电弧喷涂工艺参数对Zn-Al伪合金制模涂层性能的影响

为了提高电弧喷涂模具的复制精度和使用寿命,研究了喷涂工艺参数变化对电弧喷涂制模中Zn-Al伪合金金属壳的硬度和致密性的影响.试验采用Zn丝作阴极,Al丝作阳极进行电弧喷涂.在固定喷枪移动速度和喷涂角度为90°的条件下,分析得出,送丝速度和喷涂距离对伪合金涂层硬度、孔隙率影响较小,而电弧电压和压缩空气压力对伪合金涂层硬度、孔隙率影响较大,并通过正交分析法得出了电弧喷涂制备Zn-Al伪合金涂层的最佳工艺参数:电弧电压30 V,送丝速度5m/min,喷涂距离200mm,压缩空气压力0.5 MPa.最后分析了不同工艺参数下涂层的金相组织.     

喷涂工艺参数对NICrBSi涂层显微组织和性能的影响

采用微束等离子喷涂系统制备了NiCrBSi涂层。研究了电弧功率、喷涂距离和等离子气体流量对涂层显微组织和性能的影响。试验结果表明,NiCrBSi涂层的致密程度与显微硬度随电弧功率和气体流量的增加而增加。当喷涂距离超过40mm时,喷涂距离对涂层显微硬度没有显著影响。采用微束等离子喷涂工艺制备的NiCrBSi涂层显微硬度可达HV0．2700。     

基于正交试验设计的电弧喷涂NiAl/3Cr18Mo复合涂层的性能研究

为获得制备NiAl/3Cr18Mo复合涂层综合性能较优的最佳工艺参数,采用正交法设计试验方案,利用电弧喷涂技术制备NiAl/3Cr18Mo复合涂层,系统研究了工作电流、电弧电压、空气压力和工作距离对复合涂层性能稳定性的影响规律.利用超景深三维显微系统对涂层的显微组织进行分析,并以结合强度及硬度为判据,总结了工艺参数与涂层性能的关系.结果 表明:工艺参数中工作电流、工作距离对NiAl/3Cr18Mo复合涂层结合强度的影响程度最大,空气压力和电弧电压影响较小;工作电流、工作距离对NiAl/3Cr18Mo复合涂层硬度的影响程度较大,电弧电压和空气压力影响次之.在工作电流200 A、电压32 V、空气压力0.6 MPa、工作距离170 mm时所制备的涂层综合性能最好.     

超音速电弧喷涂Ti-Al涂层抗滑动磨损性能研究

采用二次正交回归试验设计原理和钛铝双丝超音速电弧喷涂Ti-Al合金复合涂层方法，对LY12铝合金进行了表面强化研究，并采用金相、XRD、SEM、硬度和磨损试验方法，对涂层的组织结构及力学性能进行了表征，考察了喷涂工艺参数对涂层孔隙率、显微硬度和耐滑动磨损性能的影响，研究结果表明：在本文的实验条件下，涂层的体积磨损量、孔隙率、显微硬度与喷涂电压和喷涂距离之间的变化规律，可用回归模型进行描述；随喷涂电压的增大，涂层磨损量逐渐下降；喷涂距离小于220mm时，随喷涂距离的增大涂层磨损量逐渐增大；喷涂距离为220mm时，磨损量达到最大，继续增加喷涂距离，涂层的磨损量逐渐下降；在干摩擦条件下，Ti-Al合金涂层的磨损机制主要以化合物相剥落引起的磨粒磨损和氧化磨损为主。     

电弧喷涂工艺参数对1Cr13涂层与45钢结合强度的影响

电弧喷涂技术常用于机械零件如柱塞、曲轴等的修复.喷涂层与基体的结合强度直接影响其寿命,并与喷涂工艺有密切的关系.用正交设计试验方案,在45钢基体上采用电弧喷涂方法制备了1Cr13涂层,并通过涂层结合强度试验考察了喷涂工艺参数与涂层结合强度的关系.结果表明:电弧喷涂1Cr13钢丝的优化工艺参数为:电压32 V,电流240 A,喷涂压力0.7 MPa,喷涂距离150 mm;影响涂层结合强度的工艺参数从主到次依次为电弧电流、喷涂压力、喷涂距离和喷涂电压.     

铸态和挤压态 AZ31 镁合金在 3.5%的 NaCl 溶液中的腐蚀性能比较

目的研究铸态和挤压态AZ31镁合金在3.5%NaCl溶液中的腐蚀性能。方法采用光学显微镜和X射线衍射分析了铸态AZ31镁合金挤压前后的显微组织。利用静态浸泡失重实验和电化学实验研究了铸态和挤压态AZ31镁合金在3.5%NaCl溶液中的腐蚀性能。结果热挤压可有效细化AZ31合金的晶粒,铸态试样的平均晶粒大小约为111μm,挤压态试样的平均晶粒大小约为9μm。AZ31镁合金在3.5%NaCl溶液中的腐蚀初期,合金表面没有发生钝化。挤压后合金的自腐蚀电位从铸态的-1.55 V提高到-1.52 V。浸泡72 h后,铸态试样的腐蚀速率为4.293 mm/a,挤压态试样的腐蚀速率为2.957 mm/a。结论挤压提高了AZ31镁合金在3.5%NaCl溶液中的腐蚀性能。     

钛-铝双丝超音速电弧喷涂层显微硬度特性研究

利用SAS-Ⅱ型超音速电弧喷涂设备、工业级钛、铝丝材在LY12铝合金基体上制备了钛铝复合涂层,并对其显微硬度进行了测定.根据均匀设计实验方案和二次多项式逐步回归分析,获得了实验范围内,显著水平为0.002、相关系数为0.98的钛铝超音速电弧喷涂涂层显微硬度与喷涂电压、喷涂电流和喷涂距离的关系式.进一步分析表明:当喷涂电流较小时,随喷涂电压的增大,涂层的硬度逐渐下降;当喷涂电流较大时,随电压的增大,涂层的硬度随之增大,而且喷涂电流越大,其硬度的上升速度越快.而喷涂距离对涂层显微硬度的影响呈弱线性递增的关系.     

AZ31镁合金表面多层膜的结构与性能研究

研究了在AZ31镁合金表面依次进行浸锌、化学镀镍、电镀铜、电弧离子镀Cr/CrN的复合镀膜工艺.利用x射线晶体分析仪、扫描电镜、显微硬度计、腐蚀测量系统及热震法等仪器和方法对复合镀层的显微组织及性能进行了研究.结果表明,在此复合镀工艺条件下,可以在AZ31镁合金表面形成致密度高、结合强度好、耐蚀性好且硬度高的复合合金镀层;AZ31镁合金镀膜后的显微硬度形成一个梯度,由71.1HK提高到2224.8HK;耐蚀性明显提高,腐蚀电位从-1481mV提高到-382mV.     

工艺参数对超音速电弧喷涂钛-铝涂层表面粗糙度的影响

利用SAS-Ⅱ型超音速电弧喷涂设备、工业级钛、铝丝材在LY12铝合金基体上制备了钛铝复合涂层,通过均匀设计方法实验研究了超音速电弧喷涂工艺参数对涂层表面粗糙度(Ra)的影响规律.结果表明:在一定的雾化条件下,随喷涂电压的增大,涂层的Ra逐渐增大,当电压增至32V时,Ra达到最高值,此后,随喷涂电压的继续增大,Ra逐渐下降;随喷涂距离的增大,涂层的Ra逐渐降低,当喷涂距离增至一定程度时,涂层的Ra降到最小值,随喷涂距离的继续增大,涂层的Ra又逐渐增大;随喷涂电流的增大,涂层的Ra呈线性增大的趋势.涂层Ra最小的超音速电弧喷涂工艺参数:喷涂电压为20V,喷涂电流为20A,喷涂距离为0.242m.     

45钢表面大气等离子喷涂氧化钇部分稳定氧化锆热障涂层及其性能

为了制备高性能热障涂层,缩短国内外差距,在45钢表面大气等离子喷涂氧化钇部分稳定的氧化锆(YSZ)热障涂层。利用X射线衍射和扫描电镜分析YSZ涂层的相结构和微观形貌,分别测定了YSZ涂层的孔隙率、热导率、显微硬度、结合强度及隔热性能。结果表明:YSZ涂层的孔隙率、隔热温差随喷涂电压增大而减小,随喷涂距离的增加而增大;维氏硬度、结合强度和热导率随喷涂电压增大而增大,随喷涂距离增加而减小;当喷涂电压为80 V,喷涂距离为100 mm时,YSZ热障涂层的结合强度为36.78 MPa,热导率为0.705 W/(m·K),具有较好的隔热性能。     

Estimation of Parameters of Universal Distribution of Moments of Failure of Products

A method is proposed for estimating the parameters of a mixture of exponential and Weibull distributions for which the accuracy of preliminary estimates obtained by graphical analysis is refined in accordance with the criterion of maximum likelihood. The efficiency of the proposed method is supported by the results of statistical modeling.     

Analysis of the rate of propagation of the wave of change of boiling modes

An approximate analytical expression is derived for the velocity of the front of the wave of change of boiling modes on a rod and on a plate. The impact of the Thomson effect and of the heater orientation in the gravity field is included. Adequate agreement is demonstrated between the derived relations and experimental data.     

Evaluation of optical properties of highly scattering media by moments of distributions of times of flight of photons

A novel method for the determination of the optical properties of tissue from time-domain measurements is presented. The data analysis is based on the evaluation of the first moment and the second centralized moment, i.e., the mean time of flight and the variance of the measured distribution of times of flight (DTOF) of photons injected by short (picosecond) laser pulses. Analytical expressions are derived for calculation of absorption and of reduced scattering coefficients from these moments by application of diffusion theory for infinite and semi-infinite homogeneous media. The proposed method was tested on experimental data obtained with phantoms, and results for absorption and reduced scattering coefficients obtained by the proposed method are compared with those obtained by fitting of the same data with analytical solutions of the diffusion equation. Furthermore, the accuracy of the moment analysis was investigated for a range of integration limits of the DTOF. The moment analysis may serve as a comparatively fast method for evaluating optical properties with sufficient accuracy and can be used, e.g., for on-line monitoring of optical properties of biological tissue.     

可燃气体检测报警器测量结果的不确定度评定

本文详细介绍了可燃气体检测报警器示值误差测量结果的不确定度评定方法。     

水三相点复现的不确定度评定

水三相点是开尔文热力学温度的唯一基准点，也是ITS-90国际温标重要的定义固定点。因此，水三相点不确定度分析对整个温标的建立、温度量值传递起着至关重要的作用。近3年来，中国计量科学研究院研制出一系列高质量的水三相点容器，加强了水三相点的研究，为不确定度的分析提供了更为可靠的实验依据。同时，不确定度的分析也是客观评价新研制容器性能的一个重要指标。因此，根据实验结果对新研制容器所复现的水三相点进行了不确定度评定。评定结果表明，其扩展不确定度为0．16mK(k=2．69，P=0．99)。     

心电图机电压测量示值误差测量值的不确定度评定

本文介绍了心电图机电压测量示值误差测量值的不确定度评定与表示方法。     

Estimation of potentialities of methods of summation of direct measurement errors

Conventional methods for summation of direct measurement errors are considered. Conditions under which these methods provide consistent results are stated. It is proposed to utilize for characteristic of the total error, its interval estimator or the half-sum of the value obtained by adding up its arithmetic and geometric random errors.Translated from Izmeritel'naya Tekhnika, No. 4, pp. 10–12, April, 1995.