Influence of fiber orientation and fiber content on properties of sisal‐jute‐glass fiber‐reinforced polyester composites

The incorporation of natural fibers with polymer matrix composites (PMCs) has increasing applications in many fields of engineering due to the growing concerns regarding the environmental impact and energy crisis. The objective of this work is to examine the effect of fiber orientation and fiber content on properties of sisal‐jute‐glass fiber‐reinforced polyester composites. In this experimental study, sisal‐jute‐glass fiber‐reinforced polyester composites are prepared with fiber orientations of 0° and 90° and fiber volume of sisal‐jute‐glass fibers are in the ratio of 40:0:60, 0:40:60, and 20:20:60 respectively, and the experiments were conducted. The results indicated that the hybrid composites had shown better performance and the fiber orientation and fiber content play major role in strength and water absorption properties. The morphological properties, internal structure, cracks, and fiber pull out of the fractured specimen during testing are also investigated by using scanning electron microscopy (SEM) analysis. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016 , 133, 42968.     

An investigation of sound absorption coefficient on sisal fiber poly lactic acid bio‐composites

In this research, the mechanical, acoustical, thermal, morphological, and infrared spectral properties of untreated, heat and alkaline‐treated sisal fiber‐reinforced poly‐lactic‐acid bio‐composites were analyzed. The bio‐composite samples were fabricated using a hot press molding machine. The properties mentioned above were evaluated and compared with heat‐treated and alkaline‐treated sisal fibers. Composites with heat‐treated sisal fibers were found to exhibit the best mechanical properties. Thermo‐gravimetric analysis (TGA) was conducted to study the thermal degradation of the bio‐composite samples. It was discovered that the PLA‐sisal composites with optimal heat‐treated at 160°C and alkaline‐treated fibers possess good thermal stability as compared with untreated fiber. The results indicated that the composites prepared with 30wt % of sisal had the highest sound absorption as compared with other composites. Evidence of the successful reaction of sodium hydroxide and heat treatment of the sisal fibers was provided by the infrared spectrum and implied by decreased bands at certain wavenumbers. Observations based on scanning electron microscopy of the fracture surface of the composites showed the effect of alkaline and heat treatment on the fiber surface and improved fiber‐matrix adhesion. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015 , 132, 42470.     

Reinforcement of polypropylene using sisal fibers grafted with poly(methyl methacrylate)

Sisal fiber (SF) surface modification was carried out by grafting with methyl methacrylate (MMA) using cerium and ammonium nitrate as initiator. The effects of reaction time, monomer, and initiator concentration on the grafting parameters were systematically investigated. The results showed that MMA was successfully grafted onto the sisal fiber surface. The PMMA‐grafted sisal fibers were melt blended with polypropylene (PP) and then injection molded. The PP/SF composites were characterized by means of thermal analysis, mechanical testing, wide‐angle X‐ray diffraction, and SEM examination. PMMA grafted onto the surface of SF enhanced the intermolecular interaction between the reinforcing SF and PP matrix, improved the dispersion of SF in the PP matrix, and promoted the formation of β‐crystalline PP. These enhanced the thermal stability and mechanical properties of PP/SF composites. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 88: 1055–1064, 2003     

Friction properties of sisal fiber/nano‐silica reinforced phenol formaldehyde composites

The friction‐resistant sisal fiber/nano‐silica phenol formaldehyde resin composites were prepared through compression molding. To enhance the bonding between the sisal fiber (SF) and polymer matrix, SF were treated with different surface modifiers. The worn surfaces of composites were observed by scanning electron microscope (SEM). The result shows that the matrix of nano‐silica phenol formaldehyde resin can relieve the heat fade of the friction materials. Meanwhile sisal fibers treated with borax have effectively improved the friction and wear properties of the composites when the fiber content was 15%. POLYM. COMPOS. 36:433–438, 2015. © 2014 Society of Plastics Engineers     

The influence of chemical surface modification on the performance of sisal‐polyester biocomposites

This article concerns the effectiveness of various types and degrees of surface modification of sisal fibers involving dewaxing, alkali treatment, bleaching cyanoethylation and viny1 grafting in enhancing the mechanical properties, such as tensile, flexural and impact strength, of sisal‐polyester biocomposites. The mechanical properties are optimum at a fiber loading of 30 wt%. Among all modifications, cyanoethylation and alkali treatment result in improved properties of the biocomposites. Cyanoethylated sisal‐polyester composite exhibited maximum tensile strength (84.29 MPa). The alkali treated sisal‐polyester composite exhibited best flexural (153.94 MPa) and impac strength (197.88 J/m), which are, respectively, 21.8% and 20.9% higher than the corresponding mechanical properties of the untreated sisal‐polyester composites. In the case of vinyl grafting, acrylonitrile (AN)‐grafted sisal‐polyester composites show better mechanical properties than methyl‐methacrylate (MMA)‐grafted sisal composites. Scanning electron microscopic studies were carried out to analyze the fiber‐matrix interaction in various surface‐modified sisal‐polyester composites.     

Development and physico‐mechanical behavior of LDPE–sisal prepreg‐based composites

Low‐density polyethylene (LDPE)‐coated sisal fiber prepreg was prepared by using solution coating process. These coated fiber prepregs were consolidated to make composites having different weight fraction of sisal fibers in a hot compression‐molding machine. This experimental study reveals that higher loading of sisal fiber up to 57wt% in LDPE–sisal composites is possible by this technique. Mechanical and abrasive wear characteristics of these composites were determined. The tensile strength of composites increased with the increase in sisal fiber concentration. Coating thickness of LDPE was varied by changing the viscosity of LDPE–xylene solution that manifested to different weight fraction of fiber in sisal–LDPE composites. Mechanical, dynamic mechanical, and abrasive wear characteristics of these composites were determined. The tensile strength and modulus of sisal composites reached to 17.4 and 265 MPa, respectively, as compared to 7.1 and 33MPa of LDPE. Storage modulus of sisal composites LD57 reached to 2.7 × 10⁹ MPa at 40°C as compared to 8.1 × 10⁸ MPa of LDPE. Abrasive wear properties of LDPE and its composites were determined under multi‐pass mode; pure LDPE showed minimum specific wear rate. The specific wear rate of composites decreased with the sliding distance. Increase of coated sisal fiber content increased the specific wear rate at all the sliding distances, which has been explained on the basis of worn surface microstructures observed by using SEM. POLYM. COMPOS., 2013. © 2013 Society of Plastics Engineers     

Performance of pineapple leaf fiber–natural rubber composites: The effect of fiber surface treatments

Composites of natural rubber (NR) and short pineapple leaf fiber (PALF) were prepared on a laboratory two‐roll mill. The influences of untreated fiber content and orientation on the processing and mechanical properties of the composites were investigated. The dependence of extent of orientation on fiber concentration was also established. Sodium hydroxide (NaOH) solutions (1, 3, 5, and 7% w/v) and benzoyl peroxide (BPO) (1, 3, and 5 wt % of fiber) were used to treat the surfaces of PALFs. FTIR and scanning electron microscope (SEM) observations were made of the treatments in terms of chemical composition and surface structure. The tensile strength and elongation at break of the composites were later studied. The fiber–matrix adhesion was also investigated using SEM technique. It was found that all surface modifications enhanced adhesion and tensile properties. The treatments with 5% NaOH and 1% BPO provided the best improvement of composite strength (28 and 57% respectively) when compared with that of untreated fiber. The PALF‐NR composites also exhibited better resistance to aging than its gum vulcanizate, especially when combined with the treated fibers. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 1974–1984, 2006     

Mechanical and morphological properties of carbon fiber reinforced–modified epoxy composites

Epoxy, prepared through aminomethyl 3,5,5‐trimethylcyclohexylamine hardening of diglycidylether of bisphenol‐A (DGEBA) prepolymer, toughened with polycarbonate (PC) in different proportions, and reinforced with carbon fiber, was investigated by differential scanning calorimetry, tensile and interlaminar shear strength testing, and scanning electron microscopy (SEM). A single glass transition temperature was found in all compositions of the epoxy/PC blend system. The tensile properties of the blend were found to be better than that of the pure epoxy matrix. They increased with PC content up to 10%, beyond which they decreased. The influence of carbon fiber orientation on the mechanical properties of the composites was studied, where the fiber content was kept constant at 68 wt %. Composites with 45° fiber orientation were found to have very weak mechanical properties, and the mechanical properties of the blend matrix composites were found to be better than those of the pure epoxy matrix composites. The fracture and surface morphologies of the composite samples were characterized by SEM. Good bonding was observed between the fiber and matrix for the blend matrix composites. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 101: 3529–3536, 2006     

Influence of surface treatments on the physicochemical properties of short sisal fibers: Ethylene vinyl acetate composites

Natural fibers (NFs) are rich in cellulose and also they are a low cost, easily renewable source for polymer composites. However, the presence of impurities (waxes, lignin, etc.) and hydroxyl groups produce those NFs with less ability to reinforce polymeric matrices. Short sisal fibers (SSF) were subjected to three different chemical treatments (alkaline, dicumyl peroxide, and silane). Composites of ethylene vinyl acetate (EVA) and chemically modified SSF were prepared by mechanical mixing at the melt state of the polymer matrix (130°C) using a two roll mill. The influences of fiber content and chemical treatment on the mechanical properties of the composites were evaluated. The tensile strength increased for every such treated SSF‐reinforced composite. There was also a noticeable increase in elastic modulus compared with the unfilled matrix. The elongation at break values decreased as the fiber content was increased. Moreover, it was observed that the surface treatment of the SSF improved the fiber dispersion within the EVA matrix. The thermal stability of SSF was analyzed by thermogravimetic analysis. Potentially, the recyclability of the composites might be promising due to the lower specific gravity of NF, accompanied by low cost, and with the added advantage of biodegradability. POLYM. ENG. SCI., 2013. © 2012 Society of Plastics Engineers     

Melt rheological behavior of intimately mixed short sisal–glass hybrid fiber‐reinforced low‐density polyethylene composites. II. Chemical modification

The effect of chemical modification of both fiber and matrix on melt rheological behavior of intimately mixed short sisal–glass hybrid fiber‐reinforced low‐density polyethylene composites was studied with an Instron capillary rheometer. The variations of melt viscosity with different shear rate and shear stress values for different temperatures were studied. A temperature range of 130 to 150°C and shear rates of 16.4 to 5468 s^?1 were chosen for the analysis. Chemical modifications with stearic acid, maleic anhydride, silane, and peroxides were tested for their ability to improve the interaction between the matrix and fiber. The viscosity of the hybrid composites increases with every chemical modification. In the case of peroxide‐treated composites, the increase can be attributed to the peroxide‐induced grafting of the polyethylene matrix to the fiber surface and to the crosslinking of the polyethylene matrix. These phenomena are both activated by temperature, whereas temperature causes a reverse effect for all other chemical modifications. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 89: 443–450, 2003     

Preparation and properties of L‐lactide‐grafted sisal fiber–reinforced poly(lactic acid) composites

Pretreatment of the sisal fiber (SF) grafting with L‐lactide (LA) monomer via a ring‐opening polymerization catalyzed by a Sn(II)‐based catalyst was performed to improve the interfacial adhesion between SF and poly (lactic acid) (PLA). Biocomposites from LA‐grafted SF (SF‐g‐LA) and PLA were prepared by compression molding with fiber weight fraction of 10, 20, 30, and 40%, and then were investigated in contrast with alkali‐treated sisal fiber (ASF) reinforced PLA composites and untreated SF reinforced PLA composites. PLA composites reinforced by half‐and‐half SF‐g‐LA/untreated SF (half SF‐g‐LA) were prepared and studied as well, considering the disadvantages of SF‐g‐LA. The results showed that both the tensile properties and flexural properties of the SF‐g‐LA reinforced PLA composites were improved noticeably as the introduction of SF‐g‐LA, compared with pure PLA, untreated SF reinforced PLA composites and ASF reinforced PLA composites. The mechanical properties of the half SF‐g‐LA reinforced PLA composites were not worse, even better in some aspects, than the SF‐g‐LA reinforced PLA composites. Fourier transform infrared analysis and differential scanning calorimetry analysis exhibited that both the chemical composition and crystal structure of the SFs changed after LA grafting. In addition, the fracture surface morphology of the composites was studied by scanning electron microscopy. The morphological studies demonstrated that a better adhesion between LA‐grafted SF and PLA matrix was achieved. POLYM. COMPOS., 37:802–809, 2016. © 2014 Society of Plastics Engineers     

Properties Enhancement of Mengkuang Leaf Fiber/Ethylene‐Vinyl Acetate/Natural Rubber Thermoplastic Elastomer Composites by Alkaline Peroxide Bleaching Treatment

In this article, the effect of alkaline peroxide bleaching treatment using hydrogen peroxide on mengkuang leaf fiber (MLF) to the tensile, thermal properties and water absorption of thermoplastic elastomer composites based on ethylene‐vinyl acetate/natural rubber and MLF was investigated. Fiber morphology and the fiber‐matrix interface were further characterized by scanning electron microscopy (SEM). Treated composites showed better tensile properties than untreated fiber composites. SEM of the fractured surfaces of the composite specimens indicates that the bleaching treatment improved the interfacial interaction between the fiber and the matrix. The results of thermogravimetric analysis showed a higher thermal stability for treated composites than untreated composites. Furthermore, alkaline bleaching treatment has resulted in reduction of water absorption from 31% to 26% as compared with untreated composites. J. VINYL ADDIT. TECHNOL., 26:127–134, 2020. © 2019 Society of Plastics Engineers     

Short sisal fiber‐reinforced tire rubber composites: Dynamic and mechanical properties

The world tendency toward using recycled materials demands new products from vegetable resources and waste polymers. In this work, composites made from powdered tire rubber (average particle size: 320 μm) and sisal fiber were prepared by hot‐press molding and investigated by means of dynamic mechanical thermal analysis and tensile properties. The effects of fiber length and content, chemical treatments, and temperature on dynamic mechanical and tensile properties of such composites were studied. The results showed that mercerization/acetylation treatment of the fibers improves composite performance. Under the conditions investigated the optimum fiber length obtained for the tire rubber matrix was 10 mm. Storage and loss moduli both increased with increasing fiber content. The results of this study are encouraging, demonstrating that the use of tire rubber and sisal fiber in composites offers promising potential for nonstructural applications. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 91: 670–677, 2004     

Structure and properties of UHMWPE fiber/carbon fiber hybrid composites

Ultrahigh molecular weight polyethylene (UHMWPE) fiber/carbon fiber hybrid composites were prepared by inner‐laminar and interlaminar hybrid way. The mechanical properties, dynamic mechanical analysis (DMA), and morphologies of the composites were investigated and compared with each other. The results show that the hybrid way was the major factor to affect mechanical and thermal properties of hybrid composites. The resultant properties of inner‐laminar hybrid composite were better than that of interlaminar hybrid composite. The bending strength, compressive strength, and interlaminar shear strength of hybrid composites increased with an increase in carbon fiber content. The impact strength of inner‐laminar hybrid composite was the largest (423.3 kJ/m²) for the UHMWPE fiber content at 43 wt % to carbon fiber. The results show that the storage modulus (E′), dissipation factor (tan δ), and loss modulus (E″) of the inner‐laminar hybrid composite shift toward high temperature remarkably. The results also indicate that the high‐performance composite with high strength and heat resistance may be prepared by fibers' hybrid. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 101: 1880–1884, 2006     

Relationship between processing and properties of biodegradable composites based on PCL/starch matrix and sisal fibers

Biocomposites were produced using polycaprolactone and starch as matrix, and sisal fibers as reinforcement. The matrix is a biodegradable commercial product called MaterBi‐Z, which is based on a polycaprolactone and starch system. The relationship between processing conditions and properties is reported. An alkaline treatment was performed in order to improve the adhesion and the compatibility of the fiber with the matrix. The effect of the treatment on the tensile properties and morphology was determined. Fiber content enhances the tensile properties of the biodegradable composite. The experimentally observed tensile properties (modulus and tensile strength) of short sisal fiber reinforced MaterBi‐Z matrix composites with different fiber loading are compared with the existing theories of reinforcement. SEM photomicrographs of the fractured composite surfaces are also analyzed.     

剑麻纤维增强热塑性淀粉复合材料的制备及性能研究

为研究剑麻纤维增强的热塑性淀粉复合材料的制备工艺及热稳定性,以玉米淀粉为原料,先制得热塑性淀粉,再以剑麻纤维为骨架增强体制备剑麻纤维增强热塑性淀粉复合材料,通过正交试验优化制备工艺,DSC、TG/DTG、SEM分析其热稳定性及结构。正交试验表明,各因素对材料抗拉强度影响的主次顺序为纤维长度 >纤维用量 >模压成型温度 >填料用量;最佳工艺条件为纤维长度15mm、纤维用量35g、模压成型温度200℃、填料用量5g,此时材料的抗拉强度可达到4.45MPa。利用差示扫描量热分析和热重分析分别对热塑性淀粉及剑麻纤维复合材料的热稳定性进行了分析,结果表明,热塑处理提高了淀粉的熔融温度,有利于淀粉与纤维素羟基间的氢键结合,且热塑过程在一定程度上降低了淀粉的热稳定性;剑麻纤维复合材料的热降解过程主要发生在200~400℃温度区间。SEM分析显示最佳工艺条件下得到的复合材料具有较好的泡孔结构。     

Effects of peroxide crosslinking on the mechanical and morphological properties of poly(ethylene‐co‐vinyl acetate)/zeolite composites

Uncrosslinked and chemically crosslinked ethylene‐vinyl acetate copolymers (EVAs) with 5–25 volume percentages of zeolite were prepared in a melt‐mixing process and then compression‐molded on a hot‐press machine according to standard test specifications. The mechanical properties measured by tensile test showed a reduction in tensile strength and elongation at break with increasing zeolite content. However, an increasing trend was observed for tensile modulus with addition of zeolite. Experimental results for ultimate stress were compared with those from Pukanszky equation. The experimental data showed a good fit to the Pukanszky model. The improvement in the interfacial interaction for crosslinked composites was also confirmed by this model. Morphological changes of EVA/zeolite composites were analyzed by scanning electron microscopy (SEM). The fractured surface of the composites indicated more complex morphology at higher zeolite loading. The influence of crosslinking induced by 2 wt% of dicumyl peroxide on the properties of EVA/zeolite composites was also investigated. The crosslinked composites showed better tensile properties than the uncrosslinked ones, a result which might be an indication of enhanced interaction between the EVA and zeolite. Density measurements, gel content determinations, and Fourier transform infrared analyses were also performed to evaluate the crosslink content of the composites. The changes in the properties of chemically crosslinked EVA/zeolite composites were observed. Meanwhile, SEM micrographs of the crosslinked EVA/zeolite composites showed better interfacial strength between zeolite and the EVA matrix as compared to that of the uncrosslinked composites. J. VINYL ADDIT. TECHNOL., 2012. © 2012 Society of Plastics Engineers     

Bio‐composites for structural applications: Poly‐l‐lactide reinforced with long sisal fiber bundles

Fully bio‐based and biodegradable composites were compression molded from unidirectionally aligned sisal fiber bundles and a polylactide polymer matrix (PLLA). Caustic soda treatment was employed to modify the strength of sisal fibers and to improve fiber to matrix adhesion. Mechanical properties of PLLA/sisal fiber composites improved with caustic soda treatment: the mean flexural strength and modulus increased from 279 MPa and 19.4 GPa respectively to 286 MPa and 22 GPa at a fiber volume fraction of V_f = 0.6. The glass transition temperature decreased with increasing fiber content in composites reinforced with untreated sisal fibers due to interfacial friction. The damping at the caustic soda‐treated fibers‐PLLA interface was reduced due to the presence of transcrystalline morphology at the fiber to matrix interface. It was demonstrated that high strength, high modulus sisal‐PLLA composites can be produced with effective stress transfer at well‐bonded fiber to matrix interfaces. © 2014 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2014 , 131, 40999.     

Morphology and mechanical properties of unidirectional sisal– epoxy composites

Plant fibers are of increasing interest for use in composite materials. They are renewable resources and waste management is easier than with glass fibers. In the present study, longitudinal stiffness and strength as well as morphology of unidirectional sisal–epoxy composites manufactured by resin transfer molding (RTM) were studied. Horseshoe‐shaped sisal fiber bundles (technical fibers) were nonuniformly distributed in the matrix. In contrast to many wood composites, lumen was not filled by polymer matrix. Technical sisal fibers showed higher effective modulus when included in the composite material than in the technical fiber test (40 GPa as compared with 24 GPa). In contrast, the effective technical fiber strength in the composites was estimated to be around 400 MPa in comparison with a measured technical fiber tensile strength of 550 MPa. Reasons for these phenomena are discussed. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 84: 2358–2365, 2002     

Mechanical,thermal, and water absorption properties of melamine–formaldehyde‐treated sisal fiber containing poly(lactic acid) composites

The present study focuses on the melamine–formaldehyde (MF) coating ratio and silanization of PLA/sisal composites. Poly(lactic acid) (PLA) was melt blended with short sisal fiber with and without MF resin coating. MF was applied at different weight ratios (sisal:MF = 1:1; 1:3, and 1:5) to coat the untreated or silanized sisal fibers which were incorporated up to 20 parts per hundred resin (phr) amount in PLA. PLA/sisal composites were produced by compression molding. It was found that the sisal:MF coating ratio at 1:1 by weight improved the tensile strength and tensile modulus of the composite with 10 phr sisal by 4% and 57%, respectively, compared to the virgin PLA. The initial and final decomposition (T_i) and (T_f) of PLA with untreated sisal were changed from 330.8 and 367.1 to 336.2 and 370.4 °C, respectively, after MF‐coating (sisal:MF weight ratio = 1:1). This enhancement in thermal stability was attributed to the strong interaction between the MF and sisal fiber. The water absorption of PLA/MF–sisal composites slightly decreased with increasing sisal:MF ratio. This is due to the fact that the MF‐coating substantially reduced the hydrophilic properties of sisal. Moreover, FTIR spectra and SEM images proved that sisal fibers were coated by MF resin successfully. © 2017 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2018 , 135, 45681.