Structural and transport properties of LixNi1−y−zCoyMnzO2 cathode materials

In this work structural and transport properties of layered LiNi_1−y−zCo_yMn_zO₂ (y = 0.25, 0.35, 0.5 and z = 0.1) cathode materials are presented. In the considered group of oxides, LiNi_1−y−zCo_yMn_zO₂, there is no clear correlation between electrical conductivity and the a parameter (M-M distance in the octahedra layers). A non-monotonic modification of electrical properties of Li_xNi_0.65Co_0.25Mn_0.1O₂ cathode materials is observed upon lithium deintercalation.     

Structural and electrochemical characterization of xLi[Li1/3Mn2/3]O2·(1 − x)Li[Ni1/3Mn1/3Co1/3]O2 (0 ≤ x ≤ 0.9) as cathode materials for lithium ion batteries

A series of cathode materials with molecular notation of xLi[Li_1/3Mn_2/3]O₂·(1 − x)Li[Ni_1/3Mn_1/3Co_1/3]O₂ (0 ≤ x ≤ 0.9) were synthesized by combination of co-precipitation and solid state calcination method. The prepared materials were characterized by X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) techniques, and their electrochemical performances were investigated. The results showed that sample 0.6Li[Li_1/3Mn_2/3]O₂·0.4Li[Ni_1/3Mn_1/3Co_1/3]O₂ (x = 0.6) delivers the highest capacity and shows good capacity-retention, which delivers a capacity ∼250 mAh g⁻¹ between 2.0 and 4.8 V at 18 mA g⁻¹.     

Preparation and characterization of sub-micro LiNi0.5−xMn1.5+xO4 for 5 V cathode materials synthesized by an ultrasonic-assisted co-precipitation method

Sub-micro spinel LiNi_0.5−xMn_1.5+xO₄ (x < 0.1) cathode materials powder was successfully synthesized by the ultrasonic-assisted co-precipitation (UACP) method. The structure and electrochemical performance of this as-prepared powder were characterized by powder XRD, SEM, XPS, CV and the galvanostatic charge–discharge test in detail. XRD shows that there is a small Li_yNi_1−yO impurity peak placed close to the (4 0 0) line of the spinel LiNi_0.5−xMn_1.5+xO₄, and the powders are well crystallized. XPS exhibits that the Mn oxidation state is between +3 and +4, and Ni oxidation state is +2 in LiNi_0.5−xMn_1.5+xO₄. SEM shows that the prepared powders (UACP) have the uniform and narrow size distribution which is less than 200 nm. Galvanostatic charge–discharge test indicates that the initial discharge capacities for the LiNi_0.5−xMn_1.5+xO₄ (UACP) at C/3, 1C and 2C, are 130.2, 119.0 and 110.0 mAh g⁻¹, respectively. After 100 cycles, their capacity retentions are 99.8%, 88.2%, and 73.5%, respectively. LiNi_0.5−xMn_1.5+xO₄ (UACP) at C/3 discharge rate exhibits superior capacity retention upon cycling, and it also shows well high current discharge performance. CV curve implies that LiNi_0.5−xMn_1.5+xO₄ (x < 0.1) spinel synthesized by ultrasonic-assisted co-precipitation method has both reversibility and cycle capability because of the ultrasonic-catalysis.     

Effect of CO2 on layered Li1+zNi1−x−yCoxMyO2 (M = Al,Mn) cathode materials for lithium ion batteries

We investigated the effect of CO₂ on layered Li_1+zNi_1−x−yCo_xM_yO₂ (M = Al, Mn) cathode materials for lithium ion batteries which were prepared by solid-state reactions. Li_1+zNi_(1−x)/2Co_xMn_(1−x)/2O₂ (Ni/Mn mole ratio = 1) singularly exhibited high storage stability. On the other hand, Li_1+zNi_0.80Co_0.15Al_0.05O₂ samples were very unstable due to CO₂ absorption. XPS and XRD measurements showed the reduction of Ni³⁺ to Ni²⁺ and the formation of Li₂CO₃ for Li_1+zNi_0.80Co_0.15Al_0.05O₂ samples after CO₂ exposure. SEM images also indicated that the surfaces of CO₂-treated samples were covered with passivation films, which may contain Li₂CO₃. The relationship between CO₂-exposure time and CO₃²⁻ content suggests that there are two steps in the carbonation reactions; the first step occurs with the excess Li components, Li₂O for example, and the second with LiNi_0.80Co_0.15Al_0.05O₂ itself. It is well consistent with the fact that the discharge capacity was not decreased and the capacity retention was improved until the excess lithium is consumed and then fast deterioration occurred.     

Effect of Cr doping on the structural,electrochemical properties of Li[Li0.2Ni0.2−x/2Mn0.6−x/2Crx]O2 (x = 0, 0.02, 0.04, 0.06, 0.08) as cathode materials for lithium secondary batteries

Prospective positive-electrode (cathode) materials for a lithium secondary battery, viz., Li[Li_0.2Ni_0.2−x/2Mn_0.6−x/2Cr_x]O₂ (x = 0, 0.02, 0.04, 0.06, 0.08), were synthesized using a solid-state pyrolysis method. The structural and electrochemical properties were examined by means of X-ray diffraction, cyclic voltammetry, SEM and charge–discharge tests. The results demonstrated that the powders maintain the α-NaFeO₂-type layered structure regardless of the chromium content in the range x ≤ 0.08. The Cr doping of x = 0.04 showed improved capacity and rate capability comparing to undoped Li[Li_0.2Ni_0.2Mn_0.6]O₂. ac impedance measurement showed that Cr-doped electrode has the lower impedance value during cycling. It is considered that the higher capacity and superior rate capability of Cr-doping samples would be ascribed to the reduced resistance of the electrode during cycling.     

Structural and transport properties of layered Li1+x(Mn1/3Co1/3Ni1/3)1−xO2 oxides prepared by a soft chemistry method

In this work structural and transport properties of layered Li_1+x(Mn_1/3Co_1/3Ni_1/3)_1−xO₂ oxides (x = 0; 0.03; 0.06) prepared by a “soft chemistry” method are presented. The excessive lithium was found to significantly improve transport properties of the materials, a corresponding linear decrease of the unit cell parameters was observed. The electrical conductivity of Li_1.03(Mn_1/3Co_1/3Ni_1/3)_0.97O₂ composition was high enough to use this material in a form of a pellet, without any additives, in lithium batteries and characterize structural and transport properties of deintercalated Li_1.03−y(Mn_1/3Co_1/3Ni_1/3)_0.97O₂ compounds. For deintercalated samples a linear increase of the lattice parameter c together with a linear decrease of the parameter a with the increasing deintercalation degree occurred, but only up to 0.4-0.5 mol of extracted lithium. Further deintercalation showed a reversal of the trend. Electrical conductivity measurements performed of Li_1.03−y(Mn_1/3Co_1/3Ni_1/3)_0.97O₂ samples (y = 0.1; 0.3; 0.5; 0.6) showed an ongoing improvement, almost two orders of magnitude, in relation to the starting composition. Additionally, OCV measurements, discharge characteristics and lithium diffusion coefficient measurements were performed for Li/Li⁺/Li_1.03−y(Mn_1/3Co_1/3Ni_1/3)_0.97O₂ cells.     

On the LiNi0.2Mn0.2Co0.6O2 positive electrode material

Layered LiNi_0.2Mn_0.2Co_0.6O₂ phase, belonging to a solid solution between LiNi_1/2Mn_1/2O₂ and LiCoO₂ most commercialized cathodes, was prepared via the combustion method at 900 °C for a short time (1 h). Structural, electrochemical and magnetic properties of this material were investigated. Rietveld analysis of the XRD pattern shows this compound as having the α-NaFeO₂ type structure (S.G. R-3m; a = 2.8399(2) ?; c = 14.165(1) ?) with almost none of the well-known Li/Ni cation disorder. SQUID measurements clearly indicate that the studied compound consists of Ni²⁺, Co³⁺ and Mn⁴⁺ ions in the crystal structure. X-ray analysis of the chemically delithiated Li_xNi_0.2Mn_0.2Co_0.6O₂ phases reveals that the rhombohedral symmetry was maintained during Li-extraction, confirmed by the monotonous variation of the potential-composition curve of the Li//Li_xNi_0.2Mn_0.2Co_0.6O₂ cell. LiNi_0.2Mn_0.2Co_0.6O₂ cathode has a discharge capacity of ∼160 mAh g⁻¹ in the voltage range 2.7-4.3 V corresponding to the extraction/insertion of 0.6 lithium ion with very low polarization. It exhibits a stable capacity on cycling and good rate capability in the rate range 0.2-2 C. The almost 2D structure of this cathode material, its good electrochemical performances and its relatively low cost comparing to LiCoO₂, make this material very promising for applications.     

The influence of compositional change of 0.3Li2MnO3·0.7LiMn1−xNiyCo0.1O2 (0.2 ≤ x ≤ 0.5, y = x − 0.1) cathode materials prepared by co-precipitation

Cathode materials prepared by a co-precipitation are 0.3Li₂MnO₃·0.7LiMn_1−xNi_yCo_0.1O₂ (0.2 ≤ x ≤ 0.4) cathode materials with a layered-spinel structure. In the voltage range of 2.0-4.6 V, the cathodes show more than one redox reaction peak during its cyclic voltammogram. The Li/0.3Li₂MnO₃·0.7LiMn_1−xNi_yCo_0.1O₂ (x = 0.3, y = 0.2) cell shows the initial discharge capacity of about 200 mAh g⁻¹. However, when x = 0.2 and y = 0.1, the cell exhibits a rapid decrease in discharge capacity and poor cycle life.     

Electrochemical performance of SrF2-coated LiNi1/3Co1/3Mn1/3O2 cathode materials for Li-ion batteries

SrF₂-coated LiNi_1/3Co_1/3Mn_1/3O₂ cathode materials with improved cycling performance over 2.5–4.6 V were investigated. The structural and electrochemical properties of the materials were studied using X-ray diffraction (XRD), scanning electron microscope (SEM), charge–discharge tests and electrochemical impedance spectra (EIS). The results showed that the crystalline SrF₂ with about 10–50 nm particle size is uniformly coated on the surface of LiNi_1/3Co_1/3Mn_1/3O₂ particles. As the coating amount increased from 0.0 to 2.0 mol%, the initial capacity and rate capability of the coated LiNi_1/3Co_1/3Mn_1/3O₂ decreased slightly owing to the increase of the charge-transfer resistance; however, the cycling stability was improved by suppressing the increase of the resistance during cycling. 4.0 mol% SrF₂-coated LiNi_1/3Co_1/3Mn_1/3O₂ showed remarkable decrease of the initial capacity. 2.0 mol% coated sample exhibited the best electrochemical performance. It presented an initial discharge capacity of 165.7 mAh g⁻¹, and a capacity retention of 86.9% after 50 cycles at 4.6 V cut-off cycling.     

Preparation and electrochemical properties of Li[Ni1/3Co1/3Mn1−x/3Zrx/3]O2 cathode materials for Li-ion batteries

Layer-structured Zr doped Li[Ni_1/3Co_1/3Mn_1−x/3Zr_x/3]O₂ (0 ≤ x ≤ 0.05) were synthesized via slurry spray drying method. The powders were characterized by XRD, SEM and galvanostatic charge/discharge tests. The products remained single-phase within the range of 0 ≤ x ≤ 0.03. The charge and discharge cycling of the cells showed that Zr doping enhanced cycle life compared to the bare one, while did not cause the reduction of the discharge capacity of Li[Ni_1/3Co_1/3Mn_1/3]O₂. The unchanged peak shape in the differential capacity versus voltage curve suggested that the Zr had the effect to stabilize the structure during cycling. More interestingly, the rate capability was greatly improved. The sample with x = 0.01 presented a capacity of 160.2 mAh g⁻¹ at current density of 640 mA g⁻¹(4 C), corresponding to 92.4% of its capacity at 32 mA g⁻¹(0.2 C). The favorable performance of the doped sample could be attributed to its increased lattice parameter.     

Minimization of the cation mixing in Li1+x(NMC)1−xO2 as cathode material

Li_1+x(Ni_1/3Mn_1/3Co_1/3)_1−xO₂ layered materials were synthesized by the co-precipitation method with different Li/M molar ratios (M = Ni + Mn + Co). Elemental titration evaluated by inductively coupled plasma spectrometry (ICP), structural properties studied by X-ray diffraction (XRD), Rietveld analysis of XRD data, scanning electron microscopy (SEM) and magnetic measurements carried out by superconducting quantum interference devices (SQUID) showed the well-defined α-NaFeO₂ structure with cationic distribution close to the nominal formula. The Li/Ni cation mixing on the 3b Wyckoff site of the interlayer space was consistent with the structural model [Li_1−yNi_y]_3b[Li_x+yNi_{(1−x)/3−y}Mn_(1−x)/3Co_(1−x)/3]_3aO₂ (x = 0.02, 0.04) and was very small. Both Rietveld refinements and magnetic measurements revealed a concentration of Ni²⁺-3b ions lower than 2%; moreover, for the optimized sample synthesized at Li/M = 1.10, only 1.43% of nickel ions were located into the Li sublattice. Electrochemical properties were investigated by galvanostatic charge-discharge cycling. Data obtained with Li_1+x(Ni_1/3Mn_1/3Co_1/3)_1−xO₂ reflected the high degree of sample optimization. An initial discharge capacity of 150 mAh g⁻¹ was delivered at 1 C-rate in the cut-off voltage of 3.0-4.3 V. More than 95% of its initial capacity was retained after 30 cycles at 1 C-rate. Finally, it is demonstrated that a cation mixing below 2% is considered as the threshold for which the electrochemical performance does not change for Li_1+x(Ni_1/3Mn_1/3Co_1/3)_1−xO₂.     

Synthesis and electrochemical performance of the high voltage cathode material Li[Li0.2Mn0.56Ni0.16Co0.08]O2 with improved rate capability

The high voltage layered Li[Li_0.2Mn_0.56Ni_0.16Co_0.08]O₂ cathode material, which is a solid solution between Li₂MnO₃ and LiMn_0.4Ni_0.4Co_0.2O₂, has been synthesized by co-precipitation method followed by high temperature annealing at 900 °C. XRD and SEM characterizations proved that the as prepared powder is constituted of small and homogenous particles (100-300 nm), which are seen to enhance the material rate capability. After the initial decay, no obvious capacity fading was observed when cycling the material at different rates. Steady-state reversible capacities of 220 mAh g⁻¹ at 0.2C, 190 mAh g⁻¹ at 1C, 155 mAh g⁻¹ at 5C and 110 mAh g⁻¹ at 20C were achieved in long-term cycle tests within the voltage cutoff limits of 2.5 and 4.8 V at 20 °C.     

Physical and electrochemical properties of spherical Li1+x(Ni1/3Co1/3Mn1/3)1−xO2 cathode materials

A (Ni_1/3Co_1/3Mn_1/3)CO₃ precursor with an uniform, spherical morphology was prepared by coprecipitation using a continuously stirred tank reactor method. The as-prepared spherical (Ni_1/3Co_1/3Mn_1/3)CO₃ precursor served to produce dense, spherical Li_1+x(Ni_1/3Co_1/3Mn_1/3)_1−xO₂ (0 ≤ x ≤ 0.15) cathode materials. These Li-rich cathodes were also prepared by a second synthesis route that involved the use of an M₃O₄ (M = Ni_1/3Co_1/3Mn_1/3) spinel compound, itself obtained from the carbonate (Ni_1/3Co_1/3Mn_1/3)CO₃ precursor. In both cases, the final Li_1+x(Ni_1/3Co_1/3Mn_1/3)_1−xO₂ products were highly uniform, having a narrow particle size distribution (10-μm average particle size) as a result of the homogeneity and spherical morphology of the starting mixed-metal carbonate precursor. The rate capability of the Li_1+x(Ni_1/3Co_1/3Mn_1/3)_1−xO₂ electrode materials, which was significantly improved with increased lithium content, was found to be better in the case of the denser materials made from the spinel precursor compound. This result suggests that spherical morphology, high density, and increased lithium content were key factors in enabling the high rate capabilities, and hence the power performances, of the Li-rich Li_1+x(Ni_1/3Co_1/3Mn_1/3)_1−xO₂ cathodes.     

Synthesis and electrochemical properties of Li1−xFe0.8Ni0.2O2–LixMnO2 (Mn/(Fe + Ni + Mn) = 0.8) material

A new type of Li_1−xFe_0.8Ni_0.2O₂–Li_xMnO₂ (Mn/(Fe + Ni + Mn) = 0.8) material was synthesized at 350 °C in air atmosphere using a solid-state reaction. The material had an XRD pattern that closely resembled that of the original Li_1−xFeO₂–Li_xMnO₂ (Mn/(Fe + Mn) = 0.8) with much reduced impurity peaks. The Li/Li_1−xFe_0.8Ni_0.2O₂–Li_xMnO₂ cell showed a high initial discharge capacity above 192 mAh g⁻¹, which was higher than that of the parent Li/Li_1−xFeO₂–Li_xMnO₂ (186 mAh g⁻¹). We expected that the increase of initial discharge capacity and the change of shape of discharge curve for the Li/Li_1−xFe_0.8Ni_0.2O₂–Li_xMnO₂ cell is the result from the redox reaction from Ni²⁺ to Ni³⁺ during charge/discharge process. This cell exhibited not only a typical voltage plateau in the 2.8 V region, but also an excellent cycle retention rate (96%) up to 45 cycles.     

In situ X-ray diffraction studies of mixed LiMn2O4-LiNi1/3Co1/3Mn1/3O2 composite cathode in Li-ion cells during charge-discharge cycling

The structural changes of the composite cathode made by mixing spinel LiMn₂O₄ and layered LiNi_1/3Co_1/3Mn_1/3O₂ in 1:1 wt% in both Li-half and Li-ion cells during charge/discharge are studied by in situ XRD. During the first charge up to ∼5.2 V vs. Li/Li⁺, the in situ XRD spectra for the composite cathode in the Li-half cell track the structural changes of each component. At the early stage of charge, the lithium extraction takes place in the LiNi_1/3Co_1/3Mn_1/3O₂ component only. When the cell voltage reaches at ∼4.0 V vs. Li/Li⁺, lithium extraction from the spinel LiMn₂O₄ component starts and becomes the major contributor for the cell capacity due to the higher rate capability of LiMn₂O₄. When the voltage passed 4.3 V, the major structural changes are from the LiNi_1/3Co_1/3Mn_1/3O₂ component, while the LiMn₂O₄ component is almost unchanged. In the Li-ion cell using a MCMB anode and a composite cathode cycled between 2.5 V and 4.2 V, the structural changes are dominated by the spinel LiMn₂O₄ component, with much less changes in the layered LiNi_1/3Co_1/3Mn_1/3O₂ component, comparing with the Li-half cell results. These results give us valuable information about the structural changes relating to the contributions of each individual component to the cell capacity at certain charge/discharge state, which are helpful in designing and optimizing the composite cathode using spinel- and layered-type materials for Li-ion battery research.     

Electrochemically synthesized large area network of CoxNiyAlz layered triple hydroxides nanosheets: A high performance supercapacitor

A network of Co_xNi_yAl_z layered triple hydroxides (LTHs) nanosheets was prepared by the potentiostatic deposition process at −1.0 V (vs. Ag/AgCl) onto stainless steel electrodes. X-ray diffraction patterns show that the Co_xNi_yAl_zLTHs belong to the hexagonal system with layered structure. Cyclic voltammetry and charge discharge measurements in the potential range of −0.1 to 0.5 V and 0.0–0.4 V, respectively, vs. Ag/AgCl in 1 M KOH electrolyte indicate that Co_xNi_yAl_zLTHs have excellent supercapacitive characteristics. The maximum specific capacitance of ∼1263 F g⁻¹ was obtained for Co_0.59Ni_0.21Al_0.20LTH. The impedance studies indicated highly conducting nature of the Co_xNi_yAl_zLTHs.     

An amorphous LiCo1/3Mn1/3Ni1/3O2 thin film deposited on NASICON-type electrolyte for all-solid-state Li-ion batteries

Amorphous LiCo_1/3Mn_1/3Ni_1/3O₂ thin films were deposited on the NASICON-type Li-ion conducting glass ceramics, Li_1+x+yAl_xTi_2−xSi_yP_3−yO₁₂ (LATSP), by radio frequency (RF) magnetron sputtering below 130 °C. The amorphous films were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The Li/PEO₁₈-Li(CF₃SO₂)₂N/LATSP/LiCo_1/3Mn_1/3Ni_1/3O₂/Au all-solid-state cells were fabricated to investigate the electrochemical performance of the amorphous films. It was found that the low-temperature deposited amorphous cathode film shows a high discharge voltage and a high discharge capacity of around 130 mAh g⁻¹.     

Potentiostatically deposited nanostructured CoxNi1−x layered double hydroxides as electrode materials for redox-supercapacitors

Cobalt–nickel layered double hydroxides (Co_xNi_1−x LDHs) were deposited onto stainless steel electrodes by the potentiostatic deposition method at −1.0 V vs. Ag/AgCl using various molar ratios of Co(NO₃)₂ and Ni(NO₃)₂ in distilled water. Their structure and surface morphology were studied by using X-ray diffraction analysis, energy dispersive X-ray spectroscopy and scanning electron microscopy. A network of Co_xNi_1−x LDH nanosheets was obtained. The nature of the cyclic voltammetry and charge–discharge curves suggested that the Co_xNi_1−x LDHs exist in the form of solid solutions. The capacitive characteristics of the Co_xNi_1−x LDHs in 1 M KOH electrolyte showed that Co_0.72Ni_0.28 LDHs had the highest specific capacitance value, 2104 F g⁻¹, which is also the highest yet reported value for oxide materials in general.     

Synthesis and electrochemical properties of lithium non-stoichiometric Li1+x(Ni1/3Co1/3Mn1/3)O2+δ prepared by a spray drying method

Lithium non-stoichiometric Li[Li_x(Ni_1/3Co_1/3Mn_1/3)_1−x]O₂ materials (0 ≤ x ≤ 0.17) were synthesized using a spray drying method. The electrochemical properties and structural stabilities of the synthesized materials were investigated. The synthesized materials exhibited a hexagonal structure in all the x-value and the lattice parameters of the materials were gradually decreased with increasing x-value due to an increasing amount of Ni³⁺ ions for charge compensation. The capacity retention ability and rate capability of the stoichiometric Li(Ni_1/3Co_1/3Mn_1/3)O₂ material were improved by increasing x-value, the so-called overlithiation. We found that the overlithiated materials could keep more structural integrity than the stoichiometric one during electrochemical cyclings, which could be one of reasons for a better electrochemical properties of the overlithiated materials.     

Structural and electrochemical studies of Ba0.6Sr0.4Co1−yTiyO3−δ as a new cathode material for IT-SOFCs

The influence of titanium doping level in Ba_0.6Sr_0.4Co_1−yTi_yO_3−δ (BSCT) oxides on their phase structure, electrical conductivity, thermal expansion coefficient (TEC), and single-cell performance with BSCT cathodes has been investigated. The incorporation of Ti can lead to the phase transition of Ba_0.6Sr_0.4CoO_3−δ from hexagonal to cubic structure. The solid solution limitation of Ti in Ba_0.6Sr_0.4Co_1−yTi_yO_3−δ is 0.15–0.3 under 1100 °C. BSCT shows a small polaron conduction behavior and the electrical conductivity increases steadily in the testing temperature range (300–900 °C), leading to a relatively high conductivity at high temperatures. The electrical conductivity decreases with increasing Ti content. The addition of Ti deteriorates the cathode performance of BSCT slightly but decreases the TEC significantly. The TEC of BSCT is about 14 × 10⁻⁶ K⁻¹, which results in a good physical compatibility of BSCT with Gd_0.2Ce_0.8O_2−δ (GDC) electrolyte. BSCT also shows excellent thermal cyclic stability of electrical conductivity and good chemical stability with GDC. These properties make BSCT a promising cathode candidate for intermediate temperature solid oxide fuel cells (IT-SOFCs).