Effect of polymerization potential on the actuation of free standing poly-3,4-ethylenedioxythiophene films in a propylene carbonate electrolyte

The linear actuation of poly-3,4-ethylenedioxythiophene (PEDOT) films polymerized at different potentials (0.8-1.3 V) at −27 °C in propylene carbonate (PC) solutions of TBACF₃SO₃ (tetrabutylammonium trifluoromethanesulfonate) was examined under isotonic (constant force) and isometric (constant length) conditions. The actuation properties were evaluated by electrochemomechanical deformation measurements (ECDM) during cyclic voltammetry, square wave potential steps and long term cycling. The ECDM response revealed mixed ion actuation behaviour for PEDOT films polymerized at the potential extremes of 0.8 and 1.3 V. At intermediate polymerization potentials from 0.9 to 1.2 V, cation-driven actuation was observed involving immobilized triflate anions (CF₃SO₃⁻). Long term experiments (50 cycles) showed that films prepared at polymerization potentials of 0.8 V exhibited mainly anion-driven actuation, during potential steps to and from 1.0 V; conversely PEDOT prepared at a polymerization potential of 1.1 V showed exclusively cation-driven actuation. PEDOT films prepared at a polymerization potential of 1.1 V showed the maximum cation-driven actuation during cyclic voltammetry experiments including long term cycling. SEM images showed an open porous structure in all of the PEDOT films.     

Sintering of glass-added BaZn1/3Nb2/3O3 ceramics

The complex perovskite oxide Ba(Zn_1/3Nb_2/3)O₃ (BZN) has been studied for its attractive dielectric properties which place this material interesting for applications as multilayer ceramics capacitors or hyperfrequency resonators. This material is sinterable at low temperature with combined glass phase–lithium salt additions, and exhibits, at 1 MHz very low dielectric losses combined with relatively high dielectric constant and a good stability of this later versus temperature. The 2 wt.% of ZnO–SiO₂–B₂O₃ glass phase and 1 wt.% of LiF-added BZN sample sintered at 900 °C exhibits a relative density higher than 95% and attractive dielectric properties: a dielectric constant ?_r of 39, low dielectrics losses (tan(δ) < 10⁻³) and a temperature coefficient of permittivity τ_? of 45 ppm/°C⁻¹. The 2 wt.% ZnO–SiO₂–B₂O₃ glass phase and 1 wt.% of B₂O₃-added BZN sintered at 930 °C exhibits also attractive dielectric properties (?_r = 38, tan(δ) < 10⁻³) and it is more interesting in terms of temperature coefficient of the permittivity (τ_? = −5 ppm/°C). Their good dielectric properties and their compatibility with Ag electrodes, make these ceramics suitable for L.T.C.C applications.     

Mixed-ion linear actuation behaviour of polypyrrole

The linear actuation of polypyrrole (PPy) films polymerized at 0.85 V (versus Ag-wire) and −27 °C in propylene carbonate solutions of tetrabutylammonium trifluoromethanesulfonate (TBACF₃SO₃) was investigated in the same monomer-free electrolyte. The actuation properties were evaluated by electrochemomechanical deformation measurements (ECMD) during cyclic voltammetry and potential step experiments. The ECMD response revealed mixed-ion actuation behaviour for the film, namely the polymer film actuation was dominated by cation movement at potentials less than 0 V and anion movement at potentials greater than 0 V, with film lengthening seen at both potential extremes. It was found that the ratio of cathodic to anodic actuation can be modulated by the scan rate. Longer-term actuation (50 potential steps from −1 V to 0 V, or from 0 V to +1 V), indicated better film stability when cycled in the anodic region. Changing the electropolymerisation potential to a higher value of 1.2 V led to a modification in ECMD characteristics for the PPy/CF₃SO₃ films.     

Film thickness dependence of the dielectric properties of SrTiO3/BaTiO3 multilayer thin films deposited by double target RF magnetron sputtering

Four-layer SrTiO₃/BaTiO₃ thin films ((ST/BT)₄) with various thicknesses deposited on Pt/Ti/SiO₂/Si substrates at 500 °C by double target RF magnetron sputtering have been investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM), profilometry, capacitance-voltage and current-voltage measurements. The XRD patterns reveal the frame formation of the sputter deposited (ST/BT)₄ with controlled modulation. The adhesion between the Pt bottom electrode layer and the BT layer is excellent. The dielectric constant of the (ST/BT)₄ multilayer thin film increases with increasing film thickness. The effects of temperature, frequency, and bias voltage on the dielectric constant of the (ST/BT)₄ multilayer thin films are discussed in detail. The leakage current density of the (ST/BT)₄ multilayer with a thickness of 450.0 nm is lower than 1.0 × 10⁻⁸ A/cm² for the applied voltage of less than 5 V, showing that the multilayer thin films with such a characteristic could be applied for use in dynamic random access memory (DRAMs) capacitors.     

Synthesis and characterization of high-density non-spherical Li(Ni1/3Co1/3Mn1/3)O2 cathode material for lithium ion batteries by two-step drying method

Non-spherical Li(Ni_1/3Co_1/3Mn_1/3)O₂ powders have been synthesized using a two-step drying method with 5% excess LiOH at 800 °C for 20 h. The tap-density of the powder obtained is 2.95 g cm⁻³. This value is remarkably higher than that of the Li(Ni_1/3Co_1/3Mn_1/3)O₂ powders obtained by other methods, which range from 1.50 g cm⁻³ to 2.40 g cm⁻³. The precursor and Li(Ni_1/3Co_1/3Mn_1/3)O₂ are characterized by X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD) and scanning electron microscope (SEM). XPS studies show that the predominant oxidation states of Ni, Co and Mn in the precursor are 2⁺, 3⁺ and 4⁺, respectively. XRD results show that the Li(Ni_1/3Co_1/3Mn_1/3)O₂ material obtained by the two-step drying method has a well-layered structure with a small amount of cation mixing. SEM confirms that the Li(Ni_1/3Co_1/3Mn_1/3)O₂ particles obtained by this method are uniform. The initial discharge capacity of 167 mAh g⁻¹ is obtained between 3 V and 4.3 V at a current of 0.2 C rate. The capacity of 159 mAh g⁻¹ is retained at the end of 30 charge-discharge cycle with a capacity retention of 95%.     

Comparison of AlPO4- and Co3(PO4)2-coated LiNi0.8Co0.2O2 cathode materials for Li-ion battery

Electrochemical and thermal properties of Co₃(PO₄)₂- and AlPO₄-coated LiNi_0.8Co_0.2O₂ cathode materials were compared. AlPO₄-coated LiNi_0.8Co_0.2O₂ cathodes exhibited an original specific capacity of 170.8 mAh g⁻¹ and had a capacity retention (89.1% of its initial capacity) between 4.35 and 3.0 V after 60 cycles at 150 mA g⁻¹. Co₃(PO₄)₂-coated LiNi_0.8Co_0.2O₂ cathodes exhibited an original specific capacity of 177.6 mAh g⁻¹ and excellent capacity retention (91.8% of its initial capacity), which was attributed to a lithium-reactive Co₃(PO₄)₂ coating. The Co₃(PO₄)₂ coating material could react with LiOH and Li₂CO₃ impurities during annealing to form an olivine Li_xCoPO₄ phase on the bulk surface, which minimized any side reactions with electrolytes and the dissolution of Ni⁴⁺ ions compared to the AlPO₄-coated cathode. Differential scanning calorimetry results showed Co₃(PO₄)₂-coated LiNi_0.8Co_0.2O₂ cathode material had a much improved onset temperature of the oxygen evolution of about 218 °C, and a much lower amount of exothermic-heat release compared to the AlPO₄-coated sample.     

Effect of synthesis condition on the structural and electrochemical properties of Li[Ni1/3Mn1/3Co1/3]O2 prepared by the metal acetates decomposition method

In order to get homogeneous layered oxide Li[Ni_1/3Mn_1/3Co_1/3]O₂ as a lithium insertion positive electrode material, we applied the metal acetates decomposition method. The oxide compounds were calcined at various temperatures, which results in greater difference in morphological (shape, particle size and specific surface area) and the electrochemical (first charge profile, reversible capacity and rate capability) differences. The Li[Ni_1/3Mn_1/3Co_1/3]O₂ powders were characterized by means of X-ray diffraction (XRD), charge/discharge cycling, cyclic voltammetry and SEM. XRD experiment revealed that the layered Li[Ni_1/3Mn_1/3Co_1/3]O₂ material can be best synthesized at temperature of 800 °C. In that synthesized temperature, the sample showed high discharge capacity of 190 mAh g⁻¹ as well as stable cycling performance at a current density of 0.2 mA cm⁻² in the voltage range 2.3-4.6 V. The reversible capacity after 100 cycles is more than 190 mAh g⁻¹ at room temperature.     

The performances of higher alcohol synthesis over nickel modified K2CO3/MoS2 catalyst

Ni modified K₂CO₃/MoS₂ catalyst was prepared and the performance of higher alcohol synthesis catalyst was investigated under the conditions: T = 280–340 °C, H₂/CO (molar radio) = 2.0, GHSV = 3000 h^− 1, and P = 10.0 MPa. Compared with conventional K₂CO₃/MoS₂ catalyst, Ni/K₂CO₃/MoS₂ catalyst showed higher activity and higher selectivity to C₂⁺OH. The optimum temperature range was 320–340 °C and the maximum space-time yield (STY) of alcohol 0.30 g/ml h was obtained at 320 °C. The selectivity to hydrocarbons over Ni/K₂CO₃/MoS₂ was higher, however, it was close to that of K₂CO₃/MoS₂ catalyst as the temperature increased. The results indicated that nickel was an efficient promoter to improve the activity and selectivity of K₂CO₃/MoS₂ catalyst.     

Synthesis and electrical properties of the (PVA)0.7(KI)0.3·xH2SO4 (0 ≤ x ≤ 5) polymer electrolytes and their performance in a primary Zn/MnO2 battery

Solid acid polymer electrolytes (SAPE) were synthesised using polyvinyl alcohol, potassium iodide and sulphuric acid in different molar ratios by solution cast technique. The temperature dependent nature of electrical conductivity and the impedance of the polymer electrolytes were determined along with the associated activation energy. The electrical conductivity at room temperature was found to be strongly depended on the amorphous nature of the polymers and H₂SO₄ concentration. The ac (100 Hz to 10 MHz) and dc conductivities of the polymer electrolytes with different H₂SO₄ concentrations were analyzed. A maximum dc conductivity of 1.05 × 10⁻³ S cm⁻¹ has been achieved at ambient temperature for electrolytes containing 5 M H₂SO₄. The frequency and temperature dependent dielectric and electrical modulus properties of the SAPE were studied. The charge transport in the present polymer electrolyte was obtained using Wagner's polarization technique, which demonstrated the charge transport to be mainly due to ions. Using these solid acid polymer electrolytes novel Zn/SAPE/MnO₂ solid state batteries were fabricated and their discharge capacity was calculated. An open circuit voltage of 1.758 V was obtained for 5 M H₂SO₄ based Zn/SAPE/MnO₂ battery.     

Effect of Zr/Ti ratio on piezoelectric properties of Pb(Ni1/3Sb2/3)O3-Pb(ZrTi)O3 ceramics

Piezoceramic compositions [Pb(Ni_1/3Sb_2/3)]_0.02-[Pb(Zr_1−yTi_y)]_0.98O₃ with y = 0.46-0.50 were synthesized by solid state route to study the effect of Zr/Ti ratio on crystal structure, microstructure, piezoelectric and dielectric properties. Calcination was performed at 1060 °C. The specimens were sintered at 1280 °C for 1 h. X-ray diffraction studies indicate the co-existence of tetragonal and rhombohedral perovskite phases in these compositions. Microstructural analysis showed the dense and uniform microstructure for [Pb(Ni_1/3Sb_2/3)]_0.02-[Pb(Zr_0.52Ti_0.48)]_0.98O₃. This composition was resulted in optimum values of properties viz. charge constant (d₃₃ = 301 × 10⁻¹² C/N), voltage constant (g₃₃ = 33.7 × 10⁻³ V m/N), product of piezoelectric charge constant and voltage constant (d₃₃ × g₃₃ = 10.12 × 10⁻¹² C V m/N²) and coupling factor (k_p = 0.63). Results indicated that this material composition could be suitable for power harvesting and sensor applications.     

Electrochemical and thermal studies of Li[NixLi(1/3−2x/3)Mn(2/3−x/3)]O2 (x = 1/12, 1/4, 5/12, and 1/2)

Samples of the layered cathode materials, Li[Ni_xLi_(1/3−2x/3)Mn_(2/3−x/3)]O₂ (x = 1/12, 1/4, 5/12, and 1/2), were synthesized at 900 °C. Electrodes of these samples were charged in Li-ion coin cells to remove lithium. The charged electrode materials were rinsed to remove the electrolyte salt and then added, along with EC/DEC solvent or 1 M LiPF₆ EC/DEC, to stainless steel accelerating rate calorimetry (ARC) sample holders that were then welded closed. The reactivity of the samples with electrolyte was probed at two states of charge. First, for samples charged to near 4.45 V and second, for samples charged to 4.8 V, corresponding to removal of all mobile lithium from the samples and also concomitant release of oxygen in a plateau near 4.5 V. Li[Ni_xLi_(1/3−2x/3)Mn_(2/3−x/3)]O₂ samples with x = 1/4, 5/12 and 1/2 charged to 4.45 V do not react appreciably till 190 °C in EC/DEC. Li[Ni_xLi_(1/3−2x/3)Mn_(2/3−x/3)]O₂ samples charged to 4.8 V versus Li, across the oxygen release plateau, start to significantly react with EC/DEC at about 130 °C. However, their high reactivity is similar to that of Li_0.5CoO₂ (4.2 V) with 1 μm particle size. Therefore, Li[Ni_xLi_(1/3−2x/3)Mn_(2/3−x/3)]O₂ samples showing specific capacity of up to 225 mAh/g may be acceptable for replacing LiCoO₂ (145 mAh/g to 4.2 V) from a safety point of view, if their particle size is increased.     

Electrochemical performance of the carbon coated Li3V2(PO4)3 cathode material synthesized by a sol-gel method

A carbon coated Li₃V₂(PO₄)₃ cathode material for lithium ion batteries was synthesized by a sol-gel method using V₂O₅, H₂O₂, NH₄H₂PO₄, LiOH and citric acid as starting materials, and its physicochemical properties were investigated using X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD) spectroscopy, scanning electron microscopy (SEM), energy dispersive analysis of X-ray (EDAX), transmission electron microscope (TEM), and electrochemical methods. The sample prepared displays a monoclinic structure with a space group of P2₁/n, and its surface is covered with a rough and porous carbon layer. In the voltage range of 3.0-4.3 V, the Li₃V₂(PO₄)₃ electrode displays a large reversible capacity, good rate capability and excellent cyclic stability at both 25 and 55 °C. The largest reversible capacity of 130 mAh g⁻¹ was obtained at 0.1C and 55 °C, nearly equivalent to the reversible cycling of two lithium ions per Li₃V₂(PO₄)₃ formula unit (133 mAh g⁻¹). It was found that the increase in total carbon content can improve the discharge performance of the Li₃V₂(PO₄)₃ electrode. In the voltage range of 3.0-4.8 V, the extraction and reinsertion of the third lithium ion in the carbon coated Li₃V₂(PO₄)₃ host are almost reversible, exhibiting a reversible capacity of 177 mAh g⁻¹ and good cyclic performance. The reasons for the excellent electrochemical performance of the carbon coated Li₃V₂(PO₄)₃ cathode material were also discussed.     

Effect of fluorine in the preparation of Li(Ni1/3Co1/3Mn1/3)O2 via hydroxide co-precipitation

Uniform and spherical Li(Ni_1/3Co_1/3Mn_1/3)O_(2−δ)F_δ powders were synthesized via NH₃ and F⁻ coordination hydroxide co-precipitation. The effect of F⁻ coordination agent on the morphology, structure and electrochemical properties of the Li(Ni_1/3Co_1/3Mn_1/3)O_(2−δ)F_δ were studied. The morphology, size, and distribution of (Ni_1/3Co_1/3Mn_1/3)(OH)_(2−δ)F_δ particle diameter were improved in a shorter reaction time through the addition of F⁻. The study suggested that the added F improves the layered characteristics of the lattice and the cyclic performance of Li(Ni_1/3Co_1/3Mn_1/3)O₂ in the voltage range of 2.8-4.6 V. The initial capacity of the Li(Ni_1/3Co_1/3Mn_1/3)O_1.96F_0.04 was 178 mAh g⁻¹, the maximum capacity was 186 mAh g⁻¹ and the capacity after 50 cycles was 179 mAh g⁻¹ in the voltage range of 2.8-4.6 V.     

Supercapacitive properties of a nanowire-structured MnO2 electrode in the gel electrolyte containing silica

Nanowire-structured MnO₂ active materials were prepared by a chemical precipitation method and their supercapacitive properties for use in the electrodes of supercapacitors were investigated by means of cyclic voltammetry in an aqueous gel electrolytes consisting of 1 M Na₂SO₄ and fumed silica (SiO₂). The MnO₂ electrode showed a maximum specific capacitance of 151 F g⁻¹ after 1000 cycles at 100 mV s⁻¹ when using the gel electrolyte containing 3 wt.% of SiO₂, which is higher than 121 F g⁻¹ obtained when using the 1 M Na₂SO₄ liquid electrolyte alone.     

Comparison of product selectivity during hydroprocessing of bitumen derived gas oil in the presence of NiMo/Al2O3 catalyst containing boron and phosphorus

A detailed experimental study was performed in a trickle-bed reactor using bitumen derived gas oil. The objective of this work was to compare the activity of NiMo/Al₂O₃ catalyst containing boron or phosphorus for the hydrotreating and mild hydrocracking of bitumen derived gas oil. Experiments were performed at the temperature and LHSV of 340-420 °C and 0.5-2 h⁻¹, respectively, using NiMo/Al₂O₃ catalysts containing 1.7 wt% boron or 2.7 wt% phosphorus. In the temperature range of 340-390 °C, higher nitrogen conversion was observed from boron containing catalyst than that from phosphorus containing catalyst whereas in the same temperature range, phosphorus containing catalyst gave higher relative removal of sulfur than boron containing catalyst. Phosphorus containing catalyst showed excellent hydrocracking and mild hydrocracking activities at all operating conditions. Higher naphtha yield and selectivity were obtained using phosphorus containing catalyst at all operating conditions. Maximum gasoline selectivity of ∼45 wt% was obtained at the temperature, pressure, and LHSV of 400 °C, 9.4 MPa and 0.5 h⁻¹, respectively, using catalyst containing 2.7 wt% phosphorus.     

Preparation and characterization of negative thermal expansion Sc2W3O12/Cu core-shell composite

A composite of Sc₂W₃O₁₂/Cu where Sc₂W₃O₁₂, the core, is coated by the Cu shell was synthesized using simple electroless plating method. As-prepared Sc₂W₃O₁₂/Cu composites were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectrometry (EDS) and thermomechanical analyzer (TMA) techniques. The study results show that the Pd-Sn activator was successfully formed on the surface of Sc₂W₃O₁₂ after the sensitization and activation. In the electroless plating process, Cu nanocrystals formed firstly, and then grew together to form a continuous coating. Sc₂W₃O₁₂/Cu core-shell composites exhibit a negative linear coefficient of thermal expansion CTE = −4.47 × 10⁻⁶ °C⁻¹ from room temperature to 200 °C.     

Polypyrrole and La1−xSrxMnO3 (0≤ x ≤0.4) composite electrodes for electroreduction of oxygen in alkaline medium

Composite G/PPy/PPy(La_1−xSr_xMnO₃)/PPy electrodes made of the perovskite La_1−xSr_xMnO₃ embedded into a polypyrrole (PPy) layer, sandwiched between two pure PPy films, electrodeposited on a graphite support were investigated for electrocatalysis of the oxygen reduction reaction (ORR). PPy and PPy(La_1−xSr_xMnO₃) (0≤ x ≤0.4) successive layers have been obtained on polished and pretreated graphite electrodes following sequential electrodeposition technique. The electrolytes used in the electrodeposition process were Ar saturated 0.1 mol dm⁻³ pyrrole (Py) plus 0.05 mol dm⁻³ K₂SO₄ with and without containing a suspension of 8.33 g L⁻¹ oxide powder. Films were characterized by XRD, SEM, linear sweep voltammetry, cyclic voltammetry (CV) and electrochemical impedance (EI) spectroscopy. Electrochemical investigations were carried out at pH 12 in a 0.5 mol dm⁻³ K₂SO₄ plus 5 mmol dm⁻³ KOH, under both oxygenated and deoxygenated conditions. Results indicate that the porosity of the PPy matrix is considerably enhanced in presence of oxide particles. Sr substitution is found to have little influence on the electrocatalytic activity of the composite electrode towards the ORR. However, the rate of oxygen reduction decreases with decreasing pH of the electrolyte from pH 12 to pH 6. It is noteworthy that in contrast to a non-composite electrode of the same oxide in film form, the composite electrode exhibits much better electrocatalytic activity for the ORR.     

Effect of synthesis condition on the structure and electrochemical properties of Li[Ni1/3Mn1/3Co1/3]O2 prepared by hydroxide co-precipitation method

The layered Li[Ni_1/3Co_1/3Mn_1/3]O₂ powder with good crystalline and spherical shape was prepared by hydroxide co-precipitation method. The effects of pH value, NH₄OH amount, calcination temperature and extra Li amount on the morphology, structure and electrochemical properties of the cathode material were investigated in detail. SEM results indicate that pH value affected both the morphology and the property of the cathode material, and the highest discharge capacity in the first cycle of 163 mAh g⁻¹ (2.8-4.3 V) was obtained at pH value was 12. On the contrary, the NH₄OH amount, which was used as a chelating agent, only affected the particle size distribution of the material. The calcination temperatures caused great difference in the structure and property of layered Li[Ni_1/3Co_1/3Mn_1/3]O₂, and the best electrochemical properties were obtained at the calcination temperature of 800 °C. Extra Li amount not only caused difference in the material structure, but also affected their electrochemical properties. With increasing Li amount, the lattice parameters (a and c) increased monotonously, and the highest first cycle coulombic efficiency (the ratio of discharge capacity to charge capacity in the first cycle) was obtained with the Li/M of 1.10. Therefore, the optimum synthetic conditions for the hydroxide co-precipitation reaction were: pH value was 12, NH₄OH amount was 0.36 mol L⁻¹, calcination temperature was 800 °C and the Li/M molar ratio was 1.10.     

Synthesis and properties of (BaxPb1−x)(Zn1/3Nb2/3)O3 relaxor ferroelectric ceramics using a reaction-sintering process

(Ba_xPb_1−x)(Zn_1/3Nb_2/3)O₃ (BPZN; x = 0.06–0.1) relaxor ferroelectric ceramics produced using a reaction-sintering process were investigated. Without any calcination involved, the mixture of raw materials was pressed and sintered directly. BPZN ceramics of 100% perovskite phase were obtained. Highly dense BPZN ceramics with a density higher than 98.5% of theoretical density could be obtained. Maximum dielectric constant K_max 13,500 (at 75 °C), 19,600 (at 50 °C) and 14,800 (at 28 °C) at 1 kHz could be obtained in 6BPZN, 8BPZN and 10BPZN, respectively. Dielectric maximum temperature (T_max) in BPZN ceramics via reaction-sintering process is lower than BPZN ceramics prepared via B-site precursor route.     

Decomposition of MgSiN2 in nitrogen atmosphere

Magnesium silicon nitride MgSiN₂ was prepared by direct nitridation of Si/Mg₂Si/Mg/Si₃N₄ powder compact in a temperature range 1350-1420 °C. The thermal stability examination showed that MgSiN₂ is stable up to 1400 °C at 0.1 MPa N₂ pressure. The activation energy of decomposition of MgSiN₂ calculated from the temperature dependence of mass loss in the range of 1400-1650 °C is ΔH = 501 kJ mol⁻¹. The time dependence and nitrogen pressure dependence of MgSiN₂ decomposition was also investigated at constant temperature. MgSiN₂ is stable at 1560 °C in 0.6 MPa nitrogen atmosphere. Using these experimental data together with the heat capacity published in a literature the Gibbs energy of formation of MgSiN₂ was calculated in a temperature range 25-2200 °C.