Synthesis and characterization of poly(ethylene terephthalate) nanocomposites with organoclay

Poly(ethylene terephthalate) (PET)/montmorillonite (MMT) nanocomposites were prepared by solution intercalation method. The clay was organo‐modified with the intercalation agent cetylpyridinium chloride (CPC). Wide‐angle X‐ray diffraction (XRD) showed that the layers of MMT were intercalated by CPC. Four nanocomposites with organoclay contents of 1, 5, 10, and 15 wt % were prepared by solution blending. XRD showed that the interlayer spacing of organoclay in the nanocomposites depends on the amount of organoclay present. According to the results of differential scanning calorimetry (DSC) analysis, clay behaves as a nucleating agent and enhances the crystallization rate of PET. The maximum enhancement of crystallization rate for the nanocomposites was observed in those containing about 10 wt % organoclay within the studied range of 1–15 wt %. From thermogravimetric analysis (TGA), we found that the thermal stability of the nanocomposites was enhanced by the addition of 1–15 wt % organoclay. These nanocomposites showed high levels of dispersion without agglomeration of particles at low organoclay content (5 wt %). An agglomerated structure did form in the PET matrix at 15 wt % organoclay. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 91: 140–145, 2004     

Preparation and characterization of poly(butylene terephthalate) nanocomposites with various organoclays

Layered‐silicate‐based polymer–clay nanocomposite materials were prepared depending on the surface modification of montmorillonite (MMT). Nanocomposites consisting of poly(butylene terephthalate) (PBT) as a matrix and dispersed inorganic clay modified with cetyl pyridinium chloride (CPC), benzyl dimethyl N‐hexadecyl ammonium chloride, and hexadecyl trimethyl ammonium bromide by direct melt intercalation were studied. The organoclay loading was varied from 1 to 5 wt %. The organoclays were characterized with X‐ray diffraction (XRD) to compute the crystallographic spacing and with thermogravimetric analysis to study the thermal stability. Detailed investigations of the mechanical and thermal properties as well as a dispersion study by XRD of the PBT/clay nanocomposites were conducted. X‐ray scattering showed that the layers of organoclay were intercalated with intercalating agents. According to the results of a differential scanning calorimetry analysis, clay acted as a nucleating agent, affecting the crystallization. The PBT nanocomposites containing clay treated with CPC showed good mechanical properties because of intercalation into the polymer matrix. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009     

Synthesis and evaluation of high‐performance ethylene–propylene–diene terpolymer/organoclay nanoscale composites

The main objective of this study was to synthesize and characterize the properties of ethylene–propylene–diene terpolymer (EPDM)/clay nanocomposites. Pristine clay, sodium montmorillonite (Na⁺–MMT), was intercalated with hexadecyl ammonium ion to form modified organoclay (16Me–MMT) and the effect of intercalation toward the change in interlayer spacing of the silicate layers was studied by X‐ray diffraction, which showed that the increase in interlayer spacing in Na⁺–MMT by 0.61 nm is attributed to the intercalation of hexadecyl ammonium ion within the clay layers. In the case of EPDM/16Me–MMT nanocomposites, the basal reflection peak was shifted toward a higher angle. However, gallery height remained more or less the same for different EPDM nanocomposites with organoclay content up to 8 wt %. The nanostructure of EPDM/clay composites was characterized by transmission electron microscopy, which established the coexistence of intercalated and exfoliated clay layers with an average layer thickness in the nanometer range within the EPDM matrix. The significant improvement in thermal stability and mechanical properties reflects the high‐performance nanocomposite formation. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 93: 2429–2436, 2004     

Preparation and characterization of poly(hydroxybutyrate‐co‐hydroxyvalerate)–organoclay nanocomposites

This study describes the microstructure and thermal and mechanical properties of poly(hydroxybutyrate‐co‐hydroxyvalerate) (PHB/HV)–organoclay nanocomposites prepared by melt intercalation using Cloisite 30B, a monotallow bis‐hydroxyethyl ammonium‐modified montmorillonite clay. X‐ray diffractometry and transmission electron microscopy analyses clearly confirm that an intercalated microstructure is formed and finely distributed in the PHB/HV copolymer matrix because PHB/HV has a strong hydrogen bond interaction with the hydroxyl group in the organic modifier of Cloisite 30B. The nanodispersed organoclay also acts a nucleating agent, increasing the temperature and rate of crystallization of PHB/HV; therefore, the thermal stability and tensile properties of the organoclay‐based nanocomposites are enhanced. These results confirm that the organoclay nanocomposite greatly improves the material properties of PHB/HV. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 90: 525–529, 2003     

The Nucleating Effect of Montmorillonite on Crystallization of PET/Montmorillonite Nanocomposite

Poly(ethylene terephthalate) (PET)/montmorillonite (MMT) nanocomposites were prepared by solution intercalation method. The clay was organo-modified with intercalation agent of cetyltrimetylammonium chloride (CMC). XRD showed that the layers of MMT were intercalated by CMC. Four nanocomposites with organoclay contents of 1, 5, 10, and 15 wt% were prepared by solution blending. XRD showed that the interlayer spacing of organoclay in the nanocomposites depends on the amount of organoclay. The nucleating effect of organoclay is investigated using differential scanning calorimetry (DSC) analysis. Clay behaves as a nucleating agent and enhances the crystallization rate of PET. Maximum enhancement in crystallization rate for the nanocomposites was observed in blends containing ca. 10 wt% of clay in the range of 1–15 wt%. According to transmission electron microscopy (TEM), the organoclay particle was highly dispersed in the PET matrix without a large agglomeration of particles for low organoclay content (5 wt%). Agglomerated structure did form in the PET matrix at 15 wt% organoclay content.     

Poly(vinyl alcohol) nanocomposites with different clays: Pristine clays and organoclays

Poly(vinyl alcohol) (PVA)/clay nanocomposites were synthesized using the solution intercalation method. Na ion‐exchanged clays [Na⁺–saponite (SPT) and Na⁺–montmorillonite (MMT)] and alkyl ammonium ion‐exchanged clays (C₁₂–MMT and C₁₂OOH–MMT) were used for the PVA nanocomposites. From the morphological studies, the Na ion‐exchanged clay is more easily dispersed in a PVA matrix than is the alkyl ammonium ion‐exchanged clay. Attempts were also made to improve both the thermal stabilities and the tensile properties of PVA/clay nanocomposite films, and it was found that the addition of only a small amount of clay was sufficient for that purpose. Both the ultimate tensile strength and the initial modulus for the nanocomposites increased gradually with clay loading up to 8 wt %. In C₁₂OOH–MMT, the maximum enhancement of the ultimate tensile strength and the initial modulus for the nanocomposites was observed for blends containing 6 wt % organoclay. Na ion‐exchanged clays have higher tensile strengths than those of organic alkyl‐exchanged clays in PVA nanocomposites films. On the other hand, organic alkyl‐exchanged clays have initial moduli that are better than those of Na ion‐exchanged clays. Overall, the content of clay particles in the polymer matrix affect both the thermal stability and the tensile properties of the polymer/clay nanocomposites. However, a change in thermal stability with clay was not significant. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 90: 3208–3214, 2003     

Effect of organic modifiers and silicate type on filler dispersion,thermal, and mechanical properties of ABS‐clay nanocomposites

Acrylonitrile–butadiene–styrene (ABS)–clay composite and intercalated nanocomposites were prepared by melt processing, using Na‐montmorillonite (MMT), several chemically different organically modified MMT (OMMT) and Na‐laponite clays. The polymer–clay hybrids were characterized by WAXD, TEM, DSC, TGA, tensile, and impact tests. Intercalated nanocomposites are formed with organoclays, a composite is obtained with unmodified MMT, and the nanocomposite based on synthetic laponite is almost exfoliated. An unintercalated nanocomposite is formed by one of the organically modified clays, with similar overall stack dispersion as compared to the intercalated nanocomposites. T_g of ABS is unaffected by incorporation of the silicate filler in its matrix upto 4 wt % loading for different aspect ratios and organic modifications. A significant improvement in the onset of thermal decomposition (40–44°C at 4 wt % organoclay) is seen. The Young's modulus shows improvement, the elongation‐at‐break shows reduction, and the tensile strength shows improvement. Notched and unnotched impact strength of the intercalated MMT nanocomposites is lower as compared to that of ABS matrix. However, laponite and overexchanged organomontmorillonite clay lead to improvement in ductility. For the MMT clays, the Young's modulus (E) correlates with the intercalation change in organoclay interlayer separation (Δd₀₀₁) as influenced by the chemistry of the modifier. Although ABS‐laponite composites are exfoliated, the intercalated OMMT‐based nanocomposites show greater improvement in modulus. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Physical properties of poly(trimethylene terephthalate)/organoclay nanocomposites obtained via melt compounding and in situ polymerization

Two series of poly(trimethylene terephthalate) (PTT) nanocomposites, containing an organically modified montmorillonite (MMT) clay (1,2‐aminododecanoic acid (ADA)–intercalated MMT) were prepared via melt compounding and in situ polymerization methods using dimethyl terephthalate (DMT) and 1,3‐propanediol (PDO). The effect of different methods of preparation and varying organoclay contents (1−5 wt%) on the structural, morphological, thermal, and mechanical properties were investigated. The results of wide‐angle X‐ray diffraction (WAXD) and transmission electron microscope (TEM) suggested the possible existence of intercalation morphology between ADA‐MMT and the PTT matrix obtained from melt compounding, and mostly exfoliation state from in situ polymerization depending on the amount of organoclay. From DSC studies, in melt compounding case, the addition of ADA‐MMT in PTT increases melt‐crystallization (T_cm) peak temperature by 14−15°C irrespective of the clay content. However, the melting temperature (T_m) of pristine PTT remains unchanged with increasing clay content. In the case of in situ polymerization, the T_cm and T_m peaks are shifted towards lower temperature with increasing clay content. Dynamic mechanical thermal analysis (DMTA) studies on melt compounded samples revealed a marginal lowering of glass transition temperature (T_g) irrespective of clay content, and a noticeable decrease in T_g with increasing clay content for in situ polymerized samples. The PTT/ADA‐MMT nanocomposites via melt compounding showed higher initial modulus and yield stress, and lower strain at break compared with in situ polymerization with increasing clay content. POLYM. COMPOS., 2008. © 2008 Society of Plastics Engineers     

Investigation of nanostructure and properties of aromatic–aliphatic polyamide‐based nanocomposites with clay additives

Aromatic–aliphatic polyamide/clay nanocomposites were produced using solution intercalation technique. Surface modification of the clay was performed with ammonium salt of aromatic diamine and the polyamide chains were produced by condensation of 4‐aminophenyl sulfone with sebacoyl chloride (SCC) in dimethyl acetamide. Carbonyl chloride endcapped polymer chains were prepared by adding extra SCC near the end of polymerization reaction. The nanocomposites were investigated for organoclay dispersion, water absorption, mechanical, and thermal properties. Formation of delaminated and intercalated nanostructures was confirmed by X‐ray diffraction and TEM studies. Tensile strength and modulus improved for nanocomposites with optimum organoclay content (8 wt %). Thermal stability and glass transition temperatures of nanocomposites increased relative to pristine polyamide with augmenting organoclay content. The amount of water uptake for these materials decreased as compared with the neat polyamide. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009     

Morphology and mechanical properties of heterophasic PP–EP/EVA/organoclay nanocomposites

The effect of vinyl acetat (VA) on the morphological, thermal stability, and mechanical properties of heterophasic polypropylene–(ethylene‐propylene) copolymer (PP–EP)/poly(ethylene vinyl acetate) (EVA)/organoclay nanocomposites was studied. Tailored organoclay C20A was selected to enhance the exfoliation of the clay platelets. Depending on the VA content, there were two morphological organoclay populations in the systems. Both populations were directly observed by scanning transmission electron microscopy and measured by wide‐angle X‐ray diffraction and small‐angle X‐ray scattering. The content of VA in EVA originated spherical and elongated morphologies in the resultant nanocomposites. High‐VA content led to a better intercalation of the organoclay platelets. Measurement of thermal properties suggested that higher VA decreases thermal stability in samples both with and without organoclay, although nanocomposites had higher thermal stability than samples without clay. The storage modulus increased both with nanoclay and VA content. © 2012 Wiley Periodicals, Inc. J. Appl. Polym. Sci., 2013     

Effect of clay on mechanical and gas barrier properties of blown film LDPE/clay nanocomposites

Low density polyethylene (LDPE)/clay nanocomposites, which can be used in packaging industries, were prepared by melt‐mix organoclay with polymer matrix (LDPE) and compatibilizer, polyethylene grafted maleic anhydride (PEMA). The pristine clay was first modified with alkylammonium salt surfactant, before melt‐mixed in twin screw extruder attached to blown‐film set. D‐spacing of clay and thermal behavior of nanocomposites were characterized by Wide‐Angle X‐ray Diffraction (WAXD) and differential scanning calorimetry (DSC), respectively. WAXD pattern confirmed the increase in PEMA contents exhibited better dispersion of clay in nanocomposites. Moreover, DSC was reported the increased PEMA contents caused the decrease in degree of crystallinity. Mechanical properties of blown film specimens were tested in two directions of tensile tests: in transverse tests (TD tests) and in machine direction tests (MD tests). Tensile modulus and tensile strength at yield were improved when clay contents increased because of the reinforcing behavior of clay on both TD and MD tests. Tensile modulus of 7 wt % of clay in nanocomposite was 100% increasing from neat LDPE in TD tests and 17% increasing in MD tests. However, elongation at yield decreased when increased in clay loading. Oxygen permeability tests of LDPE/clay nanocomposites also decreased by 24% as the clay content increased to 7 wt %. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2007     

Influence of organic modification on mechanical properties of melt processed intercalated poly(methyl methacrylate)–organoclay nanocomposites

The influence of organic modifiers on intercalation extent, structure, thermal and mechanical properties of poly(methyl methacrylate) (PMMA)–clay nanocomposites were studied. Two different organic modifiers with varying hydrophobicity (single tallow versus ditallow) were investigated. The nanocomposites were prepared from melt processing method and characterized using wide angle X‐ray diffraction, transmission electron microscopy, thermogravimetric analysis, differential scanning calorimetry (DSC), and tensile tests. Mechanical properties such as tensile modulus (E), break stress (σ_brk), and % break strain (ε_brk) were determined for nanocomposites at various clay loadings. Extent of PMMA intercalation is sufficient and in the range 9–15 Å depending on organoclay and filler loading. Overall thermal stability of nanocomposites increases by 16–30°C. The enhancement in T_g of nanocomposite is merely by 2–4°C. With increase in clay loading, tensile modulus increases linearly while % break strain decreases. Break stress is found to increase till 4 wt % and further decreases at higher clay loadings. The overall improvement in thermal and mechanical properties was higher for the organoclay containing organic modifier with lower hydrophobicity and single tallow amine chemical structure. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2007     

Synthesis and properties of BCDA‐based polyimide–clay nanocomposites

Bicyclo[2.2.2]oct‐7‐ene‐2,3,5,6‐tetracarboxylic dianhydride (BCDA)‐based polyimide–clay nanocomposites were prepared from their precursor, namely polyamic acid, by a solution‐casting method. The organoclay was prepared by treating sodium montmorillonite (Kunipia F) clay with dodecyltrimethylammonium bromide at 80 °C. Polyamic acid solutions containing various weight percentages of organoclay were prepared from 4,4′‐(4,4′‐isopropylidenediphenyl‐1,1′‐diyldioxy)‐dianiline and BCDA in N‐methyl‐2‐pyrrolidone containing dispersed particles of organoclay at 20 °C. These solutions were cast on a glass plate using a Doctor's blade and then heated subsequently to obtain nanocomposite films. The nanocomposites were characterized using Fourier transform infrared spectroscopy, differential scanning calorimetry, thermal mechanical analysis, dynamic mechanical analysis, polarizing microscopy, scanning electron microscopy, transmission electron microscopy, wide‐angle X‐ray diffraction (WAXD) and thermogravimetric analysis. The glass transition temperature of the nanocomposites was found to be higher than that of pristine polymer. The coefficient of thermal expansion of the nanocomposites decreased with increasing organoclay content. WAXD studies indicated that the extent of silicate layer separation in the nanocomposite films depended upon the organoclay content. Tensile strength and modulus of the nanocomposite containing 1% organoclay were significantly higher when compared to pristine polymer and other nanocomposites. The thermal stability of the nanocomposites was found to be higher than that of pristine polymer in air and nitrogen atmosphere. Copyright © 2007 Society of Chemical Industry     

Synthesis and properties of polyimide (containing naphthalene) nanocomposites with organo‐modified montmorillonites

2,7‐Bis(4‐aminophenoxy) naphthalene (BAPN), a naphthalene‐containing diamine, was synthesized and polymerized with a 3,3′,4,4′‐benzophenone tetracarboxylic dianhydride (BTDA) to obtain a polyimide (PI) via thermal imidization. To enhance the thermal and mechanical properties of the polymer, PI–Montmorillonite (MMT) nanocomposites were prepared from a DMAc solution of poly(amic acid) and a DMAc dispersion of MMT, which were organo‐modified with various amounts of n‐dodecylamine (DOA) or cetylpyridium chloride (CPC). FTIR, XRD, and TEM (transmission electron microscopy) were used to verify the incorporation of the modifying agents into the clay structure and the intercalation of the organoclay into the PI matrix. Results demonstrated that the introduction of a small amount of MMT (up to 5%) led to the improvement in thermal stability and mechanical properties of PI. The decomposition temperature of 5% weight loss (T_d,5%) in N₂ was increased by 46 and 36°C in comparison with pristine PI for the organoclay content of 5% with DOA and CPC, respectively. The nanocomposites were simultaneously strengthened and toughened. The dielectric constant, CTE, and water absorption were decreased. However, at higher organoclay contents (5–10%), these properties were reduced because the organoclay was poorly dispersed and resulted in aggregate formation. The effects of different organo‐modifiers on the properties of PI–MMT nanocomposite were also studied; the results showed that DOA was comparable with CPC. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci, 2006     

Effect of clay surface modification and organoclay purity on microstructure and thermal properties of poly(l-lactic acid)/vermiculite nanocomposites

Vermiculite (VMT) was successfully modified by cationic exchange of hexadecyltrimethyl ammonium ions, covalent grafting of glycidoxypropyl trimethoxy silane, and combining grafting and intercalation. The complete removal of excess surfactant from VMT resulted in a change in the interlayer structure and higher thermal stability of the organoclay mineral. The organosilane grafted on the clay mineral edges improved the thermal stability of the organoclay mineral. The organoclay minerals were melt compounded with poly(l-lactic acid) (PLLA), and the effect of the nanofiller concentration, type of modification and organoclay mineral purity on the nanostructure and thermal properties of nanocomposites was investigated. The removal of excess surfactant and organosilane functionalization enhanced the dispersion level of the organoclay mineral. PLLA degradation that occurred during nanocomposite processing depended on the clay mineral concentration, the extent of clean surface and the clay mineral dispersion state. The removal of excess surfactant and organosilane functionalization improved the thermal stability of nanocomposites.     

Role of the cation‐exchange capacity in the formation of polystyrene–clay nanocomposites by in situ intercalative polymerization

An effect of the cation‐exchange capacity (CEC) on the formation of polystyrene–clay nanocomposites is reported. Two types of 2:1 layered silicates with different CECs, Wyoming (97 mequiv/100 g of clay) and bentonite H (BNH; 131 mequiv/100 g of clay) were investigated. The organoclay was prepared through the mixing of purified clay and octadecyldimethylammonium chloride (ODA) in an aqueous solution. The packing of the intercalated ODA surfactant depended on the CEC and the degree of solvent extraction. Two possible phases of the interlayer packing, solidlike and liquidlike, were detected for the extracted BNH because of the charge heterogeneity of the clay. The liquidlike phase showed a good affinity toward the styrene monomer, which promoted the formation of exfoliated nanocomposites. On the other hand, the solidlike phase showed a restricted dispersion in the styrene monomer. The organoclay interlayer showed limited expansion by the styrene monomer. This led to the formation of intercalated nanocomposites. An increase in the organoclay loading hindered the formation of the exfoliated nanocomposites. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 95: 785–789, 2005     

Preparation and characterization of polyethylene–clay nanocomposites by using chlorosilane‐modified clay

Clay was modified by trimethylchlorosilane; after modification, hydroxyl groups at the edge of layers were reacted and CEC value was drastically decreased. Polyethylene–clay composites were prepared by melt compounding. Wide angle X‐ray diffraction (WAXD) and transmission electron microscopy (TEM) showed that intercalated nanocomposites were formed using organoclay ion‐exchanged from chlorosilane‐modified clay, but conventional composites formed using organoclay directly ion‐exchanged from crude clay. Dynamic mechanical analysis (DMA) of PE and PE–clay composites was conducted; the results demonstrated that nanocomposites were more effective than conventional composites in reinforcement and addition of organoclay resulted in the increase of glass transition temperature (T_g), but crude clay had no effect on T_g of PE–clay composites. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 93: 676–680, 2004     

Effect of compatibilizer and organoclay content on structure,thermal, and mechanical properties of poly(butylene succinate)/(Ethylene acrylic acid)/Organoclay nanocomposites

Poly(butylene succinate) (PBS)/(ethylene acrylic acid) (EAA)/organoclay nanocomposites were prepared by using the melt intercalation technique. EAA was used as compatibilizer and organoclay was used as inorganic filler. X‐ray diffraction and transmission electron microscopy results indicated the addition of compatibilizer led to a large increase in basal spacing of nanocomposites and better overall dispersion of organoclay in the PBS matrix. However, the basal spacing was found to be invariant as the organoclay content increased. The differential scanning calorimetry analyses revealed that the incorporation of the organoclay and EAA and the variation of organoclay content altered the melting behavior and crystallization properties of PBS. Storage and loss modulus of virgin matrix increased with the incorporation of organoclay and EAA, and a maximum for the nanocomposite with 9 wt% organoclay. Moreover, the glass transition temperatures also increased for the various organoclay‐containing samples. Mechanical properties showed an increase with the incorporation of organoclay and EAA. The 5 wt% organoclay‐filled PBS gave the highest tensile strength and notched Izod impact strength among all the composites. Further increments in organoclay loading reduced the tensile strength and notched impact strength of nanocomposites, which was thought to be the result of agglomeration. However, increments in clay loading enhanced the flexural strength and flexural modulus of nanocomposites, with a maximum at 9 wt% organoclay. J. VINYL ADDIT. TECHNOL., 23:219–227, 2017. © 2015 Society of Plastics Engineers     

Polystyrene–organoclay nanocomposites prepared by melt intercalation,in situ,and masterbatch methods

In this study, polystyrene (PS)/montmorillonite nanocomposites were prepared by melt intercalation, in situ polymerization, and masterbatch methods. In the masterbatch method, as the first step, a high clay content composite of PS–organoclay (masterbatch) was prepared by in situ polymerization, and then the prepared masterbatch was diluted to desired compositions with commercial PS in a twin‐screw extruder. The structure and mechanical properties of the nanocomposites were examined. X‐ray diffraction (XRD) analysis showed that the d‐spacing of the in situ formed nanocomposites increased from 32.9 Å for the organoclay powder to 36.3 and 36.8 Å respectively in nanocomposites containing 0.73 and 1.6 wt% organoclay, indicating intercalation. However, the d‐spacing of the other prepared materials remained nearly unchanged when compared with pure organoclay powder. Thus, at these low clay contents, in situ formed nanocomposites showed the best improvement in mechanical properties including tensile, impact strength, and Young's modulus. In situ polymerization method did not prove to be efficient at high clay loadings in terms of intercalation and mechanical properties. At high clay loadings, the effects of the three methods in promoting mechanical properties were not significantly different from each other. POLYM. COMPOS., 27:249–255, 2006. © 2006 Society of Plastics Engineers     

Polyolefin‐based nanocomposite: The effects of processing aids

PP/organoclay nanocomposites were prepared using different processing aids (EMCA and PPG), and their effects on the thermal and mechanical properties were evaluated by WAXD, TEM, SEM, DSC, and mechanical tests. This study helps to clarify the effects of processing aids on the organoclay surface and on the intercalation and exfoliation processes. Nanocomposites with elongated intercalated and partially exfoliated structures were obtained, mainly when C‐15A was used. The results for the mechanical properties showed that the processing aids increased the impact strength significantly (up to three times that of neat PP) but reduced the flexural modulus of PP nanocomposites. PPG, which is polar promoted wetting MMT surface, thus increasing its interlayer distance, mainly for PP/C‐20A nanocomposites. However, it reduced the interfacial adhesion between the clay and the matrix. Nanocomposites impact strength was improved, especially when the C‐15A organoclay was used, while were achieved better results with the C‐20A organoclay when EMCA was used. The larger the amount of processing aid added, the higher the impact strength, but the lower the flexural modulus of the nanocomposites. PPG caused debonding of the clay particles and increased the number of microvoids, generating more mechanisms to aid in the energy dissipation of the systems. EMCA promoted debonding of clay particles with the formation of fibrils, indicating stronger interactions between the clay and matrix. A slight nucleation effect for PP crystallization was observed, mainly when EMCA was used. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2011