Effect of in‐office bleaching with 35% hydrogen peroxide with and without addition of calcium on the enamel surface

This study aimed to evaluate effectiveness and effects of bleaching with 35% hydrogen peroxide with and without calcium on color, micromorphology, and the replacement of calcium and phosphate on the enamel surface. Thirty bovine enamel blocks (5.0 × 5.0 mm) were placed into the following groups: G1: artificial saliva (control); G2: 35% hydrogen peroxide gel without calcium (Whiteness HP Maxx–FGM); and G3: 35% hydrogen peroxide gel with calcium (Whiteness HP Blue–FGM). Three color measurements were performed with a spectrophotometer: untreated (baseline), after performing staining, and after application of bleaching agents. Calcium deposition on the enamel was evaluated before and after the application of bleaching agents using energy‐dispersive X‐ray spectrometry. The enamel surface micromorphology was observed under scanning electron microscopy. The pH of each product was measured. The data were subjected to one‐factor analysis of variance (ANOVA), and any differences were analyzed using Tukey's test (P < 0.05). G3 showed greater variation in total color after the experiment than G2 and G1; there was no significant difference in calcium or phosphorus concentration before and after the experimental procedures; morphological changes were observed only in G2 and G3; and the pH values of the Whiteness HP Maxx and Whiteness HP Blue bleaching agents were 5.77 and 7.79, respectively. The 35% hydrogen peroxide with calcium showed greater bleaching potential, but the addition of calcium had no effect in terms of reducing morphological changes or increasing the calcium concentration on the enamel surface. Microsc. Res. Tech. 78:975–981, 2015. © 2015 Wiley Periodicals, Inc.     

Ultrastructural evaluation of enamel after dental bleaching associated with fluoride

This study evaluated the effects on human enamel after two bleaching procedures: with a fluoridated bleaching agent and with topical fluoride application postbleaching. It used 43 enamel blocks (3 mm(2) ) that were ground flat (600-2,000 grit) and polished with polishing paste (one and one-fourth). Specimens were randomly divided into three groups according to the bleaching procedure: (1) control group, (2) hydrogen peroxide 35% (HPF) and topical application of fluoride 1.23%, and (3) HP 38% (OP) with fluoride in its composition. Bleaching agents were used according to the manufacturer's instructions. Three methodologies were used: nanoindentation, to observe surface hardness and elastic modulus; atomic force microscopy, to observe surface roughness (R(a) - R(z)); and scanning electron microscopy, to observe the enamel surface effects. Group OP had a decrease in the elastic modulus after bleaching, which was recovered at 14 days. An increased roughness (R(a); 32%) was observed on group HPF and had an increased erosion on enamel surface (67%). It was concluded that topical application of fluoride, after using the nonfluoridated whitening agent, increased the roughness values and erosion of enamel.     

Shear bond strength and ultrastructural interface analysis of different adhesive systems to bleached dentin

Background: It remains unclear as to whether or not dental bleaching affects the bond strength of dentin/resin restoration. Purpose: To evaluated the bond strength of adhesive systems to dentin submitted to bleaching with 38% hydrogen peroxide (HP) activated by LED‐laser and to assess the adhesive/dentin interfaces by means of SEM. Study design: Sixty fragments of dentin (25 mm²) were included and divided into two groups: bleached and unbleached. HP was applied for 20 s and photoactivated for 45 s. Groups were subdivided according to the adhesive systems (n = 10): (1) two‐steps conventional system (Adper Single Bond), (2) two‐steps self‐etching system (Clearfil standard error (SE) Bond), and (3) one‐step self‐etching system (Prompt L‐Pop). The specimens received the Z250 resin and, after 24 h, were submitted to the bond strength test. Additional 30 dentin fragments (n = 5) received the same surface treatments and were prepared for SEM. Data were analyzed by ANOVA and Tukey's test (α = 0.05). Results: There was significant strength reduction in bleached group when compared to unbleached group (P < 0.05). Higher bond strength was observed for Prompt. Single Bond and Clearfil presented the smallest values when used in bleached dentin. SEM analysis of the unbleached specimens revealed long tags and uniform hybrid layer for all adhesives. In bleached dentin, Single Bond provided open tubules and with few tags, Clearfil determined the absence of tags and hybrid layer, and Prompt promoted a regular hybrid layer with some tags. Conclusions: Prompt promoted higher shear bond strength, regardless of the bleaching treatment and allowed the formation of a regular and fine hybrid layer with less deep tags, when compared to Single Bond and Clearfil. Microsc. Res. Tech., 2010. © 2010 Wiley‐Liss, Inc.     

Effect of in‐office bleaching agents on the surface roughness and morphology of different dental composites: An AFM study

The aim of this study was to evaluate, using atomic force microscopy, the effect of two different bleaching agents on the modification of dental composites materials. This modification will be judged by analyzing the variation of surface roughness and surface morphology of two different composites: one containing nanoparticles and other consisting of microhybrid resin. The bleaching was performed by using two different concentrations of hydrogen peroxide: HP Blue (20% hydrogen peroxide) and Whiteness HP Maxx (35% hydrogen peroxide). Disks of Esthet X and Filtek? Z350 composites were used. Atomic force microscopy was used for analyses of the same place of the sample before and after treatment. A total of 12 analyses were performed per group (n = 12). The samples were analyzed qualitatively by evaluating morphological changes in the images and quantitatively by using roughness parameters (Ra). Data were analyzed statistically using Kruskal–Wallis, Mann–Whitney, and Friedman tests (P < 0.05). Changes were observed both qualitatively and quantitatively only in the groups where Esthet X resin was used. The use of hydrogen peroxide bleaching agents caused changes only in the surface of microhybrid composites, with no changes being observed in the composite containing nanoparticles. Despite being even significant, these alterations are clinically slight and can be eliminated by polishing them. Microsc. Res. Tech. 76:481–485, 2013. © 2013 Wiley Periodicals, Inc.     

The effect of fluoride therapies on the morphology of bleached human dental enamel

The aim of this in vitro study was to evaluate qualitatively the surface morphology of enamel bleached with 35% hydrogen peroxide (HP) followed by application of fluoridated agents. Forty intact pre molars were randomly distributed into four groups (n = 10), treated as follows: Group I (control group) remained stored in artificial saliva at 37 °C, Group II - 35% HP; Group III - 35% HP + acidulated fluoride (1.23%) and Group IV - 35% HP + neutral fluoride (2%). The experimental groups received three applications of bleaching gel and after the last application all specimens were polished. This procedure was repeated after 7 and 14 days, and during the intervals of applications, the specimens were stored in artificial saliva at 37°C. Scanning electron microscopy (SEM) analysis showed superficial irregularities and porosities to varying degrees in bleached enamel compared to control group. Sample evaluation was made by attributing scores, and data were statistically analyzed using Kruskal-Wallis and Dunn tests (P < 0.05). SEM qualitative investigation demonstrated that 35% hydrogen peroxide affected human dental enamel morphology, producing porosities, depressions, and superficial irregularities at various degrees. These morphological changes were higher after the application of 1.23% acidulated fluoride gel.     

Dentin bond strength and nanoleakage of the adhesive interface after intracoronal bleaching

This study evaluated dentin bond strength (BS) and nanoleakage of non‐ and pre‐etched dentin immediately (T₀,), 7 days (T₇), and 14 days (T₁₄) after bleaching. Bovine incisors (150) were selected and half of them submitted to intrapulpal dentin etching (e). Non‐ and pre‐etched dentin were subjected to the following (n = 15): no bleaching/control (C); 35% carbamide peroxide (CP); 35% hydrogen peroxide (35% HP); 25% hydrogen peroxide (25% HP); and sodium perborate (SP). Bleaching agents were applied to the pulp chamber four times within a 72‐h interval. Afterwards, pulp chamber dentin was prepared for the BS test at different evaluation times (n = 5): T₀, T₇, and T₁₄. Composite blocks were built on pulp chamber and sectioned in slices. Slices were reduced to an hour‐glass shape with a cross‐sectional area of 0.8 mm² and submitted to microtensile BS test. Two additional specimens for each group were prepared for nanoleakage evaluation by transmission electron microscopy (TEM). Results were analyzed by ANOVA (two‐way) and Dunnett's test (p < .05). BS decreased immediately after intracoronal bleaching for both sound and pre‐etched dentin (p < .05). At T₁₄, the BS of non‐etched bleached dentin increased for all groups, whereas the pre‐etched SPe group presented BS similar to the Ce. Nanoleakage within the hybrid layer was perceptible immediately after bleaching, although a decrease in nanoleakage was observed for all groups at T₁₄. Adhesive restorations should be performed 7–14 days after bleaching, according to the bleaching agent used. Intracoronal bleaching should be performed preferably with sodium perborate if previous dentin etching is applied.     

Efficacy of calcium‐ and fluoride‐containing materials for the remineralization of primary teeth with early enamel lesion

The aim of the study was to determine the efficacy of different products containing fluoride, calcium and phosphate for enamel remineralization in eroded primary teeth. A total of 90 sound primary canine teeth were randomly divided into 5 groups of 18 teeth each: 1) control (polished enamel), 2) 5% DuraShield sodium fluoride varnish, 3) 500 ppm fluoridated toothpaste, 4) casein phosphopeptide‐amorphous calcium phosphate (CPP‐ACP) cream, and 5) Clinpro White varnish containing functionalized tri‐calcium phosphate (fTCP). Enamel microhardness (EMH) was measured in all samples before and after demineralization and after 28 days of remineralization. Also 8 samples in groups 2 to 5 and four samples of sound and demineralized enamel were examined with atomic force microscopy (AFM). All data were analyzed with one‐way ANOVA (p<0.05). Mean microhardness of demineralized enamel was significantly lower than in enamel at baseline (p<0.001). Remineralization significantly increased microharness in groups 2 to 5 compared to the control group (p<0.001). Percent EMH after remineralization with CPP‐ACP was significantly higher than after fTCP (p=0.029), toothpaste (p< 0.001) or fluoride varnish (p<0.001); however, there was no significant difference between toothpaste and fluoride varnish (p=0.062). Microhardness increased more after fTCP treatment than after treatment with sodium fluoride varnish (p<0.001) or fluoridated toothpaste (p=0.045). AFM images showed that enamel roughness decreased most after treatment with fTCP, followed by CPP‐ACP, toothpaste and fluoride varnish. The efficacy of CPP‐ACP cream for remineralizing eroded enamel was greater than fluoride toothpaste, fluoride varnish or fTCP varnish. Microsc. Res. Tech. 78:801–806, 2015. © 2015 Wiley Periodicals, Inc.     

Effects of prolonged use of over-the-counter bleaching agents on enamel: An in vitro study

This study evaluated the effects of four over-the-counter (OTC) bleaching products on the properties of enamel. Extracted human molars were randomly assigned into four groups (n = 5): PD: Poladay (SDI), WG: White Teeth Global (White Teeth Global), CW: Crest3DWhite (Procter & Gamble), and HS: HiSmile (HiSmile). The hydrogen peroxide (H₂O₂) content in each product was analyzed via titration. Twenty teeth were sectioned into quarters, embedded in epoxy resin, and polished. Each quarter-tooth surface was treated with one of the four beaching times: T0: control/no-bleaching, T14: 14 days, T28: 28 days, and T56: 56 days. Materials were applied to enamel surfaces as recommended. Enamel surfaces were examined for ultramicrohardness (UMH), elastic modulus (EM), superficial roughness (Sa), and scanning electron microscopy (SEM). Ten additional teeth were used to evaluate color and degree of demineralization (DD) (n = 5). Data were statistically tested by two-way ANOVA and Tukey's tests (α = 5%). Enamel surfaces treated with PD and WG presented UMH values significantly lower than the controls (p < .05). Elastic modulus (E) was significantly reduced at T14 and T28 for PD, and at T14 for HS (p < .05). A significant increase in Sa was observed for CW at T14 (p < .05). Color changes were observed in the PD and WG groups. Additionally, DD analysis showed significant demineralization at T56 for CW. Overall, more evident morphological alterations were observed for bleaching products with higher concentrations of H₂O₂ (p < .05), PD, and WG. Over-the-counter bleaching products containing H₂O₂ can significantly alter enamel properties, especially when application time is extended.     

Influence of a short‐time antioxidant application on the dentin bond strength after intracoronal bleaching

This study evaluated the effects of an antioxidant application on the compromised bond strength of an adhesive to dentin bleached with 35% hydrogen peroxide. The dentin surfaces of the pulp chambers of 70 human third molars were ground, and the specimens were assigned randomly into seven groups, as follows: (a) control (unbleached); (b) bleached for 45 min, bonded immediately; (c) bleached for 45 min, treated with sodium ascorbate (SA) for 2 min, and bonded; (d) bleached for 45 min, bonded after 2 weeks; (e) bleached for 12 days, bonded immediately; (f) bleached for 12 days, treated with SA for 10 min, and bonded; and (g) bleached for 12 days, bonded after 2 weeks. In each group, the multimode adhesive was applied in etch‐and‐rinse and self‐etch modes. The dentin surfaces were covered with a resin‐based composite, and the bonded specimens were sectioned to produce composite–dentin sticks. The sticks were attached to a testing machine and subjected to a tensile force, and the representative specimens were examined via scanning electron microscopy. The bond strength was not affected by the application period of the bleaching agent. Both bleaching treatments significantly reduced the bond strength to the dentin in the self‐etch or etch‐and‐rinse mode when compared with the control group. The bond strengths returned to normal levels with the SA applications or by waiting 2 weeks, regardless of the application period of the bleaching gel. The adhesive revealed a higher bond strength in the etch‐and‐rinse mode than in the self‐etch mode.     

Antibacterial efficacy and remineralization capacity of glycyrrhizic acid added casein phosphopeptide‐amorphous calcium phosphate

The aim was to evaluate remineralization capacity and antibacterial efficiency of Tooth Mousse and various amounts of glycyrrhizic acid added Tooth Mousse on primary tooth enamel. Three groups were formed; Group 1 (CPP‐ACP), Group 2 (CPP‐ACP + 5% glycyrrhizic acid), and Group 3 (CPP‐ACP + 10% glycyrrhizic acid) in order to evaluate remineralization capacity. Enamel samples were immersed in demineralization solution and then remineralization agents were applied. Surface microhardness and SEM analyses were performed at the beginning, after demineralization and remineralization. For antibacterial tests, four groups were formed; Group 1, Group 2 and Group 3 and Group 4 (control). Biofilms were then exposed to 10% sucrose eight times per day for 7 days. After biofilm growth period, samples were treated with materials to evaluate antibacterial efficiency except control group. After application of materials, samples were incubated 2 more days at 37°C and at the end of this period, absorbance values of biofilms were determined and data were analyzed. An increase in microhardness values was Group 2 > Group 3 > Group 1, respectively, but there were no significant differences. After remineralization, microhardness values showed significant increases when compared to demineralized groups, but there was no significant difference. All groups showed decreased absorbance value of biofilm when compared with control group but they were insignificant. It was observed that both in Group 2 and Group 3, glycyrrhizic acid did not have a negative effect on remineralization and although they have an increase, it was insignificant. Although glycyrrhizic acid added CPP‐ACP groups showed increased antibacterial activity, they were not statistically significant.     

Atomic force microscopic analysis of hydrogen peroxide bleached kraft northern black spruce fibres

Hydrogen peroxide is a potent, relatively inexpensive oxidant that chemically degrades chromophoric components in pulps and textiles. Oxidation of cellulose is a byproduct of this process step that decreases the tensile strength of individual fibres. The residence time of pulp in the bleaching reactor must be optimized to achieve the desired brightness and minimizing fibre degradation. To evaluate the impact of peroxide bleaching at the microfibrillar level, a single black spruce tree was chosen and kraft pulped. Peroxide bleaching was conducted via benchtop polyethylene bag bleaching in a temperature-controlled waterbath. Atomic force microscopy (AFM) topographical images acquired before and after the bleaching step show dramatic changes in fibre structure consistent with delignification and defects in the surface topography. This was further verified by X-ray work at Brookhaven National Laboratory, NY, U.S.A.     

Hardness,friction and wear studies on hydrogen peroxide treated bovine teeth

A possible problem with peroxide based tooth whitening is the loss of tooth hardness and higher susceptibility to enamel surface wear. This study focussed on the effects of acidic and neutral hydrogen peroxide solutions (6 and 30% w/v) on hardness, friction and wear of bovine enamel. The experiments showed that treatments with neutral peroxide reduced wear and the loss of enamel hardness up to 2–3 times. In addition, further investigation on remineralisation with amorphous calcium phosphate showed an increase in hardness after treatment. Friction coefficients of teeth against steel varied between 0.25 and 0.7, and wear coefficients ranged between ≈10⁻⁶ and 10⁻⁷ mm³/N m. From this study, it is possible to explain the wear behaviour of HP treated enamel with changes in hardness.     

The effects of intrinsic and extrinsic acids on nanofilled and bulk fill resin composites: Roughness,surface hardness,and scanning electron microscopy analysis

The objective of this study was to examine the effects of extrinsic or intrinsic acids on nanofilled and bulk fill resin materials in vitro. A total of 90 disks were prepared using dental restorative material (Filtek Z350XT, GrandioSO, Filtek Bulk Fill, X‐tra fil). Thirty disks of each material were sub‐divided into three groups (n = 10) that were immersed for 7 days in deionized water (DW), 5% citric acid (CA—pH 2.1), or 0.1% hydrochloric acid (HCl—pH = 1.2). Surface hardness and roughness (stylus profilometer by R_a parameter) analysis were performed before and after immersion. Morphological changes were evaluated by scanning electron microscopy. The data were analyzed by two‐way ANOVA and Tukey's test (α = 0.05). All tested materials did not show significant differences in the effects of the DW, CA, or HCl solutions on surface roughness (p = .368). Likewise, the hardness loss was not affected by the solutions tested (p = .646), but there was a difference in the resin type (p = .002). Filtek Bulk Fill resin hardness was less affected, while Filtek Z350XT and GrandioSO presented the most hardness loss after 7 days of solution immersion. In terms of this experimental study, the results demonstrate the effectiveness of the mechanical properties (roughness and hardness surface) of nanofilled and bulk fill resin materials to resist erosion from extrinsic and intrinsic acids, therefore being potential candidates for dental applications.     

Remineralization effects of self-assembling peptide P11-4 associated with three materials on early enamel carious lesions: An in vitro study

The aim of this study was to assess the remineralization of enamel caries lesions using the self-assembling peptide P₁₁-4 associated with different materials. Artificial early enamel lesions were prepared on 154 primary teeth. The samples were randomly divided into eight groups: (1) control, (2) P₁₁-4, (3) fluoridate toothpaste (FT), (4) P₁₁-4 + FT, (5) casein phosphopeptide–amorphous calcium phosphate (CPP–ACP), (6) P₁₁-4 + CPP–ACP, (7) fluoridate bioactive glass toothpaste (BT), and (8) P₁₁-4 + BT. The surface enamel microhardness (EMH) and energy-dispersive X-ray spectroscopy (EDS) of the teeth were then measured at the baseline, after demineralization, and after 28 days of remineralization. The enamel surfaces were assessed by field emission scanning electron microscopy (FESEM) and atomic force microscopy (AFM). The data were analyzed with one-way analysis of variance (ANOVA) (p < .05). EMH after demineralization was significantly lower than the baseline value (p < .001). The interventions led to an enhanced percentage of EMH recovery (%REMH), which was higher in Groups 6 and 7. There was no significant difference between Groups 3 and 4. Groups 1 and 2 had the lowest %REMH. The mean calcium/phosphate weight percentage ratio of P₁₁-4 was significantly lower than the others (p < .001). The FESEM and AFM images revealed mineral deposition on the eroded enamel and reductions in surface roughness in Groups 5 and 7.     

Evaluation of roughness, hardness, and strength of AA 6061 molds for manufacturing polymeric microdevices

In the manufacturing of polymeric microfluidic devices, micro-molds play a key role because they determine not only the manufacturing cost but also the quality of the molded parts. Recently, a high-quality aluminum alloy 6061 (AA6061) mold with fine features less than its grain size has been fabricated economically by a hot embossing technique. However, temperature cycling during hot embossing process in mold manufacturing reduces significantly the original tensile strength and hardness of the AA6061-T6 alloy substrate, which is not desirable. In this study, a tempering process is carried out to recover the tensile strength and hardness of the embossed mold. To evaluate the changes of these properties, surface roughness, tensile strength, and hardness values were measured in each stage: (1) before hot embossing, (2) after hot embossing, and (3) tempering to T4 and tempering to T6. The results obtained demonstrate that the original strengths and hardness can be fully recovered by a post-tempering process after hot embossing, but with an increase in surface roughness. Moreover, accelerated testing was carried out to evaluate the changes in hardness and roughness of AA6061-T4 and T6 molds under the typical hot embossing temperature cycles of manufacturing polymeric devices. The results obtained indicate that these temperature cycles have only a minor effect on the roughness of both T4 and T6 molds and will increase the hardness of T4 molds to T6 temper, and have negligible effect on the hardness of a T6 temper mold.     

An improved strip FRAP method for estimating diffusion coefficients: correcting for the degree of photobleaching

Fluorescence recovery after photobleaching is a widely established method for the estimation of diffusion coefficients, strip bleaching with an associated recovery curve analysis being one of the simplest techniques. However, its implementation requires near 100% bleaching in the region of interest with negligible fluorescence loss outside, both constraints being hard to achieve concomitantly for fast diffusing molecules. We demonstrate that when these requirements are not met there is an error in the estimation of the diffusion coefficient D, either an under‐ or overestimation depending on which assumption is violated the most. We propose a simple modification to the recovery curve analysis incorporating the concept of the relative bleached mass m giving a revised recovery time parametrization τ=m²w²/4πD for a strip of width w. This modified model removes the requirement of 100% bleaching in the region of interest and allows for limited diffusion of the fluorophore during bleaching. We validate our method by estimating the (volume) diffusion coefficient of FITC‐labelled IgG in 60% glycerol solution, D= 4.09 ± 0.21 μm² s^?1 , and the (surface) diffusion coefficient of a green‐fluorescent protein‐tagged class I MHC protein expressed at the surface of a human B cell line, D= 0.32 ± 0.03 μm² s^?1 for a population of cells.     

Dentin erosion by whitening mouthwash associated to toothbrushing abrasion: A focus variation 3D scanning microscopy study

The aim of this study was to determine the erosive potential of hydrogen peroxide (HP) containing mouthwash on dentin assessed by Focus variation three‐dimensional (3D) microscopy. Twenty dentin slabs were selected and randomly allocated into two groups (n = 10): DW—Distilled water (pH = 7.27) and HP—1.5% (pH = 3.78). Each specimen was cyclically demineralized (4 × 60 s/day, 10 days) with HP or DW and brushed 3×/day (200 g, 150 strokes—toothpaste with 1,450 ppmF as NaF). Between the challenges, the specimens were exposed to artificial saliva. Afterward, dentin loss was analyzed using focus variation 3D microscopy, and the data were submitted to unpaired t‐test (α = 0.05). Statistically significant difference was found between the mean wear rate (μm, ±SD) of HP (1.98 ± 0.51) and DW (1.45 ± 0.39). The results suggest that the use of HP‐containing mouthwash associated to brushing may increase the risk of tissue loss and focus variation 3D microscopy may be used as a technique for quantifying dental wear. Microsc. Res. Tech. 76:904–908, 2013. © 2013 Wiley Periodicals, Inc.     

Enamel alteration following tooth bleaching and remineralization

The purpose of this study was to compare the effects of professional tooth whitening agents containing highly concentrated hydrogen peroxide (with and without laser activation), on the enamel surface; and the potential of four different toothpastes to remineralize any alterations. The study was performed on 50 human molars, divided in two groups: treated with Opalescence^® Boost and Mirawhite^® Laser Bleaching. Furthermore, each group was divided into five subgroups, a control one and 4 subgroups remineralized with: Mirasensitive^® hap+, Mirawhite^® Gelle?, GC Tooth Mousse? and Mirafluor^® C. The samples were analysed by SEM/3D‐SEM‐micrographs, SEM/EDX‐qualitative analysis and SEM/EDX‐semiquantitative analysis. The microphotographs show that both types of bleaching cause alterations: emphasized perikymata, erosions, loss of interprizmatic substance; the laser treatment is more aggressive and loss of integrity of the enamel is determined by shearing off the enamel rods. In all samples undergoing remineralization deposits were observed, those of toothpastes based on calcium phosphate technologies seem to merge with each other and cover almost the entire surface of the enamel. Loss of integrity and minerals were detected only in the line‐scans of the sample remineralized with GC Tooth Mousse?. The semiquantitative EDX analysis of individual elements in the surface layer of the enamel indicates that during tooth‐bleaching with HP statistically significant loss of Na and Mg occurs, whereas the bleaching in combination with a laser leads to statistically significant loss of Ca and P. The results undoubtedly confirm that teeth whitening procedures lead to enamel alterations. In this context, it must be noted that laser bleaching is more aggressive for dental substances. However, these changes are reversible and can be repaired by application of remineralization toothpastes.     

Effects of Galla chinensis on the surface topography of initial enamel carious lesion: an atomic force microscopy study

To investigate the effect of Galla chinensis on the surface topography of initial enamel carious lesion, atomic force microscope (AFM) was used, and it was a new AFM application in enamel de‐/remineralization research. Bovine sound enamel slabs were demineralized to produce initial carious lesion in vitro. Then, the lesions were exposed to a pH‐cycling regime for 12 days. Each daily cycle included 4×1 min applications with one of three treatments: negative control group: deionized water; positive control group: 1 g/L aqueous solutions of NaF; experimental group: 4 g/L aqueous solutions of G. chinensis extract (GCE). The surface topography and roughness were investigated on the enamel slabs before and after pH‐cycling by AFM. 3D AFM images revealed the surface topographical changes of GCE‐treated enamel. Significant difference existed before and after the pH‐cycling among the groups. AFM offers a powerful tool for enamel de‐/remineralization research. The surface roughness results provide the evidences to remineralization of carious lesion, and indicate the potential of G. chinensis in promoting the remineralization. G. chinensis may become one more promising agent for caries prevention. SCANNING 31: 195–203, 2009. © 2010 Wiley Periodicals, Inc.