制备方法对V_2O_5-WO_3/TiO_2选择性催化还原催化剂性能的影响

采用共沉淀法、溶胶-凝胶法和浸渍法制备了V2O5质量分数4%和WO3质量分数6%的V2O5-WO3/TiO2选择性催化还原催化剂,对比了3种方法制备的催化剂选择性催化还原NO性能。采用X射线衍射、热重、N2吸附-脱附和程序升温还原等对制备的V2O5-WO3/Ti O2催化剂的结构和性质进行表征,结果表明,共沉淀法制备的V2O5-WO3/TiO2催化剂具有更好的选择性催化还原NO活性和更大的比表面积,影响共沉淀法选择性催化还原NO活性的主要因素是催化剂的热稳定性、表面羟基数量、比表面积、粒径分布以及V、W与Ti之间的内在作用。     

TiO2-SiO2复合氧化物载体及其加氢脱硫催化剂

分别采用溶胶-凝胶法和共沉淀法制备了TiO2-SiO2复合氧化物,并以此复合氧化物为载体制备了加氢脱硫催化剂.采用氮气恒温吸附脱附、X射线衍射、傅立叶变换红外光谱(FT-IR)和NH3程序升温脱附实验(NH3-TPD)对TiO2-SiO2复合氧化物及其催化剂进行表征,并考察催化剂的加氢脱硫性能.结果表明,TiO2经SiO2复合改性后,其热稳定性和晶相稳定性得到了提高.溶胶-凝胶法与共沉淀法相比,能使Ti物种和Si物种混合得更均匀,从而有利于制得具有较大比表面积和孔容的TiO2-SiO2复合氧化物.Ti含量增加,复合氧化物中Ti的分散度会降低.TiO2-SiO2复合氧化物中以Lewis酸中心为主,共沉淀法制备的复合氧化物比溶胶-凝胶法制备的复合氧化物具有更多的酸性中心.具有较大比表面积和较高酸性的催化剂对模型化合物噻吩和锦西重油催化裂化柴油的加氢脱硫性能较高.     

以偏钛酸为原料的催化剂的脱硝性能研究

以偏钛酸为原料通过浸渍法和固相物质的热分解法来制备以NH3为还原剂选择性催化还原NOx的催化剂V2O5-WO3/TiO2。着重考察催化剂组成、NH3/NO摩尔比和模拟烟气中O2浓度对催化剂脱硝性能的影响。催化剂的脱硝性能测试结果表明催化剂V2O5(1.2%)-WO3(8.8%)/TiO2具有较高的催化活性和较宽的活性温度窗口,NO的转化率最高可达98.77%。综合考虑NH3逃逸、设备腐蚀和环境问题,NH3/NO摩尔比控制在1.2以内比较合适;富氧条件对脱硝催化反应的进行更有利。     

V_2O_5-WO_3/TiO_2催化剂的制备

采用工业钛白粉作为烟气脱硝催化剂的载体原料,通过添加助剂M对其改性,研制出了一种V2O5-WO3/Ti O2烟气脱硝催化剂,并确定助剂M的最佳量为质量分数10%;同时考察了焙烧温度对该催化剂比表面积及脱硝性能的影响,确定了最佳焙烧温度为500℃;最佳活性组分钒含量为质量分数1.5%,稳定助剂钨含量为质量分数8%的催化剂性能最好。     

沉淀pH值对TiO_2-SiO_2负载催化剂催化还原NO性能的影响

采用共沉淀法,在不同pH值下制备了3种TiO2-SiO2(TS)复合氧化物,采用BET、XRD、NH3-TPD和FTIR等方法对样品进行了表征;并以3种TS为载体,负载CuO、Cr2O3和CeO2活性组分,考察了不同Cu-Cr-Ce/TS催化剂在140～220℃NH3选择性催化还原NO的性能。结果表明,以pH值10～11的TS载体制备的Cu-Cr-Ce/TS催化剂具有最优的低温活性,这是由于该载体具有较大的比表面积和更多弱酸中心,能吸附大量易于与NO反应的氨。     

焙烧温度对Pd-Pt/TiO_2-SiO_2-Al_2O_3加氢脱芳影响

采用改进的溶胶-凝胶法以不同物质的量配比的Ti、Si、Al制备成TiO2-SiO2-Al2O3复合载体,在不同温度下焙烧并对其进行BET、XRD表征。BET结果表明,随焙烧温度的升高,TiO2-SiO2-Al2O3复合载体的比表面积减小,孔体积和平均孔径逐渐增加。XRD结果表明,复合载体中TiO2以锐钛矿晶型存在,SiO2和Al2O3在TiO2上高度分散;锐钛矿特征峰随钛含量增大逐渐增强。考察焙烧温度对Pd-Pt/TiO2-SiO2-Al2O3催化剂的加氢脱芳性能影响。     

MgO修饰的V2O5-MoO3/TiO2低温SCR催化剂

V系催化剂具有良好的抗中毒能力,广泛应用于燃煤电厂、工业锅炉烟气(固定源)和车辆尾气(移动源)脱硝领域.本文采用水热法制备了V2O5-MoO3/TiO2催化剂,并通过挤出成型得到蜂窝式V2O5-MoO3/TiO2催化剂,通过与共混法相比,发现采用水热法表现出来的较高的低温SCR活性,并研究了MgO的掺杂对V2O5-MoO3/TiO2催化剂性能的影响,发现MgO的掺杂能够降低SO2的转化率.并通过表征发现采用水热反应法得到的V2O5-MoO3/TiO2催化剂能使活性组分高度分散于TiO2载体表面上,具有较高的比表面积,从而使催化剂表现出最佳的低温活性,同时MgO修饰的V2O5-MoO3/TiO2催化剂的抗硫抗水性以及抗碱金属中毒性也做出了研究.     

V2O5/AC催化剂吸附NH3及其选择性还原脱硝活性

在不同活性焦(Activated Coke, AC)载体上以等体积浸渍法负载V2O5,制备出一系列V2O5/AC催化剂. 通过NH3暂态响应实验和NH3穿透时间实验考察了在200℃下V2O5/AC的表面积、灰分、表面官能团和V2O5对NH3的吸附量及NO的选择性催化还原活性的影响. 结果表明,对于载体未经硝酸处理的催化剂,NH3的吸附位主要是V2O5(参与脱硝反应的NH3的吸附量与催化剂上V2O5负载量的比值为1:5),活性焦及其中的灰分对NH3的吸附量很小;硝酸处理在活性焦表面引入的含氧和含氮酸性官能团对参与脱硝反应的NH3的吸附量是V2O5上吸附量的1.3倍,这些官能团不影响V2O5对NH3的吸附;活性焦上吸附的NH3的脱硝活性很低,但可迁移至V2O5上参与脱硝.     

Au-Pd/TiO2-Al2O3催化剂的加氢脱硫性能研究

采用溶胶凝胶(sol-ge1)、共沉淀(CP)和沉积沉淀(DP)法制备了介孔TiO2-Al2O3复合载体(简称复合载体);以噻吩加氢脱硫(HDS)为探针反应,考察了复合载体制备条件对负载型Au-Pd催化剂噻吩HDS反应性能的影响;并采用X射线衍射进行表征.结果表明,不同温度焙烧的TiO2一Al2O3复合载体都具有介孔结构,其中773 K焙烧制得的TiO2一Al2O3复合载体的比表面积和孔容较大,B酸中心较多;以乙醇还原的Au-Pd/TiO2-Al2O3催化剂的加氢脱硫活性较好.乙醇还原的Au-Pd/TiO2-Al2O3催化剂中Au-Pd之间及活性组分与载体之间的相互作用较强,形成AuxPdy合金的晶粒较小,活性组分的分散度和活性表面积较大,反应活化能较低,这些均有利于催化剂活性的提高.     

载体对V_2O_5-MoO_3/TiO_2催化剂表面性质及其选择性催化还原脱硝性能的影响

采用比表面积分别为101.86 m2·g-1(A)、86.37 m2·g-1(B)和7.78(C)m2·g-1(C)的TiO_2载体,通过分步浸渍法制备V2O5-Mo O3/TiO_2(A,B,C)选择性催化还原脱硝催化剂。在空速为10 000 h-1和氨氮体积比1.0条件下,以TiO_2(A)与TiO_2(B)为载体制备的催化剂脱硝活性在反应温度窗口(350~450)℃超过90%,且具有良好的高温抗硫中毒性能和相对较小的氨气氧化率。而以TiO_2(C)为载体制备的脱硝催化剂活性温度窗口窄,在350℃时获得的最高脱硝活性仅为73%,且对NH3的氧化作用较强。利用X射线衍射、低温N2吸附-脱附、紫外-可见漫反射光谱、H2程序升温还原和NH3程序升温脱附等对载体和催化剂进行表征。结果表明,活性组分V2O5在载体TiO_2(A)上分散性良好,主要以孤立态钒氧物种形式存在,因此,以TiO_2(A)为载体制备的催化剂比表面积、氧化还原性和表面酸性等性能更优。     

Na2O-Al2O3-Fe2O3系烧结过程中铝、铁的反应行为

以Al2O3, Fe2O3和Na2CO3为原料,对Na2O-Al2O3-Fe2O3系烧结过程中的反应行为进行了详细研究. 基于溶出率与时间、温度的关系,证明Na2O×Al2O3和Na2O×Fe2O3的生成反应动力学都服从Zhuralev-Lesokin-Tempelman模型,表观活化能分别为186.59和80.92 kJ/mol,表明Na2O×Fe2O3比Na2O×Al2O3在动力学上更易形成;Al2O3易与Na2O×Fe2O3反应形成Na2O×Al2O3和Fe2O3,在1273 K烧结30 min,所得熟料Al2O3溶出率达98.51%;Fe2O3对Na2O×Al2O3的形成有双重作用,在1273 K下可加速Na2O×Al2O3的形成,超过1323 K,促使Na2O×Al2O3分解成Na2O和b-Al2O3,且随着温度升高或时间延长,分解程度增高,从而导致熟料中Al2O3溶出率显著降低.     

Properties of RO-Y2O3-Al2O3-SiO2 glasses

The coefficient of linear expansion, glass-transition temperature, temperature at the orset of deformation (strain point), density. Young modulus, microhardness, crystallizability, and contact angle are studied as a function of the composition in RO–Y₂O₃–Al₂O₃–SiO₂ (R=Ca and/or Mg) glass systems. The composition ranges for glasses (with strain point >900°C and coefficient of linear expansion of (32–45)×10^–7°C^–1) that can be used for soldering silicon-nitride ceramics were established.Translated from Steklo i Keramika, No. 12, pp. 5–7, December, 1996     

Phase equilibrium in binary La2O3-Dy2O3 and ternary CeO2-La2O3-Dy2O3 systems

Cerium oxide doped with oxides of rare earth elements is a multifunctional material, a wide range of uses which is associated with its unique physicochemical properties. Phase diagrams of multicomponent systems are the physicochemical basis for the creation of new materials with improved characteristics.In this work, phase equilibria in ternary CeO₂–La₂O₃–Dy₂O₃ and binary La₂O₃–Dy₂O₃ systems in the whole concentration range were studied. No new phases have been identified in these systems. An isothermal section of the phase diagram of the CeO₂–La₂O₃–Dy₂O₃ system at a temperature of 1500 °С is constructed. No new phases have been detected in the system. It was found that in the studied ternary system solid solutions are formed on the basis of (F) modification of CeO₂ with structure of fluorite type, monoclinic (B), cubic (C) and hexagonal (A) modifications of Ln₂O₃.In the La₂O₃–Dy₂O₃ binary system (1500–1100 °С) three types of solid solutions are formed: based on hexagonal modification A-La₂O₃, monoclinic modification B-Dy₂O₃ and cubic modification C-Dy₂O₃ separated by two-phase fields (A+B) and (B+C), respectively. The boundaries of the regions of homogeneity of solid solutions based on A-La₂O₃ are determined by compositions containing 35–40, 20–25, 15–20 mol% Dy₂O₃ at 1500, 1250, 1100 °C, respectively. From the obtained data it follows that the solubility of Dy₂O₃ in the hexagonal modification of lanthanum oxide is 39 mol% at 1500 °C, 23 mol. % at 1250 °C and 16 mol% at 1100 °C. The limits of existence of solid solutions based on monoclinic B-modification are determined by compositions containing 30–35, 65–60 (1250 °С), 35–40, 55–60 (1100 °С) 40–45, 70–75 (1500 °C) mol% Dy₂O₃.In the studied system, with a decrease in temperature from 1500° to 1100°C, there is a decrease in the solubility of La₂O₃ in the crystal lattice of cubic solid solutions of C-type from 16 to 10 mol%.     

钕-铝系稀土色料的研制

通过钕-铝系列色料合成实验,分析不同配比及不同矿化剂等对色料呈色效果的影响,确定最佳工艺方法。对实验结果进行XRD及色度分析,确定其主晶相为钕酸铝,试样的明度均在70以上,色彩鲜艳亮丽。     

Fe2O3-MnO-Cr2O3-La2O3系统紫色颜料的制备及表征

采用溶胶均匀共沉淀法于低温下合成了含少量稀土氧化物La2O3的紫色颜料，并采用颜色测定、SEM、XRD等手段对颜料的颜色、检度及结晶构造等进行了表征。     

3-二氯乙酰基-2-甲基-2-乙基-1,3-噁唑烷的合成研究

以w(NaOH) =33%水溶液为催化剂、乙醇胺、丁酮和二氯乙酰氯为原料 ,一步法合成了3 二氯乙酰基 2 甲基 2 乙基 1,3 口恶唑烷。采用正交实验设计获得最佳反应条件 :三氯甲烷做溶剂 ,反应温度 - 4～ 4℃ ,反应搅拌时间 1h ,产物收率 78 6 %。产品经红外光谱、核磁共振和元素分析确证。     

2,2,3-三氯-3-苯基-3-(3-甲基苯甲酰基)丙腈的合成研究

以苯甲酰氯、四氯化碳、间甲基苯甲酰氰为原料,合成了标题化合物。重点考察了氰化过程中不同原料配比、反应温度、时间、溶剂和催化剂用量对收率的影响。实验结果表明,其最佳反应条件为:n(1,1,2-三氯-2-苯基乙烯)∶n(3-甲基苯甲酰氰)=1∶1.2,二氯甲烷为反应溶剂,3 mmol催化剂三乙胺,室温反应5 h,总收率达80.6%。     

Polycrystalline In2O3 and In2O3/Y2O3 photoanodes

Single crystal In₂O₃ shows promise as a photoanode for the decomposition of water. Because of various difficulties in the preparation of the single crystal material, two simple techniques were developed for the preparation of polycrystalline In₂O₃ anodes. One method involves the thermal decomposition of the nitrate while the other utilizes the chemical vapour deposition technique. Voltammograms and photoresponse spectra of these anodes are compared to the single crystal material. Among other observations, it is noted that the quantum efficiencies of the thermally decomposed films are comparable to the single crystal material. It is also shown that the on-set potential can be shifted to more negative values by forming the mixed oxide In₂O₃/Y₂O₃.     

Separation of Phases by Spinodal Decomposition in the Systems Al2O3−Cr2O3 and Al2O3−Cr2O3−Fe2O3

Separation of phases was investigated in the hexagonal (rhombohedral) systems Al₂O₃−Cr₂O₃ and Al₂O₃−Cr₂O₃−Fe₂O₃. The binary system shows a miscibility gap with a T_c of 950°C; the miscibility gap for the ternary system was determined for a constant Cr₂O₃ content of 16.6 mol%. Dark field transmission electron microscopy of solid solutions annealed within the miscibility gap showed dark and light lamellas ∼50 to 200 Å thick. X-ray diffraction results for the solid solutions in the ternary system indicated that, in the early stages of annealing, broadening occurred only on (hkl) reflections where l≠0. There was no major change in the X-ray diffraction patterns of the annealed solid solutions in the binary system. Electron diffraction results indicated, however, that phase separation in both systems proceeded in the [001] direction. Solid solutions in the binary system separated very slowly; the separation could be enhanced hydrothermally. The mechanism of the separation of phases in both systems is spinodal and proceeds as follows: solid solution→intermediate modulated phase→equilibrium phases.     

Bi_2O_3-B_2O_3-WO_3系统微晶玻璃的制备

采用熔融法制备了0.97[x Bi2O3(1-x)B2O3]·0.03WO3(0.25≤x≤O.75)基础玻璃,通过差热分析确定玻璃的特征温度,经热处理制备微晶玻璃.结果表明所制备的玻璃中只有x =0.67和x=0.60两个组成经热处理生成了微晶玻璃,颜色为乳黄色,晶相分别为BiO2和Bi2WO6,在扫描电镜下观察两种晶体的形貌均为颗粒状,晶粒尺寸在0.8～1.0μm.该体系玻璃的密度较大而硬度较小,但热处理后的微晶玻璃的密度和硬度均大于处理前的基础玻璃.