K2CO3-锯末干混合制备成型活性炭

以梧桐锯末为基体、无水K2CO3为活化剂,采用干混合法制备成型活性炭颗粒,通过单因素实验考察盐料质量比、活化温度、活化时间及成型密度对活性炭吸附碘性能的影响,并对其进行了表征. 结果表明,在盐料质量比2.0、活化温度950℃、活化时间80 min、成型密度1.3 g/cm3的条件下,所制成型活性炭对碘的吸附容量达1323.25 mg/g. 成型活性炭具有发达的孔结构,比表面积为1432.59 m2/g,平均孔径为1.70 nm,总孔容为0.772 cm3/g,其中微孔比表面积为1302.75 m2/g,孔容为0.566 cm3/g,微孔率达73.3%.     

复合活化剂制备稻壳活性炭影响因素及特性

以稻壳为原料,ZnCl₂-CuCl₂为复合活化剂,制备稻壳活性炭,并以BET比表面积和吸附性能为指标,通过正交试验对制备的工艺条件进行优化,并对制得的稻壳活性炭采用氮气吸附等温线、X射线衍射仪(XRD)表征。结果表明,稻壳可以被制得大比表面积活性炭。影响活性炭比表面积和吸附性能最重要的因素是氯化锌浓度和活化温度,最佳制备工艺条件是氯化锌浓度5 mol/L,氯化铜浓度 0.4 mol/L,活化温度500 ℃,活化时间2 h。该条件下制得的稻壳活性炭比表面积为1 924 m²/g,碘吸附值为1 041 mg/g,亚甲基蓝吸附值为 188 mg/g。     

磷酸活化法制备糠醛渣活性炭的研究

以碘吸附值、亚甲基蓝吸附值及活性炭得率为考察指标,选取对糠醛渣活性炭性质影响较大的浸渍比、磷酸质量分数、活化温度、保温时间4个因素进行L₁₆(4⁵)正交试验对磷酸活化法制备糠醛渣活性炭的工艺条件进行优化。由正交试验结果得到磷酸活化的最佳工艺条件为:磷酸质量分数60%,浸渍比2.5:1,活化温度550 ℃,保温1.5 h,此条件下制得的活性炭样品的碘吸附值为839.6 mg/g,亚甲基蓝吸附值为260.3 mg/g,得率为46.8%,比表面积为830.20 m²/g,孔容积为0.502 cm³/g,孔径集中在0.8~2.5 nm,具有丰富的中孔和微孔。     

两步法制备竹质活性炭

结合磷酸活化法与氯化锌活化法化制备活性炭,在较低的活化温度下取得了良好的活性炭.活化总时间为60min,磷酸活化温度500 ℃与氯化锌活化温度400 ℃,浸渍率为150%的优化条件下制得的活性炭,其亚甲基蓝脱色力为19 mL,碘吸附值为861 mg/g,孔径集中在4.5 nm,并且比表面积高达1696 m2/g,大孔仅占0.381%.     

废弃辣椒秸秆高比表面积活性炭的制备及表征

以废弃的辣椒秸秆为原料,KOH为活化剂,制备高比表面积活性炭,研究了碱炭比、活化温度、炭化温度及活化时间对活性炭吸附性能的影响。结果表明,活性炭制备的最佳工艺条件为:碱炭比为3∶1,活化温度为700℃,炭化温度为450℃,活化时间为40 min。在此条件下,制得的活性炭碘吸附值2 356.40 mg/g,亚甲基蓝吸附值41.3 mL/0.1 g,BET比表面积为2 432.135 m2/g,Langmuir比表面积高达3 270.478 m2/g,吸附总孔容为2.064 cm3/g,平均孔径为3.246 nm。SEM和XRD观察发现,辣椒秆活性炭呈不定形态,具有丰富和发达的蜂窝状孔隙结构。     

磷酸法海藻基活性炭的制备及吸附性能

以大型海藻铜藻为原料,采用H_3PO_4活化法制备活性炭,考察磷酸与藻粉的浸渍比、浸渍时间、活化温度、活化时间对得率、亚甲基蓝吸附值、碘吸附值的影响。H_3PO_4活化法制备活性炭最佳工艺如下:磷酸与藻粉的质量比为5∶1,浸渍时间100 min,活化温度550℃,活化时间75 min。最佳制备条件下制得的活性炭碘吸附值为528. 8 mg/g,亚甲基蓝吸附值为142. 5 mg/g,得率为43. 74%,比表面积为728. 73 m2/g。pH=2条件下,铜藻基活性炭对于Cr(Ⅵ)最大吸附量和吸附率可分别到达31. 5 mg/g和85%。     

石莼基微/中孔复合结构活性炭的制备及性能

以海洋海藻废弃物石莼为原料,通过热解预炭化,KOH活化制备活性炭。以碘吸附值和亚甲基蓝吸附值为吸附性能评价指标,探究了活化工艺对活性炭吸附性能的影响。结果表明,当KOH与石莼半焦质量比(碱炭比)为3.0∶1.0、活化时间为45 min、活化温度为800℃时,活性炭吸附性能最优,其碘吸附值和亚甲基蓝吸附值最大,分别为1824.19 mg/g、914.98 mg/g。FTIR测试表明,活性炭含有大量羟基等官能团。SEM测试表明,活性炭表面粗糙、存在大量孔结构。活性炭的BET比表面积为2616.3 m2/g,Langmuir比表面积高达4883.5 m2/g,平均孔径为2.73 nm。石莼基活性炭的孔结构为微/中孔复合结构,有作为储能、环保材料的潜质。     

磷酸法海藻基活性炭的制备及吸附性能

以大型海藻铜藻为原料,采用H_3PO_4活化法制备活性炭,考察磷酸与藻粉的浸渍比、浸渍时间、活化温度、活化时间对得率、亚甲基蓝吸附值、碘吸附值的影响。H_3PO_4活化法制备活性炭最佳工艺如下:磷酸与藻粉的质量比为5∶1,浸渍时间100 min,活化温度550℃,活化时间75 min。最佳制备条件下制得的活性炭碘吸附值为528. 8 mg/g,亚甲基蓝吸附值为142. 5 mg/g,得率为43. 74%,比表面积为728. 73 m2/g。pH=2条件下,铜藻基活性炭对于Cr(Ⅵ)最大吸附量和吸附率可分别到达31. 5 mg/g和85%。     

脱油沥青基活性炭的制备及对亚甲基蓝的吸附性能研究

以脱油沥青为原料,采用氢氧化钾活化法制备了比表面积高达3245m~2/g的活性炭。样品的表征利用X-射线衍射仪(XRD)及扫描电子显微镜(SEM),利用样品活性炭对亚甲基蓝的吸附研究其吸附性能。结果表明:焙烧温度为800℃、氢氧化钾与脱油沥青的质量比为5:1条件下制备出的活性炭样品,有更丰富的中孔结构。脱油沥青基活性炭亚甲基蓝的吸附等温线符合Langmuir模型;提高活化温度,活性炭对亚甲基蓝吸附容量可明显提高,最大吸附容量Q_m可高达518.1 mg/g。     

水蒸气活化再生乙酸乙烯合成触媒载体活性炭

探讨了活化温度、活化时间、水蒸气流量对再生后活性炭吸附性能和得率的影响,得到了最佳工艺条件:活化温度1 000℃,活化时间60 min,水蒸气流量2.23 g/min。该工艺条件下再生活性炭的碘吸附值1 174.37 mg/g,亚甲基蓝吸附值200 mL/g,得率为62.87%。再生后活性炭的吸附指标达到国家一级品的标准,其中亚甲基蓝吸附值是国家一级品标准的2.22倍。同时,测定了该活性炭氮吸附,通过BET计算了活性炭的比表面积,通过密度函数理论(DFT)表征了活性炭的孔结构。结果表明:该活性炭为微孔型,BET比表面积为1 254.51 m2/g,总孔容为0.592 6 mL/g。     

氯化锌活化法制备多孔炭陶复合吸附材料

以氯化锌浸渍的木屑为原料,黏土为粘结剂,制备炭陶复合吸附材料。讨论了炭化温度和保温时间对其吸附性能的影响,并对其孔隙结构进行了表征。结果表明,随温度和保温时间的增加,炭陶复合吸附材料的碘吸附值和亚甲基蓝吸附值呈先上升后下降的趋势;木屑受到活化作用形成活性炭而发生收缩,在活性炭和陶土之间形成空隙,有利于形成孔隙结构发达的炭陶复合吸附材料。在温度500℃、保温时间1 h的较佳工艺条件下,制得炭陶复合吸附材料的比表面积为809.5 m²/g,总孔容积为0.298 cm³/g,中孔容积为0.185 cm³/g,微孔容积为0.113 cm³/g,炭陶的含炭量为60.7%,碘吸附值为680.5 mg/g,亚甲基蓝吸附值为165.0 mg/g。     

The Properties of Activated Carbon Made from Waste Newsprint Paper

Activated carbon is a porous material made by activation of carbon materials, such as coal, by steam or carbon dioxide gas to form numerous micropores on the surface which gives the material high adsorption characteristics and it is widely used as a purifier for water and air. In this research, to develop a new use for waste paper, activated carbon was prepared from waste newsprint paper and its adsorption characteristics were measured. As a result, activated carbon with an iodine adsorption capacity of 1310 mg/g, a methylene blue adsorption capacity of 326 mg/g and a specific surface area of 1000 m2/g was obtained. These adsorption capacities were almost the same as ordinary activated carbon on the market.     

Preparation of activated carbon from paper mill sludge by KOH-activation

The purpose of this study is the preparation of activated carbon using paper mill sludge collected from biological wastewater treatment plant. The char produced from pyrolysis of paper mill sludge was chemically activated with potassium hydroxide. A systematic investigation of the effect of activation agent ratio, activation temperature and time on the properties of the char was carried out in a rotary kiln reactor. The chemically activated carbons were characterized by measuring iodine and methylene blue number and specific surface area. The activated carbon prepared from char of paper mill sludge in this study had maximum iodine and methylene blue number of 726.0 mg/g and 152.0 mg/g, and specific surface area of 1,002.0 m²/g, respectively. The result of estimation on adsorption capacities of metals, the Freundlich isotherms, yields a fairly good fit to the adsorption data, indicating a monolayer adsorption of metals onto activated carbon prepared from char of paper mill sludge using a potassium hydroxide as the activating agents.     

原料复配制备木质素基成型活性炭研究

以碱木质素和杉木屑为原料,磷酸为活化剂,制备碱木质素基成型活性炭,考察了碱木质素质量分数、浸渍比、活化温度、活化时间等对活性炭性能的影响。研究结果表明：碱木质素复配杉木屑(碱木质素质量分数50%)后,复配料的表面润湿性显著提高,瞬时水接触角由133.2°(碱木质素)降低至86.6°(复配料);热膨胀系数显著降低,膨胀温度区间的热膨胀系数由2 365μm/(m·℃)(碱木质素)降低至45μm/(m·℃)(复配料)。在最佳工艺条件即碱木质素质量分数50%、浸渍比1.5∶1(纯磷酸与复配料质量比)、活化温度500℃、活化时间90 min下,制备的成型活性炭得率41.76%,碘吸附值1 070 mg/g,亚甲基蓝吸附值255 mg/g,强度90%,比表面积1 646 m²/g,总孔容积为0.795 cm³/g,其中孔径小于5 nm的孔容积占总孔容积的97.2%。     

高比表面积煤基活性炭的制备及其吸附性能的研究

以太西无烟煤为原料,KOH为活化剂,采用化学活化法制备高比表面积煤基活性炭,着重考察了碱炭比、活化温度、活化时间对活性炭吸附性能的影响。研究结果表明：当碱炭比为4、活化温度为800℃、活化时间为1h时,可以制得比表面积达3215m^2／g,碘吸附值达2884mg／g,亚甲蓝吸附值达548mg／g的高比表面积煤基活性炭。     

干法制备高中孔率生物质成型活性炭

以锯末为原料,氯化锌为活化剂,不添加黏结剂,采用干法混合后直接成型活化制备高中孔率生物质成型活性炭。为考察这种工艺的可行性,通过单因素实验,以亚甲基蓝吸附值为评价指标,考察了盐料比、活化温度、活化时间与成型密度对生物质成型活性炭吸附性能的影响,得出较优工艺条件为:盐料比1.0:1,活化温度950℃,活化时间为60min,成型密度为1.4g·cm^-3。在此工艺条件下制备得到的生物质成型活性炭,其亚甲基蓝吸附值为387mg·g^-1,BET比表面积为2104m²·g^-1,平均孔径为3.11nm,总孔容为1.63cm³·g^-1,中孔孔容为1.17cm³·g^-1,中孔率高达71.8%,初步证明了干法制备高中孔率生物质成型活性炭工艺的可行性。     

油茶壳残渣制备活性炭的工艺

以油茶壳醇浸取后残渣为原料,以磷酸活化法制备活性炭,考察了浸渍比、磷酸质量分数和活化温度等对活性炭吸附性能及其得率的影响;活性炭的吸附性能由碘吸附值、亚甲基蓝吸附值表征。结果表明,在酸/炭浸渍比为3:1、磷酸质量分数70%、活化温度500℃时,活性炭的吸附性能最佳,其碘、亚甲基蓝吸附值和得率分别为1043.29mg/g、148.5mg/g和38.77%。采用物理吸附仪在77K下测定其N₂吸附脱附等温线,利用BET法和BJH法计算比表面积和孔径分布,其比表面积为1626.45m²/g,平均孔径为4.7nm,总孔容为1.94cm³/g。同时采用FTIR和XRD分析了活性炭的表面官能团和微观结构。     

磷酸法水稻秆活性炭的制备

以水稻秆为原料,采用磷酸活化法制备活性炭。研究了浸渍比、活化温度对活性炭样品吸附性能的影响,并对其微结构进行N₂吸附等温线、热重-微商热重法(TG-DTG)、扫描电子显微镜(SEM)等表征。结果表明:水稻秆适合作为磷酸法活性炭的原料,吸附性能达到市售脱色活性炭的指标要求。在浸渍比为3∶1、活化温度 450 ℃、活化时间 60 min 的条件下,制得活性炭的亚甲基蓝吸附值 215 mg/g,碘吸附值 855 mg/g,A法焦糖脱色率 110 %,BET比表面积 967.72 m²/g,总孔容积 1.23 cm³/g,中孔率 84.6 %,平均孔径 4.6 nm。