添加铜钼镍对NdFeCoB合金磁粉性能的影响

采用HDDR方法制备了磁各向异性NdFeCoB合金磁粉,并研究了添加Cu、Mo、Ni对其磁性能和磁各向异性的影响。结果表明:加入少量的Cu、Mo可以增加该合金的剩磁Br和矫顽力Hci,但随着其含量的增加,Br与Hci降低,当铜摩尔分数x为0.1时,Br达到最大值1.12T;钼摩尔分数y为0.7时,Hci可达到752.4kA/m;磁各向异性(以取向度cosθ计)会随x的增加而增加,在x为0.7时cosθ达到0.73;随着Mo摩尔分数y的增加,cosθ先增大后减少。随着Ni摩尔分数z的增加,Br变化很小,Hci降低,cosθ增加。     

磁性材料专题

高温稳定、高磁性能2：17型SmCo永磁体绝缘特性的研究;多层Z型六方铁氧体磁导率频率特性研究;制备工艺对Co2Z六方晶系铁氧体电磁特性的影响;Mn在HDDR各向异性NdFeCoB磁粉中的作用;二氧化硅包覆片状金属磁性微粉电磁特性茔分析。     

Nb添加对Fe-Y-B合金非晶形成能力和磁性能的影响

利用单辊快淬法制备了Fe74Y6-xNbxB20(x=0,1,2,3,4)非晶合金条带,利用XRD、HRTEM、DTA和VSM对样品的结构、非晶形成能力和磁性能等进行了测试。结果表明:Fe74Y6–xNbxB20(x=1,2,3,4)合金系的饱和磁化强度Ms>104 A.m2/kg,矫顽力Hc<1.59 kA/m,显示出良好的软磁性能。添加微量Nb扩大了非晶合金的过冷液相区,当Nb含量为摩尔分数1%时,过冷液相区Tx=63℃,此时合金具有最大的非晶形成能力,同时具有最大的饱和磁化强度(Ms=133 A.m2/kg)和最低的矫顽力(Hc=1.27 kA/m)。     

磁性材料、超导材料和器件

TM271 2002060054HDDR三元Nd凡B各向异性材料的制备/韩景智,孙爱芝,刘涛,肖耀福,王润(北京科技大学)11北京科技大学学报.一2002,24(2)一137一140研究了HDDR三元NdFeB各向异性磁粉的制备工艺.发现脱氢速度对HDDR三元各向异性NdFeB的磁性能具有显著影响.缓慢的脱氢处理有助于材料获得高的各向异性.在最佳工艺条件下,可获得磁能积为84kJ·m3的HDDR三元NdFeB各向异性粘结磁体图7表1参8(木)P rZ(FeCo)1。B/a一(Fe,Co)纳米复合永磁合金的组织与磁性/包小倩,张茂才、刘湘华,乔yi,高学绪,周寿增(北京科技大学)“北京科技大学学报.一2…     

溶胶pH值对CoFe_2O_4/SiO_2复合薄膜结构和磁性能的影响

采用sol-gel法制备了纳米CoFe2O4/SiO2复合薄膜(样品)。利用X射线衍射仪、原子力显微镜、振动样品磁强计对样品的结构、形貌和磁性能进行了研究。结果表明:随着溶胶pH值的减小,样品中CoFe2O4的平均晶粒尺寸变小,CoFe2O4晶粒沿(111)晶面择优取向生长。样品的矫顽力随着平均晶粒尺寸的减小明显变大,当溶胶pH值为0.29时,垂直和平行膜面的矫顽力分别为290 kA.m–1和250 kA.m–1,样品具有较明显的垂直磁各向异性。当溶胶pH值为0.59时,样品垂直和平行膜面的剩磁比(Mr/Ms)分别为53.2%和51.5%。     

铁基非晶软磁合金的制备及磁性能研究

研究了铁基非晶(Fe1–xCox)78.4Nb2.6Si9.0B9.0Cu1.0(x=0,0.15,0.35,0.55或0.75)软磁合金的制备工艺及磁性能。结果表明:采用熔体快淬法制备的非晶薄带宽约3mm,厚20～40μm;最佳工艺参数为铜轮转速35m/s,熔体射流压力0.14MPa;借XRD分析了合金的相结构,发现合金薄带为非晶态;通过振动样品磁强计(VSM)测量了磁性能,其Bs大于1.00T,Hc为2.31～5.17kA/m。用畴壁钉扎效应分析了Hc偏高的原因。     

磁性材料、超导材料和器件

TM27 96020047第十四届国际磁体工艺会议概况/余运佳,严陆光,李满园(中国科学院电工所)l/低温与超导.一1995,23(4)一66~68 介绍了第十四届国际磁体工艺会议的情况.本届大会共收到论文406篇,大会特邀报告10篇,参加代表379人,讨论了磁体技术的现状和发展。(木)5(木)TM271 96020048HDDR法制备高矫顽力NdF’eB磁粉及其微观研究/张炼,李隆,李祖鑫(华南理工大学)/l华南理丁大学学报一1995,23(7)一92一95 通过HDDR法制备出察矫顽力达到1200kA/m的NdFeB各向同性粘结磁粉,·探讨了温度、时间、抽速等工艺参数对获取高顽力的作用。图4表2参4(…     

Al含量对Ho-Co合金吸波性能的影响

通过高温电弧合金熔炼技术制备了Ho2Co17–xAlx(x=0,0.4,0.8,1.2,1.6)合金微粉,采用XRD和SEM分析了所制合金微粉的组成相和微结构,使用网络矢量分析仪研究了其吸波性能。结果表明:其所制样品均由Ho2Co17相组成;在吸波涂层厚度d=1.5 mm时,随x的增大,Ho2Co17–xAlx合金微粉的反射率最小值从–11.4 dB(x=0)降低到–49.8 dB(x=1.6)。同时,Al的添加会使Ho2Co17的吸收峰向高频移动,吸收峰频率从7.28 GHz(x=0)升高到14.32 GHz(x=1.6)。     

Fe93–xZr7Bx（x=10,12,14）合金的微观结构、热性能和磁性能研究

采用单辊快淬法制备了Fe93–x Zr7Bx(x=10,12,14)合金,并对三种合金进行了不同温度退火处理,利用X射线衍射仪(XRD)、差热分析仪(DTA)和振动样品磁强计(VSM)研究了该系列合金的微观结构、热性能和磁性能。研究结果表明:B含量的增加提高了合金的第一晶化峰峰值温度。在Fe83Zr7B10合金晶化初期仅观察到α-Fe相,而在Fe93–x Zr7Bx(x=12,14)合金晶化初期可观察到α-Fe相和Fe23B6相。三种合金淬态时的Ms随B含量的增加而增大。在高于823 K的温度下退火后,三种合金的Ms随B含量的增加而减小。高于773 K退火后,三种合金的Hc随B含量的增加而增大。     

Fe_(74)Co_xY_(6-x)B_(20)合金的热稳定性和磁性

采用单辊快淬法制备合金薄带Fe74CoxY6-xB20(粒子数分数x=2,3,4)合金系,取不同的温度对合金进行热处理,用X射线衍射(XRD),差热分析仪(DSC),振动样品磁强计(VSM)等测试手段对样品的晶化过程、热性能和磁性能进行研究。结果表明:制备的Fe74CoxY6–xB20均为非晶合金,Fe74CoxY6-xB20(x=2,3,4)非晶合金的晶化激活能分别为473.7,583.0和570.1kJ/mol,Fe74Co3Y3B20非晶合金热稳定性最好。非晶合金Fe74CoxY6-xB20(x=2,3,4)的饱和磁化强度MS分别为110,105和109A·m2·kg–1,矫顽力都较低,适量地添加Co提高了合金的非晶形成能力和磁性能。     

Enhanced Magnetic Anisotropy and Orbital Symmetry Breaking in Manganite Heterostructures

Manipulating magnetic anisotropy in complex oxide heterostructures has attracted much attention. Here, three interface‐engineering approaches are applied to address two general issues with controlling magnetic anisotropy in the La_2/3Sr_1/3MnO₃ heterostructure. One is the paradox arising from the competition between Mn_3d–O_2p orbital hybridization and MnO₆ crystal field. The other is the interfacial region where the nonuniform Mn? O bond length d and Mn? O? Mn bond angle θ disturb the structural modulation. When the interfacial region is suppressed in the interface‐engineered samples, the lateral magnetic anisotropy energy is increased eighteen times. The d‐mediated anisotropic crystal filed that overwhelms the orbital hybridization causes the lateral symmetry breaking of the Mn 3d_x²_?y² orbital, resulting in enhanced magnetic anisotropy. This is different from the classic Jahn–Teller effect where the lateral symmetry is always preserved. Moreover, the quantitative analysis on X‐ray linear dichroism data suggests a direct correlation between Mn 3d_x²_?y² orbital symmetry breaking and magnetic anisotropy energy. The findings not only advance the understanding of magnetic anisotropy in manganite heterostructures but also can be extended to other complex oxides and perovskite materials with correlated degrees of freedom.     

CCVD Synthesis of Carbon‐Encapsulated Cobalt Nanoparticles for Biomedical Applications

Carbon‐encapsulated ferromagnetic Cobalt nanoparticles (Co@C) have been synthesized by catalytic chemical vapour deposition (CCVD). The nanoparticles, mainly ranging between 10 and 15 nm, are tightly encapsulated by 2–3 concentric graphitic carbon shells and protected from oxidation. Because of their magnetic properties (saturation magnetization of 106 emu/g and a coercivity HC of 250 Oe), Co@C nanoparticles have been investigated for hyperthermia application. Although the observed values of the specific absorption rate (28.7 W/gCo@C at 30 kA/m and 215.4 W/gCo@C at 70 kA/m) are slightly lower than required in actual hyperthermia therapies, the observed strong heating effect provides a very promising starting point for future clinical application. It is also demonstrated that these nanoparticles can at the same time be used for magnetic resonance imaging (MRI) with an efficiency comparable to commercially available T2 contrast agents.     

NdFeB磁粉对粘结NdFeB/锶铁氧体复合磁体性能的影响

采用流动温压成型技术制备了各向同性粘结NdFeB/锶铁氧体复合磁体。研究了不同类型NdFeB磁粉对粘结NdFeB/锶铁氧体复合磁体磁性能和交换耦合作用的影响。结果表明,粘结贫稀土NdFeB/锶铁氧体复合磁体的综合磁性能最好,当NdFeB和铁氧体的质量比为3:2时,其磁性能Br=0.38 T,Hcj=524 kA/m,(BH)max=21.9 kJ/m3;另外,其Henkel曲线为典型的S型曲线。粘结纳米双相NdFeB/锶铁氧体复合磁体内的交换耦合作用近乎消失,磁体内以静磁交互作用为主。     

Co-Cu亚稳态块状合金的磁阻效应

利用高能球磨和冲击压缩制备了CoxCu100-x(x=10～30)亚稳态块状合金,并研究了其退火后的磁阻(magnetoresistance,MR)效应.在室温,1 000 kA/m磁场强度下的MR测试结果显示,当退火温度低于450℃时,Co30Cu70合金显示出较大的磁阻比(MR比),然而当退火温度高于450℃时,C...     

玻璃粉含量对钡铁氧体厚膜磁性能的影响

采用丝网印刷法制备了钡铁氧体厚膜,系统研究了玻璃粉含量对钡铁氧体厚膜磁性能的影响。结果表明,随着玻璃粉含量的增大,样品的致密度逐渐提高;饱和磁化强度、剩磁和矫顽力均呈现出先增大后减小的趋势;而剩磁比(Mr/Ms)单调上升。当玻璃粉含量增大到质量分数7%时,所制得样品的饱和磁化强度、剩磁和矫顽力均达到最大值,分别为151,76.6,310 kA/m。当玻璃粉含量为质量分数13%时,剩磁比达到0.615。     

铁磁性微晶玻璃的制备

采用熔融法制备了SiO_2-Na_2O-CaO-P_2O_5-Fe_2O_3系微晶玻璃。制备过程中磁铁矿晶相在玻璃自然冷却时自然析出,故不需要对玻璃进行核化和晶化等热处理。利用XRD确定了样品晶相组成并计算了样品中晶体的晶格常数和晶粒度,采用振动样品磁强计(VSM)测试了样品的磁性能。结果表明:所制微晶玻璃只含有磁铁矿晶相并具有生物活性;Fe_2O_3质量分数为45%的样品性能最佳,其比饱和磁矩为20.24A·m~2/kg,内禀矫顽力H_(cj)为7kA/m。     

球磨与共沉淀法制备MnZn铁氧体的对比研究

分别采用高能球磨和化学共沉淀法制备了MnZn铁氧体,通过XRD、VSM和金相显微镜的分析,对两种铁氧体的预烧料粉末、烧结体的显微结构以及磁性能做了比较。结果表明:化学共沉淀法所制备的预烧料粉末具有晶粒细小、均匀和活性高等优点;与高能球磨法相比,化学共沉淀法烧结磁体的密度较高、晶粒尺寸较大,磁性能更为优良。其相应的磁性能参数Ms、Mr、Hc和μi分别为3.845×102kA/m,3.421kA/m,0.722kA/m和5500。