Enhanced corrosion resistance of micro-arc oxidation coated magnesium alloy by superhydrophobic Mg−Al layered double hydroxide coating

To further enhance the corrosion resistance of the porous micro-arc oxidation (MAO) ceramic layers on AZ31 magnesium alloy, superhydrophobic Mg−Al layered double hydroxide (LDH) coating was fabricated on MAO-coated AZ31 alloy by using in-situ growth method followed by surface modification with stearic acid. The characteristics of different coatings were investigated by XRD, SEM and EDS. The effect of the hydrothermal treatment time on the formation of the LDH coatings was studied. The results demonstrated that the micro-pores and cracks of MAO coating were gradually sealed via in-situ growing LDH with prolonging hydrothermal treating time. Electrochemical measurement displayed that the lowest corrosion current density, the most positive corrosion potential and the highest impedance modulus were observed for superhydrophobic LDH/MAO coating compared with those of MAO coating and LDH/MAO coating. Immersion experiment proved that the superhydrophobic LDH/MAO coating with the active anti-corrosion capability significantly enhanced the long-term corrosion protection for MAO coated alloy.     

镁合金表面防腐蚀超疏水涂层制备研究进展

镁合金是一种有发展前途的绿色工程金属材料，但其较差的抗腐蚀性能限制了它的大规模应用。对镁合金表面进行超疏水处理，能够极大地提高镁合金的耐腐蚀性能。当超疏水试样浸泡在腐蚀溶液中时，该结构将在腐蚀介质中形成固-气-液界面层，减少镁合金表面与腐蚀介质之间的接触面积，从而降低腐蚀速度。超疏水表面需要满足微纳米结构和低表面能2个必要条件。可以采用二步法或一步法在镁合金表面制备超疏水表面，详细介绍了在镁合金表面构造微纳米结构的方法，包括激光处理、机加工、化学刻蚀、化学镀、电化学沉积、阳极氧化、微弧氧化、水热合成和喷涂等方法。超疏水表面一旦受到机械损伤，微纳米结构无法满足条件，超疏水表面的“气垫效应”消失，腐蚀介质就会直接与微纳米结构接触，因此需要保证构建的微纳米粗糙结构对镁基体具有良好的保护作用并具有自愈功能。通过制备复合涂层，提高下层微纳米结构的自愈合性能，上层涂层的超疏水性与下层涂层的良好物理屏障能力的协同效应可以改善涂层的长久耐腐蚀性能。综述了在镁合金上制备具有良好耐腐蚀性能的复合超疏水表面的方法，并对镁合金超疏水表面防护技术的研究方向进行了展望。     

KCC-1/PVDF超疏水与超滑表面的制备及其性能研究

目的将海胆状纳米二氧化硅(KCC-1)微球掺入聚偏氟乙烯(PVDF)中,制备出KCC-1/PVDF超疏水涂层,并在此基础上利用不同涂层修饰剂修饰,进一步制备出超滑涂层。方法以溴化十六烷基吡啶作为模板,结合煅烧法合成了海胆状KCC-1微球,分散到PVDF溶液中,在镁合金表面制备KCC-1/PVDF涂层,并进一步用不同修饰剂(全氟辛基三乙氧基硅烷(PFOTES)、十六烷基三甲氧基硅烷(HDTES)和二甲基硅油)对涂层表面进行改性。结果经过十六烷基三甲氧基硅烷改性,得到水接触角为155°的超疏水涂层,而灌注二甲基硅油后得到滑动角为4.5°的超滑表面。摩擦磨损实验中,超滑表面的耐磨性优于超疏水表面,优于空白镁合金;防覆冰实验结果表明超疏水和超滑表面能有效延缓液滴在表面结冰。结论KCC-1/PVDF超疏水与超滑涂层能有效地保护镁合金基底,且超滑涂层的防腐蚀性优于超疏水涂层,其腐蚀抑制效率IE分别为100%和98.28%。     

Electroplated super-hydrophobic Zn-Fe coating for corrosion protection on magnesium alloy

A superhydrophobic Zn-Fe alloy coating was prepared on the surface of a reactive magnesium alloy using a simple, low-cost, eco-friendly method. Firstly, the Zn-Fe coating was obtained in a neutral glycerol Zn-Fe plating solution, which is green, compositionally stable, and non-corrosive to the equipment. And then the superhydrophobic surface with a flower-like microstructure was obtained by grafting myristic acid onto the Zn-Fe coating via a chelation reaction. The water contact angle was >150° and the rolling angle was 3°-4°. The corrosion rate of the two groups of superhydrophobic magnesium alloy samples with electrodeposition time of 30 and 50 min, respectively, was reduced by about 87% compared to that of the bare magnesium alloy. The prepared superhydrophobic coatings exhibit high performance in self-cleaning, abrasion resistance, and corrosion resistance.     

耐久超疏水涂层的制备及其防冰防腐自清洁性能

超疏水涂层在防结冰、防腐蚀等领域具有广阔的应用前景,然而目前仍无法大规模制备稳定的超疏水表面。提出一种操作简单、成本低廉的方法,在铝合金基材上通过一步喷涂法制备出耐磨超疏水涂层。首先在铝合金基体表面涂覆环氧树脂粘结层,待其达到半固化状态时,喷涂硬脂酸修饰的微米 SiO₂ 和纳米 TiO₂ 粒子混合悬浮液,固化后该涂层与水的接触角为~ 155.4°,滚动角为~3°,实现了超疏水性。试验结果表明,该超疏水涂层具有较好的耐磨耐久性,在胶带剥离、砂纸摩擦、 紫外光长时间照射以及不同 pH 液滴等多种测试条件下仍具有良好的超疏水性。此外,此超疏水涂层在极端寒冷的天气下可以显著延缓水的冻结时间。环氧树脂和疏水颗粒的协同防腐作用使超疏水涂层在海水中表现出良好的防腐蚀性能。所制备的超疏水涂层还具有优异的自清洁特性,且因 TiO₂ 粒子本身的光降解性能,该涂层还可用于光降解污染物和净化水质。这种简单、环保的超疏水涂层在防结冰、防腐蚀等方面具有潜在的应用前景,可为克服传统超疏水表面使用耐久性差的问题提供解决思路。     

光催化型超疏水自清洁涂层研究现状

光催化型超疏水自清洁涂层是在超疏水涂层的基础上通过物理、化学方法复合光催化材料获得光催化性能，使涂层可以在光照作用下将有机附着物进行分解并通过超疏水表面达到自清洁的效果。本文对国内外光催化型超疏水自清洁涂层的构建方式进行总结，将其归纳为表面构造法、共混法、包覆法3类，构造方法的不同对涂层性能的影响方面也有所区别。与单一功能的超疏水涂层相比光催化型超疏水自清洁涂层更能解决实际应用中所面临的问题。此外，本文对光催化型超疏水自清洁涂层的相关性能进行了横向对比，对影响涂层性能较为关键的耐久性能进行了整体的整理分析，并归纳了目前研究当中的光催化型超疏水自清洁涂层的机械耐磨性、耐腐蚀性、耐冲击性和自愈性能，分析了其耐久性提升机制。最后，对光催化型超疏水自清洁涂层未来的应用前景进行了展望，建议从超疏水-光催化协同作用机制、基底结合强度提升、成本控制和复合涂层自修复等方面对光催化型超疏水自清洁涂层进行研究。     

镁合金超疏水表面制备技术的研究进展

超疏水表面因其在日常生活及工农业生产等领域有巨大的应用前景而受到科研人员的广泛关注。基于镁及其合金基底超疏水表面的制备研究可以加深对材料特性的认识、扩展材料应用范围和提高材料应用性能而具有重要的意义。介绍了超疏水表面的相关理论基础和超疏水状态下的两类模型及其相互关系,对两类模型下表面微细结构和固体表面化学成分对接触角的影响进行了讨论。从构建超疏水表面的两种途径出发,一是在低表面能物质上构建特殊微细结构,二是在微细结构表面利用低表面能物质进行修饰,着重总结归纳了镁合金基底超疏水表面制备技术的研究进展,并对镁合金超疏水表面的发展进行了展望。     

超疏水表面服役稳定性的研究进展

目的 超疏水表面脆弱、耐久性差且难以修复等情况一直是超疏水涂层在实际应用过程中面临的最大挑战，通过总结和分析找到解决这一问题的方法。方法 本文对超疏水涂层可能遇到的破坏和对应的耐久性类型进行了系统分析和总结，针对每种耐久性类型分别归纳出多种测试方法并对每种测试方法对应的控制参数进行了详细阐述，对不同耐久性类型和测试方法也分别进行了详细的举例说明。结果 针对超疏水涂层耐久性差的问题，本文总结出两类提高表面耐久性的方法，分别是是提高超疏水涂层的机械稳定性和赋予涂层良好的自修复能力。提高涂层机械耐久性的方法包括构造多层次分层结构、提高涂层与基底的黏结能力、构建自相似超疏水表面，记忆建立“盔甲”结构等。自修复能力包括粗糙结构的自修复、低表面能物质的自修复、整体的自修复。结论 有了强机械稳定性，超疏水涂层在面对破坏时也有了更好的抵御能力。而具备良好的自修复能力，则可以保障涂层在被破坏后仍可以恢复至超疏水状态。此外，本文还对超疏水涂层的未来发展进行了展望，即找到一种满足各种耐久需求、低成本、适合大面积生产的超疏水表面制备方法。     

投料顺序对镁合金表面层状双金属氢氧化物涂层性能的影响

为了考察不同投料顺序对镁合金表面层状双金属氢氧化物(LDHs)涂层性能的影响,并得到一种具有较好耐腐蚀能力的镁合金防腐蚀涂层,通过水热合成法采用不同投料顺序在镁合金表面原位沉积LDHs涂层。使用SEM、XRD、EIS、Tafel曲线和直接浸泡的方法,分别对LDHs涂层的表面形貌、结构和耐腐蚀性能进行评估。结果发现,采用不同的投料顺序得到了不同表面形貌、相似结构和不同耐腐蚀能力的LDHs涂层。所有LDHs涂层的自腐蚀电位、自腐蚀电流密度和阻抗模量相对于基底都分别发生了明显的正移、下降和增加,电位正移值约为0.7 V,自腐蚀电流密度降低值达到3~4个数量级,阻抗模量增加约4个数量级。以上结果表明通过控制投料顺序可以得到具有不同表面形貌的LDHs涂层。采用向硝酸铝中添加硝酸镁后调节溶液p H,再加入碳酸钠的投料顺序,得到LDHs涂层在NaCl溶液中的耐腐蚀能力最好。     

High-speed wire electrical discharge machining to create superhydrophobic surfaces for magnesium alloys with high corrosion and wear resistance

Herein, a superhydrophobic surface of AZ31B magnesium alloy prepared by high-speed wire electrical discharge machining and modification with stearic acid is reported. The surface morphology and wettability of the superhydrophobic surface were investigated by scanning electron microscopy and optical contact angle measurement, respectively. A uniform micro-/nanopetal-like structure was shown within the superhydrophobic surface, resulting in a contact angle of 151 ± 0.5° and a sliding angle of 4 ± 0.5°. Notably, the superhydrophobic surface had better corrosion resistance than the bare magnesium alloy, and its corrosion current density was reduced by nearly one order of magnitude. Under both dry and wet friction conditions, the friction coefficient of the superhydrophobic surface was lower than that of the bare magnesium alloy surface, with a much lower wear loss. In addition, the friction coefficient of the superhydrophobic sample was lower than that of the bare magnesium alloy sample under both the dry and wet friction conditions. Thus, the superhydrophobic sample experienced reduced wear and had a low wear rate.     

平行沟槽织构对TB6钛合金表面润湿性、摩擦学性能和耐腐蚀性的改善

提出了一种快速制备具有超疏水性、耐磨性和耐腐蚀性的Ti-10V-2Fe-3Al （TB6）钛合金表面的方法。通过纳秒激光器对抛光的钛合金进行精确烧蚀,构筑了具有平行微沟槽阵列特征的织构表面。随后,利用紫外线灯照射和十八烷基三氯硅烷溶液浸渍进行化学改性,进一步增强了表面的疏水性。从表面形态和化学组分的角度分析了微沟槽间隔对织构表面润湿性的影响。结果表明,在干滑动、水润滑和油润滑条件下,所制备的超疏水表面相较于原始亲水表面,平均摩擦系数分别降低了34%、56%和59%。此外,分析了相关摩擦系数变化的机理。通过动电位极化测试验证,所制备的超疏水表面展现出优异的耐腐蚀性,为钛合金基体提供了有效的长期保护。     

硅橡胶超疏水涂层的撒粉法制备

当前在橡胶基体上构建超疏水表面的方法大多较为复杂,不易制备,研究一种简单方法是十分必要的。以高温硫化硅橡胶(HTV)为基体,把基体打磨后在其表面覆盖一层聚二甲基硅氧烷(PDMS),采用表面撒粉法将二氧化硅(SiO₂)粉末均匀撒在未固化PDMS上,固化后制得HTV/PDMS-SiO₂超疏水表面。采用扫描电子显微镜、三维形貌及接触角测量仪对硅橡胶超疏水涂层的微观形貌和疏水特性进行分析。结果表明：HTV/PDMS-SiO₂超疏水表面构建出许多微纳突起粗糙结构,表面粗糙度Sa达到35.695μm;HTV/PDMS-SiO₂超疏水表面的静态接触角平均值达154.5°,相较于原始硅橡胶平均静态接触角112.4°提升了37.5%;液滴体积一定时,液滴接触到超疏水表面后的铺展直径和第一次弹起高度随着滴落高度的增大而增大;液滴滴落高度一定时,液滴铺展直径和初次弹起高度与液滴体积成正比。利用PDMS固化过程结合撒粉工艺构建超疏水微纳结构,可为硅橡胶超疏水表面研究提供一种简单、低成本方案。     

超疏水Ni-P-Al2O3纳米复合镀层的制备及耐腐蚀性能研究

为提高45钢基体材料的耐腐蚀性能,采用电化学法与氟硅烷修饰相结合的方式在45钢基体表面制备超疏水Ni-P-Al2O3纳米复合镀层,并对镀层的表面形貌、晶相结构、表面粗糙度、润湿性及耐蚀性能进行了研究。结果表明:采用电沉积法制备的Ni-P-Al2O3镀层表面均匀、致密,且无明显气孔缺陷,接触角测试表明其表面达到了超疏水状态,而经电化学加工后,镀层表面形成不规则的微凹坑结构,表面粗糙度值明显增大。经电化学测试,与普通Ni-P-Al2O3镀层相比,超疏水Ni-P-Al2O3镀层的腐蚀电流密度、腐蚀速率均更小,表现出优异的耐腐蚀性能。     

Corrosion resistance of composite coatings on low-carbon steel containing hydrophobic and superhydrophobic layers in combination with oxide sublayers

The methods for the design of highly- and superhydrophobic nanocomposite coatings on the surface of low-carbon steel with oxide layers have been described. To study the peculiarities of the corrosion processes on the coatings in NaCl solution, we have applied the electrochemical methods and the analysis of wetting. It is demonstrated that the most effective and durable protection against electrochemical corrosion is provided by multilayer coatings containing the nanocomposite superhydrophobic layer in combination with underlying oxide layer. The long-term durability of such coatings is affected by both the degree of water repellence and the imperfection of superhydrophobic and conversion layers.     

铝表面超疏水复合涂层的制备及其表面性能

目的 通过在纯铝表面构筑超疏水涂层,优化金属铝表面,并强化其应用性能。方法 采用阳极氧化法在铝表面构筑具有纳米孔洞的Al2O3薄膜,再利用全氟癸基三乙氧基硅烷修饰表面,得到超疏水复合涂层,并研究氧化电位和表面修饰时间对纳米结构的构筑及疏水性能的影响,研究超疏水复合涂层表面润湿性、防污、自清洁和抗结冰性能。结果 控制阳极氧化条件,在氧化电位为16～18V、氧化时间为1h时,得到1～2μm的“花瓣”聚集叠加成的多级粗糙结构。通过6 h的表面修饰,得到了接触角为163.6°的超疏水性复合膜层。进一步对该超疏水膜层的性能进行分析发现,经超疏水膜层修饰后铝具有优异的防污性能;相较于纯铝,经超疏水膜层修饰后铝片的电化学阻抗模值高达105?·cm2,而电流密度仅为1.81×10-9 A/cm2;在高温和低温环境下,超疏水膜层均能保持超疏水性能;经砂纸来回打磨200 cm后,膜层的接触角仍大于150°。结论 经阳极氧化纯铝得到具有多级粗糙结构的阳极氧化膜,并通过表面修饰可制备接触角高达163.6°的超疏水性复合膜层。该超疏水复合涂层具有优异的耐腐蚀性、自清洁性、耐污染性,以及良好的耐蚀性、机械稳定性和...     

修饰不同微结构对疏水性表面浸润性的影响

目的研究修饰微结构对疏水性材料表面浸润性的影响并指导制备超疏水表面。方法基于有限元软件建立了水滴在修饰不同微结构的疏水性表面的润湿模型,通过水滴表观接触角衡量分析了疏水材料表面修饰单一粗糙结构和复合粗糙结构对疏水性提升的效果,利用硅树脂掺杂微粒制备了不同粗糙度的疏水性涂层,涂层固化后测试其实际接触角大小,并与仿真结果对比。结果仿真结果显示,对水滴接触角为100°的表面修饰单一粗糙结构后,由于微结构形成的凹槽滞留空气,阻碍了水滴在表面铺展,使得水滴在表面的接触角增大至133°。在原微结构基础上修饰更小一级的微结构后,水滴在表面的接触角达168°,材料表面达到超疏水效果。实验中,随涂层表面粗糙度的提升,水滴在表面的接触角逐渐增大,掺混两种微粒的疏水涂层固化后,表面形成复合微观结构,水滴接触角达162°,与仿真结果拟合较好。结论在疏水性表面修饰微结构可显著提升其表面疏水性,修饰复合结构后可达到超疏水效果,此方法可用于实际工程制备超疏水表面。     

超疏水铝合金表面的制备及耦合机理分析

为制备超疏水铝合金表面,采用高速电火花切割技术在铝合金表面加工类水稻叶表面的沟槽结构。通过扫描电子显微镜(SEM)观测材料表面形貌,采用接触角测量仪表征水滴在材料表面的疏水性和黏附性。结果表明： 铝合金表面形成了排列规则的微米级沟槽结构,沟槽突起和底部覆盖着微米级凹坑、突起物和纳米级错层等结构。铝合金试样表面的接触角由加工前的61.24°提高至157.71°,最大达165.36°,实现了材料表面亲水向超疏水的转变。提拉法表明加工的铝合金表面具有高黏附特性。将测得的接触角与CassieBaxter模型计算的理论值进行比较,发现试样表面的超疏水性是微米级和纳米级等复合结构共同耦合作用的结果。铝合金试样表面的多尺度结构不仅提高了材料表面的疏水性能,同时也形成了试样表面的高黏附特性。     

水性超疏水复合涂料的制备及其机械稳定性

目的为了实现超疏水表面在实际生产生活中大规模应用,研制了一种具有大面积、低成本、可设计性和无有机溶剂等优点的水性超疏水涂料。方法以纳米级的气相二氧化硅和水性氟碳树脂为主要原料,以水为溶剂,通过氟硅烷疏水改性后获得了一种具有自清洁效应的超疏水涂料,借助场发射扫描电子显微镜、接触角测量仪、延时拍摄等手段对其进行了表征。结果该水性涂料可喷涂于各种软硬表面获得超疏水表面,其接触角均大于150°,滚动角均小于10°。水滴撞击实验表明,树脂增强的超疏水涂料经总体积为600 m L的连续水滴撞击后,其静态接触角依然大于150°,滚动角依然保持在10°以内。经砂纸打磨40周期后,水滴依然可以从其表面滚落。结论研制了一种以水为主要溶剂且价格低廉的水性超疏水涂料,将其喷涂于各种软、硬基底上均可获得均匀的超疏水涂层。该涂层还可以通过添加水性树脂来有效地增强其机械稳定性。     

低共熔溶剂在镁合金腐蚀防护中的应用

介绍了低共熔溶剂的性质及特点,综述了低共熔溶剂的国内外最新研究成果,特别是氯化胆碱基低共熔溶剂在镁合金腐蚀防护的应用,分析了镁合金在低共熔溶剂中进行表面处理的可行性。概述了在含氯化胆碱的低共熔溶剂介质中,通过热场、声场、电场以及DES液膜法调控开展镁合金表面化学转化膜的制备、耐蚀机理及反应介质的作用研究,同时将低共熔溶剂与疏水性仿生膜结合,设计出镁合金表面自愈合超疏水涂层。利用低共熔溶剂制备的转化膜的耐蚀性均明显高于镁合金基体,其腐蚀电流密度明显下降。最后对镁合金腐蚀防护的研究现状和方向进行了展望,希望对解决镁合金腐蚀起到一定的指导意义。     

防冰涂层材料及电力材料防覆冰应用的研究进展

防冰涂层材料可有效减轻自然界结冰现象的影响,其通过防冰材料低表面能或高润滑性的特点,降低在低温严寒天气条件下物体表面冰的粘附强度,延迟材料覆冰时间,减少表面覆冰量,在保护电力材料免受冰冻灾害影响方面有着重要应用价值.基于热喷涂法制备的复合型表面防冰涂层材料,以及主被动相结合的防覆冰方法,是未来电力材料防覆冰应用发展的重要方向.然而截止目前,有关复合型表面防冰涂层材料的热喷涂制备,以及涂层在电力材料防冰中应用的研究进展综述鲜见报道.从超疏水材料与光热、电热除冰相结合的除冰方式,及超疏水-超润滑复合材料实现防冰除冰的角度出发,对近年来国内外复合防冰涂层的制备及性能的研究进展进行了综述,并重点讨论了适合于热喷涂制备的复合型涂层的防冰除冰效果.最后,讨论了超疏水防冰涂层、复合型防冰涂层在电力材料表面防覆冰方面应用的研究进展,并对热喷涂法制备防冰涂层在的局限性问题进行了总结,对其应用前景进行了展望,希望在复合型防冰方面进一步开展研究,为电力材料表面防冰涂层的未来发展提供指导.