Effects of K2O-Li2O doping on surface and catalytic properties of Fe2O3/Cr2O3 system

The effects of K₂O and Li₂O-doping (0.5, 0.75 and 1.5 mol%) of Fe₂O₃/Cr₂O₃ system on its surface and the catalytic properties were investigated. Pure and differently doped solids were calcined in air at 400-600 °C. The formula of the un-doped calcined solid was 0.85Fe₂O₃:0.15Cr₂O₃. The techniques employed were TGA, DTA, XRD, N₂ adsorption at −196 °C and catalytic oxidation of CO oxidation by O₂ at 200-300 °C. The results revealed that DTA curves of pure mixed solids consisted of one endothermic peak and two exothermic peaks. Pure and doped mixed solids calcined at 400 °C are amorphous in nature and turned to α-Fe₂O₃ upon heating at 500 and 600 °C. K₂O and Li₂O doping conducted at 500 or 600 °C modified the degree of crystallinity and crystallite size of all phases present which consisted of a mixture of nanocrystalline α- and γ-Fe₂O₃ together with K₂FeO₄ and LiFe₅O₈ phases. However, the heavily Li₂O-doped sample consisted only of LiFe₅O₈ phase. The specific surface area of the system investigated decreased to an extent proportional to the amount of K₂O and Li₂O added. On the other hand, the catalytic activity was found to increase by increasing the amount of K₂O and Li₂O added. The maximum increase in the catalytic activity, expressed as the reaction rate constant (k) measured at 200 °C, attained 30.8% and 26.5% for K₂O and Li₂O doping, respectively. The doping process did not modify the activation energy of the catalyzed reaction but rather increased the concentration of the active sites without changing their energetic nature.     

Modification of TiO2 nanorods by Bi2MoO6 nanoparticles for high performance visible-light photocatalysis

In this work, TiO₂ nanorods were prepared by a hydrothermal process and then Bi₂MoO₆ nanoparticles were deposited onto the TiO₂ nanorods by a solvothermal process. The nanostructured Bi₂MoO₆/TiO₂ composites were extensively characterized by X-ray diffraction, scanning and transmission electron microscopy, X-ray photoelectron spectroscopy and UV-vis diffuse reflectance spectroscopy. The photocatalytic activity of the Bi₂MoO₆/TiO₂ composites was evaluated by degradation of methylene blue. The Bi₂MoO₆/TiO₂ composites exhibit higher catalytic activity than pure Bi₂MoO₆ and TiO₂ for degradation of methylene blue under visible light irradiation (λ > 420 nm). Further investigation revealed that the ratio of Bi₂MoO₆ to TiO₂ in the composites greatly influenced their photocatalytic activity. The experimental results indicated that the composite with Bi₂MoO₆:TiO₂ = 1:3 exhibited the highest photocatalytic activity. The enhancement mechanism of the composite catalysts was also discussed.     

The high-temperature corrosion behavior of Co-Nb alloys in mixed-gas atmospheres

The corrosion of Co-Nb alloys containing up to 30 wt.% Nb in H₂-H₂S-H₂O gas mixtures was studied over the temperature range of 600–800°C. The gas composition falls in the stability region of cobalt sulfide and Nb₂O₅ in the phase diagrams of the Co-O-S and Nb-O-S systems at all temperatures studied. Duplex scales, consisting of an outer layer of cobalt sulfide and a complex, heterophasic inner layer, were formed at all temperatures studied. In addition to cobalt sulfide and CoNb₃S₆, a small amount of NbO₂ was found in the inner layer. The reason for the formation of NbO₂ over that of Nb₂O₅ in the scale is that the outer sulfide scale lowers the oxygen activity within the scale into the NbO₂-stability region. Two-stage kinetics were observed for all alloys, including an initial irregular stage usually followed by a steady-state parabolic stage. The steady-state parabolic rate constants decreased with increasing amounts of Nb, except for Co-20Nb corroded at 700°C. Nearly identical kinetics were observed for Co-20Nb corroded at 600°C and 700°C. The presence of NbO₂ particles leads only to a limited decrease of the available cross-section area for the outward-diffusing metal ions. The activation energies for all alloys are similar and are in agreement with those obtained in a study of the sulfidation of the same alloys. The primary corrosion mechanism involves an outward Co transport.     

Fe2O3-CaO-TiO2 体系下铁酸钙的合成过程及TiO2 和CaTiO3 的影响

为了确定高钛型钒钛磁铁矿烧结过程中铁酸钙的生成是受TiO₂还是TiO₂和CaO形成的CaTiO₃影响,首先利用Fe₂O₃和CaO的纯试剂合成了铁酸钙,并研究了TiO₂和CaTiO₃对钛铁酸钙 （FCT） 形成的影响。在Factsage 7.0软件进行热力学计算的基础上,通过在空气气氛下进行烧结,获得了在1023~1423 K温度范围内、不同烧结时间的不同样品。通过X射线衍射和扫描电镜-能谱分析等表征手段,对烧结样品的物相转变和微观结构变化进行了表征。发现FCT的形成过程主要分为2个阶段：前一阶段为1023~1223 K温度范围内Fe₂O₃与CaO之间的反应,合成产物为Ca₂Fe₂O₅,反应方程式为“Fe₂O₃(s)+ 2CaO(s)= Ca₂Fe₂O₅(s)”;后一阶段为1223~1423 K温度范围内Ca₂Fe₂O₅和Fe₂O₃的反应,主要产物为CaFe₂O₄,反应为“Ca₂Fe₂O₅(s)+ Fe₂O₃(s)= 2CaFe₂O₄(s)”,该阶段尤其是温度为1423 K时,反应速率显著加快,随温度的升高CaTiO₃显著增加。然而,Ti元素在铁酸钙中的固溶很难实现,TiO₂与铁酸钙之间的反应不是形成FCT的有效途径。随着保温时间的延长,CaTiO₃和FCT相界中Fe元素含量增加。FCT主要是通过Fe组分在CaTiO₃中固溶形成的,主要反应是“Fe₂O₃+CaTiO₃(s)=FCT(s)”。     

Synthesis of lanthanum carbonate nanoparticles via sonochemical method for preparation of lanthanum hydroxide and lanthanum oxide nanoparticles

Lanthanum carbonate nanoparticles were synthesized from the reaction of lanthanum acetate and Na₂CO₃ under sonication via sonochemical method. Lanthanum hydroxide nanoparticles were prepared by facial hydrothermal processing from the resulted product at 110 °C for 24 h. The role of surfactant, calcination temperature and sonication time were investigated on the morphology and particle size of the products. Products were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray photoelectron spectrum (XPS), and Fourier transform infrared (FT-IR) spectra. La₂O₃ nanoparticles were obtained by calcinations of the nanoparticles of lanthanum carbonate at 600 °C.     

Corrosion behavior of select MAX phases in NaOH, HCl and H2SO4

In this paper we report on the electrochemical corrosion of select MAX phases, namely Ti₂AlC, (Ti,Nb)₂AlC, V₂AlC, V₂GeC, Cr₂AlC, Ti₂AlN, Ti₄AlN₃, Ti₃SiC₂ and Ti₃GeC₂ in 1 M NaOH, 1 M HCl and 1 M H₂SO₄ solutions. Polarization characteristics recorded in 1 M NaOH show that V₂AlC, V₂GeC and Cr₂AlC undergo active dissolution at potentials more positive than the corrosion potential, while Ti₂AlC, (Ti,Nb)₂AlC, Ti₃SiC₂ and Ti₃GeC₂ passivate. In the 1 M HCl solutions, Ti₂AlC, V₂AlC and V₂GeC actively dissolve; Ti₃SiC₂ and Ti₃GeC₂ passivate. Depending on potential, (Ti,Nb)₂AlC and Cr₂AlC showed trans-passive behavior. In 1 M H₂SO₄ solutions, Ti₂AlC, (Ti,Nb)₂AlC, Ti₃SiC₂ and Ti₃GeC₂ passivate, V₂AlC and V₂GeC show active dissolution, while Cr₂AlC exhibits trans-passive behavior. Ti₂AlN and Ti₄AlN₃ were passive in all solutions except in 1 M HCl, where Ti₂AlN showed trans-passive behavior. Given that the corrosion behavior of (Ti,Nb)₂AlC is unlike either Ti or Nb, the behavior of the former cannot be predicted from that of the latter.     

CuInSe2 nano-crystallite reaction kinetics using solid state reaction from Cu2Se and In2Se3 powders

The reaction mechanism and CuInSe₂ formation kinetics using a solid state reaction from Cu₂Se and In₂Se₃ powders synthesized using a heating up process were investigated using X-ray diffractomy (XRD) and transmission electron microscopy (TEM). It was observed that the CuInSe₂ phase increased gradually, accompanied with a decrease in γ-In₂Se₃ with no intermediate phase as the calcination temperature and soaking time were increased. The reaction kinetics was analyzed using the Avrami and polynomial kinetic model, suggesting that CuInSe₂ formation from Cu₂Se and In₂Se₃ powders follows a diffusion-controlled reaction with an apparent activation energy of about 122.5-182.3 kJ/mol. Cu₂Se and In₂Se₃ phases react and directly transform into CIS without the occurrence of any intermediate phase and the size of the newly formed CuInSe₂ crystallites was close to that of the Cu₂Se reactant particle based on the TEM results, which indicated that the solid reaction kinetics may be dominated by the diffusion of In³⁺ ions.     

Studies on Al<Subscript>2</Subscript>O<Subscript>3</Subscript>/ZrO<Subscript>2</Subscript>/Al<Subscript>2</Subscript>O<Subscript>3</Subscript> high K gate dielectrics applied in a fully depleted SOI MOSFET

Al₂O₃/ZrO₂/Al₂O₃ gate stacks were prepared on ultrathin SOI (Silicon on insulator) substrates by ultrahigh vacuum electron beam evaporation and post-annealed in N₂ at 450°C for 30 min. Three clear nanolaminate layered structure of Al₂O₃(2.1 nm)/ZrO₂(3.5 nm)/Al₂O₃(2.3 nm) was observed with a high-resolution cross-sectional transmission electron microscope (HR-XTEM). High frequency capacitance voltage (C-V) characteristics of a fully depleted (FD) SOI MOS capacitor at 1 and 5 MHz were studied. The minority carriers determine the high frequency C-V properties, which is opposite to the case of bulk MOS capacitors. The series resistance of the SOI substrate is found to be the determinant factor of the high frequency characteristics of FD SOI MOS capacitors. This article is based on a presentation in “The 7th Korea-China Workshop on Advanced Materials” organized by the Korea-China Advanced Materials Cooperation Center and the China-Korea Advanced Materials Cooperation Center, held at Ramada Plaza Jeju Hotel, Jeju Island, Korea on August 24≈27, 2003.     

Modulated Phases in the Ba2SiO4-Ca2SiO4 System of A2BX4, K2SO4-related Structures

Abstract

The A₂BX₄ family of K₂SO₄-related structures have long been of interest to crystal chemists, largely due to the numerous different polymorphs and complicated sequences of phase transitions they sometimes exhibit as a function of temperature. For most such A₂BX₄ compounds, there are essentially only two distinct structure types or parent structures — a high-temperature, ?hexagonal‘ form isomorphous to α-K₂SO₄ and a lower-temperature, orthorhombic form isomorphous to β-K₂SO₄. In addition to these two prototype structures, however, there often exist weakly distorted, or modulated, variants. In the case of the Ba_2-xCa_xSiO₄ system, five such modulated variants have been found via an electron diffraction study and characterized. The characteristic satellite extinction conditions associated with the weak satellite reflections have been used to determine displacement eigenvectors and atomic displacement patterns associated with each of the observed modulation wave-vectors. The widespread occurrence of modulated phases within the A₂BX₄ family of K₂SO₄-related structures suggests an almost chronic instability to displacive modulation.     

Preparation and characteristic of spherical Li3V2(PO4)3

Spherical Li₃V₂(PO₄)₃ was synthesized by using N₂H₄ as reducer. The products were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The results show that single-phase, spherical and well-dispersed Li₃V₂(PO₄)₃ has been successfully synthesized in our experimental process. Electrochemical behaviors have been characterized by charge/discharge measurements. The initial discharge capacities of Li₃V₂(PO₄)₃ were 123 mAh g⁻¹ in the voltage range of 3.0–4.3 V and 132 mAh g⁻¹ in the voltage range of 3.0–4.8 V.     

In-situ TiB2 and Al2O3 formation by DC plasma spraying

In-situ plasma spraying (IPS) is a promising process to fabricate composite coatings with in-situ formed thermodynamically stable phases. In the present study, mechanically alloyed Al-12Si, B₂O₃ and TiO₂ powder was deposited onto an aluminum substrate using atmospheric plasma spraying (APS). It has been observed that, during the coating process, TiB₂ and Al₂O₃ are in-situ formed through the reaction between starting powders and finely dispersed in hypereutectic Al-Si matrix alloy. Also, obtained results demonstrate that in-situ reaction intensity strongly depends on spray conditions.     

The high-temperature corrosion behavior of Nb-Al alloys in a H2/H2S/H2O gas mixture

The corrosion behavior of pure Nb and three Nb Al alloys containing 12.5, 25, and 75 at.% Al was studied over the temperature range of 800–1000°C in a H₂/H₂S/H₂O gas mixture. Except for the Nb-12.5Al alloy consisting of a two phase structure of -Nb and Nb₃Al, other alloys studied were single phase. The corrosion kinetics followed the parabolic rate law in all cases, regardless of temperature and alloy composition. The parabolic rate constants increased with increasing temperature, but fluctuated with increasing Al content. The Nb-75Al alloy exhibited the best corrosion resistance among all alloys studied, whose corrosion rates are 1.6–2.2 orders of magnitude lower than those of pure-Nb (depending on temperature). An exclusive NbO₂ layer was formed on pure Nb, while heterophasic scales were observed on Nb-Al alloys whose compositions and amounts strongly depended on Al content and temperature. The scales formed on Nb-12.5Al consisted of mostly NbO₂ and minor amounts of Nb₂O₅, NbS2, and -Al₂O₃, while the scales formed on Nb-25Al consisted of mostly Nb₂O₅ and some -Al₂O₃. The scales formed on Nb-75Al consisted of mostly -Al₂O₃ and Nb₃S₄ atT 900°C, and mostly -Al₂O₃ , Nb₃S₄ and some AlNbO₄ at 1000°C. The formation of -Al₂O₃ and Nb₃S₄ resulted in a significant reduction of the corrosion rates.     

废旧锂离子电池中Li, Fe和V的回收及xLiFePO4-yLi3V2(PO4)3的制备

由于LiFePO_4和Li_3V_2(PO_4)_3材料的特征相近,制备方法类似,提供了一种从废旧LiFePO_4和Li_3V_2(PO_4)_3混合电池中回收Li、Fe和V,再制备xLiFePO_4-yLi_3V_2(PO_4)_3的方法。在空气气氛中600℃热处理1h后,去除粘结剂PVDF使活性物质与集流体分离。调节Li、Fe、V和P摩尔比,球磨、锻烧,配制不同比例的xLiFePO_4-yLi_3V_2(PO_4)_3(x:y=5:1,7:1,9:1)复合电极材料。表征了其形貌、结构和电化学性能,结果表明,回收制备的复合材料将同时具备LiFePO_4和Li_3V_2(PO_4)_3两种材料的电化学性能,能显著改善LiFePO_4的倍率性能。     

Protective effect in sulfuric acid media of alumina and ceria oxide layers electrodeposited on stainless steel

The influence of thin layers of Al₂O₃ and Ce₂O₃-CeO₂, electrodeposited on stainless steel OC4004, on the corrosion behaviour of the systems Al₂O₃/SS, Ce₂O₃-CeO₂/SS and Al₂O₃-Ce₂O₃-CeO₂/SS has been studied in sulfuric acid medium. A pronounced stabilizing effect on the passive state of steel and enhancement of its corrosion resistance has been established both for the samples as deposited and for the thermally treated Ce₂O₃-CeO₂/SS systems. In comparison to them the layers of Al₂O₃ have a substantial impact on the corrosion resistance of the Al₂O₃/SS system only in the cases when the system is not subjected to thermal treatment. The consecutive deposition of Al₂O₃ and Ce₂O₃-CeO₂ films on SS gives as a result an outstanding corrosion-protective effect, whereupon the corrosion potential of the system Al₂O₃/Ce₂O₃-CeO₂/SS is shifted in positive direction with ∼ 0.3 V for the samples as deposited and with ∼ 1 V—for the thermally treated samples. The so established favourable effect has been explained by the increased concentration of chromium oxides in the surface passive film, caused by the presence of cerium oxides, as well as by their action as cathode, effective with respect to the reduction corrosion reaction, shifting strongly the potential (at which this reaction is occurring) in positive direction.     

Photocatalytic performance of nano-photocatalyst from TiO2 and Fe2O3 by mechanochemical synthesis

Nano-particles of homogeneous solid solution between TiO₂ and Fe₂O₃ (up to 10 mol%) have been prepared by mechanochemical milling of TiO₂ and yellow Fe₂O₃/red Fe₂O₃/precipitated Fe (OH)₃ using a planetary ball mill. Such novel solid solution cannot be prepared by conventional co-precipitation technique. A preliminary investigation of photocatalytic activity of mixed oxide (TiO₂/Fe₂O₃) on photo-oxidation of different organic dyes like Rhodamine B (RB), Methyl orange (MO), Thymol blue (TB) and Bromocresol green (BG) under visible light (300-W Xe lamp; λ > 420 nm) showed that TiO₂ having 5 mol% of Fe₂O₃ (YFT1) is 3-5 times higher photoactive than that of P25 TiO₂. The XRD result did not show the peaks assigned to the Fe components (for example Fe₂O₃, Fe₃O₄, FeO₃, and Fe metal) on the external surface of the anatase structure in the Fe₂O₃/TiO₂ attained through mechanochemical treatment. This meant that Fe components were well incorporated into the TiO₂ anatase structure. The average crystallite size and particle size of YFT1 were found to be 12 nm and 30 ± 5 nm respectively measured from XRD and TEM conforming to nanodimensions. Together with the Fe component, they absorbed wavelength of above 387 nm. The band slightly shifted to the right without tail broadness, which was the UV absorption of Fe oxide in the Fe₂O₃/TiO₂ particle attained through mechanochemical method. This meant that Fe components were well inserted into the framework of the TiO₂ anatase structure. EPR and magnetic susceptibility show that Fe³⁺ is in low spin state corresponding to μ_B = 1.8 BM. The temperature variation of μ_B shows that Fe³⁺ is well separated from each other and does not have any antiferromagnetic or ferromagnetic interaction. The evidence of Fe³⁺ in TiO₂/Fe₂O₃ alloy is also proved by a new method that is redox titration which is again support by the XPS spectrum.     

Enhanced thermoelectric properties of n-type Bi2Te3-based nanocomposite fabricated by spark plasma sintering

Highly dense n-type Bi₂Te₃-based thermoelectric materials dispersed with x vol.% γ-Al₂O₃ nanoparticles (x = 0, 0.4, 1.0, 1.5) were fabricated by spark plasma sintering method. The effects of γ-Al₂O₃ addition on microstructure and the thermoelectric properties were studied. It was found that γ-Al₂O₃ nanoparticles locate both at grain boundaries and inside Bi₂Se_0.3Te_2.7 grains. The nanoparticles induce both potential barrier scattering effect and additional phonon scattering effect, which simultaneously enhance the Seebeck coefficient and reduce the lattice thermal conductivity of the nanocomposites in the measured temperature range of 300-500 K, respectively. The maximum dimensionless figure of merit (ZT_max) reaches up to 0.99 for the sample with x = 1.0 at 400 K, which is 35% improvement over the Bi₂Te₃-based matrix. More importantly, the average ZT value of the sample increases from 0.65 to 0.91 in the temperature range 300-500 K, making the nanocomposites much more applicable in cooling and power generation.     

Preparation and properties of sintered molybdenum doped with La2O3/MoSi2

Sintered Mo with the addition of La₂O₃/MoSi₂ was prepared via the process of solid–solid doping + powder metallurgy. X-ray diffraction experiment, hardness test, three-point bending test and high-temperature tensile test were carried out to characterize the samples. The XRD pattern of a typical sample shows that the sintered Mo was mainly composed of Mo, La₂O₃ and Mo₅Si₃. Mo₅Si₃ was probably formed through the reaction between MoSi₂ and the Mo matrix. Densities and fracture toughnesses of both doped Mo and pure Mo were measured and contrasted. Sintered Mo with the addition of 0.2 wt% La₂O₃/MoSi₂ has the highest toughness, while more addition of La₂O₃/MoSi₂ has smaller effect on improving toughness or even embrittles Mo. The results of three-point bending test and high-temperature tensile test show that the bending strength and high-temperature tensile strength of doped Mo are both higher than those of pure Mo. The formation of Mo₅Si₃ improves the high-temperature strength. The La₂O₃/Mo₅Si₃ dispersed in the Mo matrix refined the grains, and thus strengthened the Mo matrix by dispersion strengthening and grain refinement.     

Sulfidation Behavior of Inconel 738 Superalloy at 500–900°C

The high-temperature sulfidation behavior of the cast nickel-base superalloy Inconel 738 (IN-738) was studied over the temperature range 500–900°C in pure sulfur vapor over the range 10²–10⁴ Pa. The sulfidation kinetics followed the parabolic rate law in all cases. The sulfidation rates increased with increasing temperature and sulfur pressure. The scales formed were bilayered and temperature-dependent. At T700°C, the outer scale consisted of mostly NiS (with dissolved Co) and minor (CoS₂ and NiCo₂S₄, while the inner layer was a heterophasic mixture of NiS, NiCo₂S₄, and minor amounts of Al₂S₃ and chromium sulfide (Cr₂S₃/Cr₃S₄). At T750°C, the outer scale consisted of mostly Ni₃S₂ (with dissolved Co) and minor amounts of Co₃S₄ and Cr₂S₃/Cr₃S₄, while the inner layer was a complex, heterophasic mixture of Ni₃S₂, Cr₂S₃/Cr₃S₄, CoCr₂S₄, and minor Al₂S₃. Platinum markers were found to be located at the interface between the inner and outer scales, suggesting that the outer scale grew by the outward transport of cations and the inner scale grew by the inward transport of sulfur. The formation of Al₂S₃ and Cr₂S₃/Cr₃S₄ partly blocked the transport of cations through the inner scale and consequently reduced the sulfidation rates as compared to pure nickel.     

The combined effect of refractory coatings containing reactive elements on high temperature oxidation behavior of chromia-forming alloys

The high temperature oxidation behaviors of chromia-forming alloys (F17Ti and Fe-30Cr alloys) have been studied at 1273 K under isothermal conditions and at 1223 K under cyclic conditions, in air under the atmospheric pressure. To extend the oxidation lifetime, coatings have been applied onto the alloy surfaces. Al₂O₃ and Cr₂O₃ films doped with Sm₂O₃ or Nd₂O₃ were prepared via the metal-organic chemical vapor deposition technique. Single Cr₂O₃, Al₂O₃, Nd₂O₃ and codeposited Cr₂O₃-Nd₂O₃, Al₂O₃-Nd₂O₃, Al₂O₃-Sm₂O₃ coatings drastically improved the chromia-forming alloy high temperature oxidation behavior, since they decreased the oxidation rate and enhanced the oxide scale adhesion. Results showed that a critical amount of reactive element (Nd or Sm) in chromia or alumina coatings (11-18 at.%) was needed to observe the most effective effect. The fast precipitation of NdCrO₃ or NdTi₂₁O₃₈ and the segregation of reactive elements at the chromia grain boundaries slowing down outward cation transport and consequently blocking the chromia grain growth, was supposed to be the main reasons of the beneficial effect ascribed to the reactive elements in chromia scales.     

钕的添加对V2O5-MoO3/TiO2平板式脱硝催化剂性能的影响

本研究制备了一系列不同Nd含量的V₂O₅-MoO₃-Nd₂O₃/TiO₂平板式脱硝催化剂。采用XRD、N2-吸附脱附、XPS、H2-TPR、拉曼光谱、NH3-TPD和红外光谱等表征手段对催化剂进行分析。结果表明:适量的Nd2O3(0.25%、0.5%,质量分数)可以增强V₂O₅-MoO₃/TiO₂催化剂的还原性能,增加了催化剂的Oα/(Oα+Oβ)比率,从而提升了催化剂的脱硝活性。然而,过量Nd₂O₃(0.75%、1%)的添加,会导致催化剂酸性性能的显著降低,造成催化剂脱硝性能的下降。此外,过量Nd的添加还会对催化剂的耐磨性能有负面影响。各催化剂中,VMoN d(0.5%)/Ti催化剂显示了最佳的脱硝活性。并且,该催化剂还显示了优良的抗SO₂、H₂O性能。