负载型活性炭脱硫（H2S）的试验研究

进行了活性炭与氧化锌混合制得的脱硫剂用于脱除硫化氢的试验。结果表明，活性炭与氧化锌混合制得的脱硫剂具有较好的脱硫性能，其脱硫效率高于纯活性炭并且活性炭与氧化锌直接加水混合、过滤、干燥后制得的脱硫剂Ⅰ的脱硫效率高于活性炭与水蒸湿后与氧化锌混合的脱硫剂Ⅱ的脱硫效率。     

吸附法脱除烟气中二氧化硫的实验研究

采用改性的活性炭、沸石、累托石和粉煤灰作为固体吸附剂,研究了吸附法脱除模拟烟气中低浓度二氧化硫的可行性,比较了几种固体吸附剂的脱硫效果.研究结果认为4种固体吸附剂在吸附模拟烟气中SO2的吸附能力顺序为:活性炭＞粉煤灰＞累托石＞沸石,其中最佳吸附效果的是活性炭,其最大脱硫率可达98.71%,平均脱硫率也可达到66.58%.探索了改性活性炭脱除烟气中低浓度二氧化硫的影响因素,实验表明:空速对活性炭脱硫效果的影响较大.随着空速的增加,停留时间变短,在同样累计通气时刻,脱硫率下降;低温吸附时,随吸附温度升高,吸附量降低;但在高温出现化学反应吸附时,吸附温度高则反应速度快,脱硫效果好;此外,硝酸浸泡时间越长,活性炭吸附脱硫效果越好.     

不同生物质活性炭脱除烟气中SO_2/NO_x的实验研究

利用锯末、麦秸、麦秸掺10%煤3种生物质颗粒制取的活性炭,根据比表面积、孔径分布、孔容、微孔结构、碱金属含量等特征参数讨论了活性炭品质。利用立式固定床管式炉系统进行了活性炭颗粒的烟气脱硫脱氮实验,研究了不同的活性炭原材料、工作温度对联合脱硫脱氮性能的影响,对脱除机理进行了分析。通过综合比较分析表明:秸秆加煤材料的活性炭在较长的时间里维持脱硫效率95%以上和脱氮效率85%以上;其在工作温度较低(70℃)时以物理吸附为主,在较高的工作温度(130℃)以化学吸附为主,均具有良好的吸附性能。     

吸附法脱除烟气中二氧化硫的实验研究

采用改性的活性炭、沸石、累托石和粉煤灰作为固体吸附剂,研究了吸附法脱除模拟烟气中低浓度二氧化硫的可行性,比较了几种固体吸附剂的脱硫效果．研究结果认为4种固体吸附剂在吸附模拟烟气中SO2的吸附能力顺序为：活性炭〉粉煤灰〉累托石〉沸石,其中最佳吸附效果的是活性炭,其最大脱硫率可达98．71％,平均脱硫率也可达到66．58％．探索了改性活性炭脱除烟气中低浓度二氧化硫的影响因素,实验表明：空速对活性炭脱硫效果的影响较大．随着空速的增加,停留时间变短,在同样累计通气时刻,脱硫率下降;低温吸附时,随吸附温度升高,吸附量降低;但在高温出现化学反应吸附时,吸附温度高则反应速度快,脱毓效果好;此外,硝酸浸泡时间越长,活性炭吸附脱硫效果越好．     

燃气栲胶脱硫机理与工艺设计

用栲胶脱除燃料气中硫化氢的方法是新技术,目前这方面参考资料不多。我国盛产栲胶,开发此法的前景是光明的。本文阐明栲胶脱硫剂特点,并提出其脱硫机理,这给主要设备设计提供证据。最后,指出主要设备设计原则。建议公式与调研结果重合性较好,可供工程设计参考。     

邯钢赤泥用于脱除硫化氢的研究

研究了以邯钢废赤泥脱除硫化氢,结果表明:活性赤泥具有较好的脱硫性能,其脱硫效率明显高于未加添加剂的废赤泥。同时实验了不同烘干温度、不同配比下赤泥的脱硫效率,筛选出活性赤泥的最佳配比为:赤泥85%,木屑5%,氧化钙10%,烘干温度130℃,并且与活性炭相比简要说明了赤泥的应用前景。     

邯钢赤泥用于脱除硫化氢的研究

研究了以邯钢废赤泥脱除硫化氢，结果表明：活性赤泥具有较好的脱硫性能．其脱硫效率明显高于未加添加剂的废赤泥。同时实验了不同烘干温度、不同配比下赤泥的脱硫效率，筛选出活性赤泥的最佳配比为：赤泥85％，木屑5％，氧化钙10％，烘干温度130℃，并且与活性炭相比简要说明了赤泥的应用前景     

稀土改性烟气脱硫剂脱硫作用的研究

经过理论分析和实验验证,研究开发了一种新型高效、预计将具有很大发展潜力的稀土改性烟气脱硫剂。实验证明:该脱硫剂中稀土氧化物掺杂不超过20%时均具有一定的脱硫效率,其中稀土氧化物含量为15%时脱硫效率较高(98%);同时实验考察了脱硫剂在不同温度下对模拟烟道气中SO2的脱除效果,结果发现在100～200℃温度范围内,稀土型烟气脱硫剂均具有很好的脱硫作用;此外,还实验考察了这类脱硫剂再生的条件和再生后脱硫的活性,表明在720℃左右的温度下焙烧再生后,其脱硫能力和新鲜脱硫剂相差不大。     

稀土型烟道气脱硫剂脱硫作用的研究

采用稀土型脱硫剂对模拟烟道气进行脱硫实验,考察了稀土含量,温度对脱硫效率的影响,并对脱硫剂进行了再生实验。结果表明,某些稀土化合作在较大的温度范围内对烟道气中SO2有较高的吸附,催化转化作用,脱硫效率可达90％左右;脱硫剂可再生重复使用,再生操作简便易行。     

水涤脱附条件下活性炭脱除SO2和NO中吸附反应空间的研究

以不同吸附材料吸附性能测试实验的结果为依据,对水涤脱附条件下活性炭同时脱硫脱硝过程的机理进行了研究,并对参与吸附过程的反应空间进行了分析.研究表明,活性炭的孔径分布是决定吸附材料对SO2和NO吸附性能的关键因素,活性炭同时吸附SO2和NO时,反应构型临界尺寸比单纯脱硫过程中的尺寸增大,直径为1.1～1.5nm的孔隙成为主要的吸附场所,平均孔径为6.27nm、微分孔径分布峰值为1.0～3.5nm的活性炭AC6成为一种具有最佳吸附性能的活性炭.     

负载金属球形活性炭吸附苯并噻吩的研究

通过负载不同过渡金属于阳离子交换树脂,再经焙烧及CO2活化,制备负载金属球形活性炭吸附剂,并采用间歇床实验研究制备条件与脱硫条件对吸附剂脱硫性能的影响.结果表明:3类负载金属球形活性炭C-Fe、C-Ni和C-Cu的最佳炭化温度分别为430℃、450℃和440℃;对苯并噻吩的平衡吸附硫容分别为14.33 mg/g、12.97 mg/g和10.22 mg/g;吸附时间为4 h.当剂油质量比分别为0.15、0.17、0.22时,脱硫率达到最大,分别为67%、63%、54%.采用乙醇超声清洗和焙烧的方法,经3次再生处理后,吸附剂脱硫活性显著降低.     

M/AC和MY分子筛吸附脱除FCC汽油中硫的研究

制备了金属离子改性吸附剂--M/AC和MY分子筛,用于真实汽油吸附脱硫,并检测了它们对真实汽油的脱硫效果。其中考察不同金属离子改性吸附剂、吸附剂的用量(剂油比)等对脱硫性能的影响,及改性后的吸附剂Cu/AC于不同吸附温度和不同吸附时间对脱硫性能的影响。结果表明:Cu2+、Ag+改性的分子筛和活性炭表现出良好的吸附能力,并且活性炭对FCC汽油脱硫性能优于NaY分子筛的脱硫性能。综合考虑,筛选出吸附剂Cu2+/AC,在温度为30℃、静态吸附6 h、剂油比(g/mL)为1∶10的条件下对FCC燃料油吸附脱硫最佳。     

Removal characteristics of disinfection by-products formation potential by bioaugmentation activated carbon process

The high-active bacteria were screened from 8 dominant bacteria obtained from the natural water body,and then the bioaugmentation activated carbon was formed by hydraulic immobilization of the high-active bacteria. Plant-scale studies on removal characteristics of disinfection by-products formation potentials (DBPFP) by bioaugmentation activated carbon process were conducted for micro-polluted raw water treatment. The results show that the bioaugmentation activated carbon process has adopted better purification efficiency to THMFP and HAAFP than traditional biological activated carbon process,and that average removal efficiencies of THMFP and HAAFP can reach 35% and 39.7% during the test period,increasing by more than 10% compared with traditional biological activated carbon process. The removal efficiencies of THMFP and HAAFP are stable because of the biodegradation of the high-active bacteria and the adsorption of active carbon. The biodegradability of CHCl3 formation potential is better as compared with that of CHCl2Br and CHClBr2 formation potentials among THMFP,and high removal efficiency of CHCl3formation potential is obtained by bioaugmentation degradation of the high-active bacteria. The biodegradability of HAAFP is better in comparison with that of THMFP,and the chemical properties of HAAFP are propitious to adsorption of activated carbon. Thus,HAAFP is on predominance during the competitive removal process with THMFP.     

脱硫效果评定指标的探讨

本文通过对国内外常用脱硫效果评定指标的分析，结合脱硫过程的特点，提出采用一个新的效率指标η＿ｓ作为脱硫效果评定指标。通过实例验证，具有较好的评定效果。     

低温Ni/AC脱硫剂的制备与表征

采用过量浸渍法制备了Ni/AC脱硫剂,着重考察了酸预处理和操作条件对Ni/AC脱硫性能的影响,同时用BET、XPS和XRD对脱硫剂的织构和结构性能进行了表征.结果表明:酸预处理能增加活性炭载体的比表面积和孔容,提高表面含氧官能团的比例;酸预处理能显著提高Ni/AC的脱硫活性,表现出高的低温脱硫活性;操作条件对Ni/AC的脱硫活性具有较大的影响,脱硫反应必须在适宜反应条件下进行,Ni/AC脱硫剂才能表现出好的脱硫活性.     

超重力法炼厂干气MDEA选择性脱硫实验研究

炼厂干气含有大量H₂S和CO₂ 组分,为了提高炼厂干气脱硫效率,提高胺液选择性吸收脱硫的效果,采用超重力旋转床作为吸收脱硫反应器代替传统板式吸收塔进行实验研究。考察了旋转床转速、胺液流量以及吸收温度对脱硫脱碳吸收效果的影响。实验得出较优的操作条件:在干气流量4500m3/h,压力0.8MPa,胺液流量8m3/h,转速800r/min,吸收温度42~45℃的条件下,可以获得较好的吸收效果,吸收后干气中H₂S体积分数为0.01%,满足后续硫含量排放要求。结果表明,吸收剂在反应器中的停留时间越短,H₂S的选择性吸收效果越好;采用旋转床反应器可以代替传统板式吸收塔是可行的。     

S⁃Zorb反应吸附脱硫技术的研究进展

S⁃Zorb反应吸附脱硫技术因其高效的脱硫效果、温和的工艺条件已经成为重要的汽油深度脱硫技术之一,S⁃Zorb脱硫技术由Phillips公司开发,自从被中国石化独家收购以来,在国内被广泛推广。但是目前,其吸附剂的组成尚未完全公布,因此S⁃Zorb工艺研究的重点在于吸附剂的国产化,以及通过对反应吸附机理的深入研究来不断提高脱硫剂的活性和稳定性。综述了S⁃Zorb反应吸附脱硫技术的工艺发展、运行中存在的问题以及S⁃Zorb反应吸附剂的研究与开发的最新进展,并对反应吸附脱硫的机理进行了讨论。     

功率超声下柴油的氧化吸附脱硫

对超声作用下柴油氧化吸附脱硫进行了研究,首先对柴油进行超声氧化,再对氧化后的柴油进行活性炭吸附脱硫。以H2O2为氧化剂,以磷酸和硫酸混合作酸促进剂(V(H3PO4):V(H2SO4)为1:1),再加入催化剂在超声波下对柴油进行氧化。对活性炭进行了不同的预处理,主要考察不同处理方法的活性炭对氧化后柴油的吸附脱硫效果。结果表明,对氧化后的柴油先用KOH溶液洗涤,之后再用硝酸氧化处理后的活性炭进行吸附,柴油脱硫率达到97.70%,柴油回收率达到91.05%。     

基于双流体模型的烟气喷动床脱硫过程的数值模拟

以气固两相流体动力学为基础,采用欧拉双流体模型及颗粒动力学理论,引入复相催化脱硫反应动力学模型,对喷动床应用活性炭颗粒脱硫的过程进行模拟。获得了喷动床具有喷射区、环隙区和喷泉区的流动状态,分析了床内气目的速度矢量分布及SO2质量分数的分布情况。结果表明：喷动床内环隙区脱硫效果最好,且流经环隙区烟气量占总进气量的60％-859／6,说明喷动床内特有的流动状态有利于烟气的脱硫。当表观速度由1.099m／s减小到0.732m／s时,喷动床的脱硫效率提高25％。因此在保证喷动床稳定工作的情况下,适当减小入口的烟气速度,有利于提高活性炭喷动床的脱硫效率。