涤纶过滤布表面热压法固着羟基磷灰石颗粒

通过热压法在涤纶过滤布表面固着羟基磷灰石颗粒,探讨了热压工艺对颗粒固载率和孔径的影响。FT-IR结果表明,562、601和1026cm-1处出现振动吸收峰;XRD结果表明,在25.45°、31.78°和32.54°处出现羟基磷灰石的三强峰,证实颗粒被固着到过滤布的表面,热压过的过滤布表面变得平实。当热压温度245℃、热压时间120s、压力3N、悬浮液质量浓度为10g/L时,羟基磷灰石颗粒的固载率为48.8%,过滤布的孔径减小了53.2%,为88.3μm,可以满足过滤的要求;在镉离子原液质量浓度为387.7mg/L时,吸附24h对镉离子的去除率可达42.1%。     

PEEK/HA生物复合材料的热稳定性

缩聚合成聚醚醚酮,与纳米羟基磷灰石混合,制成聚醚醚酮/羟基磷灰石生物复合材料,用热重分析法研究其热稳定性.研究表明,该材料热分解起始温度在500℃以上,热稳定性好;升温速率对热重曲线有重要影响,随着升温速率加快,热失重曲线向高温区平移,起始分解温度和最大热分解速率温度提高,反应临近结束的拐点温度也提高;随着羟基磷灰石含量的增大,该复合材料的最大分解速率逐渐降低,热稳定性优于聚醚醚酮.细胞毒性试验显示,该复合材料对Hela细胞无明显毒性,对细胞生长有促进作用,生物相容性良好.     

热喷涂HA复合涂层的组织分析

为了制备羟基磷灰石（HA）复合涂层,采用化学沉淀法制备羟基磷灰石粉末,对制备的超细粉末加入PVA溶液充分搅拌、干燥、研磨和过筛,制备出微米级、近似球状的、在等离子送粉器中容易流动的羟基磷灰石粉末.利用等离子喷涂和电弧喷涂的复合喷涂方法制备出羟基磷灰石不锈钢复合涂层和氧化铝不锈钢复合涂层,并通过扫描电镜分析了涂层的组织形态.结果表明,羟基磷灰石粉末比重很轻,不易进入等离子弧中心而被融化,等离子弧将羟基磷灰石粉末加热并载入电弧喷涂气流中,由不锈钢雾化液滴一并打在基体上形成复合涂层.对于氧化铝/不锈钢涂层和复合涂层,2种粒子虽然分布不均匀,但却获得了良好的冶金结合.     

微乳液法制备多孔中空羟基磷灰石微球的研究

以自制的纳米羟基磷灰石粉末为原料,在明胶/水/植物油微乳体系中制得羟基磷灰石/明胶微球,经高温烧结将明胶去除后,得到多孔羟基磷灰石微球.采用TEM、XRD、TG、SEM、压汞仪对产品进行了表征.结果表明:利用本方法制得的羟基磷灰石微球尺寸较均匀,约为(800±200)μm该微球呈现内部多孔结构,且孔隙率随微乳体系中明胶含量的增加而增加.当羟基磷灰石/明胶的质量比为4:6时,微球出现空心现象.这种多孔且中空的羟基磷灰石微球在骨修复/填充和药物携带缓释方面具有潜在的应用前景.     

海藻酸钠/聚乙烯醇/羟基磷灰石复合纤维制备工艺及其性能

以溶液纺丝法制备了海藻酸钠/聚乙烯醇/羟基磷灰石复合纤维,采用正交试验法和单因素分析法对复合纤维制备工艺与断裂强度和镉离子吸附量的关系进行研究。结果表明,SA与PVA质量分数为6%、SA与PVA质量比为4∶1、凝固浴CaCl2质量分数为2%、凝固浴温度为60℃、纺丝头牵伸比为2倍时纤维的吸附量最大。随着羟基磷灰石含量的增加,复合纤维对镉离子吸附量大幅度提高。     

羟基磷灰石／壳聚糖生物复合材料研究进展

羟基磷灰石基人工骨作为最有前途的生物医用材料之一,在生物医用材料和医学研究领域有着广泛的应用和研究.羟基磷灰石/壳聚糖复合材料因其生物相容性和合适的力学性能逐渐成为骨修复生物材料研究的热点.本文综述了羟基磷灰石/壳聚糖复合材料的研究现状,探讨了其特点、制备和性能.另外对羟基磷灰石/壳聚糖复合材料的研究发展前景予以展望.     

HA-ZrO2生物复合材料的制备

钇稳定的二氧化镐中分别掺杂1％,5％,15％的羟基磷灰石来制备生物性能良好,且具有较好的机械强度和断裂韧性的生物复合材料以满足承载方面的需要。对其力学性能、微观结构和生物性能进行了研究,用扫描电镜（SEM）、x射线衍射仪（XRD）等对复合材料进行了分析。结果表明掺杂羟基磷灰石的复合材料的维氏硬度远远高于单一羟基磷灰石的硬度,几乎接近于二氧化镐的硬度。最大的抗弯强度为976.21MPa,K1c为5.2—10.4MPa·m^1/2。生物模拟试验表明该种复合材料具有良好的骨传导作用,具有生物活性,是一种较理想的骨植入材料。     

纳米羟基磷灰石的镉离子吸附性能

以硝酸钙、磷酸、氨水为原料,采用共沉淀法合成了纳米羟基磷灰石粉体.以硝酸镉水溶液作为模拟废水,用Visual MINTEQ软件对模拟废水的溶液化学特征进行了计算,主要研究了溶液的初始pH值、反应时间以及镉离子(Cd2+)初始浓度等因素对纳米羟基磷灰石的镉离子吸附量的影响.实验结果表明,纳米羟基磷灰石的镉离子吸附性能在溶液初始pH为4～9的范围内比较稳定,其去除水溶液中镉离子的过程符合准二级动力学模型,并且与朗缪尔等温吸附和弗伦德里希等温吸附均表现出了较高的相关性,反映了纳米羟基磷灰石吸附水溶液中镉离子的反应以离子交换作用为主的特点.纳米羟基磷灰石不仅镉离子吸附容量大,而且初期吸附速率很快,是一种性能良好的环境矿物吸附材料.     

羟基磷灰石对水溶液中锌离子的吸附动力学

研究了羟基磷灰石对水溶液中锌离子的吸附动力学.研究结果表明羟基磷灰石对水溶液中锌离子的吸附符合Langmiur等温吸附:ρR/q=0.152 97 ρR+0.122 47 ;该吸附反应符合二级反应动力学方程:1/ρ R=0.010 84t+0.496 89;反应速率k1和温度T之间的关系符合阿仑尼乌斯 (Arr henius)公式:lnk1=-0.895 25×1/T+0.155 41,吸附的活化能为Ea=7 .444 J/mol.     

羟基磷灰石改性聚甲基丙烯酸甲酯的耐热性能

为了改善聚甲基丙烯酸甲酯的热性能,通过微乳液合成方法制备了羟基磷灰石与聚甲基丙烯酸甲酯的杂化材料,并利用扫描电镜、傅立叶红外光谱、X射线衍射和热分析方法对羟基磷灰石/聚甲基丙烯酸甲酯杂化材料的结构与形貌进行表征,研究了羟基磷灰石含量对于杂化材料热性能的影响.结果表明在杂化材料中,羟基磷灰石被聚甲基丙烯酸甲酯所包覆;羟基磷灰石/聚甲基丙烯酸甲酯杂化材料的热性能明显优于纯的聚甲基丙烯酸甲酯;随着羟基磷灰石含量的增加,聚甲基丙烯酸甲酯的热性能显著提高;当羟基磷灰石含量为5%时,聚甲基丙烯酸甲酯的玻璃化转变温度增加到132℃,而且羟基磷灰石/聚甲基丙烯酸甲酯杂化材料的热稳定性也随着羟基磷灰石含量的增加而增强.     

新型变切深镗削系统的研究

在总结国内外变切深镗削技术研究现状的基础上,提出一种新的变切深镗削技术,并对智能镗杆的总体结构、微进给机构、控制方法等方面进行了具体的介绍。     

Preparation of Hydroxyapatite Fibers by the Homogeneous Precipitation Method

This paper discussed the preparing process of hydroxyapatite fibers which were widely used as reinforcement for biomedical materials by homogeneous precipitation method.The needle-like hydroxyapatite crystals were synthesized in an aqueous system.They were transferred from precursors-dicalcium phosphate anhydrate and octacalcium phosphate crystals.The reaction conditions were well controlled in order to obtain crystals in given morphology.The products were characterized by X-ray powder diffractometry(XRD),scanning electron microscopy (SEM) and infrared spectroscopy(IR),They were verified to be ydroxyapatite crystals with needle-like in shape.     

氧气-乙炔火焰法制备球形二氧化硅粉体研究

以天然二氧化硅粉体为原料,采用氧气-乙炔火焰球化法制备球形二氧化硅。实验中选取燃烧气体参数:乙炔流量0.6～0.9m3/h,氧气流量0.8～1.2m3/h。借助XRD衍射仪、扫描电子显微镜对球形化前后样品进行表征,研究了原料粒度、送粉速率对球化效果的影响。结果表明,采用该实验设备和工艺路线可以制备出球化率95%以上的球形二氧化硅,送粉速率越小,原料颗粒粒径越小且粒度分布越均匀(≤10μm),所制备产品的球化率和熔融度越高。     

3-D transient numerical simulation on the process of laser cladding by powder feeding

A 3-D transient mathematical model for laser cladding by powder feeding was developed to examine the macroscopic heat and momentum transport during the process, based on which a novel method for determining the configuration and thickness of cladding layer was presented. By using Lambert-Beer theorem and Mie‘s theory, the interaction between powder stream and laser beam was treated to evoke their subtle effects on heat transfer and fluid flow in laser molten pool. The numerical study was performed in a co-ordinate system moving with the laser at a constant scanning speed. A fixed grid enthalpy-porosity approach was used,which predicted the evolutionary development of the laser molten pool. The commercial software PHOENICS, to which several modules were appended, was used to accomplish the simulation. The results obtained by the simulation were coincident with those measured in experiment basically.     

WC/Ni60激光熔覆复合涂层的强碱腐蚀磨损行为

利用激光熔覆制备WC增强涂层,通过光学显微镜(OM)、电子扫描显微镜(SEM)和EDS对试样观察和分析,并依据颗粒相分布均匀性,获得推荐优化工艺参数是送粉量为7.8g/min、扫描速度为4mm/s、激光功率为2.0kW和离焦量为50mm。在此基础上,应用M-200摩擦磨损试验机考察了WC/Ni60涂层在40% NaOH强碱溶液作用下的摩擦磨损行为,结果表明,涂层的摩擦磨损机制随工况的变化而变化,钝化膜的生成和溶解成为一个动态过程,且所制备的涂层在中速中载时较干摩擦能够显著降低摩擦因数和磨损量。     

The Effects of Dense/Nanometer Hydroxyapatite on Proliferation and Osteogenetic Differentiation of Periodontal Ligament Cells

1Introduction Hydroxyapatite(HA),asyntheticcalciumphos phate,iscommonlyusedinperiodontalsurgeryforresto rationofperiodontium.Manyreportsrecommendthisma terialbecauseitsgoodbiocompatibilityandosteoconduct ibility.However,accordingtosomestudies,newperi odon…     

Energy analysis of mechanical alloying of molybdenum disilicide in a new-type high energy vibrating ball mill

In order to understand the fundamentals of a high energy vibrating type milling process, the energy transfer during me-chanical alloying of molybdenum disilicide is investigated based on the Magini-lasonna energy transfer method, amended by Murty.The efficiency factor and total energy of milling are calculated. MoSi2 synthesized by a mechanically induced self-propagating .reaction has also been studied according to different milling parameters, such as the number of balls and the ball to powder weight ratio. The results indicate that the efficiency factor is between 1.944 and 8.507 J/(g·s). A total milling energy of about 19.38-26.47 kJ/g is found to be necessary for the mechanically induced self-propagating reaction of a Mo:2Si powder mixture. The efficiency of milling energy transfer is about 3.3%-4.5%. The experiment and modeling show that the optimum condition for mechanical alloy-ing is a half full vial of balls.     

微量给粉装置的设计与实验

针对已有典型微量给粉装置,进行了分类和工作原理分析．依据螺旋—气动给粉装置的工作原理和结构特性,给出了关键设计参数和设计原则,导出了给粉量计算公式．利用自制的螺旋—气动给粉器,在30～380g／min血给粉范围内,对电厂灰和滑石粉进行实验测试．结果表明,实测给粉量与计算给粉量符合度高,给粉性能稳定,可调范围大．     

鳙鱼鱼鳞盐酸脱钙工艺及动力学研究

鱼鳞脱钙是从鱼鳞中提取胶原蛋白的重要的前处理过程。以鳙鱼鱼鳞为对象、盐酸溶液为脱钙剂、羟基磷酸钙消耗速率为目标,采用单因素实验方法分别考察了反应时间、羟基磷酸钙浓度、盐酸溶液浓度和反应温度对羟基磷酸钙消耗速率的影响并确定了最佳工艺条件分别为40 min、0.017 4 mol·L-1、0.5 mol·L-1和20℃。在最佳工艺条件下,羟基磷酸钙消耗速率为3.744 9×10-4mol·L-1·min-1,相应的脱钙率为86.20%。建立了盐酸脱钙的动力学方程,模型反映了羟基磷酸钙消耗速率随羟基磷酸钙浓度、盐酸溶液浓度与温度的变化关系,其理论值与实验值基本吻合,可用于过程调节、产品控制和预测不同条件下羟基磷酸钙的反应消耗速率。     

镁粉含量对Mg-HA牙体充填材料结构与性能的影响

以氢氧化钙和磷酸二氢钙等为原料采用化学沉淀法制备羟基磷灰石粉体,与适当含量的镁粉烧结制备Mg-HA粉体.以聚甲基丙烯酸酯为有机粘结剂控制合适的比例调和制备Mg-HA牙体充填材料,通过扫描电子显微分析（SEM）、X射线衍射分析（XRD）和力学性能测试等方法,研究了镁粉含量对其固化试样结构与抗压强度的影响.结果表明：不同镁含量的试样均可获得较高的抗压强度（大于90MPa）,实验条件下,随镁含量增大,试样的抗压强度有略微上升的趋势;Mg-HA基体与高聚物粘结剂能达到良好的结合,并具备较高的性能.