin films are adhesive and abrasion wears, respectively. It has been found that the microstructure, mechanical and wear properties of the films were correlated to bias voltage, grain size, and amorphous Si₃N₄ nanocomposite formed in film structure, resulting in a superhard TiSiN coating.     

Nitriding in cathodic cage of stainless steel AISI 316: Influence of sample position

Cathodic cage plasma nitriding is a new growth technique based on multiple hollow cathode effects. The samples are kept at a floating potential inside a cage that acts as a cathode and shields the samples from the cathodic potential. The aim of this work is to perform a systematic study of the properties of nitrided layers as a function of the distance from the nitriding sample surface to the cage wall using this technique. Cylindrical austenitic stainless steel AISI 316 samples were placed in different positions on an alumina plate inside the cathodic cage. The nitrided samples were characterized by optical microscopy, X-ray diffraction and microhardness measurements. The results show that the temperature inside the cage is nearly uniform and that the nitrided layers possess good physical properties and uniformity. Therefore, the differences in the nitrided layer thicknesses obtained at different positions must be due to particle flow reaching the sample surface, depending on how far the sample is from the cage walls.     

Pitting corrosion failure of an AISI stainless steel pointer rod

In this study, failure analysis of a thermostatic mixing valve pointer rod made of AISI 304 stainless steel was performed. Visual examination, followed by an in-depth microstructural characterization using optical and scanning electron microscopy, was carried out for understanding the primary cause of failure. Energy dispersive X-ray, X-ray diffraction analysis and transmission electron microscopic analyses were also necessary supplements to this investigation. Finally, the obtained results infer that the combined effect of large amounts of MnS inclusions and the presence of deformation induced martensite adversely affected the pitting corrosion resistance of the pointer rod material. It is concluded that the pointer rod material was not properly investigated for defects prior to and after its fabrication.     

Effects of low-temperature duplex coatings on the abrasive and erosive behavior of ADI

This study utilized electroless nickel (EN) and cathodic arc evaporation (CAE) technologies, which have the well-known advantage of low processing temperature (EN = 90 °C and CAE = 230 °C), to treat the austempered ductile iron (ADI) substrate. The eligibility of applying the EN and CAE-CrTiAlN duplex coatings on ADI, along with the coating properties, such as structure, roughness, and adhesion, was evaluated and analyzed. Wear and erosive tests were also performed to further understand the effects of the coatings on the abrasive and erosive behaviors of ADI. The results show that the unique microstructure of ADI does not deteriorate after EN and CAE treatments. With regard to erosion resistance, the duplex coated specimens perform better than do the uncoated and monolithic EN or CrTiAlN coated ones. Moreover, the duplex coatings achieve a remarkable reduction in ADI's friction coefficient from 0.85 to 0.6.     

Monotonic vis-à-vis cyclic fracture behaviour of AISI 304LN stainless steel

This investigation is aimed to examine the monotonic and cyclic fracture behaviour of AISI 304LN stainless steel and its weldments, in order to assess their integrity under seismic loading conditions. The monotonic fracture resistance of the steel has been determined using standard J-integral technique; whereas the cyclic fracture resistance has been evaluated using periodic unloading to different extents fixed by pre-determined R-ratio. Comparison of the fracture toughness values of the steel estimated under monotonic and cyclic loading indicates that the latter could be as low as one-fifth of the former. The observed degradation in cyclic fracture resistance has been attributed to crack tip re-sharpening during cyclic loading.     

Cyclic fracture behaviour of 304LN stainless steel under load and displacement control modes

Attempts have been made to understand cyclic fracture behaviour of AISI 304LN stainless steel used for nuclear piping materials under load vis‐à‐vis displacement controlled fracture tests; the former closely simulate the seismic loading conditions. The load controlled tests indicate that a material fails in a limited number of cycles even when the load amplitudes are sufficiently below the maximum load in a monotonic J–R test. The displacement controlled tests, on the other hand, show that the energy absorbing ability of a material gets severely reduced under cyclic loading conditions. The obtained results on standard laboratory specimens have been compared with similar available results on components in order to provide guidelines for maximum load bearing capability of engineering components under cyclic loading.     

Characterization of failure modes for different welding processes of AISI/SAE 304 stainless steels

Weld joints manufactured with a welding electrode type 308L and by three different arc welding processes shielded metal arc welding (SMAW), gas metal arc welding (GMAW) and flux cored arc welding (FCAW) in a AISI/SAE 304 were studied in order to compare the failure mechanisms associated with their mechanical and microstructural properties. Chemical compositions were analyzed by optical emission spectroscopy and the ferrite numbers (FN) of the welds were also identified. Relevant microstructural characteristics of the different processes were analyzed by microscopy techniques. Finally, fatigue tests were performed to study the variations in the mechanical properties of each process and to analyze their most probable failure modes by means of a fractographic study, in which the characteristic morphologies of each one (nucleation, propagation, final fracture) were identified by means of optical stereoscopy and scanning electron microscopy (SEM). Three different fracture modes were found at the welding joints that showed correlations with microstructural changes produced during the welding process. The first failure mode displayed that the nucleation of the crack was at the weld root. The second failure mode was generated at the heat affected zone (HAZ), where the crack nucleated due to a variation in the grain size produced by the process and then further propagated through the edge of the weld. The third failure mode appeared due to the presence of exogenous inclusions generated by the welding process, which acted as stress concentrators in the weld and produce the initiation and further propagation of the crack. Lastly, some welding processes presented a combination of the previous failure modes and consequently multiple sites of crack nucleation.     

304不锈钢激光原位合成自润滑涂层的宽温域摩擦学性能

由于304不锈钢在中、高温下摩擦学性能较差,制约了其在重要摩擦运动副零部件上的应用。为改善304不锈钢的摩擦学性能,以Ni60粉末为增韧相,WS2为合成润滑相的前驱化合物,TiC为高硬度耐磨相,采用高能激光束在其表面原位合成自润滑耐磨复合涂层。利用X射线衍射仪、扫描电子显微镜、显微硬度计、摩擦磨损试验机和探针式材料表面磨痕测量仪表征涂层和基体的物相、微观结构、显微硬度与表面形貌,并系统研究涂层和基体在20,300,600,800℃下的摩擦学性能及其磨损机理。结果表明:涂层主要由Cr0.19Fe0.7Ni0.11,Ti2SC,Fe2C,Cr7C3,CrS和WS2组成;涂层的平均显微硬度(302.0HV0.5)略高于基体(257.2HV0.5),但涂层上部区域的硬度(425.4HV0.5)约为基体的1.65倍;涂层在所有等温摩擦学实验中摩擦因数和磨损率均低于基体,300℃时涂层润滑效果最好,摩擦因数为0.3031,600℃时涂层耐磨效果最好,磨损率为9.699×10^-5 mm^3·N^-1·m^-1。     

Measurement of the Thermal Conductivity of Stainless Steel AISI 304L Up to 550 K

New measurements of the thermal conductivity of stainless steel AISI 304L over the temperature range 300 to 550 K are reported. To perform the measurements, the transient hot-wire technique was employed, with a new wire sensor. The sensor makes use of a soft silicone paste material and of two thin polyimide films, between the hot wires of the apparatus and the stainless steel specimen. The transient temperature rise of the wire sensor is measured in response to an electrical heating step over a period of 40 s to 2 s, allowing an absolute determination of the thermal conductivity of the solid, as well as of the polyimide film and the silicone paste. The method is based on a full theoretical model with equations solved by a two-dimensional finite-element method applied to the exact geometry. At the 95% confidence level, the standard deviation of the thermal conductivity measurements is 0.6%, while the standard uncertainty of the technique is less than 1.5%.     

Critical hydrogen concentration for hydrogen-induced blistering on AISI 430 stainless steel

Effects of cold work on hydrogen diffusivity, hydrogen concentration and hydrogen trap density in AISI 430 stainless steel were investigated. Hydrogen concentration and trap density were increased with increasing cold work, but diffusivity was decreased. The increase in trap density as a result of cold work was responsible for the decrease in hydrogen diffusivity and the increase in hydrogen concentration. Trap densities varied from 10²¹ cm⁻³ for the cold-worked specimen to 10¹⁷ cm⁻³ for the annealed. The cold-worked steel was more sensitive to hydrogen-induced blistering due to its higher hydrogen concentration and trap density, but no blistering was found on annealed specimens.     

Characterization of transition joints of commercially pure titanium to 304 stainless steel

Solid-state direct bonding between commercially pure titanium and type 304 austenitic stainless steel has been carried out in the temperature range of 850–950 °C, under a uniaxial pressure of 3 MPa for 1 h. The diffusion bonds have been evaluated using light microscopy, electron probe microanalysis (EPMA), X-ray diffraction (XRD) technique and tensile testing. Light microscopy shows that different intermediate layers are formed in the reaction zone, and the width of these layers increases with an increase in bonding temperature. EPMA revealed that, at any particular bonding temperature, Ti traverses a minimum distance in the 304 stainless steel side, whereas Fe, Cr and Ni travel comparatively larger distances in the Ti side. This microanalysis also indicated different step formations in the concentration profile of Ti, Fe and Cr over different composition ranges in the diffusion zone indicating formation of intermetallic phases that were detected by XRD. Brittle intermetallic phases lower the strength and ductility of the diffusion bonded couples significantly. Best room temperature tensile strength, 217 MPa, has been obtained at 850 °C processing temperature due to minimal deleterious effects.